CN101397711A - Dual-color polar fleece and method for producing the same - Google Patents
Dual-color polar fleece and method for producing the same Download PDFInfo
- Publication number
- CN101397711A CN101397711A CNA2007100467377A CN200710046737A CN101397711A CN 101397711 A CN101397711 A CN 101397711A CN A2007100467377 A CNA2007100467377 A CN A2007100467377A CN 200710046737 A CN200710046737 A CN 200710046737A CN 101397711 A CN101397711 A CN 101397711A
- Authority
- CN
- China
- Prior art keywords
- color
- polar fleece
- dual
- terry
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a bi-color polar fleece which is formed by the means of one-time weaving by a double-face terry machine. One production method thereof is as follows: common polyester and modified cationic polyester are taken as raw materials, weaved into a double-face solid terry cloth; yarns of the terry at the right side and the terry at the wrong side of the cloth adopt different types of polyesters, then are dyed and produced into the bi-color polar fleece by post treatment. The second production method thereof is as follows: the material of common polyester yarns is dyed into two different colors; then the yarns of different colors are respectively adopted as the yarns of the terry at the right side and the terry at the wrong side, weaved into a double-face terry cloth with different colors at the two sides and produced into the bi-color polar fleece by post treatment. The bi-color polar fleece of the invention completely overcomes a plurality of defects of the bi-color polar fleece produced by adopting a compound way. The bi-color polar fleece of the invention not only has good heat insulation performance, but also is washable and has light weight and good ventilating performance, therefore, people feel relaxed and comfortable when wearing the bi-color polar fleece.
Description
Technical field
The present invention relates to a kind of production method of textiles, particularly a kind of dual-color polar fleece and production method thereof.
Background technology
The two sides of prior art has the dual-color polar fleece of two kinds of different colours, general all is the form production of adopting the lining with two kinds of different colours to be combined with each other with adhesive, it is low in conjunction with brute force, cause peeling off of composite surface easily after the washing repeatedly, thereby make lining " hollowing " phenomenon occur, cause the lining serviceability and be worth to descend.Secondly adhesive that composite material adopted has a penetrating odor qualitatively, has caused unnecessary pollution.In addition, composite material is generally comparatively thick and heavy, heavy wearing, and its permeability is relatively poor.
Summary of the invention
Purpose of the present invention, exactly in order to overcome the deficiency that prior art exists, and the dual-color polar fleece and the production method thereof that provide a kind of disposable braiding to form.
To achieve these goals, the present invention has adopted following technical scheme: a kind of dual-color polar fleece, its two sides are cotton flannel surface and have different colors, are characterized in, adopt the disposable braiding of two-sided terry machine to form.
First kind of production method of above-mentioned dual-color polar fleece, be to be raw material with ordinary polyester and modified cation terylene, earlier with the woven two-sided terry plain color cloth that causes of two-sided terry, its front looped pile and reverse side looped pile advance yarn and adopt different types of terylene respectively, and it is ordinary polyester or modified cation terylene that wire gauze advances yarn; Dye then, use earlier disperse dyeing, the back cationic dyeing, again through softness, typing, two sides plucking, carding, cropping, shake, finalize the design, produce dual-color polar fleece.
Described ordinary polyester is selected from a kind of in DTY, HOY, FDY, UDY long filament or the short silk, and described modified cation terylene is selected from a kind of in DTY CATION long filament terylene and the short gauze line of UDY CATION.
Described CATION terylene face dyes dark relatively, and the ordinary polyester face dyes light color relatively.
The dyeing temperature of described DISPERSE DYES is controlled at 95-130 ℃, and the time was controlled at 25-40 minutes; The dyeing temperature of described cation dyes is controlled at 90-100 ℃, and the time was controlled at 30-50 minutes.
Second kind of production method of above-mentioned dual-color polar fleece, be earlier ordinary polyester yarn raw material to be dyed two kinds of different colors in batches, then with the yarn of different colours respectively as the yarn that advances that advances yarn and reverse side looped pile of front looped pile, weave out the two-sided terry cloth that the two sides has different colours, again through softness, typing, two sides plucking, carding, cropping, shake the grain, the typing, produce dual-color polar fleece.
In above-mentioned first kind of manufacture method, when the two sides looped pile is made into differing heights, that face that the type that wire gauze advances yarn and terry height are low to advance the yarn type identical.
In above-mentioned second kind of manufacture method, when the two sides looped pile is made into differing heights, that face that the color that wire gauze advances yarn and terry height are low to advance the yarn color identical.
In above-mentioned two kinds of manufacture methods, in the plucking step of described two sides, the Pressure control of napper pressure roll is at 8-10kg, and rotating speed is controlled at 800-900 rev/mins, and first twice are drawn light looped pile face, back twice pull and stretch look looped pile face.
The present invention is owing to adopted above technical scheme, its dual-color polar fleece of producing to overcome many shortcomings of the dual-color polar fleece of prior art employing complex form production fully.Not only good heat insulating, and water-fast washing, the weight warp, permeability is good, wears easily comfortable.
The specific embodiment
Embodiment 1
Raw material: the DTY75D/36F that the CATION terylene adopts Xiamen Xiang aigret to produce, ordinary polyester adopt the 75D/36F DTY of constant force chemical fibre production and the 50D/24F FDY that Yizheng Fiber Optical plant is produced.
Weaving process:
Weave machine and adopt 16G, 30 " the two-sided terry machine
| The front looped pile advances yarn | The reverse side looped pile advances yarn | Wire gauze advances yarn |
| DTY?75D/36F | 75D/36F?DTY | 50D/24F?FDY |
| Line length 42cm/50N | Line length 50cm/50N | Line length 16cm/50N |
The dyeing flow process:
1, pre-treatment (90 ℃ of temperature, 30 minutes time);
Close fine degreaser addition 2g/L;
2, ordinary polyester dyeing (108 ℃ of temperature, 30 minutes time), dye formulation is as follows:
The lucky magnificent chemical industry 0.285% in the lucky magnificent disperse yellow of Yellow LS Hangzhou;
The lucky magnificent chemical industry 0.1% in the lucky magnificent disperse red of Rubine 4B Hangzhou;
The lucky China of Blue PTD disperses the lucky magnificent chemical industry 0.168% in blue Hangzhou;
The big auspicious chemical industry of dispersant---huge legendary turtle is closed dispersant (25DX, PC680) 1.2%;
The holy inferior chemical industry in acetic acid Shanghai---0.8%;
3, reduction cleaning (85 ℃ of temperature, 30 minutes time), the cleaning fluid prescription is as follows:
Thiourea dioxide Shanghai sincerity chemical industry 0.5%;
The true ancient cooking vessel in soda ash Shanghai refers to chemical industry 1.5%;
First chemical industry 4g/L continues in sodium hydrosulfite Shanghai;
The holy inferior chemical industry 0.8% in acetic acid Shanghai;
4, CATION terylene dyeing (98 ℃ of temperature, 40 minutes time), dye formulation is as follows:
Yellow X-G2 Shanghai chemical industry cationic yellow 1.94%;
Red X-C2R2 Shanghai chemical industry cationic red 1.46%;
Blue X-B2 Shanghai chemical industry CATION orchid 0.47%;
The holy inferior chemical industry 2% in acetic acid Shanghai;
Dispersant IW Hangzhou etherealize worker 1% of a specified duration;
5, soap (50 ℃ of temperature, 15 minutes time)
Adopt Yantai to moisten the efficient soaping agent RLS of blue or green Chemical Manufacture, addition 1g/L.
6, soft (30 ℃ of temperature, 20 minutes time)
The LFT hydrophilic softener that adopts the beautiful peaking worker in Shanghai to produce, addition 4g/L.
Brushing process:
Pressure roll pressure 8kg, 820 rev/mins of rotating speeds, first twice are drawn light face, back twice pull and stretch look face.
Other technologies with prior art are identical.
Embodiment 2
Raw material: the DTY 75D/36F that the CATION terylene adopts Xiamen Xiang aigret to produce, ordinary polyester adopt the 150D/72F HOY of Yizheng Fiber Optical plant production and the 75D/36F FDY that the constant force chemical fibre is produced.
Weaving process:
Weave machine and adopt 16G, 30 " the two-sided terry machine
| The front looped pile advances yarn | The reverse side looped pile advances yarn | Wire gauze advances yarn |
| DTY75D/36F | 150D/72F?HOY | 75D/36F?FDY |
| Line length 45cm/50N | Line length 56cm/50N | Line length 15cm/50N |
The dyeing flow process:
1, pre-treatment (90 ℃ of temperature, 30 minutes time)
Close fine degreaser addition 2g/L.
2, ordinary polyester dyeing (128 ℃ of temperature, 35 minutes time), dye formulation is as follows:
The lucky magnificent chemical industry 3.51% in the lucky magnificent disperse red of RED X GRL Hangzhou;
The lucky China of BLUE X GB disperses the lucky magnificent chemical industry 1.56% in emerald green blue Hangzhou;
The lucky magnificent chemical industry 0.14% in the lucky magnificent disperse yellow of YELLOW X8GL Hangzhou;
The big auspicious chemical industry of dispersant---huge legendary turtle is closed dispersant 25DX, and PC680) 1.2%;
The holy inferior chemical industry in acetic acid Shanghai---0.8%.
3, reduction cleaning (85 ℃ of temperature, 30 minutes time), the cleaning fluid prescription is as follows:
Thiourea dioxide Shanghai sincerity chemical industry 1%;
The true ancient cooking vessel in soda ash Shanghai refers to chemical industry 1%;
First chemical industry 4g/L continues in sodium hydrosulfite Shanghai;
The holy inferior chemical industry 0.8% in acetic acid Shanghai;
4, CATION terylene dyeing (93 ℃ of temperature, 50 minutes time), dye formulation is as follows:
RED HRD GFL Shanghai chemical industry cationic red 3.49%;
NAVY BLUE HRD 2RE Shanghai chemical industry CATION navy blue 2.18%;
The holy inferior chemical industry 2% in acetic acid Shanghai;
Dispersant IW Hangzhou etherealize worker 1.5% of a specified duration.
5, soap (50 ℃ of temperature, 15 minutes time)
Adopt Yantai to moisten the efficient soaping agent RLS of blue or green Chemical Manufacture, addition 1g/L.
6, soft (30 ℃ of temperature, 20 minutes time)
The LFT hydrophilic softener that adopts the beautiful peaking worker in Shanghai to produce, addition 4g/L.
Brushing process:
Pressure roll pressure 9kg, 880 rev/mins of rotating speeds, first twice are drawn light face, back twice pull and stretch look face.
Other technologies with prior art are identical.
Embodiment 3
Raw material: be ordinary polyester, adopt 150D/144F DTY, the 150D/96FDTY of Xiamen Xiang aigret production and the 75D/36F FDY that the constant force chemical fibre is produced.
Yarn dyeing, by the week limited thread dyeing of ShaoXing,ZheJiang state, 150D/144F DTY dyes dark relatively; 150D/96F DTY dyes relative light color with 75D/36F FDY;
Weaving process:
Weave machine and adopt 16G, 30 " the two-sided terry machine
| The front looped pile advances yarn | The reverse side looped pile advances yarn | Wire gauze advances yarn |
| 150D/144F?DTYF | 150D/96F?DTY | 75D/36F?FDY |
| Line length 44cm/50N | Line length 55cm/50N | Line length 16cm/50N |
Brushing process:
Pressure roll pressure 10kg, 890 rev/mins of rotating speeds, first twice are drawn light face, back twice pull and stretch look face.
Other technologies with prior art are identical.
Claims (8)
1, a kind of dual-color polar fleece, its two sides are cotton flannel surface and have different colors, it is characterized in that: adopt the disposable braiding of two-sided terry machine to form.
2, the production method of dual-color polar fleece according to claim 1, it is characterized in that: with ordinary polyester and modified cation terylene is raw material, earlier with the woven two-sided terry plain color cloth that causes of two-sided terry, its front looped pile and reverse side looped pile advance yarn and adopt different types of terylene respectively, and it is ordinary polyester or modified cation terylene that wire gauze advances yarn; Dye then, use earlier disperse dyeing, the back cationic dyeing, again through softness, typing, two sides plucking, carding, cropping, shake, finalize the design, produce dual-color polar fleece.
3, dual-color polar fleece according to claim 2, it is characterized in that: described ordinary polyester is selected from a kind of in DTY, HOY, FDY, UDY long filament or the short silk, and described modified cation terylene is selected from a kind of in DTY CATION long filament terylene and the short gauze line of UDY CATION.
4, dual-color polar fleece according to claim 2 is characterized in that: described CATION terylene face dyes dark relatively, and the ordinary polyester face dyes light color relatively.
5, the production method of dual-color polar fleece according to claim 2 is characterized in that: the dyeing temperature of described DISPERSE DYES is controlled at 95-130 ℃, and the time was controlled at 25-40 minutes; The dyeing temperature of described cation dyes is controlled at 90-100 ℃, and the time was controlled at 30-50 minutes.
6, the production method of dual-color polar fleece according to claim 1, it is characterized in that: earlier ordinary polyester yarn raw material is dyed two kinds of different colors in batches, then with the yarn of different colours respectively as the yarn that advances that advances yarn and reverse side looped pile of front looped pile, weave out the two-sided terry cloth that the two sides has different colours, again through softness, typing, two sides plucking, carding, cropping, shake the grain, the typing, produce dual-color polar fleece.
7, according to the production method of claim 2 or 6 described dual-color polar fleeces, it is characterized in that: when the two sides looped pile is made into differing heights, wire gauze advance that low face of the type of yarn or color and terry height advance the yarn type or color identical.
8, according to the production method of claim 2 or 6 described dual-color polar fleeces, it is characterized in that: in the plucking step of described two sides, the Pressure control of napper pressure roll is at 8-10kg, and rotating speed is controlled at 800-900 rev/mins, elder generation's twice are drawn light looped pile face, back twice pull and stretch look looped pile face.