CN100409057C - 大面积铍窗封接方法 - Google Patents
大面积铍窗封接方法 Download PDFInfo
- Publication number
- CN100409057C CN100409057C CNB200510040724XA CN200510040724A CN100409057C CN 100409057 C CN100409057 C CN 100409057C CN B200510040724X A CNB200510040724X A CN B200510040724XA CN 200510040724 A CN200510040724 A CN 200510040724A CN 100409057 C CN100409057 C CN 100409057C
- Authority
- CN
- China
- Prior art keywords
- beryllium
- sheet
- window
- sealing
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种天文观测仪器上的大面积铍窗封装技术：大面积铍窗封接方法，步骤如下：准备压铍片用的重物和金属板，金属板的尺寸比待粘贴的铍片略小；对铍窗结构件、铍片、金属板、重物预加热；将调配好的环氧树脂涂敷在窗框的封接面上；把铍片放置到窗框封接面上；将金属板压在铍片上，保持离各边距离相等，在铝板上再加上重物；待胶固化、硬化后即可。本发明的封接方法比传统封装方法简单、实用，能够保证铍窗封接的气密性。更主要是，本方法可以实现传统方法所无法完成的，大面积铍窗的封接。
Description
技术领域
本发明涉及一种天文观测仪器上的大面积铍窗封装技术，具体涉及一种采用高真空环氧树脂密封胶的特殊工艺操作方法，可实现10cm×10cm这样大面积的铍窗真空密封封接。
背景技术
因为铍对X射线的透射率最高，所以探测X射线的正比计数管、电离室强流管、盖革管等，都设置铍窗。铍窗安装的基本要求是必须有严格的气密性，保证仓室的真空。随着天文观测技术的发展，仪器规格的扩大，对铍窗的面积要求也越来越大，其真空封装的技术难度也越来越大。
传统的铍窗真空封接多在高频真空炉、真空电热炉内进行，采用银铜焊料(如铜28)等作为焊料。但设备昂贵，工艺复杂，且成品率较低，特别是铍窗面积难以超过
发明内容
为了适应天文观测的发展需要，克服铍窗传统真空封接技术的不足，本发明将提供一种大面积铍窗封接方法，在保证铍窗封接的气密性等技术要求的前提下，实现大面积铍窗的封接。
完成上述发明任务的技术方案是：大面积铍窗封接方法，步骤如下：
准备压铍片用的重物和金属板，金属板的尺寸比待粘贴的铍片略小；
对铍窗结构件、铍片、金属板、重物预加热；
将调配好的环氧树脂涂敷在窗框的封接面上；
把铍片放置到窗框封接面上；
将金属板压在铍片上，保持离各边距离相等，在铝板上再加上重物；
胶固化、硬化后即可。
因环氧树脂的特性是遇热很快稀化，但随之也较快地固化、硬化，所以预热和加压，使环氧树脂迅速稀释，并因毛细管虹吸现象流散，因而得到十分均匀的封接面，然后树脂固化，保证了封装的气密性。
以上所述的“环氧树脂”，推荐采用Torr胶；
所述的“金属板”，推荐采用铝板；
所述的“重物”，推荐采用铁块；
所述的“金属板的尺寸比待粘贴的铍片略小”，推荐采用铝板的各边比铍片小2mm；
所述的“预加热”推荐采用预加热至80℃。
更具体和更优化地说，本发明的操作步骤是：
1、将铍窗结构件、铍片、铝板、铁块加热至80℃；
2、将调配好的Torr胶尽快涂敷在窗框的封接面上；
3、迅速把铍片放置到窗框封接面上；
4、将10mm厚90mm×96mm的铝板压在铍片上，保持离各边距离相等(各为2mm)，在铝板上再加上约为2公斤左右的铁块。
预热和加压，使Torr胶迅速稀释，并因毛细管虹吸现象流散，因而得到十分均匀的封接面，保证了气密性。采用Torr高真空密封胶，其固化时间为25℃24小时；60℃2小时，硬化时间为25℃，1～2小时；60℃30分。
本发明的大面积铍窗封接方法，比传统封装方法简单、实用，能够保证铍窗封接的气密性。更主要是，本方法可以实现传统方法所无法完成的，大面积铍窗的封接。
具体实施方式
实施例1，铍窗框架结构件上的铍窗真空密封，单片铍窗面积为92mm×98mm；封接面宽度均为3mm。采用Torr高真空密封胶，其固化时间为25℃24小时；60℃2小时，硬化时间为25℃，1～2小时；60℃30分。工作温度为-45℃～120℃。
操作步骤如下：
1、将铍窗结构件预加热至80℃；
2、将调配好的Torr胶尽快塗敷在窗框的封接面上，(Torr胶遇热很快稀化，但随之也较快地固化、硬化)；
3、迅速把铍片放置到窗框封接面上；
4、将10mm厚90mm×96mm的铝板压在铍片上，保持离各边距离相等(各为2mm)，在铝板上再加上约为2公斤左右的铁块。
(铍片、铝板、铁块在使用前均预加热到80℃)
预热和加压，使Torr胶迅速稀释，并因毛细管虹吸现象流散，因而得到十分均匀的封接面，保证了气密性。
Claims (2)
1. 一种大面积铍窗封接方法，步骤如下：
准备压铍片用的重物和金属板，金属板的尺寸比待粘贴的铍片略小；
对铍窗结构件、铍片、金属板、重物预加热；
将调配好的环氧树脂涂敷在窗框的封接面上；
把铍片放置到窗框封接面上；
将金属板压在铍片上，保持离各边距离相等，在铝板上再加上重物；
待胶固化、硬化后即可。
2. 按照权利要求1所述的大面积铍窗封接方法，其特征在于，操作步骤是：
(1、)将铍窗结构件、铍片、重物和金属板加热至80℃，所述的重物和金属板分别采用铁块和铝板；
(2、)将调配好的环氧树脂尽快涂敷在窗框的封接面上，所述的环氧树脂采用Torr胶；
(3、)迅速把铍片放置到窗框封接面上；
(4、)将10mm厚90mm×96mm的铝板压在铍片上，保持离各边距离相等，各为2mm，在铝板上再加上约为2公斤左右的铁块；
固化时间为25℃24小时；60℃2小时，硬化时间为25℃，1～2小时；60℃30分。