BR0005133A - Chapas de aço, chapas de aço imersas a quente, e chapas de aço ligadas imersas a quente bem como método para produção das mesmas - Google Patents

Chapas de aço, chapas de aço imersas a quente, e chapas de aço ligadas imersas a quente bem como método para produção das mesmas

Info

Publication number
BR0005133A
BR0005133A BR0005133-0A BR0005133A BR0005133A BR 0005133 A BR0005133 A BR 0005133A BR 0005133 A BR0005133 A BR 0005133A BR 0005133 A BR0005133 A BR 0005133A
Authority
BR
Brazil
Prior art keywords
steel sheets
hot
dipped
steel
well
Prior art date
Application number
BR0005133-0A
Other languages
English (en)
Other versions
BR0005133B1 (pt
Inventor
Kazuaki Kyono
Shigeru Umino
Akio Tosaka
Keiji Nishimura
Hiromasa Hayashi
Original Assignee
Kawasaki Steel Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP05505899A external-priority patent/JP3555483B2/ja
Priority claimed from JP11221499A external-priority patent/JP3606102B2/ja
Priority claimed from JP32253799A external-priority patent/JP3835083B2/ja
Application filed by Kawasaki Steel Co filed Critical Kawasaki Steel Co
Publication of BR0005133A publication Critical patent/BR0005133A/pt
Publication of BR0005133B1 publication Critical patent/BR0005133B1/pt

Abstract

Patente de Invenção:<B>"CHAPAS DE AçO, CHAPAS DE AçO IMERSAS A QUENTE, E CHAPAS DE AçO LIGADAS IMERSAS A QUENTE BEM COMO MéTODO PARA PRODUçãO DAS MESMAS"<D>. Esta invenção pode formar suficientemente uma camada interna de óxido em uma porção da camada de superfície de uma matriz de ferro de uma chapa de aço laminando-se a quente um aço base e submetendo a um tratamento térmico a uma faixa de temperatura de 650-950°C em uma atmosfera que não cause substancialmente redução enguanto é aderida a uma escama de superfície preta sem se importar com a composição química ou com a história da produção, ou mesmo quando um aquecimento tipo radiação de um tubo radial ou similar é usado em um recozimento de recristalização antes do tratamento de imersão a quente, e então excelentes propriedades de imersão a quente e de tratamento de conversão podem ser dadas a uma chapa de aço para imersão a quente.
BRPI0005133-0A 1999-02-25 2000-02-21 Chapas de aço e chapas de aço ligadas, imersas a quente, e método para produção das mesmas BR0005133B1 (pt)

Applications Claiming Priority (9)

Application Number Priority Date Filing Date Title
JP11/48142 1999-02-25
JP4814299 1999-02-25
JP11/55058 1999-03-03
JP05505899A JP3555483B2 (ja) 1999-03-03 1999-03-03 加工性に優れた冷延鋼板、溶融めっき鋼板およびそれらの製造方法
JP11221499A JP3606102B2 (ja) 1999-04-20 1999-04-20 熱延鋼板、溶融めっき熱延鋼板およびそれらの製造方法
JP11/112214 1999-04-20
JP11/322537 1999-11-12
JP32253799A JP3835083B2 (ja) 1999-02-25 1999-11-12 冷延鋼板および溶融めっき鋼板ならびにそれらの製造方法
PCT/JP2000/000975 WO2000050659A1 (fr) 1999-02-25 2000-02-21 Plaque d'acier, plaque d'acier obtenue par immersion a chaud et alliage de plaque d'acier obtenue par immersion a chaud et leurs procedes de production

Publications (2)

Publication Number Publication Date
BR0005133A true BR0005133A (pt) 2001-01-09
BR0005133B1 BR0005133B1 (pt) 2014-11-04

Family

ID=27462152

Family Applications (1)

Application Number Title Priority Date Filing Date
BRPI0005133-0A BR0005133B1 (pt) 1999-02-25 2000-02-21 Chapas de aço e chapas de aço ligadas, imersas a quente, e método para produção das mesmas

Country Status (8)

Country Link
US (1) US6398884B1 (pt)
EP (1) EP1076105A4 (pt)
KR (1) KR100679796B1 (pt)
CN (1) CN1170954C (pt)
BR (1) BR0005133B1 (pt)
CA (1) CA2330010C (pt)
TW (1) TW460583B (pt)
WO (1) WO2000050659A1 (pt)

Families Citing this family (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TW504519B (en) 1999-11-08 2002-10-01 Kawasaki Steel Co Hot dip galvanized steel plate excellent in balance of strength and ductility and in adhesiveness between steel and plating layer, and method for producing the same
BR0107195B1 (pt) * 2000-09-12 2011-04-05 chapa de aço imersa a quente de alta resistência à tração e método para produzì-la.
JP4886118B2 (ja) * 2001-04-25 2012-02-29 株式会社神戸製鋼所 溶融亜鉛めっき鋼板
FR2828888B1 (fr) * 2001-08-21 2003-12-12 Stein Heurtey Procede de galvanisation a chaud de bandes metalliques d'aciers a haute resistance
JP4729850B2 (ja) * 2003-02-10 2011-07-20 Ｊｆｅスチール株式会社 めっき密着性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法
ES2347435T3 (es) * 2003-03-31 2010-10-29 Nippon Steel Corporation Chapa de acero recubierta en caliente con cinc aleado y metodo para su produccion.
KR20050118306A (ko) * 2003-04-10 2005-12-16 신닛뽄세이테쯔 카부시키카이샤 고강도 용융 아연 도금 강판 및 그 제조 방법
JP3934604B2 (ja) * 2003-12-25 2007-06-20 株式会社神戸製鋼所 塗膜密着性に優れた高強度冷延鋼板
KR100711356B1 (ko) * 2005-08-25 2007-04-27 주식회사 포스코 가공성이 우수한 아연도금용 강판 및 그 제조방법
BE1017086A3 (fr) * 2006-03-29 2008-02-05 Ct Rech Metallurgiques Asbl Procede de recuit et preparation en continu d'une bande en acier a haute resistance en vue de sa galvanisation au trempe.
JP5058769B2 (ja) * 2007-01-09 2012-10-24 新日本製鐵株式会社 化成処理性に優れた高強度冷延鋼板の製造方法および製造設備
WO2008126945A1 (ja) * 2007-04-11 2008-10-23 Nippon Steel Corporation 低温靱性に優れたプレス加工用溶融めっき高強度鋼板およびその製造方法
US20100291305A1 (en) * 2007-12-28 2010-11-18 United States Gypsum Company Decreased evaporation with retarder for a high water to stucco radio lightweight board
KR101010971B1 (ko) * 2008-03-24 2011-01-26 주식회사 포스코 저온 열처리 특성을 가지는 성형용 강판, 그 제조방법,이를 이용한 부품의 제조방법 및 제조된 부품
KR20100076744A (ko) * 2008-12-26 2010-07-06 주식회사 포스코 강판의 소둔 장치, 도금 품질이 우수한 도금 강판의 제조 장치 및 이를 이용한 도금 강판의 제조방법
JP5779847B2 (ja) * 2009-07-29 2015-09-16 Ｊｆｅスチール株式会社 化成処理性に優れた高強度冷延鋼板の製造方法
KR101253703B1 (ko) * 2012-10-26 2013-04-12 주식회사 에스에이씨 배치식 소둔 열처리 설비
KR101482345B1 (ko) * 2012-12-26 2015-01-13 주식회사 포스코 고강도 열연강판, 이를 이용한 용융아연도금강판, 합금화 용융아연도금강판 및 이들의 제조방법
MX2016002449A (es) 2013-08-26 2016-06-24 Jfe Steel Corp Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
KR20160085830A (ko) 2013-12-10 2016-07-18 아르셀러미탈 강판의 어닐링 방법
WO2016074057A1 (pt) * 2014-11-12 2016-05-19 Companhia Siderúrgica Nacional Produto laminado a quente em aços longos e uso do mesmo
EP3382049B1 (en) * 2015-11-26 2023-05-10 JFE Steel Corporation Method for manufacturing cold-rolled steel sheet for high-strength hot-dip galvanized steel sheet, method for manufacturing high-strength hot-dip galvanized steel sheet
KR102075182B1 (ko) * 2015-12-24 2020-02-10 주식회사 포스코 도금성이 우수한 고강도 용융 아연계 도금 강재 및 그 제조방법
CN106119687B (zh) * 2016-06-28 2018-01-26 宝山钢铁股份有限公司 一种高表面质量的免酸洗热轧带钢及其制造方法
CN106244923B (zh) * 2016-08-30 2018-07-06 宝山钢铁股份有限公司 一种磷化性能和成形性能优良的冷轧高强度钢板及其制造方法
DE102016218957A1 (de) * 2016-09-30 2018-04-05 Thyssenkrupp Ag Temporäre Korrosionsschutzschicht
CN109425319B (zh) * 2017-08-25 2020-06-23 宝山钢铁股份有限公司 一种检测酸洗过程对横向断面影响程度的方法
CN111926248B (zh) * 2020-07-14 2021-11-30 辽宁科技学院 一种添加Ce合金的热冲压成形钢及热冲压成形工艺
CN111926252B (zh) * 2020-07-31 2022-01-18 马鞍山钢铁股份有限公司 一种深冲用途的热轧酸洗钢板及其生产方法

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2411891A1 (fr) * 1977-12-14 1979-07-13 Siderurgie Fse Inst Rech Procede de traitement thermique de pieces d'acier destinees a etre recouvertes superficiellement a chaud par un autre compose
JPS58110659A (ja) * 1981-12-25 1983-07-01 Nippon Kokan Kk <Nkk> 深絞り用亜鉛めつき鋼板およびその製造方法
JP3238211B2 (ja) * 1992-10-02 2001-12-10 新日本製鐵株式会社 焼付硬化性と非時効性とに優れた冷延鋼板あるいは溶融亜鉛メッキ冷延鋼板の製造方法
JP3354610B2 (ja) * 1992-12-15 2002-12-09 川崎製鉄株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
US5954896A (en) * 1995-02-23 1999-09-21 Nippon Steel Corporation Cold rolled steel sheet and galvanized steel sheet having improved homogeneity in workability and process for producing same
JP3020846B2 (ja) * 1995-07-31 2000-03-15 川崎製鉄株式会社 高張力溶融亜鉛めっき鋼板の製造方法
JPH09287064A (ja) * 1996-04-19 1997-11-04 Kawasaki Steel Corp Ｐ添加鋼の合金化溶融亜鉛めっき鋼板の製造方法
CA2215110C (en) * 1997-01-13 2001-08-14 Kawasaki Steel Corporation Zinc and zinc-alloy hot-dip-coated steel sheet having decreased bare spots and excellent coating adhesion and a method for manufacturing the same
JP3468004B2 (ja) * 1997-01-16 2003-11-17 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき熱延鋼板
JPH10287964A (ja) * 1997-04-14 1998-10-27 Nippon Steel Corp パウダリング性に優れた合金化溶融亜鉛メッキ鋼板およびその製造方法

Also Published As

Publication number Publication date
CN1170954C (zh) 2004-10-13
BR0005133B1 (pt) 2014-11-04
EP1076105A4 (en) 2009-01-07
KR100679796B1 (ko) 2007-02-07
TW460583B (en) 2001-10-21
CA2330010C (en) 2008-11-18
US6398884B1 (en) 2002-06-04
CN1294637A (zh) 2001-05-09
EP1076105A1 (en) 2001-02-14
WO2000050659A1 (fr) 2000-08-31
CA2330010A1 (en) 2000-08-31
KR20010042985A (ko) 2001-05-25

Similar Documents

Publication Publication Date Title
BR0005133A (pt) Chapas de aço, chapas de aço imersas a quente, e chapas de aço ligadas imersas a quente bem como método para produção das mesmas
ES2393093T3 (es) Procedimiento para la fabricación de un componente templado de un acero templable
RU2015112317A (ru) Способ изготовления деформационно-упрочнённых стальных деталей с покрытием и листы с предварительно нанесённым покрытием для изготовления этих деталей
RU2472868C2 (ru) Сталь для высокопрочных деталей из лент, листов или труб с превосходной деформируемостью и особо пригодная для способов высокотемпературного нанесения покрытий
JP2000038640A5 (pt)
DK0971044T3 (da) Overtrukket varmvalset og koldvalset stålplade med meget høj modstand efter termisk behandling
BR112014000086A2 (pt) método para produção de folha de aço laminada a frio
BR0107195A (pt) Chapa de aço imersa a quente de alta resistência à tração e método para produzì-la
BR9711091A (pt) Aço para estiramento profundo de alta resistência desenvolvida por reação com amÈnia
BR9612531A (pt) Aço contendo vanádio endurecido por cozimento
ATE62280T1 (de) Verfahren zur herstellung einer fuer waermeaustauscher geeigneten hochtemperaturbestaendigen legierung.
ATE232965T1 (de) Heizelement für einen regenerativ-wärmetauscher und verfahren zum herstellen eines heizelementes
ES2180532T3 (es) Procedimiento de fabricacion de chapas delgadas destinadas a embuticion.
TW370567B (en) Bake hardenable vanadium containing steel effect amount of vanadium in low carbon steels capable of producing an improved bake hardenable product
CN103692726B (zh) 无铬绝缘涂层电工钢带及其生产方法
ES2111380T3 (es) Procedimiento de revestimiento por inmersion y sin formacion de aleacion de una chapa de acero de bajo contenido intersticial.
BR9914517A (pt) Utilização de uma composição para a esmaltagem, que permite evitar as unhadas e chapa esmaltada obtida
CN107326163A (zh) 一种贝氏体区等温+热冲压变形生产先进高强钢的方法
KR910018560A (ko) 저철손 입자 방향성 실리콘 강판의 제조방법
RU96113845A (ru) Способ производства анизотропной электротехнической стали
BR9913530A (pt) Processo para preparação de tiras ou chapas laminadas a frio
JP3477049B2 (ja) スケール密着性が優れた厚鋼板の製造法
TWI245811B (en) Chemically processed steel sheet improved in corrosion resistance
TISHCHENKO et al. INCREASING THE LEVEL OF PHYSICAL AND MECHANICAL PROPERTIES OF COLD-ROLLED STEEL OF THE BRAND DC01 IN ORDER TO ENSURE ITS REQUIREMENTS EN 10130 IN THE CONDITIONS OF PJSC" ZAPORIZHSTAL"
ES469147A1 (es) Un procedimiento de tratamiento termico en continuo de cha- pas de acero laminadas en frio

Legal Events

Date Code Title Description
B07A Application suspended after technical examination (opinion) [chapter 7.1 patent gazette]
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B25D Requested change of name of applicant approved

Owner name: JFE STEEL CORPORATION (JP)

B25G Requested change of headquarter approved

Owner name: JFE STEEL CORPORATION (JP)

B09X Republication of the decision to grant [chapter 9.1.3 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 10 (DEZ) ANOS CONTADOS A PARTIR DE 04/11/2014, OBSERVADAS AS CONDICOES LEGAIS.

B21F Lapse acc. art. 78, item iv - on non-payment of the annual fees in time

Free format text: REFERENTE A 16A ANUIDADE.

B24J Lapse because of non-payment of annual fees (definitively: art 78 iv lpi, resolution 113/2013 art. 12)

Free format text: EM VIRTUDE DA EXTINCAO PUBLICADA NA RPI 2364 DE 26-04-2016 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDA A EXTINCAO DA PATENTE E SEUS CERTIFICADOS, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013.