BR112021022882A2 - Método de produção para reduzir a tensão residual de trilhos de aço tratados termicamente e trilhos de aço obtidos pelo mesmo - Google Patents
Método de produção para reduzir a tensão residual de trilhos de aço tratados termicamente e trilhos de aço obtidos pelo mesmoInfo
- Publication number
- BR112021022882A2 BR112021022882A2 BR112021022882A BR112021022882A BR112021022882A2 BR 112021022882 A2 BR112021022882 A2 BR 112021022882A2 BR 112021022882 A BR112021022882 A BR 112021022882A BR 112021022882 A BR112021022882 A BR 112021022882A BR 112021022882 A2 BR112021022882 A2 BR 112021022882A2
- Authority
- BR
- Brazil
- Prior art keywords
- rail
- cooling
- steel rails
- production method
- residual stress
- Prior art date
Abstract
método de produção para reduzir a tensão residual de trilhos de aço tratados termicamente e trilhos de aço obtidos pelo mesmo. a presente divulgação divulga um método de produção para reduzir a tensão residual de um trilho de aço tratado termicamente. o tratamento de resfriamento acelerado em linha é realizado em um trilho laminado a quente, em que uma temperatura inicial de resfriamento é 700 a 880°c, uma taxa de resfriamento de um boleto de trilho é de 5 a 8°c/s, uma taxa de resfriamento de um fundo de trilho é 1,5 a 3°c/s, e o resfriamento é realizado até que a temperatura do boleto de trilho seja reduzida para 460 a 550°c; em seguida, o tratamento de resfriamento lento é realizado, uma taxa de resfriamento lenta é de 0,5 a 1°c/s, e o resfriamento lento é executado até que a temperatura do boleto de trilho seja reduzida para 350 a 450°c; e a taxa de resfriamento do boleto de trilho seja mantida em 0,5 a 1°c/s, a taxa de resfriamento do fundo de trilho é controlada a 0,5 a 2°c/s, o resfriamento acelerado é interrompido quando uma diferença de temperatura entre o boleto de trilho e o fundo de trilho atinge um determinado intervalo, e o trilho de aço é naturalmente resfriado à temperatura ambiente. a presente divulgação fornece ainda trilhos de aço obtidos por este método de produção. o método fornecido pela presente divulgação pode reduzir efetivamente a tensão residual no fundo de trilho do trilho de aço, prolongar a vida útil do trilho de aço e melhorar a segurança do tráfego.
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| CN201910922813.9A CN110592355B (zh) | 2019-09-27 | 2019-09-27 | 一种降低热处理钢轨残余应力的生产方法及其所得钢轨 |
| PCT/CN2020/095377 WO2021057094A1 (zh) | 2019-09-27 | 2020-06-10 | 一种降低热处理钢轨残余应力的生产方法及其所得钢轨 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| BR112021022882A2 true BR112021022882A2 (pt) | 2022-04-12 |
Family
ID=68863987
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| BR112021022882A BR112021022882A2 (pt) | 2019-09-27 | 2020-06-10 | Método de produção para reduzir a tensão residual de trilhos de aço tratados termicamente e trilhos de aço obtidos pelo mesmo |
Country Status (3)
| Country | Link |
|---|---|
| CN (1) | CN110592355B (pt) |
| BR (1) | BR112021022882A2 (pt) |
| WO (1) | WO2021057094A1 (pt) |
Families Citing this family (14)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN110592355B (zh) * | 2019-09-27 | 2020-12-29 | 武汉钢铁有限公司 | 一种降低热处理钢轨残余应力的生产方法及其所得钢轨 |
| CN111485074B (zh) * | 2020-04-07 | 2022-02-25 | 包头钢铁（集团）有限责任公司 | 一种合金钢铸坯加热控温式缓冷去氢方法 |
| CN111349862A (zh) * | 2020-04-13 | 2020-06-30 | 攀钢集团攀枝花钢铁研究院有限公司 | 高速铁路用钢轨及其制备方法 |
| CN111575463B (zh) * | 2020-05-12 | 2022-02-01 | 武汉钢铁有限公司 | 一种降低磁浮铁路f型轨端部扭转的生产方法 |
| CN111635987B (zh) * | 2020-05-18 | 2022-02-01 | 武汉钢铁有限公司 | 一种提高f型轨全断面残余应力均匀性的生产方法 |
| CN111621631B (zh) * | 2020-05-29 | 2022-03-15 | 武汉钢铁有限公司 | 钢轨高效热处理生产方法及由该方法制得的钢轨 |
| CN112195413A (zh) * | 2020-10-19 | 2021-01-08 | 攀钢集团攀枝花钢铁研究院有限公司 | 冻融循环线耐疲劳钢轨及其生产方法 |
| CN112475821B (zh) * | 2020-11-13 | 2022-07-19 | 攀钢集团攀枝花钢铁研究院有限公司 | 一种低轨腰残余拉应力钢轨及其制备方法 |
| CN112877531B (zh) * | 2021-01-12 | 2023-01-24 | 包头钢铁（集团）有限责任公司 | 一种提高在线热处理钢轨淬火后平直度的生产控制方法 |
| CN113977211A (zh) * | 2021-10-28 | 2022-01-28 | 攀钢集团攀枝花钢铁研究院有限公司 | 一种中等强度钢轨及其生产方法 |
| CN114250349A (zh) * | 2021-12-09 | 2022-03-29 | 邯郸钢铁集团有限责任公司 | 一种提高热处理钢轨踏面硬度的方法 |
| CN114774663A (zh) * | 2022-04-27 | 2022-07-22 | 包头钢铁（集团）有限责任公司 | 一种重载铁路用百米定尺75kg/m在线热处理贝氏体钢轨的生产方法 |
| CN114854963B (zh) * | 2022-04-29 | 2023-09-05 | 武汉钢铁有限公司 | 一种低残余应力的槽型钢轨及其制备方法 |
| CN115369229A (zh) * | 2022-09-13 | 2022-11-22 | 包头钢铁（集团）有限责任公司 | 一种提高在线热处理道岔钢轨淬火后平直度的生产控制方法 |
Family Cites Families (10)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN1032656C (zh) * | 1992-11-26 | 1996-08-28 | 冶金工业部重庆钢铁设计研究院 | 钢轨热处理方法和装置 |
| JPH06279927A (ja) * | 1993-03-29 | 1994-10-04 | Nippon Steel Corp | 延性および靭性に優れた高強度レールおよびその製造法 |
| ES2671632T3 (es) * | 2012-04-23 | 2018-06-07 | Nippon Steel & Sumitomo Metal Corporation | Raíl |
| CN106086370B (zh) * | 2016-06-24 | 2018-10-09 | 成都先进金属材料产业技术研究院有限公司 | 一种降低钢轨残余应力的方法以及所得钢轨及其应用 |
| CN106086622B (zh) * | 2016-06-24 | 2017-12-15 | 攀钢集团攀枝花钢铁研究院有限公司 | 一种客货混运铁路用钢轨的热处理生产方法以及所得钢轨 |
| CN107475616B (zh) * | 2017-10-10 | 2019-01-04 | 攀钢集团研究院有限公司 | 高强韧性珠光体钢轨及其制造方法 |
| CN108504923A (zh) * | 2018-03-20 | 2018-09-07 | 包头钢铁（集团）有限责任公司 | 一种百米定尺75kg/m在线热处理钢轨及其生产方法 |
| CN109371219B (zh) * | 2018-11-30 | 2021-01-26 | 攀钢集团攀枝花钢铁研究院有限公司 | 珠光体钢轨在线处理方法 |
| CN109280760B (zh) * | 2018-11-30 | 2021-01-22 | 攀钢集团攀枝花钢铁研究院有限公司 | 珠光体钢轨处理方法 |
| CN110592355B (zh) * | 2019-09-27 | 2020-12-29 | 武汉钢铁有限公司 | 一种降低热处理钢轨残余应力的生产方法及其所得钢轨 |
-
2019
- 2019-09-27 CN CN201910922813.9A patent/CN110592355B/zh active Active
-
2020
- 2020-06-10 WO PCT/CN2020/095377 patent/WO2021057094A1/zh active Application Filing
- 2020-06-10 BR BR112021022882A patent/BR112021022882A2/pt unknown
Also Published As
| Publication number | Publication date |
|---|---|
| WO2021057094A1 (zh) | 2021-04-01 |
| CN110592355A (zh) | 2019-12-20 |
| CN110592355B (zh) | 2020-12-29 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| BR112021022882A2 (pt) | Método de produção para reduzir a tensão residual de trilhos de aço tratados termicamente e trilhos de aço obtidos pelo mesmo | |
| BR112015008461A8 (pt) | Método de processamento de uma peça de trabalho para inibir a precipitação de compostos intermetálicos | |
| BR112015020046A2 (pt) | placa de aço resistente à abrasão que possui rigidez à baixa temperatura e método de fabricação da mesma | |
| BR112017000010A2 (pt) | "método de produção de uma folha de aço revestida ou não revestida de resistência extremamente alta e folha obtida" | |
| BR112016030065A2 (pt) | método para produzir uma folha de aço e folha de aço | |
| BR112012021454A2 (pt) | método para produção de chapa de aço elétrico com grão orientado. | |
| BR112018015072A2 (pt) | processo de tratamento térmico e dispositivo de tratamento térmico | |
| BR112017004212A2 (pt) | mola ou barra de torção, método para a produção de uma mola e/ou de uma barra de torção, e, aplicação de um arame de aço | |
| BR112017000023A2 (pt) | ?método para produzir uma lâmina de aço revestida e lâmina de aço revestida? | |
| BR112017008044A2 (pt) | método para a produção de um aço nitretado para embalagem | |
| BR112012015515B8 (pt) | Processo de tratamento termomecânico para a produção de chapa grossa e chapa grossa obtida | |
| BR112018016231A2 (pt) | método para produzir chapa de aço elétrico de grão orientado | |
| BR112017028512A2 (pt) | processo de tratamento térmico para correntes de amarração de nível r6 | |
| BR112018014951A2 (pt) | processo e dispositivo para o tratamento térmico de um componente metálico | |
| BR112015003767A2 (pt) | método para fabricação de estabilizador, e dispositivo de aquecimento | |
| BRPI0606382A2 (pt) | processo para laminação-fundição com velocidade de fundição aumentada e laminação a quente subseqüente de biletes de metal, especialmente de material de aço relativamente fino, e dispositivo de laminação-fundição | |
| CN105855299A (zh) | 一种钢的轧制方法及使用该方法获得的钢 | |
| MX2016014415A (es) | Laminacion hibrida refrigerada por aceite y agua. | |
| MX2020004626A (es) | Lamina de acero laminada en caliente y metodo para producir la misma. | |
| BR112014008002A2 (pt) | placa de aço e método de produção da mesma | |
| CN106493169A (zh) | 一种轧钢的生产工艺 | |
| BR112017002702A2 (pt) | método de fabricação de trilho de cabeça endurecida e aparelho de fabricação | |
| MX2021015958A (es) | Metodo de tratamiento termico de una banda o fleje de acero laminado en frio de alta resistencia. | |
| MX2021009093A (es) | Metodo para producir una lamina o tira a partir de una aleacion de aluminio y una lamina, tira o parte formada producida de esta manera. | |
| MX2020003344A (es) | Metodo y sistema para formar material en bruto de aleacion de aluminio. |