CH713119B1 - Wooden parquet element for a parquet floor, parquet floor and method of producing a wooden parquet element. - Google Patents
Wooden parquet element for a parquet floor, parquet floor and method of producing a wooden parquet element. Download PDFInfo
- Publication number
- CH713119B1 CH713119B1 CH01493/16A CH14932016A CH713119B1 CH 713119 B1 CH713119 B1 CH 713119B1 CH 01493/16 A CH01493/16 A CH 01493/16A CH 14932016 A CH14932016 A CH 14932016A CH 713119 B1 CH713119 B1 CH 713119B1
- Authority
- CH
- Switzerland
- Prior art keywords
- parquet
- wooden
- wood
- elements
- angle
- Prior art date
Abstract
Das erfindungsgemässe Holzparkettelement (2) für einen Parkettboden weist eine erste und eine zweite lange Seite (2.1, 2.2) sowie eine erste und eine zweite kurze Seite (2.3, 2.4) auf, wobei die beiden kurzen Seiten gegenüberliegend sind. Auf der ersten langen Seite (2.1) ist eine Nut (2.8) und auf der zweiten langen Seite (2.2) ist ein Kamm (2.6) vorgesehen. Zudem weist das Holzparkettelement (2) eine Längsachse (LAR) auf, die quer zur ersten und zweiten kurzen Seite (2.3, 2.4) verläuft. Die Längsachse (LAR) und die Faserrichtung (F) des Holzparkettelements (2) schliessen einen Winkel (α) zwischen 10° und 80° oder zwischen 100° und 170° ein. Die Erfindung betrifft zudem einen Parkettboden mit mehreren Holzparkettelementen, die im Verband angeordnet sind. Die Erfindung betrifft zudem ein Verfahren zur Herstellung eines Holzparkettelements, bei dem das Holzparkettelement mit einer CNC-Maschine aus einem Brett mit einer Faserrichtung entlang der Längsachse (LAB) gefräst wird.The inventive wood parquet element (2) for a parquet floor has a first and a second long side (2.1, 2.2) and a first and a second short side (2.3, 2.4), wherein the two short sides are opposite. On the first long side (2.1) is a groove (2.8) and on the second long side (2.2) is a comb (2.6) is provided. In addition, the wooden parquet element (2) has a longitudinal axis (LAR) which runs transversely to the first and second short sides (2.3, 2.4). The longitudinal axis (LAR) and the fiber direction (F) of the Holzparkettelements (2) enclose an angle (α) between 10 ° and 80 ° or between 100 ° and 170 °. The invention also relates to a parquet floor with a plurality of wood parquet elements, which are arranged in association. The invention also relates to a method for producing a Holzparkettelements in which the Holzparkettelement is milled with a CNC machine from a board with a fiber direction along the longitudinal axis (LAB).
Description
Beschreibungdescription
Technisches Gebiet [0001] Die Erfindung betrifft ein Holzparkettelement für einen Parkettboden und einen aus solchen Holzparkettelementen hergestellten Parkettboden. Zudem betrifft die Erfindung ein Verfahren zur Herstellung eines Holzparkettelements für einen Parkettboden.Technical Field The invention relates to a wooden parquet element for a parquet floor and a parquet floor made from such wooden parquet elements. The invention also relates to a method for producing a wooden parquet element for a parquet floor.
Darstellung der Erfindung [0002] Eine Aufgabe der Erfindung ist es, ein Holzparkettelement für einen Parkettboden, einen Parkettboden mit solchen Holzparkettelementen und ein Verfahren zur Herstellung eines solchen Holzparkettelements anzugeben, wobei das Holzparkettelement so ausgebildet ist, dass es einfach verlegbar ist.DESCRIPTION OF THE INVENTION An object of the invention is to provide a wooden parquet element for a parquet floor, a parquet floor with such wooden parquet elements and a method for producing such a wooden parquet element, the wooden parquet element being designed so that it can be easily installed.
[0003] Vorteilhafterweise können mit den erfindungsgemässen Holzparkettelementen verschiedene Muster im Parkettboden erzeugt werden.[0003] Advantageously, different patterns can be created in the parquet floor with the wooden parquet elements according to the invention.
[0004] Des Weiteren kann der Parkettboden mit den erfindungsgemässen Holzparkettelementen so verlegt sein, dass die benachbarten Holzparkettelemente sich deutlich optisch voneinander abgrenzen.[0004] Furthermore, the parquet floor with the wooden parquet elements according to the invention can be laid in such a way that the neighboring wooden parquet elements are clearly visually distinguished from one another.
[0005] Die Aufgabe wird durch ein Holzparkettelement für einen Parkettboden mit den in Patentanspruch 1 angegebenen Merkmalen gelöst.The object is achieved by a wooden parquet element for a parquet floor with the features specified in claim 1.
[0006] Das erfindungsgemässe Holzparkettelement für einen Parkettboden weist eine erste und eine zweite lange Seite sowie eine erste und eine zweite kurze Seite auf. Auf der ersten langen Seite ist eine Nut und auf der zweiten langen Seite ist ein Kamm vorgesehen. Zudem weist das Holzparkettelement eine Längsachse auf, die quer zur ersten und zweiten kurzen Seite verläuft. Die Längsachse und die Faserrichtung des Holzparkettelements schliessen einen Winkel zwischen 10° und 80° oder zwischen 100° und 170° ein.The wood parquet element according to the invention for a parquet floor has a first and a second long side and a first and a second short side. There is a groove on the first long side and a comb on the second long side. In addition, the wooden parquet element has a longitudinal axis that runs transversely to the first and second short sides. The longitudinal axis and the fiber direction of the wooden parquet element form an angle between 10 ° and 80 ° or between 100 ° and 170 °.
[0007] Die Aufgabe wird zudem durch einen die oben genannten Holzparkettelemente aufweisenden Parkettboden mit den in Patentanspruch 12 angegebenen Merkmalen gelöst.The object is also achieved by a parquet floor having the above-mentioned wooden parquet elements with the features specified in claim 12.
[0008] Der erfindungsgemässe Parkettboden weist mehrere der oben beschriebenen Holzparkettelemente auf, die im Verband angeordnet sind.The parquet flooring according to the invention has several of the wooden parquet elements described above, which are arranged in the association.
[0009] Darüber hinaus wird die Aufgabe durch ein Verfahren zur Herstellung der oben genannten Holzparkettelemente mit den in Patentanspruch 14 angegebenen Merkmalen gelöst.In addition, the object is achieved by a method for producing the above-mentioned wooden parquet elements with the features specified in claim 14.
[0010] Bei dem erfindungsgemässen Verfahren zur Herstellung eines Holzparkettelements wird das Holzparkettelement aus einem Brett mittels einer CNC-Maschine gefräst. Besonders von Vorteil ist es, wenn bei dem Brett die Faserrichtung parallel zur Längsseite des Bretts verläuft. Eine solche Herstellungsweise weist einen besonders geringen Materialverlust auf.In the inventive method for producing a wooden parquet element, the wooden parquet element is milled from a board by means of a CNC machine. It is particularly advantageous if the grain of the board runs parallel to the long side of the board. Such a method of production has a particularly low loss of material.
[0011] Vorteilhafte Weiterbildungen der Erfindung ergeben sich aus den in den abhängigen Patentansprüchen angegebenen Merkmalen.Advantageous further developments of the invention result from the features specified in the dependent claims.
[0012] Das erfindungsgemässe Holzparkettelement kann aus Massivholz hergestellt sein. Ein solches Holzparkettelement lässt sich ohne weiteres mehrmals abschleifen und versiegeln.[0012] The wood parquet element according to the invention can be made from solid wood. Such a wooden parquet element can easily be sanded and sealed several times.
[0013] Stattdessen kann das erfindungsgemässe Holzparkettelement auch eine Decklage aus Holz aufweisen, die auf einer Trägerschicht angeordnet ist. Die Decklage ist vorzugsweise aus einem Hartholz. Unterhalb der Trägerschicht können eine oder mehrere weitere Trägerschichten angeordnet sein. Das so aufgebaute Holzparkettelement ist kostengünstiger herstellbar als das Holzparkettelement aus Massivholz.Instead, the wood parquet element according to the invention can also have a top layer made of wood, which is arranged on a carrier layer. The top layer is preferably made of hardwood. One or more further carrier layers can be arranged below the carrier layer. The wood parquet element constructed in this way is less expensive to manufacture than the wood parquet element made of solid wood.
[0014] Bei einer Ausführungsform des erfindungsgemässen Holzparkettelements sind die erste und eine zweite lange Seite gekrümmt.In one embodiment of the wooden parquet element according to the invention, the first and a second long side are curved.
[0015] Gemäss einer weiteren Ausführungsform kann das erfindungsgemässe Holzparkettelement linsenförmig ausgebildet sein. Dadurch kann ein besonderer optischer Eindruck erzeugt werden.[0015] According to a further embodiment, the wood parquet element according to the invention can be lenticular. This can create a special visual impression.
[0016] Stattdessen kann das erfindungsgemässe Holzparkettelement auch die Form eines Parallelogramms oder einer Raute haben, wobei dessen respektive deren spitze Ecken abgeschnitten sind.Instead, the wood parquet element according to the invention can also have the shape of a parallelogram or a rhombus, the respective corners of which are cut off.
[0017] Gemäss einer zusätzlichen Ausführungsform kann das erfindungsgemässe Holzparkettelement so ausgebildet sein, dass dessen Oberseite symmetrisch zur Längsachse ist.[0017] According to an additional embodiment, the wood parquet element according to the invention can be designed such that its top is symmetrical to the longitudinal axis.
[0018] Es ist auch möglich, das erfindungsgemässe Holzparkettelement so auszubilden, dass dessen erste kurze Seite eine Nut aufweist.It is also possible to design the wooden parquet element according to the invention so that its first short side has a groove.
[0019] Bei einer Weiterbildung des erfindungsgemässen Holzparkettelements weist die zweite kurze Seite einen Kamm auf.In a further development of the wooden parquet element according to the invention, the second short side has a comb.
[0020] Schliesslich kann bei dem erfindunqsqemässen Holzparkettelement vorqesehen sein, dass der Winkel zwischen 20° und 60° liegt.Finally, it can be provided with the inventive wooden parquet element that the angle is between 20 ° and 60 °.
[0021] Bei einer Weiterbildung des erfindungsgemässen Parkettbodens ist bei einem Teil der Holzparkettelemente vorgesehen, dass der Winkel zwischen 10° und 80° liegt. Bei einem weiteren Teil der Holzparkettelemente ist vorgesehen, dass der Winkel zwischen 100° und 170° liegt. Dadurch, dass bezüglich des Faserverlaufs unterschiedliche Holzparkettelemente nebeneinander liegen, heben sich die benachbarten Holzparkettelemente deutlich voneinander ab.In a development of the parquet flooring according to the invention, it is provided in some of the wooden parquet elements that the angle is between 10 ° and 80 °. In a further part of the wooden parquet elements, it is provided that the angle is between 100 ° and 170 °. The fact that different wood parquet elements lie next to each other with respect to the fiber orientation means that the neighboring wood parquet elements stand out clearly from one another.
[0022] Bei einer möglichen Ausführungsform des erfindungsgemässen Verfahrens zur Herstellung eines Holzparkettelements wird das Holzparkettelement mit einer Kennzeichnung versehen, wenn der Winkel zwischen 10° und 80° liegt. Liegt der Winkel jedoch zwischen 100° und 170°, wird das Holzparkettelement mit einer anderen Kennzeichnung versehen.In a possible embodiment of the method according to the invention for producing a wooden parquet element, the wooden parquet element is provided with a label when the angle is between 10 ° and 80 °. However, if the angle is between 100 ° and 170 °, the wooden parquet element is given a different label.
Kurze Beschreibung der Zeichnungen [0023] Im Folgenden wird die Erfindung mit mehreren Ausführungsbeispielen anhand der folgenden Figuren weiter erläutert.BRIEF DESCRIPTION OF THE DRAWINGS The invention is explained in more detail below with several exemplary embodiments with reference to the following figures.
Wege zur Ausführung der Erfindung [0024] In Fig. 1 ist eine erste mögliche Ausführungsform des erfindungsgemässen Holzparkettelements 2 in verschiedenen Ansichten dargestellt. Fig. 1 zeigt oben das Holzparkettelement 2 der Seitenansicht, links in Fig. 1 ist das Holzparkettelement 2 in der Ansicht von vorne und rechts in der Draufsicht dargestellt. Fig. 2 zeigt eine zweite mögliche Ausführungsform des erfindungsgemässen Holzparkettelements 2 ebenfalls in der Seitenansicht, in der Ansicht von vorne und in der Draufsicht.WAYS OF IMPLEMENTING THE INVENTION FIG. 1 shows a first possible embodiment of the wooden parquet element 2 according to the invention in different views. 1 shows the wooden parquet element 2 from the side, the left in FIG. 1 shows the wooden parquet element 2 from the front and the right from the top view. 2 shows a second possible embodiment of the wooden parquet element 2 according to the invention, likewise in a side view, in a view from the front and in a top view.
[0025] Das Holzparkettelement 2 weist eine erste lange Seite 2.1 und eine zweite lange Seite 2.2 sowie eine erste kurze Seite 2.3 und eine zweite kurze Seite 2.4 auf. Die beiden langen Seiten 2.1 und 2.2 sind länger und vorzugsweise deutlich länger als die beiden kurzen Seiten 2.3 und 2.4. Als lange Seite wird jene Seite bezeichnet, die sich im Wesentlichen in Richtung der Längsachse LAR des Holzparkettelements 2 erstreckt. Die kurze Seite erstreckt sich hingegen nicht oder nur wenig entlang der Längsachse LAR des Holzparkettelements 2. Die Längsrichtung verläuft parallel zur Längsachse LAR des Holzparkettelements 2.The wood parquet element 2 has a first long side 2.1 and a second long side 2.2 and a first short side 2.3 and a second short side 2.4. The two long sides 2.1 and 2.2 are longer and preferably significantly longer than the two short sides 2.3 and 2.4. The long side is the side that extends essentially in the direction of the longitudinal axis LAR of the wooden parquet element 2. The short side, however, does not extend, or only slightly, along the longitudinal axis LAR of the wooden parquet element 2. The longitudinal direction runs parallel to the longitudinal axis LAR of the wooden parquet element 2.
[0026] Bei den in den Fig. 1 und 2 gezeigten Ausführungsformen haben die beiden langen Seiten 2.1 und 2.2 eine gekrümmte Form. Die beiden kurzen Seiten 2.3 und 2.4 hingegen sind gerade. Vorzugsweise haben die beiden kurzen SeitenIn the embodiments shown in FIGS. 1 and 2, the two long sides 2.1 and 2.2 have a curved shape. The two short pages 2.3 and 2.4, however, are straight. Preferably the two short sides
2.3 und 2.4 die gleiche Breite B. In der Draufsicht hat das Holzparkettelement 2 die Form einer Linse. Die Längsachse LAR des Holzparkettelements 2 verläuft quer und vorzugsweise im rechten Winkel zur ersten und zweiten kurzen Seite 2.3, 2.4. Das Holzparkettelement 2 hat zudem einen Faserverlauf, auch Faserrichtung F genannt, die von der Längsachse LAR in einem Winkel α abweicht. Die Faserrichtung F ist die Richtung der gerichteten Zellen des Holzes. Der Winkel α wird im Folgenden auch als Faserwinkel bezeichnet. Der Winkel a, den die Längsachse LAR und die Faserrichtung F einschliessen, ist ein spitzer Winkel und liegt zwischen 10° und 70°. Der Winkel α kann aber auch - wie in Fig. 3d gezeigt - ein stumpfer Winkel sein, der zum Beispiel zwischen 100° und 170° liegt. Bei den Ausführungsbeispielen gemäss den Fig. 1 und 2 ist der Faserverlauf um rund 26° entgegen dem Uhrzeigersinn gegenüber der Längsachse LAR gedreht. In Fig. 3d hingegen ist er um rund 49° im Uhrzeigersinn gegenüber der Längsachse LAR gedreht, sodass sich ein Faserwinkel α von 131° ergibt.2.3 and 2.4 the same width B. In the plan view, the wooden parquet element 2 has the shape of a lens. The longitudinal axis LAR of the wooden parquet element 2 runs transversely and preferably at right angles to the first and second short sides 2.3, 2.4. The wood parquet element 2 also has a fiber course, also called fiber direction F, which deviates from the longitudinal axis LAR at an angle α. The fiber direction F is the direction of the directional cells of the wood. The angle α is also referred to below as the fiber angle. The angle a, which the longitudinal axis LAR and the fiber direction F form, is an acute angle and is between 10 ° and 70 °. However, as shown in FIG. 3d, the angle α can also be an obtuse angle which is, for example, between 100 ° and 170 °. In the exemplary embodiments according to FIGS. 1 and 2, the fiber course is rotated by approximately 26 ° counterclockwise with respect to the longitudinal axis LAR. In contrast, in FIG. 3d it is rotated clockwise by approximately 49 ° with respect to the longitudinal axis LAR, so that a fiber angle α of 131 ° results.
[0027] Sowohl bei dem Ausführungsbeispiel gemäss Fig. 1 als auch bei dem Ausführungsbeispiel gemäss Fig. 2 ist auf der ersten langen Seite 2.1 eine Nut 2.8 vorgesehen. Auf der zweiten langen Seite 2.2 befindet sich ein Kamm 2.6. Der Kamm 2.6 und die Nut 2.8 sind so ausgebildet, dass ein zweites baugleiches Holzparkettelement 2 mit seinem Kamm 2.6 in die Nut 2.8 des anderen Holparkettelements 2 gesteckt werden kann und mit diesem einen Formschluss bildet.Both in the embodiment shown in FIG. 1 and in the embodiment shown in FIG. 2, a groove 2.8 is provided on the first long side 2.1. On the second long page 2.2 there is a comb 2.6. The comb 2.6 and the groove 2.8 are designed such that a second wooden parquet element 2 of identical construction can be inserted with its comb 2.6 into the groove 2.8 of the other wooden parquet element 2 and forms a positive fit with the latter.
[0028] Es kann vorgesehen sein, dass das Holzparkettelement 2 auf den kurzen Seiten 2.3 und 2.4 weder eine Nut noch einen Kamm aufweist. In Fig. 1 ist dies zur Veranschaulichung beispielhaft auf der kurzen Seite 2.3 dargestellt.It can be provided that the wooden parquet element 2 on the short sides 2.3 and 2.4 has neither a groove nor a comb. In Fig. 1, this is exemplified on the short page 2.3.
[0029] Es kann auch vorgesehen sein, dass das Holzparkettelement 2 auf den kurzen Seiten 2.3 und 2.4 jeweils eine Nut aufweist. In Fig. 1 ist dies zur Veranschaulichung beispielhaft auf der kurzen Seite 2.4 dargestellt.It can also be provided that the wooden parquet element 2 has a groove on the short sides 2.3 and 2.4. In Fig. 1, this is exemplified on the short page 2.4.
[0030] Stattdessen kann auch vorgesehen sein, dass das Holzparkettelement 2 auf der ersten kurzen Seite 2.3 eine Nut 2.9 und auf der zweiten kurzen Seite 2.4 einen Kamm 2.7 aufweist. Diese Ausführungsform ist in Fig. 2 dargestellt. Selbstverständlich können der Kamm 2.7 auch auf der ersten kurzen Seite 2.3 und die Nut 2.9 auch auf der zweiten kurzen Seite 2.4 angeordnet sein.Instead, it can also be provided that the wooden parquet element 2 has a groove 2.9 on the first short side 2.3 and a comb 2.7 on the second short side 2.4. This embodiment is shown in FIG. 2. Of course, the comb 2.7 can also be arranged on the first short side 2.3 and the groove 2.9 on the second short side 2.4.
[0031] Das Holzparkettelement 2 kann aus Massivholz bestehen oder aus mehreren Schichten aufgebaut sein.The wood parquet element 2 can consist of solid wood or be constructed from several layers.
[0032] Ein solches aus ganzen, massiven Holzparkettelementen 2 erzeugtes Massivparkett hat eine durchgängige Hartholzschicht mit einer Gesamtdicke zwischen 22 und 35 mm. Die Nutzschicht beträgt in der Regel zwischen 12 und 15 mm. Aufgrund dieser dicken Nutzschicht kann das Massivholzparkett sehr häufig abgeschliffen werden. Erst nachdem der Parkettboden verlegt ist, findet das Abschleifen und die Oberflächenbehandlung statt.Such a solid parquet produced from whole, solid wood parquet elements 2 has a continuous hardwood layer with a total thickness between 22 and 35 mm. The wear layer is usually between 12 and 15 mm. Due to this thick wear layer, the solid wood parquet can be sanded down very often. Sanding and surface treatment take place only after the parquet floor has been laid.
[0033] Wenn das Holzparkettelement 2 aus mehreren Schichten aufgebaut ist, wird es als Mehrschichtparkett bezeichnet. Durch den mehrschichtigen Aufbau erhält das Parkettelement 2 die gewünschte Formstabilität, das heisst, das Quellen und Schwinden des Holzes durch wechselnde Luftfeuchtigkeit wird reduziert. Das Mehrschichtparkett umfasst mehrere miteinander verleimte Holzschichten, wobei in der Regel nur die oberste Schicht, die auch als Nutzschicht oder Decklage bezeichnet wird, aus hochwertigem Holz ist. Die Dicke der Decklage kann zum Beispiel zwischen 2,5 mm und 6,0 mm liegen. Die darunter liegende Schicht respektive Schichten, die auch als Trägerschichten bezeichnet werden, können aus günstigerem Holz als die Decklage hergestellt sein. Die Gesamtdicke des Parkettelements 2 liegt vorzugsweise zwischen 10 und 20 mm. Das Mehrschichtparkett kann zum Beispiel als 2-Schicht-oder als 3-Schicht-Parkett hergestellt sein.If the wooden parquet element 2 is constructed from several layers, it is referred to as multilayer parquet. The multi-layer structure gives the parquet element 2 the desired dimensional stability, which means that the swelling and shrinking of the wood due to changing air humidity is reduced. The multi-layer parquet comprises several layers of wood glued together, whereby usually only the top layer, which is also referred to as the wear layer or top layer, is made of high quality wood. The thickness of the top layer can be, for example, between 2.5 mm and 6.0 mm. The underlying layer or layers, which are also referred to as backing layers, can be made of cheaper wood than the top layer. The total thickness of the parquet element 2 is preferably between 10 and 20 mm. The multi-layer parquet can be produced, for example, as a 2-layer or as a 3-layer parquet.
[0034] Das 2-Schicht-Parkett umfasst die Decklage und eine Trägerschicht, die mit der Decklage verklebt ist. Das 2Schicht-Parkett wird in der Regel vollflächig auf eine Unterlage geklebt, da die Decklage und die Trägerschicht meist nicht stabil genug sind, um von alleine in Form zu bleiben.The 2-layer parquet comprises the top layer and a backing layer which is glued to the top layer. The two-layer parquet is generally glued to a surface over its entire surface, since the top layer and the backing layer are usually not stable enough to remain in shape on their own.
[0035] Das 3-Schicht-Parkett umfasst die Decklage und zwei Trägerschichten, die miteinander verklebt sind. Die unterste Trägerschicht wird auch als Rückzugsfurnier bezeichnet. Das 3-Schicht-Parkett kann schwimmend verlegt oder verklebt werden.The 3-layer parquet comprises the top layer and two backing layers which are glued together. The bottom backing layer is also referred to as a retractable veneer. The 3-layer parquet can be laid floating or glued.
[0036] Wenn die Decklage des Holzparkettelements 2 ausreichend dick ist, vorzugsweise mehr als 2,5 mm, lässt sich Parkettelement 2 auch mehrmals abschleifen und versiegeln.If the top layer of the wooden parquet element 2 is sufficiently thick, preferably more than 2.5 mm, parquet element 2 can also be sanded and sealed several times.
[0037] Wenn die Gesamtdicke des Holzparkettelements 2 gering und damit ein guter Wärmedurchtritt möglich ist, eignet es sich gut für eine Fussbodenheizung.If the total thickness of the wooden parquet element 2 is small and good heat transfer is possible, it is well suited for underfloor heating.
[0038] Wenn die Oberfläche des Mehrschichtparketts bereits geschliffen und versiegelt respektive geölt ist, wird es auch als Fertigparkett bezeichnet. Anders als beim Massivparkett entfällt beim Fertigparkett das Schleifen und Versiegeln auf der Baustelle.If the surface of the multilayer parquet is already sanded and sealed or oiled, it is also referred to as a finished parquet. In contrast to solid parquet, there is no need for sanding and sealing on the construction site.
[0039] Das erfindungsgemässe Holzparkettelement 2 kann auch zu Tafelparkett verarbeitet werden, das auch «Französisches Parkett» genannt wird. Die Holzparkettelemente 2 können zu einem geometrischen Muster auf einer, häufig quadratischen Trägerschicht aufgeklebt werden. Die so hergestellten Tafeln können dann auf der Baustelle verlegt werden.The wood parquet element 2 according to the invention can also be processed into panel parquet, which is also called «French parquet». The wooden parquet elements 2 can be glued to a geometric pattern on a, often square, support layer. The panels produced in this way can then be laid on the construction site.
[0040] In der Draufsicht haben die erste und die zweite Ausführungsform des Holzparkettelements 2 (Fig. 1 und 2), abgesehen von den Nuten und Kämmen, die gleiche Geometrie.In the top view, the first and the second embodiment of the wooden parquet element 2 (FIGS. 1 and 2), apart from the grooves and combs, have the same geometry.
[0041] Das Holzparkettelement 2 kann zum Beispiel wie folgt hergestellt werden. Ausgangsmaterial ist ein in Fig. 3a in der Draufsicht gezeigtes Brett 1. Im vorliegenden Ausführungsbeispiel hat das Brett 1 eine erste Längsseite 1.1 und eine zweite Längsseite 1.2, die zueinander parallel verlaufen. Dies ist für das Herstellungsverfahren aber nicht zwingend. Die Längsachse LAB des Bretts 1 verläuft parallel zum Faserverlauf F. Somit verlaufen die Holzfasern quer zu den StirnseitenThe wood parquet element 2 can be produced, for example, as follows. The starting material is a board 1 shown in plan view in FIG. 3a. In the present exemplary embodiment, the board 1 has a first long side 1.1 and a second long side 1.2, which run parallel to one another. However, this is not mandatory for the manufacturing process. The longitudinal axis LAB of the board 1 runs parallel to the fiber course F. Thus, the wood fibers run transversely to the end faces
1.3 und 1.4 des Bretts 1. Das Brett 1 wird durch eine Reihe von Schnitten in einem Winkel ß, auch Schnittwinkel genannt, entlang der Schnittlinien 4 in zum Beispiel acht Parallelogramme respektive acht Rauten zerteilt. Der Winkel ß kann zum Beispiel 70° betragen. Jedes der acht rautenförmigen Bretter bildet die Grundform für jeweils ein Holzparkettelement 2.1.3 and 1.4 of the board 1. The board 1 is divided by a series of cuts at an angle β, also called cutting angle, along the cutting lines 4 into, for example, eight parallelograms or eight diamonds. The angle β can be, for example, 70 °. Each of the eight diamond-shaped boards forms the basic shape for a wooden parquet element 2.
[0042] Nun wird mittels einer CNC-Maschine (CNC = Computerized Numerical Control), die auch als CNC-Werkzeugfräsmaschine bezeichnet wird, aus den rautenförmigen Brettern die Kontur des Holzparkettelements 2 herausgefräst. Bei Bedarf kann die CNC-Maschine mit entsprechend geformten Fräsern neben der Kontur auch gleichzeitig die Seiten 2.1-2.4 profilieren, also mit den entsprechenden Nuten 2.8, 2.9 und Kämmen 2.6, 2.7 versehen.Now the contour of the wooden parquet element 2 is milled out of the diamond-shaped boards by means of a CNC machine (CNC = Computerized Numerical Control), which is also referred to as a CNC tool milling machine. If necessary, the CNC machine can also profile the sides 2.1-2.4 with correspondingly shaped cutters in addition to the contour, i.e. provide the corresponding grooves 2.8, 2.9 and combs 2.6, 2.7.
[0043] Fig. 3b zeigt eines der aus dem Brett 1 ausgeschnittenen Holzparkettelemente 2 in der Draufsicht, wobei die ausgeschnittenen Holzparkettelemente 2 allesamt eine erste Faserrichtung F aufweisen. Das in diesem Ausführungsbeispiel hergestellte Parkettelement 2 hat einen Faserwinkel α von rund 49°, das heisst, die Faserrichtung F ist gegenüber der Längsachse LAR des Holzparkettelements 2 um 49° entgegen dem Uhrzeigersinn gedreht. Das Holzparkettelement 2 hat wie das Holzparkettelement 2 aus Fig. 1 und 2 eine Linsenform, ist aber breiter als dieses.3b shows a top view of one of the wooden parquet elements 2 cut out of the board 1, the cut wooden parquet elements 2 all having a first fiber direction F. The parquet element 2 produced in this exemplary embodiment has a fiber angle α of approximately 49 °, that is to say the fiber direction F is rotated counterclockwise by 49 ° with respect to the longitudinal axis LAR of the wooden parquet element 2. Like the wooden parquet element 2 from FIGS. 1 and 2, the wooden parquet element 2 has a lens shape, but is wider than this.
[0044] Auf die oben beschriebene Art und Weise können auch die in den Fig. 3c und 3d dargestellten Holzparkettelemente 20 hergestellt werden. Dazu wird das Brett 1 dieses Mal im Winkel ß= 110° entlang den Schnittlinien 14 in zum Beispiel acht rautenförmige Bretter zerteilt. Anschliessend werden mit der CNC-Maschine aus den rautenförmigen Brettern die Konturen respektive Profile der Holzparkettelemente 20 herausgefräst. Dies kann sinngemäss auf die bereits oben beschriebene Art und Weise geschehen.The wood parquet elements 20 shown in FIGS. 3c and 3d can also be produced in the manner described above. For this purpose, the board 1 is divided this time at an angle β = 110 ° along the cutting lines 14 into, for example, eight diamond-shaped boards. The contours or profiles of the wooden parquet elements 20 are then milled out of the diamond-shaped boards with the CNC machine. This can be done analogously in the manner already described above.
[0045] Die in den Fig. 3c und 3d dargestellten Parkettelemente 20 haben jeweils einen stumpfen Faserwinkel α von rund 131°. Die Faserrichtung F ist also gegenüber der Längsachse LAR des Holzparkettelements 20 um 131° entgegen dem Uhrzeigersinn gedreht.The parquet elements 20 shown in FIGS. 3c and 3d each have an obtuse fiber angle α of around 131 °. The fiber direction F is thus rotated counterclockwise by 131 ° with respect to the longitudinal axis LAR of the wooden parquet element 20.
[0046] Um die verschiedenen Holzparkettelemente 2 und 20 einfach unterscheiden zu können, kann vorgesehen sein, sie mit unterschiedlichen Kennzeichnungen zu versehen. So kann dasjenige Holzparkettelement 2, bei dem der Faserwinkel α spitz ist, mit einer ersten Kennzeichnung versehen werden. Dasjenige Holzparkettelement 20 mit einem stumpfen Faserwinkel α (zwischen 110° und 170°) wird hingegen mit einer anderen Kennzeichnung versehen. Eine solche Kennzeichnung kann für den Parkettbodenleger von Hilfe sein.In order to be able to easily differentiate between the different wooden parquet elements 2 and 20, it can be provided that they are provided with different markings. That wooden parquet element 2 in which the fiber angle α is acute can be provided with a first identification. The wood parquet element 20 with an obtuse fiber angle α (between 110 ° and 170 °), on the other hand, is given a different label. Such a label can be of help to the parquet floor layer.
[0047] Mit den in den Fig. 3a bis 3d gezeigten Holzparkettelementen 2 und 20 kann ein Parkettboden hergestellt werden, der zum Beispiel das in Fig. 3e zeigte Muster aufweist. Der Winkel γ oder auch Verlaufswinkel genannt, gibt an, in welchem Winkel benachbarte Parkettelemente 2 zueinander versetzt sind. Bei dem in Fig. 3e gezeigten Parkettboden beträgt der Verlaufswinkel γ rund 41 °.With the wooden parquet elements 2 and 20 shown in FIGS. 3a to 3d, a parquet floor can be produced which, for example, has the pattern shown in FIG. 3e. The angle γ or also called the progression angle indicates the angle at which adjacent parquet elements 2 are offset from one another. In the parquet floor shown in Fig. 3e, the angle γ is around 41 °.
[0048] Wenn die Faserrichtungen zweier benachbarter Holzparkettelemente 2 und 20 sich in einem Winkel zwischen 40° und 90° schneiden, ist der Unterschied zwischen den Holzparkettelementen besonders gut erkennbar.If the fiber directions of two adjacent wooden parquet elements 2 and 20 intersect at an angle between 40 ° and 90 °, the difference between the wooden parquet elements can be seen particularly well.
[0049] In Fig. 4a sind die Konturen von vier der erfindungsgemässen Holzparkettelemente 2 in vier verschiedenen Grössen in der Draufsicht dargestellt. Die Profile mit den Nuten und Kämmen sind in dieser Darstellung der Übersichtlichkeit halber weggelassen. Die Holzparkettelemente 2b bis 2d sind gegenüber dem Holzparkettelemente 2a zentrisch vergrössert. Allesamt haben die Form einer Linse.4a shows the contours of four of the wooden parquet elements 2 according to the invention in four different sizes in a top view. The profiles with the grooves and combs are omitted in this illustration for the sake of clarity. The wooden parquet elements 2b to 2d are enlarged centrally compared to the wooden parquet elements 2a. All have the shape of a lens.
[0050] Fig. 4b links zeigt ein Holzparkettelement 2 mit einem ersten, spitzen Faserwinkel α und Fig. 4b rechts ein Holzparkettelement 20 mit einem zweiten, stumpfen Faserwinkel α in der Draufsicht. Die Holzparkettelemente 2 und 20 können auf die oben beschriebene Art und Weise hergestellt sein. Fig. 4c zeigt eine zweite mögliche Ausführungsform des erfindungsgemässen Parkettbodens mit einigen der Holzparkettelemente 2 und 20 aus Fig. 4b in der Draufsicht. Dabei sind in der ersten und dritten Zeile die Holzparkettelemente 2 mit dem spitzen Faserwinkel und in der zweiten und vierten Zeile die Holzparkettelemente 20 mit dem stumpfen Faserwinkel verlegt.4b on the left shows a wooden parquet element 2 with a first, acute fiber angle α and FIG. 4b on the right a wooden parquet element 20 with a second, obtuse fiber angle α in a top view. The wooden parquet elements 2 and 20 can be produced in the manner described above. FIG. 4c shows a second possible embodiment of the parquet floor according to the invention with some of the wooden parquet elements 2 and 20 from FIG. 4b in a top view. The wood parquet elements 2 with the acute fiber angle are laid in the first and third lines and the wood parquet elements 20 with the obtuse fiber angle in the second and fourth lines.
[0051] Fig. 4d links zeigt ein gegenüber dem Parkettelement 2 aus Fig. 4b links grösseres Holzparkettelement 2 mit dem gleichen spitzen Faserwinkel a. Fig. 4d rechts zeigt ein gegenüber dem Parkettelement 20 aus Fig. 4b rechts grösseres Holzparkettelement 20 mit dem gleichen stumpfen Faserwinkel a. Fig. 4e zeigt eine dritte mögliche Ausführungsform des erfindungsgemässen Parkettbodens mit einigen der Holzparkettelemente 2 und 20 aus Fig. 4d in der Draufsicht.FIG. 4d on the left shows a wood parquet element 2 larger than the parquet element 2 from FIG. 4b on the left with the same acute fiber angle a. FIG. 4d on the right shows a wood parquet element 20 larger than the parquet element 20 from FIG. 4b on the right with the same obtuse fiber angle a. FIG. 4e shows a third possible embodiment of the parquet floor according to the invention with some of the wooden parquet elements 2 and 20 from FIG. 4d in a top view.
[0052] Aus den Fig. 4a-4e ist zu entnehmen, dass der Winkel γ unabhängig von der Grösse der einzelnen Holzparkettelemente 2 und 20 ist, wenn diese zentrisch vergrössert oder verkleinert sind.4a-4e it can be seen that the angle γ is independent of the size of the individual wooden parquet elements 2 and 20 if they are enlarged or reduced centrally.
[0053] Fig. 5a zeigt ein drittes Brett 1 mit mehreren der erfindungsgemässen Holzparkettelementen 2 in der Draufsicht.5a shows a third board 1 with several of the wooden parquet elements 2 according to the invention in a top view.
[0054] Fig. 5b links zeigt eines der aus dem Brett 1 ausgeschnittenen Holzparkettelemente 2 in der Draufsicht mit einer ersten Faserrichtung und Fig. 5b rechts ein Holzparkettelement 20 mit einer von der ersten Faserrichtung abweichenden zweiten Faserrichtung. Das Holzparkettelement 2 in Fig. 5b links hat einen spitzen Faserwinkel α von rund 10°, wohingegen das Holzparkettelement 20 in Fig. 5b rechts einen stumpfen Faserwinkel α von rund 170° aufweist. Auch diese Holzparkettelemente 2 und 20 haben die Form einer Linse, wobei deren lange Seiten 2.1 und 2.2 weniger stark gekrümmt sind als die langen Seiten 2.1 und 2.2 der Holzparkettelemente 2 aus Fig. 1 und 2.5b on the left shows one of the wood parquet elements 2 cut out of the board 1 in a top view with a first fiber direction and FIG. 5b on the right shows a wood parquet element 20 with a second fiber direction that deviates from the first fiber direction. The wood parquet element 2 in FIG. 5b on the left has an acute fiber angle α of around 10 °, whereas the wood parquet element 20 in FIG. 5b on the right has an obtuse fiber angle α of around 170 °. These wooden parquet elements 2 and 20 also have the shape of a lens, the long sides 2.1 and 2.2 of which are less curved than the long sides 2.1 and 2.2 of the wooden parquet elements 2 from FIGS. 1 and 2.
[0055] Fig. 5c zeigt eine vierte Ausführungsform eines erfindungsgemässen Parkettbodens mit einigen der Holzparkettelemente 2 und 20 aus Fig. 5b in der Draufsicht. Mit den in den Fig. 5b gezeigten Holzparkettelementen 2 und 20 kann also ein Parkettboden hergestellt werden, der zum Beispiel das in Fig. 5c zeigte Muster aufweist. Die Anordnung der einzelnen Holzparkettelemente 2 und 20 erfolgt wie bereits oben beschrieben alternierend. Dies ist aber nicht zwingend.FIG. 5c shows a fourth embodiment of a parquet floor according to the invention with some of the wooden parquet elements 2 and 20 from FIG. 5b in a top view. With the wooden parquet elements 2 and 20 shown in FIG. 5b, a parquet floor can be produced which has, for example, the pattern shown in FIG. 5c. The individual wooden parquet elements 2 and 20 are arranged alternately, as already described above. However, this is not mandatory.
[0056] In Fig. 6a ist ein viertes Brett 1 mit mehreren der erfindungsgemässen Holzparkettelemente 2 in der Draufsicht dargestellt.6a shows a fourth board 1 with several of the wooden parquet elements 2 according to the invention in a top view.
[0057] Ähnlich wie in Fig. 5b zeigt Fig. 6b links eines der aus dem Brett 1 ausgeschnittenen Holzparkettelemente 2 in der Draufsicht mit einer ersten Faserrichtung und Fig. 6b rechts ein Holzparkettelement 20 mit einer von der ersten Faserrichtung abweichenden Faserrichtung. Das Holzparkettelement 2 in Fig. 6b links hat einen spitzen Faserwinkel α von rund 20°, wohingegen das Holzparkettelement 2 in Fig. 6b rechts einen stumpfen Faserwinkel α von rund 160° aufweist. Die Holzparkettelemente 2 und 20 haben die Form einer Raute mit vier langen Seiten 2.1,2.2,2.12 und 2.13. Die spitzen Ecken der Raute sind abgeschnitten, sodass sich zwei kurze Seiten 2.3 und 2.4 ergeben. Dies hat den Vorteil, dass die kurzen Seiten 2.3 und 2.4 beim Verlegen des Parketts als Anschlag dienen können. So kann ein Holzparkettelement 2 mit seiner kurzen Seite 2.3 ohne weiteres an die kurze Seite 2.4 eines anderen Holzparkettelements 2 gestossen werden. Würden die Holzparkettelemente 2 statt der kurzen Seiten 2.3 und 2.4 spitze Ecken aufweisen, würde die Gefahr bestehen, dass sich das Holz beim Aneinanderstossen an den spitzen Ecken verformt, was zu einer ungenauen Verlegung führen kann.Similar to FIG. 5b, FIG. 6b shows on the left one of the wood parquet elements 2 cut out of the board 1 in a top view with a first fiber direction and FIG. 6b on the right shows a wood parquet element 20 with a fiber direction that deviates from the first fiber direction. The wood parquet element 2 in FIG. 6b on the left has an acute fiber angle α of around 20 °, whereas the wood parquet element 2 in FIG. 6b on the right has an obtuse fiber angle α of around 160 °. The wooden parquet elements 2 and 20 have the shape of a diamond with four long sides 2.1.2.2.2.12 and 2.13. The pointed corners of the rhombus are cut off, so that there are two short sides 2.3 and 2.4. This has the advantage that the short sides 2.3 and 2.4 can serve as a stop when laying the parquet. Thus, a wooden parquet element 2 with its short side 2.3 can easily be pushed against the short side 2.4 of another wooden parquet element 2. If the wooden parquet elements 2 had pointed corners instead of the short sides 2.3 and 2.4, there would be a risk that the wood would deform at the pointed corners when they collided, which could lead to inaccurate laying.
[0058] Der oben genannte Vorteil gilt grundsätzlich für alle Ausführungsformen der erfindungsgemässen Holzparkettelemente 2 und 20.The above-mentioned advantage basically applies to all embodiments of the wooden parquet elements 2 and 20 according to the invention.
[0059] Fig. 6c zeigt eine vierte Ausführungsform eines erfindungsgemässen Parkettbodens mit einigen der Holzparkettelemente 2 und 20 aus Fig. 6b. Mit den in den Fig. 6b gezeigten Holzparkettelementen 2 und 20 kann ein Parkettboden hergestellt werden, der zum Beispiel das in Fig. 6c zeigte Muster aufweist. Die Anordnung der einzelnen Holzparkettelemente 2 und 20 erfolgt wie bereits oben beschrieben alternierend. Dies ist aber nicht zwingend. Stattdessen können auch lauter gleiche Holzparkettelemente 2 verlegt werden. Es ist auch möglich mit den Holzparkettelementen 2 und 20 ein anderes als das in Fig. 6c gezeigte Muster zu erzeugen. Bei dem in Fig. 6c gezeigten Parkettboden beträgt der Verlaufswinkel γ rund 20°.6c shows a fourth embodiment of a parquet floor according to the invention with some of the wooden parquet elements 2 and 20 from FIG. 6b. With the wooden parquet elements 2 and 20 shown in FIG. 6b, a parquet floor can be produced which, for example, has the pattern shown in FIG. 6c. The individual wooden parquet elements 2 and 20 are arranged alternately, as already described above. However, this is not mandatory. Instead, all the same wooden parquet elements 2 can be laid. It is also possible to produce a pattern other than the one shown in FIG. 6c with the wooden parquet elements 2 and 20. In the parquet floor shown in FIG. 6c, the development angle γ is around 20 °.
[0060] Die vorhergehende Beschreibung der Ausführungsbeispiele gemäss der vorliegenden Erfindung dient mir zu illustrativen Zwecken und nicht zum Zwecke der Beschränkung der Erfindung. Im Rahmen der Erfindung sind verschiedene Änderungen und Modifikationen möglich. So sind beispielsweise die verschiedenen in den Fig. 1 bis 6 gezeigten Komponenten der Holzparkettelemente 2 und 20 auch auf eine andere als in den Figuren gezeigte Weise miteinander kombinierbar.The previous description of the exemplary embodiments according to the present invention serves me for illustrative purposes and not for the purpose of restricting the invention. Various changes and modifications are possible within the scope of the invention. For example, the various components of the wooden parquet elements 2 and 20 shown in FIGS. 1 to 6 can also be combined with one another in a different way than shown in the figures.
Bezugszeichenliste [0061]Reference symbol list [0061]
Brettboard
1.1 Längsseite des Bretts1.1 Long side of the board
1.2 Längsseite des Bretts1.2 Long side of the board
1.3 Stirnseite des Bretts1.3 face of the board
1.4 Stirnseite des Bretts1.4 Face of the board
ParkettelementA flooring element
2.1 erste lange Seite des Parkettelements2.1 first long side of the parquet element
Geänderte PatentansprücheAmended claims
Claims (14)