CN100372994C - Manual technique for fabricating blue printed true silk, and protection sgainst dyeing paste dedicated to manual blue printing - Google Patents
Manual technique for fabricating blue printed true silk, and protection sgainst dyeing paste dedicated to manual blue printing Download PDFInfo
- Publication number
- CN100372994C CN100372994C CNB2004100533568A CN200410053356A CN100372994C CN 100372994 C CN100372994 C CN 100372994C CN B2004100533568 A CNB2004100533568 A CN B2004100533568A CN 200410053356 A CN200410053356 A CN 200410053356A CN 100372994 C CN100372994 C CN 100372994C
- Authority
- CN
- China
- Prior art keywords
- real silk
- resist printing
- manual
- printing slurry
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a manual fabrication process for blue printed true silks, and dyeing protection slurry. The manual fabrication process for blue printed true silks comprises the following steps that after glued by tung oil, 10 to 20 layers of leather paper are dried and are maintained strong and smooth; 2 to 3 layers of glued paper plates are fixed together and patterns designed in advance are drawn or printed on one paper plate on the upper layer; according to patterns on the paper plate, a nicking tool is used for enchasing or opening through; the enchased flower plate is grinding to be smooth, and is waxed, brushed with the tung oil and dried. The flower plate is laid on white real silk blanks, and the dyeing protection slurry is brushed into pattern interspaces by a trowel; the white real silk blank brushed with the dyeing protection slurry is dried and is soaked in 30 to 50 DEG C of warm water to be softened; then, immersion dyeing by using plate indigo, rinsing, drying and rolling are carried out. The dyeing protection slurry comprises bean flour, lime powder, water and soybean oil, wherein the bean flour takes 45 to 65 shares (quality shares) and the lime powder takes 35 to 55 shares.
Description
Technical field
The present invention relates to a kind of printing technology, particularly a kind of manual blue resist printing slurry that prints the real silk manufacture craft and be exclusively used in the manual blue seal of real silk.
Background technology
In China, existing more than the 2000 year history of manual blue seal art, reportedly the basin, the Qiantang River in its origin last years of a dynasty or reign in spring and autumn is that the war of Wu Yue contention for hegemony flow into the Yangtze river basin, and is among the people as indispensable lining in people's daily life to Qin Han.Manual blue seal is also shining brilliance so far as outstanding folk art, the ancient dyeing method of manual blue seal, it except in external, also in the Java, states such as Egypt, Persian, India, Thailand, Japan spread.It is existing global, meets current artistic trend again, except that dyeing cloth, also is used for the technique of expression of high art, it not only ancient the but also young artistic technique be subjected to the generally attention of international industrial art circle.
Manual blue seal belongs to " resisting printing method " technology.The basic principle of resist printing is to utilize the method for " coverings ", makes fabric be difficult for dying, produce blank, thereby form decorative pattern, manual blue seal is to use lime, analysis for soybean powder, soya-bean oil furnishing slurry, scrapes slurry on cloth, contaminate then, because of be coated with dye partly can not on dye to show and spend.But when dyeing is owing to stir, make to have individually when dying and break, dye liquor permeates along the crack, so just stayed artificial untraceable natural water wave, dry slurry again, washing, though belong to same pattern sometimes, but water wave is different, and natural natural charm has the irreplaceable effect unique of other dyeing methods.
Real silk mainly adopts silk processing braiding to form, be the important a kind of natural animal azelon fabric of China, it has breathes freely, natural, environmental protection etc. are many a bit, very popular, but seldom have at all times the blue seal of craft is used for real silk fabric, thereby makes the manual indigo plant of real silk be printed as blank.Its main cause is because real silk is mainly made by animal protein, smooth surface, and in conjunction with comparatively difficult, the resist printing slurry comes off the very difficult predetermined pattern of printing and dyeing out to inorganic compound easily in the process of contaminating with it.
Summary of the invention
The present invention has filled up the blank of the manual blue seal technology of real silk, it is difficult with combining of real silk to have solved existing in prior technology resist printing slurry, the resist printing slurry comes off in the process of contaminating easily, the very difficult predetermined problems such as pattern of printing and dyeing out, provide a kind of technology simple, can carry out craft indigo plant seal to real silk, the resist printing slurry is difficult drop-off in the process of contaminating, the manual blue resist printing slurry that prints the real silk manufacture craft and be exclusively used in the manual blue seal of real silk of environmental protection.
Above-mentioned technical purpose of the present invention solves by the following technical programs, and the manufacture craft of manual blue seal real silk comprises the steps:
1), 10 to 20 layers of mulberry paper or peach blossom paper are dried after with the tung oil gummed, make it keep strong smooth;
2), the paper mold behind 2 to 3 layers of gummed is fixed together, describe or stamp the pattern that designs in advance on one deck paper mold in the above;
3), engrave according to the pattern on the paper mold or saturating empty, press the known method processing with carving good flower version with icking tool;
4), will spend the version be layered on the real silk openpore, with trowel the resist printing slurry is inserted the decorative pattern space;
5), the real silk openpore that will be filled with the resist printing slurry dries, and adds the porcine blood plasma of 0.1 ‰～1 ‰ (mass ratioes) in 30～50 ℃ of warm water, again the real silk openpore that dries is put into wherein to be dipped to and feels like jelly;
6), adopt vegetable indigo to contaminate rinsing, airing, roll extrusion.
Because the main component of real silk and the composition of soybean mainly are protein, the main component of the porcine blood plasma that adds also is a protein, pig blood also is rich in iron simultaneously, phosphorus, calcium, therefore, in the process that the real silk openpore of scraping the resist printing slurry soaks, add an amount of porcine blood plasma in warm water, protein in the porcine blood plasma can combine with the soybean protein in the resist printing slurry, and the calcium in the porcine blood plasma etc. can be strengthened the precipitation of lime, prevent that a spot of lime of part is soluble in water, can reinforce the combination of resist printing slurry and real silk, prevent coming off of resist printing slurry in the dip-dye process, improve the quality of printing and dyeing, make pattern clearly more demarcated.Wherein, mulberry paper also can be used peach blossom paper, glues together mulberry paper with tung oil, is a little that water breakthrough is insoluble, non-scale, and then attached drying on the wall can keep strong smooth; Icking tool generally has round mouth, nock, flat mouthful and angle four classes, the round mouth cutter is " blunderbuss " again, have the size several, be mainly used to the blunderbuss circular hole, the nock cutter is " tulwar " again, and various radians are arranged, be used to carve the sharp cusp of crescent moon, flat blade is used for the sharp wedge angle of engraving straight line, and the angle cutter is then carved upright sword feed, can accomplish without any letup than long lines; In the dip-dye process, the lining of different-thickness will adopt diverse ways, as set about when printing and dyeing kimono silk to want light, can not disorderly grab or stab with rod, in order to avoid the resist printing slurry is wiped off, the lining after having printed and dyed will repeatedly rinsing in water, and pattern is clearly demarcated more and have levels, the lining that dyed is pulled out all will clean by dye vat at every turn and is dried, so should there be enough washing machines in the dyehouse, the outdoor perpendicular hack that has is chosen hack by the dyer bamboo pole cloth that will wet that expands, wrinkle are arranged after drying more, just spool with the round log post, with pin step on the megalith roll extrusion it, the cloth of pressing, positive and negative clearly demarcated, zero diopter is pleasing; The real silk openpore of scraping the resist printing slurry helps indigo going into to dye through the immersion of warm water.
As preferably, described real silk openpore has added the porcine blood plasma of 0.2 ‰～0.5 ‰ (mass ratioes) in 30～50 ℃ of emerge in worm water processes; Described porcine blood plasma is preferably 0.25 ‰.
As preferably, the warm water temperature that the described real silk openpore that is brushed with the resist printing slurry soaks is 45 ℃.
As preferably, described flower version comprises the lid version that is mated use, and the space in the space of lid version cooperates the composition ring-type with the space of flower version.Blue seal real silk has the blue end to spend in vain with white background indigo plant to spend two kinds, and spend in vain at the blue end only needs a flower edition stamp, and the spot of formation grain pattern does not join mutually; White background indigo plant is spent and is generally all adopted the chromatography of two flower versions, print cry " the flower version " of first pass, be " lid version " for second time, the effect of lid version is the dyeing-resisted layer that the dyeing-resisted layer that the flower version produces is connected into ring-type, promptly when spending intermediate section in vain and be furnished with blue decorative pattern, the dyeing-resisted layer amalgamation that lid version and flower version produce can form ring-type white pattern together, thereby has solved the insurmountable problem of ring-type white pattern monolithic flower version, more clearly sets off out blue decorative pattern.
Be exclusively used in the resist printing slurry of the manual blue seal of real silk, comprise analysis for soybean powder, pulverized limestone, water and oleum sojae, wherein analysis for soybean powder is 45～65 parts (mass fractions), pulverized limestone is 35～55 parts; Described analysis for soybean powder is preferably 50～60 parts, and pulverized limestone is preferably 40～50 parts.Analysis for soybean powder and pulverized limestone mixed add water and a small amount of oleum sojae together, the furnishing pasty state, also available pulverized limestone is admixed soft beancurd, stirs evenly after the fermentation, and furnishing pasty state, lime and pulverized limestone all require thin more good more, make spending in vain of dyeing more limpid.The ratio of analysis for soybean powder hour in the resist printing slurry, analysis for soybean powder and pulverized limestone are in admixture, when the ratio of analysis for soybean powder is enough big, in the resist printing slurry of furnishing pasty state, analysis for soybean powder can wrap up pulverized limestone, leak the analysis for soybean powder that is mainly in the outside, simultaneously, because the main component of analysis for soybean powder and real silk is protein, therefore, the resist printing slurry is easier to be combined with the real silk openpore, and be filled with real silk openpore resist printing slurry difficult drop-off in the process of printing and dyeing of resist printing slurry, the predetermined pattern of printing and dyeing out, thus realized that manual indigo plant is imprinted on the application in the real silk, filled up the blank of the manual blue seal of real silk.
As preferably, the order number of described analysis for soybean powder and pulverized limestone is 170～280 orders; The order number of described analysis for soybean powder and pulverized limestone is preferably 200～280 orders.Analysis for soybean powder and pulverized limestone are as the main component of resist printing slurry, combine with the real silk openpore in the thin more easy more space that enters the real silk openpore, make the resist printing slurry firm more, difficult drop-off in the process of contaminating, the manual blue seal real silk that the pattern of printing and dyeing out is clearly demarcated with combining of real silk openpore.
As preferably, described oleum sojae is 1%～5% (mass percent).The grease of oleum sojae can wrap the resist printing pulp bales, thereby stops the resist printing slurry to dissolve in the water, further improves the fixing that resist printing slurry and real silk combine in immersion and dyeing process.
Therefore, the present invention has and can carry out the blue seal of craft to real silk, and pattern is clearly demarcated on the real silk of printing and dyeing out, and technology is simple, characteristics such as environmental protection.Because the main component of real silk and the composition of soybean mainly are protein, the main component of the porcine blood plasma that adds also is a protein, pig blood also is rich in iron simultaneously, phosphorus, calcium, therefore, in the process that the real silk openpore of scraping the resist printing slurry soaks, add an amount of porcine blood plasma in warm water, protein in the porcine blood plasma can combine with the soybean protein in the resist printing slurry, and the calcium in the porcine blood plasma etc. can be strengthened the precipitation of lime, prevent that a spot of lime of part is soluble in water, can reinforce the combination of resist printing slurry and real silk, prevent coming off of resist printing slurry in the dip-dye process, improve the quality of printing and dyeing, make pattern clearly more demarcated.Wherein, mulberry paper also can be used peach blossom paper, glues together mulberry paper with tung oil, and advantage is that water breakthrough is insoluble, non-scale, and then attached drying on the wall can keep strong smooth; Icking tool generally has round mouth, nock, flat mouthful and angle four classes, the round mouth cutter is " blunderbuss " again, have the size several, be mainly used to the blunderbuss circular hole, the nock cutter is " tulwar " again, and various radians are arranged, be used to carve the sharp cusp of crescent moon, flat blade is used for the sharp wedge angle of engraving straight line, and the angle cutter is then carved upright sword feed, can accomplish without any letup than long lines; In the dip-dye process, the lining of different-thickness will adopt diverse ways, as set about when printing and dyeing kimono silk to want light, can not disorderly grab or stab with rod, in order to avoid the resist printing slurry is wiped off, the lining after having printed and dyed will repeatedly rinsing in water, and pattern is clearly demarcated more and have levels, the lining that dyed is pulled out all will clean by dye vat at every turn and is dried, so should there be enough washing machines in the dyehouse, the outdoor perpendicular hack that has is chosen hack by the dyer bamboo pole cloth that will wet that expands, wrinkle are arranged after drying more, just spool with the round log post, with pin step on the megalith roll extrusion it, the cloth of pressing, positive and negative clearly demarcated, zero diopter is pleasing; The real silk openpore of scraping the resist printing slurry helps indigo going into to dye through the immersion of warm water.Analysis for soybean powder and pulverized limestone are as the main component of resist printing slurry, combine with the real silk openpore in the thin more easy more space that enters the real silk openpore, make the resist printing slurry firm more, difficult drop-off in the process of contaminating, the manual blue seal real silk that the pattern of printing and dyeing out is clearly demarcated with combining of real silk openpore.The grease of oleum sojae can wrap the resist printing pulp bales, thereby stops the resist printing slurry to dissolve in the water in the water, further improves the fixing that resist printing slurry and real silk combine in immersion and dyeing process.
The specific embodiment
Below by specific embodiment, and in conjunction with the accompanying drawings, technical scheme of the present invention is described in further detail.
Embodiment 1: the composition of resist printing slurry: 45 parts of analysis for soybean powder, and pulverized limestone 55 powder add the oleum sojae of water and 1%, the furnishing pasty state, wherein the order number of analysis for soybean powder and pulverized limestone is about 240 orders.
The manufacture craft of manual blue seal real silk: adopt mulberry paper to glue together with tung oil, mount 10 layers, attached drying on the wall makes it keep strong smooth; 2 to 3 layers of paper mold are nailed together, in the above one deck pattern of describing to design in advance or will stencil on paper mold at decorative pattern; Engrave according to the decorative pattern on the paper mold or saturating sky with icking tool; Polish flat carving good flower version with cobble earlier, and waxing, be called and press and smooth version, brush tung oil then, can use after drying; With " trowel " that ox bone or plank are done the resist printing slurry is brushed into the decorative pattern space, required smooth even; The real silk openpore of scraping the resist printing slurry is dried, in 45 ℃ of warm water, soak, in warm water, add 0.25 ‰ porcine blood plasma, can fastening resist printing slurry, be purple after dying simultaneously, feel like jelly until immersion; Go into to dye rinsing, airing, roll extrusion.In the dip-dye process, the lining of different-thickness will adopt diverse ways, as set about when printing and dyeing kimono silk to want light, can not disorderly grab or stab with rod, in order to avoid the resist printing slurry is wiped off, the lining after having printed and dyed will repeatedly rinsing in water, and pattern is clearly demarcated more and have levels, the lining that dyed is pulled out all will clean by dye vat at every turn and is dried, so should there be enough washing machines in the dyehouse, the outdoor perpendicular hack that has is chosen hack by the dyer bamboo pole cloth that will wet that expands, wrinkle are arranged after drying more, just spool with the round log post, with pin step on the megalith roll extrusion it, the cloth of pressing, positive and negative clearly demarcated, zero diopter is pleasing.
Embodiment 2: the composition of resist printing slurry: 65 parts of analysis for soybean powder, and pulverized limestone 35 powder add water and 5% oleum sojae, the furnishing pasty state, wherein the order number of analysis for soybean powder and pulverized limestone is about 170 orders.
The manufacture craft of manual blue seal real silk: adopt peach blossom paper to glue together with tung oil, mount 20 layers, attached drying on the wall makes it keep strong smooth; 2 to 3 layers of paper mold are nailed together, in the above one deck pattern of describing to design in advance or will stencil on paper mold at decorative pattern; Engrave according to the decorative pattern on the paper mold or saturating sky with icking tool; Polish flat carving good flower version with cobble earlier, and waxing, be called and press and smooth version, brush tung oil then, can use after drying; With " trowel " that ox bone or plank are done the resist printing slurry is brushed into the decorative pattern space, required smooth even; The lid version that connects with the white background on the real silk openpore that flower version tie point can be produced is layered on the real silk openpore that is brushed with the resist printing slurry, and the resist printing slurry is brushed in the space of covering version; The real silk openpore of scraping the resist printing slurry is dried, in 30 ℃ of warm water, soak, in warm water, add 0.1 ‰ porcine blood plasma, can fastening resist printing slurry, be purple after dying simultaneously, feel like jelly until immersion; Go into to dye rinsing, airing, roll extrusion.
Embodiment 3: the composition of resist printing slurry: 50 parts of analysis for soybean powder, and pulverized limestone 50 powder add water and 2.5% oleum sojae, the furnishing pasty state, wherein the order number of analysis for soybean powder and pulverized limestone is about 200 orders.
The manufacture craft of manual blue seal real silk: 15 layers mulberry paper is glued together with tung oil, and the soaking temperature of real silk openpore in warm water of scraping the resist printing slurry is 50 ℃, adds 1 ‰ porcine blood plasma in warm water, and other steps are referring to embodiment 1.
Embodiment 4: the composition of resist printing slurry: 60 parts of analysis for soybean powder, and pulverized limestone 40 powder add water and 3% oleum sojae, the furnishing pasty state, wherein the order number of analysis for soybean powder and pulverized limestone is about 280 orders.
The manufacture craft of manual blue seal real silk: the ratio that adds porcine blood plasma is 0.2 ‰, and other step is referring to embodiment 1.
Embodiment 5: the composition of resist printing slurry is referring to embodiment 1.
The manufacture craft of manual blue seal real silk: the ratio of porcine blood plasma is 0.5 ‰, and other step is referring to embodiment 1.
Claims (10)
1. a manual indigo plant is printed the real silk manufacture craft, it is characterized in that processing step is as follows:
1), 10 to 20 layers of mulberry paper or peach blossom paper are dried after with the tung oil gummed, make it keep strong smooth;
2), the paper mold behind 2 to 3 layers of gummed is fixed together, describe or stamp the pattern that designs in advance on one deck paper mold in the above;
3), engrave according to the pattern on the paper mold or saturating empty, press the known method processing with carving good flower version with icking tool;
4), will spend the version be layered on the real silk openpore, with trowel the resist printing slurry is inserted the decorative pattern space;
5), the real silk openpore that will be filled with the resist printing slurry dries, and adds the porcine blood plasma of 0.1 ‰～1 ‰ (mass ratioes) in 30～50 ℃ of warm water, again the real silk openpore that dries is put into wherein to be dipped to and feels like jelly;
6), adopt vegetable indigo to contaminate rinsing, airing, roll extrusion.
2. manual blue seal real silk manufacture craft according to claim 1 is characterized in that described real silk openpore has added the porcine blood plasma of 0.2 ‰～0.5 ‰ (mass ratioes) in 30～50 ℃ of emerge in worm water processes.
3. manual blue seal real silk manufacture craft according to claim 1 and 2 is characterized in that the warm water temperature that the described real silk openpore that is brushed with the resist printing slurry soaks is 45 ℃.
4. manual blue seal real silk manufacture craft according to claim 1 and 2 is characterized in that described porcine blood plasma is 0.25 ‰.
5. manual blue seal real silk manufacture craft according to claim 1 and 2 is characterized in that described flower version comprises the lid version that is mated use, and the space of lid version cooperates with the space of flower version and forms ring-type.
6. a resist printing slurry that is applied to the described manual blue seal real silk manufacture craft of claim 1 comprises analysis for soybean powder, pulverized limestone, and water and oleum sojae is characterized in that: analysis for soybean powder is 45～65 parts (mass fractions), and pulverized limestone is 35～55 parts.
7. resist printing slurry according to claim 6 is characterized in that described analysis for soybean powder is 50～60 parts, and pulverized limestone is 40～50 parts.
8. according to claim 6 or 7 described resist printing slurries, the order number that it is characterized in that described analysis for soybean powder and pulverized limestone is 150～280 orders.
9. resist printing slurry according to claim 8, the order number that it is characterized in that described analysis for soybean powder and pulverized limestone is 200～280 orders.
10. according to claim 6 or 7 described resist printing slurries, it is characterized in that described oleum sojae is 1%～5% (mass percent).