WO2020246154A1 - Procédé de production de polyuréthane et procédé de production d'un film de finition pour carte de câblage souple - Google Patents
Procédé de production de polyuréthane et procédé de production d'un film de finition pour carte de câblage souple Download PDFInfo
- Publication number
- WO2020246154A1 WO2020246154A1 PCT/JP2020/016908 JP2020016908W WO2020246154A1 WO 2020246154 A1 WO2020246154 A1 WO 2020246154A1 JP 2020016908 W JP2020016908 W JP 2020016908W WO 2020246154 A1 WO2020246154 A1 WO 2020246154A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyurethane
- polyol compound
- compound
- curable composition
- producing
- Prior art date
Abstract
L'invention concerne un procédé de production d'un polyuréthane capable de donner une composition durcissable à partir de laquelle il est possible de former une carte de câblage souple qui présente un faible gauchissement et supprime la déconnexion de câblage. Un polyuréthane est produit par réaction d'un composé polyisocyanate I avec un premier composé polyol H1, un deuxième composé polyol H2 et un troisième composé polyol H3. Le premier composé polyol H1 a une densité de cycle aromatique supérieure à celle du deuxième composé polyol H2, et le premier composé polyol H1 et le deuxième composé polyol H2 ont chacun une constante de vitesse de réaction plus élevée pour une réaction de formation de liaison uréthane que le troisième composé polyol H3. La totalité du composé polyisocyanate I, la totalité du premier composé polyol H1 et une partie du troisième composé polyol H3 sont mélangés et une réaction de polymérisation est induite pour obtenir un polymère intermédiaire, puis la totalité du deuxième composé polyol H2 et le reste du troisième polyol H3 sont ajoutés au polymère intermédiaire et une autre réaction de polymérisation est induite.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2019104580 | 2019-06-04 | ||
JP2019-104580 | 2019-06-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2020246154A1 true WO2020246154A1 (fr) | 2020-12-10 |
Family
ID=73652765
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2020/016908 WO2020246154A1 (fr) | 2019-06-04 | 2020-04-17 | Procédé de production de polyuréthane et procédé de production d'un film de finition pour carte de câblage souple |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2020246154A1 (fr) |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2008201877A (ja) * | 2007-02-19 | 2008-09-04 | Adeka Corp | ノンクロム処理金属材塗料用水系ポリウレタン樹脂組成物、及び該ポリウレタン樹脂組成物を含有する水系ノンクロム処理金属材用塗料 |
JP2008208281A (ja) * | 2007-02-28 | 2008-09-11 | Toyo Ink Mfg Co Ltd | ウレタン樹脂およびその製造方法、ならびにウレタン樹脂含有粘着剤 |
JP2009280686A (ja) * | 2008-05-21 | 2009-12-03 | Hitachi Chem Co Ltd | 熱硬化性樹脂組成物 |
JP2014189746A (ja) * | 2013-03-28 | 2014-10-06 | Dic Corp | ウレタン樹脂組成物、プライマー、積層体及び画像表示装置 |
WO2017110591A1 (fr) * | 2015-12-25 | 2017-06-29 | 昭和電工株式会社 | Nouvelle composition durcissable, de polyuréthane, film de protection, et carte de circuit imprimé souple et son procédé de production |
WO2017110326A1 (fr) * | 2015-12-25 | 2017-06-29 | 昭和電工株式会社 | Composition durcissable, objet durci, film de couverture avec dépassement, carte de câblage flexible revêtue, et procédé de production associé |
-
2020
- 2020-04-17 WO PCT/JP2020/016908 patent/WO2020246154A1/fr active Application Filing
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2008201877A (ja) * | 2007-02-19 | 2008-09-04 | Adeka Corp | ノンクロム処理金属材塗料用水系ポリウレタン樹脂組成物、及び該ポリウレタン樹脂組成物を含有する水系ノンクロム処理金属材用塗料 |
JP2008208281A (ja) * | 2007-02-28 | 2008-09-11 | Toyo Ink Mfg Co Ltd | ウレタン樹脂およびその製造方法、ならびにウレタン樹脂含有粘着剤 |
JP2009280686A (ja) * | 2008-05-21 | 2009-12-03 | Hitachi Chem Co Ltd | 熱硬化性樹脂組成物 |
JP2014189746A (ja) * | 2013-03-28 | 2014-10-06 | Dic Corp | ウレタン樹脂組成物、プライマー、積層体及び画像表示装置 |
WO2017110591A1 (fr) * | 2015-12-25 | 2017-06-29 | 昭和電工株式会社 | Nouvelle composition durcissable, de polyuréthane, film de protection, et carte de circuit imprimé souple et son procédé de production |
WO2017110326A1 (fr) * | 2015-12-25 | 2017-06-29 | 昭和電工株式会社 | Composition durcissable, objet durci, film de couverture avec dépassement, carte de câblage flexible revêtue, et procédé de production associé |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN108368336B (zh) | 固化性组合物、固化物、外涂膜、覆盖柔性配线板及其制造方法 | |
KR101276986B1 (ko) | (폴리)카르보네이트 폴리올 및 상기 (폴리)카르보네이트 폴리올을 원료로 하는 카르복실기 함유 폴리우레탄 | |
JP6901973B2 (ja) | 新規ポリウレタン、硬化性組成物、オーバーコート膜ならびにフレキシブル配線板およびその製造方法 | |
KR101503987B1 (ko) | 열경화성 조성물 | |
WO2017183497A1 (fr) | Composition durcissable, film durci utilisant ladite composition et film de finition | |
KR101271999B1 (ko) | 카르복실기 함유 폴리우레탄 | |
WO2010073981A1 (fr) | Composition durcissable | |
WO2021005914A1 (fr) | Objet durci, film de couverture, et carte de circuit imprimé souple | |
WO2020246154A1 (fr) | Procédé de production de polyuréthane et procédé de production d'un film de finition pour carte de câblage souple | |
WO2020246221A1 (fr) | Procédé de production de polyuréthane et procédé de production d'un film de revêtement pour carte de câblage souple | |
JP2021012123A (ja) | 硬化物特性値推定方法 | |
JP6882263B2 (ja) | 硬化性組成物、該組成物を用いる硬化膜およびオーバーコート膜 | |
WO2020137347A1 (fr) | Procédé pour la production de polyuréthane, procédé pour la production de composition durcissable, procédé pour la production de produit durci, procédé pour la production de film de recouvrement et procédé pour la production de carte de câblage souple | |
TWI757764B (zh) | 聚胺基甲酸酯及硬化性組成物 | |
JP7521814B2 (ja) | 硬化性組成物、硬化物、オーバーコート膜、並びにフレキシブル配線板及びその製造方法 | |
JP2021011545A (ja) | ポリウレタン及び硬化性組成物 | |
JP2021095478A (ja) | ポリウレタン及び硬化性組成物 | |
JP2021095458A (ja) | ポリウレタン及び硬化性組成物 | |
JP2021127375A (ja) | ポリウレタン及び硬化性組成物 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 20817733 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 20817733 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: JP |