WO2022118697A1 - 眼科デバイス用改質剤 - Google Patents

眼科デバイス用改質剤 Download PDF

Info

Publication number
WO2022118697A1
WO2022118697A1 PCT/JP2021/042877 JP2021042877W WO2022118697A1 WO 2022118697 A1 WO2022118697 A1 WO 2022118697A1 JP 2021042877 W JP2021042877 W JP 2021042877W WO 2022118697 A1 WO2022118697 A1 WO 2022118697A1
Authority
WO
WIPO (PCT)
Prior art keywords
monomer
group
formula
copolymer
silicone hydrogel
Prior art date
Application number
PCT/JP2021/042877
Other languages
English (en)
French (fr)
Inventor
裕貴 鈴木
規郎 岩切
Original Assignee
日油株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日油株式会社 filed Critical 日油株式会社
Priority to JP2022566853A priority Critical patent/JPWO2022118697A1/ja
Priority to CN202180080764.4A priority patent/CN116490532A/zh
Priority to US18/039,442 priority patent/US20240117094A1/en
Publication of WO2022118697A1 publication Critical patent/WO2022118697A1/ja

Abstract

シリコーンハイドロゲルに高い濡れ性、滑り性を付与することができる眼科デバイス用改質剤、詳しくは、少量の含有量でその効果を発現可能な眼科デバイス用改質剤を提供することにある。また、眼科デバイス用改質剤を含むシリコーンハイドロゲル組成物を硬化させて得られるシリコーンハイドロゲル、及び該シリコーンハイドロゲルを用いた眼科デバイスを提供することにある。　ホスホリルコリン基含有単量体、及び特定のシリコーン単量体を共重合させた水溶性のシリコーン含有水溶性共重合体が、少量の含有量でシリコーンハイドロゲルに高い濡れ性、滑り性を付与することができることを見出した。

Description

眼科デバイス用改質剤
　本発明は、コンタクトレンズ、眼内レンズ、人口角膜等を例とする眼科デバイスの製造において、該デバイスに含有させることが最適な、シリコーン含有水溶性共重合体を含む眼科デバイス用改質剤に関する。
　本出願は、参照によりここに援用されるところの日本出願特願2020-199789号優先権を請求する。
　シリコーンハイドロゲルコンタクトレンズは、従来のコンタクトレンズと比較して著しく高い酸素透過性を有しているので、角膜への酸素供給量が多く眼組織への負担を軽減させることができる。シリコーンハイドロゲルコンタクトレンズは、近年処方されるコンタクトレンズの主流となりつつあり、今後益々普及すると期待されている。
　一方、シリコーンハイドロゲルレンズは、含水率が低く疎水性が高いため、涙液をはじきやすく、脂質汚れが付着しやすいという欠点があった。また近年、瞬目時の眼瞼結膜縁と眼表面との摩擦が原因となって、眼瞼結膜表層の上皮細胞の脱落と変性が起こることが報告されている（非特許文献１、非特許文献２）。これにより、シリコーンハイドロゲルレンズに親水性とともに滑り性を付与することが求められている。そのため、シリコーンハイドロゲルレンズの表面の親水性、滑り性を改善するために、様々な方案が検討されている。
　例えば、コンタクトレンズの生産工程において、レンズのプラズマ処理工程を含めることが広く実施されている。プラズマ処理は比較的高い親水性と耐久性を付与できるという利点があるが、滑り性が付与できず、また大規模な設備投資を必要とするという欠点がある。
　大規模な設備投資を必要としない方法として、親水性のモノマーを使用してレンズを製造することが広く行われている。特に、両性イオン型の構造を有する２－メタクリロイルオキシエチルホスホリルコリン（以下「ＭＰＣ」と略記する場合がある）を用いた場合、レンズは高い親水性と滑り性が得られることが知られている。
　特許文献１には、ＭＰＣを含有しうる特定の組成物から得られるシリコーンハイドロゲルレンズについて記載されている。しかし、特許文献１においては、水のブレイクアップ時間の測定によってレンズ表面の親水性の改善が示されているものの、レンズ表面の摩擦を低減する意味での滑り性については検討されておらず、改善の余地がある。
　特許文献２には、ＭＰＣと特定の他のモノマーを特定の組成比で用いることにより、滑り性も良好なシリコーンハイドロゲルレンズを得られることが開示されている。しかし、良好な滑り性を得るためにはＭＰＣを５重量％以上、最も高い滑り性を得るためには約２０重量％添加する必要があり、このような高濃度のＭＰＣを疎水性の高いシリコーン成分と相溶させるためには、レンズモノマー組成に一定の制約が伴う。
　以上により、より幅広いレンズ組成に応用可能な技術の開発が求められていた。
特開２０１４－８９４７７号 国際公開２０２０／０５４７１１号
Ｄ．Ｒ．Ｋｏｒｂ　ｅｔ　ａｌ．，２００２，ＣＬＡＯ　Ｊ．，２８，２１１－１２６ Ｄ．Ｒ．Ｋｏｒｂ　ｅｔ　ａｌ．，２００５，Ｅｙｅ＆Ｃｏｎｔａｃｔ　Ｌｅｎｓ，３１，２－８
　本発明の課題は、シリコーンハイドロゲルに高い濡れ性、滑り性を付与することができる眼科デバイス用改質剤、詳しくは、少量の含有量でその効果を発現可能な眼科デバイス用改質剤を提供することにある。また、眼科デバイス用改質剤を含むシリコーンハイドロゲル組成物を硬化させて得られるシリコーンハイドロゲル、及び該シリコーンハイドロゲルを用いた眼科デバイスを提供することにある。
　本発明者らは、上記課題に鑑み鋭意検討した結果、驚くべきことに、ホスホリルコリン基含有単量体、及び特定のシリコーン単量体を共重合させた水溶性のシリコーン含有水溶性共重合体が、少量の含有量でシリコーンハイドロゲルに高い濡れ性、滑り性を付与することができることを見出し、本発明を完成した。
　すなわち、本発明は以下の通りである。
　１．下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体を含む眼科デバイス用改質剤。
Figure JPOXMLDOC01-appb-C000004
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000005
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000006
 （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
　２．前記共重合体が、熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位をさらに含有する、前項１に記載の眼科デバイス用改質剤。
　３．前記式（１）で表される親水性単量体ａに基づく構成単位が２－メタクリロイルオキシエチルホスホリルコリンであり、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位がトリス（トリメチルシロキシ）シリルプロピルメタクリレート、ポリジメチルシロキサンモノメタクリレート、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート若しくは３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレートであり、並びに、熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位がグリシジルメタクリレート、メタクリロイルオキシベンゾフェノン若しくは４－（４－アジドベンゾイルオキシメチル）ビニルベンゼンである、前項２に記載の眼科デバイス用改質剤。
　４．前記式（１）で表される親水性単量体ａに基づく構成単位、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位、及び／又は、反応性単量体もしくは光反応性単量体ｃに基づく構成単位の組み合わせは、以下のいずれか１から選択される、前項２に記載の眼科デバイス用改質剤。
　１）２－メタクリロイルオキシエチルホスホリルコリン及びトリス（トリメチルシロキシ）シリルプロピルメタクリレート
　２）２－メタクリロイルオキシエチルホスホリルコリン及びポリジメチルシロキサンモノメタクリレート
　３）２－メタクリロイルオキシエチルホスホリルコリン及び４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
　４）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びグリシジルメタクリレート
　５）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びグリシジルメタクリレート
　６）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びメタクリロイルオキシベンゾフェノン
　７）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びメタクリロイルオキシベンゾフェノン
　８）２－メタクリロイルオキシエチルホスホリルコリン、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート及び４－（４－アジドベンゾイルオキシメチル）ビニルベンゼン、及び
　９）２－メタクリロイルオキシエチルホスホリルコリン、３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート及びメタクリロイルオキシベンゾフェノン
　５．前項１または２記載の共重合体並びにベース組成物を含む、シリコーンハイドロゲル組成物であって、
　該共重合体が該ベース組成物１００質量部に対して０．０５～２質量部含まれる、シリコーンハイドロゲル組成物。
　６．前項５に記載のシリコーンハイドロゲル組成物を硬化させて得られるシリコーンハイドロゲル。
　７．前項６に記載のシリコーンハイドロゲルを用いた眼科デバイス。
　８．ソフトコンタクトレンズである前項７に記載の眼科デバイス。
　９．共重合体を含むシリコーンハイドロゲル組成物を硬化する工程を含む、シリコーンハイドロゲルの製造方法、
　ここで、該共重合体は、下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体である、製造方法。
Figure JPOXMLDOC01-appb-C000007
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000008
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000009
 （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
　１０．前記シリコーンハイドロゲル組成物中の前記共重合体の量は、０．１～１質量部である、前項９に記載のシリコーンハイドロゲルの製造方法。
　１１．前記シリコーンハイドロゲル組成物が、さらに、ベース組成物を含み、かつ前記共重合体が該ベース組成物１００質量部に対して０．０５～２質量部である、前項９に記載のシリコーンハイドロゲルの製造方法。
　１２．前記式（１）で表される親水性単量体ａに基づく構成単位が２－メタクリロイルオキシエチルホスホリルコリンであり、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位がトリス（トリメチルシロキシ）シリルプロピルメタクリレート、ポリジメチルシロキサンモノメタクリレート、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート若しくは３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレートであり、並びに、熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位がグリシジルメタクリレート、メタクリロイルオキシベンゾフェノン若しくは４－（４－アジドベンゾイルオキシメチル）ビニルベンゼンである、前項９に記載のシリコーンハイドロゲルの製造方法。
　１３．前記式（１）で表される親水性単量体ａに基づく構成単位、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位、及び／又は、反応性単量体もしくは光反応性単量体ｃに基づく構成単位の組み合わせは、以下のいずれか１から選択される、前項９に記載のシリコーンハイドロゲルの製造方法。
　１）２－メタクリロイルオキシエチルホスホリルコリン及びトリス（トリメチルシロキシ）シリルプロピルメタクリレート
　２）２－メタクリロイルオキシエチルホスホリルコリン及びポリジメチルシロキサンモノメタクリレート
　３）２－メタクリロイルオキシエチルホスホリルコリン及び４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
　４）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びグリシジルメタクリレート
　５）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びグリシジルメタクリレート
　６）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びメタクリロイルオキシベンゾフェノン
　７）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びメタクリロイルオキシベンゾフェノン
　８）２－メタクリロイルオキシエチルホスホリルコリン、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート及び４－（４－アジドベンゾイルオキシメチル）ビニルベンゼン、及び
　９）２－メタクリロイルオキシエチルホスホリルコリン、３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート及びメタクリロイルオキシベンゾフェノン
　１４．下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体を眼科デバイス用改質剤の製造としての使用。
Figure JPOXMLDOC01-appb-C000010
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000011
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000012
 （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
　１５．前記式（１）で表される親水性単量体ａに基づく構成単位が２－メタクリロイルオキシエチルホスホリルコリンであり、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位がトリス（トリメチルシロキシ）シリルプロピルメタクリレート、ポリジメチルシロキサンモノメタクリレート、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート若しくは３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレートであり、並びに、熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位がグリシジルメタクリレート、メタクリロイルオキシベンゾフェノン若しくは４－（４－アジドベンゾイルオキシメチル）ビニルベンゼンである、前項１４に記載の眼科デバイス用改質剤の製造としての使用。
　１６．前記式（１）で表される親水性単量体ａに基づく構成単位、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位、及び／又は、反応性単量体もしくは光反応性単量体ｃに基づく構成単位の組み合わせは、以下のいずれか１から選択される、前項１４に記載の眼科デバイス用改質剤の製造としての使用。
　１）２－メタクリロイルオキシエチルホスホリルコリン及びトリス（トリメチルシロキシ）シリルプロピルメタクリレート
　２）２－メタクリロイルオキシエチルホスホリルコリン及びポリジメチルシロキサンモノメタクリレート
　３）２－メタクリロイルオキシエチルホスホリルコリン及び４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
　４）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びグリシジルメタクリレート
　５）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びグリシジルメタクリレート
　６）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びメタクリロイルオキシベンゾフェノン
　７）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びメタクリロイルオキシベンゾフェノン
　８）２－メタクリロイルオキシエチルホスホリルコリン、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート及び４－（４－アジドベンゾイルオキシメチル）ビニルベンゼン、及び
　９）２－メタクリロイルオキシエチルホスホリルコリン、３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート及びメタクリロイルオキシベンゾフェノン
　本発明の眼科デバイス用改質剤を用いると、シリコーンハイドロゲルに高い濡れ性、滑り性を付与することができる。
　以下、本発明を更に詳細に説明する。
　なお、本明細書において、「（メタ）アクリル酸」とは、「アクリル酸又はメタクリル酸」を意味し、他の類似用語についても同様である。
　また、本明細書において、好ましい数値範囲（例えば、含有量や重量平均分子量の範囲）を段階的に記載した場合、各下限値及び上限値は、それぞれ独立して組み合わせることができる。例えば、「好ましくは１０～１００、より好ましくは２０～９０」という記載において、「好ましい下限値：１０」と「より好ましい上限値：９０」とを組み合わせて「１０～９０」とすることができる。
　本発明の眼科デバイス用改質剤又はシリコーンハイドロゲル組成物に含まれる共重合体（以後、「本発明の共重合体」と称する場合がある）の１つの形態は、下記の式（１）で表される親水性単量体ａ、及び下記の式（２）または式（３）で表されるシリコーン単量体ｂを共重合して得られる共重合体（下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体）であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体である。
Figure JPOXMLDOC01-appb-C000013
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000014
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表す。またＬ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよい。またＲ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表す。ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000015
 （式（３）中、Ｒ１４は水素原子またはメチル基を表す。またＬ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよい。ｎ２は４～２０の整数を表す。Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
［親水性単量体ａ］
　式（１）で表される親水性単量体ａのＲ１は水素原子またはメチル基を表すが、原料入手性の観点からメチル基が好ましい。
　またＬ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよいが、原料入手性の観点から－Ｃ２Ｈ４－、－Ｃ２Ｈ４－Ｏ－Ｃ２Ｈ４－、－Ｃ２Ｈ５－が好ましく、特に－Ｃ２Ｈ５－が好ましい。
　ここで、有機基とは、Ｃ、Ｓｉ、Ｎ、Ｐ、Ｏ、Ｓといった元素により構成される基であり、繰り返し単位を有する重合体であってもよい。また、その構造中に、ケトン基、エステル基、エーテル基、ヒドロキシル基、アミド基、チオエーテル基、イソシアヌレート基等の基を含んでもよい。
　またＲ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表すが、原料入手性の観点から全てメチル基とすることが好ましい。
　従って、親水性単量体ａの具体例としては、２－メタクリロイルオキシエチルホスホリルコリン等を好ましく挙げることができる。
　本発明で用いる単量体ａとしては、単一の単量体を用いてもよいし、複数の単量体を組合わせて用いてもよい。
［シリコーン単量体ｂ］
　式（２）で表される場合のシリコーン単量体ｂのＸ１は、（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基のいずれかの重合性官能基を表す。このうち、原料入手性の観点からはメタクリロイルオキシ基が好ましく選択され、また、親水性単量体との相溶性の観点からは３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基が好ましく選択される。
　またＬ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよいが、原料入手性の観点から－ｎ－Ｃ３Ｈ６－が好ましく選択される。
　またＲ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表すが、原料入手性の観点から全てメチル基とすることが好ましい。
　また、ｎ１は０または１を表すが、シリコーンハイドロゲル組成物との相溶性を高める観点から、１とすることが好ましい。
　従って、式（２）で表される単量体ｂの具体例としては、トリス（トリメチルシロキシ）シリルプロピルメタクリレート、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート等を好ましく挙げることができる。
　式（３）で表される場合のシリコーン単量体ｂのＲ１４は水素原子またはメチル基を表すが、得られる共重合体の保存安定性の観点からメチル基とすることが好ましい。
　またＬ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよい。
　またｎ２は４～２０の整数を表す。また通常ｎ２は分布を有し、その場合その数平均値が４～２０の範囲内であることが好ましい。
　また、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。
　従って、式（３）で表される単量体ｂの具体例としては、ポリジメチルシロキサンモノメタクリレート、片末端モノメタクリロイルオキシプロピル変性ポリジメチルシロキサン等を好ましく挙げることができる。
　本発明で用いる単量体ｂとしては、単一の単量体を用いてもよいし、複数の単量体を組合わせて用いてもよい。また、式（２）で表される単量体と式（３）で表される単量体のいずれかのみを用いてもよいし、双方を組合わせて用いてもよい。
　シリコーンハイドロゲルモノマー配合物（シリコーンハイドロゲル組成物）への相溶性の観点では、式（２）で表される単量体を単独で用いることが好ましい。
［単量体ａと単量体ｂの比率］
　単量体ａと単量体ｂの比率は、単量体ａ：単量体ｂ＝２：１～３００：１（質量比）とすることが好ましく、５：１～５０：１とすることがより好ましく、７：１～２５：１とすることがよりさらに好ましい。これらの範囲とすることで、シリコーンハイドロゲル組成物に好ましく相溶し、該シリコーンハイドロゲル組成物を硬化させて得られるシリコーンハイドロゲルに濡れ性、滑り性を付与する効果が高くなる。
　また、単量体ａが１００質量部に対して、単量体ｂが０．３～５０質量部、好ましくは２～２０質量部、より好ましくは４～１４質量部とすることができる。
　また、本発明の共重合体を調製する際に使用する全ての単量体のうちに占める単量体ａ及びｂを合わせた比率は、５０～１００ｍｏｌ％とすることが好ましく、９０～１００ｍｏｌ％とすることがさらに好ましい。本発明の効果が好ましく発現するからである。
［熱反応性単量体または光反応性単量体ｃ］
　本発明の共重合体のもう１つの形態は、前記の単量体ａ及びｂに加えて、さらに熱反応性単量体または光反応性単量体ｃを共重合させた共重合体（親水性単量体ａに基づく構成単位、シリコーン単量体ｂに基づく構成単位並びに熱反応性単量体若しくは光反応性単量体ｃに基づく構成単位を含有する共重合体）であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体である。
　本発明の熱反応性単量体または光反応性単量体ｃとは、単量体ｃを共重合させた共重合体が、加熱または光照射によって誘導され、共重合体と共存する有機物との間に炭素間共有結合を形成し得るような反応性を付与できる官能基を有する単量体を意味する。
　単量体ｃは、本発明の共重合体を用いたシリコーンハイドロゲルの調製方法が熱重合による場合には、加熱によって誘導される熱反応性単量体が好ましい。また、シリコーンハイドロゲルの調製方法が光重合による場合には、光照射によって誘導される光反応性単量体が好ましい。
　加熱によって反応性が誘導される単量体ｃの具体例としては、グリシジル（メタ）アクリレート等が好ましく挙げられる。
　光照射によって反応性が誘導される単量体ｃの具体例としては、４－（メタ）アクリロイルオキシベンゾフェノン、（アジドベンゾイルオキシメチル）ビニルベンゼン等が好ましく挙げられる。
　上記の単量体ｃの反応性を利用して、共重合体の合成後に高分子反応によって（メタ）アクリル基、ビニル基等の重合性官能基を導入することも、本発明の趣旨から可能である。
　本発明で用いる単量体ｃとしては、単一の単量体を用いてもよいし、複数の単量体を組み合わせて用いてもよい。
　本発明の共重合体を調製する際に使用する全ての単量体に占める単量体ｃの比率は、０～５０ｍｏｌ％とすることが好ましく、０～１０ｍｏｌ％とすることがさらに好ましい。本発明の効果が好ましく発現するからである。
［その他の単量体ｄ］
　本発明の、単量体ａ及びｂを共重合させた共重合体、及び単量体ａ、ｂ及びｃを共重合させた共重合体は、本発明の効果を損なわない範囲で、さらに他の単量体ｄを共重合させたものであってもよい。
　単量体ｄは、単量体ａ、ｂ及びｃと共重合可能な単量体から任意に選択できる。
　そのような単量体としては例えば、（メタ）アクリル酸及びその誘導体、（メタ）アクリルアミド及びその誘導体、ビニル化合物が好ましく挙げられる。
　（メタ）アクリル酸の誘導体としては、例えば、（メタ）アクリル酸メチル、（メタ）アクリル酸エチル等の（メタ）アクリル酸アルキル、ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレート等が好ましく挙げられる。
　（メタ）アクリルアミド誘導体としては例えば、ジメチル（メタ）アクリルアミド、ヒドロキシエチル（メタ）アクリルアミド等が好ましく挙げられる。
　ビニル化合物としては例えば、ヒドロキシエチルビニルエーテル、ヒドロキシブチルビニルエーテル等のヒドロキシアルキルビニルエーテル、ジエチレングリコールモノビニルエーテル等のオリゴエチレングリコールモノビニルエーテル、Ｎ－ビニルピロリドン等のピロリドン誘導体が好ましく挙げられる。
　単量体ｄは単一の単量体を用いてもよいし、複数の単量体を組み合わせて用いてもよい。
　本発明の共重合体を調製する際に使用する全ての単量体のうちに占める単量体ｄの比率は０～１０ｍｏｌ％とすることが好ましい。本発明の効果が好ましく発現するからである。
［共重合体の製造］
　本発明の共重合体を得るための重合方法としては、溶液重合、塊状重合、乳化重合、懸濁重合等の公知の方法を用いることができ、例えば、単量体ａ及びｂ、さらに必要に応じて単量体ｃ及びｄを溶媒中で重合開始剤の存在下で重合させる、ラジカル重合などの方法を採用することができる。
　重合反応に用いる開始剤としては、通常用いられる開始剤ならばいずれを用いてもよく、例えば、ラジカル重合の場合には脂肪族アゾ化合物、有機過酸化物、過硫酸塩等を用いることができる。これらの重合開始剤の例としては、例えば、２，２’－アゾビス（イソブチロニトリル）、２，２’－アゾビス（２，４－ジメチルヴァレロニトリル）、過酸化ベンゾイル、過酸化ラウロイル、ジイソプロピルペルオキシジカーボネート、ｔ－ブチルペルオキシ－２－エチルヘキサノエート、ｔ－ブチルペルオキシピバレート、ｔ－ブチルペルオキシジイソブチレート、過硫酸カリウム、過硫酸アンモニウム等が挙げられる。これらの重合開始剤は２種以上を混合して使用してもよい。また、重合開始剤の使用にはレドックス系のラジカル促進剤を使用してもよい。
　重合温度としては、３０～８０℃が好ましく、４０～７０℃がより好ましい。また重合時間は２～７２時間が好ましい。重合反応が良好に進行するからである。
　さらに、重合反応を円滑に行うために溶媒を用いてもよく、該溶媒としては、水、メタノール、エタノール、プロパノール等のアルコール、ベンゼン、トルエン、ジメチルホルムアミド、テトラヒドロフラン、ジオキサン、クロロホルム、またはこれらの混合溶媒を挙げることができる。
［共重合体の分子量］
　本発明の共重合体の重量平均分子量は、２０，０００～２，０００，０００とすることが好ましく、５０，０００～１，６００，０００とすることがさらに好ましく、１００，０００～１，０００，０００とすることがよりさらに好ましく、２００，０００～５００，０００が特に好ましい。重量平均分子量をこのような範囲とすることで、シリコーンハイドロゲルモノマー配合物（シリコーンハイドロゲル組成物）に相溶しやすく、かつシリコーンハイドロゲルに濡れ性と滑り性を好ましく付与することができる。
　なお、本発明の共重合体の重量平均分子量は、例えば、ＥｃｏＳＥＣシステム（東ソー株式会社製）を用いたＧＰＣ（ゲルろ過クロマトグラフィー）測定により、ポリエチレングリコール換算で求められる。
［共重合体の水溶性］
　本発明の共重合体は、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する。
　２０℃の水に１．０％（ｗ／ｖ）以上溶解する高い水溶性を有する場合は、疎水性の高いシリコーン成分を含むシリコーンハイドロゲルモノマー配合物との相溶性が損なわれる可能性が高まる。また沸水に０．１％（ｗ／ｖ）溶解しない低い水溶性では、シリコーンハイドロゲルに濡れ性を付与する効果が損なわれる可能性が高い。
　本発明の共重合体の水溶性は、例えば以下のような手順で容易に評価することができる。
（１）密栓可能な耐熱容器に、適量の共重合体を秤量する。そのような容器としては、例えばガラスバキュームバイアルが挙げられる。
（２）所定の濃度に調製すべく純水を該容器に添加する。
　例えば５．０％（ｗ／ｖ）に調製する場合は、０．５ｇの共重合体に対し、１０ｍＬの純水を添加する。
（３）２０℃条件下で攪拌し、目視で溶解性を確認する。
（４）常圧下で３０分煮沸した後攪拌し、室温に戻してから目視で溶解性を確認する。（沸水への溶解性）
　煮沸に代えて、１２１℃、２０分間オートクレーブ処理してもよい。
　なお、ここで言う「溶解」とは、目視下において、投入した共重合体の全てが水と均一に混合し、不溶分や濁り、よどみが視認できなくなる状態を指す。
　前記本発明の共重合体の水溶性は、共重合体の単量体ａ／単量体ｂ（質量比）の比の値と正の相関があり、また共重合体の重量平均分子量と負の相関がある。
　そこで、水溶性の指標ＷＳＩ（Ｗａｔｅｒ　Ｓｏｌｕｂｉｌｉｔｙ　Ｉｎｄｅｘ）を下式（４）の通り定義できる。
Figure JPOXMLDOC01-appb-M000016
 　上記のＷＳＩは５以上１，０００以下となることが好ましく、９以上７００以下とすることがさらに好ましく、２０以上３００以下とすることがよりさらに好ましい。
　ＷＳＩが上記の範囲となるとき、好ましい水溶性を有する共重合体が得やすい。
［シリコーンハイドロゲル組成物］
　本発明は、以下のシリコーンハイドロゲル組成物も対象とする。
　下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体、又は
　下記の式（１）で表される親水性単量体ａに基づく構成単位、下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位、並びに熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位を含有する共重合体であって、
　ここで、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体、並びに、
　ベース組成物を含むシリコーンハイドロゲル組成物であって、
　該共重合体は、該ベース組成物１００質量部に対して０．０５～２質量部含む、シリコーンハイドロゲル組成物。
Figure JPOXMLDOC01-appb-C000017
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000018
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000019
 （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
［シリコーンハイドロゲル］
　本発明のもう１つの形態は、ベース組成物１００質量部に対して本発明の共重合体を０．０５～２質量部含むモノマー組成物（シリコーンハイドロゲル組成物）を硬化させて得られるシリコーンハイドロゲルである。
　シリコーンハイドロゲル組成物中に占める本発明の共重合体の量は、０．１～１質量部とすることがより好ましい。これにより、シリコーンハイドロゲル組成物に好ましく相溶し、かつシリコーンハイドロゲルに濡れ性、滑り性をより好ましく付与することができる。
　以上の好適範囲を総合すると、本発明のシリコーンハイドロゲル組成物１００重量部に占める単量体ａの割合は、好ましくは多くとも２質量部となることが期待される。すなわち、従来技術よりも格段に少量のＭＰＣ型親水性単量体の配合によって、シリコーンハイドロゲルに好ましく濡れ性と滑り性を付与することができる。
　本明細書のベース組成物とは、シリコーンハイドロゲルを調製するためのモノマー、反応開始剤、及び必要に応じて添加される他の成分の混合物をいう。
　ベース組成物は、プロパノール等のアルコール、及びヒドロキシエチル（メタ）アクリレート等の水酸基含有モノマーを、合わせて１５重量部以上含むことが好ましい。本発明の共重合体の相溶性が高まるからである。
　ベース組成物に含まれる化合物の例として、プロパノール、ヘキサノール、ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート、Ｎ－ビニルピロリドン、メチル（メタ）アクリレート、テトラエチレングリコールジ（メタ）アクリレート、トリエチレングリコールジビニルエーテル、（メタ）アクリル酸、アミノエチル（メタ）アクリレート、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート、ポリジメチルシロキサンモノ（メタ）アクリレート等があるが特に限定されない。
　シリコーンハイドロゲル組成物の調製、及びこれを用いたシリコーンハイドロゲルの調製は、国際公開ＷＯ２０２０／０５４７１１号等に開示されている様な公知の方法を用いて行うことができる。
　シリコーンハイドロゲル組成物を硬化させる工程は、加熱（熱重合）または光照射（光重合）によることが好ましい。
［本発明の共重合体を含むシリコーンハイドロゲル組成物を硬化する工程を含む、シリコーンハイドロゲルの製造方法］
　本発明は、以下のシリコーンハイドロゲルの製造方法も含む。
　本発明の共重合体を含むシリコーンハイドロゲル組成物を硬化する工程を含む、シリコーンハイドロゲルの製造方法。
　該共重合体は、下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体である。
Figure JPOXMLDOC01-appb-C000020
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000021
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000022
 （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
　なお、シリコーンハイドロゲル組成物中の前記共重合体の量は、０．１～１質量部であることが好ましい。
　なお、シリコーンハイドロゲル組成物が、さらに、ベース組成物を含み、かつ該共重合体が該ベース組成物１００質量部に対して０．０５～２質量部であることが好ましい。
［本発明の共重合体を眼科デバイス用改質剤の製造としての使用］
　本発明は、以下の本発明の共重合体を眼科デバイス用改質剤の製造としての使用も含む。
　下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体を眼科デバイス用改質剤の製造としての使用。
Figure JPOXMLDOC01-appb-C000023
 （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
Figure JPOXMLDOC01-appb-C000024
 （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
Figure JPOXMLDOC01-appb-C000025
 （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
　本発明の共重合体の式（１）で表される親水性単量体ａに基づく構成単位、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位、反応性単量体もしくは光反応性単量体ｃに基づく構成単位、及び／又は、他の単量体ｄに基づく構成単位の組み合わせは、以下の表１に記載を例示することができる。
　また、当業者は、表１の記載の各構成単位の構成を適宜変更することにより、様々な構成単位を含む共重合体を得ることができる。
　以下、本発明を実施例により更に詳細に説明するが、本発明はこれらに限定されない。
［共重合体の合成］
　実施例に用いる共重合体の合成のため、表１に示す１４種の共重合体、すなわち本発明の範囲内である共重合体１－１～３－６を合成した。
［合成例１－１］
　２－メタクリロイルオキシエチルホスホリルコリン（以下、ＭＰＣと記載）２２．５ｇ、トリス（トリメチルシロキシ）シリルプロピルメタクリレート（以下、ＴＲＩＳと記載）１．０ｇ（モノマー組成モル比：ＭＰＣ／ＴＲＩＳ＝９７／３）を重合用ガラス製フラスコに秤量し、重合溶媒であるエタノール３５．３ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤として２，２’－アゾビス（２，４－ジメチルバレロニトリル）（以下、ＡＤＶＮと記載）１２ｍｇを加え、ゆっくりと６０℃に昇温してそのまま一晩６０℃に保つことで重合反応を行った。得られた反応液を大過剰のアセトンに滴下することで重合体を沈殿させた。沈殿を濾別し、アセトンで洗浄した後、真空乾燥して白色固体の共重合体１－１を得た。
　得られた共重合体１－１の重量平均分子量は、ゲル濾過クロマトグラフィー（以下、ＧＰＣと記載）測定により、ポリエチレングリコール換算で３５６，０００と決定された。
［合成例１－２］
　ＭＰＣ　２１．２ｇ、ＴＲＩＳ　２．３ｇ（モノマー組成モル比：ＭＰＣ／ＴＲＩＳ＝９３／７）を重合用ガラス製フラスコに秤量し、重合溶媒であるｎ－プロパノール（以下、ＮＰＡと記載）３５．３ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　１２ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体１－２を得た。
　得られた共重合体１－２の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で２８８，０００と決定された。
［合成例１－３］
　ＭＰＣ　１９．５ｇ、ＴＲＩＳ　４．０ｇ（モノマー組成モル比：ＭＰＣ／ＴＲＩＳ＝８７．５／１２．５）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　３５．３ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　８ｍｇを加え、その後は合成例１－１と同様にして重合と回収を行い、白色固体の共重合体１－３を得た。
　得られた共重合体１－３の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で４１１，０００と決定された。
［合成例１－４］
　ＭＰＣ　２３．１ｇ、ポリジメチルシロキサンモノメタクリレート（信越化学株式会社製、以下、ＰＤＭＳＭＡと記載）　０．５ｇ（モノマー組成モル比：ＭＰＣ／ＰＤＭＳＭＡ＝９９．４／０．６、ＰＤＭＳＭＡの数平均分子量を１，０００として計算）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　９４．１ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　６ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体１－４を得た。
　得られた共重合体１－４の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で３６４，０００と決定された。
［合成例１－５］
　ＭＰＣ　２３．１ｇ、ＰＤＭＳＭＡ　０．５ｇ（モノマー組成モル比：ＭＰＣ／ＰＤＭＳＭＡ＝９９．４／０．６）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　３５．３ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤として２，２’－アゾビス（イソブチロニトリル）（以下、ＡＩＢＮと記載）　８ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体１－５を得た。
　得られた共重合体１－５の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で１，５５０，０００と決定された。
［合成例１－６］
　ＭＰＣ　２１．４ｇ、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート（以下、ＥＴＳと記載）　２．６ｇ、ヒドロキシエチルアクリルアミド（以下、ＨＥＡＡと記載）１．０ｇ（モノマー組成モル比：ＭＰＣ／ＥＴＳ／ＨＥＡＡ＝８４／６／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　１００．０ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　６ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体１－６を得た。
　得られた共重合体１－６の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で３０１，０００と決定された。
［合成例２－１］
　ＭＰＣ　１９．０ｇ、ＴＲＩＳ　２．１ｇ、グリシジルメタクリレート（以下、ＧＭＡと記載）１．１ｇ（モノマー組成モル比：ＭＰＣ／ＴＲＩＳ／ＧＭＡ＝８４／６／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　８８．９ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　５５ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体２－１を得た。
　得られた共重合体２－１の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で７２，０００と決定された。
［合成例２－２］
　ＭＰＣ　２０．７ｇ、ＰＤＭＳＭＡ　０．４ｇ、ＧＭＡ　１．１ｇ（モノマー組成モル比：ＭＰＣ／ＰＤＭＳＭＡ／ＧＭＡ＝８９．５／０．５／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　８８．９ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　５５ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体２－２を得た。
　得られた共重合体２－２の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で１５０，０００と決定された。
［合成例３－１］
　ＭＰＣ　１８．４ｇ、ＴＲＩＳ　１．９ｇ、４－メタクリロイルオキシベンゾフェノン（以下、ＭＢＰと記載）　２．０ｇ（モノマー組成モル比：ＭＰＣ／ＴＲＩＳ／ＭＢＰ＝８４／６／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　８８．９ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　５５ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体３－１を得た。
　得られた共重合体３－１の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で７２，０００と決定された。
［合成例３－２］
　ＭＰＣ　１６．０ｇ、ＴＲＩＳ　３．３ｇ、ＭＢＰ　１．８ｇ（モノマー組成モル比：ＭＰＣ／ＴＲＩＳ／ＭＢＰ＝７９／１１／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　８４．２ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　５２ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体３－２を得た。
　得られた共重合体３－２の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で２１，０００と決定された。
［合成例３－３］
　ＭＰＣ　２１．０ｇ、ＰＤＭＳＭＡ　０．４ｇ、ＭＢＰ　２．１ｇ（モノマー組成モル比：ＭＰＣ／ＰＤＭＳＭＡ／ＭＢＰ＝８９．５／０．５／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　９４．１ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　５９ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体３－３を得た。
　得られた共重合体３－３の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で１０５，０００と決定された。
［合成例３－４］
　ＭＰＣ　２１．０ｇ、ＰＤＭＳＭＡ　０．４ｇ、ＭＢＰ　２．１ｇ（モノマー組成モル比：ＭＰＣ／ＰＤＭＳＭＡ／ＭＢＰ＝８９．５／０．５／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　３５．３ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　６ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体３－４を得た。
　得られた共重合体３－４の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で９５１，０００と決定された。
［合成例３－５］
　ＭＰＣ　２０．２ｇ、ＥＴＳ　２．５ｇ、４－（４－アジドベンゾイルオキシメチル）ビニルベンゼン（以下、ＡｚＳｔと記載）　２．３ｇ（モノマー組成モル比：ＭＰＣ／ＥＴＳ／ＡｚＳｔ＝８４／６／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　１００．０ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　６２ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体３－５を得た。
　得られた共重合体３－５の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で７０，０００と決定された。
［合成例３－６］
　ＭＰＣ　１８．４ｇ、３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート（以下、ＳｉＧＭＡと記載）１．９ｇ、ＭＢＰ　２．０ｇ（モノマー組成モル比：ＭＰＣ／ＳｉＧＭＡ／ＭＢＰ＝８４／６／１０）を重合用ガラス製フラスコに秤量し、重合溶媒であるＮＰＡ　８８．９ｇを加えて溶解させた。反応容器内を十分に窒素置換した後、重合開始剤としてＡＤＶＮ　５５ｍｇを加え、その後は合成例１－１と同様に重合と回収を行い、白色固体の共重合体３－６を得た。
　得られた共重合体３－６の重量平均分子量は、ＧＰＣ測定により、ポリエチレングリコール換算で７４，０００と決定された。
［ＧＰＣ測定］
　上記合成例１－１～３－６の各共重合体のＧＰＣ測定は以下の条件で実施した。
　ＧＰＣシステム：ＥｃｏＳＥＣシステム（東ソー株式会社製）
　カラム：Ｓｈｏｄｅｘ　ＯＨｐａｋ　ＳＢ－８０２．５ＨＱ（昭和電工株式会社製）、及びＳＢ－８０６ＨＱ（昭和電工株式会社製）を直列に接続
　展開溶媒：２０ｍＭりん酸ナトリウム緩衝液（ｐＨ　７．４）
　検出器：示差屈折率検出器
　分子量標準：ＥａｓｉＶｉａｌ　ＰＥＧ／ＰＥＯ（Ａｇｉｌｅｎｔ　Ｔｅｃｈｎｏｌｏｇｉｅｓ社製）
　流速：０．５ｍＬ／分
　カラム温度：４０℃
　サンプル：得られた共重合体を終濃度０．１重量％となるよう展開溶媒で希釈
　注入量：１００μＬ
［水溶性の判定］
　前記合成例１－１～３－６に記載の各共重合体の水溶性の判定は以下の手順で実施した。
（１）３０ｃｃガラスバイアルに、各共重合体を下記の所定濃度とすべく適量秤量した。
（２）１０ｍＬのイオン交換水を添加した。
（３）２０℃条件下で攪拌し、目視で２０℃の水への溶解性を確認した。
（４）１２１℃、２０分間オートクレーブした後攪拌し、室温に戻してから目視で沸水への溶解性を確認した。
（５）上記（１）～（４）を、０．１％（ｗ／ｖ）、０．５％（ｗ／ｖ）、１．０％（ｗ／ｖ）、５．０％（ｗ／ｖ）の濃度について行った。
（６）２０℃の水、沸水のそれぞれについて、上記４濃度のうち、溶解することが確認された最大の濃度を記録した。ただし、０．１％（ｗ／ｖ）でも溶解しなかったものについては、「×」と記録した。
　以上、合成例１－１～３－６で得られた各共重合体の水溶性、重量平均分子量を表１に記載した。
Figure JPOXMLDOC01-appb-T000026
※１
　ＭＰＣ：２－メタクリロイルオキシエチルホスホリルコリン
　ＴＲＩＳ：トリス（トリメチルシロキシ）シリルプロピルメタクリレート
　ＰＤＭＳＭＡ：ポリジメチルシロキサンモノメタクリレート
　ＥＴＳ：４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
　ＨＥＡＡ：ヒドロキシエチルアクリルアミド
　ＧＭＡ：グリシジルメタクリレート
　ＭＢＰ：メタクリロイルオキシベンゾフェノン
　ＡｚＳｔ：４－（４－アジドベンゾイルオキシメチル）ビニルベンゼン
　ＳｉＧＭＡ：３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート
　―：該当する単量体を含まない
※２
　２０℃の水、沸水（１００℃以上）のそれぞれについて、各共重合体が溶解した最大の濃度を記載（単位：％（ｗ／ｖ）。ただし、０．１％（ｗ／ｖ）溶解しなかったものについては「×」と記載。
　共重合体１－１～３－６は、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解することを確認した。
［シリコーンハイドロゲル組成物の調製］
　シリコーンハイドロゲルを調製し、後述の評価を行うことにより、本発明の共重合体の効果を検証した。
　実施例、及び比較例に用いるシリコーンハイドロゲルの調製は以下の要領で行った。
［モノマー組成物の調製］
　前記各合成例で調製した各共重合体の所定量と、表２に示す共通組成熱１～３及び光１～２の各レンズモノマーとを混合し、モノマー組成物を調製した。
　各合成例で調製した各共重合体（参照：表３）、ＮＰＡ、ヒドロキシエチルメタクリレート（以下、ＨＥＭＡと記載）を所定量秤量して混和させたあと、Ｎ－ビニルピロリドン（以下、ＮＶＰと記載）、光１及び光２ではメチルメタクリレート（以下、ＭＭＡと記載）、テトラエチレングリコールジメタクリレート（以下、ＴＥＧＤＭＡと記載）、トリエチレングリコールジビニルエーテル（以下、ＴＥＧＤＶと記載）、熱２ではメタクリル酸（以下、ＭＡと記載）、熱３ではアミノエチルメタクリレート（以下、ＡｅＭＡと記載）を所定量添加して再び混和させ、ＥＴＳを添加してまた再び混和させ、ＰＤＭＳＭＡを添加してさらに再び混和させ、最後に熱１～３では反応開始剤であるＡＩＢＮ、光１では反応開始剤である２－ヒドロキシ－２－メチル－１－フェニルプロパノン（以下、Ｏ－１１７３と記載）、光２では反応開始剤であるビス（２，４，６－トリメチルベンゾイル）フェニルホスフィンオキサイド（以下、Ｏ－８１９と記載））を添加することで調製した。
Figure JPOXMLDOC01-appb-T000027
　ＮＰＡ：ｎ－プロパノール
　ＨＥＭＡ：ヒドロキシエチルメタクリレート
　ＮＶＰ：Ｎ－ビニルピロリドン
　ＭＭＡ：メチルメタクリレート
　ＴＥＧＤＭＡ：テトラエチレングリコールジメタクリレート
　ＴＥＧＤＶ：トリエチレングリコールジビニルエーテル
　ＭＡ：メタクリル酸
　ＡｅＭＡ：アミノエチルメタクリレート（１１ｗｔ％水溶液）
　ＥＴＳ：４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
　ＰＤＭＳＭＡ：ポリジメチルシロキサンモノメタクリレート
　ＡＩＢＮ：２，２’－アゾビス（イソブチロニトリル）
　Ｏ－１１７３：２－ヒドロキシ－２－メチル－１－フェニルプロパノン
　Ｏ－８１９：ビス（２，４，６－トリメチルベンゾイル）フェニルホスフィンオキサイド
［熱硬化によるシリコーンハイドロゲルの調製］
　前記のモノマー組成物である熱１、熱２及び熱３（参照：表２）をコンタクトレンズのモデルとして円盤状に成形すべく、内寸φ１．１ｃｍ×０．１ｍｍのポリプロピレン製の鋳型に注入し、オーブン内に静置した。オーブン内を窒素置換した後、ゆっくりと８０℃に昇温し、そのまま８０℃で１２時間保温することで、熱硬化を行い、硬化物を得た。
　この硬化物を鋳型から取り出し、硬化物１枚につき４０ｇのｉｓｏ－プロパノール（以下、ＩＰＡと記載）に４時間浸漬した後、５０ｇのイオン交換水に４時間浸漬して、未反応物等を抽出除去する精製を行った。
　次に、上記の硬化物を取り出してＩＳＯ－１８３６９－３に記載の生理食塩水（以下、ＰＢＳと記載）に４時間浸漬した後、新鮮なＰＢＳに浸漬した状態でオートクレーブ滅菌し、シリコーンハイドロゲルを得た。
［光硬化によるシリコーンハイドロゲルの調製］
　前記モノマー組成物である光１及び光２（参照：表２）をコンタクトレンズのモデルとして円盤状に成形すべく、内寸φ１．１ｃｍ×０．１ｍｍのポリプロピレン製の鋳型に注入し、光照射機内に静置した。波長３６５ｎｍまたは４０５ｎｍ、照度１．５ｍＷ／ｃｍ２の光を２０分照射することで光硬化を行い、硬化物を得た。
　この後は熱硬化の場合と同様に、硬化物の取り出し、精製、滅菌を行い、シリコーンハイドロゲルを得た。
［モノマー組成物の相溶性］
　調製したモノマー組成物を透明なガラス容器に入れ、モノマー組成物の相溶性を目視により以下の基準に従って評価した。
　＋＋：均一、透明
　＋：微かな濁り、散乱
　×：濁り、沈殿
［シリコーンハイドロゲルの評価］
　調製したシリコーンハイドロゲルについて、以下の評価を行った。
［透明性］
　調製したシリコーンハイドロゲルの透明性を目視により以下の基準で判定した。
　＋＋：透明
　＋：微濁
　×：白濁
［形状］
　調製したシリコーンハイドロゲルの形状について、目視により以下の基準で判定した。
　＋＋：歪みを認めない
　＋：やや歪みを認める
　×：歪み、硬化不良を認める
［濡れ性］
　調製したシリコーンハイドロゲルの表面濡れ性について、以下の手順で評価した。
（１）ＰＢＳに漬かっている調製したシリコーンハイドロゲルを、ピンセットを用いて空中に取り出した。
（２）シリコーンハイドロゲルの表面を目視で観察し、取り出してから表面の水膜が切れ始めるまでの時間［秒］（ＢＵＴ）を測定した。すなわち、ＢＵＴが長いほど、表面濡れ性が高いものとして評価した。
（３）以下の基準に従って判定した。
　＋＋＋：３０秒≦ＢＵＴ
　＋＋：１０秒≦ＢＵＴ＜３０秒
　＋：５秒≦ＢＵＴ＜１０秒
　×：ＢＵＴ＜５秒
［滑り性］
　調製したシリコーンハイドロゲルの表面滑り性について、以下の手順で評価した。
（１）シリコーンハイドロゲルレンズを親指と中指でつまんだ。
（２）官能評価により、Ｐｏｌｙｍａｃｏｎの滑り性を２点、Ｏｍａｆｉｌｃｏｎ　Ａの滑り性を８点として０～１０点の評点を付した。すなわち、評点が高いほど、滑り性が高いことを示す。
（３）以下の基準に従って判定した。
　＋＋＋：８点～１０点
　＋＋：５点～７点
　＋：３～４点
　×：０～２点
［実施例１－１～１－５］
　単量体ｂが前記式（２）で表される共重合体１－１～１－３のそれぞれをシリコーンハイドロゲル組成物に添加した場合の、得られるシリコーンハイドロゲルについて評価した。なお、共通組成は熱１を用い、硬化は熱硬化によった。
［実施例１－６～１－７］
　共重合体１－４～１－５のそれぞれをシリコーンハイドロゲル組成物に添加した場合の、得られるシリコーンハイドロゲルについて評価した。なお、共通組成は熱１を用い、硬化は熱硬化によった。
［実施例１－８］
　共重合体１－６をシリコーンハイドロゲル組成物に添加した場合の、得られるシリコーンハイドロゲルについて評価した。なお、共通組成は熱１を用い、硬化は熱硬化によった。
［実施例２－１～２－４］
　表３に記載の共重合体、共通組成、硬化方法を用いて、実施例１と同様に、得られるシリコーンハイドロゲルについて評価した。
［実施例３－１～３－８］
　表３に記載の共重合体、共通組成を用いて、実施例１と同様に、得られるシリコーンハイドロゲルについて評価した。なお、硬化は波長３６５ｎｍ、照度１．５ｍＷ／ｃｍ２の紫外光を照射することにより実施した。
［実施例３－９］
　表３に記載の共重合体、共通組成を用いて、実施例１と同様に、得られるシリコーンハイドロゲルについて評価した。なお、硬化は波長４０５ｎｍ、照度１．５ｍＷ／ｃｍ２の紫色光を照射することにより実施した。
　以上の手順で行ったシリコーンハイドロゲルの調製、及びその評価結果を表３に記載した。
Figure JPOXMLDOC01-appb-T000028
Figure JPOXMLDOC01-appb-T000029
Figure JPOXMLDOC01-appb-T000030
※１
　ＭＰＣ：２－メタクリロイルオキシエチルホスホリルコリン
　ＴＲＩＳ：トリス（トリメチルシロキシ）シリルプロピルメタクリレート
　ＰＤＭＳＭＡ：ポリジメチルシロキサンモノメタクリレート
　ＥＴＳ：４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
　ＨＥＡＡ：ヒドロキシエチルアクリルアミド
　ＧＭＡ：グリシジルメタクリレート
　ＭＢＰ：４－メタクリロイルオキシベンゾフェノン
　ＡｚＳｔ：（アジドベンゾイルオキシメチル）ビニルベンゼン
　ＳｉＧＭＡ：３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート
※２
　２０℃１％（ｗ／ｖ）、及び沸水０．１％（ｗ／ｖ）の各条件で、水溶性が認められたものは○、認められなかったものは×を付した。
［比較例１－１～２－３］
　本発明の共重合体を用いない対照試験として、表４に示す７種のシリコーンハイドロゲルを実施例と同様の方法で調製し、実施例と同様の方法で評価した。
Figure JPOXMLDOC01-appb-T000031
　ＭＰＣ：２－メタクリロイルオキシエチルホスホリルコリン
　表３及び表４の結果より、実施例１－１～３－９のシリコーンハイドロゲルは、優れた相溶性、透明性及び形状を有し、さらに、高い濡れ性及び滑り性を同時に示したのに対し、比較例１－１～２－３は本発明の共重合体を含まないため、濡れ性及び滑り性のいずれか又は両方が低かった。比較例１－２及び２－２は、本発明の共重合体に代えて、ＭＰＣをモノマーとして配合しても濡れ性及び滑り性の両方が低かった。
　以上の実施例及び比較例より、本発明の眼科デバイス用改質剤を用いることで、シリコーンハイドロゲルの濡れ性、滑り性を好適に改善できることが明らかである。
　本発明の眼科デバイス用改質剤を含むシリコーンハイドロゲル組成物を硬化させて得られるシリコーンハイドロゲルを用いて、コンタクトレンズ、眼内レンズ、人口角膜等を例とする眼科デバイスが提供できる。

Claims (8)

  1. 　下記の式（１）で表される親水性単量体ａに基づく構成単位、並びに下記の式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位を含有する共重合体であって、２０℃の水に１．０％（ｗ／ｖ）溶解しないが、沸水に０．１％（ｗ／ｖ）以上溶解する共重合体を含む眼科デバイス用改質剤。
    Figure JPOXMLDOC01-appb-C000001
     （式（１）中、Ｒ１は水素原子またはメチル基を表し、Ｌ１は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ２～Ｒ４はそれぞれ独立して炭素数１～３の炭化水素基を表す。）
    Figure JPOXMLDOC01-appb-C000002
     （式（２）中、Ｘ１は（メタ）アクリロイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－２－メチレンプロパノイルオキシ基、３－（２－ヒドロキシエチルオキシカルボニル）－３－ブテノイルオキシ基または３－（２－ヒドロキシエチルオキシカルボニル）－２－プロペノイルオキシ基を表し、Ｌ２は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、Ｒ５～Ｒ１３はそれぞれ独立してメチル基またはエチル基を表し、ｎ１は０または１を表す。）
    Figure JPOXMLDOC01-appb-C000003
     （式（３）中、Ｒ１４は水素原子またはメチル基を表し、Ｌ３は炭素数２～６の有機基を表し、ここで該有機基は任意に１個のエーテル結合および／または１個のヒドロキシ基を含んでもよく、ｎ２は４～２０の整数を表し、Ｒ１５～Ｒ１７はそれぞれ独立して炭素数１～８のアルキル基を表す。）
  2. 　前記共重合体が、熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位をさらに含有する、請求項１に記載の眼科デバイス用改質剤。
     
  3. 　前記式（１）で表される親水性単量体ａに基づく構成単位が２－メタクリロイルオキシエチルホスホリルコリンであり、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位がトリス（トリメチルシロキシ）シリルプロピルメタクリレート、ポリジメチルシロキサンモノメタクリレート、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート若しくは３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレートであり、並びに、熱反応性単量体もしくは光反応性単量体ｃに基づく構成単位がグリシジルメタクリレート、メタクリロイルオキシベンゾフェノン若しくは４－（４－アジドベンゾイルオキシメチル）ビニルベンゼンである、請求項２に記載の眼科デバイス用改質剤。
     
  4. 　前記式（１）で表される親水性単量体ａに基づく構成単位、前記式（２）または式（３）で表されるシリコーン単量体ｂに基づく構成単位、及び／又は、反応性単量体もしくは光反応性単量体ｃに基づく構成単位の組み合わせは、以下のいずれか１から選択される、請求項２に記載の眼科デバイス用改質剤。
    　１）２－メタクリロイルオキシエチルホスホリルコリン及びトリス（トリメチルシロキシ）シリルプロピルメタクリレート
    　２）２－メタクリロイルオキシエチルホスホリルコリン及びポリジメチルシロキサンモノメタクリレート
    　３）２－メタクリロイルオキシエチルホスホリルコリン及び４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート
    　４）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びグリシジルメタクリレート
    　５）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びグリシジルメタクリレート
    　６）２－メタクリロイルオキシエチルホスホリルコリン、トリス（トリメチルシロキシ）シリルプロピルメタクリレート及びメタクリロイルオキシベンゾフェノン
    　７）２－メタクリロイルオキシエチルホスホリルコリン、ポリジメチルシロキサンモノメタクリレート及びメタクリロイルオキシベンゾフェノン
    　８）２－メタクリロイルオキシエチルホスホリルコリン、４－（２－ヒドロキシエチル）－２－メチレン－１－（トリス（トリメチルシロキシ）シリルプロピル）ブタン－１，４－ジオエート及び４－（４－アジドベンゾイルオキシメチル）ビニルベンゼン、及び
    　９）２－メタクリロイルオキシエチルホスホリルコリン、３－（３－（メチルビス（トリメチルシロキシ）シリル）プロピル）グリセロール－１－メタクリレート及びメタクリロイルオキシベンゾフェノン
  5. 　請求項１または２記載の共重合体並びにベース組成物を含む、シリコーンハイドロゲル組成物であって、
    　該共重合体が該ベース組成物１００質量部に対して０．０５～２質量部含まれる、シリコーンハイドロゲル組成物。
  6. 　請求項５に記載のシリコーンハイドロゲル組成物を硬化させて得られるシリコーンハイドロゲル。
  7. 　請求項６に記載のシリコーンハイドロゲルを用いた眼科デバイス。
  8. 　ソフトコンタクトレンズである請求項７に記載の眼科デバイス。
PCT/JP2021/042877 2020-12-01 2021-11-24 眼科デバイス用改質剤 WO2022118697A1 (ja)