CN101334623A - Cleaning member - Google Patents
Cleaning member Download PDFInfo
- Publication number
- CN101334623A CN101334623A CNA2008101092630A CN200810109263A CN101334623A CN 101334623 A CN101334623 A CN 101334623A CN A2008101092630 A CNA2008101092630 A CN A2008101092630A CN 200810109263 A CN200810109263 A CN 200810109263A CN 101334623 A CN101334623 A CN 101334623A
- Authority
- CN
- China
- Prior art keywords
- double
- clearer
- sided belt
- cleaning member
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The object of the present invention is to provide a cleaning member which can be produced at low cost and maintains excellent cleaning performance for a long period of time. The cleaning member has a lower layer 12 formed through winding a double-faced tape formed of a sponge member having an adhesive layer on each side thereof around the surface of a core member 11, and an upper layer 13 provided on the outer surface of the lower layer 12. The upper layer13 comprises knitted fabric knitted by yarn 13A which is entwisted by fabric 13a.
Description
Technical field
The present invention relates to be used to remove the cleaning member of toner, external additive, paper powder etc., especially relate to the cleaning member that is suitable as the clearer that is used for removing the toner that adheres on the charged roller of uses such as duplicating machine, printer, facsimile recorder.
Background technology
At image processing system for example duplicating machine, printer or have concurrently in their the compound OA machine etc. of function, use cleaning balde, clearer.Clearer and photoreceptor, charged roller butt (when connecing) and remove toner, external additive, paper powder, other foreign matter of attachment removal, but when clearer can not fully be removed foreign matters such as toner, may damage photoreceptor, charged roller etc., even it is bad also to produce printed images.So, all the time, seek the clearer of keeping clean property for a long time.
So, proposed to have the cleaning member that comprises sponge member Charging system (with reference to patent documentation 1), comprise fibrolaminar color powder feeding roller (with reference to patent documentation 2) that cylindric elastic body and the complexing of thermal welding fiber form etc.
But, in patent documentation 1, with foaming body be shaped the back punching pass core body, in patent documentation 2, behind the lining hot melt property fiber on the roller of once-forming,, exist manufacturing process many, expensive problem again with mold heated etc.In addition, also exist foreign matter to be difficult to problems such as long-term use because of being difficult to keep removing.
Patent documentation 1: No. 2847524 communique of Japan's special permission
Patent documentation 2: TOHKEMY 2006-064774 communique
Summary of the invention
The present invention In view of the foregoing, purpose is to provide cost low, and keeps the cleaning member of good spatter property for a long time.
Solve the cleaning member of the present invention's the 1st mode of foregoing problems, it is characterized in that, these parts are included in core surface coiling double-sided belt (both faces テ one プ) lower floor that forms and the upper strata that is arranged at above-mentioned lower floor outside surface, above-mentioned upper strata comprises at least one layer of fibrage, and described fibrage comprises woven fabric (Woven thing) or knitted fabric (Knitting thing); Wherein said double-sided belt is the double-sided belt that has tack coat on the two sides of sponge member (ス Port Application ジ portion material).
The cleaning member of the present invention's the 2nd mode is characterised in that in the described cleaning member of the 1st mode, the thickness of described double-sided belt is 0.4～3.0mm.
The 3rd mode of the present invention is characterised in that in the described cleaning member of the 1st or the 2nd mode, described sponge member comprises polyolefin or acrylic rubber.
The present invention's the 4th mode is characterised in that, in the described cleaning member of the 1st～3 arbitrary mode, described upper strata is a plurality of stacked formation of fibrage of the same race or not of the same race.
The present invention's the 5th mode is characterised in that in the described cleaning member of the 1st～4 arbitrary mode, described cleaning member is the roller shape.
According to the present invention, can provide cost low, and keep the cleaning member of good spatter property for a long time.
Description of drawings
Fig. 1 is the figure of expression as the clearer of an example of cleaning member of the present invention.
Fig. 2 is the figure of manufacture method of the clearer of presentation graphs 1.
Fig. 3 is the enlarged diagram of a part on the surface (upper strata) of clearer.
Symbol description
10 clearers
11 core bodys
12 lower floors
13 upper stratas
Embodiment
Cleaning member of the present invention is included in the lower floor of core surface coiling double-sided belt formation and is arranged at the upper strata of lower floor's outside surface, and wherein said double-sided belt is the double-sided belt that possesses tack coat on the two sides of sponge member.Like this, by having the lower floor that the double-sided belt that possesses tack coat on the two sides that core surface is wound on the sponge parts forms and the upper strata of regulation, can remove toner, external additive, paper powder, other foreign matter of the parts of butt for a long time suitably.
Following illustration describes the present invention in detail as the clearer of an example of cleaning member of the present invention.
Figure 1 shows that the clearer of an example of cleaning member of the present invention.Fig. 1 (a) is that sectional view, Fig. 1 (b) of cleaning member is the synoptic diagram that the part on the surface (fibrage) of cleaning member is amplified.
Manufacture method by the clearer 10 of Fig. 2 simple declaration Fig. 1.At first, shown in Fig. 2 (a), be wound into spiral fashion by the double-sided belt that will possess tack coat on core body 11 surfaces and form lower floor 12 on the two sides of sponge member.Then, shown in Fig. 2 (b),, upper strata 13 is set in lower floor 12, thereby makes clearer 10 by knitted fabric being covered and being bonded in the lower floor 12.Like this, the clearer 10 of present embodiment is considerably less because of manufacturing process, therefore can make with low cost.
Certainly, also the knitted fabric as upper strata 13 can be bonded on the one side of double-sided belt after, it be wound on the core body 11 and form the clearer 10 that comprises lower floor 12 and upper strata 13.
At this, as mentioned above, the two sides that lower floor 12 is included in sponge member possesses the double-sided belt of tack coat, has replaced the elastic layer of existing cleaning member.Such double-sided belt is bonded on the core body 11 easily, and upper strata 13 easily also bonds.In addition, owing to comprise tack coat and sponge member, therefore be wound on the surface of core body 11 easily.
The thickness that forms the double-sided belt of lower floor 12 is preferably 0.4～3.0mm.The double-sided belt of such thickness range has the elastic force of sponge member requirement etc., therefore can give full play to the sanitary characteristics on clearer surface.When used thickness during, can obtain cleaning effect, but during as clearer,, therefore be not suitable for the miniaturization of compound OA equipment because of the diameter chap of roller greater than the double-sided belt of 3.0mm.Certainly, also can double-sided belt two-layer or more multi-layered thin thickness than above-mentioned double-sided belt is stacked, reach above-mentioned thickness.
The preferred Asker C of sponge member hardness is below 80 ° and compression set at room temperature is below 30%.This is the lower floor 12 that can guarantee that in order to form decrement (ニ Star プ amount) and distortion recover easily, promptly have recuperability.
In addition, sponge member preferably comprises polyolefin or acrylic rubber.This is the elasticity of necessity in order to obtain to clean.
In addition, the width of double-sided belt is not had special restriction, but be preferably about 5～20mm.This is in order to be wound on the core body easily.
In the present embodiment, shown in Fig. 1 (b), upper strata 13 comprises the knitted fabric that yarn (yarn) 13A that fiber 13a twisting is obtained weaves into.Diameter at this said fiber 13a is 5 μ m～100 μ m, and length is wealthy to be more than 100 than (L/D ratio).Adopt the yarn 13A that fiber 13a is twisted with the fingers in the present embodiment.
Diameter at this said yarn 13A is very little.For example diameter (apparent fineness degree) is preferably 80～500 μ m.This is because for example be 5～10 μ m attached to the particle diameter of the toner of object parts, is fit to scrape get such toner.In addition, the space 14 that also forms because of braiding this yarn 13A is for being fit to scrape foreign matters such as getting toner and with its size that wraps into.Further also because can obtain cleaning required abundant intensity.The apparent fineness degree of yarn during less than 80 μ m physical strength may reduce, the apparent fineness degree of yarn may damage the flexibility on upper strata 13, thereby reduce spatter property during greater than 500 μ m, and is therefore not preferred.
Preferred row width of above-mentioned knitted fabric (μ m) and wale width (μ m) are 3～10 times with respect to the apparent fineness degree (μ m) of yarn 13A, preferred especially 3～7 times.In addition, not with danier, the represented constant length number method fineness degree of dtex at the apparent fineness degree of this said yarn, but with observed fineness degrees such as microscopes.
Shown in Fig. 3 (a), row is meant the horizontal row of arranging of coil 13A ' (line), and wale is the vertical row of arranging of coil 13A ' (file).And the row width is the width of line, the distance between coil 13A ' summit specifically, and the wale width is meant the width of file, is the width of the pitch (ピ Star チ) of coil 13A ' at this.Row width and wale width are 3 times～10 times knitted fabric with respect to the apparent fineness degree of yarn, and yarn 13A is not the state that is completely fixed, but the state that can move up and down.It is yarn 13A has tracing ability to variation state.Therefore and butt parts when rubbing, scrape toner, paper powder, other foreign matter of getting the butt parts easily.In addition, row width and wale width are 3 times～10 times knitted fabric with respect to the apparent fineness degree of yarn, form bigger space 14A, not only can wrap into space 14A with scraping the foreign matter of getting, and make foreign matter fall into the inside on upper strata 13 easily, thereby can keep foreign matter in large quantities from space 14A.Therefore, clearer 10 keeping clean property for a long time.In addition, row width and wale width be with respect to the apparent fineness degree of the yarn knitted fabric less than 3 times, and yarn 13A is not only for changing no tracing ability, and be difficult to keep scraping the foreign matter of getting.In addition, row width and wale width are with respect to the apparent fineness degree of the yarn knitted fabric greater than 10 times, and yarn improves for the tracing ability that changes, but reduce with the contact area of butt parts, and spatter property may descend.
Weave to knitted fabric is not particularly limited, and can enumerate for example flat pin (flat Knitting), ribbed knitting, tuck knitting, flotation line braiding, half-cardigan rib (sheet furrow Knitting), double rib braiding (both faces Knitting), petinet ocular tissue (レ one ス Knitting), pile braiding (adding a mao Knitting) etc.
The clearer of present embodiment moves along the sense of rotation of roller by yarn 13A and to scrape toner of getting the butt parts etc., cleans.Specifically, at least a portion fiber 13a that constitutes yarn 13A tangles toner etc., when other fiber 13a supports them, sense of rotation along clearer 10 moves, thus, the quilts such as toner of object parts are scraped and are got, and are scraped toner of getting etc. and fall into space 14 between the yarn 13A.Like this, the knitted fabric that will be weaved into by the yarn 13A that fiber 13a twists with the fingers can be removed toner, external additive, paper powder, other foreign matter etc. reliably.
In the present embodiment, adopt knitted fabric as upper strata 13, but also can use woven fabric,, three foundation weave, re-organized such as plain weave, twill-weave and satin weave are arranged as woven fabric.
Above-mentioned woven fabric, preferred warp thread (Longitudinal yarn) interval (μ m) between is that interval (μ m) between 3～10 times and the weft yarn (horizontal yarn) is 3～10 times with respect to the apparent fineness degree (μ m) of weft yarn with respect to the apparent fineness degree (μ m) of warp thread, is preferably 3～7 times especially.Shown in Fig. 3 (b), the interval between interval between the warp thread 13B or the weft yarn 13C is respectively the distance between centers of the thickness of yarn degree direction of adjacency.Interval between the warp thread 13B (μ m) is that interval (μ m) between 3 times～10 times and the weft yarn 13C is 3 times～10 times woven fabric with respect to the apparent fineness degree (μ m) of weft yarn 13C with respect to the apparent fineness degree (μ m) of warp thread 13B, warp thread 13B and weft yarn 13C are not the states that is completely fixed, but the state that can move up and down can form bigger space 14B in addition.Thus, can obtain the effect same with above-mentioned embodiment.In addition, interval between the warp thread 13B (μ m) is with respect to 3 times of apparent fineness degree (μ m) less thaies of warp thread 13B or the interval (μ m) between the weft yarn 13C woven fabric with respect to 3 times of apparent fineness degree (μ m) less thaies of weft yarn 13C, warp thread 13B or weft yarn 13C not only do not have tracing ability to variation, and are difficult to keep scraping the foreign matter of getting.In addition, interval between the warp thread 13B (μ m) with respect to the apparent fineness degree (μ m) of warp thread 13B greater than the interval (μ m) between 10 times or the weft yarn 13C with respect to the apparent fineness degree (μ m) of weft yarn 13C greater than 10 times woven fabrics, though warp thread 13B or weft yarn 13C improve the tracing ability that changes, but reduce with the contact area of butt parts, spatter property may descend.
In addition, the warp thread of woven fabric and the apparent fineness degree of weft yarn are not particularly limited.In addition, the material of the warp thread of woven fabric and weft yarn, apparent fineness degree are different also passable.
The yarn (knitted fabric), warp thread and the weft yarn (woven fabric) that constitute upper strata 13 obtain the collection of filaments, certainly, also fiber twisting can be obtained, fibrage can also be obtained, and also can be to contain the collection of filaments of decorating silk (Ornaments り yarn) (fiber) in the scope of not damaging spatter property to obtain.In addition, the preferred fineness degree of fiber of formation yarn (knitted fabric), warp thread and weft yarn (woven fabric) is 5～100 μ m.During the fineness degree less than 5 μ m of fiber, the yarn that is difficult to obtain to have full intensity.When the fineness degree of fiber surpasses 100 μ m, be difficult to obtain the flexibility on upper strata 13, spatter property may reduce.
Knitted fabric or woven fabric are except that the yarn that satisfies above-mentioned condition respectively or warp thread and weft yarn, in the scope of not damaging spatter property, also can there be other yarn, for example can exist than yarn or warp thread and the thinner yarn of weft yarn, also can have the yarn of fluffing (fluffing) state.
Material to yarn (knitted fabric), warp thread and weft yarn (woven fabric) does not all have special restriction, for example can enumerate: cotton, fiber crops, wool, silk, polyester, nylon, acrylic compounds (ア Network リ Le) etc., consider preferred polyester, nylon, acrylic compounds from permanance and cost aspect.
In addition, the apparent thickness on upper strata 13 is preferably more than the 0.5mm.This is because mechanical properties such as physical strength, wearing quality are good like this.
In addition, as long as upper strata 13 can remove foreign matters such as toner reliably, also can carry out a plurality of woven fabrics, knitted fabric stacked and form.When a plurality of woven fabrics, knitted fabric are carried out stacked formation upper strata 13, can be that for example woven fabric and knitted fabric carry out stacked and form with mutual different fabric, certainly, also can be that identical fabric (woven fabric and woven fabric, knitted fabric and knitted fabric) is laminated.In addition, identical woven fabric is being carried out under the stacked situation, the woven fabric that comprises different fibers can carried out stackedly, certainly, also can carry out the woven fabric that comprises identical fibre stacked.
In addition, upper strata 13 is not limited only to the above, also can be the woven fabric that comprises pile weave construction (パ イ ル Group Woven).Pile weave construction is meant the woven fabric that with warp thread or weft yarn pile (uncut pile ((Wheels how)) and clipping (cutting hair)) is inweaved woven face with pile in addition and obtain except that filling.
The thickness on the upper strata that is formed by pile weave construction is preferably 0.5～3.0mm.During thickness is not enough 0.5mm, can not get enough decrements, thickness can obtain cleaning effect during greater than 3.0mm, but when making clearer, therefore the diameter chap of roller is unsuitable for the miniaturization of compound OA machine.
The filamentary fineness degree of pile weave construction is preferably 5～500 dtexs.Because in cleaning, can obtain full intensity like this.During ultimate fibre less than 5 dtexs, physical strength may reduce, and ultimate fibre can be detrimental to the flexibility on upper strata 13 during greater than 500 dtexs, thereby damage butt parts are therefore not preferred.
In addition, the density of the yarn of pile weave construction is preferably 6400～46000/cm
2The density of yarn reaches this scope, and then foreign matter can be remained on upper strata 13 fully.
Filamentary material to pile weave construction is not particularly limited, and can enumerate polyamide, polyester, acrylic compounds, polyolefin etc.
As mentioned above, by using the clearer 10 of present embodiment, the foreign matters such as toner of butt parts can be scraped and are taken on the upper strata 13.And, also be maintained on the tack coat of lower floor 12 attached to toner on the upper strata 13 etc.Therefore, the clearer 10 of present embodiment can be for a long time cleans well to the foreign matters such as toner of butt parts.
In addition, when the clearer 10 long-term use spatter properties of present embodiment descend, lower floor 12 easily can be peeled off from core body 11, therefore core body 11 can be utilized again.Clearer after reclaim using also utilizes core body 11 again, can make the cost of clearer 10 lower.
Cleaning member of the present invention is suitable as clearer.Especially be suitable as the clearer of removing attached to the toner on employed charged roller, the photoreceptors such as duplicating machine, printer, facsimile recorder.
Below, specific embodiment is described, the invention is not restricted to this certainly.
Embodiment 1
Possessing Asker C hardness is that compression set under 69 °, room temperature is that the thickness of 13% acrylic compounds foaming body is double-sided belt (the HHT higher high tensile double-sided belt of 1.3mm, 3M society system) one side bonds, and (the apparent fineness degree of yarn is 80 μ m to the banded knitted fabric that comprises rayon, interval between the warp thread is about 500 μ m, interval between the weft yarn is about 600 μ m, apparent thickness 500 μ m), it is wound into spiral fashion on the mandrel of φ 6mm, be cut into prescribed level, form the clearer of embodiment 1 thus.
Embodiment 2
Remove and to use that to have Asker C hardness be that 58 °, compression set at room temperature are double-sided belt (the HHT higher high tensile double-sided belt of the thickness of 3% polyethylene-based foaming body as 1.1mm, NITTO society system) replaces double-sided belt (super-strength double-sided belt: 3M society system) in addition, operate similarly to Example 1, obtain the clearer of embodiment 2.
Embodiment 3
Remove and to use that to possess Asker C hardness be that 63 °, compression set at room temperature are double-sided belt (the HHT higher high tensile double-sided belt of the thickness of 16% acrylic acid series foaming body as 0.8mm, 3M society system) replaces double-sided belt (HHT higher high tensile double-sided belt, 3M society system) in addition, operate similarly to Example 1, obtain the clearer of embodiment 3.
Embodiment 4
Remove and to use that to possess Asker C hardness be that 72 ° and compression set at room temperature are double-sided belt (HHT higher high tensile double-sided belt: temple ridge make institute society system) replacement double-sided belt (the HHT higher high tensile double-sided belt of the thickness of 10% acrylic compounds foaming body as 0.4mm, 3M society system) in addition, operate similarly to Example 1, obtain the clearer of embodiment 4.
Embodiment 5
To possess Asker C hardness be that 53 °, at room temperature compression set are double-sided belt (the HHT higher high tensile double-sided belt: LINTEC society system) replace double-sided belt (HHT higher high tensile double-sided belt: 3M society system) of the thickness of 4% polyolefin foaming body as 1.0mm except that using, operate similarly to Example 1, obtain the clearer of embodiment 5.
Embodiment 6
To possess Asker C hardness be that compression set under 69 °, room temperature is double-sided belt (the HHT higher high tensile double-sided belt: ス リ オ Application テ Star Network society system) replace double-sided belt (HHT higher high tensile double-sided belt: 3M society system) of the thickness of 13% acrylic compounds foaming body as 0.9mm except that using, operate similarly to Example 1, obtain the clearer of embodiment 6.
Embodiment 7
The thickness that will possess A sker C hardness and be 69 °, compression set at room temperature and be 13% acrylic compounds foaming body is that (the HHT higher high tensile double-sided belt: 3M society system) helically is wound on the mandrel of φ 6mm and forms lower floor the double-sided belt of 1.3mm.Then, (comprise fineness degree is the ultimate fibre that comprises nylon of 110 dtexs to the woven fabric that is covered in lower floor, 33000/cm
2, thickness is the pile weave construction of 1.9mm), be cut into prescribed level, form the clearer of embodiment 7 thus.
Embodiment 8
Use the ultimate fibre that comprises nylon comprise fineness degree 110 dtexs, 27000/cm as woven fabric
2, thickness 18mm pile weave construction, in addition, operation similarly to Example 7 obtains the clearer of embodiment 8.
Embodiment 9
Use the ultimate fibre that contains acetate comprise fineness degree 130 dtexs, 19800/cm as woven fabric
2, thickness 1.9mm pile weave construction, obtain the clearer of embodiment 9 in addition similarly to Example 7.
Use as woven fabric and to comprise the ultimate fibre that comprises ester that fineness degree is 84/2 dtex (ultimate fibre of 84 dtexs is divided into two parts), 34000/cm
2, thickness is the pile weave construction of 1.9mm, in addition, obtains the clearer of embodiment 10 similarly to Example 7.
Comparative example 1
Melmac foaming body (BASF society system) is cut into horn shape (horn shape), opens the hole of inserting core body.Insert the core body that has been coated with cementing agent therein, after the thermal welding surface is ground, form the roller shape, cut into prescribed level, obtain the clearer of comparative example 1.
Comparative example 2
Utilize shaping dies shaped resilient layer, the surface is ground, thus, comprise the elastic layer of polyurethane in the core surface moulding.(サ イ PVC ノ one Le HM-680: サ イ デ Application KCC system), lining banded knitted fabric similarly to Example 1 thereon is cut into the size of regulation, obtains the clearer of comparative example 2 thus at the surface coated cementing agent of this elastic layer.
The manufacturing process of the clearer of each embodiment and the clearer of each comparative example is as shown in table 1.
Table 1
| Operation | Embodiment 1～6 | Embodiment 7～10 | Comparative example 1 | Comparative example 2 |
| 1 | Banded knitted fabric is bonded on the double-sided belt | Double-sided belt is wound on the core body | The foaming body moulding | The elastic layer moulding |
| 2 | Double-sided belt is wound on the core body | Woven fabric is bonded on the double-sided belt | Cutting | The elastic layer surface grinding |
| 3 | Cut off | Cut off | Punching | At elastic layer surface coated adhesive |
| 4 | -- | -- | On core body, be coated with cementing agent | Banded knitted fabric is covered |
| 5 | -- | -- | Surface grinding | Cut off |
| 6 | -- | -- | Cut off | -- |
The clearer of each embodiment is compared with the clearer of comparative example 2 with comparative example 1, and manufacturing process is few.Clearer of the present invention as can be known is manufacturing process's clearer few, that just can make with low cost.
Test example 1
The clearer that makes each embodiment and each comparative example is with overmask amount (Shi い Write body amount) be the mode of 0.1mm and the charged roller butt of photoreceptor butt.Then, be coated with about 0.03g toner equably, photoreceptor rotated with 300rpm by CD-ROM drive motor in the scope of the wide 100mm of charged roller.This moment, charged roller and clearer connected commentaries on classics.
The CD-ROM drive motor running was observed the clean conditions on charged roller surface after 15 minutes, and the surface of charged roller is measured when cleaning goodly, carries out same operation again, shut-down operation when charged roller no longer purifies.Its result is as shown in table 2.
(kind of toner)
Numeral toner (デ ジ Le ト Na one, コ ミ カ ミ ノ Le society system)
Polystyrene resin: 6 μ m
Siloxane-based external additive
+ 0.6 μ m titanium dioxide
Table 2
| Cleaning time (inferior) | |
| Embodiment 1 | 7 |
| Embodiment 2 | 7 |
| Embodiment 3 | 8 |
| Embodiment 4 | 6 |
| Embodiment 5 | 9 |
| Embodiment 6 | 7 |
| Embodiment 7 | More than 20 |
| Embodiment 8 | More than 20 |
| Embodiment 9 | More than 20 |
| |
More than 20 |
| Comparative example 1 | 8 |
| Comparative example 2 | 9 |
(result's conclusion)
As shown in Table 2, the clearer of embodiment 1～6 is the clearer that can clean well charged roller etc. for a long time as the clearer of comparative example 1, comparative example 2.In addition, the clearer of embodiment 7～10 all is the clearer that clearer than comparative example 1 and comparative example 2 more can keep good spatter property for a long time.
This shows, cleaning member of the present invention be manufacturing process few, with the cleaning member that low cost just can be made, can keep good spatter property for a long time.
Claims (5)
1, cleaning member is characterized in that, these parts are included in the lower floor of core surface coiling double-sided belt formation and are arranged at the upper strata of above-mentioned lower floor outside surface, and above-mentioned upper strata comprises at least one layer of fibrage, and described fibrage comprises woven fabric or knitted fabric; Wherein said double-sided belt is the double-sided belt that has tack coat on the two sides of sponge member.
2, cleaning member as claimed in claim 1, the thickness of wherein said double-sided belt are 0.4～3.0mm.
3, cleaning member as claimed in claim 1 or 2, wherein said sponge member comprises polyolefin or acrylic rubber.
4, cleaning member as claimed in claim 1, wherein above-mentioned upper strata are a plurality of stacked formation of fibrage of the same race or not of the same race.
5, cleaning member as claimed in claim 1, wherein, above-mentioned cleaning member is the roller shape.