CN101556837A - 高温无铅碳浆及其制备方法 - Google Patents
高温无铅碳浆及其制备方法 Download PDFInfo
- Publication number
- CN101556837A CN101556837A CNA2009100395039A CN200910039503A CN101556837A CN 101556837 A CN101556837 A CN 101556837A CN A2009100395039 A CNA2009100395039 A CN A2009100395039A CN 200910039503 A CN200910039503 A CN 200910039503A CN 101556837 A CN101556837 A CN 101556837A
- Authority
- CN
- China
- Prior art keywords
- percentage
- weight
- glass
- high temperature
- temperature lead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种高温无铅碳浆及其制备方法,提供一种无铅环保的、使用温度高的、方阻可调且烧成特性优良的高温无铅碳浆的制备工艺。本发明由固相组分包括石墨碳粉加高温无铅玻璃粉,和有机粘结剂组合,固相成份与有机溶剂的重量百分比为30~60∶70~40,固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为30~70∶70~30,粒径均小于1μm。
Description
技术领域
本发明涉及一种基于陶瓷、云母、玻璃等耐高温材料上用的厚膜电阻浆料,尤其涉及一种耐高温的无铅稀土碳浆的电阻浆料及其制备方法。
背景技术
在电加热领域中,新型的加热元件要求体积要小,功率要大,表面热负荷要大,热情性要小,热效率要高,耗电要低,热启动要快,温度场要均匀,无电磁污染,绿色、环保、安全可靠。电子浆料是制造厚膜元件的基础材料,是一种由固体粉末和有机溶剂经过三辊轧制混合均匀的膏状物。在厚膜电路技术领域,传统的基板有陶瓷基板和金属,二者均有其局限性。目前国内外采用的碳浆做为厚膜电阻用的含铅里很高,有的甚至高达70%对环境造成极大的污染,而且使用温度比校低,在200℃以下,超过200℃或老化,使寿命发生衰减,影响产品的广泛应用。
发明内容
针对现有技术存在的问题,本发明所要解决的技术问题之一是要提供一种,本发明所要解决的问题是提供一种无铅环保的、使用温度高的、方阻可调且烧成特性优良的高温无铅碳浆的制备工艺。
为达上述目的,本发明高温无铅碳浆通过下述技术方案予以实现:
一种高温无铅碳浆,由固相组分包括石墨碳粉加高温无铅玻璃粉,和有机粘结剂组合,固相成份与有机溶剂的重量百分比为(30~60)∶(70~40),所述固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为(30~70)∶(70~30),粒径均小于1цm。
进一步地,所述高温无铅玻璃粉为Bi2O3-B2O3-SiO2-La2O3系高温无铅稀土封接玻璃,各类原料及其重量比为:
Bi2O3:60~90,B2O3:5~15,
SiO2:0.5~8,La2O3:0.1~5;
有机溶剂中各组重量百分比是:
松油醇:90~98%,乙基纤维素:1~8%,
丁基卡必醇:0~15%,蓖麻油:0.1~3%,
大豆卵磷脂:0~0.1%,甲基纤维素:0~5%。
本发明的基于高温无铅碳浆的制备方法,包括下述步骤:
①、首先制备高温无铅稀土玻璃粉:分别以化学纯Bi2O3、由分析纯分引入SiO2,由分析纯硼酸引入B2O3,由分析纯引入La2O3,按重量百分比为:
Bi2O3:60~90,B2O3:5~15,
SiO2:0.5~8,La2O3:0.1~5,
配好料,混合均匀,用刚玉坩埚在高温炉中于1100~1350℃下熔化,保温1小时,水淬,得到高温无铅稀土玻璃微渣,玻璃放用行星球磨机中磨到粒度不大于1цm的玻璃粉;
②、再制备有机溶剂,按重量百分比为:
松油醇:90~98%,乙基纤维素:1~8%,
丁基卡必醇:0~15%,蓖麻油:0.1~3%,
大豆卵磷脂:0~0.1%,甲基纤维素:0~5%,
调节各种重量百分比使粘度在100~200mPas;
③、浆料的调试:按固相成份与有机溶剂的重量百分比为30~60∶70~40,所述固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为30~70∶70~30进行重量百分比调试,得到不同方阻的电阻浆料,玻璃含量越高,烧结时粘结性能越好,附着力也强,但方阻越大。
本发明优点:采用无机非金属复合材料,无铅无毒、环保,而且使用温度比传统的高出100℃,另外由于采用具有封接力强的玻璃做为固相成分,粘着力强,附着强度高,使用寿命长。
具体实施方式
下面结合具体实施方式对本发明作进一步详细描述:
本发明高温无铅稀土碳浆的制备,其特点由固相组分(石墨碳粉+高温无铅玻璃粉)和有机粘结剂组合,固相成份与有机溶剂的重量百分比为(30~60)∶(70~40),所述固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为(30~70)∶(70~30),粒径均小于1цm。经过高温烧结,使用温度能达到300℃,大大地提高产品的使用,给社会带来良好的经济效益。
作为本发明的进一步改进,所述的玻璃为Bi2O3-B2O3-SiO2-La2O3系高温无铅稀土封接玻璃,各类原料及其重量百分比(重量比)为:
Bi2O3(60~90),B2O3(5~15),
SiO2(0.5~8),La2O3(0.1~5),
与陶瓷、玻璃等基材具有良好的封接特性,烧结过程中流动能力强,不会过早析晶,通常情况下其转变温度在400℃左右,其膨胀系数在(60~80)×10-7/℃之间。由于掺杂稀土La2O3可大大地浆料的导电性,抗氧化能力,增加在玻玻烧结过程中的流动性及润湿性。而且无铅又环保。
所述有机溶剂中各组重量百分比是:
松油醇(90~98%),乙基纤维素(1~8%),
丁基卡必醇(0~15),蓖麻油(0.1~3%),
大豆卵磷脂(0~0.1%),甲基纤维素(0~5%)。
本发明的高温无铅碳浆的制备方法,包括下述步骤:
A:制备高温无铅稀土玻璃粉:分别以化学纯Bi2O3、由分析纯分引入SiO2,由分析纯硼酸引入B2O3,由分析纯引入La2O3,按重量百分比为:
Bi2O3(60~90),B2O3(5~15),
SiO2(0.5~8),La2O3(0.1~5),
配好料,混合均匀,用刚玉坩埚在高温炉中于1100~1350℃下熔化,保温1小时,水淬,得到高温无铅稀土玻璃微渣,玻璃放用行星球磨机中磨到粒度不大于1цm的玻璃粉;
B:配制有机溶剂,松油醇(90~98%),乙基纤维素(1~8%),丁基卡必醇(0~15),蓖麻油(0.1~3%),大豆卵磷脂(0~0.1%),甲基纤维素(0~5%).调节各种重量百分比使粘度在100~200mPas;
C:浆料的调试:按固相成份与有机溶剂的重量百分比为(30~60)∶(70~40),所述固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为(30~70)∶(70~30)进行重量百分比调试,得到不同方阻的电阻浆料,玻璃含量越高,烧结时粘结性能越好,附着力也强,但方阻越大。
举例说明:
1、玻璃相制得:Bi2O380%,B2O315%,SiO24.5%,La2O30.5%,按重量百分比配好,在1200℃熔化,水淬得到玻璃渣,球磨到1цm;
2、固相成分:石墨碳粉40%,玻璃粉:60%;
3、有机熔剂:松油醇96%,乙基纤维素3%,丁基卡必醇0.2%,蓖麻油0.2%,大豆卵磷脂0.1%,甲基纤维素(0.5%);
4、浆料特性:
方阻:1KΩ/□,粘度150Pas;
5、使用温度
将浆料用150目的丝网印刷,在600℃下进行烧结,然后在320℃的工作温度下工作1000小时功率变化2.5%。
以上所举实施例仅用为方便举例说明本发明,仅为本发明之较佳实施例而已,并非对本发明作实施任何形式上的限制,任何所属技术领域中具有通常知识者,若在不脱离本发明所提技术特征的范围内,利用本发明所揭示技术内容做出局部更改均等变化、或修饰的等效实施例,并且未脱离本发明的技术特征内容,均仍属于本发明技术特征的涵盖范围内。
Claims (4)
1、一种高温无铅碳浆,其特征是:由固相组分包括石墨碳粉加高温无铅玻璃粉,和有机粘结剂组合,固相成份与有机溶剂的重量百分比为30~60∶70~40,所述固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为30~70∶70~30,粒径小于1цm。
2、根据权利要求1所述的高温无铅碳浆,其特征在于:所述高温无铅玻璃粉为Bi2O3-B2O3-SiO2-La2O3系高温无铅稀土封接玻璃,各类原料重量比为:
Bi2O3:60~90, B2O3:5~15,
SiO2:0.5~8, La2O3:0.1~5。
3、根据权利要求1所述的高温无铅碳浆,其特征在于:所述有机溶剂中各组重量百分比是:
松油醇:90~98%, 乙基纤维素:1~8%,
丁基卡必醇:0~15%, 蓖麻油:0.1~3%,
大豆卵磷脂:0~0.1%, 甲基纤维素:0~5%。
4、一种高温无铅碳浆的制备方法,其特征是,包括下述步骤:
①、首先制备高温无铅稀土玻璃粉:分别以化学纯Bi2O3、由分析纯分引入SiO2,由分析纯硼酸引入B2O3,由分析纯引入La2O3,按重量百分比为:
Bi2O3:60~90, B2O3:5~15,
SiO2:0.5~8, La2O3:0.1~5,
配好料,混合均匀,用刚玉坩埚在高温炉中于1100~1350℃下熔化,保温1小时,水淬,得到高温无铅稀土玻璃微渣,玻璃放用行星球磨机中磨到粒度不大于1цm的玻璃粉;
②、再制备有机溶剂,按重量百分比为:
松油醇:90~98%, 乙基纤维素:1~8%,
丁基卡必醇:0~15%, 蓖麻油:0.1~3%,
大豆卵磷脂:0~0.1%, 甲基纤维素:0~5%,
调节各种重量百分比使粘度在100~200mPas;
③、浆料的调试:按固相成份与有机溶剂的重量百分比为30~60∶70~40,所述固相成分中高温无铅稀土玻璃与石墨碳粉的重量百分比为30~70∶70~30进行重量百分比调试,得到电阻浆料。