CN100445238C - 一种制造低膨胀系数蜂窝陶瓷灶具片的工艺 - Google Patents
一种制造低膨胀系数蜂窝陶瓷灶具片的工艺 Download PDFInfo
- Publication number
- CN100445238C CN100445238C CNB2006100892447A CN200610089244A CN100445238C CN 100445238 C CN100445238 C CN 100445238C CN B2006100892447 A CNB2006100892447 A CN B2006100892447A CN 200610089244 A CN200610089244 A CN 200610089244A CN 100445238 C CN100445238 C CN 100445238C
- Authority
- CN
- China
- Prior art keywords
- kitchen range
- honeycomb ceramic
- ceramic kitchen
- range sheet
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
原料 | 形貌 | 粒度 |
滑石 | 片状 | D<sub>50</sub>=10μm |
高岭土 | 鳞片状 | D<sub>50</sub>=2μm |
煅烧氧化铝 | 粒状 | D<sub>50</sub>=1μm |
二氧化硅 | 粒状 | D<sub>50</sub>=1μm |
原料 | 要求 |
滑石 | CaO≤0.5%,K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
高岭土 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
氧化铝 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
二氧化硅 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
原料 | 形貌 | 粒度 |
滑石 | 片状 | D<sub>50</sub>=20μm |
高岭土 | 鳞片状 | D<sub>50</sub>=3μm |
煅烧氧化铝 | 粒状 | D<sub>50</sub>=2μm |
二氧化硅 | 粒状 | D<sub>50</sub>=5μm |
原料 | 要求 |
滑石 | CaO≤O.5%,K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
高岭土 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
氧化铝 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
二氧化硅 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
原料 | 形貌 | 粒度 |
滑石 | 片状 | D<sub>50</sub>=30μm |
高岭土 | 鳞片状 | D<sub>50</sub>=4μm |
煅烧氧化铝 | 粒状 | D<sub>50</sub>=3μm |
二氧化硅 | 粒状 | D<sub>50</sub>=10μm |
原料 | 要求 |
滑石 | CaO≤0.5%,K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
高岭土 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
氧化铝 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
二氧化硅 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
原料 | 形貌 | 粒度 |
滑石 | 片状 | D<sub>50</sub>=40μm |
高岭土 | 鳞片状 | D<sub>50</sub>=5μm |
煅烧氧化铝 | 粒状 | D<sub>50</sub>=3μm |
二氧化硅 | 粒状 | D<sub>50</sub>=10μm |
原料 | 要求 |
滑石 | CaO≤0.5%,K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
高岭土 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
氧化铝 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
二氧化硅 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
原料 | 形貌 | 粒度 |
滑石 | 片状 | D<sub>50</sub>=35μm |
高岭土 | 鳞片状 | D<sub>50</sub>=4.5μm |
煅烧氧化铝 | 粒状 | D<sub>50</sub>=2.5μm |
二氧化硅 | 粒状 | D<sub>50</sub>=5μm |
原料 | 要求 |
滑石 | CaO≤0.5%,K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
高岭土 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
氧化铝 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1% |
二氧化硅 | K<sub>2</sub>O+Na<sub>2</sub>O≤0.1%,CaO≤0.5% |
Claims (9)