WO2023189197A1 - 微細金属粒子の製造方法 - Google Patents

微細金属粒子の製造方法 Download PDF

Info

Publication number
WO2023189197A1
WO2023189197A1 PCT/JP2023/007950 JP2023007950W WO2023189197A1 WO 2023189197 A1 WO2023189197 A1 WO 2023189197A1 JP 2023007950 W JP2023007950 W JP 2023007950W WO 2023189197 A1 WO2023189197 A1 WO 2023189197A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal particles
temperature
gas
metal
producing fine
Prior art date
Application number
PCT/JP2023/007950
Other languages
English (en)
French (fr)
Inventor
敦 田中
聡信 安武
崇史 久保田
正志 清澤
Original Assignee
三菱重工業株式会社
三菱パワー株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱重工業株式会社, 三菱パワー株式会社 filed Critical 三菱重工業株式会社
Publication of WO2023189197A1 publication Critical patent/WO2023189197A1/ja

Abstract

微細金属粒子の製造方法は、金属粒子を準備するステップと、炭化水素を含む供給ガスを金属粒子に供給するステップとを含み、供給ガスと金属粒子との接触は６００℃～９００℃の温度範囲で行われ、供給ガスと金属粒子との接触中に、温度範囲内の温度を６００℃未満に低下した後、再び温度範囲内の温度に上昇させる。

Description

微細金属粒子の製造方法
　本開示は、微細金属粒子の製造方法に関する。
　本開示は、２０２２年３月３０日に日本国特許庁に出願された特願２０２２－０５５６２６号に基づき優先権を主張し、その内容をここに援用する。
　金属を微粒化する技術として、固体金属の粉砕や、溶融した金属を噴射冷却するアトマイズ法（例えば、特許文献１参照）等がある。しかしながら、従来の多くの技術はマイクロメートルオーダーの粒径までの微粒化技術であり、サブミクロンオーダーの粒径まで金属を微粒化することには不向きである。これに対し、本開示の発明者らの研究により、金属粒子を触媒として炭化水素の直接分解を行うと、金属がサブミクロンオーダーの粒径まで微細化できることを明らかにしている（本願出願人により出願された特願２０２１－１７７８１１号）。
特開２０１８－１４１２２３号公報（００３１段落）
　しかしながら、本開示の発明者らの研究では、金属粒子を触媒として炭化水素の直接分解を行うことにより、金属がサブミクロンオーダーの粒径まで微細化できることは明らかになったものの、さらに効率的に金属をサブミクロンオーダーの粒径まで微細化することが望まれている。
　上述の事情に鑑みて、本開示の少なくとも１つの実施形態は、効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる微細金属粒子の製造方法を提供することを目的とする。
　上記目的を達成するため、本開示に係る微細金属粒子の製造方法は、金属粒子を準備するステップと、炭化水素を含む供給ガスを前記金属粒子に供給するステップとを含み、前記供給ガスと前記金属粒子との接触は６００℃～９００℃の温度範囲で行われ、前記供給ガスと前記金属粒子との接触中に、前記温度範囲内の温度を６００℃未満に低下した後、再び前記温度範囲内の温度に上昇させる。
　本開示の微細金属粒子の製造方法によれば、炭化水素をカーボン及び水素に直接分解する反応の触媒として金属粒子が機能する。この触媒作用の過程で、生成した水素による水素侵食によって金属粒子に粒界が生じ、この粒界を起点として、金属粒子から微粒子がマイグレーションにより移動し、生成したカーボンと反応して金属カーバイドが形成される。水素侵食に伴って金属のカーバイド化が進行し、サブミクロンオーダーの粒径の微粒子に分割されていく。生成したカーボンは、６００℃～９００℃の温度範囲では金属中に溶解しているが、温度を６００℃未満に低下する間に、金属へのカーボンの溶解度が低下することによりカーボンが金属の外に追い出される。カーボンが金属の外に追い出される際に金属粒子が破壊されるので、温度を低下させない場合に比べて、金属粒子がより微細化される。これにより、温度を再び６００℃～９００℃の温度範囲に上昇させた後の触媒活性が向上するので、効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる。
本開示の一実施形態に係る微細金属粒子の製造方法を実施するための装置の構成模式図である。 本開示の一実施形態に係る微細金属粒子の製造方法の効果を検証するための実験装置の構成模式図である。 実施例１及び２並びに比較例１及び２の実験における供給ガス転化率の経時変化を示すグラフである。 実施例１及び２の実験において、温度低下前後の供給ガス転化率の変化を示すグラフである。
　以下、本開示の実施形態による微細金属粒子の製造方法について、図面に基づいて説明する。以下で説明する実施形態は、本開示の一態様を示すものであり、この開示を限定するものではなく、本開示の技術的思想の範囲内で任意に変更可能である。
＜本開示の発明者らの先行研究による知見＞
　本願出願人の先願（特願２０２１－１７７８１１号）では、６００℃～９００℃の温度で金属粒子に炭化水素を含むガスを接触させることで、金属をサブミクロンオーダーの粒径まで微細化できることを明らかにした。この方法では、炭化水素をカーボン及び水素に直接分解する反応の触媒として金属粒子が機能する。この触媒作用の過程で、生成した水素による水素侵食によって金属粒子に粒界が生じ、この粒界を起点として、金属粒子から微粒子がマイグレーションにより移動し、生成したカーボンと反応して金属カーバイドが形成される。水素侵食に伴って金属のカーバイド化が進行し、サブミクロンオーダーの粒径の微粒子に分割されていく。このようにして、金属をサブミクロンオーダーの粒径まで微粒化することができる。先願では、微細化できる金属として、鉄、ニッケル、コバルト、又はこれらのうちの少なくとも２つの合金を例示している。この知見に基づき、本開示では以下において、さらに効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる微細金属粒子の製造方法を説明する。
＜本開示の一実施形態に係る微細金属粒子の製造方法を実施するための装置の構成＞
　図１に示されるように、本開示の一実施形態に係る微細金属粒子の製造方法を実施するための装置１は、微粒化される金属粒子２が収容された反応器３を備えている。反応器３には、反応器３の内部、特に金属粒子２を昇温するための加熱装置４（例えば、スチームが流通するジャケット等）が設けられている。反応器３には、炭化水素を含む供給ガスを反応器３に供給するための供給ライン５と、反応器３から流出する流出ガスが流通する流出ガス流通ライン６とが接続されている。
　金属粒子２を形成する金属は、鉄、ニッケル、コバルト、又はこれらのうちの少なくとも２つの合金である。また、供給ガスは炭化水素のみを含んでもよいが、炭化水素の他に不活性ガス（窒素又は希ガス）を含んでもよい。さらに、炭化水素としては、メタンのみでもよいし、メタンと２以上の炭素を含む少なくとも１種類の炭化水素（エタン、エチレン、プロパン等）との混合物であってもよい。このような混合物を直接分解される炭化水素として使用する場合、混合物の組成は、メタンが９０ｖｏｌ％であるとともに２以上の炭素を含む少なくとも１種類の炭化水素が１０ｖｏｌ％であることが好ましい。
＜本開示の一実施形態に係る微細金属粒子の製造方法＞
　次に、本開示の一実施形態に係る微細金属粒子の製造方法について説明する。反応器３内に、微粒化される金属粒子２を収容する。次に、供給ライン５を介して反応器３内に供給ガスを供給し、反応器３内で供給ガスを金属粒子２に接触させる。この際、供給ガス中の炭化水素は、金属粒子２の触媒作用によって水素とカーボンに直接分解される。この分解反応（「直接分解反応」とも言う）における炭化水素としてメタンを例にすると、下記の反応式（１）で表される反応が反応器３内で生じる。
　　ＣＨ４→２Ｈ２＋Ｃ　・・・（１）
　尚、この分解反応を促進するために、加熱装置４によって金属粒子２の温度を６００℃～９００℃の範囲に維持することが好ましい。
　本開示の製造方法では、供給ガスと金属粒子２との接触中に、温度を６００℃未満に低下した後、再び６００℃～９００℃の範囲に上昇させる。反応式（１）の活性が十分に上がるまでには数時間がかかることから、温度を低下させるタイミングについては、反応式（１）の活性が十分に上がった後が好ましい。反応式（１）の活性が十分に上がるまでに必要な時間が経験上分かっている場合は、反応開始からその時間が経過した後に温度を低下すればよい。そのような時間が分かっていない場合には、流出ガス流通ライン６を流通する流出ガスを定期的にサンプリングし、ガスクロマトグラフで流出ガスの組成を分析することにより、炭化水素の転化率の経時変化が得られるので、この経時変化から、温度を下げるタイミングを決定することができる。
　本開示の製造方法によれば、金属粒子２が炭化水素をカーボン及び水素に直接分解する反応の触媒として機能する過程で、生成した水素による水素侵食によって金属粒子に粒界が生じ、この粒界を起点として、金属粒子から微粒子がマイグレーションにより移動し、生成したカーボンと反応して金属カーバイドが形成される。水素侵食に伴って金属のカーバイド化が進行し、サブミクロンオーダーの粒径の微粒子に分割されていく。生成したカーボンは、６００℃～９００℃の温度範囲では金属中に溶解しているが、温度を６００℃未満に低下する間に、金属へのカーボンの溶解度が低下することによりカーボンが金属の外に追い出される。カーボンが金属の外に追い出される際に金属粒子が破壊されるので、温度を低下させない場合に比べて、金属粒子がより微細化される。これにより、温度を再び６００℃～９００℃の温度範囲に上昇させた後の触媒活性が向上するので、効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる。尚、反応式（１）の活性が十分に上がった後に温度を下げることが好ましいと述べたが、鉄の内部に溶解したカーボンが温度の低下によって析出することで活性が向上することからすれば、必ずしも活性が十分に上がった後でなくても、活性が十分に上がる前、少なくとも活性の発現を確認できた後であれば、同様の効果が得られると考えられる。
＜実験装置の構成＞
　後述する実施例１及び２並びに比較例１及び２によって、本開示の製造方法の作用効果を検証するが、その検証のために行われる実験で使用する実験装置の構成を図２に示す。実験装置２０は、金属粒子２を載置した目皿２８を内部に収容する内径１６ｍｍの石英製の反応器２３を備えている。反応器２３は、電気炉２４で加熱可能になっている。反応器２３には、供給ガス又はアルゴンを供給するための供給ライン２５と、供給ガスに含まれる炭化水素の直接分解反応によって生成した水素を含む流出ガスが反応器２３から流出後に流通する流出ガス流通ライン２６とが接続されている。流出ガス流通ライン２６は、流出ガスの組成を測定するためのガスクロマトグラフ２７に接続されている。
＜実験方法＞
　次に、実施例１及び２並びに比較例１及び２の実験方法について説明する。この実験装置２０において、金属粒子２を反応器２３内の目皿２８上に設置した後、反応器２３内をアルゴンで置換した。次に、反応器２３内にアルゴンを流通させながら、電気炉２４を起動して、反応器２３内を８００℃まで昇温した。反応器２３内の温度が８００℃となったら、反応器２３内に供給するガスを供給ガスに切り替えて、炭化水素を直接分解する実験を行った。
　実施例１及び２については、反応器２３内に供給するガスを供給ガスに切り替えてから８時間経過後に、電気炉２４を停止し、反応器２３内に供給するガスをアルゴンに切り替えることによって反応器２３内をアルゴンで置換した。１～４時間放置することで、反応器２３内の温度が２５℃となった。１０時間後、反応器２３内にアルゴンを流通させながら、電気炉２４を起動して、反応器２３内の温度を１００℃／ｍｉｎの昇温速度で８００℃まで昇温した。反応器２３内の温度が８００℃となったら、反応器２３内に供給するガスを供給ガスに切り替えて、炭化水素を直接分解する実験を再開した。比較例１及び２については、反応容器２３内の温度を低下せず、実験終了まで８００℃を維持した。
　実施例１及び２並びに比較例１及び２の実験条件を下記表１に示す。尚、金属粒子２として、株式会社ニラコから入手可能な電解鉄製粒子を使用した。この電解鉄製粒子は、平均粒径が４５μｍであり、鉄の純度は９９質量％である。
Figure JPOXMLDOC01-appb-T000001
　実施例１及び２並びに比較例１及び２のそれぞれの直接分解反応の実験において、ガスクロマトグラフ２７によって測定された反応ガスの組成から、下記式（２）によって、供給ガス転化率ＣＲ［％］を算出した。
　　ＣＲ＝（１－Ｈ１／Ｈ０）×１００　・・・（２）
ここで、Ｈ０は供給ガスが持つ水素原子数であり、Ｈ１は反応ガス中の炭化水素ガスが持つ水素原子数である。それぞれのガスが持つ水素原子数は、それぞれのガス組成と流量とから算出することができる。
　実施例１及び２並びに比較例１及び２のそれぞれの供給ガス転化率の経時変化を図３に示す。実施例１及び２では、反応器２３内に供給ガスを供給してから（直接分解反応を開始してから）８時間経過後に、供給ガスの供給を停止して温度を２５℃まで低下し、その後再び８００℃まで昇温してから供給ガスの供給を再開しているが、図３ではこの操作の期間は経時時間にカウントしていない。すなわち、反応器２３内に供給ガスを供給してから８時間後のプロットの後のプロットは、この操作が終わって直接分解反応が再開した後のプロットとなっている。このため、図３では、実施例１及び２における供給ガス転化率の経時変化は、反応器２３内に供給ガスを供給してから８時間後に急変するようになっている。実施例１及び２のそれぞれと比較例１及び２のそれぞれとを比較すると、反応器２３内に供給ガスを供給してから８時間経過後の供給ガス転化率が増加している。
　図４には、実施例１及び２のそれぞれにおいて、温度低下開始直前の供給ガス転化率と温度低下後に直接分解反応を再開した時の供給ガス転化率との比較を示す。図４から、炭化水素の直接分解中に温度を２５℃まで低下し、その後温度を基に戻して直接分解反応を再開することで、供給ガス転化率が上昇することがわかった。また、供給ガス転化率が上昇する効果は、供給ガスとしてメタンのみを使用した場合に比べて、２以上の炭素を含む炭化水素を含んだ供給ガスを使用した場合の方が大きいこともわかった。
　したがって、６００℃～９００℃の温度範囲で炭化水素を直接分解している間に温度を２５℃に低下した後に再び温度を元の温度範囲に戻すことによって、この操作の後における供給ガス転化率がこの操作前における供給ガス転化率よりも上昇するので、効率的に金属をサブミクロンオーダーの粒径まで微粒化することができると言える。
　上記各実施形態に記載の内容は、例えば以下のように把握される。
［１］一の態様に係る微細金属粒子の製造方法は、
　金属粒子を準備するステップと、
　炭化水素を含む供給ガスを前記金属粒子に供給するステップと
を含み、
　前記供給ガスと前記金属粒子との接触は６００℃～９００℃の温度範囲で行われ、
　前記供給ガスと前記金属粒子との接触中に、前記温度範囲内の温度を６００℃未満に低下した後、再び前記温度範囲内の温度に上昇させる。
　本開示の微細金属粒子の製造方法によれば、炭化水素をカーボン及び水素に直接分解する反応の触媒として金属粒子が機能する。この触媒作用の過程で、生成した水素による水素侵食によって金属粒子に粒界が生じ、この粒界を起点として、金属粒子から微粒子がマイグレーションにより移動し、生成したカーボンと反応して金属カーバイドが形成される。水素侵食に伴って金属のカーバイド化が進行し、サブミクロンオーダーの粒径の微粒子に分割されていく。生成したカーボンは、６００℃～９００℃の温度範囲では金属中に溶解しているが、温度を６００℃未満に低下する間に、金属へのカーボンの溶解度が低下することによりカーボンが金属の外に追い出される。カーボンが金属の外に追い出される際に金属粒子が破壊されるので、温度を低下させない場合に比べて、金属粒子がより微細化される。これにより、温度を再び６００℃～９００℃の温度範囲に上昇させた後の触媒活性が向上するので、効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる。
［２］別の態様に係る微細金属粒子の製造方法は、［１］の微細金属粒子の製造方法であって、
　炭化水素の転化率を測定するステップを含み、
　測定された前記転化率が予め決められた設定値以上となったら、前記温度範囲内の温度を６００℃未満に低下した後、再び前記温度範囲内の温度に上昇させる。
　このような製造方法によれば、十分な量のカーボンが生成された後に、温度の低下及び再度の上昇を行うことになる。そうすると、不十分な量のカーボンしか生成されていないときのこの動作を行う場合に比べて、カーボンが金属の外に追い出される量が多いので、金属がより微細化される。これにより、効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる。
［３］さらに別の態様に係る微細金属粒子の製造方法は、［１］または［２］の微細金属粒子の製造方法であって、
　前記供給ガスは、
　９０ｖｏｌ％のメタンと、
　１０ｖｏｌ％の２以上の炭素を含む炭化水素と
を含む。
　このような製造方法によれば、２以上の炭素を含む炭化水素の方がメタンに比べて分解しやすいので、メタンのみの供給ガスを使用した場合に比べて、より効率的に金属をサブミクロンオーダーの粒径まで微粒化することができる。
［４］さらに別の態様に係る微細金属粒子の製造方法は、［１］～［３］のいずれかの微細金属粒子の製造方法であって、
　前記金属粒子を形成する金属は、鉄、ニッケル、コバルト、又はこれらのうちの少なくとも２つの合金である。
　このような製造構成によれば、鉄製、ニッケル製、コバルト製、又はこれらのうちの少なくとも２つの合金製の微細金属粒子を得ることができる。
２　金属粒子

Claims (4)

  1. 　金属粒子を準備するステップと、
    　炭化水素を含む供給ガスを前記金属粒子に供給するステップと
    を含み、
    　前記供給ガスと前記金属粒子との接触は６００℃～９００℃の温度範囲で行われ、
    　前記供給ガスと前記金属粒子との接触中に、前記温度範囲内の温度を６００℃未満に低下した後、再び前記温度範囲内の温度に上昇させる、微細金属粒子の製造方法。
  2. 　炭化水素の転化率を測定するステップを含み、
    　測定された前記転化率が予め決められた設定値以上となったら、前記温度範囲内の温度を６００℃未満に低下した後、再び前記温度範囲内の温度に上昇させる、請求項１に記載の微細金属粒子の製造方法。
  3. 　前記供給ガスは、
    　９０ｖｏｌ％のメタンと、
    　１０ｖｏｌ％の２以上の炭素を含む炭化水素と
    を含む、請求項１または２に記載の微細金属粒子の製造方法。
  4. 　前記金属粒子を形成する金属は、鉄、ニッケル、コバルト、又はこれらのうちの少なくとも２つの合金である、請求項１または２に記載の微細金属粒子の製造方法。
PCT/JP2023/007950 2022-03-30 2023-03-03 微細金属粒子の製造方法 WO2023189197A1 (ja)