CN100459046C - Production of high-quality magnesium silicide thin-film on silicon wafer - Google Patents
Production of high-quality magnesium silicide thin-film on silicon wafer Download PDFInfo
- Publication number
- CN100459046C CN100459046C CNB2007100647774A CN200710064777A CN100459046C CN 100459046 C CN100459046 C CN 100459046C CN B2007100647774 A CNB2007100647774 A CN B2007100647774A CN 200710064777 A CN200710064777 A CN 200710064777A CN 100459046 C CN100459046 C CN 100459046C
- Authority
- CN
- China
- Prior art keywords
- film
- magnesium
- layer
- silicon wafer
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention is concerned with high performance Mg2Si thin film production on wafer, relating to get clean wafer surface by heating treatment wafer in ultra-high vacuum, deposit magnesium thin film with low temperature, get MgO layer by the oxidation of magnesium thin film with low temperature, deposit oxide cover layer with low temperature and form Mg2Si thin film layer with high temperature and anneal. The method produces high performance Mg2Si thin film, and the predominant crystallinity shows the thin film is fit for producing high performance optoelectronic devices and thermoelectric devices. Mg2Si is a kind of narrow band-gap semiconductor with high thermoelectric coefficient, low resistivity, low thermal conductivity, and is a kind of excellent material for thermoelectric devices. And it is well Ohmic Contact material for n tape silicon with important application to silicon-based Integrated circuit, micro-electronics/photoelectron devices.
Description
Technical field
The present invention relates to a kind of preparation low-gap semiconductor magnesium silicide (Mg
2Si) method of film.
Background technology
Low-gap semiconductor Mg
2The band gap of Si is about 0.7eV, has very high Seebeck coefficient, very low resistivity and thermal conductivity, has significant application value in opto-electronic device and thermoelectric device.While Mg
2Si is again a n type silicon good Ohmic contact material, and important application prospects is also arranged in si-substrate integrated circuit, microelectronics/opto-electronic device.Device high-quality Mg
2The preparation of Si film is the basis of realizing its device application.Usually; people can mix magnesium metal with silicon in a vacuum or in the protective gas; utilize the high activity of magnesium metal, under suitable temperature, carry out solid phase reaction and obtain magnesium silicide material (as Chinese patent CN1062710 and foreign patent RU2083492-C1 etc.) with silicon.Be difficult to and will utilize this method on silicon wafer, to prepare the magnesium silicide material, in the world about on the Si wafer, preparing Mg
2The Si film, especially high-quality Mg
2The Si single crystal film reports that seldom one of them major reason is that the saturated vapor pressure of magnesium is very high, is easy to evaporate again under higher temperature, be unfavorable for absorption on silicon wafer, reaction.People such as A.Vantomme point out that (200-500 ℃) is difficult to realize Mg by the reactive deposition magnesium metal on the silicon wafer of heat
2The preparation of Si, because magnesium coefficient of viscosity on silicon under this temperature is almost nil, they adopt the method for molecular beam epitaxy technique magnesium silicon codeposition to prepare magnesium silicide thin-film on 200 ℃ silicon, but this film of test shows is a polycrystalline, thereby influenced its actual use value (Microelectronic Engineering50, (2000) 237-242).
Therefore, develop and a kind ofly can efficiently suppress magnesium method of evaporation again on silicon wafer, promote the solid phase reaction of silicon and magnesium, thus on silicon wafer realization high-quality Mg
2The preparation of Si film then is the key that magnesium silicide is applied in opto-electronic device and thermoelectric device.
Summary of the invention
The purpose of this invention is to provide a kind of new Mg that on silicon wafer, prepares
2The method of Si film, Si surface, low temperature depositing 5~500nm thick magnesium metal layer, the oxidation of the magnesium film superficial layer formation magnesium oxide layer, the low temperature that promptly divided for five steps wafer heat treating obtains cleaning under ultra-high vacuum environment successively prepare oxide cover layer and generate Mg with evaporation again, the high annealing that suppresses magnesium to quicken magnesium silicon solid phase reaction
2The Si film, its superior crystallinity shows that this film is very suitable for the making of high performance device.
The method for preparing magnesium silicide thin-film on silicon wafer provided by the invention is achieved by the following technical solution:
1) by the oxide layer of known hf etching method removal silicon wafer surface, imports ultra high vacuum system film system then; Wherein the sample stage of ultra high vacuum system film system has the heating and cooling function;
2) under the ultra high vacuum (UHV), be warming up to 700~950 ℃, high temperature is removed the residual oxygen silicon layer down, obtains the silicon face of cleaning;
3) above-mentioned silicon wafer is cooled to-10~-50 ℃, the thick magnesium metal layer of deposition 5~500nn;
4) utilize oxygen or active oxygen source that the metallic magnesium surface layer is carried out oxidation processes, obtain rock salt phase burning magnesium film layer;
5) further growth oxide cover layer on above-mentioned magnesia film layer, and make the thickness of oxide reach 30~100nm;
6) with 2~10 ℃/minute speed above-mentioned film is warming up to 100~400 ℃, annealed 1~10 hour, allow magnesium layer and silicon wafer generation solid phase reaction under oxide cover layer, thereby generate Mg
2The Si film.
Further, described silicon wafer is Si (111), Si (100) or Si (110) wafer.
Further, described ultra high vacuum system film system is molecular beam epitaxy (MBE) system.
Further, described oxide cover layer is magnesia film, indium oxide, titanium oxide or zinc-oxide film.
Above-mentioned Mg on silicon wafer
2The difference of Si method for manufacturing thin film and existing method mainly is: magnesium silicon solid phase reaction is carried out under the oxide cover layer protection; in order to achieve this end; the present invention has adopted low temperature deposit magnesium metal film, the superficial layer oxidation of magnesium film and deposition oxide cover layer successively, and high annealing generates Mg
2The process of Si layer.The purpose of low temperature deposit magnesium metal is in order to prevent that magnesium evaporation again and silicon and magnesium at high temperature from by counterdiffusion the formation that silicification reaction influences the magnesium metal thin layer taking place.We utilize reflection high energy electron diffraction (RHEED), have clearly observed below-10 ℃, and the phenomenon that the counterdiffusion of magnesium silicon is suppressed has fully obtained the magnesium film of high crystalline.After low temperature magnesium layer forms, open active oxygen source as utilizing oxygen containing radio frequency (rf) plasma, electron cyclotron resonace (ECR) plasma or ozone etc., active oxygen progressively is oxidized to magnesium oxide with magnesium film top layer to the diffusion of magnesium film.Because oxygen is no more than 2nm to the diffusion depth of magnesium film at low temperatures, therefore, we adopt the method further growth magnesium oxide or the zinc oxide of epitaxial growth oxide, make oxide cover layer reach 30~100nm, thereby have formed the MgO/Mg/Si double heterojunction at low temperatures.This structure has been protected magnesium desorption at high temperature effectively.At last, above-mentioned double heterojunction was annealed 1~10 hour down at 100~300 ℃, allowed magnesium and silicon fully react under the oxide cover layer protection, thereby generated MgO/Mg
2The Si/Si double heterojunction has been realized Mg
2The preparation of Si film.The thickness of oxide cover layer, annealing temperature and annealing time can determine according to the thickness of magnesium film, and cover layer can be magnesium oxide or more cheap zinc oxide etc.
Because this method adopts the magnesium silicon solid phase reaction under the oxide cover layer protection to prepare Mg
2The Si film, it is good to have under equilibrium state a preparation crystalline quality that film had, and uniformity height, thickness such as can arbitrarily control at advantage, compare with existing this non-equilibrium growing method of magnesium silicon codeposition to have outstanding superiority.
Description of drawings
Fig. 1 prepares Mg for the present invention on silicon wafer
2The process chart of Si film;
Fig. 2 be the embodiment of the invention 1 on 7 * 7 surfaces of-10 ℃ of Si (111) RHEED pattern of structure, magnesium film and rock salt phase oxidation magnesium film again;
Fig. 3 is that the embodiment of the invention 1 goes up the Mg that obtains at Si (111)
2The cross section full resolution pricture of the near interface transmission electron microscope of Si sample.
Embodiment
The present invention is described in detail below in conjunction with preparation method of the present invention and accompanying drawing.Embodiment 1 prepares Mg on Si (111) wafer
2The Si monocrystal thin films
Process chart of the present invention as shown in Figure 1 prepares Mg on Si (111) wafer
2The concrete steps of Si monocrystal thin films are as follows:
1. by known hf etching method Si (111) substrate is removed the silicon oxide layer on surface, import the MBE system then;
At air pressure less than 4.0 * 10
-7Under the Pa, be warming up to 750 ℃ and kept 30 minutes, utilize the high temperature desorption to remove the remaining silicon oxide layer of silicon face, obtain the silicon wafer surface of cleaning;
3. silicon wafer is cooled to-10 ℃, and this moment, the surface was typical 7 * 7 structures again, and the magnesium diffusion furnace is heated up, and made the line of magnesium reach 5 * 10
-5About Pa, the thick magnesium metal single crystalline layer of deposition 6nm;
4. open oxygen radio frequency plasma body source, the superficial layer of magnesium metal film was carried out oxidation processes 10 minutes, obtain the magnesium oxide single-crystal film; The flow of used oxygen is 1SCCM, and radio-frequency power is 200 watts;
5. the 50nm magnesia film cover layer of growing successively on above-mentioned magnesium oxide layer, the line of magnesium is 3 * 10
-5Pa, the flow of oxygen are 1SCCM, and radio-frequency power is 200 watts; And
6. with 5 ℃/minute speed above-mentioned film is warming up to 150 ℃, annealed 3 hours, allow in oxidation
Infratectal magnesium layer of thing and silicon wafer generation solid phase reaction, thus Mg generated
2The Si film.
In above-mentioned preparation thin-film process, we utilize reflection high energy electron diffraction (RHEED) that sample is carried out home position observation, and corresponding with film-forming process, its result as shown in Figure 2.Wherein Fig. 2 (a) be silicon (111) substrate in ultra high vacuum through the clean surface after the high-temperature process, be clearly 7 * 7 structures again this moment.Fig. 2 (b) shows among the figure that for being deposited on the RHEED pattern of the magnesium metal layer on the silicon (111) sharp keen wire diffraction pattern shows that magnesium (0001) has good crystallinity, and low temperature depositing magnesium has fully reduced the counterdiffusion of silicon magnesium, has suppressed the reaction between silicon and the magnesium; Pattern shows that also grid is superimposed upon on silicon (111) grid in Mg (0001) face, at this moment Mg<10-10〉//Si<11-2 〉; Mg<11-20〉//Si<10-1 〉.Fig. 2 (c) is the surface after the magnesium metal oxidation, and this pattern is typical rock salt phase oxidation magnesium, and its aufwuchsplate is (111) face, and the grid in the face also is superimposed upon on Si (111) grid, i.e. MgO<11-2〉//Si<11-2 〉; Mg<10-1〉//Si<10-1 〉.Deposition oxide cover layer easily on this magnesium oxide layer.Fig. 3 is that Si (111) goes up the Mg that obtains
2The cross section full resolution pricture of the near interface transmission electron microscope of Si sample shows among the figure between Si substrate and MgO layer to have formed the layer of even single crystalline layer that composition test shows that this layer is a magnesium silicide, and magnesium is 2 to 1 with the ratio of silicon, i.e. Mg
2The Si monocrystal thin films, under thermal equilibrium condition, the Mg of cubic structure
2Si is the stable state crystalline phase of magnesium silicide.
Claims (4)
1, a kind of Mg that on silicon wafer, prepares
2The method of Si film, its step is as follows:
1) by the oxide layer of known hf etching method removal silicon wafer surface, imports ultra high vacuum system film system then; Wherein the sample stage of ultra high vacuum system film system has the heating and cooling function;
2) under the ultra high vacuum (UHV), be warming up to 700~950 ℃, high temperature is removed the residual oxygen silicon layer down, obtains the silicon face of cleaning;
3) above-mentioned silicon wafer is cooled to-10~-50 ℃, the thick magnesium metal layer of deposition 5~500nm;
4) utilize oxygen or active oxygen source that the metallic magnesium surface layer is carried out oxidation processes, obtain rock salt phase burning magnesium film layer;
5) further growth oxide cover layer on above-mentioned magnesia film layer, and make the thickness of oxide reach 30~100nm;
6) with 2~10 ℃/minute speed above-mentioned film is warming up to 100~400 ℃, annealed 1~10 hour, allow magnesium layer and silicon wafer generation solid phase reaction under oxide cover layer, thereby generate Mg
2The Si film.
2, the Mg that on silicon wafer, prepares according to claim 1
2The method of Si film is characterized in that, the oxide cover layer described in the step 5) is magnesium oxide, indium oxide, titanium oxide or zinc-oxide film.
3, the Mg that on silicon wafer, prepares according to claim 1
2The method of Si film is characterized in that, described silicon wafer is Si (111), Si (100) or Si (110) wafer.
4, the Mg that on silicon wafer, prepares according to claim 1
2The method of Si film is characterized in that, described ultra high vacuum system film system is a molecular beam epitaxy system.