WO2022272139A1 - Nouvelle stratégie de dopage pour matériaux d'électrode d'oxyde en couches utilisés dans des batteries au lithium-ion - Google Patents
Nouvelle stratégie de dopage pour matériaux d'électrode d'oxyde en couches utilisés dans des batteries au lithium-ion Download PDFInfo
- Publication number
- WO2022272139A1 WO2022272139A1 PCT/US2022/035007 US2022035007W WO2022272139A1 WO 2022272139 A1 WO2022272139 A1 WO 2022272139A1 US 2022035007 W US2022035007 W US 2022035007W WO 2022272139 A1 WO2022272139 A1 WO 2022272139A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- salt
- composition
- hydroxide precursor
- ranges
- solution
- Prior art date
Abstract
La présente invention concerne une nouvelle manière de doper des matériaux de cathode en couches dans des batteries au lithium-ion. À l'aide d'une stratégie de dopage "à entropie élevée" ou "cocktail'', plus de quatre éléments d'impureté peuvent être introduits dans les matériaux hôtes. La présente invention applique cette stratégie de dopage à entropie élevée à un matériau d'oxyde en couches à haute teneur en nickel et à un matériau riche en lithium-manganèse. Cette nouvelle stratégie de dopage à entropie élevée permet aux matériaux d'oxyde en couches utilisés dans l'électrode positive d'une batterie au lithium-ion d'avoir une densité d'énergie élevée, un cycle de longue durée de vie et une dépendance réduite au cobalt onéreux et toxique, tous ceux-ci étant des attributs souhaités pour améliorer la performance des batteries au lithium-ion et réduire leur coût.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP22829440.1A EP4358830A1 (fr) | 2021-06-25 | 2022-06-24 | Nouvelle stratégie de dopage pour matériaux d'électrode d'oxyde en couches utilisés dans des batteries au lithium-ion |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US17/358,460 US20220336802A1 (en) | 2020-06-25 | 2021-06-25 | New doping strategy for layered oxide electrode materials used in lithium-ion batteries |
US17/358,460 | 2021-06-25 | ||
US17/508,540 | 2021-10-22 | ||
US17/508,540 US11728482B2 (en) | 2020-06-25 | 2021-10-22 | Doping strategy for layered oxide electrode materials used in lithium-ion batteries |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2022272139A1 true WO2022272139A1 (fr) | 2022-12-29 |
WO2022272139A9 WO2022272139A9 (fr) | 2023-03-09 |
Family
ID=84544705
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2022/035007 WO2022272139A1 (fr) | 2021-06-25 | 2022-06-24 | Nouvelle stratégie de dopage pour matériaux d'électrode d'oxyde en couches utilisés dans des batteries au lithium-ion |
Country Status (2)
Country | Link |
---|---|
EP (1) | EP4358830A1 (fr) |
WO (1) | WO2022272139A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN117154086A (zh) * | 2023-07-28 | 2023-12-01 | 南京大学 | 一种Fe/Mg掺杂调控的层状富锂正极材料、制备方法以及锂离子电池 |
CN117832477A (zh) * | 2024-03-05 | 2024-04-05 | 宁德时代新能源科技股份有限公司 | 正极活性材料、二次电池和用电装置 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20170112427A1 (en) * | 2014-05-30 | 2017-04-27 | Adam J. Simon | Multimodal health assessment with neuro-opthalmological saccade tests |
US20190113973A1 (en) * | 2012-09-14 | 2019-04-18 | Interaxon Inc | Systems and methods for collecting, analyzing, and sharing bio-signal and non-bio-signal data |
WO2020047253A1 (fr) * | 2018-08-31 | 2020-03-05 | Blackthorn Therapeutics, Inc. | Biomarqueurs multimodaux prédictifs de la gravité d'un symptôme transdiagnostique |
WO2021081418A1 (fr) * | 2019-10-25 | 2021-04-29 | Ellipsis Health, Inc. | Modèles de traitement de langage acoustique et naturel pour la sélection par commande vocale et la surveillance de conditions de santé comportementale |
-
2022
- 2022-06-24 EP EP22829440.1A patent/EP4358830A1/fr active Pending
- 2022-06-24 WO PCT/US2022/035007 patent/WO2022272139A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20190113973A1 (en) * | 2012-09-14 | 2019-04-18 | Interaxon Inc | Systems and methods for collecting, analyzing, and sharing bio-signal and non-bio-signal data |
US20170112427A1 (en) * | 2014-05-30 | 2017-04-27 | Adam J. Simon | Multimodal health assessment with neuro-opthalmological saccade tests |
WO2020047253A1 (fr) * | 2018-08-31 | 2020-03-05 | Blackthorn Therapeutics, Inc. | Biomarqueurs multimodaux prédictifs de la gravité d'un symptôme transdiagnostique |
WO2021081418A1 (fr) * | 2019-10-25 | 2021-04-29 | Ellipsis Health, Inc. | Modèles de traitement de langage acoustique et naturel pour la sélection par commande vocale et la surveillance de conditions de santé comportementale |
Non-Patent Citations (1)
Title |
---|
SYED ARBAAZ QURESHI ET AL: "The Verbal and Non Verbal Signals of Depression -- Combining Acoustics, Text and Visuals for Estimating Depression Level", ARXIV.ORG, CORNELL UNIVERSITY LIBRARY, 201 OLIN LIBRARY CORNELL UNIVERSITY ITHACA, NY 14853, 2 April 2019 (2019-04-02), 201 Olin Library Cornell University Ithaca, NY 14853 , XP081170003 * |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN117154086A (zh) * | 2023-07-28 | 2023-12-01 | 南京大学 | 一种Fe/Mg掺杂调控的层状富锂正极材料、制备方法以及锂离子电池 |
CN117832477A (zh) * | 2024-03-05 | 2024-04-05 | 宁德时代新能源科技股份有限公司 | 正极活性材料、二次电池和用电装置 |
Also Published As
Publication number | Publication date |
---|---|
EP4358830A1 (fr) | 2024-05-01 |
WO2022272139A9 (fr) | 2023-03-09 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20220411284A1 (en) | Cathode active material, method for manufacturing same, and lithium secondary battery comprising cathode containing same | |
US11728482B2 (en) | Doping strategy for layered oxide electrode materials used in lithium-ion batteries | |
US20220336802A1 (en) | New doping strategy for layered oxide electrode materials used in lithium-ion batteries | |
US9653725B2 (en) | Lithium rechargeable battery | |
US20190123347A1 (en) | Ni based cathode material for rechargeable lithium-ion batteries | |
US11492266B2 (en) | Processes for preparing positive electrode active substance for non-aqueous electrolyte secondary batteries | |
Knight et al. | Effect of nickel oxidation state on the structural and electrochemical characteristics of lithium-rich layered oxide cathodes | |
JP2015213075A (ja) | 高い比容量および優れたサイクルを有する積層リチウムリッチ錯体金属酸化物 | |
EP3632851A1 (fr) | Matériau actif de cathode composite, cathode et batterie au lithium chacune comprenant le matériau actif de cathode composite et procédé de préparation du matériau actif de cathode composite | |
WO2008039808A2 (fr) | Cathodes d'oxyfluorure et d'oxyde de spinelle à substituants cationiques pour batteries au lithium | |
JP2013543219A (ja) | リチウムイオン電池正極材料上の金属ハロゲン化物コーティングおよびそれに対応する電池 | |
WO2022272139A1 (fr) | Nouvelle stratégie de dopage pour matériaux d'électrode d'oxyde en couches utilisés dans des batteries au lithium-ion | |
US20230170478A1 (en) | Cathode active material for lithium secondary battery, production method thereof, and lithium secondary battery comprising same | |
JP2024500898A (ja) | リチウム二次電池用正極活物質、その製造方法およびこれを含むリチウム二次電池 | |
JP2023523668A (ja) | 正極活物質、その製造方法、及びそれを含む正極を含むリチウム二次電池 | |
JP2022523183A (ja) | 正極活物質、その製造方法、及びそれを含む正極を含むリチウム二次電池 | |
WO2017042659A1 (fr) | Matériau oxyde métallique de lithium, son utilisation dans une électrode positive d'une pile rechargeable, et procédé de préparation d'un tel matériau oxyde métallique de lithium | |
JP7402566B2 (ja) | 正極活物質、その製造方法、及びそれを含む正極を含むリチウム二次電池 | |
JP7258373B6 (ja) | 正極活物質、その製造方法、及びそれを含む正極を含むリチウム二次電池 | |
JP7258372B2 (ja) | 正極活物質、その製造方法、及びそれを含む正極を含むリチウム二次電池 | |
US20220020982A1 (en) | Cathode active material and lithium secondary battery comprising same | |
KR102523095B1 (ko) | 양극활물질, 이의 제조방법, 및 상기 양극활물질을 포함하는 리튬이차전지 | |
JP2022521083A (ja) | 正極活物質、その製造方法、及びそれを含む正極を含むリチウム二次電池 | |
US20240234707A1 (en) | Positive electrode active material, method for preparing same, and lithium secondary battery including positive electrode comprising same | |
WO2023039517A2 (fr) | Cathodes de sel gemme riches en li à haute énergie ayant une migration de cations inhibée |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22829440 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2022829440 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |