CN101210132A - 高硬度烤漆组合物 - Google Patents

高硬度烤漆组合物 Download PDF

Info

Publication number
CN101210132A
CN101210132A CNA2006101324501A CN200610132450A CN101210132A CN 101210132 A CN101210132 A CN 101210132A CN A2006101324501 A CNA2006101324501 A CN A2006101324501A CN 200610132450 A CN200610132450 A CN 200610132450A CN 101210132 A CN101210132 A CN 101210132A
Authority
CN
China
Prior art keywords
varnish composition
baking varnish
resin
high hardness
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006101324501A
Other languages
English (en)
Inventor
彭亚培
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CNA2006101324501A priority Critical patent/CN101210132A/zh
Publication of CN101210132A publication Critical patent/CN101210132A/zh
Pending legal-status Critical Current

Abstract

本发明揭示了一种高硬度烤漆组合物，其主要成分以重量分数表示为热固性丙烯酸树脂53.1～61，高亚氨基树脂25－33，环氧树脂2～3.1，特殊改性官能基酯合物1～2，溶剂9～13，聚醚改性溶液0～0.5，非离子改性聚酯聚合物0.5－1。其中，所述的热固性丙烯酸树脂、高亚氨基树脂以及环氧树脂为主体成膜物质，所述的溶剂为乙二醇丁醚、正丁醇、二甲苯。本发明所述之油漆烘烤温度低，能源消耗少，且耐腐蚀、耐冲击性能优异，并且附着力强。

Description

高硬度烤漆组合物
技术领域
本发明涉及到一种溶剂型烤漆组合物，特别是涉及到一种高硬度溶剂型烤漆组合物。
背景技术
金属的腐蚀，是金属受环境介质的化学或电化学作用而被破坏的现象。金属设备防腐蚀最有效、最常用的方法之一是在金属表面涂敷防腐蚀涂层，以隔绝腐蚀介质与金属基体，但是一般普通金属烤漆硬度为三菱铅笔2H-3H，已经开始不适应一些对硬度有较高要求的金属烤漆需求，因此迫切需要研制一种高硬度金属烤漆。
发明内容
为解决上述问题，本发明提供了一种对金属外观保护性强的高硬度金属烤漆组合物。
本发明的技术方案为：一种高硬度溶剂型烤漆组合物，其主要成分以重量分数表示为：
热固性丙烯酸树脂            53.1～61；
高亚氨基树脂                25-33；
环氧树脂                    2-3.1；
溶剂                        9-13；
流平剂                      0～0.5；
附着力促进剂                0.5～1；
特殊改性官能基酯合物        1～2。
其中，所述的热固性丙烯酸树脂、高亚氨基树脂以及环氧树脂为主体成膜物质，所述的溶剂为乙二醇丁醚、正丁醇、二甲苯，所述的流平剂为聚醚改性溶液，以促进漆膜流平，所述的附着力促进剂为非离子改性聚酯聚合物，以增强附着力。
上述烤漆组合物涂装于金属表面，其耐腐蚀性强，环保无毒害，涂装金属后所生成的油漆膜层能通过盐雾实验240小时，且该油漆膜层硬度达到三菱铅笔6H，附着力强。
本发明提供的用于涂装金属表面的烤漆其性能优越，友好环境，具有较好的社会和经济效益。
具体实施方式
实施例1
按照上述技术方案中的配方，各组分重量份数分别为：
热固性丙烯酸树脂            61；
高亚氨基树脂                33；
环氧树脂                    3.1；
乙二醇丁醚                  3；
正丁醇                      4；
二甲苯                      6；
聚醚改性溶液                0.5；
非离子改性聚酯聚合物        1；
特殊改性官能基酯合物        2。
将上述称取好的原料按常规方法混合均匀后制成油漆，然后将该油漆涂装于一镁合金样品表面，使用方法与其它油漆相同，接着按照烤漆流程，在160℃的温度下烘烤20分钟，然后检验该生成的油漆膜层，经检验，该油漆适合铁基、铝基及合金、锌基及合金、不锈钢、电镀基材等，附着力强，耐溶剂、耐化学品及耐冲击性能优异，且耐盐雾可达240小时以上，性能优异，具有良好的社会及经济效益。
实施例2
按照上述技术方案中的配方，各组分重量份数分别为：
热固性丙烯酸树脂                60；
高亚氨基树脂                    32；
环氧树脂                        3.1；
乙二醇丁醚                      3；
正丁醇                          3；
二甲苯                          5.6；
聚醚改性溶液                    0.4；
非离子改性聚酯聚合物            0.9；
特殊改性官能基酯合物            1.6。
其中，上述两实施例中的特殊改性官能基酯合物为助剂。
本发明烤漆组合物，在160℃的温度下烘烤干燥，且该烤漆膜层硬度达到三菱铅笔6H，附着力强，可满足高硬度烤漆需求。

Claims (5)

1.一种高硬度烤漆组合物，其特征在于：主要成分以重量分数表示为，
热固性丙烯酸树脂              53.1～61；
高亚氨基树脂                  25-33；
环氧树脂                      2-3.1；
溶剂                          9-13；
流平剂                        0～0.5；
附着力促进剂                  0.5～1；
特殊改性官能基酯合物          1～2。
2.根据权利要求1所述的一种高硬度烤漆组合物，其特征在于：所述的溶剂为乙二醇丁醚、正丁醇、二甲苯。
3.根据权利要求1所述的一种高硬度烤漆组合物，其特征在于：所述的流平剂为聚醚改性溶液。
4.根据权利要求1所述的一种高硬度烤漆组合物，其特征在于：所述的附着力促进剂为非离子改性聚酯聚合物。
5.根据权利要求1所述的一种高硬度烤漆组合物，其特征在于：该烤漆组合物的最佳配方以重量分数表示为：
热固性丙烯酸树脂             61；
高亚氨基树脂                 33；
环氧树脂                     3.1；
乙二醇丁醚                   3；
正丁醇                       4；
二甲苯                       6；
聚醚改性溶液                 0.5；
非离子改性聚酯聚合物         1；
特殊改性官能基酯合物         2。
CNA2006101324501A 2006-12-29 2006-12-29 高硬度烤漆组合物 Pending CN101210132A (zh)