WO2023190612A1 - 積層体、発光デバイス、及びセンシングデバイス - Google Patents
積層体、発光デバイス、及びセンシングデバイス Download PDFInfo
- Publication number
- WO2023190612A1 WO2023190612A1 PCT/JP2023/012691 JP2023012691W WO2023190612A1 WO 2023190612 A1 WO2023190612 A1 WO 2023190612A1 JP 2023012691 W JP2023012691 W JP 2023012691W WO 2023190612 A1 WO2023190612 A1 WO 2023190612A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- laminate
- metal layer
- base
- metal
- Prior art date
Abstract
本発明は、基体と下地層と金属層とをこの順に備え、前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である積層体、該積層体を有する、発光デバイス、及びセンシングデバイスに関する。
Description
本発明は、積層体、発光デバイス、及びセンシングデバイスに関する。
近年、局在表面プラズモン共鳴(localized surface plasmon resonance:LSPR)とよばれる光学現象が注目されている。
LSPRは、波長スケール以下の領域に閉じ込められた強い強度の共鳴であり、金属ナノ粒子等の金属ナノ構造体に光を入射すると、特定の波長域において金属ナノ構造体表面上の電子の集団振動現象が起こり、吸収および散乱による光の強い消光が生じる、という光学現象(LSPR現象)である。
LSPRは、波長スケール以下の領域に閉じ込められた強い強度の共鳴であり、金属ナノ粒子等の金属ナノ構造体に光を入射すると、特定の波長域において金属ナノ構造体表面上の電子の集団振動現象が起こり、吸収および散乱による光の強い消光が生じる、という光学現象(LSPR現象)である。
この現象を応用することにより様々なデバイスの高精度化ができるものと期待されており、表示デバイスにおける波長制御、LED(light emitting diode)や太陽電池における高効率化、センシングデバイスにおける高感度化等が検討されている。
上記現象の発現の有無や、上記現象が生じる光の波長域や周波数は、光を入射する金属ナノ構造体の材料、金属粒子の粒径、密度等に強く依存することが知られている。
例えば、非特許文献1には、LSPRの共鳴波長は金属ナノ粒子の粒径が大きくなると長波長側にシフトすることが記載されている。
例えば、非特許文献1には、LSPRの共鳴波長は金属ナノ粒子の粒径が大きくなると長波長側にシフトすることが記載されている。
一方、金属ナノ粒子の粒径調整方法として、非特許文献2には、シリコンウエハ上に金属ナノ粒子を付着させた後に高温で熱処理することにより、金属ナノ粒子の粒径を大きくすることができる旨が記載されている。
A.R. Shafiqa et al 2018 J.Phys.:Conf.Ser.1083 012040
Xin Sun and Hao Li 2013 Nanotechnology 24 355706
上記のようなLSPR現象を生じる金属ナノ構造体は各種の基体上に形成することができ、基体としてフィルム基材を用いた場合には、生産性向上などの利点があり用途拡大が見込まれる。しかしながら、基体としてフィルム基材を用いた場合、非特許文献2に開示されているような高温処理は耐熱性に問題が生じるため適用が難しい。
このように、LSPR現象を生じ得る金属層を有する積層体を得るには課題が残されている。
本発明は、上記に鑑みてなされたものであり、LSPR現象を生じ得る金属層を有する積層体を提供することを目的とする。
このように、LSPR現象を生じ得る金属層を有する積層体を得るには課題が残されている。
本発明は、上記に鑑みてなされたものであり、LSPR現象を生じ得る金属層を有する積層体を提供することを目的とする。
本発明者等は、鋭意検討を重ねた結果、基体、下地層、金属層、をこの順に備える積層体において、下地層の金属層側の面の算術平均表面粗さRaを一定以上の大きさとすることにより、LSPR現象を生じ得る大きさの金属ナノ構造を有する金属層を備えた積層体が得られることを見出し、本発明を完成するに至った。
すなわち、本発明は以下のとおりである。
〔1〕
基体と下地層と金属層とをこの順に備え、
前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、
前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である積層体。
〔2〕
前記下地層の厚みが、20~1000nmである〔1〕に記載の積層体。
〔3〕
前記下地層が、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、インジウム亜鉛酸化物(IZO)、SiO2、AlO3、TiO2、及びZnOから選択される少なくとも一種を含む無機酸化物含有層である〔1〕に記載の積層体。
〔4〕
前記無機酸化物含有層が、前記酸化インジウム(In2O3)、前記インジウム錫酸化物(ITO)、及び前記インジウム亜鉛酸化物(IZO)から選択される少なくとも一種を含有する酸化インジウム含有層である、〔3〕に記載の積層体。
〔5〕
前記積層体における前記金属層側表面の算術平均表面粗さRaが3nm以上である、〔1〕に記載の積層体。
〔6〕
前記金属層が、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有する、〔1〕に記載の積層体。
〔7〕
前記金属層が銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有する、〔6〕に記載の積層体。
〔8〕
前記金属層が、LSPR現象を生じ得るものである、〔1〕に記載の積層体。
〔9〕
前記基体が基材フィルムである、〔1〕に記載の積層体。
〔10〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有する発光デバイス。
〔11〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有するセンシングデバイス。
〔1〕
基体と下地層と金属層とをこの順に備え、
前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、
前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である積層体。
〔2〕
前記下地層の厚みが、20~1000nmである〔1〕に記載の積層体。
〔3〕
前記下地層が、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、インジウム亜鉛酸化物(IZO)、SiO2、AlO3、TiO2、及びZnOから選択される少なくとも一種を含む無機酸化物含有層である〔1〕に記載の積層体。
〔4〕
前記無機酸化物含有層が、前記酸化インジウム(In2O3)、前記インジウム錫酸化物(ITO)、及び前記インジウム亜鉛酸化物(IZO)から選択される少なくとも一種を含有する酸化インジウム含有層である、〔3〕に記載の積層体。
〔5〕
前記積層体における前記金属層側表面の算術平均表面粗さRaが3nm以上である、〔1〕に記載の積層体。
〔6〕
前記金属層が、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有する、〔1〕に記載の積層体。
〔7〕
前記金属層が銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有する、〔6〕に記載の積層体。
〔8〕
前記金属層が、LSPR現象を生じ得るものである、〔1〕に記載の積層体。
〔9〕
前記基体が基材フィルムである、〔1〕に記載の積層体。
〔10〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有する発光デバイス。
〔11〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有するセンシングデバイス。
本発明によれば、金属ナノ構造体の大きさが好適に制御された、LSPR現象を生じ得る金属層を有する積層体、発光デバイス、及びセンシングデバイスを提供することができる。
以下、添付図面を参照しつつ、本発明の好適な実施形態について説明する。以下においては、説明の便宜のために本発明の好適な実施形態のみを示すが、勿論、これによって本発明を限定しようとするものではない。
<1.基本構成>
本発明の実施形態にかかる積層体は、基体と下地層と金属層とをこの順に備え、前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である。
本発明の実施形態にかかる積層体は、基体と下地層と金属層とをこの順に備え、前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である。
図1に、本発明の一実施形態による積層体1の概略断面図を示す。また、図2に、本発明の一実施形態による積層体1の金属層側表面の原子間力顕微鏡写真(AFM画像)の一例を示す。
図1に示すように、積層体1は、基体10と、基体10の上に形成された、下地層11と、金属層12とをこの順で有する。
下地層11は、基体10上に連続状態で、言い換えれば、隙間なく、設けるのが好ましい。連続状態で設けることにより、下地層11、ひいては、積層体1の平滑性や、基体10と下地層11の密着性を向上させることができ、また、下地層11を面内にばらつきなく成膜することも容易となる。
図1に示すように、金属層12は下地層11上に積層されている。金属層12は複数の部分12aを含む。下地層11上に積層されることにより、これらの部分12aは、少なくとも一部において互いに不連続の状態、言い換えれば、少なくとも一部において隙間12bによって隔てられ、複数の部分12aが島状に形成される。
これらの各部分12aは金属を蒸着、スパッタ等することによって形成された粒子の集合体である。該粒子が基体10等の基体上で薄膜を形成する際には、基体上での粒子の表面拡散性が薄膜の形状に影響を及ぼす。
本発明の一実施形態による積層体1は、基体10上に、金属層側の面のRaが0.3nm以上である下地層11が積層されている。このような下地層上に金属をスパッタすることにより、形成された粒子の表面拡散性が促進され、LSPR現象を発現し得る金属薄膜の形状が得られるものと考えられる。
本発明の一実施形態による積層体1は、基体10上に、金属層側の面のRaが0.3nm以上である下地層11が積層されている。このような下地層上に金属をスパッタすることにより、形成された粒子の表面拡散性が促進され、LSPR現象を発現し得る金属薄膜の形状が得られるものと考えられる。
なお、本明細書でいう「不連続の状態」とは、隙間12bによって互いに僅かに離間した状態をいい、一部接触した状態を含んでいてもよい。不連続の形態は、特に限定されるものではなく、例えば、島状等が含まれる。
ここで「島状」とは、図2の積層体の金属層の表面の原子間力顕微鏡写真(AFM画像)に示されているように、スパッタ粒子の集合体である粒子同士が各々独立しており、それらの粒子が、互いに僅かに離間しまたは一部接触した状態で敷き詰められてなる構造を意味する。
<2.基体>
本実施形態にかかる積層体において、基体10を構成する材料としては、樹脂、ガラス、セラミックス等が挙げられる。
基体10は、基材フィルム、樹脂成型物基材、ガラス基材、またはLSPR現象を発現させたい物品のいずれかであってもよいが、積層体の生産性、用途拡大の観点から、基材フィルムであることが好ましい。
本実施形態にかかる積層体において、基体10を構成する材料としては、樹脂、ガラス、セラミックス等が挙げられる。
基体10は、基材フィルム、樹脂成型物基材、ガラス基材、またはLSPR現象を発現させたい物品のいずれかであってもよいが、積層体の生産性、用途拡大の観点から、基材フィルムであることが好ましい。
より具体的には、基材フィルムとしては、例えば、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)、ポリブチレンテレフタレート、ポリアミド、ポリ塩化ビニル、ポリカーボネート(PC)、シクロオレフィンポリマー(COP)、ポリスチレン、ポリプロピレン(PP)、ポリエチレン、ポリシクロオレフィン、ポリウレタン、アクリル(PMMA)、ABSなどの単独重合体や共重合体からなる透明フィルムを用いることができる。
但し、下地層11や金属層12を後に形成する観点から、蒸着やスパッタ等の処理に必要な熱に耐え得るものであることが好ましい。従って、上記材料の中でも、例えば、ポリエチレンテレフタレート、ポリエチレンナフタレート、アクリル、ポリカーボネート、シクロオレフィンポリマー、ABS、ポリプロピレン、ポリウレタンが好ましい。なかでも、耐熱性とコストとのバランスがよいことからポリエチレンテレフタレートやシクロオレフィンポリマー、ポリカーボネート、アクリルが好ましい。
基材フィルムは、単層フィルムでもよいし積層フィルムでもよい。加工のし易さ等から、厚さは、例えば、6μm~250μm程度が好ましい。下地層11との付着力を強くするために、プラズマ処理や易接着処理などが施されてもよい。
基体10が基材フィルムの場合、下地層11及び金属層12は基材フィルム上の少なくとも一部に設ければよく、基材フィルムの片面のみに設けてもよく、両面に設けてもよい。
基体10が基材フィルムの場合、下地層11及び金属層12は基材フィルム上の少なくとも一部に設ければよく、基材フィルムの片面のみに設けてもよく、両面に設けてもよい。
基材フィルムは、必要に応じてハードコート層が形成されていてもよい。ハードコート層が設けられることにより、金属層の擦傷性を向上させることができる。ハードコート層は、硬化性樹脂を含有する溶液を塗布する事により形成できる。
硬化性樹脂としては、熱硬化型樹脂、紫外線硬化型樹脂、電子線硬化型樹脂等が挙げられる。硬化性樹脂の種類としてはポリエステル系、アクリル系、ウレタン系、アクリルウレタン系、アミド系、シリコーン系、シリケート系、エポキシ系、メラミン系、オキセタン系、アクリルウレタン系等の各種の樹脂があげられる。これら硬化性樹脂は、一種または二種以上を、適宜に選択して使用できる。これらの中でも、硬度が高く、紫外線硬化が可能で生産性に優れることから、アクリル系樹脂、アクリルウレタン系樹脂、およびエポキシ系樹脂が好ましい。
ここで、基材フィルムは、その表面上に下地層11及び金属層12を形成することができる対象(基体10)の一例にすぎない点に注意すべきである。基体10には、上記のとおり基材フィルムの他、樹脂成型物基材、ガラス基材、LSPR現象を発現させたい物品それ自体も含まれる。樹脂成型物基材、およびLSPR現象を発現させたい物品としては、例えば、透明スクリーンなどの表示デバイス、発光ダイオードなどの光デバイス、太陽電池、表面増強ラマン散乱評価用の基板等が挙げられる。
下地層11及び金属層12は、これら全ての基体上に形成することができ、基体の表面の一部に形成してもよく、基体の表面の全てに形成してもよい。この場合、金属層12を付与すべき基体10は、上記の基材フィルムと同様の材質、条件を満たしていることが好ましい。
<3.下地層>
本実施形態にかかる積層体1は、図1に示されるように、基体10と金属層12の間に、下地層11を備える。下地層11は、基体10の面に直接設けられていてもよいし、基体10の面に設けられた保護膜等を介して間接的に設けられてもよい。下地層11は、上記したとおり、連続状態で、言い換えれば、隙間なく、設けられるのが好ましい。連続状態で設けられることにより、下地層11、ひいては、金属層12や積層体1の平滑性や基体10と下地層11の密着性を向上させることができ、また、下地層11を面内にばらつきなく成膜することも容易となる。
本実施形態にかかる積層体1は、図1に示されるように、基体10と金属層12の間に、下地層11を備える。下地層11は、基体10の面に直接設けられていてもよいし、基体10の面に設けられた保護膜等を介して間接的に設けられてもよい。下地層11は、上記したとおり、連続状態で、言い換えれば、隙間なく、設けられるのが好ましい。連続状態で設けられることにより、下地層11、ひいては、金属層12や積層体1の平滑性や基体10と下地層11の密着性を向上させることができ、また、下地層11を面内にばらつきなく成膜することも容易となる。
このように、基体10と金属層12の間に、下地層11を備えること、すなわち、基体10の上に下地層11を形成し、その上に金属層12を形成することにより、金属層12を不連続の状態で形成しやすくなる。そのメカニズムの詳細は必ずしも明らかではないが、金属の蒸着やスパッタによるスパッタ粒子が基体上で薄膜を形成する際には、基体上での粒子の表面拡散性が薄膜の形状に影響を及ぼし、基体の温度が高く、基体に対する金属層の濡れ性が小さく、金属層の材料の融点が低い方が不連続構造を形成しやすいと考えられる。そして、基体上に下地層11を設けることにより、その表面上の金属粒子の表面拡散性が促進されて金属粒子の濡れ性がより小さくなり、金属層12を不連続の状態で成長させ、島状構造が得られやすくなると考えられる。
本実施形態にかかる積層体1は、下地層11の金属層12側の面の算術平均表面粗さRaが、0.3nm以上である。Raが0.3nm未満であると、下地層上に形成される金属層において、十分な大きさのRaが得られず、LSPRの強度が小さくなる。
下地層11のRaは、金属層におけるLSPR現象発現の観点から、0.3nm以上である必要がある。下地層のRaの上限としては特に限定されないが、生産性の観点から、50nm以下が好ましく、30nm以下がさらに好ましい。
下地層の算術平均表面粗さRaは、JIS B 0601:1994に準じて測定することができる。
下地層11のRaは、金属層におけるLSPR現象発現の観点から、0.3nm以上である必要がある。下地層のRaの上限としては特に限定されないが、生産性の観点から、50nm以下が好ましく、30nm以下がさらに好ましい。
下地層の算術平均表面粗さRaは、JIS B 0601:1994に準じて測定することができる。
下地層のRaを上記範囲とするには、下地層の厚みを後述の好ましい範囲としたり、酸素プラズマ処理等の表面粗化処理を施すことにより、達成し得る。
下地層11としては、薄膜形成が可能な無機酸化物含有層が好ましい。下地層11は、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、インジウム亜鉛酸化物(IZO)、SiO2、AlO3、TiO2、及びZnOから選択される少なくとも一種を含む無機酸化物含有層であることが好ましい。無機酸化物含有層は、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、及びインジウム亜鉛酸化物(IZO)から選択される少なくとも一種を含む酸化インジウム含有層であることが好ましい。
酸化インジウム含有層として、酸化インジウム(In2O3)そのものを使用することもできるし、例えば、インジウム錫酸化物(ITO)や、インジウム亜鉛酸化物(IZO)のような金属含有物を使用することもできる。但し、第二の金属を含有したITOやIZOの方が、スパッタリング工程での放電安定性が高い点で、より好ましい。これらの下地層11を用いることにより、基体の面に沿って連続状態の膜を形成することもでき、また、この場合には、下地層11の上に積層される金属層12を、例えば、島状の不連続構造としやすくなるため、好ましい。
酸化インジウム含有層として、酸化インジウム(In2O3)そのものを使用することもできるし、例えば、インジウム錫酸化物(ITO)や、インジウム亜鉛酸化物(IZO)のような金属含有物を使用することもできる。但し、第二の金属を含有したITOやIZOの方が、スパッタリング工程での放電安定性が高い点で、より好ましい。これらの下地層11を用いることにより、基体の面に沿って連続状態の膜を形成することもでき、また、この場合には、下地層11の上に積層される金属層12を、例えば、島状の不連続構造としやすくなるため、好ましい。
ITOに含まれる酸化錫(SnО2)の質量比率である含有率(含有率=(SnO2/(In2O3+SnO2))×100)は特に限定されるものではないが、例えば、2.5質量%~30質量%、より好ましくは、3質量%~10質量%である。また、IZOに含まれる酸化亜鉛(ZnO)の質量比率である含有率(含有率=(ZnO/(In2O3+ZnO))×100)は、例えば、2質量%~20質量%である。
下地層11の厚みは、1~1000nmであることが好ましく、20~1000nmであることがより好ましい。層の厚みが大きいほど、その表面のRaを大きくすることができるため、Raが0.3nm以上の下地層を形成し易くする観点からは、下限としては、1nm以上であることが好ましく、3nm以上であることがより好ましく、10nm以上がさらに好ましく、20nm以上がよりさらに好ましく、30nm以上が特に好ましい。また、上限としては、生産性の観点から、1000nm以下が好ましく、700nm以下がより好ましく、500nm以下がさらに好ましく、300nm以下がよりさらに好ましい。
なお、下地層の厚みが50nm以下、例えば20nm程度の厚みである場合であっても、表面に酸素プラズマ処理等の表面粗化処理を施すことによって、下地層のRaを大きくすることは可能である。
下地層の厚みは、例えば、積層体の断面TEM画像を測定し、得られたTEM画像より求めることができる。
<4.金属層>
金属層12は下地層11上に形成され、少なくとも一部において互いに不連続の状態にある複数の部分を含む。
金属層12は、LSPR現象発現の観点から、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有することが好ましく、銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有することがより好ましく、銀、金、及びこれらの金属の合金を含有することがさらに好ましい。
本発明の実施形態において、金属層が、LSPR現象を生じ得るものであることが好ましい。
金属層12は下地層11上に形成され、少なくとも一部において互いに不連続の状態にある複数の部分を含む。
金属層12は、LSPR現象発現の観点から、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有することが好ましく、銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有することがより好ましく、銀、金、及びこれらの金属の合金を含有することがさらに好ましい。
本発明の実施形態において、金属層が、LSPR現象を生じ得るものであることが好ましい。
金属層12が下地層上で不連続状態となるメカニズムの詳細は必ずしも明らかではないが、おおよそ、次のようなものであると推測される。即ち、金属層12の薄膜形成プロセスにおいて、不連続構造の形成しやすさは、金属層12が付与される基体上での表面拡散と関連性があり、基体の温度が高く、基体に対する金属層の濡れ性が小さく、金属層の材料の融点が低い方が不連続構造を形成しやすい、というものである。そして、本実施形態に係る積層体では、基体上に下地層11を設けているため、その表面上の金属粒子の表面拡散性が促進されて、金属層12の濡れ性がより小さくなり、島状構造が得られやすくなると考えられる。
複数の部分12aの平均粒径の粒度分布は小さい方が好ましい。粒度分布を小さくすることで、LSPR現象が生じる光の波長域がより限定され、得られる光の吸収スペクトルにおける吸収のピーク幅がシャープになると考えられる。そのため、例えば本実施形態の積層体をセンシングデバイスに応用した場合には、より高感度なセンシングが可能になるものと期待される。
ここで、複数の部分12aの平均粒径とは、複数の部分12aの円相当径の平均値を意味する。部分12aの円相当径とは、部分12aの面積に相当する真円の直径のことである。
ここで、複数の部分12aの平均粒径とは、複数の部分12aの円相当径の平均値を意味する。部分12aの円相当径とは、部分12aの面積に相当する真円の直径のことである。
金属ナノ構造の大きさについては、上記の平均粒径以外に、金属層の算術平均表面粗さRaを指標として用いることも好ましい。
本実施形態にかかる積層体1は、LSPR現象発現の観点から、金属層12側表面の算術平均表面粗さRaが、3nm以上であることが好ましく、より好ましくは4nm以上であり、さらに好ましくは5nm以上である。金属層側表面のRaの上限としては、表面粗さが光学特性に影響を及ぼす観点から、300nm以下が好ましく、100nm以下がさらに好ましい。
金属層の算術平均表面粗さRaは、JIS B 0601:1994に準じて測定することができる。
本実施形態にかかる積層体1は、LSPR現象発現の観点から、金属層12側表面の算術平均表面粗さRaが、3nm以上であることが好ましく、より好ましくは4nm以上であり、さらに好ましくは5nm以上である。金属層側表面のRaの上限としては、表面粗さが光学特性に影響を及ぼす観点から、300nm以下が好ましく、100nm以下がさらに好ましい。
金属層の算術平均表面粗さRaは、JIS B 0601:1994に準じて測定することができる。
金属層12の厚さは、LSPRの発現強度の観点から3nm以上であることが好ましく、5nm以上であることがより好ましく、7nm以上であることがさらに好ましい。また、不連続膜形成の観点から15nm以下であることが好ましく、12nm以下であることがより好ましく、10nm以下であることがさらに好ましい。
この厚さは、均一な膜を生産性良く形成するのにも適している。
金属層の厚みは、例えば、積層体の断面TEM画像を測定し、得られたTEM画像より求めることができる。具体的には、実施例に記載の方法により求めることができる。
この厚さは、均一な膜を生産性良く形成するのにも適している。
金属層の厚みは、例えば、積層体の断面TEM画像を測定し、得られたTEM画像より求めることができる。具体的には、実施例に記載の方法により求めることができる。
<5.その他の層>
本実施形態の積層体1には、本発明の効果を奏する限りにおいて上述の金属層12、下地層11の他に、用途に応じてその他の層を設けてもよい。その他の層としては、粘着剤層等の樹脂層、色味等の外観を調整するための高屈折材料等の光学調整層(色味調整層)、耐湿性や耐擦傷性等の耐久性を向上させるための保護層(耐擦傷性層)、バリア層(腐食防止層)等が挙げられる。
本実施形態の積層体1には、本発明の効果を奏する限りにおいて上述の金属層12、下地層11の他に、用途に応じてその他の層を設けてもよい。その他の層としては、粘着剤層等の樹脂層、色味等の外観を調整するための高屈折材料等の光学調整層(色味調整層)、耐湿性や耐擦傷性等の耐久性を向上させるための保護層(耐擦傷性層)、バリア層(腐食防止層)等が挙げられる。
本実施形態の積層体1は、樹脂層を備えていてもよい。樹脂層は、金属層12の基体10側の面と反対側の面に備えていてもよく金属層上に形成してもよい。
樹脂層は、粘着剤層、色味等の外観を調整するための高屈折材料等の光学調整層(色味調整層)、耐湿性や耐擦傷性等の耐久性を向上させるための保護層(耐擦傷性層)、易接着層、上述したハードコート層、反射防止層、光取出し層、アンチグレア層等であってもよい。
樹脂層は複数設けることができる。
樹脂層は複数設けることができる。
本実施形態の積層体1は、粘着剤層を介して被着部材に貼付されて用いられてもよい。
粘着剤層を形成する粘着剤は透明粘着剤であれば特に限定されず、例えばアクリル系粘着剤、ゴム系粘着剤、シリコーン系粘着剤、ポリエステル系粘着剤、ウレタン系粘着剤、エポキシ系粘着剤、およびポリエーテル系粘着剤のいずれかを単独で、あるいは、2種類以上を組み合わせて使用することができる。透明性、加工性および耐久性などの観点から、アクリル系粘着剤を用いることが好ましい。
粘着剤層の厚みは特に限定されないが、薄くすることで最終製品構成の薄型化への寄与や可視光透過性や膜厚精度、平坦性を向上させることができるため、100μm以下であることが好ましく、75μm以下であることがより好ましく、50μm以下であることがさらに好ましい。
また、粘着剤層を構成する透明粘着剤は着色されていてもよい。
透明粘着剤を着色する方法は特に限定されないが、例えば色素を微量添加することにより着色することができる。
透明粘着剤を着色する方法は特に限定されないが、例えば色素を微量添加することにより着色することができる。
粘着剤層の上には、被着部材に貼付する際まで粘着剤層を保護するために、はく離ライナーを設けてもよい。
<6.積層体の製造>
積層体の製造方法の一例について、説明する。特に説明しないが、基材フィルム以外の基体を用いた場合についても同様の方法で製造することができる。
積層体の製造方法の一例について、説明する。特に説明しないが、基材フィルム以外の基体を用いた場合についても同様の方法で製造することができる。
下地層11を形成するにあたっては、真空蒸着、スパッタリング、イオンプレーティング等の方法を用いることができる。但し、大面積でも厚さを厳密に制御できる点から、スパッタリングが好ましい。
金属層12を形成するにあたっては、例えば、真空蒸着、スパッタリング等の方法を用いることができる。
粘着剤層を設ける場合には、粘着剤層を設ける面に粘着剤組成物を塗布等することや、はく離ライナーに形成した粘着剤層を転写することにより形成できる。
粘着剤組成物の塗布は、慣用のコーター、例えば、グラビヤロールコーター、リバースロールコーター、キスロールコーター、ディップロールコーター、バーコーター、ナイフコーター、スプレーコーターなどを用いて行うことができる。乾燥温度は、適宜採用可能であるが、好ましくは40℃~200℃であり、さらに好ましくは、50℃~180℃であり、特に好ましくは70℃~120℃である。乾燥時間は、適宜、適切な時間が採用され得る。上記乾燥時間は、好ましくは5秒~20分、さらに好ましくは5秒~10分、特に好ましくは、10秒~5分である。
粘着剤組成物の塗布は、慣用のコーター、例えば、グラビヤロールコーター、リバースロールコーター、キスロールコーター、ディップロールコーター、バーコーター、ナイフコーター、スプレーコーターなどを用いて行うことができる。乾燥温度は、適宜採用可能であるが、好ましくは40℃~200℃であり、さらに好ましくは、50℃~180℃であり、特に好ましくは70℃~120℃である。乾燥時間は、適宜、適切な時間が採用され得る。上記乾燥時間は、好ましくは5秒~20分、さらに好ましくは5秒~10分、特に好ましくは、10秒~5分である。
なお、本発明では、基体上に、下地層、金属層をこの順に備えればよく、これらの層間にその他の層を設けてもよい。ただし、下地層11と金属層12の間には、他の層を介在させずに直接接触させるのが好ましい。
<7.部材>
本実施形態に係る部材は、被着部材と、上述の積層体とを備え、前記積層体1が前記粘着剤層を介して前記被着部材に貼付された部材である。
本実施形態に係る部材は、被着部材と、上述の積層体とを備え、前記積層体1が前記粘着剤層を介して前記被着部材に貼付された部材である。
図11に、本発明の一実施形態による部材2の概略断面図を示す。本発明の一実施形態による部材2は、積層体1が被着部材15に貼付された状態の概略断面図である。本実施形態の部材2は、積層体1が、粘着剤層14を介して、被着部材15に貼付されている。
被着部材15としては、例えば、ガラスやプラスチックからなる部材を使用することもできるが、これに限定されるものではない。
積層体1を被着部材15に貼付する方法は特に限定されないが、例えば真空成形により貼付することができる。真空成形とは、積層体1を加熱軟化しつつ展張し、積層体1の被着部材側の空間を減圧し、必要に応じ反対側の空間を加圧することにより、積層体1を被着部材の表面の三次元立体形状に沿って成形しつつ貼付積層する方法である。
積層体1としては、上述の説明をそのまま援用し得る。
積層体1としては、上述の説明をそのまま援用し得る。
<8.積層体の用途>
本実施形態の積層体は、表示デバイスや光デバイス、発光デバイス、センシングデバイス等に応用することにより各種性能向上が期待される。
例えば、スクリーン、プラズモニックカラーデバイス、フィルタ、有機EL、フォトクロミック、メタマテリアルに応用することにより、波長制御機能を付与したり、発光ダイオードや太陽電池に応用することにより、光の増強や高効率化、エネルギー変換機能を付与したり、センシングデバイスや光触媒に応用することにより、高感度化を図ることが期待できる。
本発明の実施形態に係る発光デバイスは、本発明の実施形態に係る積層体を有する。また、本発明の実施形態に係るセンシングデバイスは、本発明の実施形態に係る積層体を有する。
本実施形態の積層体は、表示デバイスや光デバイス、発光デバイス、センシングデバイス等に応用することにより各種性能向上が期待される。
例えば、スクリーン、プラズモニックカラーデバイス、フィルタ、有機EL、フォトクロミック、メタマテリアルに応用することにより、波長制御機能を付与したり、発光ダイオードや太陽電池に応用することにより、光の増強や高効率化、エネルギー変換機能を付与したり、センシングデバイスや光触媒に応用することにより、高感度化を図ることが期待できる。
本発明の実施形態に係る発光デバイスは、本発明の実施形態に係る積層体を有する。また、本発明の実施形態に係るセンシングデバイスは、本発明の実施形態に係る積層体を有する。
以上説明したように、本明細書には次の事項が開示されている。
〔1〕
基体と下地層と金属層とをこの順に備え、
前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、
前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である積層体。
〔2〕
前記下地層の厚みが、20~1000nmである〔1〕に記載の積層体。
〔3〕
前記下地層が、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、インジウム亜鉛酸化物(IZO)、SiO2、AlO3、TiO2、及びZnOから選択される少なくとも一種を含む無機酸化物含有層である〔1〕又は〔2〕に記載の積層体。
〔4〕
前記無機酸化物含有層が、前記酸化インジウム(In2O3)、前記インジウム錫酸化物(ITO)、及び前記インジウム亜鉛酸化物(IZO)から選択される少なくとも一種を含有する酸化インジウム含有層である、〔3〕に記載の積層体。
〔5〕
前記積層体における前記金属層側表面の算術平均表面粗さRaが3nm以上である、〔1〕~〔4〕のいずれか1項に記載の積層体。
〔6〕
前記金属層が、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有する、〔1〕~〔5〕のいずれか1項に記載の積層体。
〔7〕
前記金属層が、銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有する、〔6〕に記載の積層体。
〔8〕
前記金属層が、LSPR現象を生じ得るものである、〔1〕~〔7〕のいずれか1項に記載の積層体。
〔9〕
前記基体が基材フィルムである、〔1〕~〔8〕のいずれか1項に記載の積層体。
〔10〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有する発光デバイス。
〔11〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有するセンシングデバイス。
〔1〕
基体と下地層と金属層とをこの順に備え、
前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、
前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である積層体。
〔2〕
前記下地層の厚みが、20~1000nmである〔1〕に記載の積層体。
〔3〕
前記下地層が、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、インジウム亜鉛酸化物(IZO)、SiO2、AlO3、TiO2、及びZnOから選択される少なくとも一種を含む無機酸化物含有層である〔1〕又は〔2〕に記載の積層体。
〔4〕
前記無機酸化物含有層が、前記酸化インジウム(In2O3)、前記インジウム錫酸化物(ITO)、及び前記インジウム亜鉛酸化物(IZO)から選択される少なくとも一種を含有する酸化インジウム含有層である、〔3〕に記載の積層体。
〔5〕
前記積層体における前記金属層側表面の算術平均表面粗さRaが3nm以上である、〔1〕~〔4〕のいずれか1項に記載の積層体。
〔6〕
前記金属層が、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有する、〔1〕~〔5〕のいずれか1項に記載の積層体。
〔7〕
前記金属層が、銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有する、〔6〕に記載の積層体。
〔8〕
前記金属層が、LSPR現象を生じ得るものである、〔1〕~〔7〕のいずれか1項に記載の積層体。
〔9〕
前記基体が基材フィルムである、〔1〕~〔8〕のいずれか1項に記載の積層体。
〔10〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有する発光デバイス。
〔11〕
〔1〕~〔9〕のいずれか1項に記載の積層体を有するセンシングデバイス。
以下、実施例および比較例を挙げて、本発明をより具体的に説明する。積層体を作製し評価を行った。なお、基体10としては、基材フィルムを用いた。
評価方法の詳細は以下のとおりである。
<金属層の厚み>
実施例1と同様にして紫外線硬化樹脂層付き基材フィルム上にITO層を形成し、ITO層上に金属層を厚さ100nmを目標として成膜し、Dektak15(株式会社アルバック製)にて金属層の膜厚を測定し、得られた膜厚の測定値と成膜時間から成膜レートを求め、この成膜レートに基づいて成膜時間により厚みを決定し、「金属層の厚み」とした。
実施例1と同様にして紫外線硬化樹脂層付き基材フィルム上にITO層を形成し、ITO層上に金属層を厚さ100nmを目標として成膜し、Dektak15(株式会社アルバック製)にて金属層の膜厚を測定し、得られた膜厚の測定値と成膜時間から成膜レートを求め、この成膜レートに基づいて成膜時間により厚みを決定し、「金属層の厚み」とした。
<下地層の厚み>
実施例1と同様にして紫外線硬化樹脂層付き基材フィルム上にITO層を厚さ100nmを目標として成膜し、Dektak15(株式会社アルバック製)にてITO層の膜厚を測定し、得られた膜厚の測定値と成膜時間から成膜レートを求め、この成膜レートに基づいて成膜時間により厚みを決定し、下地層の厚みとした。
実施例1と同様にして紫外線硬化樹脂層付き基材フィルム上にITO層を厚さ100nmを目標として成膜し、Dektak15(株式会社アルバック製)にてITO層の膜厚を測定し、得られた膜厚の測定値と成膜時間から成膜レートを求め、この成膜レートに基づいて成膜時間により厚みを決定し、下地層の厚みとした。
<金属層の表面粗さ>
金属層の算術平均表面粗さ(Ra)は、JIS B 0601:1994に準じ、ブルカージャパン株式会社製AFM MultiMode8を用い、下記の条件にて実施例及び比較例の積層体の金属層側表面の算術平均表面粗さ(Ra)(nm)を測定した。
測定モード:タッピングモード
バネ定数:200N/m
測定範囲:1μm
金属層の算術平均表面粗さ(Ra)は、JIS B 0601:1994に準じ、ブルカージャパン株式会社製AFM MultiMode8を用い、下記の条件にて実施例及び比較例の積層体の金属層側表面の算術平均表面粗さ(Ra)(nm)を測定した。
測定モード:タッピングモード
バネ定数:200N/m
測定範囲:1μm
<下地層の表面粗さ>
紫外線硬化樹脂層付き基材フィルムの紫外線硬化樹脂層の上に下地層としてのITO層を積層した実施例及び比較例の中間積層物について、ITO層側表面の算術平均表面粗さ(Ra)を、金属層における測定と同様の条件にて測定した。
紫外線硬化樹脂層付き基材フィルムの紫外線硬化樹脂層の上に下地層としてのITO層を積層した実施例及び比較例の中間積層物について、ITO層側表面の算術平均表面粗さ(Ra)を、金属層における測定と同様の条件にて測定した。
<吸収率評価>
実施例及び比較例で得られた積層体について、光の波長別透過率および反射率(波長範囲:300~900nm)を分光光度計(U4100、(株)日立ハイテクサイエンス製)を用いて評価し、吸収率を算出した。
実施例及び比較例で得られた積層体について、光の波長別透過率および反射率(波長範囲:300~900nm)を分光光度計(U4100、(株)日立ハイテクサイエンス製)を用いて評価し、吸収率を算出した。
[実施例1]
基材フィルムとして、東レ株式会社製PETフィルム50-U483(厚さ50μm)に厚み1.5μmの紫外線硬化樹脂層(ハードコート層)を形成し、紫外線硬化樹脂層付き基材フィルムを得た。
先ず、マグネトロンスパッタリング装置にITOターゲットを取り付け、Arガスを導入しながらスパッタリングをすることで紫外線硬化樹脂層付き基材フィルムの面に沿って、下地層としてのITO層を厚さ200nmで紫外線硬化樹脂層の上に直接形成し、中間積層物を得た。ITOに含まれる酸化錫(SnО2)の含有率(含有率=(SnO2/(In2O3+SnO2))×100)は10質量%であった。
次に、マグネトロンスパッタリング装置に銀(Ag)ターゲットを取り付け、Arガスを導入しながらスパッタリングすることで中間積層物のITO層の上に金属層としてのAg層を厚さ5nmで形成し、積層体を得た。得られたAg層は図3で示すような金属層表面の島状金属層であった。
基材フィルムとして、東レ株式会社製PETフィルム50-U483(厚さ50μm)に厚み1.5μmの紫外線硬化樹脂層(ハードコート層)を形成し、紫外線硬化樹脂層付き基材フィルムを得た。
先ず、マグネトロンスパッタリング装置にITOターゲットを取り付け、Arガスを導入しながらスパッタリングをすることで紫外線硬化樹脂層付き基材フィルムの面に沿って、下地層としてのITO層を厚さ200nmで紫外線硬化樹脂層の上に直接形成し、中間積層物を得た。ITOに含まれる酸化錫(SnО2)の含有率(含有率=(SnO2/(In2O3+SnO2))×100)は10質量%であった。
次に、マグネトロンスパッタリング装置に銀(Ag)ターゲットを取り付け、Arガスを導入しながらスパッタリングすることで中間積層物のITO層の上に金属層としてのAg層を厚さ5nmで形成し、積層体を得た。得られたAg層は図3で示すような金属層表面の島状金属層であった。
以上により基材フィルム、紫外線硬化樹脂層、下地層、金属層がこの順に積層された実施例1の積層体を得た。
[実施例2、比較例1、2]
実施例1における下地層の厚みを、表1に示すように変更したこと以外は、実施例1と同様にして、実施例2及び比較例1、2の積層体を得た。
実施例1における下地層の厚みを、表1に示すように変更したこと以外は、実施例1と同様にして、実施例2及び比較例1、2の積層体を得た。
得られた実施例及び比較例の積層体について、特性を上記の方法により測定し、表1に記載した。
実施例1、2及び比較例1、2の積層体について、金属層表面のAFM画像を図3~図6にそれぞれ示す。また、実施例1、2及び比較例1、2の積層体について、吸収率評価により得られた吸収スペクトル(各波長(nm)における吸収率(%)を示したもの)を、図7~10にそれぞれ示す。
吸収スペクトルにおいて明確な吸収ピークを確認することができたものを〇、明確な吸収ピークを確認することができなかったものを×と評価した。
実施例1、2及び比較例1、2の積層体について、金属層表面のAFM画像を図3~図6にそれぞれ示す。また、実施例1、2及び比較例1、2の積層体について、吸収率評価により得られた吸収スペクトル(各波長(nm)における吸収率(%)を示したもの)を、図7~10にそれぞれ示す。
吸収スペクトルにおいて明確な吸収ピークを確認することができたものを〇、明確な吸収ピークを確認することができなかったものを×と評価した。
表1、及び図3~10から明らかなように、実施例の積層体は、下地層表面のRaを0.3nm以上とすることにより、金属層表面のRaが大きくなり、吸収スペクトルにおいて500~600nm付近に明確な吸収ピークを確認することができた。一方、比較例の積層体は下地層表面のRaが0.3nm未満であるため、金属層表面のRaも小さくなり、吸収スペクトルにおいて明確な吸収ピークを確認することはできなかった。
本発明は前記実施例に限定されるものではなく、発明の趣旨から逸脱しない範囲で適宜変更して具体化することもできる。
本発明によれば、LSPR現象を生じ得る金属層を有する積層体、発光デバイス、及びセンシングデバイスを提供することができる。
本発明を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。
本出願は、2022年3月30日出願の日本特許出願(特願2022-057000)に基づくものであり、その内容はここに参照として取り込まれる。
本出願は、2022年3月30日出願の日本特許出願(特願2022-057000)に基づくものであり、その内容はここに参照として取り込まれる。
1 積層体
2 部材
10 基体
11 下地層
12 金属層
12a 部分
12b 隙間
14 粘着剤層
15 被着部材
2 部材
10 基体
11 下地層
12 金属層
12a 部分
12b 隙間
14 粘着剤層
15 被着部材
Claims (11)
- 基体と下地層と金属層とをこの順に備え、
前記金属層は、少なくとも一部において互いに不連続の状態にある複数の部分を含み、
前記下地層の前記金属層側の面の算術平均表面粗さRaが、0.3nm以上である積層体。 - 前記下地層の厚みが、20~1000nmである請求項1に記載の積層体。
- 前記下地層が、酸化インジウム(In2O3)、インジウム錫酸化物(ITO)、インジウム亜鉛酸化物(IZO)、SiO2、AlO3、TiO2、及びZnOから選択される少なくとも一種を含む無機酸化物含有層である請求項1に記載の積層体。
- 前記無機酸化物含有層が、前記酸化インジウム(In2O3)、前記インジウム錫酸化物(ITO)、及び前記インジウム亜鉛酸化物(IZO)から選択される少なくとも一種を含有する酸化インジウム含有層である、請求項3に記載の積層体。
- 前記積層体における前記金属層側表面の算術平均表面粗さRaが3nm以上である、請求項1に記載の積層体。
- 前記金属層が、銀、金、ニッケル、銅、コバルト、アルミニウム、及びこれらの金属の合金から選ばれる金属を含有する、請求項1に記載の積層体。
- 前記金属層が、銀、金、ニッケル、銅、コバルト、及びこれらの金属の合金から選ばれる金属を含有する、請求項6に記載の積層体。
- 前記金属層が、LSPR現象を生じ得るものである、請求項1に記載の積層体。
- 前記基体が基材フィルムである、請求項1に記載の積層体。
- 請求項1~9のいずれか1項に記載の積層体を有する発光デバイス。
- 請求項1~9のいずれか1項に記載の積層体を有するセンシングデバイス。