CN101747579A - 一种低烟无卤阻燃热塑性弹性体及其制备方法 - Google Patents

一种低烟无卤阻燃热塑性弹性体及其制备方法 Download PDF

Info

Publication number
CN101747579A
CN101747579A CN200810207538A CN200810207538A CN101747579A CN 101747579 A CN101747579 A CN 101747579A CN 200810207538 A CN200810207538 A CN 200810207538A CN 200810207538 A CN200810207538 A CN 200810207538A CN 101747579 A CN101747579 A CN 101747579A
Authority
CN
China
Prior art keywords
thermoplastic elastomer
low
smoke halogen
free flame
retardant thermoplastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810207538A
Other languages
English (en)
Inventor
杨涛
郭建鹏
陈晓东
肖健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Rizhisheng New Technology Development Co Ltd
Original Assignee
Shanghai Rizhisheng New Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Rizhisheng New Technology Development Co Ltd filed Critical Shanghai Rizhisheng New Technology Development Co Ltd
Priority to CN200810207538A priority Critical patent/CN101747579A/zh
Publication of CN101747579A publication Critical patent/CN101747579A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种低烟无卤阻燃热塑性弹性体及其制备方法，它由以下重量配比的原料制成：聚丙烯5-20％、相容剂1-5％、SEBS 10-30％、填充油20-50％、氢氧化镁8-15％，氮磷系阻燃剂20-30％，PE蜡1-3％、抗氧剂0.1-0.5％。其制备方法为：按重量配比秤取原料；先将SEBS和白油放入高混机中混合均匀，然后加入其他原料混混合2-5分钟，出料；将混合均匀的原料放入螺杆机中挤出造粒。本发明的特点是制备的低烟无卤热塑性弹性体具有非常好的阻燃效果，可以达到UL94V0级，可用于挤出低压电线的外皮，如数据线，充电器电线表皮等。

Description

一种低烟无卤阻燃热塑性弹性体及其制备方法
技术领域
本发明涉及一种低烟无卤阻燃热塑性弹性体及其制备方法，该材料具有低烟无卤阻燃特征，可以达到UL94 V0级，属于热塑性弹性体技术领域。
背景技术
目前市场上常见的阻燃级TPE为溴系阻燃剂制备而成，此种产品在燃烧时不但会放出大量的烟，而且会放出有毒气体，另外也不符合欧盟的环保指令。因此制备低烟无卤阻燃级的TPE具有重要的意义。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种低烟无卤阻燃热塑性弹性体及其制备方法。
本发明的目的可以通过以下技术方案来实现：
一种低烟无卤阻燃热塑性弹性体，其特征在于，它由以下重量配比的原料制成：
聚丙烯5-20％，
相容剂1-5％，
SEBS 10-30％，
填充油20-50％，
氢氧化镁8-15％，
氮磷系阻燃剂20-30％，
PE蜡1-3％，
抗氧剂0.1-0.5％。
所述的聚丙烯为均聚或者共聚聚丙烯，其熔融指数为10-60g/10min。
所述的相容剂为有马来酸酐接枝聚丙烯，其熔融指数为80-100g/10min。
所述的SEBS为粉状，氢化度＞95％。
所述的填充油为环烷油或白油。
所述的氢氧化镁为2000目，市售。
所述的氮磷系阻燃剂，可以是聚磷酸铵(APP)、磷酸酯、三聚氰胺氰尿酸盐(MCA)等的一种或多种。
所述的PE蜡为普通工业级聚乙烯蜡。
所述的抗氧剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂复配，优选抗氧剂1010与抗氧剂168复配。
一种低烟无卤阻燃热塑性弹性体的制备方法，其特征在于，该方法包括以下工艺步骤：
(1)按重量配比秤取原料：聚丙烯5-20％，相容剂1-5％，SEBS 10-30％，填充油20-50％，氢氧化镁8-15％，氮磷系阻燃剂20-30％，PE蜡1-3％，抗氧剂0.1-0.5％；
(2)先将SEBS和填充油放入高混机中混合3-5分钟，然后加入其他原料混合3-5分钟，出料；
(3)将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180-600转/分，温度为160-190℃。
本发明制备的低烟无卤阻燃热塑性弹性体材料不但具有良好的阻燃性能，而且具有优异的力学性能和加工性能，可直接挤出制备低压电线表皮，如数据线表皮，充电器电线表皮等，应用前景广阔。
具体实施方式
下面结合实施例，对本发明作进一步详细说明。
实施例1～2
实施例1～2配比(重量％)见表1。
表1
  原料名称   实施例1   实施例2
  聚丙烯   5.7   10.7
  相容剂   4   4
  SEBS   20   18
  白油   35   32
  氢氧化镁   8   8
  氮磷系阻燃剂   25   25
  PE蜡   2   2
  1010/168(1∶1)   0.3   0.3
将所有组分先将SEBS和白油放入高混机中混合3-5分钟，然后加入其他原料混合3-5分钟，加工温度在分别为165、175、185、190、190、190、190、、190、180℃，螺杆转数在300转/分。
对实施例1、2所得的低烟无卤阻燃热塑性弹性体，力学性能以ASTM测试。
实施例1样品和实施例2样品性能对照见表2。
表2
  测试项目  实施例1样品  实施例2样品
  拉伸强度MPa   2.1   2.9
  断裂伸长率％   ＞300   ＞300
  邵氏硬度A   62   73
  阻燃性   V0   V0

Claims (10)

1.一种低烟无卤阻燃热塑性弹性体，其特征在于，它由以下重量配比的原料制成：
聚丙烯5-20％，
相容剂1-5％，
SEBS 10-30％，
填充油20-50％，
氢氧化镁8-15％，
氮磷系阻燃剂20-30％，
PE蜡1-3％，
抗氧剂0.1-0.5％。
2.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的聚丙烯为均聚或者共聚聚丙烯，其熔融指数为10-60g/10min。
3.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的相容剂为有马来酸酐接枝聚丙烯，其熔融指数为80-100g/10min。
4.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的SEBS为粉状，氢化度＞95％。
5.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的填充油为环烷油或白油。
6.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的氢氧化镁为2000目，市售。
7.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的氮磷系阻燃剂，可以是聚磷酸铵(APP)、磷酸酯、三聚氰胺氰尿酸盐(MCA)等的一种或多种。
8.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的PE蜡为普通工业级聚乙烯蜡。
9.根据权利要求1所述的一种低烟无卤阻燃热塑性弹性体，其特征在于，所述的抗氧剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂复配，优选抗氧剂1010与抗氧剂168复配。
10.一种如权利要求1所述低烟无卤阻燃热塑性弹性体的制备方法，其特征在于，该方法包括以下工艺步骤：
(1)按重量配比秤取原料：聚丙烯5-20％，相容剂1-5％，SEBS 10-30％，填充油20-50％，氢氧化镁8-15％，氮磷系阻燃剂20-30％，PE蜡1-3％，抗氧剂0.1-0.5％；
(2)先将SEBS和填充油放入高混机中混合3-5分钟，然后加入其他原料混合3-5分钟，出料；
(3)将混合的原料放入螺杆机中挤出造粒，螺杆机的转速为180-600转/分，温度为160-190℃。
CN200810207538A 2008-12-22 2008-12-22 一种低烟无卤阻燃热塑性弹性体及其制备方法 Pending CN101747579A (zh)