CN101696124B - 一种强化釉骨质瓷的烧成工艺 - Google Patents
一种强化釉骨质瓷的烧成工艺 Download PDFInfo
- Publication number
- CN101696124B CN101696124B CN200910186320XA CN200910186320A CN101696124B CN 101696124 B CN101696124 B CN 101696124B CN 200910186320X A CN200910186320X A CN 200910186320XA CN 200910186320 A CN200910186320 A CN 200910186320A CN 101696124 B CN101696124 B CN 101696124B
- Authority
- CN
- China
- Prior art keywords
- glaze
- firing
- base
- goods
- mouth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于陶瓷烧成技术领域,特别涉及一种强化釉骨质瓷的烧成工艺。其特征是:将坯子成型好后,经过780-800℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,第一次烧成采用还原火焰一次烧成,烧成温1330-1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;烧制好冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1270-1280℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。本发明的强化釉骨质瓷具有白度好,半透明性好,热稳定性好,釉面硬度高,无铅镉溶出等特点。
Description
技术领域
本发明属于陶瓷烧成技术领域,特别涉及一种强化釉骨质瓷的烧成工艺。
背景技术
骨质瓷通常是经过高温素烧和低温釉烧,两次烧制而成的一种瓷器。瓷质细腻通透,釉面润泽光亮,陈设高雅等特点,是公认的高档瓷器之一。但由于采用低温釉烧故而釉面强度较低,不易保养,在清洗时只能用手,不可用洗碗机或清洁球清洗以免釉面擦伤以后,形成污垢。使用微波炉热交换次数多了会损伤瓷质使瓷器釉面发黑,不能耐酸等。如:申请号为200610102103.4,发明名称为《彩色骨质瓷及其生产方法》公开的方法,注浆或机制产品成型后素烧成坯,素烧温度:1225℃-1235℃;泥坯经细磨后施透明釉再烧成瓷,烧成温度:900℃-1100℃;又如:申请号为200510063373.4发明名称为《一种骨质瓷用高温硬质釉配方及骨质瓷生产工艺》公开的工艺为:第一步是在干燥后的坯体的正面喷施骨质瓷用高温硬质釉,同时在坯体背面用仿形匣钵支撑,防止坯体变形,然后送入素窑内在1270℃-1280℃烧成;第二步是在第一次喷施高温硬质釉烧成的瓷件制品背面喷施低温釉,送入釉烧窑内在1050℃-1160℃进行第二次釉烧。
发明内容
本发明的目的在于提供一种强化釉骨质瓷,通过调整坯釉配方来提高烧成温度,强化釉骨质瓷的第一次烧成温度在1350℃左右,第二次烧成温度在1280℃左右,第一次烧成时采用坯釉一起烧成以及第二次口釉烧成的同时进行釉中彩的烧制和采用本坯泥做垫饼的装坯工艺的强化釉骨质瓷的烧成工艺。
本发明是这样实现的:
1)、将坯子成型好后,经过780-800℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
2)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原火焰一次烧成,烧成温度1330-1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
3)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1270-1280℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。
本发明有如下特点:
1、提高了瓷器的釉面强度
提高了坯釉的烧成温度,二次烧成都采用还原焰气氛烧成,并且烧成温度都在1280℃以上,比传统骨质瓷烧成温度提高了120℃左右,烧成温度高,可增强瓷器强度,釉面的硬度提高了1.0Gpa;
2、提高了瓷器质量
由于采用了本坯泥做垫饼,垫饼做成与制品口沿完全吻合的凹槽,把制品口沿放到垫饼凹槽内烧制,因制品与垫饼所用泥料一致(故称本坯泥),因此烧成时制品与垫饼同时收缩并且收缩一致可完全控制变形缺陷,可提高质量10%以上。
3、降低了成本,提高了档次
第一次烧成时采用了坯釉一次烧成,烧成后贴釉中彩花纸与口沿上釉后一起二次烧制,减少了烤花工序可节约成本10%,同时全部做成釉中彩后,致使产品无铅无毒提高了档次。
本发明的强化釉骨质瓷具有白度好,半透明性好,热稳定性好,釉面硬度高,无铅镉溶出等特点。通过国家陶瓷产品质量监督检验中心(江西)检测,达到以下技术数据参数:
1、热稳定性:180/20℃热交换一次未裂,检测依据GB/T3298-2008。
2、吸水率:0.17~0.21%,检测依据GB/T3299-1996。
3、铅溶出:0.0mg/l,检测依据GB/T3534-2002。
4、镉溶出:0.00/l,检测依据GB/T3534-2002。
5、白度:80.1~80.6,检测依据QB/T1503-1992。
6,釉面硬度:5.8Gpa,检测依据GB/T3731-1999。
具体实施方式
本发明可以通过发明内容中说明的技术具体实施,通过下面的实施例可以对本发明进行进一步的描述,然而,本发明的范围并不限于下述实施例。
实施例1:
1)、采用坯釉由下列各成分重量百分数组成:骨粉为40-55%,高岭土为25-34%,粘土为8-12%,长石或石英为8-14%,其余为电解质添加剂,百分数总量为100%。目的是提高烧成温度。
2)、将坯子成型好后,经过800℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
3)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原气氛一次烧成,烧成温度1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
4)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1280℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。
实施例2:坯釉材料同上
1)、将坯子成型好后,经过780℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
2)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原火焰一次烧成,烧成温度1330℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
3)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1270℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。
实施例3:坯釉材料同上
1)、将坯子成型好后,经过800℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
2)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原火焰一次烧成,烧成温度1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
3)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1280℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。
实施例4:坯釉材料同上
1)、将坯子成型好后,经过780℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
2)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原火焰一次烧成,烧成温度1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
3)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1270℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。
Claims (2)
1.一种强化釉骨质瓷的烧成工艺,其特征是:
1)、将坯子成型好后,经过780-800℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
2)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原火焰一次烧成,烧成温度1330-1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
3)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1270-1280℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。
2.根据权利要求1所述的一种强化釉骨质瓷的烧成工艺,其特征是:
1)、采用坯釉由下列各成分重量百分数组成:骨粉为40-55%,高岭土为25-34%,粘土为8-12%,长石或石英为8-14%,其余为电解质添加剂,百分数总量为100%。
2)、将坯子成型好后,经过800℃素烧后打磨光滑,再上釉,再把口沿与底沿釉去掉;
3)、装坯时把去掉口沿釉的制品的口沿倒放于定型垫饼的凹槽内,一起装坯入窑,坯与釉的第一次烧成采用还原火焰一次烧成,烧成温度1350℃,所述定型垫饼是采用与制品所用泥料一致的本坯泥做成的与制品口沿完全吻合的凹槽垫饼;
4)、烧制好后,冷却后,选瓷分级,贴釉中彩花,等花纸干了以后再上口沿釉,然后通过1280℃的弱还原气氛二次烧成,即第二次口釉烧成的同时进行釉中彩的烧制。