WO2022130484A1 - アルミニウム合金及びアルミニウム合金鋳物材 - Google Patents

アルミニウム合金及びアルミニウム合金鋳物材 Download PDF

Info

Publication number
WO2022130484A1
WO2022130484A1 PCT/JP2020/046678 JP2020046678W WO2022130484A1 WO 2022130484 A1 WO2022130484 A1 WO 2022130484A1 JP 2020046678 W JP2020046678 W JP 2020046678W WO 2022130484 A1 WO2022130484 A1 WO 2022130484A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminum alloy
mass
casting material
present
casting
Prior art date
Application number
PCT/JP2020/046678
Other languages
English (en)
French (fr)
Inventor
晋也 三輪
宏 堀川
Original Assignee
日軽エムシーアルミ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日軽エムシーアルミ株式会社 filed Critical 日軽エムシーアルミ株式会社
Priority to US18/039,829 priority Critical patent/US20240018632A1/en
Priority to PCT/JP2020/046678 priority patent/WO2022130484A1/ja
Priority to JP2022569355A priority patent/JP7472318B2/ja
Priority to CN202080107953.1A priority patent/CN116635549A/zh
Publication of WO2022130484A1 publication Critical patent/WO2022130484A1/ja

Abstract

本発明は、優れた鋳造性を有すると共に、熱処理を施すことなく高い機械的性質を発現することができるアルミニウム合金及びアルミニウム合金鋳物材を提供する。より具体的には、優れた鋳造性を有すると共に、熱処理を施すことなく高い０．２％耐力と優れた延性を有するアルミニウム合金及びアルミニウム合金鋳物材を提供する。本発明に係るアルミニウム合金は、Ｓｉ：７．０～９．０質量％、Ｃｕ：２．０～４．０質量％、Ｍｇ：０．８～１．２質量％、Ｆｅ：０．３～０．５質量％、Ｍｎ：０．３～０．５質量％、Ｚｎ：２．０～４．０質量％、を含み、残部がＡｌ及び不可避不純物よりなること、を特徴とするアルミニウム合金である。

Description

アルミニウム合金及びアルミニウム合金鋳物材
　本発明は鋳物用のアルミニウム合金及び当該アルミニウム合金からなるアルミニウム合金鋳物材に関する。
　軽量であることに加えて優れた質感を有していることから、携帯可能な電子機器や電子端末の筐体にアルミニウム合金材が使用されている。これらの携帯用電子機器に対する薄さ及び軽量化の要求は年々高くなっており、筐体に用いられるアルミニウム合金にはより高い強度が求められている。
　特に、スマートフォンは使用されない際はポケット等にしまわれることが多く、当該状況においては曲げ応力が印加される場合が多い。即ち、携帯用電子機器の筐体に使用されるアルミニウム合金は優れた鋳造性に加えて、高い強度と延性（靭性）を有することが必要不可欠である。
　これに対し、例えば、特許文献１（特開昭４８－３２７１９号公報）では、Ａｌ－Ｃｕ－Ｓｉ系あるいはＡｌ－Ｓｉ－Ｃｕ－Ｍｇ系合金の優れた鋳造性を生かして、且つ従来の鋳造用高力アルミニウム合金に匹敵する強度を有する合金を得ることを目的とし、重量で珪素７．５～１．２％、銅４．０～５．５％、マグネシウム０．２～１．０％、残部アルミニウム及び不純物からなる鋳造性の優れた鋳物用高力アルミニウム合金、が開示されている。
　上記特許文献１に記載の鋳物用高力アルミニウム合金においては、約５００℃の溶体化処理を行った後に時効硬化させることで、アルミニウム合金鋳物に優れた機械的性質を与えることができる、とされている。
　また、特許文献２（特開昭６０－５７４９７号公報）では、鋳造性が良好で強靭性に富み、且つ耐熱性の優れた熱処理型の高力アルミニウム合金を得ることを目的として、重量で６％を超え１３％までの珪素、３％を超え５．５％までの銅、１％を超え４％までの亜鉛、０．２％を超え１％までのマグネシウム及び０．０３％を超え１％までのアンチモンを含み、残部アルミニウム及び不純物よりなる耐熱性高力アルミニウム合金、が開示されている。
　上記特許文献２に記載の耐熱性高力アルミニウム合金においては、Ａｌ－Ｓｉ－Ｃｕ－Ｚｎ－Ｍｇ系合金において銅が３％を超えて含まれる場合に、合金中にアンチモンを添加すると時効処理に際して合金の時効硬化性が促進され靭性をそれほど低下することなしに合金強度が著しく向上すると共に合金の耐熱衝撃性が著しく改善される、とされている。
特開昭４８－３２７１９号公報 特開昭６０－５７４９７号公報
　上記特許文献１に記載の鋳物用高力アルミニウム合金及び上記特許文献２に記載の耐熱性高力アルミニウム合金においては、優れた鋳造性に加えて優れた機械的性質が付与されているとしているが、当該機械的性質を実現するためには人工時効等の熱処理が必須となっている。
　しかしながら、熱処理工程は製造コストや製造時間を増加させるだけでなく、アルミニウム合金鋳物材の寸法及び形状にも影響する。特に、携帯用電子機器の筐体は薄いことに加えて高い寸法精度が求められるため、熱処理を施すことなく高い強度及び優れた延性を実現できることが望ましい。
　以上のような従来技術における問題点に鑑み、本発明の目的は、優れた鋳造性を有すると共に、熱処理を施すことなく高い機械的性質を発現することができるアルミニウム合金及びアルミニウム合金鋳物材を提供することにある。より具体的には、本発明は、優れた鋳造性を有すると共に、熱処理を施すことなく高い０．２％耐力と優れた延性を有するアルミニウム合金及びアルミニウム合金鋳物材を提供することを目的としている。
　本発明者らは、上記目的を達成すべく、アルミニウム合金の組成範囲について鋭意研究を重ねた結果、Ｓｉ、Ｃｕ、Ｍｇ、Ｆｅ、Ｍｎ及びＺｎの添加量を全て厳密に制御すること等が極めて有効であることを見出し、本発明に到達した。
　即ち、本発明は、
　Ｓｉ：７．０～９．０質量％、
　Ｃｕ：２．０～４．０質量％、
　Ｍｇ：０．８～１．２質量％、
　Ｆｅ：０．３～０．５質量％、
　Ｍｎ：０．３～０．５質量％、
　Ｚｎ：２．０～４．０質量％、を含み、
　残部がＡｌ及び不可避不純物よりなること、
　を特徴とするアルミニウム合金、を提供する。
　本発明のアルミニウム合金は、
　Ｓｒ：０．００８～０．０４質量％、
　Ｂｅ：０．００１～０．００４質量％、
　Ｔｉ：０．０５～０．００５質量％、
　Ｂ：０．０１～０．００５質量％、
　のうちのいずれか一種以上を含むこと、が好ましい。
　また、本発明は、
　本発明のアルミニウム合金からなり、
　０．２％耐力が２３０ＭＰａ以上であり、
　破断伸びが２．５％以上であること、
　を特徴とするアルミニウム合金鋳物材、も提供する。
　本発明のアルミニウム合金鋳物材は、鋳造によって所望の形状とした後、熱処理を施すことなく２３０ＭＰａ以上の０．２％耐力と２．５％以上の破断伸びを発現することができる。より好ましい０．２％耐力は２４０ＭＰａ以上であり、より好ましい破断伸びは３．０％以上である。
　本発明によれば、優れた鋳造性を有すると共に、熱処理を施すことなく高い機械的性質を発現することができるアルミニウム合金及びアルミニウム合金鋳物材を提供することができる。より具体的には、本発明によれば、優れた鋳造性を有すると共に、熱処理を施すことなく高い０．２％耐力と優れた延性を有するアルミニウム合金及びアルミニウム合金鋳物材を提供することができる。
　以下、本発明のアルミニウム合金及びアルミニウム合金鋳物材の代表的な実施形態について詳細に説明するが、本発明はこれらのみに限定されるものではない。
１．アルミニウム合金
　本発明のアルミニウム合金は、Ｓｉ：７．０～９．０質量％、Ｃｕ：２．０～４．０質量％、Ｍｇ：０．８～１．２質量％、Ｆｅ：０．３～０．５質量％、Ｍｎ：０．３～０．５質量％、Ｚｎ：２．０～４．０質量％、を含み、残部がＡｌ及び不可避不純物よりなるアルミニウム合金である。以下、各成分について詳細に説明する。
（１）必須の添加元素
　Ｓｉ：７．０～９．０質量％
　Ｓｉはアルミニウムの鋳造性を向上させる特性を有するとともに引張強度等の機械的性質を向上させる作用がある。この作用はＳｉ：７．０質量％以上で顕著となる。逆にＳｉ：９．０質量％以上となると晶出する共晶Ｓｉや初晶Ｓｉが粗大化しやすくなる。それら化合物が粗大化すると破断する際の起点となりやすいため、伸びの低下につながりやすい。より好ましいＳｉの添加量は７．５～８．５質量％である。
　Ｃｕ：２．０～４．０質量％
　Ｃｕは、引張強度等の機械的性質を向上させる作用を有する。この作用はＣｕ：２．０質量％以上で顕著となる。逆に、４．０質量％より多くするとＣｕ系晶出物が粗大化しやすくなり、伸びが低下しやすくなる。またＣｕの含有量が大きくなると耐食性も低下する。更に、アルマイト処理した際に、色彩が黄色味を帯びやすくなる。より好ましいＣｕの添加量は２．５～３．７質量％であり、更に好ましくは３．５質量％以下である。
　Ｍｇ：０．８～１．２質量％
　Ｍｇは、引張強度等の機械的性質を向上させる作用を有する。この作用はＭｇ：０．８質量％以上で顕著となる。逆に１．２質量％を超えると粗大な化合物が形成されやすくなり、伸びが低下しやすくなる。
　Ｓｉ、Ｍｇ及びＣｕは、時効処理によって化合物として析出し、析出強化に寄与する元素であるが、本発明のアルミニウム合金は非熱処理材として用いられることを主としており、これらの元素による強化機構は基本的に固溶強化となる。
　Ｆｅ：０．２～０．５質量％
　Ｆｅは、引張強度等の機械的性質を向上させる作用を有する。この作用はＦｅ：０．２質量％以上で顕著となる。また、ダイカスト法等の金型鋳造において、焼き付きを防止する効果もある。０．５質量％を超えると破断の起点となる粗大な針状のＡｌ－（Ｓｉ，Ｆｅ，Ｍｎ）系化合物を形成しやすくなる。
　Ｍｎ：０．３～０．５質量％
　Ｍｎは、引張強度等の機械的性質を向上させる作用を有する。この作用は、Ｍｎ：０．３質量％以上で顕著となる。また、Ａｌ－（Ｓｉ，Ｆｅ，Ｍｎ）系化合物を粒状にする作用も有する。逆に０．５質量％を超えるとＡｌ－（Ｓｉ，Ｆｅ，Ｍｎ）系化合物が粗大化しやすい。
　Ｚｎ：２．０～４．０質量％
　Ｚｎは、引張強度等の機械的性質を向上させる作用を有する。この作用は、Ｚｎ：２．０質量％以上で顕著となる。逆に４．０質量％を超えると応力腐食割れが起こりやすくなる。また、陽極酸化皮膜処理を施した際に、変色や色むらが起こりやすくなる。
（２）任意の添加元素
　Ｓｒ：０．００８～０．０４質量％
　Ｓｒは、共晶Ｓｉを微細化、粒状化させる作用を有し、この効果は、Ｓｒ：０．００８質量％以上で顕著となる。０．０４質量％を超えて添加しても、効果の向上があまり認められないため、０．０４質量％未満にすることが好ましい。
　Ｂｅ：０．００１～０．００４質量％
　Ｂｅは、溶解した際に溶湯表面に酸化被膜を形成し、Ｍｇ等の他の元素の減耗を抑制する効果がある。また、鋳物の表面が黒色化することを抑制する効果もある。この効果は、Ｂｅ０．００１質量％以上で顕著となる。０．００４質量％を超えて添加されても、効果の向上があまり認められないため、０．００４質量％未満にすることが好ましい。
　Ｔｉ：０．０５～０．００５質量％
　Ｔｉは組織を微細化することで、主に靭性に寄与する。下限値未満ではその効果が小さく、上限値を超えて含有させても、すでに十分に微細化されており効果がない上、過剰に加えると粗大晶出物を形成することで延性に悪影響を及ぼすようになるため、上記範囲で制限する必要がある。
　Ｂ：０．０１～０．００５質量％
　Ｂは組織を微細化することで、主に靭性に寄与する。下限値未満ではその効果が小さく、上限値を超えて含有させても、すでに十分に微細化されており効果がない上、過剰に加えると粗大晶出物を形成することで延性に悪影響を及ぼすようになるため、上記範囲で制限する必要がある。
　なお、本発明の効果を損なわない限りにおいて、本発明のアルミニウム合金の製造方法は特に限定されず、従来公知の種々の製造方法を用いればよい。
２．アルミニウム合金鋳物材
　本発明のアルミニウム合金鋳物材は、本発明のアルミニウム合金からなり、０．２％耐力が２３０ＭＰａ以上、破断伸びが２．５％以上であること、を特徴としている。より好ましい０．２％耐力は２４０ＭＰａ以上であり、より好ましい破断伸びは３．０％以上である。
　優れた機械的性質は基本的に組成を厳密に最適化したことによって実現されており、アルミニウム合金鋳物材の形状及びサイズに依らず、またアルミニウム合金鋳物材の部位及び方位に依らず、当該機械的性質を有している。
　また、本発明のアルミニウム合金鋳物材においては、時効処理等の熱処理を施すことなく、２３０ＭＰａ以上の０．２％耐力と２．５％以上の破断伸びを発現することができる。
　なお、本発明の効果を損なわない限りにおいて、アルミニウム合金鋳物材の形状及びサイズは特に限定されず、従来公知の種々の部材として使用することができる。当該部材としては、例えば、電子端末筐体を挙げることができる。
　また、本発明の効果を損なわない限りにおいて、本発明のアルミニウム合金鋳物材の製造方法は特に限定されず、本発明のアルミニウム合金を用いて従来公知の種々の方法で鋳造を行えばよい。更に、本発明の合金を用いた鋳物材は、非熱処理でも優れた機械的特性、特に靭性を有するが、時効処理等の熱処理を行っても良い。時効処理を行うとＳｉ，Ｍｇ，Ｃｕ，Ｚｎ等の化合物の析出強化により、より高い機械的特性を得ることができる。
　以上、本発明の代表的な実施形態について説明したが、本発明はこれらのみに限定されるものではなく、種々の設計変更が可能であり、それら設計変更は全て本発明の技術的範囲に含まれる。
≪実施例≫
　表１において、実施例１～実施例５として記載されている組成を有するアルミニウム合金を溶製し、鋳造圧力を１２０ＭＰａ、溶湯温度を７３０℃、金型温度を１７０℃ とし、ダイカストを行った。金型形状は５５ｍｍ×１１０ｍｍ×３ｍｍの板状である。アルミニウム合金は優れたダイカスト性を有しており、良好なアルミニウム合金鋳物材（ダイカスト材）が得られた。なお、表１に記載の数値の単位は質量％濃度である。
Figure JPOXMLDOC01-appb-T000001
　得られた各実施アルミニウム合金鋳物材よりＪＩＳ－Ｚ２２４１に定められる１４Ｂ号試験片を採取し、室温にて引張試験を行ったところ、引張強度、０．２％耐力及び破断伸びは表２に記載の値となった。また、得られた実施アルミニウム合金鋳物材のロックウェル硬さを測定したところ、表２に記載の値となった。ここで、実施アルミニウム合金鋳物材はダイカストのままであり、時効処理等の熱処理は施していない。
Figure JPOXMLDOC01-appb-T000002
　≪比較例≫
　表１に比較例１～比較例２２として記載の成分となるように溶解材を調整したこと以外は実施例と同様にして、比較アルミニウム合金鋳物材（ダイカスト材）を得た。また、実施例と同様にして、引張特性及びロックウェル硬さを測定した。得られた値を表２に示す。なお、数値の記載がない場合は測定を行っていないことを意味している。
　実施例及び比較例で得られた各アルミニウム合金鋳物材の引張特性を比較すると、実施例で得られたアルミニウム合金鋳物材のみが２３０ＭＰａ以上の０．２％耐力と２．５％以上の破断伸びを共に有していることが分かる。また、実施例において、Ｓｒを添加した実施例１の方が、Ｓｒを添加していない（Ｓｒの含有量が極めて少ない）実施例４より、引張強度と伸びが高いことが分かる。
　Ｓｉ、Ｃｕ及びＭｎの含有量が多い比較例１～比較例５の組成を有するアルミニウム合金鋳物材は高い０．２％耐力を示しているが、破断伸びが２．０％以下となっている。また、Ｆｅの含有量が多い比較例６～比較例１０、比較例１３～１９の組成を有するアルミニウム合金鋳物材も破断伸びが２．５％に達していない。
　また、Ｍｇの添加量が少なくＺｎを含んでいない比較例１１及びＭｇの添加量が少ない比較例１２の組成を有するアルミニウム合金鋳物材の硬度は低い値となっており、十分な強度が得られていないことが分かる。
　更に、Ｓｉ及びＣｕの含有量が少ない比較例２０の組成を有するアルミニウム合金鋳物材は２．５％以上の破断伸びを有しているが、０．２％耐力が低い値となっている。また、ＳｉとＺｎの含有量が少なく、ＣｕとＭｎの含有量が多い比較例２１は、高い引張強度と０．２％耐力を有しているが、破断伸びが２．５％未満と低い値となっている。また、ＣｕとＭｎの含有量が多い比較例２２は、破断伸びが２．５％未満と低い値となっていることに加え、０．２％耐力も２３０ＭＰａに達していない。
　以上の結果より、アルミニウム合金鋳物材に熱処理を施すことなく２３０ＭＰａ以上の０．２％耐力と２．５％以上の破断伸びを発現させるためには、Ｓｉ、Ｃｕ、Ｍｇ、Ｆｅ、Ｍｎ及びＺｎの添加量を厳密に制御することが必要であることが分かる。

Claims (3)

  1. Ｓｉ：７．０～９．０質量％、
    Ｃｕ：２．０～４．０質量％、
    Ｍｇ：０．８～１．２質量％、
    Ｆｅ：０．３～０．５質量％、
    Ｍｎ：０．３～０．５質量％、
    Ｚｎ：２．０～４．０質量％、を含み、
    残部がＡｌ及び不可避不純物よりなること、
    を特徴とするアルミニウム合金。
  2. Ｓｒ：０．００８～０．０４質量％、
    Ｂｅ：０．００１～０．００４質量％、
    Ｔｉ：０．０５～０．００５質量％、
    Ｂ：０．０１～０．００５質量％、
    のうちのいずれか一種以上を含むこと、
    を特徴とする請求項１に記載のアルミニウム合金。
  3. 請求項１又は請求項２に記載のアルミニウム合金からなり、
    ０．２％耐力が２３０ＭＰａ以上であり、
    破断伸びが２．５％以上であること、
    を特徴とするアルミニウム合金鋳物材。
PCT/JP2020/046678 2020-12-15 2020-12-15 アルミニウム合金及びアルミニウム合金鋳物材 WO2022130484A1 (ja)