WO2022226814A1 - Pièce polaire d'électrode, appareil électrochimique la comprenant et dispositif électronique - Google Patents
Pièce polaire d'électrode, appareil électrochimique la comprenant et dispositif électronique Download PDFInfo
- Publication number
- WO2022226814A1 WO2022226814A1 PCT/CN2021/090393 CN2021090393W WO2022226814A1 WO 2022226814 A1 WO2022226814 A1 WO 2022226814A1 CN 2021090393 W CN2021090393 W CN 2021090393W WO 2022226814 A1 WO2022226814 A1 WO 2022226814A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- insulating
- pole piece
- fibers
- electrode
- conductive
- Prior art date
Abstract
La présente invention concerne le domaine technique du stockage d'énergie, et concerne spécifiquement une pièce polaire d'électrode, un appareil électrochimique la comprenant, et un dispositif électronique. La pièce polaire d'électrode de la présente invention comprend : un collecteur de courant ; une couche conductrice, qui comprend une structure de réseau conducteur formée à partir de fibres conductrices ; et une couche isolante, qui comprend une structure de réseau isolant formée à partir de fibres isolantes et de particules isolantes disposées dans la structure de réseau isolant. La couche conductrice est située entre le collecteur de courant et la couche isolante. Le diamètre des fibres conductrices est supérieur au diamètre des fibres isolantes. Dans la présente invention, le problème de dilatation volumique d'une pièce polaire d'électrode pendant un processus de cycle d'un appareil électrochimique peut être amélioré, ce qui permet de réduire le risque de court-circuitage de l'appareil électrochimique. En outre, les performances de cycle de l'appareil électrochimique peuvent être améliorées.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2021/090393 WO2022226814A1 (fr) | 2021-04-28 | 2021-04-28 | Pièce polaire d'électrode, appareil électrochimique la comprenant et dispositif électronique |
CN202180005157.1A CN114375511B (zh) | 2021-04-28 | 2021-04-28 | 电极极片及包含其的电化学装置和电子设备 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2021/090393 WO2022226814A1 (fr) | 2021-04-28 | 2021-04-28 | Pièce polaire d'électrode, appareil électrochimique la comprenant et dispositif électronique |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022226814A1 true WO2022226814A1 (fr) | 2022-11-03 |
Family
ID=81142860
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2021/090393 WO2022226814A1 (fr) | 2021-04-28 | 2021-04-28 | Pièce polaire d'électrode, appareil électrochimique la comprenant et dispositif électronique |
Country Status (2)
Country | Link |
---|---|
CN (1) | CN114375511B (fr) |
WO (1) | WO2022226814A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20110318642A1 (en) * | 2009-03-09 | 2011-12-29 | Kuraray Co., Ltd. | Conductive sheet and electrode |
CN108172761A (zh) * | 2017-12-30 | 2018-06-15 | 中南大学 | 一种用于锂二次电池的复合负极、及其制备和应用 |
CN111613773A (zh) * | 2020-04-21 | 2020-09-01 | 浙江锋锂新能源科技有限公司 | 一种分级结构玻璃纤维与金属锂的复合物及其制备方法 |
WO2020258809A1 (fr) * | 2019-06-28 | 2020-12-30 | 宁德时代新能源科技股份有限公司 | Pièce polaire d'électrode et dispositif électrochimique |
US20200411877A1 (en) * | 2018-03-05 | 2020-12-31 | Robert Bosch Gmbh | Ion Deposition Biasing to Inhibit Dendrite Formation and Growth in a Metal Ion Battery Cell |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20170117649A (ko) * | 2016-04-14 | 2017-10-24 | 주식회사 엘지화학 | 리튬 전극용 보호막, 이를 포함하는 리튬 전극 및 리튬 이차전지 |
JP6927102B2 (ja) * | 2018-03-16 | 2021-08-25 | トヨタ自動車株式会社 | リチウム金属二次電池 |
CN112054203A (zh) * | 2020-09-15 | 2020-12-08 | 昆山宝创新能源科技有限公司 | 自支撑锂金属负极材料及其制备方法和应用 |
-
2021
- 2021-04-28 WO PCT/CN2021/090393 patent/WO2022226814A1/fr active Application Filing
- 2021-04-28 CN CN202180005157.1A patent/CN114375511B/zh active Active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20110318642A1 (en) * | 2009-03-09 | 2011-12-29 | Kuraray Co., Ltd. | Conductive sheet and electrode |
CN108172761A (zh) * | 2017-12-30 | 2018-06-15 | 中南大学 | 一种用于锂二次电池的复合负极、及其制备和应用 |
US20200411877A1 (en) * | 2018-03-05 | 2020-12-31 | Robert Bosch Gmbh | Ion Deposition Biasing to Inhibit Dendrite Formation and Growth in a Metal Ion Battery Cell |
WO2020258809A1 (fr) * | 2019-06-28 | 2020-12-30 | 宁德时代新能源科技股份有限公司 | Pièce polaire d'électrode et dispositif électrochimique |
CN111613773A (zh) * | 2020-04-21 | 2020-09-01 | 浙江锋锂新能源科技有限公司 | 一种分级结构玻璃纤维与金属锂的复合物及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
CN114375511A (zh) | 2022-04-19 |
CN114375511B (zh) | 2023-12-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US11342554B2 (en) | Anode, and electrochemical device and electronic device comprising same | |
JP5640546B2 (ja) | 非水系電解液二次電池用セパレータ及び非水系電解液二次電池 | |
JP6156939B2 (ja) | リチウムイオン二次電池 | |
US20090191458A1 (en) | Porous network negative electrodes for non-aqueous electrolyte secondary battery | |
WO2022267503A1 (fr) | Appareil électrochimique et appareil électronique | |
WO2022267535A1 (fr) | Plaque d'électrode négative à lithium métallique, appareil électrochimique et dispositif électronique | |
JP2012043627A (ja) | 非水系電解液二次電池 | |
JP2012043629A (ja) | 非水系電解液二次電池用セパレータ及び非水系電解液二次電池 | |
CN113471406A (zh) | 负极极片与包含其的电化学装置 | |
WO2023070988A1 (fr) | Dispositif électrochimique et dispositif électronique le contenant | |
WO2023082245A1 (fr) | Électrode et son procédé de fabrication, dispositif électrochimique et dispositif électronique | |
WO2022198651A1 (fr) | Plaque d'électrode positive et dispositif électrochimique et dispositif électronique comprenant une plaque d'électrode positive | |
WO2023070516A1 (fr) | Batterie secondaire, module de batterie, bloc-batterie et dispositif électrique | |
WO2023004821A1 (fr) | Électrolyte, batterie secondaire, module de batterie, bloc-batterie et dispositif électrique | |
WO2022226814A1 (fr) | Pièce polaire d'électrode, appareil électrochimique la comprenant et dispositif électronique | |
WO2022241712A1 (fr) | Batterie secondaire au lithium-ion, module de batterie, bloc-batterie et dispositif électrique | |
KR20230088782A (ko) | 복합 분리막, 전기화학적 에너지 저장 장치 및 전기 장치 | |
WO2022140902A1 (fr) | Plaque d'électrode négative et son procédé de préparation, batterie secondaire, module de batterie, bloc-batterie et appareil | |
WO2022205134A1 (fr) | Dispositif électrochimique et dispositif électronique | |
WO2023133833A1 (fr) | Batterie secondaire, module de batterie, bloc-batterie et appareil électrique | |
WO2021195881A1 (fr) | Pièce polaire négative et dispositif électrochimique la contenant | |
WO2023082248A1 (fr) | Électrode et son procédé de fabrication, dispositif électrochimique et dispositif électronique | |
EP4239722A1 (fr) | Matériau actif d'électrode négative, son procédé de préparation et batterie secondaire le comprenant | |
WO2024040525A1 (fr) | Batterie secondaire et dispositif électrique | |
US20240079600A1 (en) | Cathode plate, secondary battery, battery module, battery pack, and electric device |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21938300 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21938300 Country of ref document: EP Kind code of ref document: A1 |