WO2023120136A1 - 離型フィルム付き粘着シート、フレキシブル画像表示装置用積層体、フレキシブル画像表示装置及び粘着シート - Google Patents
離型フィルム付き粘着シート、フレキシブル画像表示装置用積層体、フレキシブル画像表示装置及び粘着シート Download PDFInfo
- Publication number
- WO2023120136A1 WO2023120136A1 PCT/JP2022/044730 JP2022044730W WO2023120136A1 WO 2023120136 A1 WO2023120136 A1 WO 2023120136A1 JP 2022044730 W JP2022044730 W JP 2022044730W WO 2023120136 A1 WO2023120136 A1 WO 2023120136A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive sheet
- pressure
- sensitive adhesive
- release film
- image display
- Prior art date
Abstract
粘着シートの表裏一側又は両側にフレキシブル画像表示装置用構成部材を積層し、積層状態のまま伸縮させたときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離して"剥がれ"が生じるのを防ぐことができる粘着シートを備えた離型フィルム付き粘着シートとして、離型フィルムと粘着シートとの間に空間部を有し、当該空間部の空隙率（Ｘ）が３～７０％である離型フィルム付き粘着シートを提案する。
Description
本発明は、離型フィルム付き粘着シートに関し、とりわけフレキシブル画像表示装置用構成部材を他の被着部材に貼り合わせるために用いられる離型フィルム付き粘着シートに関する。更に詳しくは、フレキシブル性に優れることから、ローラブル用やストレッチャブル用の画像表示装置用積層体に用いるのに有用な粘着シートを備えた離型フィルム付き粘着シートに関する。また、当該粘着シートを備えたフレキシブル画像表示装置用積層体及びフレキシブル画像表示装置に関する。
近年、画像表示装置においては、その視認性を向上させるために、液晶ディスプレイ（ＬＣＤ）、プラズマディスプレイ（ＰＤＰ）、エレクトロルミネッセンスディスプレイ（ＥＬＤ）等の画像表示パネルと、その前面側（視認側）に配置する保護パネルやタッチパネル部材との間の空隙を、粘着シート等で充填し、入射光や表示画像からの出射光の空気層界面での反射を抑えることが行われている。
一方、有機発光ダイオード（ＯＬＥＤ）や量子ドット（ＱＤ）を用いた、フレキシブル画像表示装置が開発され、広く商用化されつつある。
フレキシブル画像表示装置としては、画像表示面が曲面形状を有するベンダブル、繰り返し折り曲げが可能なフォルダブル、巻き取ることができるローラブル、伸縮されるストレッチャブル等を挙げることができる。中でも、コンパクトで大面積なディスプレイの実現が可能な点から、巻き取ることができるローラブル用の画像表示装置（「ローラブル画像表示装置」とも称する）は特に注目されている。また、同様にコンパクトなディスプレイから大面積なディスプレイの実現が可能な点からストレッチャブル用の画像表示装置（「ストレッチャブル画像表示装置」とも称する）が注目されている。
フレキシブル画像表示装置としては、画像表示面が曲面形状を有するベンダブル、繰り返し折り曲げが可能なフォルダブル、巻き取ることができるローラブル、伸縮されるストレッチャブル等を挙げることができる。中でも、コンパクトで大面積なディスプレイの実現が可能な点から、巻き取ることができるローラブル用の画像表示装置（「ローラブル画像表示装置」とも称する）は特に注目されている。また、同様にコンパクトなディスプレイから大面積なディスプレイの実現が可能な点からストレッチャブル用の画像表示装置（「ストレッチャブル画像表示装置」とも称する）が注目されている。
ローラブル画像表示装置に用いることが可能な粘着シートとしては、例えば特許文献１において、フレキシブルディスプレイを構成する二つの光学部材を貼合するために用いられる粘着剤層付セパレートフィルムとして、セパレートフィルムと反対側の粘着層表面に凹部を設けたものが開示されている。
従来開示されていた粘着シートに関しては、例えば図１及び図２に示すように、粘着シート１０の表裏一側又は両側にフレキシブル画像表示装置用構成部材２０（３０）を積層し、積層状態のまま、巻芯５０に巻き付けて巻き取り、その後、巻き戻して展開したときに、粘着シート１０とフレキシブル画像表示装置用構成部材２０（３０）とが一部剥離して“浮き”が発生する場合があるなどの課題を抱えていた。
また、前記積層状態のまま伸縮させたときにも、粘着シート１０とフレキシブル画像表示装置用構成部材２０（３０）とが一部剥離する場合があった。
また、前記積層状態のまま伸縮させたときにも、粘着シート１０とフレキシブル画像表示装置用構成部材２０（３０）とが一部剥離する場合があった。
そこで、本発明の目的は、粘着シートの表裏一側又は両側にフレキシブル画像表示装置用構成部材を積層し、積層状態のまま、巻き取り、その後、巻き戻して展開したときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離して“浮き”が生じるのを防ぐことができる粘着シートを備えた離型フィルム付き粘着シートを提供することにある。
更に、本発明の他の目的は、粘着シートの表裏一側又は両側にフレキシブル画像表示装置用構成部材を積層し、積層状態のまま伸縮させたときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離して“剥がれ”が生じるのを防ぐことができる粘着シートを備えた離型フィルム付き粘着シートを提供することにある。
更に、本発明の他の目的は、粘着シートの表裏一側又は両側にフレキシブル画像表示装置用構成部材を積層し、積層状態のまま伸縮させたときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離して“剥がれ”が生じるのを防ぐことができる粘着シートを備えた離型フィルム付き粘着シートを提供することにある。
本発明が提案する離型フィルム付き粘着シート、フレキシブル画像表示装置用積層体及びフレキシブル画像表示装置は、上記課題を解決するために、次の構成を有する。
[１] 本発明の第１の態様は、離型フィルムと粘着シートを備えた離型フィルム付き粘着シートであって、離型フィルムと粘着シートとの間に空間部を有し、当該空間部の空隙率（Ｘ）が３～７０％である離型フィルム付き粘着シートである。
[２] 本発明の第２の態様は、前記第１の態様において、前記粘着シートの少なくとも表裏一側の粘着面に、凸部を有する凹凸単位が少なくとも１つ設けられてなる凹凸パターンを備える、離型フィルム付き粘着シートである。
[３] 本発明の第３の態様は、前記第２の態様において、前記凹凸単位における凸部の高さ（α）が７～１００μｍである、離型フィルム付き粘着シートである。
[４] 本発明の第４の態様は、前記第２又は第３の態様において、前記凹凸単位を構成する凸部の最大幅（ｗ１）が１～１０００μｍである、離型フィルム付き粘着シートである。
[５] 本発明の第５の態様は、前記第２～第４の何れか一の態様において、粘着シートの厚み（ｂ）に対する、前記凸部の高さ（α）の比率（α／ｂ）が０．０１以上１未満である、離型フィルム付き粘着シートである。
[６] 本発明の第６の態様は、前記第２～第５の何れか一の態様において、前記凹凸単位が繰り返される凹凸パターンを備えるものであり、前記凹凸単位の繰り返しピッチ（ｗ２）が２～１０００μｍである、離型フィルム付き粘着シートである。
[７] 本発明の第７の態様は、前記第２～第６の何れか一の態様において、前記凹凸単位を構成する凸部と隣接する凸部との間隔（ｗ３）が１～１０００μｍである、離型フィルム付き粘着シートである。
[８] 本発明の第８の態様は、前記第２～第７の何れか一の態様において、前記凹凸単位における凸部の頂面は平坦面であり、前記凸部頂面幅（ｗ４）が１～１０００μｍである、離型フィルム付き粘着シートである。
[９] 本発明の第９の態様は、前記第２～第８の何れか一の態様において、前記凹凸単位を構成する凸部の最大幅（ｗ１）に対する、凸部の高さ（α）に比率（α／ｗ１）が０．０３～０．３である、離型フィルム付き粘着シートである。
[３] 本発明の第３の態様は、前記第２の態様において、前記凹凸単位における凸部の高さ（α）が７～１００μｍである、離型フィルム付き粘着シートである。
[４] 本発明の第４の態様は、前記第２又は第３の態様において、前記凹凸単位を構成する凸部の最大幅（ｗ１）が１～１０００μｍである、離型フィルム付き粘着シートである。
[５] 本発明の第５の態様は、前記第２～第４の何れか一の態様において、粘着シートの厚み（ｂ）に対する、前記凸部の高さ（α）の比率（α／ｂ）が０．０１以上１未満である、離型フィルム付き粘着シートである。
[６] 本発明の第６の態様は、前記第２～第５の何れか一の態様において、前記凹凸単位が繰り返される凹凸パターンを備えるものであり、前記凹凸単位の繰り返しピッチ（ｗ２）が２～１０００μｍである、離型フィルム付き粘着シートである。
[７] 本発明の第７の態様は、前記第２～第６の何れか一の態様において、前記凹凸単位を構成する凸部と隣接する凸部との間隔（ｗ３）が１～１０００μｍである、離型フィルム付き粘着シートである。
[８] 本発明の第８の態様は、前記第２～第７の何れか一の態様において、前記凹凸単位における凸部の頂面は平坦面であり、前記凸部頂面幅（ｗ４）が１～１０００μｍである、離型フィルム付き粘着シートである。
[９] 本発明の第９の態様は、前記第２～第８の何れか一の態様において、前記凹凸単位を構成する凸部の最大幅（ｗ１）に対する、凸部の高さ（α）に比率（α／ｗ１）が０．０３～０．３である、離型フィルム付き粘着シートである。
[１０] 本発明の第１０の態様は、前記第１～第９の何れか一の態様において、ポリエチレンテレフタレートシートに対する９０℃剥離による粘着力（剥離速度３００ｍｍ／ｍｉｎ）が０．５～３０Ｎ／２０ｍｍである、離型フィルム付き粘着シートである。
[１１] 本発明の第１１の態様は、前記第１～第１０の何れか一の態様において、粘着シートの厚み（ｂ）が１０～１００μｍである、離型フィルム付き粘着シートである。
[１１] 本発明の第１１の態様は、前記第１～第１０の何れか一の態様において、粘着シートの厚み（ｂ）が１０～１００μｍである、離型フィルム付き粘着シートである。
[１２] 本発明の第１２の態様は、前記第１～第１１の何れか一の態様において、前記粘着シートが、（メタ）アクリル系重合体（Ａ）及び光重合開始剤（Ｂ）を含有する光硬化性粘着剤組成物から形成される粘着シートである、離型フィルム付き粘着シートである。
[１３] 本発明の第１３の態様は、前記第１２の態様において、光硬化性粘着剤組成物が架橋剤（Ｃ）を含有する、離型フィルム付き粘着シートである。
[１３] 本発明の第１３の態様は、前記第１２の態様において、光硬化性粘着剤組成物が架橋剤（Ｃ）を含有する、離型フィルム付き粘着シートである。
[１４] 本発明の第１４の態様は、前記第１～第１３の何れか一の態様において、フレキシブル画像表示装置用構成部材を貼り合わせるために用いられる、離型フィルム付き粘着シートである。
[１５] 本発明の第１５の態様は、前記第１４の態様において、前記フレキシブル画像表示装置用構成部材がローラブル部材である、離型フィルム付き粘着シートである。
[１６] 本発明の第１６の態様は、前記第１４の態様において、前記フレキシブル画像表示装置用構成部材がストレッチャブル部材である、離型フィルム付き粘着シートである。
[１５] 本発明の第１５の態様は、前記第１４の態様において、前記フレキシブル画像表示装置用構成部材がローラブル部材である、離型フィルム付き粘着シートである。
[１６] 本発明の第１６の態様は、前記第１４の態様において、前記フレキシブル画像表示装置用構成部材がストレッチャブル部材である、離型フィルム付き粘着シートである。
[１７] 本発明の第１７の態様は、前記第１～第１６の何れか一の態様における離型フィルム付き粘着シートの粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたフレキシブル画像表示装置用積層体である。
[１８] 本発明の第１８の態様は、前記第１～第１６の何れか一の態様における離型フィルム付き粘着シートの粘着シートが硬化してなる硬化後粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたフレキシブル画像表示装置用積層体である。
[１８] 本発明の第１８の態様は、前記第１～第１６の何れか一の態様における離型フィルム付き粘着シートの粘着シートが硬化してなる硬化後粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたフレキシブル画像表示装置用積層体である。
[１９] 本発明の第１９の態様は、フレキシブル画像表示装置用構成部材と粘着シートとが積層してなる構成を備えたフレキシブル画像表示装置用積層体であって、
フレキシブル画像表示装置用構成部材と粘着シートとの間に形成された空間部の空隙率（Ｘ）が３～７０％であるフレキシブル画像表示装置用積層体である。
[２０] 本発明の第２０の態様は、前記第１９の態様における前記粘着シートは、前記第１～第１６の何れか一の態様における離型フィルム付き粘着シートの粘着シートである、フレキシブル画像表示装置用積層体である。
フレキシブル画像表示装置用構成部材と粘着シートとの間に形成された空間部の空隙率（Ｘ）が３～７０％であるフレキシブル画像表示装置用積層体である。
[２０] 本発明の第２０の態様は、前記第１９の態様における前記粘着シートは、前記第１～第１６の何れか一の態様における離型フィルム付き粘着シートの粘着シートである、フレキシブル画像表示装置用積層体である。
[２１] 本発明の第２１の態様は、前記第１７～第２０の何れか一の態様におけるフレキシブル画像表示装置用積層体を備えたフレキシブル画像表示装置である。
[２２] 本発明の第２２の態様は、フレキシブル画像表示装置用構成部材を貼り合わせるために使用する粘着シートであって、前記粘着シートの少なくとも表裏一側の粘着面に、凸部を有する凹凸単位が少なくとも１つ設けられてなる凹凸パターンを備え、前記凹凸単位における凸部の高さ（α）が７～１００μｍであり、前記凹凸単位を構成する凸部の最大幅（ｗ１）が１～１０００μｍである粘着シートである。
本発明が提案する離型フィルム付き粘着シートは、離型フィルムと粘着シートとの間に空間部が形成されており、当該空間部は所定範囲の空隙率（Ｘ）を有している。そのため、離型フィルムを剥離した粘着シートを、表面平坦なフレキシブル画像表示装置用構成部材に貼着して積層した場合にも、粘着シートとフレキシブル画像表示装置用構成部材との間に同様の空隙率（Ｘ）を有する空間部を形成することができる。そのように離型フィルムを剥離した粘着シートを、フレキシブル画像表示装置用構成部材に貼着して積層した状態で巻き取り、巻き戻して広げた場合、前記空間部によって、粘着シートの巻き長差分による歪みに由来する応力を緩和することができ、粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができる。よって、本発明が提案する離型フィルム付き粘着シートの粘着シートは、フレキシブル性、特にローラブル性に優れた効果を有することができる。
また、本発明では、前記空間部の空隙率を更に調整することにより、離型フィルムを剥離した粘着シートを、フレキシブル画像表示装置用構成部材に貼着して積層した状態で伸縮させた場合も、粘着シートとフレキシブル画像表示装置用構成部材との間に形成された空間を設けることで応力分散が可能となり応力を緩和することができ、粘着シートとフレキシブル画像表示装置用構成部材との間の“剥がれ”が生じるのを防ぐことができる。よって、本発明が提案する離型フィルム付き粘着シートは、特にストレッチャブル性にも優れた効果をも有することができる。
次に、実施の形態例に基づいて本発明を説明する。但し、本発明が次に説明する実施形態に限定されるものではない。
前述したように、粘着シート１０の表裏一側又は両側にフレキシブル画像表示装置用構成部材２０（３０）を積層し、積層状態のまま、巻き取り、その後、巻き戻して展開したときに、粘着シート１０とフレキシブル画像表示装置用構成部材２０（３０）とが一部剥離して“浮き”が発生する原因は、巻き取った際に生じる粘着シート１０の内側単位円周長（内側巻き長）Ｌ１と外側単位円周長（外側巻き長）Ｌ２との巻き長差（ΔＬ＝Ｌ２－Ｌ１）の、粘着シート１０の厚みｂに対する比率（ΔＬ／ｂ、「巻き長差分」とも称する。）による歪のためであると考えられる（図３参照）。そこで、フレキシブル画像表示装置用構成部材を積層する側の粘着シート表面に、所定の凸部の高さを有する凹凸パターンを形成したところ、巻き取った際に生じる歪を緩和することができ、巻き戻して展開したときに、粘着シートとフレキシブル画像表示装置用構成部材との間に浮きが生じるのを防ぐことができた。また、前記のように積層した状態で伸縮させた場合も、より好ましい空隙率を有する空間部を設けることで応力分散が可能となり、引張応力を緩和することができ、粘着シートとフレキシブル画像表示装置用構成部材との間の“剥がれ”が生じるのを防ぐことができた。
＜＜本発明離型フィルム付き粘着シート＞＞
本発明の実施形態の一例である離型フィルム付き粘着シート（「本発明離型フィルム付き粘着シート」と称する）は、本発明の実施形態の一例に係る粘着シート（以下、「本発明粘着シート」とも称する。）と、本発明の実施形態の一例に係る離型フィルム（以下、「本発明離型フィルム」とも称する。）とを備えたものであり、本発明粘着シートの表裏一側又は両側に本発明離型フィルムが積層された構成を備えたものである。
なお、本発明離型フィルム付き粘着シートにおける本発明粘着シートは、硬化前の状態、硬化後の状態、及び、硬化途中の状態すなわち未だ硬化される余地のある状態に硬化された状態のいずれも包含する。
本発明の実施形態の一例である離型フィルム付き粘着シート（「本発明離型フィルム付き粘着シート」と称する）は、本発明の実施形態の一例に係る粘着シート（以下、「本発明粘着シート」とも称する。）と、本発明の実施形態の一例に係る離型フィルム（以下、「本発明離型フィルム」とも称する。）とを備えたものであり、本発明粘着シートの表裏一側又は両側に本発明離型フィルムが積層された構成を備えたものである。
なお、本発明離型フィルム付き粘着シートにおける本発明粘着シートは、硬化前の状態、硬化後の状態、及び、硬化途中の状態すなわち未だ硬化される余地のある状態に硬化された状態のいずれも包含する。
本発明離型フィルム付き粘着シートは、後述するように、フレキシブル画像表示装置用構成部材を貼り合わせるために好適に使用することができる。
＜空間部＞
本発明離型フィルム付き粘着シートにおいては、本発明離型フィルムで挟持された際に形成される空間部、すなわち、本発明離型フィルムと本発明粘着シートとの間に形成された空間部の空隙率（Ｘ）が３～７０％である粘着シートであるのが好ましい。
当該空間部の空隙率（Ｘ）が３～７０％であれば、本発明離型フィルムを剥離した本発明粘着シートを、表面平坦なフレキシブル画像表示装置用構成部材に貼着して積層した場合にも、本発明粘着シートとフレキシブル画像表示装置用構成部材との間に同様の空隙率（Ｘ）を有する空間部を形成することができる。そのように本発明離型フィルムを剥離した本発明粘着シートを、フレキシブル画像表示装置用構成部材に貼着して積層した状態で巻き取り、巻き戻して広げた時に、前記空間部によって、本発明粘着シートの巻き長差分による歪みに由来する応力を緩和することができ、本発明粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができる。更に、前記のように積層した状態で伸縮させた場合も、前記空間部を更に調整して設けることで応力分散が可能となり応力を緩和することができ、本発明粘着シートとフレキシブル画像表示装置用構成部材との間の“剥がれ”が生じるのを防ぐことができる。
よって、空間部の空隙率（Ｘ）は３％以上であるのが好ましく、中でも４％以上、４．５％以上、５％以上、６％以上、特には８％以上、その中でも１０％以上であるのがさらに好ましい。他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
特に、伸縮させた場合（ストレッチャブル性を目的とする場合）は、空間部の空隙率（Ｘ）は４％以上が好ましく、中でも４．５％以上、５％以上、６％以上、特には８％以上、その中でも１０％以上であり、他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
本発明離型フィルム付き粘着シートにおいては、本発明離型フィルムで挟持された際に形成される空間部、すなわち、本発明離型フィルムと本発明粘着シートとの間に形成された空間部の空隙率（Ｘ）が３～７０％である粘着シートであるのが好ましい。
当該空間部の空隙率（Ｘ）が３～７０％であれば、本発明離型フィルムを剥離した本発明粘着シートを、表面平坦なフレキシブル画像表示装置用構成部材に貼着して積層した場合にも、本発明粘着シートとフレキシブル画像表示装置用構成部材との間に同様の空隙率（Ｘ）を有する空間部を形成することができる。そのように本発明離型フィルムを剥離した本発明粘着シートを、フレキシブル画像表示装置用構成部材に貼着して積層した状態で巻き取り、巻き戻して広げた時に、前記空間部によって、本発明粘着シートの巻き長差分による歪みに由来する応力を緩和することができ、本発明粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができる。更に、前記のように積層した状態で伸縮させた場合も、前記空間部を更に調整して設けることで応力分散が可能となり応力を緩和することができ、本発明粘着シートとフレキシブル画像表示装置用構成部材との間の“剥がれ”が生じるのを防ぐことができる。
よって、空間部の空隙率（Ｘ）は３％以上であるのが好ましく、中でも４％以上、４．５％以上、５％以上、６％以上、特には８％以上、その中でも１０％以上であるのがさらに好ましい。他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
特に、伸縮させた場合（ストレッチャブル性を目的とする場合）は、空間部の空隙率（Ｘ）は４％以上が好ましく、中でも４．５％以上、５％以上、６％以上、特には８％以上、その中でも１０％以上であり、他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
このように、本発明離型フィルムと本発明粘着シートとの間に空間部を形成するには、上記のように、本発明粘着シートの表面に、所定の凸部の高さを有する凹凸パターンを形成するようにすればよい。そして上記空間部の空隙率を上記範囲に調整するには、凸部の高さ（α）や凸部の最大幅（ｗ１）（μｍ）、繰り返しピッチ（ｗ２）（μｍ）、隣接する凸部との間隔（ｗ３）（μｍ）、隣接する凸部との間隔（ｗ３）に対する凸部の高さ（α）の比率（α／ｗ３）、凸部頂面幅（ｗ４）（μｍ）、粘着シートの厚み（ｂ）（μｍ）、粘着シートの厚み（ｂ）に対する凸部の高さ（α）の比率（α／ｂ）、アスペクト比（α／ｗ１）等を適宜調整することにより得られる。
前記空隙率（％）は、以下の方法により測定することができる。
離型フィルム付き粘着シートの表面を、光学顕微鏡を用いて、単位面積当たりの凹凸面積を求め、次いで、凹凸構造を有する離型フィルム付き粘着シートの断面を、光学顕微鏡を用いて、凹凸の高さを求める。凹凸面積と凹凸高さの積より空隙率（％）を測定する。
具体的には例えば、先ず、凹凸構造を有する本発明離型フィルム付き粘着シートの表面を、離型フィルム越しに、光学顕微鏡（例えばキーエンス社製、マイクロスコープＶＨＸ－６００）を用いて、凸部の幅（ｗ２、ｗ３、ｗ４）を測定する。また、本発明離型フィルム付き粘着シートを厚さ方向に切断し、断面における凹凸の高さ（ｈ）及び粘着シート厚み（Ｈ）を、光学顕微鏡を用いて測定する。得られた結果より（（ｗ３＋（ｗ２－ｗ４））×ｈ÷２）／（ｗ２×Ｈ）より空隙率（％）を測定することができる。
但し、空間部の形状によって測定方法を変更してもよい。例えば、凸部がマイクロレンズアレイのような間欠形状の場合には、光学顕微鏡より凸部の直径、高さを測定、また粘着シート厚みＨを測定した後に、単位体積当たりの凸部の体積率より空隙率を算出することもできる。
離型フィルム付き粘着シートの表面を、光学顕微鏡を用いて、単位面積当たりの凹凸面積を求め、次いで、凹凸構造を有する離型フィルム付き粘着シートの断面を、光学顕微鏡を用いて、凹凸の高さを求める。凹凸面積と凹凸高さの積より空隙率（％）を測定する。
具体的には例えば、先ず、凹凸構造を有する本発明離型フィルム付き粘着シートの表面を、離型フィルム越しに、光学顕微鏡（例えばキーエンス社製、マイクロスコープＶＨＸ－６００）を用いて、凸部の幅（ｗ２、ｗ３、ｗ４）を測定する。また、本発明離型フィルム付き粘着シートを厚さ方向に切断し、断面における凹凸の高さ（ｈ）及び粘着シート厚み（Ｈ）を、光学顕微鏡を用いて測定する。得られた結果より（（ｗ３＋（ｗ２－ｗ４））×ｈ÷２）／（ｗ２×Ｈ）より空隙率（％）を測定することができる。
但し、空間部の形状によって測定方法を変更してもよい。例えば、凸部がマイクロレンズアレイのような間欠形状の場合には、光学顕微鏡より凸部の直径、高さを測定、また粘着シート厚みＨを測定した後に、単位体積当たりの凸部の体積率より空隙率を算出することもできる。
＜本発明粘着シート＞
本発明の実施形態の一例に係る本発明粘着シートは、粘着シート１の表裏一側又は両側の粘着面２に、凸部３Ａを有する凹凸単位３が少なくとも１つ以上設けられてなる凹凸パターン４を備えた粘着シートである。
なお、凸部３Ａとは突起した部分であり、凹部３Ｂとは窪んだ部分である。よって、仮に粘着シートの粘着面に凹部３Ｂを形成した場合、同時に凸部３Ａも形成されることになる。
本発明の実施形態の一例に係る本発明粘着シートは、粘着シート１の表裏一側又は両側の粘着面２に、凸部３Ａを有する凹凸単位３が少なくとも１つ以上設けられてなる凹凸パターン４を備えた粘着シートである。
なお、凸部３Ａとは突起した部分であり、凹部３Ｂとは窪んだ部分である。よって、仮に粘着シートの粘着面に凹部３Ｂを形成した場合、同時に凸部３Ａも形成されることになる。
本発明粘着シートは、硬化前の状態、硬化後の状態、及び、硬化途中の状態すなわち未だ硬化される余地のある状態に硬化された状態のいずれも包含する。
本発明粘着シートは、粘着シート１の表裏一側の粘着面２に凹凸パターン４を備えていても、粘着シート１の表裏両側の粘着面２、２に凹凸パターン４を備えていてもよい。
本発明粘着シートを上面視した際の前記凹凸パターン４の形状は、例えば、ストライプ状、円状、矩形状など、所定の平面視形状を有する凹凸単位３が、一定方向、好ましくは巻き周方向とする方向に形成されるものであればよく、好ましくは繰り返し形成されてなる形状であれば好適に採用できる（図４参照）。
この際、前記凹凸パターン４は、凹凸単位３が規則的に繰り返すように形成されていてもよいし、不規則に繰り返すように形成されていてもよい。
但し、製造のし易さなどを考慮すれば、直線状に伸びた凹状溝部又は凸状部又はこれら両方の組み合わせが一定方向、好ましくは巻き周方向に繰り返してなるストライプ状を呈するものが好ましい。
なお、前記凹凸パターン４は、１つの凹凸単位３からなる場合も包含する。例えば巻き径が顕著に大きい場合や、フォルダブルの曲率部のみに適用する場合など、凹凸パターン４が局所的に形成されていれば十分である場合があるため、そのような場合は、凹凸パターン４が１つの凹凸単位３からなる場合であっても本発明の効果を享受することができる。
この際、前記凹凸パターン４は、凹凸単位３が規則的に繰り返すように形成されていてもよいし、不規則に繰り返すように形成されていてもよい。
但し、製造のし易さなどを考慮すれば、直線状に伸びた凹状溝部又は凸状部又はこれら両方の組み合わせが一定方向、好ましくは巻き周方向に繰り返してなるストライプ状を呈するものが好ましい。
なお、前記凹凸パターン４は、１つの凹凸単位３からなる場合も包含する。例えば巻き径が顕著に大きい場合や、フォルダブルの曲率部のみに適用する場合など、凹凸パターン４が局所的に形成されていれば十分である場合があるため、そのような場合は、凹凸パターン４が１つの凹凸単位３からなる場合であっても本発明の効果を享受することができる。
前記凹凸パターン４を構成する凹凸単位３は、粘着シートの幅方向、すなわち巻き周方向とする方向と直交する方向に伸びる凸状部又は凹状溝部又はこれらの組み合わせであるのが好ましい。
本発明粘着シートを一定方向、例えば巻き周方向に沿って肉厚方向に切断した縦断面に見て、凹凸パターン４を構成する凹凸単位３の断面形状は、例えば三角状、四角状、台形状、半円状、半楕円状など、任意の所定形状の凹部３Ｂ又は凸部３Ａが繰返してなる形状であればよい（図５参照）。
前記凹凸単位３における凸部３Ａの高さ（α）は７～１００μｍであるのが好ましい。
凹凸単位３における凸部３Ａの高さ（α）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凹凸単位３における最頂部と最低部を基準とする縦長さの意味である。
凹凸単位３における凸部３Ａの高さ（α）が７μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力を緩和することができ、浮きの発生を防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより防ぐことができる。他方、１００μｍ以下であれば、成形性に優れ均一な凹凸単位３を得ることができる。
かかる観点から、凹凸単位３における凸部３Ａの高さ（α）は７．５μｍ以上であるのがより好ましく、８μｍ以上であるのがさらに好ましく、８．５μｍ以上であるのが特に好ましい。他方、１００μｍ以下であるのがより好ましく、さらに９５μｍ以下、特に９０μｍ以下であるのが好ましく、８０μｍ以下であるのが特に好ましく、７５μｍ以下であるのが殊に好ましく、７０μｍ以下であるのが最も好ましい。
凹凸単位３における凸部３Ａの高さ（α）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凹凸単位３における最頂部と最低部を基準とする縦長さの意味である。
凹凸単位３における凸部３Ａの高さ（α）が７μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力を緩和することができ、浮きの発生を防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより防ぐことができる。他方、１００μｍ以下であれば、成形性に優れ均一な凹凸単位３を得ることができる。
かかる観点から、凹凸単位３における凸部３Ａの高さ（α）は７．５μｍ以上であるのがより好ましく、８μｍ以上であるのがさらに好ましく、８．５μｍ以上であるのが特に好ましい。他方、１００μｍ以下であるのがより好ましく、さらに９５μｍ以下、特に９０μｍ以下であるのが好ましく、８０μｍ以下であるのが特に好ましく、７５μｍ以下であるのが殊に好ましく、７０μｍ以下であるのが最も好ましい。
本発明粘着シートの厚み（ｂ）に対する、前記凸部３Ａの高さ（α）の比率（α／ｂ）は０．０１以上１未満であるのが、好ましい。
当該比率（α／ｂ）が０．０１以上であれば、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１未満であれば、成形性に優れ均一な凹凸単位３を得ることができる。
かかる観点から、本発明粘着シートの厚み（ｂ）に対する、前記凸部３Ａの高さ（α）の比率（α／ｂ）は０．０１５以上であるのがより好ましく、０．０１７以上であるのがさらに好ましく、０．０２以上、０．０３以上、０．０５以上、０．１以上、０．１５以上であるのが特に好ましい。他方、１未満であるのが好ましく、０．９９８以下であるのがさらに好ましく、０．９９５以下、０．９９以下、０．９５以下、０．９０以下であるのが特に好ましい。
当該比率（α／ｂ）が０．０１以上であれば、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１未満であれば、成形性に優れ均一な凹凸単位３を得ることができる。
かかる観点から、本発明粘着シートの厚み（ｂ）に対する、前記凸部３Ａの高さ（α）の比率（α／ｂ）は０．０１５以上であるのがより好ましく、０．０１７以上であるのがさらに好ましく、０．０２以上、０．０３以上、０．０５以上、０．１以上、０．１５以上であるのが特に好ましい。他方、１未満であるのが好ましく、０．９９８以下であるのがさらに好ましく、０．９９５以下、０．９９以下、０．９５以下、０．９０以下であるのが特に好ましい。
前記凹凸単位３を構成する凸部３Ａの最大幅（ｗ１）は１～１０００μｍであるのが好ましい。
凹凸単位３を構成する凸部３Ａの最大幅（ｗ１）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凸部３Ａの当該巻き周方向に最長な部分の横幅の意味である。例えば、凸部３Ａが台形状の場合は底辺部の長さが最大幅（ｗ１）となる。
凸部３Ａの最大幅（ｗ１）が１μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、前記凹凸単位３を構成する凸部３Ａの最大幅（ｗ１）は２μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上、５０μｍ以上、１００μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下であるのが特に好ましい。
凹凸単位３を構成する凸部３Ａの最大幅（ｗ１）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凸部３Ａの当該巻き周方向に最長な部分の横幅の意味である。例えば、凸部３Ａが台形状の場合は底辺部の長さが最大幅（ｗ１）となる。
凸部３Ａの最大幅（ｗ１）が１μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、前記凹凸単位３を構成する凸部３Ａの最大幅（ｗ１）は２μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上、５０μｍ以上、１００μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下であるのが特に好ましい。
凹凸単位３が繰り返される場合、凹凸単位３の繰り返しピッチ（ｗ２）は２～１０００μｍであるのが好ましい。
凹凸単位３の繰り返しピッチ（ｗ２）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、隣の凹凸単位３の同一形状部分との距離の意味である。
当該繰り返しピッチ（ｗ２）が２μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、前記凹凸単位３の繰り返しピッチ（ｗ２）は３μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上、５０μｍ以上、１００μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下であるのが特に好ましい。
なお、繰り返しピッチ（ｗ２）は必ずしも一定である必要はない。
凹凸単位３の繰り返しピッチ（ｗ２）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、隣の凹凸単位３の同一形状部分との距離の意味である。
当該繰り返しピッチ（ｗ２）が２μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、前記凹凸単位３の繰り返しピッチ（ｗ２）は３μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上、５０μｍ以上、１００μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下であるのが特に好ましい。
なお、繰り返しピッチ（ｗ２）は必ずしも一定である必要はない。
凹凸単位３が繰り返される場合、前記凹凸単位３を構成する凸部３Ａと隣接する凸部３Ａとの間隔（ｗ３）は１～１０００μｍであるのが好ましい。
凸部３Ａと隣接する凸部３Ａとの間隔（ｗ３）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凸部３Ａと隣接する凸部３Ａとの間の平面部の巻き周方向長さの意味である。
当該間隔（ｗ３）が１μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な粘着性が確保できるため好ましい。
かかる観点から、前記凹凸単位３を構成する凸部３Ａと隣接する凸部３Ａとの間隔（ｗ３）は２μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上、３０μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下、５００μｍ以下、２００μｍ以下であるのが特に好ましい。
なお、図５（Ｄ）のように、隣接する凸部３Ａとの間隔（ｗ３）がゼロの場合もある。
凸部３Ａと隣接する凸部３Ａとの間隔（ｗ３）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凸部３Ａと隣接する凸部３Ａとの間の平面部の巻き周方向長さの意味である。
当該間隔（ｗ３）が１μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な粘着性が確保できるため好ましい。
かかる観点から、前記凹凸単位３を構成する凸部３Ａと隣接する凸部３Ａとの間隔（ｗ３）は２μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上、３０μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下、５００μｍ以下、２００μｍ以下であるのが特に好ましい。
なお、図５（Ｄ）のように、隣接する凸部３Ａとの間隔（ｗ３）がゼロの場合もある。
前記凹凸単位３を構成する凸部３Ａの頂面幅（ｗ４）は、１～１０００μｍであるのが好ましい。
凸部３Ａの頂面幅（ｗ４）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凸部頂上部の平面部の巻き周方向長さの意味である。
凸部３Ａの頂面幅（ｗ４）が１μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、凸部３Ａの頂面幅（ｗ４）は２μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下であるのが特に好ましい。
なお、図５（Ｃ）のように、凸部３Ａの頂面幅（ｗ４）がゼロの場合もある。
凸部３Ａの頂面幅（ｗ４）とは、本発明粘着シートを巻き周方向とする方向に沿って肉厚方向に切断した縦断面に見た際に、凸部頂上部の平面部の巻き周方向長さの意味である。
凸部３Ａの頂面幅（ｗ４）が１μｍ以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、１０００μｍ以下であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、凸部３Ａの頂面幅（ｗ４）は２μｍ以上であるのがより好ましく、５μｍ以上であるのがさらに好ましく、１０μｍ以上であるのが特に好ましい。他方、９００μｍ以下であるのがより好ましく、８００μｍ以下であるのがさらに好ましく、７００μｍ以下であるのが特に好ましい。
なお、図５（Ｃ）のように、凸部３Ａの頂面幅（ｗ４）がゼロの場合もある。
本発明粘着シートの厚み（ｂ）は１０μｍ～１００μｍであるのが好ましい。
本発明粘着シートの厚み（ｂ）は、凹凸パターン４の厚みを含めた厚みである。
本発明粘着シートの厚み（ｂ）が１０μｍ以上であれば、所望の粘着力を発現することができ、１００μｍ以下であれば、巻き長差分（ΔＬ／ｂ）が小さくなり、それによる歪をより一層抑えることができる。
かかる観点から、本発明粘着シートの厚み（ｂ）は１５μｍ以上であるのがより好ましく、２０μｍ以上であるのがさらに好ましく、２５μｍ以上であるのが特に好ましい。他方、９０μｍ以下であるのがより好ましく、８５μｍ以下であるのがさらに好ましく、８０μｍ以下であるのが特に好ましい。
本発明粘着シートの厚み（ｂ）は、凹凸パターン４の厚みを含めた厚みである。
本発明粘着シートの厚み（ｂ）が１０μｍ以上であれば、所望の粘着力を発現することができ、１００μｍ以下であれば、巻き長差分（ΔＬ／ｂ）が小さくなり、それによる歪をより一層抑えることができる。
かかる観点から、本発明粘着シートの厚み（ｂ）は１５μｍ以上であるのがより好ましく、２０μｍ以上であるのがさらに好ましく、２５μｍ以上であるのが特に好ましい。他方、９０μｍ以下であるのがより好ましく、８５μｍ以下であるのがさらに好ましく、８０μｍ以下であるのが特に好ましい。
本発明粘着シートにおいて、粘着シートの厚み（ｂ）に対する凸部の高さ（α）の比率（α／ｂ）は、０．０１以上１未満であるのが好ましい。
比率（α／ｂ）が上記下限値以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、上記上限値未満であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、比率（α／ｂ）は０．０１５以上であるのがより好ましく、０．０１７以上であるのがさらに好ましく、０．０３以上、０．０５以上、０．１以上、０．１５以上であるのが特に好ましい。他方、０．９９８以下であるのがさらに好ましく、０．９９５以下、０．９９以下、０．９５以下、０．９０以下であるのが特に好ましい。
比率（α／ｂ）が上記下限値以上であれば、フレキシブル画像表示装置用構成部材２０（３０）と粘着面２の間に十分な空間を設けることができるため、巻き取り及び巻き戻し時に巻き長差分により生じる歪みに由来する応力をより一層緩和することができ、浮きの発生をより一層防ぐことができる。また、伸縮時の応力を緩和することができ、剥がれをより一層防ぐことができる。他方、上記上限値未満であれば、巻き取った際又は伸縮時に生じる歪、応力を緩和することができる。
かかる観点から、比率（α／ｂ）は０．０１５以上であるのがより好ましく、０．０１７以上であるのがさらに好ましく、０．０３以上、０．０５以上、０．１以上、０．１５以上であるのが特に好ましい。他方、０．９９８以下であるのがさらに好ましく、０．９９５以下、０．９９以下、０．９５以下、０．９０以下であるのが特に好ましい。
更に、凹凸パターンにおける凸部のアスペクト比、すなわち前記凹凸単位を構成する凸部の最大幅（ｗ１）に対する、凸部の高さ（α）に比率（α／ｗ１）は０．０３～０．３であることが好ましい。
凸部のアスペクト比（α／ｗ１）が０．０３以上であれば空間を維持することが可能であり、０．３以下であれば伸縮時の応力を緩和することができ、剥がれを一層防ぐことができることから好ましい。
よって、凸部のアスペクト比（α／ｗ１）は０．０３２以上であるのがさらに好ましく、中でも０．０３４以上、その中でも０．０３５以上であるのがさらに好ましい。他方、０．２９以下であるのがさらに好ましく、中でも０．２８以下、その中でも０．２６以下であるのがさらに好ましい。
凸部のアスペクト比（α／ｗ１）が０．０３以上であれば空間を維持することが可能であり、０．３以下であれば伸縮時の応力を緩和することができ、剥がれを一層防ぐことができることから好ましい。
よって、凸部のアスペクト比（α／ｗ１）は０．０３２以上であるのがさらに好ましく、中でも０．０３４以上、その中でも０．０３５以上であるのがさらに好ましい。他方、０．２９以下であるのがさらに好ましく、中でも０．２８以下、その中でも０．２６以下であるのがさらに好ましい。
凹凸パターン４は、粘着シートの粘着面全面に均等に形成することもできるし、曲率がかかる部分にのみ形成することもできる。
＜本発明粘着剤組成物＞
本発明粘着シートは、（メタ）アクリル系重合体（Ａ）及び光重合開始剤（Ｂ）、必要に応じてさらに架橋剤（Ｃ）、さらにその他の成分を含有する光硬化性粘着剤組成物（「本発明粘着剤組成物」とも称する）から形成することができる。
本発明粘着シートは、（メタ）アクリル系重合体（Ａ）及び光重合開始剤（Ｂ）、必要に応じてさらに架橋剤（Ｃ）、さらにその他の成分を含有する光硬化性粘着剤組成物（「本発明粘着剤組成物」とも称する）から形成することができる。
（(メタ)アクリル系重合体（Ａ））
本発明粘着剤組成物において、(メタ)アクリル系重合体（Ａ）を含有し、とりわけ主成分樹脂として含有するものである。
すなわち、(メタ)アクリル系重合体（Ａ）は、本発明粘着剤組成物を構成する不揮発成分の中で最も質量割合が高い成分である。この際、本発明粘着剤組成物を構成する不揮発成分のうち、(メタ)アクリル系重合体（Ａ）の質量割合は５０質量％以上、中でも７０質量％以上、その中でも８０質量％以上、その中でも９０質量％以上であってもよい。
本発明粘着剤組成物において、(メタ)アクリル系重合体（Ａ）を含有し、とりわけ主成分樹脂として含有するものである。
すなわち、(メタ)アクリル系重合体（Ａ）は、本発明粘着剤組成物を構成する不揮発成分の中で最も質量割合が高い成分である。この際、本発明粘着剤組成物を構成する不揮発成分のうち、(メタ)アクリル系重合体（Ａ）の質量割合は５０質量％以上、中でも７０質量％以上、その中でも８０質量％以上、その中でも９０質量％以上であってもよい。
前記（メタ）アクリル系重合体（Ａ）としては、次の式１（式中、Ｒ１は水素原子又はメチル基を表し、Ｒ２は炭素原子数４～１８の直鎖もしくは分岐状のアルキル基または脂環式炭化水素を表す。）で示される化合物由来の構造単位を含むものであり、当該モノマー成分を５０質量％以上含む重合成分を重合したものが好ましい。
中でも、（メタ）アクリル系重合体（Ａ）は、前記モノマー成分を重合成分として５５質量％以上含み重合したものがさらに好ましく、その中でも６０質量％以上含み重合したものが特に好ましい。
なお、本発明において、「（メタ）アクリル」とは、アクリル及びメタクリルを、「（メタ）アクリロイル」とは、アクリロイル及びメタクリロイルを、「（メタ）アクリレート」とはアクリレート及びメタクリレートをそれぞれ包括する意味であり、「（共）重合体」とは、重合体及び共重合体を包括する意味である。
前記式１で表されるモノマーとしては、例えばｎ－ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｓｅｃ－ブチル（メタ）アクリレート、ｔ－ブチル（メタ）アクリレート、ペンチル（メタ）アクリレート、イソペンチル（メタ）アクリレート、ネオペンチル（メタ）アクリレート、ヘキシル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ｎ－オクチル（メタ）アクリート、イソオクチル（メタ）アクリレート、ノニル（メタ）アクリレート、イソノニル（メタ）アクリレート、ｔ－ブチルシクロヘキシル（メタ）アクリレート、デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ウンデシル（メタ）アクリレート、ラウリル（メタ）アクリレート、トリデシル（メタ）アクリレート、テトラデシル（メタ）アクリレート、セチル（メタ）アクリレート、ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレート、イソボルニル（メタ）アクリレート、３，５，５－トリメチルシクロヘキサン（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート、ジシクロペンテニル（メタ）アクリレート等を挙げることができる。これらは１種又は２種以上を組み合わせて使用してもよい。前記の中でも、ブチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ｎ－オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ラウリル（メタ）アクリレートの何れか１種以上を含むことが特に好ましい。
前記（メタ）アクリル系重合体（Ａ）は、前記モノマー成分以外の「他の共重合性モノマー」を共重合成分として有する共重合体であるのが好ましい。
前記「他の共重合性モノマー」は、（メタ）アクリル系重合体（Ａ）中に、１～３０質量％含むことが好ましく、中でも２質量％以上或いは２５質量％以下の割合で含まれることがより好ましい。
当該「他の共重合性モノマー」としては、例えば（ａ）カルボキシル基含有モノマー（以下「共重合性モノマーａ１」とも称する。）、（ｂ）水酸基含有モノマー（以下「共重合性モノマーａ２」とも称する。）、（ｃ）アミノ基含有モノマー（以下「共重合性モノマーａ３」とも称する。）、（ｄ）エポキシ基含有モノマー（以下「共重合性モノマーａ４」とも称する。）、（ｅ）アミド基含有モノマー（以下「共重合性モノマーａ５」とも称する。）、（ｆ）ビニルモノマー（以下「共重合性モノマーａ６」とも称する。）、（ｇ）アルキル基の炭素数が１～３の（メタ）アクリレートモノマー（以下「共重合性モノマーａ７」とも称する。）、（ｈ）マクロモノマー（以下「共重合性モノマーａ８」とも称する。）、（ｉ）芳香族含有モノマー（以下「共重合性モノマーａ９」と称する）や、（ｊ）その他官能基含有モノマー（以下「共重合性モノマーａ１０」）を挙げることができる。上記の中でも、（ａ）カルボキシル基含有モノマーや、（ｂ）水酸基含有モノマー、（ｈ）マクロモノマーを含有することが好ましい。これらは１種又は２種以上を組み合わせてもよい。
前記共重合性モノマーａ１としては、例えば（メタ）アクリル酸、カルボキシエチル（メタ）アクリレート、カルボキシプロピル（メタ）アクリレート、カルボキシブチル（メタ）アクリレート、ω－カルボキシポリカプロラクトンモノ（メタ）アクリレート、２－（メタ）アクリロイルオキシエチルヘキサヒドロフタル酸、２－（メタ）アクリロイルオキシプロピルヘキサヒドロフタル酸、２－（メタ）アクリロイルオキシエチルフタル酸、２－（メタ）アクリロイルオキシプロピルフタル酸、２－（メタ）アクリロイルオキシエチルマレイン酸、２－（メタ）アクリロイルオキシプロピルマレイン酸、２－（メタ）アクリロイルオキシエチルコハク酸、２－（メタ）アクリロイルオキシプロピルコハク酸、クロトン酸、フマル酸、マレイン酸、イタコン酸を挙げることができる。これらは１種又は２種以上を組み合わせてもよい。
前記共重合性モノマーａ２としては、例えば２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシ－１－メチルエチルアクリレート、３－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、グリセリンモノ（メタ）アクリレート、ポリエチレングリコールモノ（メタ）アクリレート、ポリプロピレングリコールモノ(メタ)アクリレート、ポリエチレングリコールポリプロピレングリコールモノ(メタ)アクリレート、ポリエチレングリコールポリブチレングリコールモノ(メタ)アクリレート、ポリプロピレングリコールポリブチレングリコールモノ(メタ)アクリレート、ヒドロキシフェニル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレート類を挙げることができる。これらは１種又は２種以上を組み合わせてもよい。
前記共重合性モノマーａ８としてのマクロモノマーは、末端の官能基と高分子量骨格成分とを有する高分子単量体である。
前記「他の共重合性モノマー」が共重合性モノマーａ８である場合、前記（メタ）アクリル系重合体（Ａ）は、マクロモノマー由来の構造単位を含む共重合体である。
前記「他の共重合性モノマー」が共重合性モノマーａ８である場合、前記（メタ）アクリル系重合体（Ａ）は、マクロモノマー由来の構造単位を含む共重合体である。
本樹脂組成物においては、前記マクロモノマーとしては、炭素数１～３の直鎖もしくは分岐状のアルキル基を持つ（メタ）アクリレートが共重合されたマクロモノマーであることで、加工性や保管安定性を向上させることができるから良好である。
かかるマクロモノマーの数平均分子量としては、好ましくは１０００～１００００、特に好ましくは１５００以上或いは５０００以下、更に好ましくは２０００以上或いは４０００以下である。
かかるマクロモノマーの数平均分子量としては、好ましくは１０００～１００００、特に好ましくは１５００以上或いは５０００以下、更に好ましくは２０００以上或いは４０００以下である。
特に本樹脂組成物においては、（メタ）アクリル系重合体（Ａ）におけるマクロモノマーの共重合割合が３０質量％以下であることがホットメルト時の流動性付与の点で好ましく、より好ましくは２質量％以上或いは１５質量％以下、さらに好ましくは３質量％以上或いは１０質量％以下、とくに好ましくは４質量％以上或いは７質量％以下である。
前記（メタ）アクリル系重合体（Ａ）は、金属腐食防止性及び耐湿熱白化性などの観点から、前記「共重合性モノマーａ１」を含まない又は実質的に含まないものであるのが好ましい。
なお、「共重合性モノマーａ１を含まない又は実質的に含まない」とは、完全に含まない場合のみならず、（メタ）アクリル酸エステル（共）重合体中に、共重合性モノマーａ１が０．５質量％未満、好ましくは、０．１質量％未満で含むものを許容する意である。
なお、「共重合性モノマーａ１を含まない又は実質的に含まない」とは、完全に含まない場合のみならず、（メタ）アクリル酸エステル（共）重合体中に、共重合性モノマーａ１が０．５質量％未満、好ましくは、０．１質量％未満で含むものを許容する意である。
（メタ）アクリル系重合体（Ａ）のガラス転移温度は－７０～０℃であるのが好ましい。
なお、共重合体成分のガラス転移温度とは、当該共重合体各成分のホモポリマーから得られるポリマーのガラス転移温度と構成比率から、Ｆｏｘの計算式によって算出される値を意味する。
Ｆｏｘの計算式とは、以下の式により求められる計算値であり、ポリマーハンドブック〔ＰｏｌｙｍｅｒＨａｎｄＢｏｏｋ，Ｊ．Ｂｒａｎｄｒｕｐ，Ｉｎｔｅｒｓｃｉｅｎｃｅ，１９８９〕に記載されている値を用いて求めることができる。
１／（２７３＋Ｔｇ）＝Σ（Ｗｉ／（２７３＋Ｔｇｉ））
［式中、Ｗｉはモノマーｉの重量分率、ＴｇｉはモノマーｉのホモポリマーのＴｇ（℃）を示す。］
Ｆｏｘの計算式とは、以下の式により求められる計算値であり、ポリマーハンドブック〔ＰｏｌｙｍｅｒＨａｎｄＢｏｏｋ，Ｊ．Ｂｒａｎｄｒｕｐ，Ｉｎｔｅｒｓｃｉｅｎｃｅ，１９８９〕に記載されている値を用いて求めることができる。
１／（２７３＋Ｔｇ）＝Σ（Ｗｉ／（２７３＋Ｔｇｉ））
［式中、Ｗｉはモノマーｉの重量分率、ＴｇｉはモノマーｉのホモポリマーのＴｇ（℃）を示す。］
上記（メタ）アクリル系重合体（Ａ）を得るに際しては、（メタ）アクリル系重合体（Ａ）が有する（メタ）アクリル酸エステル由来の繰り返し単位のうち、少なくとも１つの繰り返し単位のガラス転移温度は－７０～０℃であるのが好ましい。
また、（メタ）アクリル系重合体（Ａ）が有する（メタ）アクリル酸エステル由来の繰り返し単位のうち、少なくとも１つの繰り返し単位のガラス転移温度が２０～１２０℃である場合には、優れた加工性や保管安定性を保持できる為好ましい。具体的には、本発明粘着シートのホットメルト温度に影響するため、このガラス転移温度（Ｔｇ）は３０℃～１２０℃であるのが好ましく、中でも４０℃以上或いは１１０℃以下、その中でも５０℃以上或いは１００℃以下であるのがさらに好ましい。
このようなガラス転移温度（Ｔｇ）を有する繰り返し単位があれば、分子量を調整することにより、優れた加工性や保管安定性を保持できると共に、５０℃以上でホットメルトするように調整することができる。
このようなガラス転移温度（Ｔｇ）を有する繰り返し単位があれば、分子量を調整することにより、優れた加工性や保管安定性を保持できると共に、５０℃以上でホットメルトするように調整することができる。
（重合開始剤（Ｂ））
重合開始剤（Ｂ）は、本発明粘着シートに活性エネルギー線硬化性を付与するものであり、活性エネルギー線によってラジカルを発生する化合物であればよい。
重合開始剤（Ｂ）は、ラジカル発生機構によって大きく２つに分類され、重合開始剤自身の単結合を開裂分解してラジカルを発生させることができる開裂型光開始剤と、励起した開始剤と系中の水素供与体とが励起錯体を形成し、水素供与体の水素を転移させることができる水素引抜型光開始剤と、に大別される。
なお、（メタ）アクリル系重合体（Ａ）が、例えば、ベンゾフェノン構造等のように、活性エネルギー線照射により励起し、その励起状態において、系中の水素ラジカルを引き抜くことができる構造を有する場合や、活性エネルギー線として電子線を用いる場合は、必ずしも重合開始剤（Ｂ）を含む必要はない。
重合開始剤（Ｂ）は、本発明粘着シートに活性エネルギー線硬化性を付与するものであり、活性エネルギー線によってラジカルを発生する化合物であればよい。
重合開始剤（Ｂ）は、ラジカル発生機構によって大きく２つに分類され、重合開始剤自身の単結合を開裂分解してラジカルを発生させることができる開裂型光開始剤と、励起した開始剤と系中の水素供与体とが励起錯体を形成し、水素供与体の水素を転移させることができる水素引抜型光開始剤と、に大別される。
なお、（メタ）アクリル系重合体（Ａ）が、例えば、ベンゾフェノン構造等のように、活性エネルギー線照射により励起し、その励起状態において、系中の水素ラジカルを引き抜くことができる構造を有する場合や、活性エネルギー線として電子線を用いる場合は、必ずしも重合開始剤（Ｂ）を含む必要はない。
重合開始剤（Ｂ）としては、開裂型光開始剤及び水素引抜型光開始剤のいずれであってもよく、それぞれ単独に使用しても両者を混合して使用してもよく、さらに、各々について１種又は２種以上を併用してもよい。
光開始剤として水素引抜型光開始剤を用いた場合、（メタ）アクリル系重合体からも水素引抜反応を起こして、活性エネルギー線硬化性化合物のみならず（メタ）アクリル系重合体も架橋構造に取り込まれ、架橋点が多い架橋構造を形成することができる点で好ましい。
また、重合開始剤（Ｂ）として開裂型光開始剤を用いた場合、一度ラジカル発生させると分解して失活することから、硬化後に予期せぬ反応や劣化をおこす恐れがない点で好ましい。
光開始剤として水素引抜型光開始剤を用いた場合、（メタ）アクリル系重合体からも水素引抜反応を起こして、活性エネルギー線硬化性化合物のみならず（メタ）アクリル系重合体も架橋構造に取り込まれ、架橋点が多い架橋構造を形成することができる点で好ましい。
また、重合開始剤（Ｂ）として開裂型光開始剤を用いた場合、一度ラジカル発生させると分解して失活することから、硬化後に予期せぬ反応や劣化をおこす恐れがない点で好ましい。
開裂型光開始剤としては、例えば２,２－ジメトキシ－１,２－ジフェニルエタン－１－オン、１－ヒドロキシシクロヘキシルフェニルケトン、２－ヒドロキシ－２－メチル－１－フェニル－プロパン－１－オン、１－（４－（２－ヒドロキシエトキシ）フェニル）－２－ヒドロキシ－２－メチル－１－プロパン－１－オン、２－ヒロドキシ－１－［４－｛４－（２－ヒドロキシ－２－メチル－プロピオニル）ベンジル｝フェニル］－２－メチル－プロパン－１－オン、オリゴ（２－ヒドロキシ－２－メチル－１－（４－（１－メチルビニル）フェニル）プロパノン）、フェニルグリオキシリック酸メチル、２－ベンジル－２－ジメチルアミノ－１－（４－モルフォリノフェニル）ブタン－１－オン、２－メチル－１－［４－（メチルチオ）フェニル］－２－モルフォリノプロパン－１－オン、２－（ジメチルアミノ）－２－[（４－メチルフェニル）メチル]－１－[４－（４－モルホリニル）フェニル]－１－ブタノン、ビス（２，４，６－トリメチルベンゾイル）－フェニルフォスフィンオキサイド、２，４，６－トリメチルベンゾイルジフェニルフォスフィンオキサイド、（２，４，６－トリメチルベンゾイル）エトキシフェニルホスフィンオキサイド、ビス（２，６－ジメトキシベンゾイル）２，４，４－トリメチルペンチルフォスフィンオキサイドや、それらの誘導体などを挙げることができる。
水素引抜型光開始剤としては、例えばベンゾフェノン、４－メチル－ベンゾフェノン、２，４，６－トリメチルベンゾフェノン、４－フェニルベンゾフェノン、３，３’－ジメチル－４－メトキシベンゾフェノン、４－（メタ）アクリロイルオキシベンゾフェノン、２－ベンゾイル安息香酸メチル、ベンゾイル蟻酸メチル、ビス（２－フェニル－２－オキソ酢酸）オキシビスエチレン、４－（１，３－アクリロイル－１，４，７，１０，１３－ペンタオキソトリデシル）ベンゾフェノン、チオキサントン、２－クロロチオキサントン、３－メチルチオキサントン、２，４－ジメチルチオキサントン、２－メチルアントラキノン、２－エチルアントラキノン、２－ｔｅｒｔ－ブチルアントラキノン、２－アミノアントラキノンやその誘導体などを挙げることができる。
上記重合開始剤（Ｂ）の含有量は特に制限されるものではない。目安としては、（メタ）アクリル系重合体（Ａ）１００質量部に対して０．５質量部以上５質量部以下、中でも１質量部以上或いは４質量部以下、その中でも１．２質量部以上或いは３質量部以下の割合で含有するのが好ましい。
（架橋剤（Ｃ））
架橋剤（Ｃ）は、本発明粘着剤組成物に架橋構造を形成する化合物乃至組成物であり、２以上の架橋性官能基を有する化合物である。
本発明粘着剤組成物が、架橋剤（Ｃ）を含むことにより、本発明粘着剤組成物が架橋構造を形成し、本発明粘着シートに耐久性を付与することができる。
但し、（メタ）アクリル系重合体（Ａ）が重合開始剤（Ｂ）等の作用によって水素引抜反応を起こして、（メタ）アクリル系重合体（Ａ）内及び／又は（メタ）アクリル系重合体（Ａ）間で十分な架橋構造を形成することができる場合は、必ずしも架橋剤（Ｃ）を含む必要はない。
架橋剤（Ｃ）は、本発明粘着剤組成物に架橋構造を形成する化合物乃至組成物であり、２以上の架橋性官能基を有する化合物である。
本発明粘着剤組成物が、架橋剤（Ｃ）を含むことにより、本発明粘着剤組成物が架橋構造を形成し、本発明粘着シートに耐久性を付与することができる。
但し、（メタ）アクリル系重合体（Ａ）が重合開始剤（Ｂ）等の作用によって水素引抜反応を起こして、（メタ）アクリル系重合体（Ａ）内及び／又は（メタ）アクリル系重合体（Ａ）間で十分な架橋構造を形成することができる場合は、必ずしも架橋剤（Ｃ）を含む必要はない。
前記架橋性官能基としては、例えばイソシアネート基、エポキシ基、（メタ）アクリロイル基、チオイソシアネート基、１級もしくは２級のアミノ基及びチオール基を挙げることができる。これらは適当な保護基で保護されていてもよい。
架橋剤に含まれる架橋性官能基の好ましい組み合わせとしては、エポキシ基のみ、イソシアネート基のみ、（メタ）アクリロイル基のみ、チオイソシアネート基のみ、チオール基のみ、１級もしくは２級のアミノ基のみ、エポキシ基と（メタ）アクリロイル基、イソシアネート基と（メタ）アクリロイル基の組み合わせを挙げることができる。
中でも、本発明粘着シートが活性エネルギー線を照射されることにより硬化する性質を担保する観点から、架橋剤（Ｃ）として、（メタ）アクリロイル基を２つ以上有する多官能（メタ）アクリレート（ｃ１）であるのが好ましい。
中でも、本発明粘着シートが活性エネルギー線を照射されることにより硬化する性質を担保する観点から、架橋剤（Ｃ）として、（メタ）アクリロイル基を２つ以上有する多官能（メタ）アクリレート（ｃ１）であるのが好ましい。
多官能（メタ）アクリレート（ｃ１）の含有質量は、(メタ)アクリル系重合体（Ａ）１００質量部に対して、０．５質量部以上であるのが好ましく、中でも１質量部以上、その中で１．５質量部以上である方がより好ましい。
上限値に関しては、適度な柔軟性を維持して折り曲げ時の被着体への追従性を担保する観点から、２０質量部以下であるのが好ましく、１５質量部以下であるのがより好ましく、１０質量部以下であるのがさらに好ましく、さらにその中でも５質量部以下、その中でも３質量部以下、特に２質量部以下である方が好ましい。
上限値に関しては、適度な柔軟性を維持して折り曲げ時の被着体への追従性を担保する観点から、２０質量部以下であるのが好ましく、１５質量部以下であるのがより好ましく、１０質量部以下であるのがさらに好ましく、さらにその中でも５質量部以下、その中でも３質量部以下、特に２質量部以下である方が好ましい。
多官能（メタ）アクリレート（ｃ１）としては、例えば１，４－ブタンジオールジ（メタ）アクリレート、グリセリンジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、グリセリングリシジルエーテルジ（メタ）アクリレート、１，６－ヘキサンジオールジ（メタ）アクリレート、１，９－ノナンジオールジ（メタ）アクリレート、トリシクロデカンジメタクリレート、トリシクロデカンジメタノールジ（メタ）アクリレート、ビスフェノールＡポリエトキシジ（メタ）アクリレート、ビスフェノールＡポリプロポキシジ（メタ）アクリレート、ビスフェノールＦポリエトキシジ（メタ）アクリレート、エチレングリコールジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、トリメチロールプロパントリオキシエチル（メタ）アクリレート、ε－カプロラクトン変性トリス（２－ヒドロキシエチル）イソシアヌレートトリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、プロポキシ化ペンタエリスリトールトリ（メタ）アクリレート、エトキシ化ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、プロポキシ化ペンタエリスリトールテトラ（メタ）アクリレート、エトキシ化ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ポリエチレングリコールジ（メタ）アクリレート、ポリプロピレングリコールジ（メタ）アクリレート、ポリテトラメチレングリコールジ（メタ）アクリレート、（トリス（アクリロキシエチル）イソシアヌレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、トリペンタエリスリトールヘキサ（メタ）アクリレート、トリペンタエリスリトールペンタ（メタ）アクリレート、ヒドロキシビバリン酸ネオペンチルグリコールジ（メタ）アクリレート、ヒドロキシビバリン酸ネオペングリコールのε－カプロラクトン付加物のジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンポリエトキシトリ（メタ）アクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート等の紫外線硬化型の多官能（メタ）アクリル系モノマーの他、ポリエステル（メタ）アクリレート、エポキシ（メタ）アクリレート、ウレタン（メタ）アクリレート、ポリエーテル（メタ）アクリレート等の多官能（メタ）アクリル系オリゴマーを挙げることができる。中でも、プロポキシ化ペンタエリスリトールトリ（メタ）アクリレート、ポリテトラメチレングリコールジ（メタ）アクリレート、が好ましい。これらは１種又は２種以上を組み合わせて使用してもよい。
（単官能（メタ）アクリレート成分（Ｄ））
本発明粘着剤組成物は、さらに、（メタ）アクリロイル基を１つ有する単官能（メタ）アクリレート成分（Ｄ）を含んでいてもよい。単官能（メタ）アクリレート成分を含むことにより、硬化物の架橋点間分子量を大きくすることができるため、分子鎖の運動自由度が増し、本発明粘着シートを介して画像表示装置構成部材を貼り合わせた積層体を高温又は低温環境下で折り曲げた際に、本発明粘着剤組成物からなる本発明粘着シートはそれに追随して変形することができる。
本発明粘着剤組成物は、さらに、（メタ）アクリロイル基を１つ有する単官能（メタ）アクリレート成分（Ｄ）を含んでいてもよい。単官能（メタ）アクリレート成分を含むことにより、硬化物の架橋点間分子量を大きくすることができるため、分子鎖の運動自由度が増し、本発明粘着シートを介して画像表示装置構成部材を貼り合わせた積層体を高温又は低温環境下で折り曲げた際に、本発明粘着剤組成物からなる本発明粘着シートはそれに追随して変形することができる。
単官能（メタ）アクリレート成分（Ｄ）としては、例えばエチル（メタ）アクリレート、プロピル（メタ）アクリレート、イソプロピル（メタ）アクリレート、ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｔ－ブチル（メタ）アクリレート、アミル（メタ）アクリレート、イソアミル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ラウリル（メタ）アクリレート、オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ドデシル（メタ）アクリレート、イソドデシル（メタ）アクリレート、テトラデシル（メタ）アクリレート、ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレート、ベへニル（メタ）アクリレート、シクロプロピル（メタ）アクリレート、シクロブチル（メタ）アクリレート、シクロペンチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、シクロヘプチル（メタ）アクリレート、シクロオクチル（メタ）アクリレート、シクロノニル（メタ）アクリレート、シクロデシル（メタ）アクリレート、イソボルニル（メタ）アクリレート、ノルボルニル（メタ）アクリレート、アダマンチル（メタ）アクリレート、トリシクロデカンジメタノールアクリレート、エトキシ化－ｏ－フェニルフェノールアクリレート、２－ヒドロキシ－ｏ－フェニルフェノールプロピルアクリレート、メトキシポリエチレングリコール（メタ）アクリレート、メトキシポリプロピレングリコール（メタ）アクリレート、ポリエチレングリコール（メタ）アクリレート、ポリプロピレングリコール（メタ）アクリレート、フェノキシエチレングリコール（メタ）アクリレート、フェノキシジエチレングリコール（メタ）アクリレート、フェノキシポリエチレングリコール（メタ）アクリレート、２－ヒドロキシ－ｏ－フェニルフェノールプロピルアクリレート、２－（メタ）アクリロイルオキシエチルコハク酸、２－（メタ）アクリロイルオキシエチルテトラヒドロフタル酸、２－（メタ）アクリロイルオキシエチルヘキサヒドロフタル酸、２－（メタ）アクリロイルオキシプロピルフタル酸、２－（メタ）アクリロイルオキシプロピルヒドロフタル酸、２－（メタ）アクリロイルオキシプロピルヘキサヒドロフタル酸等ベンジル（メタ）アクリレート、ベンジル（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、フェノキシエチレングリコール（メタ）アクリレート、２－ナフチル（メタ）アクリレート、９－アントラセニル（メタ）アクリレート、１－ピレニルメチル（メタ）アクリレート、ベンジル（メタ）アクリレート、トリシクロデカンジメタノールモノアクリレートモノカルボン酸、ジシクロペンタニルアクリレート、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、３－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、トリメチロールプロパンモノ（メタ）アクリレート、グリセリンモノ（メタ）アクリレート、ペンタエリスリトールモノ（メタ）アクリレート、ジグリセリンモノ（メタ）アクリレート、ジトリメチロールプロパンモノ（メタ）アクリレート、ジペンタエリスリトールモノ（メタ）アクリレート、エトキシ化トリメチロールプロパンモノ（メタ）アクリレート、プロポキシ化トリメチロールプロパンモノ（メタ）アクリレート、エトキシ化グリセリンモノ（メタ）アクリレート、プロポキシ化グリセリンモノ（メタ）アクリレート、エトキシ化ペンタエリスリトールモノ（メタ）アクリレート、プロポキシ化ペンタエリスリトールモノ（メタ）アクリレート、エトキシ化ジトリメチロールプロパンモノ（メタ）アクリレート、プロポキシ化ジトリメチロールプロパンモノ（メタ）アクリレート、アルキレンオキサイド変性ジグリセリンモノ（メタ）アクリレート及びアルキレンオキサイド変性ジペンタエリスリトールモノ（メタ）アクリレート等の他、単官能ウレタン（メタ）アクリレート、単官能エポキシ（メタ）アクリレート、単官能ポリエステル（メタ）アクリレート等の単官能オリゴマー類を挙げることができる。これらは１種又は２種以上を組み合わせて使用してもよい。
単官能（メタ）アクリレート成分（Ｄ）を含む場合、多官能（メタ）アクリレート（ｃ１）と単官能（メタ）アクリレート成分（Ｄ）の含有質量比率は、多官能（メタ）アクリレート（ｃ１）：単官能（メタ）アクリレート（Ｄ）＝１：０．１～１：９であるのが好ましく、１：１～１：９であるのがより好ましく、１：２～１：９であるのがさらに好ましい。この範囲にあることで単官能（メタ）アクリレート成分が多すぎず、光に対する感度が落ちて生産性が低下するおそれもない。
（その他の成分）
本発明粘着剤組成物に含まれる前記以外の「その他の成分」として、例えば、必要に応じて、シランカップリング剤や、粘着付与樹脂、可塑剤、酸化防止剤、光安定化剤、金属不活性化剤、老化防止剤、吸湿剤、重合禁止剤、紫外線吸収剤、防錆剤、無機粒子、増感剤、顔料などの各種の添加剤を適宜含有させることが可能である。これら添加剤の量は、典型的には、粘着シートの硬化に悪影響を与えないように、又は、粘着シートの物理的特性に悪影響を与えないように選択するのが好ましい。
また、必要に応じて、三級アミン系化合物、四級アンモニウム系化合物、ラウリル酸スズ化合物などの反応触媒を適宜含有してもよい。
本発明粘着剤組成物に含まれる前記以外の「その他の成分」として、例えば、必要に応じて、シランカップリング剤や、粘着付与樹脂、可塑剤、酸化防止剤、光安定化剤、金属不活性化剤、老化防止剤、吸湿剤、重合禁止剤、紫外線吸収剤、防錆剤、無機粒子、増感剤、顔料などの各種の添加剤を適宜含有させることが可能である。これら添加剤の量は、典型的には、粘着シートの硬化に悪影響を与えないように、又は、粘着シートの物理的特性に悪影響を与えないように選択するのが好ましい。
また、必要に応じて、三級アミン系化合物、四級アンモニウム系化合物、ラウリル酸スズ化合物などの反応触媒を適宜含有してもよい。
＜本発明粘着シートの製造方法＞
次に、本発明粘着シートの製造方法について説明する。ただし、以下の説明は、本発明粘着シートを製造する方法の一例であり、本発明粘着シートはかかる製造方法により製造されるものに限定されるものではない。
次に、本発明粘着シートの製造方法について説明する。ただし、以下の説明は、本発明粘着シートを製造する方法の一例であり、本発明粘着シートはかかる製造方法により製造されるものに限定されるものではない。
本発明粘着シートの作製においては、(メタ)アクリル系重合体（Ａ）のほか、好ましくは、光重合開始剤（Ｂ）、さらに好ましくは架橋剤（Ｃ）、さらに必要に応じて他の成分をそれぞれ所定量混合することにより、本発明粘着剤組成物を調製し、当該粘着剤組成物をシート状に成形し、必要に応じて硬化性化合物を架橋すなわち重合反応させて硬化させて、凹凸パターンを形成して、本発明粘着シートを作製すればよい。ただし、この方法に限定するものではない。
また、本発明粘着剤組成物をシート状に成形して、凹凸パターンを形成した後に硬化させて作製することもできる。
また、本発明粘着剤組成物をシート状に成形して、凹凸パターンを形成した後に硬化させて作製することもできる。
本発明粘着剤組成物を調製する際、上記原料を、温度調節可能な混練機（例えば、一軸押出機、二軸押出機、プラネタリーミキサー、二軸ミキサー、加圧ニーダー等）を用いて混練すればよい。
なお、種々の原料を混合する際、シランカップリング剤、酸化防止剤等の各種添加剤は、予め樹脂とともにブレンドしてから混練機に供給してもよいし、予め全ての材料を溶融混合してから供給してもよいし、添加剤のみを予め樹脂に濃縮したマスターバッチを作製し供給してもよい。
なお、種々の原料を混合する際、シランカップリング剤、酸化防止剤等の各種添加剤は、予め樹脂とともにブレンドしてから混練機に供給してもよいし、予め全ての材料を溶融混合してから供給してもよいし、添加剤のみを予め樹脂に濃縮したマスターバッチを作製し供給してもよい。
本発明粘着剤組成物をシート状に成形する方法としては、公知の方法、例えばウェットラミネーション法、ドライラミネート法、Ｔダイを用いる押出キャスト法、押出ラミネート法、カレンダー法やインフレーション法、射出成型、注液硬化法等を採用することができる。中でも、シートを製造する場合は、ウェットラミネーション法、押出キャスト法、押出ラミネート法が好適である。
（硬化方法）
シート状に成形された本発明粘着剤組成物若しくは粘着シートを硬化する場合、その硬化方法としては、熱および／又は活性エネルギー線を照射して硬化させることにより硬化物とする方法を挙げることができる。
例えば、シート状に成形された本発明粘着剤組成物若しくは粘着シートに対して、熱および／又は活性エネルギー線を照射することにより硬化させることができる。
シート状に成形された本発明粘着剤組成物若しくは粘着シートを硬化する場合、その硬化方法としては、熱および／又は活性エネルギー線を照射して硬化させることにより硬化物とする方法を挙げることができる。
例えば、シート状に成形された本発明粘着剤組成物若しくは粘着シートに対して、熱および／又は活性エネルギー線を照射することにより硬化させることができる。
ここで、照射する活性エネルギー線としては、α線、β線、γ線、中性子線、電子線などの電離性放射線、紫外線、可視光線などを挙げることができ、中でも光学装置構成部材へのダメージ抑制や反応制御の観点から紫外線が好適である。
また、活性エネルギー線の照射エネルギー、照射時間、照射方法などに関しては特に限定されず、開始剤を活性化させて（メタ）アクリレート成分を重合できればよい。
また、活性エネルギー線の照射エネルギー、照射時間、照射方法などに関しては特に限定されず、開始剤を活性化させて（メタ）アクリレート成分を重合できればよい。
（他の製造方法）
また、本発明粘着シートを形成するための粘着シートの別の実施態様として、本発明粘着剤組成物を適切な溶剤に溶解させ、各種コーティング手法を用いて実施することもできる。
コーティング手法を用いた場合、上記の活性エネルギー線照射硬化の他、熱硬化させることにより粘着シートを得ることもできる。
また、本発明粘着シートを形成するための粘着シートの別の実施態様として、本発明粘着剤組成物を適切な溶剤に溶解させ、各種コーティング手法を用いて実施することもできる。
コーティング手法を用いた場合、上記の活性エネルギー線照射硬化の他、熱硬化させることにより粘着シートを得ることもできる。
コーティングの場合、粘着シートの厚みは塗工厚みと塗工液の固形分濃度によって調整できる。
（凹凸パターンの形成方法）
前記凹凸パターン４は、粘着シートの粘着面に金型の凹凸面を押圧して、金型の凹凸構造を粘着シートの粘着面に転写することにより、形成することができる。そして、凹凸パターンが形成された本発明粘着シートが得られる。
前記凹凸パターン４は、粘着シートの粘着面に金型の凹凸面を押圧して、金型の凹凸構造を粘着シートの粘着面に転写することにより、形成することができる。そして、凹凸パターンが形成された本発明粘着シートが得られる。
前記金型は、平板状のものであっても、円柱状、円筒状のものであってもよい。
前記金型の材質は、金属、樹脂、ガラスなど任意である。
前記金型の材質は、金属、樹脂、ガラスなど任意である。
粘着シートの粘着面に金型の凹凸面を押圧する際、その圧力は０．００００１～１ＭＰａとするのが好ましく、中でも０．００００５ＭＰａ以上或いは０．９ＭＰａ以下、その中でも０．０００１ＭＰａ以上或いは０．８ＭＰａ以下とするのがさらに好ましい。
また、粘着シートの粘着面に金型の凹凸面を押圧した状態で１～５００秒の間静置するのが好ましく、中でも２秒以上或いは４００秒以下、その中でも３秒以上或いは３００秒以下の間静置するのがさらに好ましい。
また、粘着シートの粘着面に金型の凹凸面を押圧した状態で１～５００秒の間静置するのが好ましく、中でも２秒以上或いは４００秒以下、その中でも３秒以上或いは３００秒以下の間静置するのがさらに好ましい。
粘着シートの粘着面に金型の凹凸面を押圧する際、必要に応じて、金型を加熱するようにしてもよい。この際、加熱温度は、２０～１００℃とするのが好ましく、中でも３０℃以上或いは９０℃以下、その中でも４０℃以上或いは８０℃以下とするのがより好ましい。
＜本発明粘着シートの層構成＞
本発明粘着シートは、本発明粘着剤組成物からなる粘着剤層（「本発明粘着剤層」とも称する）からなる単層構成であっても、本発明粘着剤層を備えた２層以上の複数層構成であってもよい。
本発明粘着シートが２層以上の複数層構成である場合、本発明粘着剤層以外の層の組成は任意である。ただし、例えば中間層や最表層或いは最裏層を本発明粘着剤層以外の層で形成する場合、層間接着性をより高める観点から、本発明粘着剤層以外の層を形成する粘着剤組成物も、（メタ）アクリル系重合体を含む粘着剤組成物から形成するのが好ましく、中でも、本発明粘着剤層と同じ（メタ）アクリル系重合体（Ａ）を含むのがより好ましい。さらには、本発明粘着剤層以外の層も、光重合開始剤（Ｂ）および／又は架橋剤（Ｃ）を含むのがより好ましい。
本発明粘着シートは、本発明粘着剤組成物からなる粘着剤層（「本発明粘着剤層」とも称する）からなる単層構成であっても、本発明粘着剤層を備えた２層以上の複数層構成であってもよい。
本発明粘着シートが２層以上の複数層構成である場合、本発明粘着剤層以外の層の組成は任意である。ただし、例えば中間層や最表層或いは最裏層を本発明粘着剤層以外の層で形成する場合、層間接着性をより高める観点から、本発明粘着剤層以外の層を形成する粘着剤組成物も、（メタ）アクリル系重合体を含む粘着剤組成物から形成するのが好ましく、中でも、本発明粘着剤層と同じ（メタ）アクリル系重合体（Ａ）を含むのがより好ましい。さらには、本発明粘着剤層以外の層も、光重合開始剤（Ｂ）および／又は架橋剤（Ｃ）を含むのがより好ましい。
本発明粘着シートが２層以上の複数層構成である場合、少なくとも、最表層、最裏層又はその両層が本発明粘着剤層に該当する層であるのが好ましい。全ての層が本発明粘着剤層に該当する層であってもよい。
本発明粘着シートが２層以上の複数層構成である場合、本発明粘着剤層に該当する層の厚みが、本発明粘着シート全体の厚みに対して１０％以上１００％以下を占めるのが好ましく、中でも１４％以上或いは７０％以下、その中でも２０％以上或いは５０％以下の割合で占めるのがさらに好ましい。
＜粘着シートの粘弾性＞
本発明粘着シートは、凹凸形状を維持する観点から、周波数１Ｈｚ、温度２３℃における貯蔵弾性率が、１×１０３～１×１０６Ｐａであることが好ましく、中でも１×１０３Ｐａ以上或いは０．５×１０６Ｐａ以下、その中でも１×１０４Ｐａ以上或いは１×１０５Ｐａ以下であることが好ましい。
なお、前記貯蔵弾性率は、例えば、レオメトリックス社製の粘弾性測定装置「ダイナミックアナライザー ＲＤＡＩＩ」を用いて剪断法により、次の条件で測定することができる。但し、この測定方法に限定するものではない。
・治具：Φ２５ｍｍパラレルプレート
・歪み：０．５％
・周波数：１Ｈｚ
・温度：－７０～２００℃（－７０℃から昇温速度３℃／ｍｉｎで測定）
・試料厚さ：５００μｍ
なお、測定する粘着シートの厚みが５００μｍに満たない場合は、それぞれ５００μｍの厚さになるまで粘着剤層を積層することで調整することができる。
本発明粘着シートは、凹凸形状を維持する観点から、周波数１Ｈｚ、温度２３℃における貯蔵弾性率が、１×１０３～１×１０６Ｐａであることが好ましく、中でも１×１０３Ｐａ以上或いは０．５×１０６Ｐａ以下、その中でも１×１０４Ｐａ以上或いは１×１０５Ｐａ以下であることが好ましい。
なお、前記貯蔵弾性率は、例えば、レオメトリックス社製の粘弾性測定装置「ダイナミックアナライザー ＲＤＡＩＩ」を用いて剪断法により、次の条件で測定することができる。但し、この測定方法に限定するものではない。
・治具：Φ２５ｍｍパラレルプレート
・歪み：０．５％
・周波数：１Ｈｚ
・温度：－７０～２００℃（－７０℃から昇温速度３℃／ｍｉｎで測定）
・試料厚さ：５００μｍ
なお、測定する粘着シートの厚みが５００μｍに満たない場合は、それぞれ５００μｍの厚さになるまで粘着剤層を積層することで調整することができる。
＜接着性＞
本発明粘着シートは、フレキシブル画像表示装置用構成部材の代替部材としてのポリエチレンテレフタレートシートに対する９０℃剥離による粘着力（剥離速度３００ｍｍ／ｍｉｎ）を０．５～３０Ｎ／２０ｍｍとすることができる。かかる粘着力は伸縮時の剥れにくさの点から０．５Ｎ／２０ｍｍ以上、更には１．０Ｎ／２０ｍｍ以上、特には１．５Ｎ／２０ｍｍ以上、殊には２．０Ｎ／２０ｍｍ以上が好ましく、一方、形状保持性の点から３０Ｎ／２０ｍｍ以下、更には２８Ｎ／２０ｍｍ以下、特には２５Ｎ／２０ｍｍ以下が好ましい。
この際、前記フレキシブル画像表示装置用構成部材の代替部材としてのポリエチレンテレフタレートシートは、２軸延伸シートであるのが好ましい。また、その厚みは５０～３００μｍであるのが好ましい。
本発明粘着シートは、フレキシブル画像表示装置用構成部材の代替部材としてのポリエチレンテレフタレートシートに対する９０℃剥離による粘着力（剥離速度３００ｍｍ／ｍｉｎ）を０．５～３０Ｎ／２０ｍｍとすることができる。かかる粘着力は伸縮時の剥れにくさの点から０．５Ｎ／２０ｍｍ以上、更には１．０Ｎ／２０ｍｍ以上、特には１．５Ｎ／２０ｍｍ以上、殊には２．０Ｎ／２０ｍｍ以上が好ましく、一方、形状保持性の点から３０Ｎ／２０ｍｍ以下、更には２８Ｎ／２０ｍｍ以下、特には２５Ｎ／２０ｍｍ以下が好ましい。
この際、前記フレキシブル画像表示装置用構成部材の代替部材としてのポリエチレンテレフタレートシートは、２軸延伸シートであるのが好ましい。また、その厚みは５０～３００μｍであるのが好ましい。
＜本発明離型フィルム＞
本発明離型フィルムの材質としては、例えばポリエステルフィルム、ポリオレフィンフィルム、ポリカーボネートフィルム、ポリスチレンフィルム、アクリルフィルム、トリアセチルセルロースフィルム、フッ素樹脂フィルム等を挙げることができる。これらの中でも、ポリエステルフィルム及びポリオレフィンフィルムが特に好ましい。
本発明離型フィルムの材質としては、例えばポリエステルフィルム、ポリオレフィンフィルム、ポリカーボネートフィルム、ポリスチレンフィルム、アクリルフィルム、トリアセチルセルロースフィルム、フッ素樹脂フィルム等を挙げることができる。これらの中でも、ポリエステルフィルム及びポリオレフィンフィルムが特に好ましい。
本発明離型フィルムの表面、特に本発明粘着シートを貼り合わせる側の表面は平坦面であるのが好ましい。
本発明離型フィルムの厚みは、特に制限するものではない。中でも、例えば加工性及びハンドリング性の観点からは、２５μｍ～５００μｍであるのが好ましく、その中でも３８μｍ以上或いは２５０μｍ以下、その中でも５０μｍ以上或いは２００μｍ以下であるのがさらに好ましい。
本発明離型フィルム付き粘着シートは、本発明離型フィルムがポリエステル系フィルムであることが好ましく、また、活性エネルギー線を照射した後にも剥離し易いものであるものが離型性の点から好ましい。かかる観点から、波長３６５ｎｍの活性エネルギー線を積算光量２０００～４０００ｍＪ／ｃｍ２照射した時の本発明粘着シートに対する剥離力が、剥離角１８０°、剥離速度３００ｍｍ／分において、０．１Ｎ／ｃｍ以下となるものであることが好ましい。
＜＜本発明フレキシブル積層体＞＞
本発明の実施形態の一例であるフレキシブル画像表示装置用積層体（「本発明フレキシブル積層体」と称する）は、本発明粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたものである。
なお、本発明フレキシブル積層体における本発明粘着シートは、硬化前の状態、硬化後の状態、及び、硬化途中の状態すなわち未だ硬化される余地のある状態に硬化された状態のいずれも包含する。
本発明の実施形態の一例であるフレキシブル画像表示装置用積層体（「本発明フレキシブル積層体」と称する）は、本発明粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたものである。
なお、本発明フレキシブル積層体における本発明粘着シートは、硬化前の状態、硬化後の状態、及び、硬化途中の状態すなわち未だ硬化される余地のある状態に硬化された状態のいずれも包含する。
前述のように、本発明離型フィルム付き粘着シートにおいて、本発明離型フィルムと本発明粘着シートとの間に所定の空隙率（Ｘ）を有する空間部が形成されていれば、本発明離型フィルムを剥離した本発明粘着シートを、表面平坦なフレキシブル画像表示装置用構成部材に貼着して本発明フレキシブル積層体を形成した場合にも、本発明粘着シートとフレキシブル画像表示装置用構成部材との間に同様の空隙率（Ｘ）を有する空間部を形成することができ、本発明フレキシブル積層体を巻き取り、巻き戻して広げた時に、本発明粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができる。また、本発明フレキシブル積層体伸縮させた場合も、本発明粘着シートとフレキシブル画像表示装置用構成部材との間の“剥がれ”が生じるのを防ぐことができる。
よって、本発明フレキシブル積層体において、フレキシブル画像表示装置用構成部材と本発明粘着シートとの間に形成された空間部の空隙率（Ｘ）は３％以上、更に４％以上であるのが好ましく、中でも４．５％以上、５％以上、６％以上、中でも８％以上、その中でも１０％以上であるのがさらに好ましい。他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
特に、伸縮させた場合（ストレッチャブル性を目的とする場合）は、空間部の空隙率（Ｘ）は４％以上が好ましく、中でも４．５％以上、５％以上、６％以上、特には８％以上、その中でも１０％以上であり、他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
よって、本発明フレキシブル積層体において、フレキシブル画像表示装置用構成部材と本発明粘着シートとの間に形成された空間部の空隙率（Ｘ）は３％以上、更に４％以上であるのが好ましく、中でも４．５％以上、５％以上、６％以上、中でも８％以上、その中でも１０％以上であるのがさらに好ましい。他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
特に、伸縮させた場合（ストレッチャブル性を目的とする場合）は、空間部の空隙率（Ｘ）は４％以上が好ましく、中でも４．５％以上、５％以上、６％以上、特には８％以上、その中でも１０％以上であり、他方、７０％以下であるのがより好ましく、中でも６０％以下、５０％以下、４８％以下、中でも４５％以下、その中でも４０％以下であるのがさらに好ましい。
本発明フレキシブル積層体の一例として、２つのフレキシブル画像表示装置用構成部材が、本発明粘着シートからなる硬化性を有する粘着層を介して積層してなる構成を備えたフレキシブル画像表示装置用積層体を挙げることができる。
本発明フレキシブル積層体の他例として、２つのフレキシブル画像表示装置用構成部材が、本発明粘着シートが硬化されてなる粘着層を介して積層してなる構成を備えたフレキシブル画像表示装置用積層体を挙げることができる。
具体的な例としては、フレキシブル積層体は、第１のフレキシブル画像表示装置構成用部材（以下「第１の部材」と称することがある）と、本発明粘着シートと、第２のフレキシブル画像表示装置構成用部材（以下「第２の部材」と称することがある）とが、この順で積層されてなる構成を備えた積層体であるのが好ましい。
さらに、第１の部材、第２の部材及び第３のフレキシブル画像表示装置構成用部材（以下「第３の部材」と称することがある）とが、それぞれ本発明粘着シートを介してこの順で積層されてなる構成を備えた積層体であってもよい。積層する２以上の部材は同じでもよいし、異なるものでもよい。
さらに、第１の部材、第２の部材及び第３のフレキシブル画像表示装置構成用部材（以下「第３の部材」と称することがある）とが、それぞれ本発明粘着シートを介してこの順で積層されてなる構成を備えた積層体であってもよい。積層する２以上の部材は同じでもよいし、異なるものでもよい。
本発明フレキシブル積層体の厚みは、特に制限されるものではない。例えば、画像表示装置に使用される場合の一例としては、本発明フレキシブル積層体はシート状であり、その厚みが０．０２ｍｍ以上であれば、ハンドリング性が良好であり、また、厚みが１．０ｍｍ以下であれば、積層体の薄型化に寄与することができる。
よって、本発明フレキシブル積層体の厚みは、０．０２ｍｍ以上であるのが好ましく、中でも０．０３ｍｍ以上、特に０．０５ｍｍ以上であるのがより好ましい。一方、上限に関しては、１．０ｍｍ以下であるのが好ましく、中でも０．７ｍｍ以下、特に０．５ｍｍ以下であるのがさらに好ましい。
よって、本発明フレキシブル積層体の厚みは、０．０２ｍｍ以上であるのが好ましく、中でも０．０３ｍｍ以上、特に０．０５ｍｍ以上であるのがより好ましい。一方、上限に関しては、１．０ｍｍ以下であるのが好ましく、中でも０．７ｍｍ以下、特に０．５ｍｍ以下であるのがさらに好ましい。
本発明粘着シートを、第１の部材、第２の部材及び／又は第３の部材に貼着することにより、本発明フレキシブル積層体を作製することができる。ただし、このような製造方法に限定するものではない。
（フレキシブル画像表示装置構成部材）
フレキシブル画像表示装置の構成や本発明粘着シートの位置にも依るが、第１の部材、第２の部材及び第３の部材（これらをまとめて「本部材」と称する場合がある）としては、例えばカバーレンズ、偏光板、位相差フィルム、バリアフィルム、タッチセンサーフィルム、発光素子、ＰＳＡ等を挙げることができる。
フレキシブル画像表示装置の構成や本発明粘着シートの位置にも依るが、第１の部材、第２の部材及び第３の部材（これらをまとめて「本部材」と称する場合がある）としては、例えばカバーレンズ、偏光板、位相差フィルム、バリアフィルム、タッチセンサーフィルム、発光素子、ＰＳＡ等を挙げることができる。
フレキシブル画像表示装置構成部材の一例として、ローラブル部材、すなわち、巻き取り、巻き戻しが可能な部材や、ストレッチャブル部材、すなわち、伸縮可能な部材を挙げることができる。具体的には、例えば反射シート、導光板と光源、拡散フィルム、プリズムシート、液晶パネル、位相差板、ガラス基板、偏光板、有機ＥＬパネル、電極、反射防止フィルム、カラーフィルター、タッチセンサー、カバーガラス、カバープラスチック、又は、これらのうちの２種類以上の部材が複合一体化されたものや、表面保護フィルムなどを挙げることができる。なお、前記部材以外にも、帯電防止層やハードコート層、アンカー層、離型層、易接着層、保護層、ブリーディング防止層及び平坦化層等、必要に応じて他の層を介在していてもよい。
また、画像表示の構成を考慮すると、第１の部材は、タッチ入力機能を有することが好ましい。本発明粘着シートが前述した第２の部材、第３の部材を有する場合、第２の部材乃至第３の部材がタッチ入力機能を有していてもよい。
また、本部材のうちの少なくとも一つは、本発明粘着シートとの接触面に、配線、印刷、パターン現像や表面処理、エンボス加工等により種々の凹凸が賦形されていてもよい。
また、本部材のうちの少なくとも一つは、本発明粘着シートとの接触面に、配線、印刷、パターン現像や表面処理、エンボス加工等により種々の凹凸が賦形されていてもよい。
貼り合わせるフレキシブル画像表示装置構成用部材（第１の部材、第２の部材及び第３の部材を包含する）のうちの少なくとも一つは、ウレタン樹脂、シクロオレフィン樹脂、トリアセチルセルロース樹脂、（メタ）アクリレート樹脂、エポキシ樹脂及びポリイミド樹脂からなる群から選択される一種若しくは二種以上の樹脂を主成分とする樹脂シート又は薄膜ガラスであってもよい。
ここで「主成分」とは、フレキシブル画像表示装置構成用部材を構成する成分のうち最も多い質量比率を占める成分であることをいい、具体的には、フレキシブル画像表示装置構成用部材の５０質量％以上を占めるもの、中でも５５質量％以上を占めるもの、中でも６０質量％以上を占めるのを想定することができる。
ここで「主成分」とは、フレキシブル画像表示装置構成用部材を構成する成分のうち最も多い質量比率を占める成分であることをいい、具体的には、フレキシブル画像表示装置構成用部材の５０質量％以上を占めるもの、中でも５５質量％以上を占めるもの、中でも６０質量％以上を占めるのを想定することができる。
本発明粘着シートは、活性エネルギー線による硬化後においてホットメルトすることも可能である。かかるホットメルトにより、被着体の被着面に凹凸を有する場合であっても、該凹凸に追随しかつ凹凸を吸収するように貼合することができ、その表面を平滑にすることもできる。そのため、２つのフレキシブル画像表示装置構成用部材を、本発明粘着シートを介して貼合する際、一方又は両方のフレキシブル画像表示装置構成用部材が光を透過しない部材であっても、該凹凸を吸収しつつ２つのフレキシブル画像表示装置構成用部材を貼合することができる。
（本発明フレキシブル積層体の製造方法）
本発明フレキシブル積層体は、例えば、凹凸パターン形成時に活性エネルギー線を照射して硬化してなる本発明粘着シートの一方を、フレキシブル画像表示装置構成用部材１に貼合し、次に、本発明粘着シートの他方の表面にフレキシブル画像表示装置構成用部材２を貼合して積層体とすることが挙げられる。
また、本発明フレキシブル積層体は、例えば、フレキシブル画像表示装置構成用部材１に、本発明粘着シートの一方の表面を貼合し、活性エネルギー線を照射して本発明粘着シートを硬化させ、次に、硬化後の本発明粘着シートの他方の表面にフレキシブル画像表示装置構成用部材２を貼合して積層体とすることができる。
また、本発明フレキシブル積層体は、例えば、フレキシブル画像表示装置構成用部材１に、本発明粘着シートの一方の表面を貼合し、本発明粘着シートの他方の表面にフレキシブル画像表示装置構成用部材２を貼合して積層体とした後、一方のフレキシブル画像表示装置構成用部材を通して、活性エネルギー線を照射して本発明粘着シートを硬化させることもできる。
本発明フレキシブル積層体は、例えば、凹凸パターン形成時に活性エネルギー線を照射して硬化してなる本発明粘着シートの一方を、フレキシブル画像表示装置構成用部材１に貼合し、次に、本発明粘着シートの他方の表面にフレキシブル画像表示装置構成用部材２を貼合して積層体とすることが挙げられる。
また、本発明フレキシブル積層体は、例えば、フレキシブル画像表示装置構成用部材１に、本発明粘着シートの一方の表面を貼合し、活性エネルギー線を照射して本発明粘着シートを硬化させ、次に、硬化後の本発明粘着シートの他方の表面にフレキシブル画像表示装置構成用部材２を貼合して積層体とすることができる。
また、本発明フレキシブル積層体は、例えば、フレキシブル画像表示装置構成用部材１に、本発明粘着シートの一方の表面を貼合し、本発明粘着シートの他方の表面にフレキシブル画像表示装置構成用部材２を貼合して積層体とした後、一方のフレキシブル画像表示装置構成用部材を通して、活性エネルギー線を照射して本発明粘着シートを硬化させることもできる。
本発明粘着シートの貼合方法としては、ロール貼合、平行平板によるプレス貼合、ダイヤフラム貼合等の既知の方式を用いることができる。
貼合環境としては、常圧で貼り合わせる大気貼合方式と、減圧下で貼り合わせる真空貼合方式がある。貼合時の気泡を防止する観点からは、減圧環境下で平行平板にて貼合する方法が好ましい。また、貼合温度を適宜調整してもよい。
貼合環境としては、常圧で貼り合わせる大気貼合方式と、減圧下で貼り合わせる真空貼合方式がある。貼合時の気泡を防止する観点からは、減圧環境下で平行平板にて貼合する方法が好ましい。また、貼合温度を適宜調整してもよい。
本発明粘着シートを貼合する際、必要に応じて、本発明粘着シート、又は画像表示装置構成用部材１又は画像表示装置構成用部材２を加熱するようにしてもよい。
この際の加熱は、例えば、画像表示装置構成用部材１／本発明粘着シート／画像表示装置構成用部材２からなる画像表示装置用積層体を、両側から、所定温度に加熱されたプレス板で加圧する方法などを挙げることができる。
また、この際の加熱温度は、温度５０℃以上８０℃以下であるのが好ましい。すなわち、５０℃以上８０℃以下に画像表示装置構成用部材１及び／又は画像表示装置構成用部材２を加熱して前記粘着シートをホットメルトさせながら、画像表示装置構成用部材２を貼合するのが好ましい。
また、プレス板で加圧する際のプレス圧は、０．０１ＭＰａ以上或いは０．４ＭＰａ以下、その中でも０．０２ＭＰａ以上或いは０．３５ＭＰａ以下であるのがさらに好ましい。
この際の加熱は、例えば、画像表示装置構成用部材１／本発明粘着シート／画像表示装置構成用部材２からなる画像表示装置用積層体を、両側から、所定温度に加熱されたプレス板で加圧する方法などを挙げることができる。
また、この際の加熱温度は、温度５０℃以上８０℃以下であるのが好ましい。すなわち、５０℃以上８０℃以下に画像表示装置構成用部材１及び／又は画像表示装置構成用部材２を加熱して前記粘着シートをホットメルトさせながら、画像表示装置構成用部材２を貼合するのが好ましい。
また、プレス板で加圧する際のプレス圧は、０．０１ＭＰａ以上或いは０．４ＭＰａ以下、その中でも０．０２ＭＰａ以上或いは０．３５ＭＰａ以下であるのがさらに好ましい。
活性エネルギー線を照射して本発明粘着シートを製造する際、活性エネルギー線としては、紫外線及び可視光線が好適である。
活性エネルギー線を照射する際の光源については、例えば高圧水銀ランプ、メタルハライドランプ、キセノンランプ、ハロゲンランプ、ＬＥＤランプ、蛍光ランプなどの中から、照射する光の波長や照射量に応じて使い分けることができる。
照射時間や照射手段に関しては特に限定されないが、例えば紫外線照射であれば、波長３６５ｎｍにおける積算光量が１０００ｍＪ／ｃｍ２以上、更に２０００ｍＪ／ｃｍ２以上、特に３０００ｍＪ／ｃｍ２以上となるように照射するのが好ましい。なお、積算光量の上限は通常１００００ｍＪ／ｃｍ２である。
活性エネルギー線を照射する際の光源については、例えば高圧水銀ランプ、メタルハライドランプ、キセノンランプ、ハロゲンランプ、ＬＥＤランプ、蛍光ランプなどの中から、照射する光の波長や照射量に応じて使い分けることができる。
照射時間や照射手段に関しては特に限定されないが、例えば紫外線照射であれば、波長３６５ｎｍにおける積算光量が１０００ｍＪ／ｃｍ２以上、更に２０００ｍＪ／ｃｍ２以上、特に３０００ｍＪ／ｃｍ２以上となるように照射するのが好ましい。なお、積算光量の上限は通常１００００ｍＪ／ｃｍ２である。
（巻き取り）
本発明フレキシブル積層体は、例えば図１に示すように、巻き芯などに巻き付けて巻き取り、その後、巻き戻して広げたときに、本発明粘着シートの巻き長差分による歪みに由来する応力を緩和することができ、粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができる。よって、本発明フレキシブル積層体は、フレキシブル性に優れ、更にはローラブル性にも優れたものである。
なお、本発明粘着シートにおいて、凹凸形状の凸部が片方に形成されている場合、凸部を外向きに巻き取っても内向きに巻き取っても同様の効果が得られる。
本発明フレキシブル積層体は、例えば図１に示すように、巻き芯などに巻き付けて巻き取り、その後、巻き戻して広げたときに、本発明粘着シートの巻き長差分による歪みに由来する応力を緩和することができ、粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができる。よって、本発明フレキシブル積層体は、フレキシブル性に優れ、更にはローラブル性にも優れたものである。
なお、本発明粘着シートにおいて、凹凸形状の凸部が片方に形成されている場合、凸部を外向きに巻き取っても内向きに巻き取っても同様の効果が得られる。
本発明フレキシブル積層体の巻き取り径ｃ、すなわち、巻芯５０の直径は５～５００ｍｍであるのが好ましい。
当該巻き取り径ｃが５ｍｍ以上であれば、巻き取った際に生じる歪をより一層緩和することができ、５００ｍｍ以下であれば、ハンドリング性に優れる。
かかる観点から、本発明フレキシブル積層体の巻き取り径ｃは６ｍｍ以上であるのがより好ましく、７ｍｍ以上であるのがさらに好ましく、１０ｍｍ以上であるのが特に好ましい。他方、４５０ｍｍ以下であるのがより好ましく、４００ｍｍ以下であるのがさらに好ましく、３５０ｍｍ以下であるのが特に好ましい。
当該巻き取り径ｃが５ｍｍ以上であれば、巻き取った際に生じる歪をより一層緩和することができ、５００ｍｍ以下であれば、ハンドリング性に優れる。
かかる観点から、本発明フレキシブル積層体の巻き取り径ｃは６ｍｍ以上であるのがより好ましく、７ｍｍ以上であるのがさらに好ましく、１０ｍｍ以上であるのが特に好ましい。他方、４５０ｍｍ以下であるのがより好ましく、４００ｍｍ以下であるのがさらに好ましく、３５０ｍｍ以下であるのが特に好ましい。
＜本フレキシブル画像表示装置＞
本発明フレキシブル積層体を組み込むことで、例えば本発明フレキシブル積層体を他の画像表示装置構成部材に積層することで、本発明フレキシブル積層体を備えたフレキシブル画像表示装置（「本フレキシブル画像表示装置」とも称する）を形成することができる。
フレキシブル画像表示装置とは、繰り返し折り曲げや湾曲操作、巻き取り操作をしても曲げ跡を残さず、折り曲げ状態や湾曲状態、巻き取り状態を解放した際には折り曲げや湾曲操作、巻き取り操作をする前の状態まで素早く回復することができ、歪みなく画像を表示できる画像表示装置をいう。とりわけ、本発明においては、ローラブル用に好適なフレキシブル画像表示装置を得ることができる。
また、本発明においては、伸ばしたり、縮めたり等の伸縮操作が繰り返し行われても画像表示装置構成部材の剥がれ等が生じることのない、ストレッチャブル用にも好適なフレキシブル画像表示装置を得ることができる。
本発明フレキシブル積層体を組み込むことで、例えば本発明フレキシブル積層体を他の画像表示装置構成部材に積層することで、本発明フレキシブル積層体を備えたフレキシブル画像表示装置（「本フレキシブル画像表示装置」とも称する）を形成することができる。
フレキシブル画像表示装置とは、繰り返し折り曲げや湾曲操作、巻き取り操作をしても曲げ跡を残さず、折り曲げ状態や湾曲状態、巻き取り状態を解放した際には折り曲げや湾曲操作、巻き取り操作をする前の状態まで素早く回復することができ、歪みなく画像を表示できる画像表示装置をいう。とりわけ、本発明においては、ローラブル用に好適なフレキシブル画像表示装置を得ることができる。
また、本発明においては、伸ばしたり、縮めたり等の伸縮操作が繰り返し行われても画像表示装置構成部材の剥がれ等が生じることのない、ストレッチャブル用にも好適なフレキシブル画像表示装置を得ることができる。
本フレキシブル画像表示装置においては、液晶パネルなどの画像表示パネルの視認側に本発明粘着シートを配置することもできるし、また、画像表示パネルの視認側とは反対側、すなわち光源側に配置することもできる。
＜＜用語の説明＞＞
本発明においては、「フィルム」と称する場合でも「シート」を含むものとし、「シート」と称する場合でも「フィルム」を含むものとする。
また、画像表示パネル、保護パネル等のように「パネル」と表現する場合、板体、シート及びフィルムを包含するものである。
本発明においては、「フィルム」と称する場合でも「シート」を含むものとし、「シート」と称する場合でも「フィルム」を含むものとする。
また、画像表示パネル、保護パネル等のように「パネル」と表現する場合、板体、シート及びフィルムを包含するものである。
本発明において、「Ｘ～Ｙ」（Ｘ，Ｙは任意の数字）と記載した場合、特にことわらない限り「Ｘ以上Ｙ以下」の意と共に、「好ましくはＸより大きい」或いは「好ましくはＹより小さい」の意も包含するものである。
また、「Ｘ以上」（Ｘは任意の数字）と記載した場合、特にことわらない限り「好ましくはＸより大きい」の意を包含し、「Ｙ以下」（Ｙは任意の数字）と記載した場合、特にことわらない限り「好ましくはＹより小さい」の意も包含するものである。
さらに、「Ｘ及び／又はＹ（Ｘ，Ｙは任意の構成）」とは、Ｘ及びＹの少なくとも一方を意味するものであって、Ｘのみ、Ｙのみ、Ｘ及びＹ、の３通りを意味するものである。
また、「Ｘ以上」（Ｘは任意の数字）と記載した場合、特にことわらない限り「好ましくはＸより大きい」の意を包含し、「Ｙ以下」（Ｙは任意の数字）と記載した場合、特にことわらない限り「好ましくはＹより小さい」の意も包含するものである。
さらに、「Ｘ及び／又はＹ（Ｘ，Ｙは任意の構成）」とは、Ｘ及びＹの少なくとも一方を意味するものであって、Ｘのみ、Ｙのみ、Ｘ及びＹ、の３通りを意味するものである。
本発明において、「（メタ）アクリル」とは、「アクリル」及び「メタクリル」を、「（メタ）アクリレート」とは、「アクリレート」及び「メタクリレート」を、「（メタ）アクリロイル」とは、「アクリロイル」及び「メタクリロイル」を、それぞれ包括する意味である。
また、「アクリル系重合体」とは、（メタ）アクリレート由来の単量体単位を含むものを意味し、（メタ）アクリル系共重合体を包含する意味である。
また、「アクリル系重合体」とは、（メタ）アクリレート由来の単量体単位を含むものを意味し、（メタ）アクリル系共重合体を包含する意味である。
以下、実施例を挙げて本発明をさらに具体的に説明するが、本発明はその要旨を超えない限り以下の実施例に限定されるものではない。
なお、下記において「部」、「％」とあるのは、質量基準を意味する。
なお、下記において「部」、「％」とあるのは、質量基準を意味する。
＜粘着シートの原料＞
次の原料を使用して粘着シートを作製した。
次の原料を使用して粘着シートを作製した。
（（メタ）アクリル系重合体（Ａ））
・（メタ）アクリル系重合体（Ａ－１）：数平均分子量２８００のポリメタクリル酸メチルマクロモノマー（Ｔｇ１０５℃）６質量部と、ブチルアクリレート（Ｔｇ－５５℃）９０質量部と、アクリル酸（Ｔｇ１０６℃）４質量部とが共重合してなるアクリル系グラフト共重合体（質量平均分子量：２２万、Ｔｇ－４５℃）
・（メタ）アクリル系重合体（Ａ－２）：数平均分子量２８００のポリメタクリル酸メチルマクロモノマー（Ｔｇ１０５℃）１５質量部と、ブチルアクリレート（Ｔｇ－５５℃）８１質量部と、アクリル酸（１０６℃）４質量部とが共重合してなるアクリル系グラフト共重合体（質量平均分子量：１６万、Ｔｇ－３６℃）
・（メタ）アクリル系重合体（Ａ－１）：数平均分子量２８００のポリメタクリル酸メチルマクロモノマー（Ｔｇ１０５℃）６質量部と、ブチルアクリレート（Ｔｇ－５５℃）９０質量部と、アクリル酸（Ｔｇ１０６℃）４質量部とが共重合してなるアクリル系グラフト共重合体（質量平均分子量：２２万、Ｔｇ－４５℃）
・（メタ）アクリル系重合体（Ａ－２）：数平均分子量２８００のポリメタクリル酸メチルマクロモノマー（Ｔｇ１０５℃）１５質量部と、ブチルアクリレート（Ｔｇ－５５℃）８１質量部と、アクリル酸（１０６℃）４質量部とが共重合してなるアクリル系グラフト共重合体（質量平均分子量：１６万、Ｔｇ－３６℃）
（光重合開始剤（Ｂ））
・開始剤（Ｂ－１）：２，４，６－トリメチルベンゾフェノン及び４－メチルベンゾフェノンの混合物（ＩＧＭ社製「Ｅｓａｃｕｒｅ ＴＺＴ」）
・開始剤（Ｂ－１）：２，４，６－トリメチルベンゾフェノン及び４－メチルベンゾフェノンの混合物（ＩＧＭ社製「Ｅｓａｃｕｒｅ ＴＺＴ」）
（架橋剤（Ｃ））
・開始剤（Ｃ－１）：プロポキシ化ペンタエリスリトールトリアクリレート
・開始剤（Ｃ－１）：プロポキシ化ペンタエリスリトールトリアクリレート
（その他）
・防錆剤：１，２，３－ベンゾトリアゾール
・防錆剤：１，２，３－ベンゾトリアゾール
＜離型フィルム付き粘着シート１の作製＞
（メタ）アクリル系重合体（Ａ－２）１００質量部、開始剤（Ｂ－１）２．５質量部、架橋剤（Ｃ－１）３質量部、防錆剤０．５質量部を混合し、粘着剤組成物を得た。
次に、得られた粘着剤組成物を１００℃に加熱してホットメルトし、シリコーン離型処理された１００μｍの離型フィルム（三菱ケミカル社製ＰＥＴフィルム、厚さ１００μｍ）と、シリコーン離型処理された７５μｍの離型フィルム（三菱ケミカル社製ＰＥＴフィルム、厚さ７５μｍ）、すなわち２枚の離型フィルムの間に挟んで、厚さ５０μｍのシート状に成形し、離型フィルム／粘着シート／離型フィルムからなる離型フィルム付き粘着シート１（凹凸パターン形成前）を得た。
なお、粘着シート１は、光を照射することにより硬化する活性エネルギー線硬化性を備えた粘着シートであった。
（メタ）アクリル系重合体（Ａ－２）１００質量部、開始剤（Ｂ－１）２．５質量部、架橋剤（Ｃ－１）３質量部、防錆剤０．５質量部を混合し、粘着剤組成物を得た。
次に、得られた粘着剤組成物を１００℃に加熱してホットメルトし、シリコーン離型処理された１００μｍの離型フィルム（三菱ケミカル社製ＰＥＴフィルム、厚さ１００μｍ）と、シリコーン離型処理された７５μｍの離型フィルム（三菱ケミカル社製ＰＥＴフィルム、厚さ７５μｍ）、すなわち２枚の離型フィルムの間に挟んで、厚さ５０μｍのシート状に成形し、離型フィルム／粘着シート／離型フィルムからなる離型フィルム付き粘着シート１（凹凸パターン形成前）を得た。
なお、粘着シート１は、光を照射することにより硬化する活性エネルギー線硬化性を備えた粘着シートであった。
＜離型フィルム付き粘着シート２の作製＞
（メタ）アクリル系重合体（Ａ－１）１００質量部、開始剤（Ｂ－１）２．５質量部、架橋剤（Ｃ－１）３質量部、防錆剤０．５質量部を混合して粘着剤組成物を得た以外は、前記離型フィルム付き粘着シート１と同様にして離型フィルム付き粘着シート２（凹凸パターン形成前）を作製した。
（メタ）アクリル系重合体（Ａ－１）１００質量部、開始剤（Ｂ－１）２．５質量部、架橋剤（Ｃ－１）３質量部、防錆剤０．５質量部を混合して粘着剤組成物を得た以外は、前記離型フィルム付き粘着シート１と同様にして離型フィルム付き粘着シート２（凹凸パターン形成前）を作製した。
＜凹凸付き金型Ｘ、及び、凹凸付き金型Ｙの作製＞
精密平板加工機に、被削材に銅めっきを使用した平板金型を取り付け、先端５０ｍｍＲの単結晶ダイヤモンドバイトを用いて鏡面加工を行った。次に、先端に２００μｍフラット部を有する挟み角３０°の単結晶ダイヤモンドバイトを用いて、送りピッチ３００μｍで切込み量５０μｍの溝加工を行うことで、図６に示すように、底幅２００μｍ、深さ５０μｍの台形状の複数の溝が、７４μｍの間隔をおいてピッチ３００μｍで繰り返し形成されてなる凹凸構造を金型表面に有する凹凸付き金型Ｘを得た。
次いで、無電解ニッケルめっき処理を行い、凹凸表面に１．０μｍ厚みの無電解ニッケルめっきを有する凹凸付き金型Ｙを得た。
精密平板加工機に、被削材に銅めっきを使用した平板金型を取り付け、先端５０ｍｍＲの単結晶ダイヤモンドバイトを用いて鏡面加工を行った。次に、先端に２００μｍフラット部を有する挟み角３０°の単結晶ダイヤモンドバイトを用いて、送りピッチ３００μｍで切込み量５０μｍの溝加工を行うことで、図６に示すように、底幅２００μｍ、深さ５０μｍの台形状の複数の溝が、７４μｍの間隔をおいてピッチ３００μｍで繰り返し形成されてなる凹凸構造を金型表面に有する凹凸付き金型Ｘを得た。
次いで、無電解ニッケルめっき処理を行い、凹凸表面に１．０μｍ厚みの無電解ニッケルめっきを有する凹凸付き金型Ｙを得た。
＜実施例１＞
図７に示すように、離型フィルム付き粘着シート１の一方の離型フィルム１２を剥離した貼着面に、金型Ｘの凹凸側を積層し、金型Ｘとは反対側の離型フィルム１２表面をローラーで貼合した後、当該離型フィルム１２表面にガラス板を載せて、金型温度２３℃、圧力０．００１ＭＰａで荷重（Ｐ）を掛けた状態で３０分静置した。次いで、ＵＶランプ（Ｆｕｓｉｏｎ社製、Ｈバルブ）を用いて、金型Ｘの反対側から離型フィルム１２を通して粘着シート１０に対して、２００～５００ｎｍ波長の光を積算光量４０００ｍＪ／ｃｍ２露光して粘着シート１０を硬化させた。露光後に、金型Ｘを離し、更に離型フィルム１３を積層することで、凹凸パターン形成された離型フィルム付き粘着シート１（本発明粘着シート）を得た。
図７に示すように、離型フィルム付き粘着シート１の一方の離型フィルム１２を剥離した貼着面に、金型Ｘの凹凸側を積層し、金型Ｘとは反対側の離型フィルム１２表面をローラーで貼合した後、当該離型フィルム１２表面にガラス板を載せて、金型温度２３℃、圧力０．００１ＭＰａで荷重（Ｐ）を掛けた状態で３０分静置した。次いで、ＵＶランプ（Ｆｕｓｉｏｎ社製、Ｈバルブ）を用いて、金型Ｘの反対側から離型フィルム１２を通して粘着シート１０に対して、２００～５００ｎｍ波長の光を積算光量４０００ｍＪ／ｃｍ２露光して粘着シート１０を硬化させた。露光後に、金型Ｘを離し、更に離型フィルム１３を積層することで、凹凸パターン形成された離型フィルム付き粘着シート１（本発明粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート１（本発明粘着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表１に記載の通りの形状を有するものであった。
＜実施例２＞
実施例１において、離型フィルム付き粘着シート２を用いて、金型温度２３℃、圧力０．００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例１と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート２（本発明粘着シート）を得た。
実施例１において、離型フィルム付き粘着シート２を用いて、金型温度２３℃、圧力０．００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例１と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート２（本発明粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート２（本発明粘着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた断面台形状の凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表１に記載の通りの形状を有するものであった。
＜実施例３＞
実施例２において、金型温度６０℃、圧力０．００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例２と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート３（本発明粘着シート）を得た。
実施例２において、金型温度６０℃、圧力０．００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例２と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート３（本発明粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート３（本粘接着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた断面台形状の凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表１に記載の通りの形状を有するものであった。
＜実施例４＞
実施例２において、金型温度２３℃、圧力０．００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例２と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート４（本発明粘着シート）を得た。
実施例２において、金型温度２３℃、圧力０．００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例２と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート４（本発明粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート４（本発明粘着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた断面台形状の凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表１に記載の通りの形状を有するものであった。
＜実施例５＞
実施例２において、金型温度２３℃、圧力０．００５ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例２と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート５（本発明粘着シート）を得た。
実施例２において、金型温度２３℃、圧力０．００５ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例２と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート５（本発明粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート５（本発明粘着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた断面台形状の凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表１に記載の通りの形状を有するものであった。
＜比較例１＞
離型フィルム付き粘着シート１をそのまま、比較例１の粘着シート１’（比較粘着シート）とした。
離型フィルム付き粘着シート１をそのまま、比較例１の粘着シート１’（比較粘着シート）とした。
＜比較例２＞
離型フィルム付き粘着シート１を用いて、金型温度２３℃、圧力０．００００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例１と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート２’（比較粘着シート）を得た。
離型フィルム付き粘着シート１を用いて、金型温度２３℃、圧力０．００００１ＭＰａで荷重を掛けた状態で３０分静置した以外は、実施例１と同様にして、凹凸パターンが形成された離型フィルム付き粘着シート２’（比較粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート２’（比較粘着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた断面台形状の凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表１に記載の通りの形状を有するものであった。
＜測定方法及び評価方法＞
実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）の各種物性値の測定方法及び評価方法について説明する。
実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）の各種物性値の測定方法及び評価方法について説明する。
＜凹凸パターン各部の測定＞
実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）のＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面を、レーザー顕微鏡（ＬＥＸＴ、オリンパス社製）を用いて観察し、粘着面に形成された凹凸パターンの各形状を測定した。測定結果は表１の通りであった。
実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）のＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面を、レーザー顕微鏡（ＬＥＸＴ、オリンパス社製）を用いて観察し、粘着面に形成された凹凸パターンの各形状を測定した。測定結果は表１の通りであった。
＜離型フィルム付き粘着シートの空間部の空隙率の測定＞
上記で得られた凹凸パターンが形成された離型フィルム付き粘着シートに関し、粘着シートの凹凸パターンが形成された粘着面と、離型フィルムとの間に存在する空間部の空隙率を次のように測定した。測定結果は表１の通りであった。
凹凸構造を有する本発明離型フィルム付き粘着シートの表面を、離型フィルム越しに、光学顕微鏡（キーエンス社製、マイクロスコープＶＨＸ－６００）を用いて、凸部の幅（ｗ２、ｗ３、ｗ４）を測定した。また、本発明離型フィルム付き粘着シートを厚さ方向に切断し、断面における凹凸の高さ（ｈ）及び粘着シート厚み（Ｈ）を、光学顕微鏡を用いて測定した。得られた結果より（（ｗ３＋（ｗ２－ｗ４））×ｈ÷２）／（ｗ２×Ｈ）より空隙率（％）を測定した。
上記で得られた凹凸パターンが形成された離型フィルム付き粘着シートに関し、粘着シートの凹凸パターンが形成された粘着面と、離型フィルムとの間に存在する空間部の空隙率を次のように測定した。測定結果は表１の通りであった。
凹凸構造を有する本発明離型フィルム付き粘着シートの表面を、離型フィルム越しに、光学顕微鏡（キーエンス社製、マイクロスコープＶＨＸ－６００）を用いて、凸部の幅（ｗ２、ｗ３、ｗ４）を測定した。また、本発明離型フィルム付き粘着シートを厚さ方向に切断し、断面における凹凸の高さ（ｈ）及び粘着シート厚み（Ｈ）を、光学顕微鏡を用いて測定した。得られた結果より（（ｗ３＋（ｗ２－ｗ４））×ｈ÷２）／（ｗ２×Ｈ）より空隙率（％）を測定した。
＜ＰＥＴフィルム基材に貼り合わせた際に形成される空間部の空隙率の測定＞
フレキシブル画像表示装置用構成部材の代替材料としてのＰＥＴフィルム基材に、粘着シートを貼り合わせた際に、粘着シートの凹凸パターンが形成された粘着面と、ＰＥＴフィルム基材との間に存在する空間部の空隙率を、上記の空隙率測定方法に準じて測定した結果、いずれの実施例・比較例においても、粘着シートの凹凸パターンが形成された粘着面と、離型フィルムとの間に存在する空間部の空隙率と同じ値であった。
フレキシブル画像表示装置用構成部材の代替材料としてのＰＥＴフィルム基材に、粘着シートを貼り合わせた際に、粘着シートの凹凸パターンが形成された粘着面と、ＰＥＴフィルム基材との間に存在する空間部の空隙率を、上記の空隙率測定方法に準じて測定した結果、いずれの実施例・比較例においても、粘着シートの凹凸パターンが形成された粘着面と、離型フィルムとの間に存在する空間部の空隙率と同じ値であった。
＜粘着力＞
図１０に示すように、実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）を幅２０ｍｍ×長さ１００ｍｍにカットし、凹凸パターンが形成された粘着剤表面側の離型フィルム１３を剥がした後、粘着剤表面を、２軸延伸フィルムであるＰＥＴフィルム基材１１（ダイアホイル、三菱ケミカル社製、「Ｔ９１３Ｅ１２５Ｃ」厚み１２５μｍ）にローラーで貼り付けて、離型フィルム１２／粘着シート１０／ＰＥＴフィルム基材１１の層構成の積層体とした。なお、粘着シートを貼り合わる際、意図的に加熱及び加圧はしていない。
そして、粘着シート１０とＰＥＴフィルム基材１１との界面において、ＪＩＳ Ｚ ０２３７：２０００に準じて、剥離速度３００ｍｍ／ｍｉｎで９０度剥離試験を行い、粘着力（Ｎ／２０ｍｍ）を測定した。
図１０に示すように、実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）を幅２０ｍｍ×長さ１００ｍｍにカットし、凹凸パターンが形成された粘着剤表面側の離型フィルム１３を剥がした後、粘着剤表面を、２軸延伸フィルムであるＰＥＴフィルム基材１１（ダイアホイル、三菱ケミカル社製、「Ｔ９１３Ｅ１２５Ｃ」厚み１２５μｍ）にローラーで貼り付けて、離型フィルム１２／粘着シート１０／ＰＥＴフィルム基材１１の層構成の積層体とした。なお、粘着シートを貼り合わる際、意図的に加熱及び加圧はしていない。
そして、粘着シート１０とＰＥＴフィルム基材１１との界面において、ＪＩＳ Ｚ ０２３７：２０００に準じて、剥離速度３００ｍｍ／ｍｉｎで９０度剥離試験を行い、粘着力（Ｎ／２０ｍｍ）を測定した。
＜ローラブル性の評価＞
図１０に示すように、実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）の凹凸パターンが形成された粘着剤表面側の離型フィルム１３を剥がした後、粘着剤表面を、２軸延伸フィルムであるＰＥＴフィルム基材１１（ダイアホイル、三菱ケミカル社製、「Ｔ９１３Ｅ１２５Ｃ」厚み１２５μｍ）にローラーで貼り付けて、離型フィルム１２／粘着シート１０／ＰＥＴフィルム基材１１の層構成の積層体とした。なお、粘着シートを貼り合わる際、意図的に加熱及び加圧はしていない。
かかる積層体を８０ｍｍ×１００ｍｍサイズにカットし、直径１０ｍｍの丸棒に巻き付けた。この際、実施例１～２、４～５及び比較例１～２は、粘着シート１０の外側にＰＥＴフィルム基材１１が来るように巻き付ける一方、実施例３は、粘着シートの内側にＰＥＴフィルム基材が来るように巻き付けた。
そして、巻き付け状態を１０秒間保持した後、巻き戻して展開し、外観を目視観察し、以下の基準で評価した。
○・・・ＰＥＴフィルム基材に浮きは見られなかった。
×・・・ＰＥＴフィルム基材に浮きが発生していた。
図１０に示すように、実施例の粘着シート１～５（本発明粘着シート）及び比較例の粘着シート１’～２’（比較粘着シート）の凹凸パターンが形成された粘着剤表面側の離型フィルム１３を剥がした後、粘着剤表面を、２軸延伸フィルムであるＰＥＴフィルム基材１１（ダイアホイル、三菱ケミカル社製、「Ｔ９１３Ｅ１２５Ｃ」厚み１２５μｍ）にローラーで貼り付けて、離型フィルム１２／粘着シート１０／ＰＥＴフィルム基材１１の層構成の積層体とした。なお、粘着シートを貼り合わる際、意図的に加熱及び加圧はしていない。
かかる積層体を８０ｍｍ×１００ｍｍサイズにカットし、直径１０ｍｍの丸棒に巻き付けた。この際、実施例１～２、４～５及び比較例１～２は、粘着シート１０の外側にＰＥＴフィルム基材１１が来るように巻き付ける一方、実施例３は、粘着シートの内側にＰＥＴフィルム基材が来るように巻き付けた。
そして、巻き付け状態を１０秒間保持した後、巻き戻して展開し、外観を目視観察し、以下の基準で評価した。
○・・・ＰＥＴフィルム基材に浮きは見られなかった。
×・・・ＰＥＴフィルム基材に浮きが発生していた。
なお、ＰＥＴフィルム基材を、画像表示装置用構成部材、中でもフレキシブル画像表示装置用構成部材の代替部材として使用して、各種評価を行うこととしたが、本発明の特徴が粘着シートの凹凸形状にあることから、基材や部材が多少異なっても、適切な評価が得られるものであると認識される。
上記実施例・比較例の結果、並びに、これまで本発明者が行ってきた試験結果から、粘着シートの少なくとも表裏一側の粘着面に、離型フィルムで挟持された際に形成される空間部の空隙率が所定範囲にあれば、粘着シートの当該粘着面にフレキシブル画像表示装置用構成部材を積層した状態で巻き取り、巻き戻して広げたときに、粘着シートとフレキシブル画像表示装置用構成部材との間に“浮き”が生じるのを防ぐことができることが分かった。
前記のように積層状態のまま、巻き取り、その後、巻き戻して展開したときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離して“浮き”が発生する原因は、粘着シートの厚みｂに対する、巻き取った際に生じる粘着シート１０の内側単位円周長（内側巻き長）Ｌ１と外側単位円周長（外側巻き長）Ｌ２との巻き長差（ΔＬ）の比率すなわち巻き長分（ΔＬ／ｂ）による歪のためであると考えられる。そこで、フレキシブル画像表示装置用構成部材を積層する側の粘着面に、所定の凸部の高さを有する凹凸パターンを形成した結果、巻き取った際に生じる巻き長分による歪を緩和することができ、浮きが生じるのを防ぐことができたと推察される。
前記のように積層状態のまま、巻き取り、その後、巻き戻して展開したときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離して“浮き”が発生する原因は、粘着シートの厚みｂに対する、巻き取った際に生じる粘着シート１０の内側単位円周長（内側巻き長）Ｌ１と外側単位円周長（外側巻き長）Ｌ２との巻き長差（ΔＬ）の比率すなわち巻き長分（ΔＬ／ｂ）による歪のためであると考えられる。そこで、フレキシブル画像表示装置用構成部材を積層する側の粘着面に、所定の凸部の高さを有する凹凸パターンを形成した結果、巻き取った際に生じる巻き長分による歪を緩和することができ、浮きが生じるのを防ぐことができたと推察される。
＜実施例６＞
図７に示すように、離型フィルム付き粘着シート２（凹凸パターン形成前）の一方の離型フィルム１２を剥離した貼着面に、金型Ｙの凹凸側を積層し、金型Ｙとは反対側の離型フィルム１２表面をローラーで貼合した後、当該離型フィルム１２表面にガラス板を載せて、金型温度２３℃、圧力０．０１ＭＰａで荷重（Ｐ）を掛けた状態で３０分静置した。次いで、ＵＶランプ（Ｆｕｓｉｏｎ社製、Ｈバルブ）を用いて、金型Ｙの反対側から離型フィルム１２を通して粘着シート１０に対して、２００～５００ｎｍ波長の光を積算光量４０００ｍＪ／ｃｍ２露光して粘着シート１０を硬化させた。露光後に、金型Ｙを離し、更に離型フィルム１３を積層することで、凹凸パターンが形成された離型フィルム付き粘着シート６（本発明粘着シート）を得た。
図７に示すように、離型フィルム付き粘着シート２（凹凸パターン形成前）の一方の離型フィルム１２を剥離した貼着面に、金型Ｙの凹凸側を積層し、金型Ｙとは反対側の離型フィルム１２表面をローラーで貼合した後、当該離型フィルム１２表面にガラス板を載せて、金型温度２３℃、圧力０．０１ＭＰａで荷重（Ｐ）を掛けた状態で３０分静置した。次いで、ＵＶランプ（Ｆｕｓｉｏｎ社製、Ｈバルブ）を用いて、金型Ｙの反対側から離型フィルム１２を通して粘着シート１０に対して、２００～５００ｎｍ波長の光を積算光量４０００ｍＪ／ｃｍ２露光して粘着シート１０を硬化させた。露光後に、金型Ｙを離し、更に離型フィルム１３を積層することで、凹凸パターンが形成された離型フィルム付き粘着シート６（本発明粘着シート）を得た。
得られた凹凸パターンが形成された離型フィルム付き粘着シート６（本発明粘着シート）には、フィルム幅方向すなわちＴＤ方向に伸びた凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表２に記載の通りの形状を有するものであった。
＜参考例１＞
図７に示すように、離型フィルム付き粘着シート２（凹凸パターン形成前）の一方の離型フィルム１２を剥離した貼着面に、金型Ｙの凹凸側を積層し、金型Ｙとは反対側の離型フィルム１２表面をローラーで貼合した後、当該離型フィルム１２表面にガラス板を載せて、金型温度２３℃、圧力０．０１ＭＰａで荷重（Ｐ）を掛けた状態で３０分静置した。次いで、ＵＶランプ（Ｆｕｓｉｏｎ社製、Ｈバルブ）を用いて、金型Ｙの反対側から離型フィルム１２を通して粘着シート１０に対して、２００～５００ｎｍ波長の光を積算光量４０００ｍＪ／ｃｍ２露光して粘着シート１０を硬化させた。露光後に、金型Ｙを離し、更に離型フィルム１３を積層することで、凹凸パターンが形成された離型フィルム付き粘着シート３’（比較粘着シート）を得た。
図７に示すように、離型フィルム付き粘着シート２（凹凸パターン形成前）の一方の離型フィルム１２を剥離した貼着面に、金型Ｙの凹凸側を積層し、金型Ｙとは反対側の離型フィルム１２表面をローラーで貼合した後、当該離型フィルム１２表面にガラス板を載せて、金型温度２３℃、圧力０．０１ＭＰａで荷重（Ｐ）を掛けた状態で３０分静置した。次いで、ＵＶランプ（Ｆｕｓｉｏｎ社製、Ｈバルブ）を用いて、金型Ｙの反対側から離型フィルム１２を通して粘着シート１０に対して、２００～５００ｎｍ波長の光を積算光量４０００ｍＪ／ｃｍ２露光して粘着シート１０を硬化させた。露光後に、金型Ｙを離し、更に離型フィルム１３を積層することで、凹凸パターンが形成された離型フィルム付き粘着シート３’（比較粘着シート）を得た。
得られた凹凸パターン形成された離型フィルム付き粘着シート３’（比較粘着シート）の粘着面には、フィルム幅方向すなわちＴＤ方向に伸びた凸状部からなる凹凸単位が、フィルム長さ方向すなわちＭＤ方向に適宜間隔を置いて繰り返し形成されてなる凹凸パターンが形成された。当該凹凸パターンは、図９に示すように、本発明粘着シートをＭＤ方向、すなわち巻き周方向とする方向に沿って肉厚方向に切断した縦断面において、表２に記載の通りの形状を有するものであった。
＜測定方法及び評価方法＞
実施例の粘着シート６（本発明粘着シート）及び参考例の粘着シート３’（比較粘着シート）の各種物性値の測定方法及び評価方法について説明する。
実施例の粘着シート６（本発明粘着シート）及び参考例の粘着シート３’（比較粘着シート）の各種物性値の測定方法及び評価方法について説明する。
＜凹凸パターン各部の測定＞
上記と同様の方法により、粘着面に形成された凹凸パターンの各形状を測定した。測定結果は表２の通りであった。
上記と同様の方法により、粘着面に形成された凹凸パターンの各形状を測定した。測定結果は表２の通りであった。
＜離型フィルム付き粘着シートの空間部の空隙率の測定＞
上記で得られた離型フィルム付き粘着シートに関し、上記と同様の方法により、粘着シート１０の凹凸パターンが形成された粘着面と、離型フィルム１３との間に存在する空間部の空隙率を測定した。測定結果は表２の通りであった。
上記で得られた離型フィルム付き粘着シートに関し、上記と同様の方法により、粘着シート１０の凹凸パターンが形成された粘着面と、離型フィルム１３との間に存在する空間部の空隙率を測定した。測定結果は表２の通りであった。
＜ＰＥＴフィルム基材に貼り合わせた際に形成される空間部の空隙率の測定＞
フレキシブル画像表示装置用構成部材の代替材料としてのＰＥＴフィルム基材１１に、粘着シート１０を貼り合わせた際に、粘着シート１０の凹凸パターンが形成された粘着面と、ＰＥＴフィルム基材１１との間に存在する空間部の空隙率を上記と同様の方法により測定した結果、いずれの実施例及び参考例においても、粘着シート１０の凹凸パターンが形成された粘着面と、離型フィルム１３との間に存在する空間部の空隙率と同じ値であった。
フレキシブル画像表示装置用構成部材の代替材料としてのＰＥＴフィルム基材１１に、粘着シート１０を貼り合わせた際に、粘着シート１０の凹凸パターンが形成された粘着面と、ＰＥＴフィルム基材１１との間に存在する空間部の空隙率を上記と同様の方法により測定した結果、いずれの実施例及び参考例においても、粘着シート１０の凹凸パターンが形成された粘着面と、離型フィルム１３との間に存在する空間部の空隙率と同じ値であった。
＜粘着力＞
上記と同様の方法により、粘着力（Ｎ／２０ｍｍ）を測定した。測定結果は表２の通りであった。
上記と同様の方法により、粘着力（Ｎ／２０ｍｍ）を測定した。測定結果は表２の通りであった。
＜ストレッチャブル性の評価＞
図１０に示すように、実施例の粘着シート６（本発明粘着シート）及び参考例の粘着シート３’（比較粘着シート）の凹凸パターンが形成された粘着剤表面側の離型フィルム１３を剥がした後、粘着剤表面を、２軸延伸フィルムであるＰＥＴフィルム基材１１（ダイアホイル、三菱ケミカル社製、「Ｔ９１３Ｅ１２５Ｃ」厚み１２５μｍ）にローラーで貼り付けて、離型フィルム１２／粘着シート１０／ＰＥＴフィルム基材１３の層構成の積層体とした。なお、粘着シート１０を貼り合わる際、意図的に加熱及び加圧はしていない。
かかる積層体を２０ｍｍ×１００ｍｍサイズにカットし、引張試験機を用いて５ｍｍ／ｍｉｎの速度で５０％の一軸引張を行った。
そして、引張試験後の外観を目視観察し、以下の基準で評価した。
○・・・ＰＥＴフィルム基材に剥がれが見られなかった。
×・・・ＰＥＴフィルム基材に剥がれが発生していた。
図１０に示すように、実施例の粘着シート６（本発明粘着シート）及び参考例の粘着シート３’（比較粘着シート）の凹凸パターンが形成された粘着剤表面側の離型フィルム１３を剥がした後、粘着剤表面を、２軸延伸フィルムであるＰＥＴフィルム基材１１（ダイアホイル、三菱ケミカル社製、「Ｔ９１３Ｅ１２５Ｃ」厚み１２５μｍ）にローラーで貼り付けて、離型フィルム１２／粘着シート１０／ＰＥＴフィルム基材１３の層構成の積層体とした。なお、粘着シート１０を貼り合わる際、意図的に加熱及び加圧はしていない。
かかる積層体を２０ｍｍ×１００ｍｍサイズにカットし、引張試験機を用いて５ｍｍ／ｍｉｎの速度で５０％の一軸引張を行った。
そして、引張試験後の外観を目視観察し、以下の基準で評価した。
○・・・ＰＥＴフィルム基材に剥がれが見られなかった。
×・・・ＰＥＴフィルム基材に剥がれが発生していた。
なお、ＰＥＴフィルム基材を、画像表示装置用構成部材、中でもフレキシブル画像表示装置用構成部材の代替部材として使用して、各種評価を行うこととしたが、本発明の特徴が粘着シートの凹凸形状にあることから、基材や部材が多少異なっても、適切な評価が得られるものであると認識される。
上記実施例、比較例及び参考例の結果、並びに、これまで本発明者が行ってきた試験結果から、粘着シートの少なくとも表裏一側の粘着面に、離型フィルムで挟持された際に形成される空間部の空隙率が所定範囲にあれば、粘着シートの当該粘着面にフレキシブル画像表示装置用構成部材を積層した状態で伸ばしたり、縮めたりしたときに、粘着シートとフレキシブル画像表示装置用構成部材との間に“剥がれ”が生じるのを防ぐことができることが分かった。
前記のように積層状態のまま、伸縮したときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離するなどの原因は、引張応力が生じた際に応力分散ができずフィルム端部よりフィルムの剥がれが生じたものであると考えられる。そこで、所定の空間部の空隙率を調整することにより、伸縮しても剥がれが生じるのを防ぐことができる粘着シートとなると推察される。
前記のように積層状態のまま、伸縮したときに、粘着シートとフレキシブル画像表示装置用構成部材とが一部剥離するなどの原因は、引張応力が生じた際に応力分散ができずフィルム端部よりフィルムの剥がれが生じたものであると考えられる。そこで、所定の空間部の空隙率を調整することにより、伸縮しても剥がれが生じるのを防ぐことができる粘着シートとなると推察される。
本発明の粘着シートは、フレキシブル性、特にローラブル性、ストレッチャブル性に優れた粘着シートであり、例えば、有機発光ダイオード（ＯＬＥＤ）や量子ドット（ＱＤ）を用いたフレキシブル画像表示装置などに有用である。
１ 粘着シート
２ 粘着面
３ 凹凸単位
３Ａ 凸部
３Ｂ 凹部
４ 凹凸パターン
１０ 粘着シート
１１ ＰＥＴフィルム基材
１２ 離型フィルム
１３ 離型フィルム
２０ フレキシブル画像表示装置用構成部材
３０ フレキシブル画像表示装置用構成部材
５０ 巻芯
Ｘ，Ｙ 金型
Ｐ 荷重
２ 粘着面
３ 凹凸単位
３Ａ 凸部
３Ｂ 凹部
４ 凹凸パターン
１０ 粘着シート
１１ ＰＥＴフィルム基材
１２ 離型フィルム
１３ 離型フィルム
２０ フレキシブル画像表示装置用構成部材
３０ フレキシブル画像表示装置用構成部材
５０ 巻芯
Ｘ，Ｙ 金型
Ｐ 荷重
Claims (22)
- 離型フィルムと粘着シートを備えた離型フィルム付き粘着シートであって、
離型フィルムと粘着シートとの間に空間部を有し、当該空間部の空隙率（Ｘ）が３～７０％である離型フィルム付き粘着シート。 - 前記粘着シートの少なくとも表裏一側の粘着面に、凸部を有する凹凸単位が少なくとも１つ設けられてなる凹凸パターンを備える、請求項１に記載の離型フィルム付き粘着シート。
- 前記凹凸単位における凸部の高さ（α）が７～１００μｍである、請求項２に記載の離型フィルム付き粘着シート。
- 前記凹凸単位を構成する凸部の最大幅（ｗ１）が１～１０００μｍである、請求項２又は３に記載の離型フィルム付き粘着シート。
- 粘着シートの厚み（ｂ）に対する、前記凸部の高さ（α）の比率（α／ｂ）が０．０１以上１未満である、請求項２～４の何れか一項に記載の離型フィルム付き粘着シート。
- 前記凹凸単位が繰り返される凹凸パターンを備えるものであり、前記凹凸単位の繰り返しピッチ（ｗ２）が２～１０００μｍである、請求項２～５の何れか一項に記載の離型フィルム付き粘着シート。
- 前記凹凸単位を構成する凸部と隣接する凸部との間隔（ｗ３）が１～１０００μｍである、請求項２～６の何れか一項に記載の離型フィルム付き粘着シート。
- 前記凹凸単位における凸部の頂面は平坦面であり、前記凸部頂面幅（ｗ４）が１～１０００μｍである、請求項２～７の何れか一項に記載の離型フィルム付き粘着シート。
- 前記凹凸単位を構成する凸部の最大幅（ｗ１）に対する、凸部の高さ（α）の比率（α／ｗ１）が０．０３～０．３である、請求項２～８の何れか一項に記載の離型フィルム付き粘着シート。
- ポリエチレンテレフタレートシートに対する９０℃剥離による粘着力（剥離速度３００ｍｍ／ｍｉｎ）が０．５～３０Ｎ／２０ｍｍである、請求項１～９の何れか一項に記載の離型フィルム付き粘着シート。
- 粘着シートの厚み（ｂ）が１０～１００μｍである、請求項１～１０の何れか一項に記載の離型フィルム付き粘着シート。
- 前記粘着シートが、（メタ）アクリル系重合体（Ａ）及び光重合開始剤（Ｂ）を含有する光硬化性粘着剤組成物から形成される粘着シートである、請求項１～１１の何れか一項に記載の離型フィルム付き粘着シート。
- 光硬化性粘着剤組成物が架橋剤（Ｃ）を含有する、請求項１２に記載の離型フィルム付き粘着シート。
- フレキシブル画像表示装置用構成部材を貼り合わせるために用いられる、請求項１～１３の何れか一項に記載の離型フィルム付き粘着シート。
- 前記フレキシブル画像表示装置用構成部材がローラブル部材である、請求項１４に記載の離型フィルム付き粘着シート。
- 前記フレキシブル画像表示装置用構成部材がストレッチャブル部材である、請求項１４に記載の離型フィルム付き粘着シート。
- 請求項１～１６の何れか一項に記載の離型フィルム付き粘着シートの粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたフレキシブル画像表示装置用積層体。
- 請求項１～１６の何れか一項に記載の離型フィルム付き粘着シートの粘着シートが硬化してなる硬化後粘着シートと、フレキシブル画像表示装置用構成部材とが積層してなる構成を備えたフレキシブル画像表示装置用積層体。
- フレキシブル画像表示装置用構成部材と粘着シートとが積層してなる構成を備えたフレキシブル画像表示装置用積層体であって、
フレキシブル画像表示装置用構成部材と粘着シートとの間に形成された空間部の空隙率（Ｘ）が３～７０％であるフレキシブル画像表示装置用積層体。 - 前記粘着シートは、請求項１～１６の何れか一項に記載の離型フィルム付き粘着シートの粘着シートである、請求項１９に記載のフレキシブル画像表示装置用積層体。
- 請求項１７～２０の何れか一項に記載のフレキシブル画像表示装置用積層体を備えたフレキシブル画像表示装置。
- フレキシブル画像表示装置用構成部材を貼り合わせるために使用する粘着シートであって、
前記粘着シートの少なくとも表裏一側の粘着面に、凸部を有する凹凸単位が少なくとも１つ設けられてなる凹凸パターンを備え、
前記凹凸単位における凸部の高さ（α）が７～１００μｍであり、
前記凹凸単位を構成する凸部の最大幅（ｗ１）が１～１０００μｍである粘着シート。