WO2023210558A1 - エネルギー貯蔵デバイス電極用薄膜形成組成物 - Google Patents

エネルギー貯蔵デバイス電極用薄膜形成組成物 Download PDF

Info

Publication number
WO2023210558A1
WO2023210558A1 PCT/JP2023/016043 JP2023016043W WO2023210558A1 WO 2023210558 A1 WO2023210558 A1 WO 2023210558A1 JP 2023016043 W JP2023016043 W JP 2023016043W WO 2023210558 A1 WO2023210558 A1 WO 2023210558A1
Authority
WO
WIPO (PCT)
Prior art keywords
energy storage
group
storage device
electrode
thin film
Prior art date
Application number
PCT/JP2023/016043
Other languages
English (en)
French (fr)
Inventor
宅磨 長▲濱▼
博史 太田
Original Assignee
日産化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産化学株式会社 filed Critical 日産化学株式会社
Publication of WO2023210558A1 publication Critical patent/WO2023210558A1/ja

Abstract

電極合材層の転写が可能であり、かつ、転写後に実用的な密着力と優れた密着力維持率を兼ね備えたプライマー層を与えるエネルギー貯蔵デバイス電極用薄膜形成組成物として、導電性炭素材料と、側鎖にオキサゾリン基を有するポリマーと、重量平均分子量が５０，０００～５，０００，０００である水酸基含有ポリマーと、溶媒とを含むエネルギー貯蔵デバイス電極用薄膜形成組成物を提供する。

Description

エネルギー貯蔵デバイス電極用薄膜形成組成物
　本発明は、エネルギー貯蔵デバイス電極用薄膜形成組成物に関する。
　スマートフォン、デジタルカメラ、携帯ゲーム機等の携帯電子機器の小型軽量化や高機能化の要求に伴い、近年、高性能電池の開発が積極的に進められており、充電により繰り返し使用できる二次電池の需要が大きく伸びている。中でも、リチウムイオン二次電池は、高エネルギー密度、高電圧を有し、また充放電時におけるメモリー効果が無いこと等から、現在最も精力的に開発が進められている二次電池である。また、近年の環境問題への取り組みから、電気自動車の開発も活発に進められており、その動力源としての二次電池には、より高い性能が求められるようになってきている。
　ところで、リチウムイオン二次電池は、リチウムを吸蔵、放出できる正極と負極と、これらの間に介在するセパレータを容器内に収容し、その中に電解液（リチウムイオンポリマー二次電池の場合は液状電解液の代わりにゲル状の電解質）を満たした構造を有する。
　正極および負極は、一般的に、リチウムを吸蔵、放出できる活物質と、主に炭素材料からなる導電材、さらにポリマーバインダーを含む組成物を、銅箔やアルミニウム箔等の集電基板上に塗布することで製造される。このバインダーは、活物質と導電材、さらにこれらと金属箔を接着するために用いられ、ポリフッ化ビニリデン（ＰＶｄＦ）等のＮ－メチルピロリドン（ＮＭＰ）に可溶なフッ素系樹脂や、オレフィン系重合体の水分散体等が市販されている。
　しかし、上述したバインダーの集電基板に対する接着力は十分とは言えず、電極の裁断工程や巻回工程等の製造工程時に、活物質や導電材の一部が集電基板から剥離、脱落し、微小短絡や電池容量のばらつきを生じる原因となる。さらに、長期間の使用により、電解液によるバインダーの膨潤や、活物質のリチウム吸蔵、放出による体積変化に伴う電極合材の体積変化により、電極合材と集電基板間の接触抵抗が増大したり、活物質や導電材の一部が集電基板から剥離、脱落したりすることによる電池容量の劣化が起こるという問題や、安全性の点で問題もある。
　上記課題を解決する試みとして、集電基板と電極合材層との間の密着性を高め、接触抵抗を低下させることで電池を低抵抗化する技術として、集電基板と電極合材層との間に導電性のアンダーコート層を介在させる方法が開発されている。例えば、特許文献１では、炭素を導電性フィラーとする導電層をアンダーコート層として、集電基板と電極合材層との間に配設する技術が開示されている。アンダーコート層を備えた複合集電体を用いることで、集電基板と電極合材層の間の接触抵抗を低減でき、かつ、高速放電時の容量減少も抑制でき、さらに電池の劣化をも抑制できることが示されている。また、特許文献２や特許文献３でも同様の技術が開示されている。特許文献４や特許文献５では、カーボンナノチューブを導電性フィラーとしたアンダーコート層が開示されている。
　しかし、これら各特許文献で開示されているアンダーコート層は、アンダーコート層上に、スラリー状の電極合材層形成用組成物を塗布し、乾燥して電極合材層を形成する湿式法には好適に適用できる一方、電極合材層形成用組成物を一旦シート状に成形し、これをアンダーコート層上に加熱圧着等によって積層する方法や、基材上に形成した電極合材層上にアンダーコート層を形成し、さらにその上に集電基板を積層した後、基材を剥離する電極合材層の転写を伴う方法等の乾式法では、密着力が不足したり、転写が困難であったりする等の問題がある。また、生産スケジュール等の都合により、アンダーコート（プライマー）層を形成した後、電極合材層と密着させるまでにタイムラグを生じることがあることから、一定時間保管された後でもその密着力が維持されていることが求められている。
特開平９－０９７６２５号公報 特開２０００－０１１９９１号公報 特開平１１－１４９９１６号公報 国際公開第２０１４／０４２０８０号 国際公開第２０１５／０２９９４９号
　本発明は、上記事情に鑑みてなされたものであり、電極合材層の転写が可能であり、かつ、転写後に実用的な密着力と優れた密着力維持率を兼ね備えたプライマー層を与えるエネルギー貯蔵デバイス電極用薄膜形成組成物を提供することを目的とする。
　本発明者らは、上記課題を解決するために鋭意検討を重ねた結果、導電性炭素材料と、側鎖にオキサゾリン基を有するポリマーと、特定範囲の重量平均分子量を有する水酸基含有ポリマーと、溶媒とを含む組成物が、電極合材層の転写が可能であり、かつ、転写後に実用的な密着力と優れた密着力維持率を兼ね備えた薄膜（プライマー層）を与えることを見出し、本発明を完成させた。
　すなわち、本発明は、エネルギー貯蔵デバイス電極を提供する。
１．　導電性炭素材料と、側鎖にオキサゾリン基を有するポリマーと、重量平均分子量が５０，０００～５，０００，０００である水酸基含有ポリマーと、溶媒とを含むエネルギー貯蔵デバイス電極用薄膜形成組成物。
２．　上記水酸基含有ポリマーの分子中に占める水酸基の質量割合が、１×１０-5～１００×１０-5である１のエネルギー貯蔵デバイス電極用薄膜形成組成物。
３．　上記水酸基含有ポリマーの分子中に占める水酸基の質量割合が、１×１０-5～５０×１０-5である２のエネルギー貯蔵デバイス電極用薄膜形成組成物。
４．　上記水酸基含有ポリマーの含有量が、上記導電性炭素材料１００質量部に対して２５～２００質量部である１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成組成物。
５．　上記水酸基含有ポリマーが、ポリアルキレングリコールである１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成組成物。
６．　上記ポリアルキレングリコールが、ポリエチレングリコールである５のエネルギー貯蔵デバイス電極用薄膜形成組成物。
７．　上記側鎖にオキサゾリン基を有するポリマーが、２位に重合性炭素－炭素二重結合含有基を有する式（１）で示されるオキサゾリンモノマーと、親水性官能基を有する（メタ）アクリル系モノマーとをラジカル重合したポリマーである１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成組成物。
Figure JPOXMLDOC01-appb-C000005
 （式中、Ｘは、重合性炭素－炭素二重結合を含む鎖状炭化水素基を表し、Ｒ1～Ｒ4は、互いに独立して、水素原子、ハロゲン原子、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数６～２０のアリール基、または炭素数７～２０のアラルキル基を表す。）
８．　上記側鎖にオキサゾリン基を有するポリマーの含有量が、上記導電性炭素材料１００質量部に対して２０～６０質量部である１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成組成物。
９．　上記導電性炭素材料が、アセチレンブラック、カーボンブラック、ケッチェンブラック、ファーネスブラック、チャンネルブラックおよびランプブラックから選ばれる１種または２種以上である１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成組成物。
１０．　さらに、下記式（ｎ１）で表される複素環式化合物を含む１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成組成物。
Figure JPOXMLDOC01-appb-C000006
 （式中、ＲaおよびＲbは、それぞれ独立して、水素原子、ハロゲン原子、置換基を有していてもよい炭素数１～６のアルキル基、置換基を有していてもよい炭素数２～６のアルケニル基、または置換基を有していてもよい炭素数６～１２のアリール基を表し、ＲaおよびＲbが互いに結合して炭素数４～６の環を形成していてもよく、Ｘaは、ＮまたはＣＨである。）
１１．　上記置換基が、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基およびエポキシ基からなる群より選ばれる少なくとも１種である１０のエネルギー貯蔵デバイス電極用薄膜形成組成物。
１２．　上記複素環式化合物が、下記式（ｎ２）で表される１０のエネルギー貯蔵デバイス電極用薄膜形成組成物。
Figure JPOXMLDOC01-appb-C000007
 （式中、Ｙaは、水素原子、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基またはエポキシ基を表す。Ｘaは、上記と同じである。）
１３．　上記複素環式化合物が、下記式（ｎ３）で表される１２のエネルギー貯蔵デバイス電極用薄膜形成組成物。
Figure JPOXMLDOC01-appb-C000008
 １４．　１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成用組成物から得られる薄膜からなるプライマー層。
１５．　集電基板と、この集電基板の上に形成された１４のプライマー層とを備えるエネルギー貯蔵デバイスの電極用複合集電体。
１６．　集電基板が、銅箔またはアルミニウム箔である１５のエネルギー貯蔵デバイスの電極用複合集電体。
１７．　１６のエネルギー貯蔵デバイスの電極用複合集電体を備えるエネルギー貯蔵デバイス用電極。
１８．　アノード電極用である１７のエネルギー貯蔵デバイス用電極。
１９．　１７のエネルギー貯蔵デバイス用電極を備えるエネルギー貯蔵デバイス。
２０．　リチウムイオン電池である１９のエネルギー貯蔵デバイス。
２１．　全固体リチウムイオン電池である２０のエネルギー貯蔵デバイス。
２２．　集電基板の上に、１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成用組成物を塗布し、乾燥してプライマー層を形成した後、このプライマー層の上に電極合材シートを積層し、加熱圧着するエネルギー貯蔵デバイス電極の製造方法。
２３．　基材上に、電極合材層形成用組成物を塗布し、乾燥して電極合材層を形成する工程と、
　この電極合材層の上に、１～３のいずれかのエネルギー貯蔵デバイス電極用薄膜形成用組成物を塗布し、乾燥してプライマー層を形成する工程と、
　このプライマー層の上に、集電基板を積層して加熱圧着した後、上記基材を剥離する工程を備えるエネルギー貯蔵デバイス電極の製造方法。
　本発明のエネルギー貯蔵デバイス電極用薄膜形成用組成物は、電極合材層の転写が可能であり、かつ、実用的な密着力と優れた密着力維持率を兼ね備えたプライマー層を与える。
　したがって、本発明のエネルギー貯蔵デバイス電極用薄膜形成用組成物を用いることで、基材付着電極合材層組成物や電極合材層シートの転写を行う乾式プロセスが適用可能になるため、高厚み、かつ、厚み精度に優れる電極合材層を備える電極を作製することができる。
　以下、本発明についてさらに詳しく説明する。
　本発明のエネルギー貯蔵デバイス電極用薄膜形成組成物（以下、単に「組成物」ということもある）は、導電性炭素材料と、側鎖にオキサゾリン基を有するポリマーと、水酸基含有ポリマーと、溶媒とを含むことを特徴とする。
［１］導電性炭素材料
　本発明の組成物に用いられる導電性炭素材料の具体例としては、アセチレンブラック、カーボンブラック、ケッチェンブラック、ファーネスブラック、チャンネルブラック、ランプブラック、カーボンナノチューブ、カーボンウイスカー、炭素繊維、天然黒鉛、人造黒鉛等の公知の導電性炭素材料から適宜選択して用いることができるが、特に、導電性、分散性、密着性、転写性等の観点から、アセチレンブラック、カーボンブラック、ケッチェンブラック、ファーネスブラック、チャンネルブラック、ランプブラックが好ましく、アセチレンブラック、カーボンブラック、ケッチェンブラックがより好ましく、アセチレンブラックがより一層好ましい。なお、上記導電性炭素材料は、単独で用いても、２種以上併用してもよい。
　導電性炭素材料は、市販品を用いることができ、その具体例としては、デンカ（株）製のアセチレンブラックであるデンカブラック（Ｌｉ－１００、Ｌｉ－２５０、Ｌｉ－４００、Ｌｉ－４３５等）、日本ケミコン（株）製ＮＨカーボン等が挙げられる。
［２］側鎖にオキサゾリン基を有するポリマー
　本発明の組成物において、側鎖にオキサゾリン基を有するポリマー（以下、オキサゾリンポリマーという）は、上記導電性炭素材料の分散剤およびバインダーポリマーとして作用するものである。
　このポリマーとしては、主鎖を構成する繰り返し単位に直接またはアルキレン基等のスペーサー基を介してオキサゾリン基が結合した重合体であれば特に限定されるものではないが、具体的には、式（１）に示されるような２位に重合性炭素－炭素二重結合含有基を有するオキサゾリンモノマーをラジカル重合して得られる、オキサゾリン環の２位でポリマー主鎖またはスペーサー基に結合した繰り返し単位を有するポリマーであることが好ましい。
Figure JPOXMLDOC01-appb-C000009
　式中、Ｘは、重合性炭素－炭素二重結合含有基を表し、Ｒ1～Ｒ4は、互いに独立して、水素原子、ハロゲン原子、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数６～２０のアリール基、または炭素数７～２０のアラルキル基を表す。
　オキサゾリンモノマーが有する重合性炭素－炭素二重結合含有基としては、重合性炭素－炭素二重結合を含んでいれば特に限定されるものではないが、重合性炭素－炭素二重結合を含む鎖状炭化水素基が好ましく、例えば、ビニル基、アリル基、イソプロペニル基などの炭素数２～８のアルケニル基等が好ましい。
　ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子等が挙げられる。
　炭素数１～５の分岐構造を有していてもよいアルキル基の具体例としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、ｎ－ペンチル基等が挙げられる。
　炭素数６～２０のアリール基の具体例としては、フェニル基、キシリル基、トリル基、ビフェニル基、ナフチル基等が挙げられる。
　炭素数７～２０のアラルキル基の具体例としては、ベンジル基、フェニルエチル基、フェニルシクロヘキシル基等が挙げられる。
　式（１）で示される２位に重合性炭素－炭素二重結合含有基を有するオキサゾリンモノマーの具体例としては、２－ビニル－２－オキサゾリン、２－ビニル－４－メチル－２－オキサゾリン、２－ビニル－４－エチル－２－オキサゾリン、２－ビニル－４－プロピル－２－オキサゾリン、２－ビニル－４－ブチル－２－オキサゾリン、２－ビニル－５－メチル－２－オキサゾリン、２－ビニル－５－エチル－２－オキサゾリン、２－ビニル－５－プロピル－２－オキサゾリン、２－ビニル－５－ブチル－２－オキサゾリン、２－イソプロペニル－２－オキサゾリン、２－イソプロペニル－４－メチル－２－オキサゾリン、２－イソプロペニル－４－エチル－２－オキサゾリン、２－イソプロペニル－４－プロピル－２－オキサゾリン、２－イソプロペニル－４－ブチル－２－オキサゾリン、２－イソプロペニル－５－メチル－２－オキサゾリン、２－イソプロペニル－５－エチル－２－オキサゾリン、２－イソプロペニル－５－プロピル－２－オキサゾリン、２－イソプロペニル－５－ブチル－２－オキサゾリン等が挙げられるが、入手容易性などの点から、２－イソプロペニル－２－オキサゾリンが好ましい。
　また、導電性炭素材料分散液を、水系溶媒を用いて調製することを考慮すると、オキサゾリンポリマーは水溶性であることが好ましい。
　このような水溶性のオキサゾリンポリマーは、上記式（１）で表されるオキサゾリンモノマーのホモポリマーでもよいが、水への溶解性をより高めるため、上記オキサゾリンモノマーと親水性官能基を有する（メタ）アクリル酸エステル系モノマーとの少なくとも２種のモノマーをラジカル重合させて得られたものであることが好ましい。
　親水性官能基を有する（メタ）アクリル系モノマーの具体例としては、（メタ）アクリル酸、アクリル酸２－ヒドロキシエチル、アクリル酸メトキシポリエチレングリコール、アクリル酸とポリエチレングリコールとのモノエステル化物、アクリル酸２－アミノエチルおよびその塩、メタクリル酸２－ヒドロキシエチル、メタクリル酸メトキシポリエチレングリコール、メタクリル酸とポリエチレングリコールとのモノエステル化物、メタクリル酸２－アミノエチルおよびその塩、（メタ）アクリル酸ナトリウム、（メタ）アクリル酸アンモニウム、（メタ）アクリルニトリル、（メタ）アクリルアミド、Ｎ－メチロール（メタ）アクリルアミド、Ｎ－（２－ヒドロキシエチル）（メタ）アクリルアミド、スチレンスルホン酸ナトリウム等が挙げられ、これらは、単独で用いても、２種以上組み合わせて用いてもよい。これらの中でも、（メタ）アクリル酸メトキシポリエチレングリコール、（メタ）アクリル酸とポリエチレングリコールとのモノエステル化物が好適である。
　また、本発明においては、得られるオキサゾリンポリマーの導電性炭素材料分散能に悪影響を及ぼさない範囲で、上記オキサゾリンモノマーおよび親水性官能基を有する（メタ）アクリル系モノマー以外のその他のモノマーを併用することができる。
　その他のモノマーの具体例としては、（メタ）アクリル酸メチル、（メタ）アクリル酸エチル、（メタ）アクリル酸ブチル、（メタ）アクリル酸２－エチルヘキシル、（メタ）アクリル酸ステアリル、（メタ）アクリル酸パーフルオロエチル、（メタ）アクリル酸フェニル等の（メタ）アクリル酸エステルモノマー；エチレン、プロピレン、ブテン、ペンテン等のα－オレフィン系モノマー；塩化ビニル、塩化ビニリデン、フッ化ビニル等のハロオレフィン系モノマー；スチレン、α－メチルスチレン等のスチレン系モノマー；酢酸ビニル、プロピオン酸ビニル等のカルボン酸ビニルエステル系モノマー；メチルビニルエーテル、エチルビニルエーテル等のビニルエーテル系モノマー等が挙げられ、これらはそれぞれ単独で用いても、２種以上組み合わせて用いてもよい。
　本発明の組成物中における、側鎖にオキサゾリン基を有するポリマーの含有量は、導電性炭素材料を分散し得る限り特に制限はないが、導電性炭素材料を十分に分散させるとともにバインダーとしての機能を発揮させることを考慮すると、その含有量は、導電性炭素材料１００質量部に対して２０～６０質量部が好ましく、３０～６０質量部がより好ましく、４０～６０質量部がより一層好ましい。
［３］水酸基含有ポリマー
　本発明の組成物において、水酸基含有ポリマーは、密着力を向上させる点から、当該水酸基含有ポリマーの分子中に占める水酸基の質量割合が、１×１０-5～１００×１０-5であることが好ましく、１×１０-5～５０×１０-5であることがより好ましい。
　上記水酸基含有ポリマーの重量平均分子量は、５０，０００～５，０００，０００であり、好ましくは５０，０００～２，５００，０００、より好ましくは１００，０００～１，０００，０００である。ポリアルキレングリコールおよび／またはポリビニルアルコールが用いられる。なお、本発明におけるポリアルキレングリコールにはポリアルキレンオキシドも含まれる。重量平均分子量は、ゲルパーミエーションクロマトグラフィーによるポリスチレン換算値である。
　また、プライマー層の密着力を考慮すると、上記水酸基含有ポリマーの融点の下限は２５℃以上であり、上限は１００℃以下であることが好ましく、７０℃以下であることがより好ましい。
　ポルアルキレングリコール（ポリアルキレンオキシド）の具体例としては、ポリエチレングリコール（ポリエチレンオキシド）、ポリプロピレングリコール（ポリプロピレンオキシド）、ポリテトラメチレンエーテルグリコール等が挙げられる。また、水酸基含有ポリマーとしては、複数種の繰り返し単位を含む共重合体であってもよく、例えば、アルキレンオキサイドとアリルグリシジルエーテルの共重合体が挙げられる。上記共重合体の具体例としては、エチレンオキサイドとアリルグリシジルエーテルの共重合体、プロピレンオキサイドとアリルグリシジルエーテルの共重合体、エチレンオキサイドとプロピレンオキサイド、アリルグリシジルエーテルの共重合体等が挙げられる。上記共重合体は、ランダム共重合体、ブロック共重合体およびグラフト共重合体のいずれであってもよいが、ランダム共重合体が好ましい。
　水酸基含有ポリマーは市販品を用いることができ、例えば、明成化学工業（株）製のアルコックスＥ－２４０、Ｅ－１６０、Ｅ－１００、Ｅ－７５、Ｅ－６０、Ｅ－４５、Ｅ－３０、Ｒ－１０００、Ｒ－４００、Ｒ－１５０（ＰＥＧ）、アルコックスＣＰ－Ａ１Ｈ、ＣＰ－Ａ２Ｈ（エチレンオキサイドとプロピレンオキサイド、アリルグリシジルエーテルのランダム共重合体）等；富士フイルム和光純薬（株）製のポリエチレングリコール２，０００、３，０００、４，０００、６，０００、８，０００、１０，０００、１２，０００、２０，０００、５００，０００等；日本酢ビ・ポバール（株）製のポリビニルアルコールＶＣ－１０、１３、２０、ＶＦ－１７２０等；三洋化成（株）製のＰＥＧ－２，０００、４，０００、６，０００、１０，０００、２０，０００（ＰＥＧ）、ニューボールＰＰ－２０００，４０００（ＰＰＧ）等；Ａｌｆａ　Ａｅｓａｒ製のＰＥＧ－２，０００、４，０００、６，０００、１０，０００、２０，０００（ＰＥＧ）等；小宗化学薬品（株）製のＰＥＧ－６，０００（ＰＥＧ）等が挙げられるが、これらに限定されるものではない。
　本発明の組成物中における水酸基含有ポリマーの含有量は、上記導電性炭素材料１００質量部に対して１０～２００質量部が好ましく、プライマー層の密着力をより高めることを考慮すると、３０～１５０質量部がより好ましく、４０～１２０質量部がより一層好ましい。
　本発明では、集電基板とプライマー層との密着性に加え、プライマー層のスクラッチ耐性を高めるために、さらに、窒素原子を２個以上含む含窒素複素環式化合物を含むことが好ましい。含窒素複素環式化合物としては、環を構成する窒素原子を２個以上含むものであれば特に限定されるものではなく、従来公知の化合物から適宜選択して用いることができるが、本発明では、イミダゾール誘導体、ピラゾール誘導体およびトリアゾール誘導体が好ましく、イミダゾール誘導体およびトリアゾール誘導体がより好ましく、トリアゾール誘導体がより一層好ましい。これらの使用可能な具体例を以下に列記する。
　イミダゾール誘導体の具体例としては、イミダゾール、ベンゾイミダゾール、５－カルボキシベンゾイミダゾール、４－カルボキシベンゾイミダゾール等が挙げられる。
　ピラゾール誘導体の具体例としては、ピラゾール、１，２－ベンゾピラゾール、４－ピラゾールカルボン酸、３－ピラゾールカルボン酸、アデニン等が挙げられる。
　トリアゾール誘導体としては、ベンゾトリアゾール系化合物が好ましく、その具体例としては、ベンゾトリアゾール、カルボキシベンゾトリアゾール、５－カルボキシベンゾトリアゾール、４－カルボキシベンゾトリアゾール、５－ヒドロキシベンゾトリアゾール、５－アミノベンゾトリアゾール、ベンゾトリアゾール－４－スルホン酸、４－メチルベンゾトリアゾール、５－メチル－１Ｈ－ベンゾトリアゾール、１－カルボキシベンゾトリアゾール、１－ヒドロキシベンゾトリアゾール、１－アミノベンゾトリアゾール、４－メチルベンゾトリアゾール、５－メチル－１Ｈ－ベンゾトリアゾール、ベンゾトリアゾール－１－メチルアミン、４－メチルベンゾトリアゾール－１－メチルアミン、５－メチルベンゾトリアゾール－１－メチルアミン、Ｎ－メチルベンゾトリアゾール－１－メチルアミン、Ｎ－エチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジメチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジエチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジプロピルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジブチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジヘキシルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジオクチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ビス（２－エチルヘキシル）－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジメチル－４－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジメチル－５－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジエチル－４－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジエチル－５－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジプロピル－４－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジプロピル－５－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジブチル－４－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジブチル－５－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジヘキシル－４－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジヘキシル－５－ベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ビス（２－エチルヘキシル）－４－メチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ビス（２－エチルヘキシル）－５－メチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジオレイル－４－メチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジオレイル－５－メチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジステアリル－４－メチルベンゾトリアゾール－１－メチルアミン、Ｎ，Ｎ－ジステアリル－５－メチルベンゾトリアゾール－１－メチルアミン、１－ヒドロキシメチルベンゾトリアゾール、１－（２－エチルヘキシルアミノ）メチル）ベンゾトリアゾール、１－（２，３－ジヒドロキシプロピル）ベンゾトリアゾール等が挙げられる。
　特に、本発明では、下記式（ｎ１）で表される化合物を用いることが好ましい。
Figure JPOXMLDOC01-appb-C000010
　上記ＲaおよびＲbは、それぞれ独立して、水素原子、ハロゲン原子、置換基を有していてもよい炭素数１～６のアルキル基、置換基を有していてもよい炭素数２～６のアルケニル基、または置換基を有していてもよい炭素数６～１２のアリール基を表し、ＲaおよびＲbが互いに結合して炭素数４～６の環を形成していてもよく、Ｘaは、ＮまたはＣＨである。
　ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子等が挙げられる。
　炭素数１～６のアルキル基としては、直鎖状、分岐鎖状、環状のいずれでもよく、その具体例としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、ｓ－ブチル基、ｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基等の炭素数１～６の直鎖または分岐鎖状アルキル基；シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基等の炭素数３～６の環状アルキル基が挙げられる。
　炭素数２～６のアルケニル基としては、エテニル、ｎ－１－プロペニル、ｎ－２－プロペニル、１－メチルエテニル、ｎ－１－ブテニル、ｎ－２－ブテニル、ｎ－３－ブテニル、２－メチル－１－プロペニル、２－メチル－２－プロペニル、１－エチルエテニル、１－メチル－１－プロペニル、１－メチル－２－プロペニル、ｎ－１－ペンテニル等が挙げられる。
　炭素数６～１２のアリール基としては、フェニル、トリル、１－ナフチル、２－ナフチル基等が挙げられる。
　上記置換基としては、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基、エポキシ基等が挙げられる。
　ＲaおよびＲbが互いに結合して形成される炭素数４～６の環としては、シクロペンタン環、シクロヘキサン環、ベンゼン環等が挙げられる。
　上記Ｘaとしては、Ｎが好ましい。
　特に、ＲaおよびＲbが互いに結合してベンゼン環を形成した下記式（ｎ２）で表される化合物がより好ましい。
Figure JPOXMLDOC01-appb-C000011
　上記Ｙaは、水素原子、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基またはエポキシ基を表すが、マイグレーション抑制効果を確保するとともに、集電体とアンダーコート層間との密着性を向上させる点から、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基およびエポキシ基が好ましく、カルボキシ基がより好ましい。
　上記Ｘaは、上記（ｎ１）と同じであるが、Ｎが好ましい。
　したがって、上記式（ｎ２）で表される複素環式化合物のより好適な態様としては、下記式（ｎ３）で表されるものが挙げられる。
Figure JPOXMLDOC01-appb-C000012
　上記式（ｎ３）で表される複素環式化合物の具体例としては、カルボキシベンゾトリアゾール、５－カルボキシベンゾトリアゾール、４－カルボキシベンゾトリアゾールが挙げられるが、カルボキシベンゾトリアゾールおよび５－カルボキシベンゾトリアゾールが好ましい。
　含窒素複素環式化合物を含む場合、その含有量は、導電性炭素材料１００質量部に対し、好ましくは０．０５～２００質量部、より好ましくは０．１～１５０質量部、より一層好ましくは５～１３０質量部、さらに好ましくは１０～１１０質量部、最も好ましくは１０～１００質量部である。なお、上記の含窒素複素環式化合物は、１種を単独で用いても、２種以上を組み合わせて用いてもよい。
［４］溶媒
　本発明の組成物の調製に用いる溶媒としては、特に限定されるものではないが、水および／または親水性溶媒が好ましい。
　親水性溶媒とは水と任意に混合する有機溶媒であり、例えば、テトラヒドロフラン（ＴＨＦ）等のエーテル類；Ｎ，Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ，Ｎ－ジメチルアセトアミド（ＤＭＡｃ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）等のアミド類；アセトン等のケトン類；メタノール、エタノール、ｎ－プロパノール、２－プロパノール等のアルコール類；エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテル等のグリコールエーテル類；エチレングリコール、プロピレングリコール等のグリコール類等の有機溶媒が挙げられる。これらの溶媒は、１種を単独で用いても、２種以上を組み合わせて用いてもよい。
　これらの中でも、導電性炭素材料の分散性を高めるという点から、水、ＮＭＰ、ＤＭＦ、ＴＨＦ、メタノール、エタノール、ｎ－プロパノール、２－プロパノール、ｎ－ブタノール、ｔ－ブタノールを含むことが好ましい。また、組成物の塗工性を向上させ得るという点から、メタノール、エタノール、ｎ－プロパノール、２－プロパノール、ｎ－ブタノール、ｔ－ブタノール、エチレングリコールモノブチルエーテルを含むことが好ましい。
　特に、コストを下げ得るという点からは、水を含むことが好ましく、溶媒中に水を７０質量％以上（有機溶媒が３０質量％以下）含むことがより好ましい。
［５］組成物の調製法
　本発明の組成物の調製法は、特に限定されるものではなく、導電性炭素材料、側鎖にオキサゾリン基を有するポリマー、水酸基含有ポリマーおよび溶媒を任意の順序で混合して調製することができるが、導電性炭素材料、側鎖にオキサゾリン基を有するポリマーおよび溶媒を混合して調製した第１液と、水酸基含有ポリマーと溶媒とを混合して調製した第２液とを混合する手法が好適である。
　この際、組成物を分散処理することが好ましく、この処理により、導電性炭素材料の分散割合をより向上させることができる。分散処理としては、機械的処理である、ボールミル、ビーズミル、ジェットミル等を用いる湿式処理や、バス型やプローブ型のソニケータを用いる超音波処理が挙げられるが、特に、ジェットミルを用いた湿式処理や超音波処理が好適である。
　分散処理の時間は任意であるが、１分から１０時間程度が好ましく、５分から５時間程度がより好ましい。なお、必要に応じて加熱処理または冷却処理を施しても構わない。
　本発明において、組成物の固形分濃度は、特に限定されるものではないが、所望の目付量や膜厚でプライマー層を形成することを考慮すると、２０質量％以下が好ましく、１５質量％以下がより好ましく、１０質量％以下がより一層好ましく、５質量％以下が更に好ましい。また、その下限は、任意であるが、実用的な観点から、０．１質量％以上が好ましく、０．５質量％以上がより好ましく、１質量％以上がより一層好ましい。
　なお、固形分とは、組成物を構成する溶媒以外の成分を意味する。
［６］プライマー層およびエネルギー貯蔵デバイス電極
　以上で説明した組成物を、集電体の少なくとも一方の面や、電極合材層の表面に塗布し、これを自然または加熱乾燥して得られた薄膜は、エネルギー貯蔵デバイス電極のプライマー層として好適に利用できる。
　エネルギー貯蔵デバイスとしては、例えば、電気二重層キャパシタ、リチウム二次電池、リチウムイオン二次電池、プロトンポリマー電池、ニッケル水素電池、アルミ固体コンデンサ、電解コンデンサ、鉛蓄電池等の各種エネルギー貯蔵デバイスが挙げられるが、本発明の組成物は、特に、電気二重層キャパシタ、リチウムイオン二次電池に好適に用いることができる。
　集電体としては、従来、エネルギー貯蔵デバイス用電極の集電体として用いられているものを使用することができる。例えば、銅、アルミニウム、チタン、ステンレス、ニッケル、金、銀およびこれらの合金や、カーボン材料、金属酸化物、導電性高分子等を用いることができるが、銅、アルミニウム、ニッケルまたはこれらの合金からなる金属箔が好ましい。
　集電体の厚みは、特に限定されるものではないが、本発明においては、１～１００μｍが好ましい。
　電極合材層は、活物質、バインダーポリマーおよび必要に応じて溶媒を合わせて作製した電極スラリー（電極合材層形成用組成物）を、基材上に塗布し、自然または加熱乾燥して形成できる。
　活物質としては、従来、エネルギー貯蔵デバイス用電極に用いられている各種活物質を用いることができる。例えば、リチウム二次電池やリチウムイオン二次電池の場合、正極活物質としてリチウムイオンを吸着・離脱可能なカルコゲン化合物またはリチウムイオン含有カルコゲン化合物、ポリアニオン系化合物、硫黄単体およびその化合物等を用いることができる。
　このようなリチウムイオンを吸着離脱可能なカルコゲン化合物としては、例えば、ＦｅＳ2、ＴｉＳ2、ＭｏＳ2、Ｖ2Ｏ6、Ｖ6Ｏ13、ＭｎＯ2等が挙げられる。
　リチウムイオン含有カルコゲン化合物としては、例えば、ＬｉＣｏＯ2、ＬｉＭｎＯ2、ＬｉＭｎ2Ｏ4、ＬｉＭｏ2Ｏ4、ＬｉＶ3Ｏ8、ＬｉＮｉＯ2、ＬｉxＮｉyＭ1-yＯ2（ただし、Ｍは、Ｃｏ、Ｍｎ、Ｔｉ、Ｃｒ、Ｖ、Ａｌ、Ｓｎ、Ｐｂ、およびＺｎから選ばれる少なくとも１種以上の金属元素を表し、０．０５≦ｘ≦１．１０、０．５≦ｙ≦１．０）等が挙げられる。
　ポリアニオン系化合物としては、例えば、ＬｉＦｅＰＯ4等が挙げられる。
　硫黄化合物としては、例えば、Ｌｉ2Ｓ、ルベアン酸等が挙げられる。
　一方、上記負極を構成する負極活物質としては、アルカリ金属、アルカリ合金、リチウムイオンを吸蔵・放出する周期表４～１５族の元素から選ばれる少なくとも１種の単体、酸化物、硫化物、窒化物、またはリチウムイオンを可逆的に吸蔵・放出可能な炭素材料を使用することができる。
　アルカリ金属としては、Ｌｉ、Ｎａ、Ｋ等が挙げられ、アルカリ金属合金としては、例えば、Ｌｉ－Ａｌ、Ｌｉ－Ｍｇ、Ｌｉ－Ａｌ－Ｎｉ、Ｎａ－Ｈｇ、Ｎａ－Ｚｎ等が挙げられる。
　リチウムイオンを吸蔵放出する周期表４～１５族の元素から選ばれる少なくとも１種の元素の単体としては、例えば、ケイ素やスズ、アルミニウム、亜鉛、砒素等が挙げられる。
　同じく酸化物としては、一酸化ケイ素（ＳｉＯ）、二酸化ケイ素（ＳｉＯ2）、スズケイ素酸化物（ＳｎＳｉＯ3）、リチウム酸化ビスマス（Ｌｉ3ＢｉＯ4）、リチウム酸化亜鉛（Ｌｉ2ＺｎＯ2）、リチウム酸化チタン（Ｌｉ4Ｔｉ5Ｏ12）、酸化チタン等が挙げられる。
　同じく硫化物としては、リチウム硫化鉄（ＬｉxＦｅＳ2（０≦ｘ≦３））、リチウム硫化銅（ＬｉxＣｕＳ（０≦ｘ≦３））等が挙げられる。
　同じく窒化物としては、リチウム含有遷移金属窒化物が挙げられ、具体的には、ＬｉxＭyＮ（Ｍ＝Ｃｏ、Ｎｉ、Ｃｕ、０≦ｘ≦３、０≦ｙ≦０．５）、リチウム鉄窒化物（Ｌｉ3ＦｅＮ4）等が挙げられる。
　リチウムイオンを可逆的に吸蔵・放出可能な炭素材料としては、グラファイト、カーボンブラック、コークス、ガラス状炭素、炭素繊維、カーボンナノチューブ、またはこれらの焼結体等が挙げられる。
　また、電気二重層キャパシタの場合、活物質として炭素質材料を用いることができる。
　この炭素質材料としては、活性炭等が挙げられ、例えば、フェノール樹脂を炭化後、賦活処理して得られた活性炭が挙げられる。
　バインダーポリマーとしては、公知の材料から適宜選択して用いることができ、例えば、ポリフッ化ビニリデン（ＰＶｄＦ）、ポリビニルピロリドン、ポリテトラフルオロエチレン、テトラフルオロエチレン－ヘキサフルオロプロピレン共重合体、フッ化ビニリデン－ヘキサフルオロプロピレン共重合体〔Ｐ（ＶＤＦ－ＨＦＰ）〕、フッ化ビニリデン－塩化３フッ化エチレン共重合体〔Ｐ（ＶＤＦ－ＣＴＦＥ）〕、ポリビニルアルコール、ポリイミド、エチレン－プロピレン－ジエン三元共重合体、スチレン－ブタジエンゴム、カルボキシメチルセルロース（ＣＭＣ）、ポリアクリル酸（ＰＡＡ）、ポリアクリル酸アンモニウム、ポリアニリン、ポリイミド、ポリアミドが挙げられる。なお、バインダーポリマーの添加量は、活物質１００質量部に対して、０．１～４０質量部、特に１～３０質量部が好ましい。
　溶媒としては、上記組成物用の溶媒で例示した溶媒が挙げられ、それらの中からバインダーの種類に応じて適宜選択すればよいが、ＰＶｄＦ等の非水溶性のバインダーの場合はＮＭＰが好適であり、ＰＡＡ等の水溶性のバインダーの場合は水が好適である。
　なお、上記電極スラリーは、導電材を含んでいてもよい。導電材としては、例えば、カーボンブラック、ケッチェンブラック、アセチレンブラック、カーボンウイスカー、炭素繊維、天然黒鉛、人造黒鉛、酸化チタン、酸化ルテニウム、アルミニウム、ニッケル等が挙げられる。
　電極スラリーの塗布方法としては、例えば、スピンコート法、ディップコート法、フローコート法、インクジェット法、キャスティング法、スプレーコート法、バーコート法、グラビアコート法、スリットコート法、ロールコート法、フレキソ印刷法、転写印刷法、刷毛塗り、ブレードコート法、エアーナイフコート法、ダイコート法等が挙げられるが、作業効率等の点から、インクジェット法、キャスティング法、ディップコート法、バーコート法、ブレードコート法、ロールコート法、グラビアコート法、フレキソ印刷法、スプレーコート法、ダイコート法が好適である。
　また、加熱乾燥する場合の温度も任意であるが、５０～４００℃程度が好ましく、８０～１５０℃程度がより好ましい。
　集電基板や電極合材層の表面に本発明の組成物を塗布する手法としては、上記電極スラリーの塗布方法と同様の方法が挙げられる。
　また、加熱乾燥する場合の温度も任意であるが、５０～２００℃程度が好ましく、８０～１５０℃程度がより好ましい。
　プライマー層の厚みは、得られるデバイスの内部抵抗を低減することを考慮すると、１ｎｍ～１０μｍが好ましく、１ｎｍ～５μｍがより好ましく、１ｎｍ～３μｍがより一層好ましい。
　厚みは、例えば、プライマー層を形成した積層体から適当な大きさの試験片を切り出し、それを手で裂く等の手法により断面を露出させ、走査電子顕微鏡（ＳＥＭ）等の顕微鏡観察により、断面部分でプライマー層が露出した部分から求めることができる。
　集電体や電極合材層の一面あたりのプライマー層の目付量は、上記膜厚を満たす限り特に限定されるものではないが、３，０００ｍｇ／ｍ2以下が好ましく、２，５００ｍｇ／ｍ2以下がより好ましく、２，０００ｍｇ／ｍ2以下がより一層好ましい。一方、プライマー層の機能を担保して優れた特性の電池を再現性よく得るため、上記一面あたりのプライマー層の目付量は、５００ｍｇ／ｍ2以上が好ましく、７５０ｍｇ／ｍ2以上がより好ましく、１，０００ｍｇ／ｍ2以上がより好ましい。
　なお、プライマー層の目付量は、プライマー層の面積（ｍ2）に対するプライマー層の質量（ｍｇ）の割合であり、プライマー層がパターン状に形成されている場合、当該面積はプライマー層のみの面積であり、パターン状に形成されたプライマー層の間に露出する集電体等の下層の面積を含まない。
　また、上記目付量は、想定目付量であってもよい。想定目付量とは、所定の固形分濃度の組成物を所定のワイヤーバーコーターを用いて下地層上に塗工した際に想定される目付量を意味し、例えば、固形分濃度５質量％の組成物を、ワイヤーバーコーターでＯＳＰ－３０を用いて塗工した場合の想定目付量として表すことができる。
　プライマー層の質量は、例えば、プライマー層を形成した積層体から適当な大きさの試験片を切り出し、その質量Ｗ０を測定し、その後、当該積層体からプライマー層を剥離し、プライマー層を剥離した後の質量Ｗ１を測定し、その差（Ｗ０－Ｗ１）から算出する、あるいは、予め集電体の質量Ｗ２を測定しておき、その後、プライマー層を形成した積層体の質量Ｗ３を測定し、その差（Ｗ３－Ｗ２）から算出することができる。プライマー層を剥離する方法としては、例えばプライマー層が溶解、もしくは膨潤する溶剤に、プライマー層を浸漬させ、布等でプライマー層をふき取るなどの方法が挙げられる。
　目付量や膜厚は、公知の方法で調整することができる。例えば、塗布によりプライマー層を形成する場合、プライマー層を形成するための塗工液（プライマー層形成用組成物）の固形分濃度、塗布回数、塗工機の塗工液投入口のクリアランス等を変えることで調整できる。目付量や膜厚を多くしたい場合は、固形分濃度を高くしたり、塗布回数を増やしたり、クリアランスを大きくしたりする。目付量や膜厚を少なくしたい場合は、固形分濃度を低くしたり、塗布回数を減らしたり、クリアランスを小さくしたりする。
　集電基板上に、上記プライマー層を形成した後、このプライマー層の表面に上記電極スラリーを塗布し、自然または加熱乾燥して電極合材層を形成してエネルギー貯蔵デバイス電極を作製することができるが、上述したとおり、本発明のプライマー層は、乾式法にも適用できるため、プライマー層上に、電極合材シートを積層し、加熱圧着してエネルギー貯蔵デバイス電極を作製することもできる。
　この場合、電極合材シートは、上述した電極スラリーを下地層上に塗布し、これを自然または加熱乾燥してシート化したものを用いることができる。
　また、基材上に、上述した電極スラリーを塗布し、乾燥して電極合材層を形成した後、この電極合材層の上に、本発明の組成物を塗布し、乾燥してプライマー層を形成し、さらにこの上に集電基板を積層して加熱圧着した後、基材を剥離して電極合材層を転写することでエネルギー貯蔵デバイス電極を作製することができる。このように、転写により電極を作製した場合であっても、本発明のプライマー層は高い密着力を発揮し得る。
　この場合、基材は任意であるが、集電体と同様の材料からなる基材を用いることができ、銅箔が好ましい。
　加熱圧着時の温度は、特に限定されるものではないが、プライマー層の密着力をより高めることを考慮すると、上記水酸基含有ポリマーの融点以上の温度とすることが好ましい。上記温度は、水酸基含有ポリマーの種類によって異なるが、概ね１１５℃未満が好ましく、１１０℃以下がより好ましく、１０５℃以下がより一層好ましい。また、その下限は、５０℃以上が好ましく、５５℃以上がより好ましく、６０℃以上がより一層好ましい。
　加熱圧着時の圧力も特に限定されるものではないが、線圧１ｋＮ／ｃｍ以上が好ましく、５ｋＮ／ｃｍ以上がより好ましく、１０ｋＮ／ｃｍ以上がより一層好ましい。
　圧着は、一般に採用されている方法を用いることができるが、特に金型プレス法やロールプレス法が好ましい。
［７］エネルギー貯蔵デバイス
　本発明に係るエネルギー貯蔵デバイスは、上述したエネルギー貯蔵デバイス用電極を備えたものであり、より具体的には、少なくとも一対の正負極と、これら各極間に介在するセパレータと、電解質とを備えて構成され、正負極の少なくとも一方が、上述したエネルギー貯蔵デバイス用電極から構成される。
　このエネルギー貯蔵デバイスは、電極として上述したエネルギー貯蔵デバイス用電極を用いることにその特徴があるため、その他のデバイス構成部材であるセパレータや、電解質などは、公知の材料から適宜選択して用いることができる。セパレータとしては、例えば、セルロース系セパレータ、ポリオレフィン系セパレータ等が挙げられる。
　電解質としては、電解質塩を溶媒に溶かしてなる液体電解質、固体電解質のいずれでもよく、また水系、非水系のいずれでもよいが、本発明のエネルギー貯蔵デバイス用電極は、固体電解質を用いた電池、特に全固体電池（例えば、全固体リチウムイオン電池）に適用することが好ましい。
　電解質塩としては、例えば、ＬｉＰＦ6、ＬｉＢＦ4、ＬｉＮ（ＳＯ2Ｆ）2、ＬｉＮ（Ｃ2Ｆ5ＳＯ2）2、ＬｉＡｓＦ6、ＬｉＳｂＦ6、ＬｉＡｌＦ4、ＬｉＧａＦ4、ＬｉＩｎＦ4、ＬｉＣｌＯ4、ＬｉＮ（ＣＦ3ＳＯ2）2、ＬｉＣＦ3ＳＯ3、ＬｉＳｉＦ6、ＬｉＮ（ＣＦ3ＳＯ2）、（Ｃ4Ｆ9ＳＯ2）等のリチウム塩、ＬｉＩ、ＮａＩ、ＫＩ、ＣｓＩ、ＣａＩ2等の金属ヨウ化物、４級イミダゾリウム化合物のヨウ化物塩、テトラアルキルアンモニウム化合物のヨウ化物塩および過塩素酸塩、ＬｉＢｒ、ＮａＢｒ、ＫＢｒ、ＣｓＢｒ、ＣａＢｒ2等の金属臭化物等が挙げられる。これらの電解質塩は、１種を単独で用いても、２種以上を組み合わせて用いてもよい。
　電解質用溶媒としては、電池を構成する物質に対して腐食や分解を生じさせて性能を劣化させるものでなく、上記電解質塩を溶解するものであれば特に限定されない。例えば、非水系の溶媒として、エチレンカーボネート、プロピレンカーボネート、ブチレンカーボネート、γ－ブチロラクトン等の環状エステル類、テトラヒドロフラン、ジメトキシエタン等のエーテル類、酢酸メチル、ジメチルカーボネート、ジエチルカーボネート、エチルメチルカーボネート等の鎖状エステル類、アセトニトリル等のニトリル類等が用いられる。これらの溶媒は、１種を単独で用いても、２種以上を組み合わせて用いてもよい。
　また、固体電解質としては、硫化物系固体電解質および酸化物系固体電解質等の無機固体電解質や、高分子系電解質等の有機固体電解質を好適に用いることができる。これらの固体電解質を用いることで電解液を使用しない全固体電池を得ることができる。
　硫化物系固体電解質としては、Ｌｉ2Ｓ－ＳｉＳ2－リチウム化合物（ここで、リチウム化合物はＬｉ3ＰＯ4、ＬｉＩおよびＬｉ4ＳｉＯ4からなる群より選ばれる少なくとも１種である）、Ｌｉ2Ｓ－Ｐ2Ｓ5、Ｌｉ2Ｓ－Ｐ2Ｏ5、Ｌｉ2Ｓ－Ｂ2Ｓ5、Ｌｉ2Ｓ－Ｐ2Ｓ5－ＧｅＳ2等のチオリシコン系材料等を挙げることができる。
　酸化物系固体電解質としては、ガーネット型構造の酸化物であるＬｉ5Ｌａ3Ｍ2Ｏ12（Ｍ＝Ｎｂ，Ｔａ）やＬｉ7Ｌａ3Ｚｒ2Ｏ12、ＬＩＳＩＣＯＮと総称されるγ－Ｌｉ3ＰＯ4構造を基本とする酸素酸塩化合物、ペロブスカイト型、ＬＩＰＯＮと総称されるＬｉ3.3ＰＯ3.8Ｎ0.22、ナトリウム／アルミナ等を挙げることができる。
　高分子系固体電解質としては、ポリエチレンオキシド系材料や、ヘキサフルオロプロピレン、テトラフルオロエチレン、トリフルオロエチレン、エチレン、プロピレン、アクリロニトリル、塩化ビニリデン、アクリル酸、メタクリル酸、メチルアクリレート、エチルアクリレート、メチルメタクリレート、スチレンおよびフッ化ビニリデン等のモノマーを重合または共重合して得られる高分子化合物等が挙げられる。
　なお、高分子系固体電解質は、支持塩および可塑剤を含んでいてもよい。
　支持塩の具体例としては、リチウム（フルオロスルホニルイミド）等を挙げることができ、可塑剤としては、スクシノニトリル等が挙げられる。
　以下、製造例、実施例、比較例および参考例を挙げて、本発明をより具体的に説明するが、本発明は下記の実施例に限定されるものではない。
　なお、実施例で用いた装置は下記のとおりである。
（１）プローブ型超音波照射装置（導電性炭素の分散）
　Ｈｉｅｌｓｃｈｅｒ　Ｕｌｔｒａｓｏｎｉｃｓ社製、ＵＩＰ１０００
（２）ワイヤーバーコーター（プライマー層形成）
　（株）エスエムテー製、ＰＭ－９０５０ＭＣ
（３）ロールプレス機（電極の圧縮）
　有限会社タクミ技研製、ＳＡ－６０２
（４）粘着・皮膜剥離解析装置（密着力測定）
　協和界面科学（株）製、ＶＰＡ－３
（５）示差走査熱量計（ＤＳＣ）（融点の測定）
　装置：株式会社日立ハイテクサイエンス社製、示差走査熱量計ＤＳＣ７０２０
　サンプル量：５－１０ｍｇ
　測定パン：Ａｌ（密閉）
　測定条件：３０℃から２００℃まで１０℃／ｍｉｎで昇温し、１ｍｉｎ保持した。２００℃から３０℃まで１０℃／ｍｉｎで降温し１ｍｉｎ保持した。その後、３０℃から２００℃まで１０℃／ｍｉｎで昇温し、吸熱ピークの温度を融点とした。
（６）トライポギア　ＴＹＰＥ３０Ｓ（スクラッチ試験）
　新東科学（株）製、トライポギア　ＴＹＰＥ３０Ｓ
　荷重：５００ｇ
　また、使用した原料等は以下のとおりである。
ＡＢ：アセチレンブラック、デンカ（株）製、デンカブラックＬｉ４３５
ＷＳ－７００：（株）日本触媒製、オキサゾリンポリマーを含む水溶液、エポクロス（登録商標）ＷＳ－７００、重量平均分子量：４．０×１０4、固形分濃度：２５．０質量％
ＷＳ－３００：（株）日本触媒製、オキサゾリンポリマーを含む水溶液、エポクロス（登録商標）ＷＳ－３００、重量平均分子量：１．２×１０5、固形分濃度：１０．０質量％
ポリビニルピロリドン：第一工業製薬（株）製、ピッツコール（登録商標）Ｋ９０、重量平均分子量１，２００，０００
Ｅ－４５：明成化学工業（株）製、ポリエチレンオキサイド、アルコックス（登録商標）Ｅ－４５、重量平均分子量：６００，０００、分子中に占める水酸基の質量割合：５．７×１０-5、融点：６１℃
Ｒ－１５０：明成化学工業（株）製、ポリエチレンオキサイド、アルコックス（登録商標）Ｒ－１５０、重量平均分子量：１００，０００、分子中に占める水酸基の質量割合：３．４×１０-4、融点：６１℃
ＣＰ－Ａ２Ｈ：明成化学工業（株）製、エチレンオキサイドとプロピレンオキサイド、アリルグリシジルエーテルのランダム共重合体、アルコックス（登録商標）ＣＰ－Ａ２Ｈ、重量平均分子量：８０，０００、分子中に占める水酸基の質量割合：４．３×１０-4、融点：４５℃
Ｅ－３００：明成化学工業（株）製、ポリエチレンオキサイド、アルコックス（登録商標）Ｅ－３００、重量平均分子量：７，０００，０００、分子中に占める水酸基の質量割合：４．９×１０-6、融点：７０℃
ＰＥＧ２０ｋ：三洋化成（株）製、ポリエチレングリコール、ＰＥＧ２０，０００、重量平均分子量：２０，０００、分子中に占める水酸基の質量割合：１．７×１０-3、融点：６３℃
ＰＥＧ１０ｋ：三洋化成（株）製、ポリエチレングリコール、ＰＥＧ１０，０００、重量平均分子量：１０，０００、分子中に占める水酸基の質量割合：３．４×１０-3、融点：６２℃
ＰＥＧ６ｋ：三洋化成（株）製、ポリエチレングリコール、ＰＥＧ６，０００、重量平均分子量：６，０００、分子中に占める水酸基の質量割合：５．６７×１０-3、融点：６１℃
２－プロパノール：純正化学（株）製
ＣＢＴ－１：城北化学工業（株）製、カルボキシベンゾトリアゾール（ＣＡＳ　ＲＮ：６０９３２－５８－３）
Ａ－３０：東亜合成（株）製、ポリアクリル酸アンモニウム、アロン（登録商標）Ａ－３０、重量平均分子量１００，０００、固形分濃度３１．６質量％
〈水酸基含有ポリマーの分子中に占める水酸基の質量割合の計算〉
　上記の水酸基含有ポリマーの分子中に占める水酸基の質量割合は下記式により算出した。
　水酸基の割合＝（１７×水酸基の数）／ポリマーの重量平均分子量
［１］分散液の調製
［製造例１］分散液Ａの調製
　導電性炭素材料であるアセチレンブラック（以下、ＡＢと略す。）１．５ｇ（１００質量部）と、オキサゾリンポリマーを含む水溶液であるＷＳ－７００　３．０ｇ（固形分として５０質量部）と、純水３８．３６ｇと、２－プロパノール２．１４ｇとを混合した。得られた混合物に対して、プローブ型超音波照射装置を用いて１５分超音波処理を行い、均一に導電性炭素材料が分散した分散液Ａを調製した。
［製造例２］分散液Ｂの調製
　導電性炭素材料であるＡＢ１．５ｇ（１００質量部）と、オキサゾリンポリマーを含む水溶液であるＷＳ－３００　７．５ｇ（固形分として５０質量部）と、純水３３．８６ｇと、２－プロパノール２．１４ｇとを混合した。得られた混合物に対して、プローブ型超音波照射装置を用いて１５分超音波処理を行い、均一に導電性炭素材料が分散した分散液Ｂを調製した。
［製造例３］分散液Ｃの調製
　導電性炭素材料であるＡＢ１．４ｇ（１００質量部）と、ポリビニルピロリドンＫ９０　０．７ｇ（５０質量部）と、純水３７．９０ｇと、２－プロパノール２．００ｇとを混合した。得られた混合物に対して、プローブ型超音波照射装置を用いて１５分超音波処理を行い、均一に導電性炭素材料が分散した分散液Ｃを調製した。
［２］エネルギー貯蔵デバイス電極用薄膜形成組成物の調製
［実施例１－１］薄膜形成組成物Ａの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ａを調製した。薄膜形成組成物ＡはＡＢが均一に分散した黒色のインクだった。
［実施例１－２］薄膜形成組成物Ｂの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液１．２ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｂを調製した。薄膜形成組成物ＢはＡＢが均一に分散した黒色のインクだった。
［実施例１－３］薄膜形成組成物Ｃの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液１．６ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｃを調製した。薄膜形成組成物ＣはＡＢが均一に分散した黒色のインクだった。
［実施例１－４］薄膜形成組成物Ｄの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液２．４ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｄを調製した。薄膜形成組成物ＤはＡＢが均一に分散した黒色のインクだった。
［実施例１－５］薄膜形成組成物Ｅの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液２．８ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｅを調製した。薄膜形成組成物ＥはＡＢが均一に分散した黒色のインクだった。
［実施例１－６］薄膜形成組成物Ｆの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液４．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｆを調製した。薄膜形成組成物ＦはＡＢが均一に分散した黒色のインクだった。
［実施例１－７］薄膜形成組成物Ｇの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　３．０ｇと、Ｅ－４５の５質量％水溶液４．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｇを調製した。薄膜形成組成物ＧはＡＢが均一に分散した黒色のインクだった。
［実施例１－８］薄膜形成組成物Ｈの調製
　水９．５ｇに水酸基含有ポリマーであるＲ－１５０を０．５ｇ溶解させ、Ｒ－１５０の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｒ－１５０の５質量％水溶液４．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｈを調製した。薄膜形成組成物ＨはＡＢが均一に分散した黒色のインクだった。
［実施例１－９］薄膜形成組成物Ｉの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例２で調製した分散液Ｂ　６．０ｇと、Ｅ－４５の５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｉを調製した。薄膜形成組成物ＩはＡＢが均一に分散した黒色のインクだった。
［実施例１－１０］薄膜形成組成物Ｊの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例２で調製した分散液Ｂ　６．０ｇと、Ｅ－４５の５質量％水溶液４．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｊを調製した。薄膜形成組成物ＪはＡＢが均一に分散した黒色のインクだった。
［実施例１－１１］薄膜形成組成物Ｋの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、ＣＰ－Ａ２Ｈの５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、ＣＰ－Ａ２Ｈの５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｋを調製した。薄膜形成組成物ＫはＡＢが均一に分散した黒色のインクだった。
［実施例１－１２］薄膜形成組成物Ｌの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－４５の５質量％水溶液０．８ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｌを調製した。薄膜形成組成物ＬはＡＢが均一に分散した黒色のインクだった。
　上記実施例のまとめを表１に示す。
Figure JPOXMLDOC01-appb-T000013
［実施例１－１３］薄膜形成組成物Ｍの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。水９．５ｇに複素環式化合物であるＣＢＴ－１を０．５ｇ溶解させ、ＣＢＴ－１の５質量％水溶液を調製した。さらに、水８．４ｇにＡ－３０を１．６ｇ溶解させ、Ａ－３０の５質量％溶液を調製した。製造例１で調製した分散液Ａ　７．５ｇと、Ｅ－４５の５質量％水溶液２．５ｇと、ＣＢＴ－１の５質量％水溶液１．０ｇと、Ａ－３０の５質量％水溶液１．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｍを調製した。薄膜形成組成物ＭはＡＢが均一に分散した黒色のインクだった。
［実施例１－１４］薄膜形成組成物Ｎの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。水９．５ｇに複素環式化合物であるＣＢＴ－１を０．５ｇ溶解させ、ＣＢＴ－１の５質量％水溶液を調製した。さらに、水８．４ｇにＡ－３０を１．６ｇ溶解させ、Ａ－３０の５質量％溶液を調製した。製造例１で調製した分散液Ａ　７．５ｇと、Ｅ－４５の５質量％水溶液２．５ｇと、ＣＢＴ－１の５質量％水溶液０．５ｇと、Ａ－３０の５質量％水溶液１．２５ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｎを調製した。薄膜形成組成物ＮはＡＢが均一に分散した黒色のインクだった。
［実施例１－１５］薄膜形成組成物Ｏの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。水９．５ｇに複素環式化合物であるＣＢＴ－１を０．５ｇ溶解させ、ＣＢＴ－１の５質量％水溶液を調製した。さらに、水８．４ｇにＡ－３０を１．６ｇ溶解させ、Ａ－３０の５質量％溶液を調製した。製造例１で調製した分散液Ａ　７．５ｇと、Ｅ－４５の５質量％水溶液２．５ｇと、ＣＢＴ－１の５質量％水溶液１．０ｇと、Ａ－３０の５質量％水溶液１．２５ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｍを調製した。薄膜形成組成物ＯはＡＢが均一に分散した黒色のインクだった。
［実施例１－１６］薄膜形成組成物Ｐの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。水８．４ｇにＡ－３０を１．６ｇ溶解させ、Ａ－３０の５質量％溶液を調製した。製造例１で調製した分散液Ａ　７．５ｇと、Ｅ－４５の５質量％水溶液２．５ｇと、Ａ－３０の５質量％水溶液１．２５ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物Ｐを調製した。薄膜形成組成物ＰはＡＢが均一に分散した黒色のインクだった。
　上記実施例のまとめを表２に示す。
Figure JPOXMLDOC01-appb-T000014
［比較例１－１］薄膜形成組成物ａの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－４５を０．５ｇ溶解させ、Ｅ－４５の５質量％水溶液を調製した。製造例３で調製した分散液Ｃ　６．０ｇと、Ｅ－４５の５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物ａを調製した。薄膜形成組成物ａはＡＢが均一に分散した黒色のインクだった。
［比較例１－２］薄膜形成組成物ｂ
　製造例１で調製した分散液Ａをそのまま薄膜形成用組成物ｂとして用いた。
［比較例１－３］薄膜形成組成物ｃの調製
　ＡＢ１．４ｇ（１００質量部）と、水酸基含有ポリマーであるＥ－４５　０．７ｇ（５０質量部）と、純水３７．９０ｇと、２－プロパノール２．００ｇとを混合した。得られた混合物に対して、プローブ型超音波照射装置を用いて１５分超音波処理を行った。薄膜形成組成物ｃはペースト状に増粘し、凝集体が存在する不均一な分散液だった。
［比較例１－４］薄膜形成組成物ｄの調製
　水９．５ｇに水酸基含有ポリマーであるＥ－３００を０．５ｇ溶解させ、Ｅ－３００の５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、Ｅ－３００の５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物ｄを調製した。薄膜形成組成物ｄはＡＢが均一に分散した黒色の粘稠なインクだった。
［比較例１－５］薄膜形成組成物ｅの調製
　水９．５ｇに水酸基含有ポリマーであるＰＥＧ２０ｋを０．５ｇ溶解させ、ＰＥＧ２０ｋの５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、ＰＥＧ２０ｋ０の５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物ｅを調製した。薄膜形成組成物ｅはＡＢが均一に分散した黒色のインクだった。
［比較例１－６］薄膜形成組成物ｆの調製
　水９．５ｇに水酸基含有ポリマーであるＰＥＧ１０ｋを０．５ｇ溶解させ、ＰＥＧ１０ｋの５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、ＰＥＧ１０ｋ０の５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物ｆを調製した。薄膜形成組成物ｆはＡＢが均一に分散した黒色のインクだった。
［比較例１－７］薄膜形成組成物ｇの調製
　水９．５ｇに水酸基含有ポリマーであるＰＥＧ６ｋを０．５ｇ溶解させ、ＰＥＧ６ｋの５質量％水溶液を調製した。製造例１で調製した分散液Ａ　６．０ｇと、ＰＥＧ６ｋの５質量％水溶液２．０ｇとを混合し、固形分濃度を５質量％とした薄膜形成組成物ｇを調製した。薄膜形成組成ｇはＡＢが均一に分散した黒色のインクだった。
　上記比較例のまとめを表３に示す。
Figure JPOXMLDOC01-appb-T000015
［３］薄膜（プライマー層）の作製
［実施例２－１］
　実施例１－１で調製した組成物Ａを、集電体である銅箔（厚さ１０μｍ）にワイヤーバーコーターでＯＳＰ－３０を用いて均一に展開した後、１２０℃で２０分乾燥して薄膜（プライマー層）を形成し、銅箔とプライマー層との積層体を作製した。得られた積層体は、銅箔の表面が導電性炭素材料により均一に覆われていた（想定目付量：１，２００ｍｇ／ｍ2）。
　上述のとおり、想定目付量とは、所定の固形分濃度の薄膜形成用組成物を所定のワイヤーバーコーターを用いて集電体上に塗工した際に想定される目付量を意味する。本発明において、固形分濃度５質量％の薄膜形成用組成物を用いた場合の想定目付量は、以下のとおりである。
　ＯＳＰ－３０：１，２００ｍｇ／ｍ2
［実施例２－２～２－１６，比較例２－１～２－７］
　組成物Ａを、実施例１－２～１－１６，比較例１－１～１－７で調製した組成物Ｂ～Ｐ、ａ～ｇに変更した以外は、実施例２－１と同様に薄膜（プライマー層）を形成し、積層体を作製した。
〔成膜性〕
　上記実施例２－１～２－１６および比較例２－１～２－７で作製した薄膜を目視により観察し、その成膜性を以下の基準により評価した。結果を表４および表５に示す。
Ａ：銅箔の表面が導電性炭素材料により均一に覆われた積層体。
Ｂ：筋状に塗工不良部分が発生し、銅箔の表面が不均一に導電性炭素材料により覆われた積層体。
－：分散性不良のため成膜不可。
Figure JPOXMLDOC01-appb-T000016
Figure JPOXMLDOC01-appb-T000017
　表４および表５に示されるように、実施例２－１～２－１６の組成物Ａ～Ｐを用いた場合、均一な薄膜（プライマー層）が形成できた。
　これに対し、比較例２－１～２－７の組成物ａ～ｇを用いた場合、組成物ｃと組成物ｄ以外は組成物Ａ～Ｐと同様に均一な薄膜（プライマー層）が形成できた。組成物ｃは凝集体が存在する不均一な分散液であったため均一な薄膜（プライマー層）は形成できなかった。また、組成物ｄは均一にＡＢが分散していたが、粘度が高く粘稠なインクであり、成膜時に筋状に塗工不良部分が発生し、銅箔の表面が不均一に導電性炭素材料により覆われた薄膜（プライマー層）となった。
　〔スクラッチ試験〕
　複素環式化合物の添加によるスクラッチ耐性を確かめるために、実施例２－１３～２－１５で作製した銅箔とプライマー層との積層体を、４０ｍｍ×９０ｍｍに切り出して加工した。上記積層体をプライマー層が表面となるようにＴＲＩＢＯＧＩＥＡＲ　ＴＹＰＥ３０Ｓに張り付けて固定した。ＴＲＩＢＯＧＩＥＡＲ　ＴＹＰＥ３０Ｓの擦る治具のプライマー層に接する部分（面積２０ｍｍ×２０ｍｍ）には、プロワイプマイクロソフトワイパーＳ２２０（大王製紙（株）製）を設けた。５００ｇの荷重をかけ、プライマー層を摺動距離５０ｍｍ往復させた後、プライマー層の状態を目視で観察し、剥離の有無を以下の基準により評価した。結果を表６に示す。
Ａ：プライマー層のスクラッチ耐性が高く、傷や剥離が確認されなかった。
Ｂ：プライマー層のスクラッチ耐性が低く、傷や剥離している部分が確認された。
Figure JPOXMLDOC01-appb-T000018
［４］転写電極の作製
［実施例３－１］
　実施例２－１で作製した銅箔とプライマー層との積層体を、成膜後１時間以内にドライブース（温度２２℃、露点－５０℃）に移した。その後、上記積層体を３０ｍｍ×１００ｍｍに切り出して加工した。銅箔上に電極合材層が形成された電極合材層複合体Ａも同様に２５ｍｍ×７０ｍｍに切り出して加工した。プライマー層と電極合材層塗工面を対向して重ね合わせ、６０℃に加熱したロールプレス機で線圧１０ｋＮ／ｃｍで圧着して、プライマー層を形成した積層体と電極合材層複合体Ａを一体化させた。その後、この一体化されたものから、電極合材層複合体Ａの銅箔のみを剥離して、積層体上に電極合材層が転写された転写電極（成膜直後）を得た。
　なお、電極合材層複合体Ａとしては、黒鉛／ＣＭＣ／ＳＢＲ（スチレン・ブタジエンゴム）＝９７．０／１．０／２．０（質量比）の組成物を、銅箔（厚み１０μｍ）に塗工（塗工量１６．１ｍｇ／ｃｍ2）し、乾燥したものを用いた。
　また、銅箔とプライマー層との積層体として、空調室（温度２２℃、露点１０－１５℃）環境にて７２時間静置したものを用いたこと以外は、上記と同様にして、転写電極（空調室保管後）を作製した。
［実施例３－２～３－１６，比較例３－１～３－６］
　積層体を、実施例２－２～２－１６，比較例２－１、２－２および２－４～２－７で作製した積層体に変更した以外は、実施例３－１と同様にして、転写電極（成膜直後）および転写電極（空調室保管後）を作製した。
〔転写電極の作製可否〕
　上記実施例３－１～３－１６および比較例３－１～３－６で作製した転写電極を目視により観察し、転写電極の作製可否を以下の基準により評価した。結果を表７および表８に示す。
Ａ：電極合材層が複合集電体上に固定化されている。
Ｂ：電極合材層が複合集電体上に固定化されていない。
〔密着力試験〕
　上記実施例３－１～３－１６および比較例３－１～３－６で作製した転写電極を、それぞれ２５ｍｍ幅で切り出し、電極合材層面に２０ｍｍ幅の両面テープを貼り付けてガラス基板上に固定した。これを粘着・皮膜剥離解析装置に固定して剥離角度９０°かつ剥離速度１００ｍｍ／ｍｉｎで剥離試験を行い、下記の算出式により密着力および密着力維持率を算出した。結果を表７および表８に併せて示す。

　密着力（Ｎ／ｍ）＝測定値*（Ｎ）／（サンプル測定幅（ｍｍ）×１０-3）
*測定値は剥離距離１０ｍｍから３５ｍｍの平均値とした。

　密着力維持率（％）＝空調室保管後の密着力（Ｎ／ｍ）／成膜直後の密着力（Ｎ／ｍ）×１００
*成膜直後、空調室保管後ともに同様の方法で密着力を算出した。
Figure JPOXMLDOC01-appb-T000019
Figure JPOXMLDOC01-appb-T000020
　表７および表８に示されるように、実施例３－１～３－１６の組成物Ａ～Ｐを用いた場合、初期密着力は高く、実用的な密着力を備えた薄膜（プライマー層）であった。空調室保管前後で密着力の変化が小さく、高い密着力維持率を示した。本発明の組成物を用いることで実用的な密着力と密着力維持率を有することが確認できた。
　一方で、比較例３－１の組成物ａを用いた場合、初期密着力は高く、実用的な密着力を備えた薄膜（プライマー層）であったが、空調室保管後は１２．８Ｎ／ｍに密着力が低下し、密着力維持率も２１．２％と低い密着力維持率であった。
　また、比較例３－２～３－６の組成物ｂ～ｇは初期密着力が小さく、実用的な密着力を備える薄膜（プライマー層）とはならかったため、空調室保管後の密着力の測定は割愛した。

Claims (23)

  1. 　導電性炭素材料と、側鎖にオキサゾリン基を有するポリマーと、重量平均分子量が５０，０００～５，０００，０００である水酸基含有ポリマーと、溶媒とを含むエネルギー貯蔵デバイス電極用薄膜形成組成物。
  2. 　上記水酸基含有ポリマーの分子中に占める水酸基の質量割合が、１×１０-5～１００×１０-5である請求項１記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  3. 　上記水酸基含有ポリマーの分子中に占める水酸基の質量割合が、１×１０-5～５０×１０-5である請求項２記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  4. 　上記水酸基含有ポリマーの含有量が、上記導電性炭素材料１００質量部に対して２５～２００質量部である請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  5. 　上記水酸基含有ポリマーが、ポリアルキレングリコールである請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  6. 　上記ポリアルキレングリコールが、ポリエチレングリコールである請求項５記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  7. 　上記側鎖にオキサゾリン基を有するポリマーが、２位に重合性炭素－炭素二重結合含有基を有する式（１）で示されるオキサゾリンモノマーと、親水性官能基を有する（メタ）アクリル系モノマーとをラジカル重合したポリマーである請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
    Figure JPOXMLDOC01-appb-C000001
     （式中、Ｘは、重合性炭素－炭素二重結合を含む鎖状炭化水素基を表し、Ｒ1～Ｒ4は、互いに独立して、水素原子、ハロゲン原子、炭素数１～５の分岐構造を有していてもよいアルキル基、炭素数６～２０のアリール基、または炭素数７～２０のアラルキル基を表す。）
  8. 　上記側鎖にオキサゾリン基を有するポリマーの含有量が、上記導電性炭素材料１００質量部に対して２０～６０質量部である請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  9. 　上記導電性炭素材料が、アセチレンブラック、カーボンブラック、ケッチェンブラック、ファーネスブラック、チャンネルブラックおよびランプブラックから選ばれる１種または２種以上である請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  10. 　さらに、下記式（ｎ１）で表される複素環式化合物を含む請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
    Figure JPOXMLDOC01-appb-C000002
     （式中、ＲaおよびＲbは、それぞれ独立して、水素原子、ハロゲン原子、置換基を有していてもよい炭素数１～６のアルキル基、置換基を有していてもよい炭素数２～６のアルケニル基、または置換基を有していてもよい炭素数６～１２のアリール基を表し、ＲaおよびＲbが互いに結合して炭素数４～６の環を形成していてもよく、Ｘaは、ＮまたはＣＨである。）
  11. 　上記置換基が、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基およびエポキシ基からなる群より選ばれる少なくとも１種である請求項１０記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
  12. 　上記複素環式化合物が、下記式（ｎ２）で表される請求項１０記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
    Figure JPOXMLDOC01-appb-C000003
     （式中、Ｙaは、水素原子、カルボキシ基、ヒドロキシ基、チオール基、アミノ基、スルホン酸基またはエポキシ基を表す。Ｘaは、上記と同じである。）
  13. 　上記複素環式化合物が、下記式（ｎ３）で表される請求項１２記載のエネルギー貯蔵デバイス電極用薄膜形成組成物。
    Figure JPOXMLDOC01-appb-C000004
  14. 　請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成用組成物から得られる薄膜からなるプライマー層。
  15. 　集電基板と、この集電基板の上に形成された請求項１４記載のプライマー層とを備えるエネルギー貯蔵デバイスの電極用複合集電体。
  16. 　集電基板が、銅箔またはアルミニウム箔である請求項１５記載のエネルギー貯蔵デバイスの電極用複合集電体。
  17. 　請求項１６記載のエネルギー貯蔵デバイスの電極用複合集電体を備えるエネルギー貯蔵デバイス用電極。
  18. 　アノード電極用である請求項１７記載のエネルギー貯蔵デバイス用電極。
  19. 　請求項１７記載のエネルギー貯蔵デバイス用電極を備えるエネルギー貯蔵デバイス。
  20. 　リチウムイオン電池である請求項１９記載のエネルギー貯蔵デバイス。
  21. 　全固体リチウムイオン電池である請求項２０記載のエネルギー貯蔵デバイス。
  22. 　集電基板の上に、請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成用組成物を塗布し、乾燥してプライマー層を形成した後、このプライマー層の上に電極合材シートを積層し、加熱圧着するエネルギー貯蔵デバイス電極の製造方法。
  23. 　基材上に、電極合材層形成用組成物を塗布し、乾燥して電極合材層を形成する工程と、
    　この電極合材層の上に、請求項１～３のいずれか１項記載のエネルギー貯蔵デバイス電極用薄膜形成用組成物を塗布し、乾燥してプライマー層を形成する工程と、
    　このプライマー層の上に、集電基板を積層して加熱圧着した後、上記基材を剥離する工程を備えるエネルギー貯蔵デバイス電極の製造方法。
PCT/JP2023/016043 2022-04-27 2023-04-24 エネルギー貯蔵デバイス電極用薄膜形成組成物 WO2023210558A1 (ja)