CN101096544A - 以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法 - Google Patents
以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法 Download PDFInfo
- Publication number
- CN101096544A CN101096544A CNA2006100144978A CN200610014497A CN101096544A CN 101096544 A CN101096544 A CN 101096544A CN A2006100144978 A CNA2006100144978 A CN A2006100144978A CN 200610014497 A CN200610014497 A CN 200610014497A CN 101096544 A CN101096544 A CN 101096544A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid polysulfide
- coating
- protective coating
- epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法，将端巯基液体聚硫预聚物4.0公斤与环氧树脂20.0公斤加入到带有搅拌器反应器中，搅拌并加热至80℃，加入5克的2，4，6-(N，N-二甲基氨甲基)苯酚，反应2小时，降至室温，得聚硫一环氧嵌段共聚物；将聚硫-环氧嵌段共聚物100份，防蜡剂5份，石英粉30份，气相二氧化硅0.1份，活性稀释剂5份，有机胺类固化剂15份充分混合均匀，将欲防护的井下器材预先进行除油、除锈等表面前处理，将涂料均匀地喷涂于器材的表面，将该涂层在100℃固化完全。本发明的优点：耐受井下高温、原油、含盐碱水的高腐蚀性使用环境，延长器材使用寿命，防结蜡。
Description
技术领域
本发明涉及一种以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法。
技术背景
目前应用最为广泛的井下器材的防护性材料是化学镀镍磷合金，具有优异的耐腐蚀性、耐高温性、耐摩擦性，但生产工艺复杂，镀覆过程中有析氢反应，非常容易造成孔隙，从而导致镀层的点腐蚀，该工艺产生大量的含重金属废水，废水较难处理，该工艺原材料成本高。有机防护性材料主要以环氧树脂以及用其它高分子材料改性的环氧树脂，如环氧酚醛树脂、环氧沥青树脂等。环氧树脂类涂层在高温、含油、含盐碱水的井下作业环境中易被破坏。
发明内容
本发明的目的在于克服上述的缺陷，提供一种以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法。
本发明的技术方案是：一种以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法，由液体聚硫预聚物和环氧树脂在有机胺类催化剂的作用下，反应生成嵌段共聚物，将欲防护的油田井下器材预先进行除油、除锈等表面前处理，以获得清洁表面，再将上述方法制备的涂料用浸涂方式涂覆在其表面成一定厚度的涂层，最后将涂层在30-120℃的温度下进行充分地固化处理。
本发明具有以下优点：耐受井下高温、原油、含盐碱水的高腐蚀性使用环境，延长器材使用寿命，防结蜡。
具体实施方式
实施例：一种以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法，将平均分子量为4000的端巯基液体聚硫预聚物4.0公斤与E-51环氧树脂20.0公斤加入到带有搅拌器反应器中，搅拌并加热至80℃，加入5克的2，4，6-(N，N-二甲基氨甲基)苯酚，反应2小时，降温至室温，得到聚硫-环氧嵌段共聚物；将获得的聚硫-环氧嵌段共聚物100份，防蜡剂5份，石英粉30份，气相二氧化硅0.1份，活性稀释剂5份，有机胺类固化剂15份充分混合均匀后备用，将欲防护的井下器材预先进行除油、除锈等表面前处理以获得清洁表面，将制备好的涂料均匀地喷涂于器材的表面，直到获得需要的厚度，将该涂层在100℃固化完全。
Claims (1)
1、一种以液体聚硫预聚物嵌段改性的环氧树脂防护性涂层制备方法，其特征在于：将平均分子量为4000的端巯基液体聚硫预聚物4.0公斤与E-51环氧树脂20.0公斤加入到带有搅拌器反应器中，搅拌并加热至80℃，加入5克的2，4，6-(N，N-二甲基氨甲基)苯酚，反应2小时，降温至室温，得到聚硫一环氧嵌段共聚物；将获得的聚硫-环氧嵌段共聚物100份，防蜡剂5份，石英粉30份，气相二氧化硅0.1份，活性稀释剂5份，有机胺类固化剂15份充分混合均匀后备用，将欲防护的井下器材预先进行除油、除锈等表面前处理以获得清洁表面，将制备好的涂料均匀地喷涂于器材的表面，直到获得需要的厚度，将该涂层在100℃固化完全。