CN101693233A - Optically variable color coating steel plate and processing method thereof - Google Patents
Optically variable color coating steel plate and processing method thereof Download PDFInfo
- Publication number
- CN101693233A CN101693233A CN200910035623A CN200910035623A CN101693233A CN 101693233 A CN101693233 A CN 101693233A CN 200910035623 A CN200910035623 A CN 200910035623A CN 200910035623 A CN200910035623 A CN 200910035623A CN 101693233 A CN101693233 A CN 101693233A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- layer
- optically variable
- color coating
- variable color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an optically variable color coating steel plate and a processing method thereof, belonging to the technical field of color coating steel plates. The steel plate comprises a hot dip galvanizing steel plate. The hot dip galvanizing steel plate is combined with a corrosion-resistant base protection layer towards one inward side under the use state; a set layer is combined on the surface of the base protection layer, and an optically variable light interference layer is combined on the surface of the set layer. The invention provides the technical scheme that the optically variable light interference layer is changed along with the difference of observation angles or the change of light source irradiating angles under the irradiation of light rays, thereby showing a color rendering effect; the recommended processing method has few process steps, is suitable for industrial application and can ensure the prominence of the technical effect of the optically variable color coating steel plates.
Description
Technical field
The invention belongs to the color coating layer steel plate technical field, be specifically related to a kind of optically variable color coating steel plate, and relate to the processing method of this steel plate.
Background technology
The surface (being generally a side surface) that color coated steel plates is based on steel plate applies the organic coating of various different colours and uses and forms coloured coating on the surface of steel plate and name, and industry also abbreviates Coil Coating Products or colored steel as.Use galvanized steel plain sheet as the color coating layer steel plate of substrate except by the protection of zinc layer, also the organic coating layer by the outer aforementioned different colours that applies of zinc layer plays desirable covering buffer action.The steel plate that applies the organic coating layer of different colours outside zinc coat improves more than 50% than promptly anticorrosive, the anti-life-span of getting rusty in the service life of simple galvanized steel plain sheet.Therefore the surface that aforesaid organic coating is coated on galvanized steel plain sheet not only has the steel plate of prolongation service life, and has desirable decoration and sight effect.
Since above-mentioned color coating layer steel plate have lightweight, attractive in appearance, corrosion resistance good and the strong point of easily processing, thereby be widely used in building, the manufacturing of boats and ships, vehicle, household electrical appliances, furniture and electronic electric equipment.But, also there is following shortcoming: although both had the steel plate of prolongation service life at the organic coating layer of the various different pigment of the surface-coated of galvanized steel plain sheet, the effect that has cosmetic decoration again, yet, this organic coating layer does not have peculiar multicolor effect, so-called peculiar multicolor effect is meant under the irradiation of light, difference along with viewing angle, the color of dope layer changes, perhaps viewing angle is constant and change the light source irradiating angle, the color of dope layer changes thereupon, present phenomenon such as red-Huang-green-multiple color swaps such as indigo plant, only this could embody rich texture, gloss is unique graceful and embody value of art appreciation and color rendering effect, and then the purposes of color coating layer steel plate is expanded and use value is able to further lifting.Yet the color coating layer steel plate in the prior art still is not enough to possess this advantage.
In view of this, the applicant thinks, be necessary the color coating layer steel plate in the prior art is done rationally to improve,, the use value of color coating layer steel plate further embodied so that satisfy the pursuit requirement of the decorative effect that people play up unique graceful, the art appreciation of rich texture, gloss and color.For this reason, the applicant retrieves, yet there is no all technology enlightenments of being used for reference that has in disclosed Chinese patent literature and the professional journals.
Summary of the invention
Task of the present invention is to provide a kind of and had both helped to improve corrosion-resistant and use and increase the service life, and helps again promoting the color rendering effect and uses the expanded application scope and promote the optically variable color coating steel plate of use value.
An also task of the present invention is to provide a kind of processing method of optically variable color coating steel plate, and this method processing step is simple and can ensure comprehensive embodiment of the technique effect of optically variable color coating steel plate.
Task of the present invention is finished like this; a kind of optically variable color coating steel plate; comprise hot-dip galvanizing sheet steel; this hot-dip galvanizing sheet steel is combined with corrosion-resistant protective layer towards the surface of an interior side under user mode; and hot-dip galvanizing sheet steel outward surface of a side under user mode is combined with end sheath; be combined with on the surface of end sheath and set off layer, and be combined with the angle-dependent heterochromous light interference layer on the surface of setting off layer.
In a specific embodiment of the present invention, the thickness of described corrosion-resistant protective layer is 6-8 μ m; The thickness of sheath of the described end is 4-6 μ m; The described thickness that sets off layer is 9-11 μ m; The thickness of described angle-dependent heterochromous light interference layer is 8-12 μ m.
In another specific embodiment of the present invention, described corrosion-resistant protective layer is an epoxy resin coating; Sheath of the described end is a polyurethane paint; The described layer that sets off is fluorocarbon coating; Described angle-dependent heterochromous light interference layer is a fluorine carbon varnish.
In another specific embodiment of the present invention, described fluorine carbon varnish is to be made by following raw materials in weight portion: 100 parts of fluorocarbon resins, solvent 180-220 part, effect interference pigment 60-100 part.
In another specific embodiment of the present invention, described solvent is the mixture of toluene or dimethylbenzene and your ketone of different fluorine, and wherein, your weight part ratio of ketone of toluene or dimethylbenzene and different fluorine is 140-160: 100.
An also task of the present invention is finished like this, a kind of processing method of optically variable color coating steel plate, and it may further comprise the steps:
A) preliminary treatment scribbles oily hot-dip galvanizing sheet steel 1 to the surface earlier and carries out degreasing, and the degreasing after washing uses the Chrome-free pretreatment fluid to handle after washing, obtains treating the application hot-dip galvanizing sheet steel;
B) application, treat application hot-dip galvanizing sheet steel corrosion-resistant protective layer of surface-coated towards an interior side under user mode, and to hot-dip galvanizing sheet steel sheath at the bottom of outward the surface-coated of a side under the user mode, the baking of introducing oven, and control baking temperature and time, obtain coated steel plate one time;
C) secondary application is set off layer to the surface-coated of the end sheath of a coated steel plate, applies to set off layer back and introduce oven baking, regulates baking temperature and time, obtains the secondary coated steel plate;
D) three applications to the surface-coated angle-dependent heterochromous light interference layer that sets off layer of secondary coated steel plate, are introduced the oven baking behind the coating angle-dependent heterochromous light interference layer, adjust baking temperature and time, obtain optically variable color coating steel plate.
More of the present invention and in specific embodiment; the thickness of the corrosion-resistant protective layer step B) is 6-8 μ m; the thickness of sheath of the described end is 4-6 μ m, and described control baking temperature and time are that baking temperature and time are controlled to be 190-210 ℃ and 20-30s respectively.
In of the present invention and then specific embodiment, step C) thickness that sets off layer described in is 9-11 μ m, and described adjusting baking temperature and time are that baking temperature and time are adjusted to 210-230 ℃ and 20-30s respectively.
The thickness of the angle-dependent heterochromous light interference layer in again of the present invention and then specific embodiment, step D) is 8-12 μ m, and described adjustment baking temperature and time are that baking temperature and time are adjusted into 210-230 ℃ and 20-30s respectively.
Technical scheme provided by the invention is owing to be combined with end sheath successively, set off layer and angle-dependent heterochromous light interference layer hot-dip galvanizing sheet steel outward surface of a side under user mode, thereby under the irradiation of light along with the difference of viewing angle or the change of light source irradiating angle, the angle-dependent heterochromous light interference layer is subjected to interference of light and changes, present the color rendering effect, make the application of hot-dip galvanizing sheet steel effectively extended to high-grade household electrical appliances with sheet material, automobile sheet material and high-grade decorate to decorate promoted with sheet material and use value; The recommended processing method processing step is few, can adapt to industrial application, and can ensure the appearing suddenly of technique effect of optically variable color coating steel plate.
Description of drawings
Accompanying drawing is the cutaway view of optically variable color coating steel plate of the present invention.
The specific embodiment
Embodiment 1:
Ask for an interview accompanying drawing, process optically variable color coating steel plate shown in the drawings according to the following steps.
A) preliminary treatment, earlier surface (two sides) is scribbled the hot-dip galvanizing sheet steel 1 degreasing agent degreasing of oil, after degreasing, wash, here degreasing of being said and washing belongs to known technology, and for the production industry of color coating layer steel plate is widely to know and use, therefore the applicant no longer gives unnecessary details it, after washing, carry out preliminary treatment with the Chrome-free pretreatment fluid, the Chrome-free pretreatment fluid preferably adopts the Chrome-free pretreatment fluid of the CT-E218 trade mark of the rapids smart Co., Ltd of Chinese Shanghai handkerchief card production and sales, when the pretreated hot-dip galvanizing sheet steel 1 of Chrome-free pretreatment fluid can be in application, strengthen and below adhesion between the end sheath 3 that is about to mention, obtain treating the application hot-dip galvanizing sheet steel;
B) application, utilize color coating layer steel plate production firm widely uses in the prior art coating machine to by steps A) resulting treat the application hot-dip galvanizing sheet steel under user mode towards the surface-coated thickness of an interior side be 7 μ m's and the corrosion-resistant protective layer 2 filled the post of by epoxy resin coating, simultaneously to outward the surface-coated thickness of a side under user mode be 5 μ m's and the end sheath 3 filled the post of by polyurethane paint, apply corrosion-resistant protective layer 2 on one side, when applying on one side end sheath 3 hot-dip galvanizing sheet steel 1 is introduced the oven baking, baking temperature is controlled to be 200 ℃, stoving time is controlled to be 25s, stoving time depends on the gait of march of hot-dip galvanizing sheet steel 1 in fact, be expert at behind the oven, obtain coated steel plate one time;
C) secondary application, to by step B) the surface-coated thickness of the end sheath 3 of a coated steel plate obtaining be 10 μ m's and by color be the fluorocarbon coating of black fill the post of set off layer 4, set off layer 4 by this and promptly work the effect of setting off for angle-dependent heterochromous light interference layer 5 plays to set off, after layer 4 is set off in coating, steel plate is introduced oven, baking temperature is adjusted to 220 ℃, stoving time is adjusted to 25s, steel plate is capable go out oven after, obtain the secondary coated steel plate;
D) three applications, to the secondary coated steel plate set off layer 4 surface-coated thickness be 10 μ m's and the angle-dependent heterochromous light interference layer 5 filled the post of by fluorine carbon varnish, and applying the 5 back introducing oven baking of angle-dependent heterochromous light interference layer, baking temperature is adjusted into 220 ℃, stoving time is adjusted into 25s, obtains by optically variable color coating steel plate shown in the drawings.Fluorine carbon varnish in this step is to be made by following raw materials in weight portion: 80 parts of 100 parts of fluorocarbon resins, 200 parts of solvents and effect interference pigments, these three kinds of raw materials are used mechanical or manually stir and fully stir evenly, wherein: solvent is the mixture of dimethylbenzene and your ketone of different fluorine, and your weight part ratio of ketone of dimethylbenzene and different fluorine is 150: 100.Described effect interference pigment can be from the market acquisition, for example preferably uses by the trade mark of the Chinese Guangdong province Longhua Pearly-Lustre Pigment Co., Ltd., Shantou production interference of light camouflage paint as 52IY.
Embodiment 2:
Ask for an interview accompanying drawing, process optically variable color coating steel plate shown in the drawings according to the following steps.
A) preliminary treatment, earlier hot-dip galvanizing sheet steel 1 usefulness that surface (two sides) is scribbled oil is taken off the finger agent and is taken off finger, after degreasing, wash, here degreasing of being said and washing belongs to known technology, and for the production industry of color coating layer steel plate is widely to know and use, therefore the applicant no longer gives unnecessary details it, after washing, carry out preliminary treatment (the Chrome-free pretreatment fluid is the Chrome-free pretreatment fluid of the rapids smart CT-E218 of the Co., Ltd trade mark of Shanghai handkerchief card) with the Chrome-free pretreatment fluid, when the pretreated hot-dip galvanizing sheet steel 1 of Chrome-free pretreatment fluid can be in application, strengthen and below adhesion between the end sheath 3 that is about to mention, obtain treating the application hot-dip galvanizing sheet steel;
B) application, utilize color coating layer steel plate production firm widely uses in the prior art coating machine to by steps A) the resulting surface-coated thickness for the treatment of application hot-dip galvanizing sheet steel side in existing under user mode be 8 μ m's and the corrosion-resistant protective layer 2 filled the post of by epoxy resin coating, simultaneously to outward the surface-coated thickness of a side under user mode be 4 μ m's and the end sheath 3 filled the post of by polyurethane paint, apply corrosion-resistant protective layer 2 on one side, when applying on one side end sheath 3 hot-dip galvanizing sheet steel 1 is introduced the oven baking, baking temperature is controlled to be 190 ℃, stoving time is controlled to be 30s, stoving time depends on the gait of march of hot-dip galvanizing sheet steel 1 in fact, be expert at behind the oven, obtain coated steel plate one time;
C) secondary application, to by step B) the surface-coated thickness of the end sheath 3 of a coated steel plate obtaining be 9 μ m's and by color be the fluorocarbon coating of black fill the post of set off layer 4, set off layer 4 by this and promptly work the effect of setting off for angle-dependent heterochromous light interference layer 5 plays to set off, after layer 4 is set off in coating, steel plate is introduced oven, baking temperature is adjusted to 210 ℃, stoving time is adjusted to 30s, steel plate is capable go out oven after, obtain the secondary coated steel plate;
D) three applications, to the secondary coated steel plate set off layer 4 surface-coated thickness be 12 μ m's and the angle-dependent heterochromous light interference layer 5 filled the post of by fluorine carbon varnish, and applying the 5 back introducing oven baking of angle-dependent heterochromous light interference layer, baking temperature is adjusted into 210 ℃, stoving time is adjusted into 30s, obtains by optically variable color coating steel plate shown in the drawings.Fluorine carbon varnish in this step is to be made by following raw materials in weight portion: 100 parts of 100 parts of fluorocarbon resins, 180 parts of solvents and effect interference pigments, these three kinds of raw materials are used mechanical or manually stir and fully stir evenly, wherein: solvent is the mixture of dimethylbenzene and your ketone of different fluorine, and your weight part ratio of ketone of dimethylbenzene and different fluorine is 160: 100.Described effect interference pigment can be from the market acquisition, for example preferably uses by the trade mark of the Chinese Guangdong province Longhua Pearly-Lustre Pigment Co., Ltd., Shantou production interference of light camouflage paint as 52IY.
Embodiment 3:
Ask for an interview accompanying drawing, process optically variable color coating steel plate shown in the drawings according to the following steps.
A) preliminary treatment, earlier hot-dip galvanizing sheet steel 1 usefulness that surface (two sides) is scribbled oil is taken off the finger agent and is taken off finger, after degreasing, wash, here degreasing of being said and washing belongs to known technology, and for the production industry of color coating layer steel plate is widely to know and use, therefore the applicant no longer gives unnecessary details it, after washing, carry out preliminary treatment (the Chrome-free pretreatment fluid is the Chrome-free pretreatment fluid of the rapids smart CT-E218 of the Co., Ltd trade mark of Shanghai handkerchief card) with the Chrome-free pretreatment fluid, when the pretreated hot-dip galvanizing sheet steel 1 of Chrome-free pretreatment fluid can be in application, strengthen and below adhesion between the end sheath 3 that is about to mention, obtain treating the application hot-dip galvanizing sheet steel;
B) application, utilize color coating layer steel plate production firm widely uses in the prior art coating machine to by steps A) the resulting surface-coated thickness for the treatment of application hot-dip galvanizing sheet steel side in existing under user mode be 6 μ m's and the corrosion-resistant protective layer 2 filled the post of by epoxy resin coating, simultaneously to outward the surface-coated thickness of a side under user mode be 6 μ m's and the end sheath 3 filled the post of by polyurethane paint, apply corrosion-resistant protective layer 2 on one side, when applying on one side end sheath 3 hot-dip galvanizing sheet steel 1 is introduced the oven baking, baking temperature is controlled to be 210 ℃, stoving time is controlled to be 20s, stoving time depends on the gait of march of hot-dip galvanizing sheet steel 1 in fact, be expert at behind the oven, obtain coated steel plate one time;
C) secondary application, to by step B) the surface-coated thickness of the end sheath 3 of a coated steel plate obtaining be 11 μ m's and by color be the fluorocarbon coating of black fill the post of set off layer 4, set off layer 4 by this and promptly work the effect of setting off for angle-dependent heterochromous light interference layer 5 plays to set off, after layer 4 is set off in coating, steel plate is introduced oven, baking temperature is adjusted to 230 ℃, stoving time is adjusted to 20s, steel plate is capable go out oven after, obtain the secondary coated steel plate;
D) three applications, to the secondary coated steel plate set off layer 4 surface-coated thickness be 8 μ m's and the angle-dependent heterochromous light interference layer 5 filled the post of by fluorine carbon varnish, and applying the 5 back introducing oven baking of angle-dependent heterochromous light interference layer, baking temperature is adjusted into 230 ℃, stoving time is adjusted into 20s, obtains by optically variable color coating steel plate shown in the drawings.Fluorine carbon varnish in this step is to be made by following raw materials in weight portion: 60 parts of 100 parts of fluorocarbon resins, 220 parts of solvents and effect interference pigments, these three kinds of raw materials are used mechanical or manually stir and fully stir evenly, wherein: solvent is the mixture of dimethylbenzene and your ketone of different fluorine, and your weight part ratio of ketone of dimethylbenzene and different fluorine is 140: 100.Described effect interference pigment can be from the market acquisition, for example preferably uses by the trade mark of the Chinese Guangdong province Longhua Pearly-Lustre Pigment Co., Ltd., Shantou production interference of light camouflage paint as 52IY.
Can be used as high-grade household electrical appliance, automobile and the high-grade sheet material of decorateing of decorating by the foregoing description 1 to 3 resulting optically variable color coating steel plate.
Claims (9)
1. optically variable color coating steel plate; it is characterized in that comprising hot-dip galvanizing sheet steel (1); this hot-dip galvanizing sheet steel (1) is combined with corrosion-resistant protective layer (2) towards the surface of an interior side under user mode; and hot-dip galvanizing sheet steel (1) outward surface of a side under user mode is combined with end sheath (3); be combined with on the surface of end sheath (3) and set off layer (4), and be combined with angle-dependent heterochromous light interference layer (5) on the surface of setting off layer (4).
2. optically variable color coating steel plate according to claim 1, the thickness that it is characterized in that described corrosion-resistant protective layer (2) are 6-8 μ m; The thickness of sheath of the described end (3) is 4-6 μ m; The described thickness that sets off layer (4) is 9-11 μ m; The thickness of described angle-dependent heterochromous light interference layer (5) is 8-12 μ m.
3. optically variable color coating steel plate according to claim 1 and 2 is characterized in that described corrosion-resistant protective layer (2) is an epoxy resin coating; Sheath of the described end (3) is a polyurethane paint; The described layer (4) that sets off is fluorocarbon coating; Described angle-dependent heterochromous light interference layer (5) is a fluorine carbon varnish.
4. optically variable color coating steel plate according to claim 3 is characterized in that described fluorine carbon varnish is to be made by following raw materials in weight portion: 100 parts of fluorocarbon resins, solvent 180-220 part, effect interference pigment 60-100 part.
5. optically variable color coating steel plate according to claim 4 is characterized in that described solvent is the mixture of toluene or dimethylbenzene and your ketone of different fluorine, and wherein, your weight part ratio of ketone of toluene or dimethylbenzene and different fluorine is 140-160: 100.
6. the processing method of an optically variable color coating steel plate as claimed in claim 1 is characterized in that it may further comprise the steps:
A) preliminary treatment scribbles oily hot-dip galvanizing sheet steel 1 to the surface earlier and carries out degreasing, and the degreasing after washing uses the Chrome-free pretreatment fluid to handle after washing, obtains treating the application hot-dip galvanizing sheet steel;
B) application, treat application hot-dip galvanizing sheet steel corrosion-resistant protective layer of surface-coated towards an interior side under user mode, and to hot-dip galvanizing sheet steel sheath at the bottom of outward the surface-coated of a side under the user mode, the baking of introducing oven, and control baking temperature and time, obtain coated steel plate one time;
C) secondary application is set off layer to the surface-coated of the end sheath of a coated steel plate, applies to set off layer back and introduce oven baking, regulates baking temperature and time, obtains the secondary coated steel plate;
D) three applications to the surface-coated angle-dependent heterochromous light interference layer that sets off layer of secondary coated steel plate, are introduced the oven baking behind the coating angle-dependent heterochromous light interference layer, adjust baking temperature and time, obtain optically variable color coating steel plate.
7. the processing method of optically variable color coating steel plate according to claim 6; it is characterized in that step B) described in the thickness of corrosion-resistant protective layer be 6-8 μ m; the thickness of sheath of the described end is 4-6 μ m, and described control baking temperature and time are that baking temperature and time are controlled to be 190-210 ℃ and 20-30s respectively.
8. the processing method of optically variable color coating steel plate according to claim 6, it is characterized in that step C) described in set off the layer thickness be 9-11 μ m, described adjusting baking temperature and time are that baking temperature and time are adjusted to 210-230 ℃ and 20-30s respectively.
9. the processing method of optically variable color coating steel plate according to claim 6, it is characterized in that step D) described in the thickness of angle-dependent heterochromous light interference layer be 8-12 μ m, described adjustment baking temperature and time are that baking temperature and time are adjusted into 210-230 ℃ and 20-30s respectively.