AU2017249647B2

AU2017249647B2 - Method for the powder-metallurgical production of components from titanium or titanium alloys

Info

Publication number: AU2017249647B2
Application number: AU2017249647A
Authority: AU
Inventors: Markus Lang; Matthias SCHARVOGEL; Ulf VIEHÖFER; Wendelin Winkelmüller
Original assignee: Element 22 GmbH
Current assignee: Element 22 GmbH
Priority date: 2016-04-14
Filing date: 2017-04-04
Publication date: 2019-09-05
Anticipated expiration: 2037-04-04
Also published as: HUE037106T2; MY183957A; SG11201808189VA; CN109311086B; RU2018139866A; IL262260B; ES2667872T3; KR102341739B1; SA518400144B1; WO2017178289A1; NZ746808A; PT3231536T; CN109311086A; IL262260A; KR20180134953A; NO3231536T3; CA3018808A1; CA3018808C; EP3231536B1; JP2019516021A

Abstract

A method for the powder-metallurgical production of a component from titanium or a titanium alloy is disclosed. In this method, following the customary procedure, first a green part is formed by using metal powder formed from titanium or the titanium alloy and is densified and compacted in a subsequent sintering step. What makes the method according to the invention special is that metal powder of titanium or the titanium alloy with an average particle size of < 25

Description

Method for the powder-metallurgical production of components from titanium or titanium alloys

The present invention relates to a method for the powder-metallurgical production of a component from titanium or a titanium alloy, wherein first, using metal powder produced from titanium or the titanium alloy, a green part is formed and this is densified and compacted in a subsequent sintering step.

Various powder-metallurgical methods for producing true-to-size titanium components (here and in the following, “components from titanium” will be used here and in the following as a simplified term for components made from titanium (pure titanium) or one or more titanium alloys) are known, where in all methods, first a green part is produced, and this is densified and compacted in a subsequent sintering step. The green part can be produced in various ways, especially using additive production methods, metal powder injection molding, extrusion methods and non-pressurized powder-metallurgical production methods.

Because of the excellent properties of the material, titanium, plus the efficient and economical production method, the powder-metallurgical production of titanium is becoming increasingly more widely used. The good biocompatibility and the high specific strength of the material, titanium, play an important role especially in applications in medical engineering and air and space technology. The economically most significant alloy with sales figures accounting for more than 50% of the total titanium market I Ti6A14V.

As a rule, the following steps must be executed to produce a powder-metallurgically processed titanium component:

a) forming

b) debinding

c) sintering

The objective of forming is to bring the titanium powder particles into the tightest possible packing in a form close to the final contour. In this step, depending on the method employed, additives are used which must be removed in one or more subsequent debinding step(s). In the subsequent process step, frequently also the final one, sintering, the powder particles are consolidated by material transport.

Because of the high reactivity of titanium, all processing steps must take place under special process conditions. In patent EP 1 119 429 Bl [1], Gerling et al. describe necessary process conditions for sintering titanium. The combined implementation of debinding and sintering in a combined furnace design is described by Blum in EP 1 496 325 A2 [2],

Titanium has two crystal modifications. The hexagonal a phase, which with pure titanium and normal pressure is present up to a temperature of 882.5°C, and the cubic space-centered β phase, which with pure titanium and normal pressure occurs above the aforementioned temperature. The presence of the different phases at room temperature is used to classify titanium alloys into α-Ti, (α+β)-Τί and β-Ti alloys. T16A14V, for example, is an (α+β)-η11ογ, i.e., both phases are present in the grain structure at room temperature. To produce components with a generally desired density >97% in the process of sintering titanium and titanium-alloy components, sintering temperatures of about 1100-1400°C at a sintering duration of about 2-5 h are needed. For pure titanium and T16A14V this means that the materials are processed in the βphase region, which leads to a massive β -grain growth.

In EP 1 119 429 Bl [1], Gerling et al. describe that the grain structure that becomes established has a β-grain growth of about 150 pm. Here, the nomenclature according to Sieniawski et al. [3], shown in Fig. 1, is used to describe the sizes of the various structures in the lamellar (α+β) alloys. The following designations are used:

D: grain size of the primary β phase d: the size of a parallel α-lamella colony t: the width of an a-lamella

In contrast to reforming processes, forming takes place as the first step on the powder metallurgy route. In the next process step, sintering, the compacted titanium alloy, previously brought into shape, is produced. In contrast to standard processing approaches, because of the reverse sequence of the process steps (1. forming, 2. material consolidation) in the powder metallurgy approach, the possibility of refining or optimizing the grain structure of the metal and thus its material properties by thermal/mechanical working before the forming step does not exist. For powder-metallurgical methods for producing components from titanium and/or titanium alloys, precisely the process-determined inverse sequence, combined with the very limited influence on the grain structure that develops during the familiar sintering process, is a limiting factor. As an example: the grain structure of a T16A14V sample produced in the standard manner from titanium powders commonly used in the prior art (with powder grain sizes <45 pm) and sintered under sintering conditions typically used in the prior art is shown in Fig. 2. Here it is possible to recognize the typical lamellar mixed grain structure for titanium components produced in the known way by powder metallurgy and sintered, made up of a phases and β phases, the (α+β) grain structure, with a mean primary β-phase grain size (D) of about 190 pm.

The production of powder-metallurgically processed titanium and titanium alloys with small grain sizes is described in US 4,601,874 [4] by Marty et al. Through the targeted admixtures of S,

P, B, As, Se, Te, Y and lanthanoids, during the consolidation process a material is produced with grain sizes smaller by two orders of magnitude than the titanium powder particles used. The drawback of this approach is that the use of titanium and titanium alloys is widespread precisely

2017249647 18 Jul 2019 in strictly regulated market segments. For these application purposes, the chemical compositions of the material and its mechanical properties are regulated by standards. For example, the material compositions and mechanical properties of Ti6A14V and pure titanium are regulated in the standards ASTM F2885 and ASTM F2889 respectively.

An additional procedure for producing fine-grained titanium and such titanium alloys by powder metallurgy is described in WO 2012/148471 Al. Here a green part made from titanium (alloy) powder with grain sizes of less than 325 mesh (less than 44 pm) is produced and then subjected to a multistep process of compaction and forming. In a first step the green part is sintered in a hydrogen atmosphere at temperatures of 1100 to 1500°C; in the embodiments, the processing temperature is always given as 1200°C. In this process titanium material in the β-phase forms. In a subsequent step of controlled cooling, a phase transformation occurs, in which restructuring occurs in the β-grains, resulting in a phase mixture of fine a-grains, β-grains and δ- phases. Then in a final step, the hydrogen must be expelled from the component obtained, which is done by applying a vacuum. With this procedure especially the use of hydrogen is especially problematic, since this gas can only be expelled from the component with great effort and often not completely expelled. Negative effects on the material properties and the stability of the material have been blamed on hydrogen remaining in the grain structure of the material. Outgassing from residual hydrogen from the finished component in various applications is also anything but desirable.

Any discussion of documents, acts, materials, devices, articles or the like which has been included in the present specification is not to be taken as an admission that any or all of these matters form part of the prior art base or were common general knowledge in the field relevant to the present disclosure as it existed before the priority date of each of the appended claims.

Throughout this specification the word comprise, or variations such as comprises or comprising, will be understood to imply the inclusion of a stated element, integer or step, or group of elements, integers or steps, but not the exclusion of any other element, integer or step, or group of elements, integers or steps.

One goal generally pursued with the invention is that of creating the possibility, in the case of powder-metallurgically produced and sintered titanium components, of manipulating the grain structure and optimizing the material properties. In particular the intention was to make it possible to adapt the material properties to the specific use case directly in the sintering process and/or to create, during the sintering process, an

2017249647 18 Jul 2019

3A optimal starting point for further thermal treatment steps after sintering. For example, it should be possible, by modifying the sintering conditions, to create a primarily globular grain structure with high ductility.

Disclosed herein is a process for the powder metallurgical production of a component from titanium or a titanium alloy, wherein a green part is first formed by using metal powder formed from titanium or the titanium alloy and this is then compacted and solidified in a subsequent sintering step, wherein for the production of the green part metal powder of titanium or the titanium alloy is used, with an average particle size <25 pm, as measured by laser beam scattering according to ASTM B822 10 and that the sintering step is performed at a sintering temperature up to maximum of 1100 °C, in an atmosphere with reduced pressure compared to the normal pressure.

An essential prerequisite for implementing the process according to the invention and creating the possibility of influencing the material properties in the sintering process is the use of metal powder, produced from titanium or a titanium 15 alloy, with a mean grain size of <25 pm, so-called fine powder. In such fine powder used for the process according to the invention, the maximum grain size may in particular be <30 pm. The maximum grain size is specified as a limit value by the manufacturers of such fine powders. At the same time, a small fraction of particles in such batches can always have grain sizes above this limit. Such a fraction, as a rule, is generally specified as a maximum of 1 to a maximum of 5 wt.-%.

The mean grain size may advantageously even be lower, especially <20 pm, advantageously <10 pm and particularly preferably even <5 pm. The smaller the grain size of the metal powder is, the more readily high final densities can be achieved even at sintering temperatures markedly reduced compared to the relatively high sintering temperatures previously used.

The measurement of the grain sizes essential for the invention and the distribution thereof is performed by grain size testing using laser diffraction according to ASTM B822-10 (published 2010), valid at the time of this application. The grain size distribution is determined by wt.-% and according to D10/D50/D90, wherein D50 is the mean grain size. Specifically, the grain sizes given here in comparison tests were measured using the COULTER® LS grain size analyzer made by Beckman Coulter and evaluated using the Fraunhofer theory according to ASTM B822-

10.

For spherical particles, the grain size in the sense of the invention is specified as the particle diameter. For nonspherical particles, the grain size corresponds to the projected maximum particle dimension.

As a result of the reduced grain size, the surface area in the nonconsolidated component available for the sintering process increases, and thus so does the stored surface energy. Since the reduction of this energy is the driving force in the sintering process, the sintering process can then take place using little thermal energy.

An additional advantage of using fine powders of the sizes indicated above for forming the green part is that more powder particles can be introduced per unit volume. In addition to the enlarged surface, this leads to a higher number of contact points per unit volume, as shown in Fig. 3. There, in a schematic representation, the effect of reducing the grain size by half (using the example of spherical particles) on the particle count to fill a defined volume is shown.

The contact points of the particles in turn are the starting point and a necessary condition for the sintering process, which is driven by diffusion processes. The increased number of such contact points per unit volume therefore improves the starting conditions for the sintering process.

Through the use according to the invention of fine powders with mean grain sizes <25 pm, when considering the ideal packing density in addition to the aforementioned advantages, the result also occurs that the volume enclosed by the powder particles, as shown in an idealized representation in Fig. 4, is decreased. In Fig. 4, in a schematic representation the decrease in size of the hollow space between adjacent particles is illustrated by reducing the grain size by half (using the example of spherical particles). Since this hollow space must be closed to achieve the

- high - material density desired for the component following the sintering process must be closed by material transport during the sintering process, a smaller volume to be covered is an additional decisive reason for an improvement in the process result.

The sintering step typically takes place in a reduced-pressure atmosphere. This can be a vacuum with a pressure of < 10^-3 mbar, especially < 10^-5 mbar. However, it may also be a reduced-pressure inert gas atmosphere with a pressure of, e.g., < 300 mbar. Argon gas in particular is considered as the inert gas here.

The sintering temperatures according to the invention are below 1100°C. They can in particular be a maximum of 1050°C, a maximum of 1000°C, and even a maximum of only 950°C. Preferably, however, to achieve a good sintering result, the sintering temperature selected advantageously should not be below 860°C. The sintering temperature may be kept uniform. In particular, however, it is also possible and falls within the meaning of the invention to vary the temperature during the sintering process. The sintering temperature is defined here as the temperature that the workpiece to be sintered has undergone. Depending on the sintering unit, in the unit control, an adapted process temperature is to be selected, which distinguishes the process temperature measured at a distance remote from the workpiece from the sintering temperature undergone by the workpiece.

The duration of sintering may especially be < 3.5 h, often also < 3 h or even < 2.5 h. However, it was found that as a rule, for achieving good results, the sintering time should amount to at least 1 hour, preferably at least 2 hours.

After the sintering step, components from titanium or titanium alloys produced with the method of the invention generally have a final density of >97%. However, final densities above 98% may also be reached, even > 99%.

To achieve a globular grain structure, the titanium components are sintered at less than the βtransition temperature (e.g., at a temperature 30°C below the β-transition temperature.

For example, in initial experiments at a sintering temperature of 950°C, which is below the βtransition temperature, and with a sintering duration of less than three hours, components with a final density of >97% were produced. These had a globular grain structure with an α-grain size on average of 10.1 pm and a max. size of 29 pm. The grain structure of this material is shown in Fig. 5. These grain sizes fall in the order of magnitude of the powder particles used.

According to the literature, the β-transition temperature of T16A14V falls in the range of

985°C to 1015°C [3; 5], This relatively wide range given in the literature is attributable, on one hand, to the distribution of the alloying elements in the titanium alloys. On the other hand, the ambient pressure is an additional influential factor. For example, Huang et al. describe that as a result of elevated process pressures (1500 bar), a reduction of the a-transition temperature can be observed in the alloy Ti4A18Nb [6],

The inventors now believe that depending on the process conditions, shifts in the β -transition temperature of only a maximum of 20° C will be observable due to pressure variations.

For creating a bimodal structure, the components were sintered close to the β-transition temperature, but still below this.

For example, in order also to produce the lamellar grain structure with reduced primary βphase grain size of the T16A14V alloy, which is also advantageous for many use cases, initially samples were produced in which the titanium components were sintered at a sintering temperature of 1000°C (Fig. 6). As shown by studies of the samples obtained with respect to the grain structure formed, this sintering temperature was still below the β -transition temperature, although only slightly. The bimodal grain structure formed is composed of globular a-structure and small portions of lamellar (α+β) structures, wherein the mean β-grain size is 81 pm.

The density measurement was performed according to the specifications of ASTM B962 and ASTM B311. The grain size determination was performed according to the provisions of ASTM El 12.

For creating a lamellar grain structure with the smallest possible grain size of the primary β-phase grains, the components were largely sintered, i.e., for the greatest part of the time, below the β—transition temperature, but with a minimal hold time that remained below 30 min, preferably below 20 min, especially below 10 min, and also above the β-transition temperature in phases, so that the β -phase is entirely present, in order thus to create the lamellar grain structure, but also the primary β -phase grain does not exceed the size range given in claim 16. The sintering above the β-transition temperature always took place at a temperature in excess of 1015°C. This temperature was always kept below 1080°C, but advantageously was below 1040°C and especially < 1020°C was selected.

The possibilities mentioned above for influencing the phase composition in the sintered material by systematic adjustment of the sintering conditions at sintering temperatures below 1100°C, especially primarily below the β-transition temperature, present a particular advantage of the process according to the invention. The prerequisite for this variability is that sufficiently compact titanium components can be produced below the β -transition temperature, which is possible, as the inventors recognized, based on the use of the fine powder, essential to the invention, with grain sizes below <30 pm.

Thus it has been shown that according to the method of the invention, powdermetallurgical moldings from titanium and titanium alloys can be sintered at sintering temperatures below the usual mark of beyond 1100°C, generally 1200°C or more, advantageously below the β -transition temperature, and thereby components with good structural and other material properties can be obtained. It was possible to show that at distinctly lower set sintering temperatures compared with the sintering temperatures customary in the prior artunexpectedly - components with high final densities of >97% can be obtained. In particular it was shown that the method according to the invention makes it possible to vary the grain structure of the titanium component in the sintering process and drastically reduce the grain size, which makes it possible to optimize the mechanical properties of the components, e.g., the tensile strength, ductility and fatigue strength.

For example, within the scope of the invention, a particularly low temperature may also be selected for sintering, e.g., a temperature below 950°C, can be selected, and if the desired material density in the finished component (generally >97%) is not yet achieved in such a sintering step, further compaction of the material can be performed in the subsequently performed pressing step, in which the material is subjected to pressure and optionally a temperature, especially by cold isostatic pressing (CIP) or hot isostatic pressing (HIP). Here, for example, the material density after sintering may be at <97%, and it may be compacted to >97% by the pressing step after sintering.

In addition, following the sintering step, components produced according to the method of the invention may be subjected to additional thermal aftertreatments to further modify the properties of the materials. Such additional thermal aftertreatments can, for example, be one or more of the following methods: hot isostatic pressing (HIP), quench, uniform rapid quench (URQ).

The lower sintering temperature compared to the sintering temperatures from the prior art also result in additional environmental/financial and process technology advantages. On one hand, less thermal energy is required in the sintering process, leading to lower costs but also to shorter processing times. On the other hand, the method in accordance with the invention performed with reduced sintering temperature also allows the use of how-wall furnace designs which are once again more economical than furnaces designed for process temperatures >1100°C, where cold-wall furnaces are typically used.

The selective combination of fine powders with mean grain size <25 pm, preferably also with maximum grain sizes <30 pm, and reduced sintering temperatures compared with the prior art, to be classified as low, allows the unrivaled manipulation of the grain structure and thus of the material properties.

The figures mentioned above show:

Fig. 1 a representation of a lamellar (α+β) grain structure of a T16A14V sample with description of the gran structure fractions according to Sieniawski et al. [3];

Fig. 2 an enlarged photomicrograph of a standard sintered T16A14V sample, produced by powder-metallurgically using powder particles <45 pm and standard-sintered and confirms a lamellar (α+β) grain structure for this;

Fig. 3 a schematic representation of the effect of reducing the grain size by half (using the example of spherical particles) on the number of particles required to fill a defined volume;

Fig. 4 a schematic representation of the reduction in size of the hollow space between adjacent particles due to reducing the grain size by half (using the example of spherical particles);

Fig. 5 an enlarged polished micrograph section of a powder-metallurgically produced and sintered T16A14V sample made from powder particles <20 pm, confirming the formation of a distinct globular a-structure; and

Fig. 6 an enlarged polished micrograph section of a powder-metallurgically produced and sintered T16A14V sample made from powder particles <20 pm, confirming the formation of a bimodal grain structure with a globular a-structure and distinct lamellar (α+β) grain structure.

References:

[1] R. Gerling, T. Ebel, T. Hartwig: Method for producing components by metal powder injection molding. European patent EPl 119429B1, 2003.

[2] H.-J. Blum: Method for combined debinding and sintering of glass-ceramic, ceramic and metal molded parts. European Patent EP1496325A2, 2004.

[3] J. Sieniawski, W. Ziaja, K. Kubiak, M. Motyka: Microstructure and Mechanical Properties of High Strength Two-Phase Titanium Alloys. Materials Science / Metals and Nonmetals “Titanium Alloys - Advances in Properties Control,” 2013, ISBN 978-953-51-1110-8.

[4] M. Marty, H. Octor, A. Walder: Process for forming a titanium base alloy with small grain size by powder metallurgy. United States Patent U.S. 4,601,874, 1986.

[5] J. Lindemann: Titanium alloys, Laboratory Course on Lightweight Construction Materials, Department of Metals Science and Materials Technology Brandenburg Technical University Cottbus, 2012.

[6] A. Huang, D. Hu, M.H. Loretto, J. Mei, X, Wu: The influence of pressure on solid-state transformations in Ti-46Al-8Nb. Scripta Materialia, Vol. 56, 4^th Ed., 2007, p. 253-324.

Claims

1. A process for the powder metallurgical production of a component from titanium or a titanium alloy, wherein a green part is first formed by using metal powder formed from titanium or the titanium alloy and this is then compacted and solidified in a subsequent

5 sintering step, wherein for the production of the green part metal powder of titanium or the titanium alloy is used, with an average particle size <25 pm, as measured by laser beam scattering according to ASTM B822 and that the sintering step is performed at a sintering temperature up to maximum of 1100 °C, in an atmosphere with reduced pressure compared to the normal pressure.

2. The method according to claim 1, wherein the maximum particle size of the metal powder of titanium or titanium alloy is <30 microns.

3. The method according to any one of the preceding claims, wherein the sintering step is 15 carried out in a vacuum with a pressure < 10³ mbar.

4. The method according to any one of the preceding claims, wherein the sintering step is carried out in a vacuum with a pressure < 10⁵ mbar.

20

5. The method according to claim 1 or claim 2, wherein the sintering step is performed in an inert gas atmosphere.

6. The method according to claim 1, 2 or 5, wherein the sintering step is performed in an argon atmosphere, at a pressure < 300 mbar.

7. The method according to any one of the preceding claims, wherein for the production of the green part, metal powder of titanium or titanium alloy is used, having an average particle size <20 pm.

30

8. The method according to any one of the preceding claims, wherein for the production of the green part, metal powder of titanium or titanium alloy is used, having an average particle size <10 pm, or <5 pm.

9.

The method according to any one of the preceding claims, wherein the sintering step ίο

2017249647 18 Jul 2019 has a sintering time of < 5 hours.

10. The method according to any one of the preceding claims, wherein the sintering step has a sintering time of < 3.5 hours.

11. The method according to any one of the preceding claims, wherein the sintering step has a sintering time of < 3 hours or < 2.5 hours.

12. The method according to any one of the preceding claims, wherein the sintering step 10 has a sintering time of at least 1 hour.

13. The method according to any one of the preceding claims, wherein the sintering step has a sintering time of at least 2 hours.

15 14. The method according to any one of the preceding claims, wherein the sintering temperature has a maximum temperature of 1050 °C.

15. The method according to any one of the preceding claims, wherein the sintering temperature has a maximum temperature of 1000°C or 950°C.

16. The method according to any one of the preceding claims, wherein the sintering temperature is at least 860 °C.

17. The method according to any one of the preceding claims, wherein in the sintering step,

25 the sintering temperature is adjusted at a temperature below a β-transus temperature of the titanium or titanium alloy material.

18. The method according to any one of the preceding claims, wherein the component after the sintering step has a material density > 97%, > 98%, or > 99%.

19. The method according to any one of claims 1 to 13, wherein in the sintering step, a sintering temperature below 950 °C is selected and that to achieve a material density of the component > 97%, said component is subjected in a further step to pressure and optionally to a temperature, wherein the further step is optionally cold isostatic pressing (CIP) and/or hot π

2017249647 18 Jul 2019 isostatic pressing (HIP).

20. The method according to any one of the preceding claims, wherein the component is subjected to a subsequent thermal treatment after the sintering step.

21. The method according to claim 20, wherein the thermal post-treatment is carried out in the form of one or more of the following treatment methods: hot isostatic pressing (HIP), quenching, uniform rapid quenching (URQ).