WO2021125729A1 - Tôle d'acier ayant une excellente résistance à l'usure et une excellente résistance à la corrosion des composites, et son procédé de fabrication - Google Patents
Tôle d'acier ayant une excellente résistance à l'usure et une excellente résistance à la corrosion des composites, et son procédé de fabrication Download PDFInfo
- Publication number
- WO2021125729A1 WO2021125729A1 PCT/KR2020/018284 KR2020018284W WO2021125729A1 WO 2021125729 A1 WO2021125729 A1 WO 2021125729A1 KR 2020018284 W KR2020018284 W KR 2020018284W WO 2021125729 A1 WO2021125729 A1 WO 2021125729A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel sheet
- corrosion
- hot
- equation
- weight
- Prior art date
Abstract
La présente invention concerne une tôle d'acier ayant une excellente résistance à l'usure et une excellente résistance à la corrosion des composites, et son procédé de fabrication. Une tôle d'acier résistant à la corrosion selon un mode de réalisation de la présente invention comprend, en % en poids : 0,04 à 0,10 % de carbone (C); 0,1 % ou moins (à l'exclusion de 0 %) de silicium (Si); 0,20 à 0,35 % de cuivre (Cu); 0,1 à 0,2 % de nickel (Ni); 0,05 à 0,15 % d'antimoine (Sb); 0,07 à 0,22 % d'étain (Sn); 0,05 à 0,15 % de titane (Ti); 0,01 % ou moins (à l'exclusion de 0 %) de soufre (S); 0,005 % ou moins (à l'exclusion de 0 %) d'azote (N), le reste étant du fer (Fe) et les inévitables impuretés, et satisfaisant à la formule 1 et à la formule 2 ci-dessous. [Formule 1] [Ni]/ [Cu] ≥ 0,5; et [Formule 2] 48 x ( [Ti]/48 - [S]/32 - [N]/14) ≥ 0,04. Dans les formules 1 et 2, [Ni], [Cu], [Ti], [S], et [N] représentent respectivement la teneur (% en poids) en Ni, Cu, Ti, S et N dans la tôle d'acier.
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2022538262A JP2023507661A (ja) | 2019-12-19 | 2020-12-14 | 耐摩耗性と複合耐食性に優れた鋼板およびその製造方法 |
US17/785,846 US20230033491A1 (en) | 2019-12-19 | 2020-12-14 | Steel plate having excellent wear resistance and composite corrosion resistance and method for manufacturing same |
CN202080097198.3A CN115135797B (zh) | 2019-12-19 | 2020-12-14 | 耐磨性和复合耐蚀性优异的钢板及其制造方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020190170978A KR102326323B1 (ko) | 2019-12-19 | 2019-12-19 | 내마모성과 복합내식성이 우수한 강판 및 그 제조방법 |
KR10-2019-0170978 | 2019-12-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2021125729A1 true WO2021125729A1 (fr) | 2021-06-24 |
Family
ID=76477759
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2020/018284 WO2021125729A1 (fr) | 2019-12-19 | 2020-12-14 | Tôle d'acier ayant une excellente résistance à l'usure et une excellente résistance à la corrosion des composites, et son procédé de fabrication |
Country Status (5)
Country | Link |
---|---|
US (1) | US20230033491A1 (fr) |
JP (1) | JP2023507661A (fr) |
KR (1) | KR102326323B1 (fr) |
CN (1) | CN115135797B (fr) |
WO (1) | WO2021125729A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20130143375A (ko) * | 2012-06-21 | 2013-12-31 | 주식회사 포스코 | 황산내식성 및 표면특성이 우수한 냉연강판 및 그 제조방법 |
JP2015113506A (ja) * | 2013-12-12 | 2015-06-22 | Jfeスチール株式会社 | 耐食性に優れる原油タンク用鋼材および原油タンク |
KR101657787B1 (ko) * | 2014-12-04 | 2016-09-20 | 주식회사 포스코 | 황산 내식성 및 법랑 밀착성이 우수한 강판 및 그 제조방법 |
WO2019003856A1 (fr) * | 2017-06-30 | 2019-01-03 | Jfeスチール株式会社 | Matériau d'acier structural et structure |
KR20190062480A (ko) * | 2016-10-06 | 2019-06-05 | 제이에프이 스틸 가부시키가이샤 | 선박 밸러스트 탱크용 강재 및 선박 |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4427207B2 (ja) * | 2001-05-01 | 2010-03-03 | 新日本製鐵株式会社 | 冷間加工性、高温特性、耐低温腐食性に優れた鋼およびその製造方法 |
JP4904847B2 (ja) * | 2006-02-24 | 2012-03-28 | Jfeスチール株式会社 | 耐酸腐食性に優れる鋼材 |
JP5278226B2 (ja) * | 2009-07-29 | 2013-09-04 | 新日鐵住金株式会社 | 省合金型高強度熱延鋼板及びその製造方法 |
WO2016190467A1 (fr) * | 2015-05-28 | 2016-12-01 | 주식회사 포스코 | Tôle d'acier laminée à chaud ayant une excellente résistance combinée à la corrosion par l'acide sulfurique et l'acide chlorhydrique et son procédé de fabrication |
JP6515282B2 (ja) * | 2015-07-01 | 2019-05-22 | 日本製鉄株式会社 | 酸性環境用耐食鋼材及び防食方法 |
KR101746404B1 (ko) * | 2015-12-23 | 2017-06-14 | 주식회사 포스코 | 내식성 및 가공성이 향상된 린 듀플렉스 스테인리스강 및 이의 제조 방법 |
JP7127355B2 (ja) * | 2018-05-11 | 2022-08-30 | 日本製鉄株式会社 | 鋼材 |
WO2020111782A1 (fr) * | 2018-11-30 | 2020-06-04 | 주식회사 포스코 | Tôle d'acier présentant une résistance à la corrosion dans une atmosphère de condensation de complexe acide sulfurique/acide chlorhydrique à faible concentration et son procédé de fabrication |
KR20200065990A (ko) * | 2018-11-30 | 2020-06-09 | 주식회사 포스코 | 황산 및 황산/염산 복합 응축 환경에서 내식성을 갖는 강판 및 그 제조방법 |
CN109576591B (zh) * | 2019-02-12 | 2020-03-31 | 鞍钢股份有限公司 | 一种700MPa级冷轧耐蚀双相钢及其制造方法 |
-
2019
- 2019-12-19 KR KR1020190170978A patent/KR102326323B1/ko active IP Right Grant
-
2020
- 2020-12-14 US US17/785,846 patent/US20230033491A1/en active Pending
- 2020-12-14 JP JP2022538262A patent/JP2023507661A/ja active Pending
- 2020-12-14 CN CN202080097198.3A patent/CN115135797B/zh active Active
- 2020-12-14 WO PCT/KR2020/018284 patent/WO2021125729A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20130143375A (ko) * | 2012-06-21 | 2013-12-31 | 주식회사 포스코 | 황산내식성 및 표면특성이 우수한 냉연강판 및 그 제조방법 |
JP2015113506A (ja) * | 2013-12-12 | 2015-06-22 | Jfeスチール株式会社 | 耐食性に優れる原油タンク用鋼材および原油タンク |
KR101657787B1 (ko) * | 2014-12-04 | 2016-09-20 | 주식회사 포스코 | 황산 내식성 및 법랑 밀착성이 우수한 강판 및 그 제조방법 |
KR20190062480A (ko) * | 2016-10-06 | 2019-06-05 | 제이에프이 스틸 가부시키가이샤 | 선박 밸러스트 탱크용 강재 및 선박 |
WO2019003856A1 (fr) * | 2017-06-30 | 2019-01-03 | Jfeスチール株式会社 | Matériau d'acier structural et structure |
Also Published As
Publication number | Publication date |
---|---|
KR102326323B1 (ko) | 2021-11-12 |
CN115135797A (zh) | 2022-09-30 |
KR20210078976A (ko) | 2021-06-29 |
CN115135797B (zh) | 2023-09-22 |
US20230033491A1 (en) | 2023-02-02 |
JP2023507661A (ja) | 2023-02-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2018117543A1 (fr) | Tôle d'acier plaquée par pressage à chaud dotée d'une résistance élevée aux chocs, élément de moulage par pressage à chaud et son procédé de fabrication | |
WO2015099221A1 (fr) | Feuille d'acier ayant une résistance élevée et une basse densité et son procédé de fabrication | |
WO2017105064A1 (fr) | Tôle en acier galvanisé à chaud à haute résistance ayant d'excellentes qualité de surface et soudabilité par points, et procédé de fabrication de celle-ci | |
WO2019231023A1 (fr) | Tôle d'acier plaquée d'alliage al-fe destinée à un formage à chaud, présentant d'excellentes caractéristiques de soudage twb, élément de formage à chaud et procédés de fabrication s'y rapportant | |
WO2017105025A1 (fr) | Tôle d'acier de très haute résistance présentant une excellente aptitude au traitement de conversion chimique et au traitement par pliage et son procédé de fabrication | |
WO2017105026A1 (fr) | Tôle d'acier de très haute résistance présentant une excellente aptitude au traitement de conversion chimique et d'expansion de trou et son procédé de fabrication | |
WO2013081422A1 (fr) | Acier inoxydable duplex pauvre et son procédé de fabrication | |
WO2018117724A1 (fr) | Tôle d'acier laminée à chaud de résistance élevée et tôle d'acier laminée à froid d'excellente productivité continue, tôle d'acier galvanisée par immersion à chaud de résistance élevée présentant une excellente qualité de surface et une excellente adhérence de plaquage, et son procédé de fabrication | |
WO2017082621A1 (fr) | Tôle d'acier électrique à grains orientés et son procédé de fabrication | |
WO2020060051A1 (fr) | Tôle d'acier inoxydable ferritique laminée à chaud et non recuite ayant une excellente solidité au choc, et son procédé de fabrication | |
WO2020130675A1 (fr) | Tôle d'acier laminée à froid à haute résistance possédant une excellente aptitude au cintrage, et procédé de fabrication associé | |
WO2022086050A1 (fr) | Tôle d'acier à ultra-haute résistance présentant une excellente ductilité et son procédé de fabrication | |
WO2016104837A1 (fr) | Tôle d'acier laminée à chaud pour tôle d'acier galvanisée à haute résistance, ayant une excellente qualité de surface, et son procédé de production | |
WO2018110906A1 (fr) | Feuillard d'acier à haute teneur en carbone laminé à chaud offrant une excellente qualité de surface, et son procédé de fabrication | |
WO2020111889A1 (fr) | Tôle d'acier présentant une résistance à la corrosion dans des environnements de condensation d'acide sulfurique et d'acide sulfurique/acide chlorhydrique et son procédé de fabrication | |
WO2019124781A1 (fr) | Tôle d'acier revêtue d'un placage à base de zinc ayant une excellente résistance au vieillissement à température ambiante et une excellente aptitude au durcissement par cuisson, et son procédé de fabrication | |
WO2020111782A1 (fr) | Tôle d'acier présentant une résistance à la corrosion dans une atmosphère de condensation de complexe acide sulfurique/acide chlorhydrique à faible concentration et son procédé de fabrication | |
WO2016104838A1 (fr) | Tôle d'acier laminée à chaud pour tôle d'acier galvanisé haute résistance, présentant une excellente qualité de surface, et son procédé de production | |
WO2020226301A1 (fr) | Feuille d'acier très haute résistance offrant une excellente ouvrabilité de cisaillement et son procédé de fabrication | |
WO2021125729A1 (fr) | Tôle d'acier ayant une excellente résistance à l'usure et une excellente résistance à la corrosion des composites, et son procédé de fabrication | |
WO2020085888A1 (fr) | Tôle d'acier à haute résistance ayant une excellente résistance à la fissuration par contrainte de sulfure, et son procédé de fabrication | |
WO2021125730A2 (fr) | Tôle d'acier ayant une excellente résistance à l'usure et une excellente résistance à la corrosion des composites, et son procédé de fabrication | |
WO2022097965A1 (fr) | Tôles d'acier plaquées destinées au formage à la presse à chaud présentant d'excellentes propriétés de résistance aux chocs et de résistance à la fragilisation par l'hydrogène, éléments formés à la presse à chaud, et procédés de fabrication associés | |
WO2022086049A1 (fr) | Tôle d'acier à haute résistance présentant une excellente stabilité thermique, et son procédé de fabrication | |
WO2018117539A1 (fr) | Tôle d'acier laminée à chaud à haute résistance ayant d'excellentes soudabilité et ductilité et son procédé de fabrication |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 20901957 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2022538262 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 20901957 Country of ref document: EP Kind code of ref document: A1 |