WO2020223638A1 - Milieu filtrant comprenant une couche de nanofibres de polyamide - Google Patents

Milieu filtrant comprenant une couche de nanofibres de polyamide Download PDF

Info

Publication number
WO2020223638A1
WO2020223638A1 PCT/US2020/031038 US2020031038W WO2020223638A1 WO 2020223638 A1 WO2020223638 A1 WO 2020223638A1 US 2020031038 W US2020031038 W US 2020031038W WO 2020223638 A1 WO2020223638 A1 WO 2020223638A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
polyamide
filter media
nanofiber
filter
Prior art date
Application number
PCT/US2020/031038
Other languages
English (en)
Inventor
Wai-Shing Yung
Scott E. Osborn
Joseph L. Menner
Albert E. Ortega
Original Assignee
Ascend Performance Materials Operations Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ascend Performance Materials Operations Llc filed Critical Ascend Performance Materials Operations Llc
Priority to KR1020217039357A priority Critical patent/KR20210153137A/ko
Priority to JP2021564444A priority patent/JP7340037B2/ja
Priority to CN202080027843.4A priority patent/CN113710344A/zh
Priority to MX2021013375A priority patent/MX2021013375A/es
Priority to EP20727779.9A priority patent/EP3962626A1/fr
Priority to CA3138150A priority patent/CA3138150C/fr
Priority to BR112021020488A priority patent/BR112021020488A2/pt
Publication of WO2020223638A1 publication Critical patent/WO2020223638A1/fr

Abstract

L'invention concerne un milieu filtrant comprenant une couche de nanofibres de polyamide. Le polyamide peut avoir une Viscosité Relative de 2 à 200 . La couche de nanofibres de polyamide peut avoir un point de fusion de 225C ou plus. Les nanofibres peuvent avoir un diamètre de fibre moyen inférieur à 1000 nanomètres (1 micron). L'invention concerne également des procédés pour préparer le milieu filtrant. En général, le procédé comprend les étapes suivantes : (a) la fourniture d'une composition de polymère de polyamide filable, le polyamide ayant une Viscosité Relative de 2 à 200 ; (b) le filage à l'état fondu de la composition de polymère de polyamide en une pluralité de nanofibres ayant un diamètre moyen de fibre inférieur à 1 micron, suivi de (c) la formation de la couche de nanofibres de polyamide.
PCT/US2020/031038 2019-05-01 2020-05-01 Milieu filtrant comprenant une couche de nanofibres de polyamide WO2020223638A1 (fr)

Priority Applications (7)

Application Number Priority Date Filing Date Title
KR1020217039357A KR20210153137A (ko) 2019-05-01 2020-05-01 폴리아마이드 나노섬유 층을 포함하는 필터 매체
JP2021564444A JP7340037B2 (ja) 2019-05-01 2020-05-01 ポリアミドナノファイバー層を含むろ過媒体
CN202080027843.4A CN113710344A (zh) 2019-05-01 2020-05-01 包含聚酰胺纳米纤维层的过滤介质
MX2021013375A MX2021013375A (es) 2019-05-01 2020-05-01 Medios de filtro que comprenden una capa de nanofibra de poliamida.
EP20727779.9A EP3962626A1 (fr) 2019-05-01 2020-05-01 Milieu filtrant comprenant une couche de nanofibres de polyamide
CA3138150A CA3138150C (fr) 2019-05-01 2020-05-01 Milieu filtrant comprenant une couche de nanofibres de polyamide
BR112021020488A BR112021020488A2 (pt) 2019-05-01 2020-05-01 Meio filtrante compreendendo camada de nanofibra de poliamida

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201962841485P 2019-05-01 2019-05-01
US62/841,485 2019-05-01

Publications (1)

Publication Number Publication Date
WO2020223638A1 true WO2020223638A1 (fr) 2020-11-05

Family

ID=70802948

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2020/031038 WO2020223638A1 (fr) 2019-05-01 2020-05-01 Milieu filtrant comprenant une couche de nanofibres de polyamide

Country Status (9)

Country Link
EP (1) EP3962626A1 (fr)
JP (1) JP7340037B2 (fr)
KR (1) KR20210153137A (fr)
CN (1) CN113710344A (fr)
BR (1) BR112021020488A2 (fr)
CA (1) CA3138150C (fr)
MX (1) MX2021013375A (fr)
TW (1) TWI758722B (fr)
WO (1) WO2020223638A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU205640U1 (ru) * 2020-12-03 2021-07-26 Ольга Александровна Лещинская Электростатический фильтр
CN114889252A (zh) * 2022-04-29 2022-08-12 广东埃力生高新科技有限公司 一种气凝胶-双组分针刺纤维毡的复合材料及其制备方法和应用

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102018103682A1 (de) * 2018-02-19 2019-08-22 Twe Gmbh & Co. Kg Filtermedium
CN114713051B (zh) * 2022-03-28 2023-06-27 金发科技股份有限公司 聚酰胺膜、光修复聚酰胺膜的制备方法和应用
CN115487586B (zh) * 2022-09-19 2024-05-07 上海聚蓝水处理科技有限公司 电晶膜复合滤芯

Citations (112)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US425189A (en) 1890-04-08 Gar-coupling
US3016599A (en) 1954-06-01 1962-01-16 Du Pont Microfiber and staple fiber batt
US3288299A (en) 1963-07-05 1966-11-29 Fram Corp Oil filter cartridge
US3431611A (en) 1966-09-16 1969-03-11 Gen Electric Method for forming nonwoven electric blanket shells
US3525124A (en) 1965-08-13 1970-08-25 Werner & Pfleiderer Extracting apparatus for processing material having eliminable components
US3676242A (en) 1969-08-13 1972-07-11 Exxon Research Engineering Co Method of making a nonwoven polymer laminate
US3704198A (en) 1969-10-09 1972-11-28 Exxon Research Engineering Co Nonwoven polypropylene mats of increased strip tensile strength
US3755527A (en) 1969-10-09 1973-08-28 Exxon Research Engineering Co Process for producing melt blown nonwoven synthetic polymer mat having high tear resistance
US3841953A (en) 1970-12-31 1974-10-15 Exxon Research Engineering Co Nonwoven mats of thermoplastic blends by melt blowing
US3849241A (en) 1968-12-23 1974-11-19 Exxon Research Engineering Co Non-woven mats by melt blowing
US3878014A (en) 1973-04-30 1975-04-15 Beloit Corp Process for matting melt blow microfibers
US3912631A (en) 1972-06-09 1975-10-14 William C Turman Oil filter and adapter
US3978185A (en) 1968-12-23 1976-08-31 Exxon Research And Engineering Company Melt blowing process
US4011067A (en) 1974-01-30 1977-03-08 Minnesota Mining And Manufacturing Company Filter medium layered between supporting layers
US4082476A (en) 1977-04-06 1978-04-04 Fridrikh Lvovich Kopelev Machine for precision boring operations
US4100324A (en) 1974-03-26 1978-07-11 Kimberly-Clark Corporation Nonwoven fabric and method of producing same
US4118531A (en) 1976-08-02 1978-10-03 Minnesota Mining And Manufacturing Company Web of blended microfibers and crimped bulking fibers
US4127706A (en) 1974-09-26 1978-11-28 Imperial Chemical Industries Limited Porous fluoropolymeric fibrous sheet and method of manufacture
US4174358A (en) 1975-05-23 1979-11-13 E. I. Du Pont De Nemours And Company Tough thermoplastic nylon compositions
US4215682A (en) 1978-02-06 1980-08-05 Minnesota Mining And Manufacturing Company Melt-blown fibrous electrets
US4410661A (en) 1981-08-21 1983-10-18 E. I. Du Pont De Nemours And Company Toughened polyamide blends
US4478978A (en) 1980-10-20 1984-10-23 E. I. Du Pont De Nemours And Company Toughened polyamide blends
US4536361A (en) 1978-08-28 1985-08-20 Torobin Leonard B Method for producing plastic microfilaments
US4554320A (en) 1982-05-29 1985-11-19 Basf Aktiengesellschaft Nylon molding materials having high impact strength
US4556601A (en) 1984-01-05 1985-12-03 E. I. Du Pont De Nemours And Company Heavy-weight nonwoven fabric of hydraulically-entangled fibers
US4592815A (en) 1984-02-10 1986-06-03 Japan Vilene Co., Ltd. Method of manufacturing an electret filter
US4663220A (en) 1985-07-30 1987-05-05 Kimberly-Clark Corporation Polyolefin-containing extrudable compositions and methods for their formation into elastomeric products including microfibers
US4720292A (en) 1986-07-14 1988-01-19 Donaldson Company, Inc. Cylindrical air filter with lightweight housing and radially directed seal
US4729371A (en) 1983-10-11 1988-03-08 Minnesota Mining And Manufacturing Company Respirator comprised of blown bicomponent fibers
US4760129A (en) 1985-07-31 1988-07-26 Werner & Pfleiderer Process for preparing highly viscous polyhexamethyleneadipamide
US4798850A (en) 1986-05-19 1989-01-17 National Research Development Corporation Blended-fibre filter material
US4955116A (en) 1987-11-16 1990-09-11 Japan Vilene Company, Ltd. Method for producing tubular needle punched felt
US4983434A (en) 1989-04-07 1991-01-08 W. L. Gore & Associates, Inc. Filter laminates
US5082476A (en) 1990-10-19 1992-01-21 Donaldson Company, Inc. Filtration arrangement and method
US5104537A (en) 1990-07-20 1992-04-14 Donaldson Company, Inc. High pressure hydraulic spin-on filter
US5171339A (en) 1991-11-07 1992-12-15 E. I. Du Pont De Nemours And Company Filter bag for hot gases
US5238474A (en) 1990-10-19 1993-08-24 Donaldson Company, Inc. Filtration arrangement
US5401446A (en) 1992-10-09 1995-03-28 The University Of Tennessee Research Corporation Method and apparatus for the electrostatic charging of a web or film
US5401466A (en) 1993-06-01 1995-03-28 Miles Inc. Device for the direct measurement of low density lipoprotein cholesterol
US5496507A (en) 1993-08-17 1996-03-05 Minnesota Mining And Manufacturing Company Method of charging electret filter media
US5504185A (en) 1992-11-02 1996-04-02 Mitsubishi Gas Chemical Company, Inc. Process for production of polyamides, polyamides produced by said process and polyamide film or sheet
US5543495A (en) 1994-03-08 1996-08-06 E. I. Du Pont De Nemours And Company Process for increasing the molecular weight of polyamides and other condensation polymers
US5613992A (en) 1994-11-23 1997-03-25 Donaldson Company, Inc. Reverse flow air filter arrangement and method
US5652050A (en) 1994-07-28 1997-07-29 Pall Corporation Fibrous web for processing a fluid
US5698658A (en) 1996-05-31 1997-12-16 E. I. Du Pont De Nemours And Company Linear very high molecular weight polyamides and process for producing them
US5820646A (en) 1996-04-26 1998-10-13 Donaldson Company, Inc. Inline filter apparatus
US5853442A (en) 1997-04-18 1998-12-29 Donaldson Company, Inc. Bolt connector assembly having retainer ring construction and reduced diameter shank portion
US5908598A (en) 1995-08-14 1999-06-01 Minnesota Mining And Manufacturing Company Fibrous webs having enhanced electret properties
US5913993A (en) 1997-01-10 1999-06-22 Cerex Advanced Fabrics, L.P. Nonwoven nylon and polyethylene fabric
US5954849A (en) 1995-01-12 1999-09-21 Donaldson Company, Inc. Filter element
US5993943A (en) 1987-12-21 1999-11-30 3M Innovative Properties Company Oriented melt-blown fibers, processes for making such fibers and webs made from such fibers
US6011134A (en) 1998-01-30 2000-01-04 E. I. Du Pont De Nemours And Company Method for manufacturing poly(hexamethylene adipamide) from monomethyladipate and hexamethylenediamine
US6074869A (en) 1994-07-28 2000-06-13 Pall Corporation Fibrous web for processing a fluid
US6136947A (en) 1995-12-12 2000-10-24 Polymer Engineering Gmbh Process and device for the standardized continuous production of polyamides
US6169162B1 (en) 1999-05-24 2001-01-02 Solutia Inc. Continuous polyamidation process
US6183670B1 (en) 1997-09-23 2001-02-06 Leonard Torobin Method and apparatus for producing high efficiency fibrous media incorporating discontinuous sub-micron diameter fibers, and web media formed thereby
US6315806B1 (en) 1997-09-23 2001-11-13 Leonard Torobin Method and apparatus for producing high efficiency fibrous media incorporating discontinuous sub-micron diameter fibers, and web media formed thereby
US6375886B1 (en) 1999-10-08 2002-04-23 3M Innovative Properties Company Method and apparatus for making a nonwoven fibrous electret web from free-fiber and polar liquid
US20020059868A1 (en) * 2000-09-05 2002-05-23 Gogins Mark A. Air filter assembly for filtering an air stream to remove particulate matter entrained in the stream
US6398847B1 (en) 1998-07-02 2002-06-04 3M Innovative Properties Company Method of removing contaminants from an aerosol using a new electret article
US6406657B1 (en) 1999-10-08 2002-06-18 3M Innovative Properties Company Method and apparatus for making a fibrous electret web using a wetting liquid and an aqueous polar liquid
US6454986B1 (en) 1999-10-08 2002-09-24 3M Innovative Properties Company Method of making a fibrous electret web using a nonaqueous polar liquid
US6554881B1 (en) 1999-10-29 2003-04-29 Hollingsworth & Vose Company Filter media
US6598749B2 (en) 2000-09-15 2003-07-29 Cuno Incorporated Spiral pleated filter cartridges
US6627563B1 (en) 1999-08-19 2003-09-30 3M Innovative Properties Company Oily-mist resistant filter that has nondecreasing efficiency
WO2003080905A1 (fr) 2002-03-26 2003-10-02 Nano Technics Co., Ltd. Dispositif de fabrication et procede de preparation de nanofibres par un processus de filage par « electro-soufflage »
US6673136B2 (en) 2000-09-05 2004-01-06 Donaldson Company, Inc. Air filtration arrangements having fluted media constructions and methods
US20040038014A1 (en) 2002-08-20 2004-02-26 Donaldson Company, Inc. Fiber containing filter media
US6740142B2 (en) 2000-09-05 2004-05-25 Donaldson Company, Inc. Industrial bag house elements
US6743464B1 (en) 2000-04-13 2004-06-01 3M Innovative Properties Company Method of making electrets through vapor condensation
US6743273B2 (en) 2000-09-05 2004-06-01 Donaldson Company, Inc. Polymer, polymer microfiber, polymer nanofiber and applications including filter structures
US6746517B2 (en) 2000-09-05 2004-06-08 Donaldson Company, Inc. Filter structure with two or more layers of fine fiber having extended useful service life
US6827764B2 (en) 2002-07-25 2004-12-07 3M Innovative Properties Company Molded filter element that contains thermally bonded staple fibers and electrically-charged microfibers
US7008465B2 (en) 2003-06-19 2006-03-07 Donaldson Company, Inc. Cleanable high efficiency filter media structure and applications for use
US7115150B2 (en) 2000-09-05 2006-10-03 Donaldson Company, Inc. Mist filtration arrangement utilizing fine fiber layer in contact with media having a pleated construction and floor filter method
US7138482B2 (en) 2002-11-07 2006-11-21 Mitsubishi Gas Chemical Company, Inc. Production method of polyamide
US20070074628A1 (en) 2005-09-30 2007-04-05 Jones David C Coalescing filtration medium and process
US7270693B2 (en) 2000-09-05 2007-09-18 Donaldson Company, Inc. Polymer, polymer microfiber, polymer nanofiber and applications including filter structures
US7300272B1 (en) 2003-01-23 2007-11-27 Hills, Inc. Fiber extrusion pack including split distribution plates
US7316723B2 (en) 2001-05-31 2008-01-08 Donaldson Company, Inc. Air filter with fine fiber and spun bonded media
US20080116125A1 (en) 2006-11-20 2008-05-22 Kx Technologies Llc Fluid filtration apparatus and method of using the same
US7381788B2 (en) 2002-08-30 2008-06-03 Toyo Boseki Kabushiki Kaisha Method for continuous production of polyamide
WO2009010020A2 (fr) 2007-07-17 2009-01-22 Elmarco S.R.O, Procédé servant à filer une matrice liquide, dispositif pour la production de nanofibres par filage électrostatique de matrice liquide et électrode de filage pour un tel dispositif
US7488365B2 (en) 2001-12-03 2009-02-10 Donaldson Company, Inc. Filter element using corrugated media sheet
US20090199717A1 (en) 2007-11-20 2009-08-13 Clarcor Inc. Filtration Medias, Fine Fibers Under 100 Nanometers, and Methods
US20090205226A1 (en) 2005-03-02 2009-08-20 Wisconsin Engineering, Cz S.R.O. Snow blower apparatus
US7585437B2 (en) 2003-09-08 2009-09-08 Technicka Universita V Liberci Method of nanofibres production from a polymer solution using electrostatic spinning and a device for carrying out the method
US7608125B2 (en) 2006-05-24 2009-10-27 Johns Manville Nonwoven fibrous mat for MERV filter and method of making
WO2010107503A1 (fr) 2009-03-19 2010-09-23 Millipore Corporation Élimination de micro-organismes dans des échantillons de fluide en utilisant des milieux de filtration à nanofibres
US7877704B2 (en) 2000-04-13 2011-01-25 Nokia Corporation Radio terminal
EP2321029A2 (fr) 2008-07-18 2011-05-18 Clarcor INC. Milieu filtrant à plusieurs composants avec un accessoire de nanofibres
US20110305872A1 (en) 2010-06-09 2011-12-15 Jun Li Non-fouling, anti-microbial, anti-thrombogenic graft-from compositons
US20120175298A1 (en) 2010-10-21 2012-07-12 Eastman Chemical Company High efficiency filter
US8236082B2 (en) 2009-06-19 2012-08-07 Hollingsworth & Vose Company Flutable fiber webs with high dust holding capacity
US8308834B2 (en) 2007-03-05 2012-11-13 Bha Group, Inc. Composite filter media
US8512432B2 (en) 2008-08-01 2013-08-20 David Charles Jones Composite filter media
US20130233789A1 (en) 2012-03-09 2013-09-12 Ina PARKER High efficiency and high capacity glass-free fuel filtration media and fuel filters and methods employing the same
US8639220B2 (en) 2010-05-14 2014-01-28 Samsung Electronics Co., Ltd. Method and system for providing Wi-Fi service by Wi-Fi device
US8668854B2 (en) 2012-06-07 2014-03-11 Verdex Technologies, Inc. Process and apparatus for producing nanofibers using a two phase flow nozzle
US8679218B2 (en) 2010-04-27 2014-03-25 Hollingsworth & Vose Company Filter media with a multi-layer structure
US20140097558A1 (en) 2012-10-05 2014-04-10 Honeywell International Inc. Nanofiber filtering material for disposable/reusable respirators
WO2014074818A2 (fr) 2012-11-08 2014-05-15 Emergent Sensor Technologies, Llc Filtre sélectif et procédés d'utilisation
US20140166945A1 (en) 2012-12-13 2014-06-19 Juanita N. Kurtin Ceramic composition having dispersion of nano-particles therein and methods of fabricating same
US8759475B2 (en) 2007-03-27 2014-06-24 Rhodia Operations Continuous production of polyamides
US8777599B2 (en) 2011-02-07 2014-07-15 Fiberio Technology Corporation Multilayer apparatuses and methods for the production of microfibers and nanofibers
US8784542B2 (en) 2009-07-15 2014-07-22 Dsm Ip Assets B.V. Nanofibre membrane layer for water and air filtration
US8808594B1 (en) 2013-03-16 2014-08-19 Verdex Technologies, Inc. Coform fibrous materials and method for making same
US20150111019A1 (en) 2013-10-21 2015-04-23 E I Du Pont De Nemours And Company Electret nanofibrous web
US20150107457A1 (en) 2013-10-21 2015-04-23 E I Du Pont De Nemours And Company Electret nanofibrous web as air filtration media
US20150145175A1 (en) 2012-10-05 2015-05-28 Honeywell International Inc. Nanofiber filtering material for disposable/reusable respirators
US20150157971A1 (en) 2013-12-09 2015-06-11 Nano and Advanced Materials Institute Ltd. Interlaced Filtration Barrier
WO2018227069A1 (fr) * 2017-06-08 2018-12-13 Ascend Performance Materials Operations Llc Non-tissés en nanofibres de polyamide

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08144166A (ja) * 1994-11-21 1996-06-04 Toyobo Co Ltd ポリアミド極細繊維不織布およびその製造法
US20080105626A1 (en) * 2006-11-02 2008-05-08 David Charles Jones Fuel filter
US8679217B2 (en) * 2007-09-07 2014-03-25 E I Du Pont De Nemours And Company Pleated nanoweb structures
JP5165435B2 (ja) * 2008-03-26 2013-03-21 株式会社クラレ 気体フィルター用濾材
KR20100003817A (ko) * 2008-07-02 2010-01-12 코오롱패션머티리얼 (주) 방진마스크
SG175043A1 (en) * 2009-04-13 2011-11-28 Entegris Inc Porous composite membrane
US8523971B2 (en) * 2009-05-07 2013-09-03 The Hong Kong Polytechnic University Multilayer nanofiber filter
WO2012021308A2 (fr) * 2010-08-10 2012-02-16 Millipore Corporation Procédé pour l'élimination de rétrovirus
JP7039492B2 (ja) * 2016-06-10 2022-03-22 アセンド・パフォーマンス・マテリアルズ・オペレーションズ・リミテッド・ライアビリティ・カンパニー 溶液紡糸ポリアミドナノファイバー不織布

Patent Citations (131)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US425189A (en) 1890-04-08 Gar-coupling
US3016599A (en) 1954-06-01 1962-01-16 Du Pont Microfiber and staple fiber batt
US3288299A (en) 1963-07-05 1966-11-29 Fram Corp Oil filter cartridge
US3525124A (en) 1965-08-13 1970-08-25 Werner & Pfleiderer Extracting apparatus for processing material having eliminable components
US3431611A (en) 1966-09-16 1969-03-11 Gen Electric Method for forming nonwoven electric blanket shells
US3978185A (en) 1968-12-23 1976-08-31 Exxon Research And Engineering Company Melt blowing process
US3849241A (en) 1968-12-23 1974-11-19 Exxon Research Engineering Co Non-woven mats by melt blowing
US3676242A (en) 1969-08-13 1972-07-11 Exxon Research Engineering Co Method of making a nonwoven polymer laminate
US3704198A (en) 1969-10-09 1972-11-28 Exxon Research Engineering Co Nonwoven polypropylene mats of increased strip tensile strength
US3755527A (en) 1969-10-09 1973-08-28 Exxon Research Engineering Co Process for producing melt blown nonwoven synthetic polymer mat having high tear resistance
US3841953A (en) 1970-12-31 1974-10-15 Exxon Research Engineering Co Nonwoven mats of thermoplastic blends by melt blowing
US3912631A (en) 1972-06-09 1975-10-14 William C Turman Oil filter and adapter
US3878014A (en) 1973-04-30 1975-04-15 Beloit Corp Process for matting melt blow microfibers
US4011067A (en) 1974-01-30 1977-03-08 Minnesota Mining And Manufacturing Company Filter medium layered between supporting layers
US4100324A (en) 1974-03-26 1978-07-11 Kimberly-Clark Corporation Nonwoven fabric and method of producing same
US4127706A (en) 1974-09-26 1978-11-28 Imperial Chemical Industries Limited Porous fluoropolymeric fibrous sheet and method of manufacture
US4174358A (en) 1975-05-23 1979-11-13 E. I. Du Pont De Nemours And Company Tough thermoplastic nylon compositions
US4174358B1 (fr) 1975-05-23 1992-08-04 Du Pont
US4118531A (en) 1976-08-02 1978-10-03 Minnesota Mining And Manufacturing Company Web of blended microfibers and crimped bulking fibers
US4082476A (en) 1977-04-06 1978-04-04 Fridrikh Lvovich Kopelev Machine for precision boring operations
US4215682A (en) 1978-02-06 1980-08-05 Minnesota Mining And Manufacturing Company Melt-blown fibrous electrets
US4536361A (en) 1978-08-28 1985-08-20 Torobin Leonard B Method for producing plastic microfilaments
US4478978A (en) 1980-10-20 1984-10-23 E. I. Du Pont De Nemours And Company Toughened polyamide blends
US4410661A (en) 1981-08-21 1983-10-18 E. I. Du Pont De Nemours And Company Toughened polyamide blends
US4554320A (en) 1982-05-29 1985-11-19 Basf Aktiengesellschaft Nylon molding materials having high impact strength
US4729371A (en) 1983-10-11 1988-03-08 Minnesota Mining And Manufacturing Company Respirator comprised of blown bicomponent fibers
US4556601A (en) 1984-01-05 1985-12-03 E. I. Du Pont De Nemours And Company Heavy-weight nonwoven fabric of hydraulically-entangled fibers
US4592815A (en) 1984-02-10 1986-06-03 Japan Vilene Co., Ltd. Method of manufacturing an electret filter
US4663220A (en) 1985-07-30 1987-05-05 Kimberly-Clark Corporation Polyolefin-containing extrudable compositions and methods for their formation into elastomeric products including microfibers
US4760129A (en) 1985-07-31 1988-07-26 Werner & Pfleiderer Process for preparing highly viscous polyhexamethyleneadipamide
US4798850A (en) 1986-05-19 1989-01-17 National Research Development Corporation Blended-fibre filter material
US4720292A (en) 1986-07-14 1988-01-19 Donaldson Company, Inc. Cylindrical air filter with lightweight housing and radially directed seal
US4720292B1 (en) 1986-07-14 1991-09-10 Cylindrical air filter with lightweight housing and radially directed seal
US4720292B2 (fr) 1986-07-14 1994-02-22 Donaldson Company, Inc.
US4955116A (en) 1987-11-16 1990-09-11 Japan Vilene Company, Ltd. Method for producing tubular needle punched felt
US5993943A (en) 1987-12-21 1999-11-30 3M Innovative Properties Company Oriented melt-blown fibers, processes for making such fibers and webs made from such fibers
US4983434A (en) 1989-04-07 1991-01-08 W. L. Gore & Associates, Inc. Filter laminates
US5104537A (en) 1990-07-20 1992-04-14 Donaldson Company, Inc. High pressure hydraulic spin-on filter
US5238474A (en) 1990-10-19 1993-08-24 Donaldson Company, Inc. Filtration arrangement
US5364456A (en) 1990-10-19 1994-11-15 Donaldson Company, Inc. Filtration arrangement and method
US5423892A (en) 1990-10-19 1995-06-13 Donaldson Company, Inc. Filtration arrangement
US5082476A (en) 1990-10-19 1992-01-21 Donaldson Company, Inc. Filtration arrangement and method
US5171339A (en) 1991-11-07 1992-12-15 E. I. Du Pont De Nemours And Company Filter bag for hot gases
US5401446A (en) 1992-10-09 1995-03-28 The University Of Tennessee Research Corporation Method and apparatus for the electrostatic charging of a web or film
US5504185A (en) 1992-11-02 1996-04-02 Mitsubishi Gas Chemical Company, Inc. Process for production of polyamides, polyamides produced by said process and polyamide film or sheet
US5401466A (en) 1993-06-01 1995-03-28 Miles Inc. Device for the direct measurement of low density lipoprotein cholesterol
US6119691A (en) 1993-08-17 2000-09-19 Minnesota Mining And Manufacturing Company Electret filter media
US5496507A (en) 1993-08-17 1996-03-05 Minnesota Mining And Manufacturing Company Method of charging electret filter media
US5543495A (en) 1994-03-08 1996-08-06 E. I. Du Pont De Nemours And Company Process for increasing the molecular weight of polyamides and other condensation polymers
US5652050A (en) 1994-07-28 1997-07-29 Pall Corporation Fibrous web for processing a fluid
US6074869A (en) 1994-07-28 2000-06-13 Pall Corporation Fibrous web for processing a fluid
US5846438A (en) 1994-07-28 1998-12-08 Pall Corporation Fibrous web for processing a fluid
US5613992A (en) 1994-11-23 1997-03-25 Donaldson Company, Inc. Reverse flow air filter arrangement and method
US5954849A (en) 1995-01-12 1999-09-21 Donaldson Company, Inc. Filter element
US5908598A (en) 1995-08-14 1999-06-01 Minnesota Mining And Manufacturing Company Fibrous webs having enhanced electret properties
US6136947A (en) 1995-12-12 2000-10-24 Polymer Engineering Gmbh Process and device for the standardized continuous production of polyamides
US5820646A (en) 1996-04-26 1998-10-13 Donaldson Company, Inc. Inline filter apparatus
US5698658A (en) 1996-05-31 1997-12-16 E. I. Du Pont De Nemours And Company Linear very high molecular weight polyamides and process for producing them
US5913993A (en) 1997-01-10 1999-06-22 Cerex Advanced Fabrics, L.P. Nonwoven nylon and polyethylene fabric
US5853442A (en) 1997-04-18 1998-12-29 Donaldson Company, Inc. Bolt connector assembly having retainer ring construction and reduced diameter shank portion
US6183670B1 (en) 1997-09-23 2001-02-06 Leonard Torobin Method and apparatus for producing high efficiency fibrous media incorporating discontinuous sub-micron diameter fibers, and web media formed thereby
US6315806B1 (en) 1997-09-23 2001-11-13 Leonard Torobin Method and apparatus for producing high efficiency fibrous media incorporating discontinuous sub-micron diameter fibers, and web media formed thereby
US6011134A (en) 1998-01-30 2000-01-04 E. I. Du Pont De Nemours And Company Method for manufacturing poly(hexamethylene adipamide) from monomethyladipate and hexamethylenediamine
US6409806B1 (en) 1998-07-02 2002-06-25 3M Innovative Properties Company Fluorinated electret
US6398847B1 (en) 1998-07-02 2002-06-04 3M Innovative Properties Company Method of removing contaminants from an aerosol using a new electret article
US6397458B1 (en) 1998-07-02 2002-06-04 3M Innovative Properties Company Method of making an electret article by transferring fluorine to the article from a gaseous phase
US6562112B2 (en) 1998-07-02 2003-05-13 3M Innovative Properties Company Fluorinated electret
US6169162B1 (en) 1999-05-24 2001-01-02 Solutia Inc. Continuous polyamidation process
US6627563B1 (en) 1999-08-19 2003-09-30 3M Innovative Properties Company Oily-mist resistant filter that has nondecreasing efficiency
US6375886B1 (en) 1999-10-08 2002-04-23 3M Innovative Properties Company Method and apparatus for making a nonwoven fibrous electret web from free-fiber and polar liquid
US6406657B1 (en) 1999-10-08 2002-06-18 3M Innovative Properties Company Method and apparatus for making a fibrous electret web using a wetting liquid and an aqueous polar liquid
US6454986B1 (en) 1999-10-08 2002-09-24 3M Innovative Properties Company Method of making a fibrous electret web using a nonaqueous polar liquid
US6554881B1 (en) 1999-10-29 2003-04-29 Hollingsworth & Vose Company Filter media
US6743464B1 (en) 2000-04-13 2004-06-01 3M Innovative Properties Company Method of making electrets through vapor condensation
US7877704B2 (en) 2000-04-13 2011-01-25 Nokia Corporation Radio terminal
US7270693B2 (en) 2000-09-05 2007-09-18 Donaldson Company, Inc. Polymer, polymer microfiber, polymer nanofiber and applications including filter structures
US7318852B2 (en) 2000-09-05 2008-01-15 Donaldson Company, Inc. Bag house filter with fine fiber and spun bonded media
US20020059868A1 (en) * 2000-09-05 2002-05-23 Gogins Mark A. Air filter assembly for filtering an air stream to remove particulate matter entrained in the stream
US6716274B2 (en) 2000-09-05 2004-04-06 Donaldson Company, Inc. Air filter assembly for filtering an air stream to remove particulate matter entrained in the stream
US6740142B2 (en) 2000-09-05 2004-05-25 Donaldson Company, Inc. Industrial bag house elements
US8366797B2 (en) 2000-09-05 2013-02-05 Donaldson Company, Inc. Fine fiber media layer
US6743273B2 (en) 2000-09-05 2004-06-01 Donaldson Company, Inc. Polymer, polymer microfiber, polymer nanofiber and applications including filter structures
US6746517B2 (en) 2000-09-05 2004-06-08 Donaldson Company, Inc. Filter structure with two or more layers of fine fiber having extended useful service life
US8709118B2 (en) 2000-09-05 2014-04-29 Donaldson Company, Inc. Fine fiber media layer
US6955775B2 (en) 2000-09-05 2005-10-18 Donaldson Company, Inc. Process if making fine fiber material
US6673136B2 (en) 2000-09-05 2004-01-06 Donaldson Company, Inc. Air filtration arrangements having fluted media constructions and methods
US7070640B2 (en) 2000-09-05 2006-07-04 Donaldson Company, Inc. Polymer, polymer microfiber, polymer nanofiber and applications including filter structures
US7115150B2 (en) 2000-09-05 2006-10-03 Donaldson Company, Inc. Mist filtration arrangement utilizing fine fiber layer in contact with media having a pleated construction and floor filter method
US9718012B2 (en) 2000-09-05 2017-08-01 Donaldson Company, Inc. Fine fiber media layer
US7179317B2 (en) 2000-09-05 2007-02-20 Donaldson Company, Inc. Polymer, polymer microfiber, polymer nanofiber and applications including filter structures
US6598749B2 (en) 2000-09-15 2003-07-29 Cuno Incorporated Spiral pleated filter cartridges
US7316723B2 (en) 2001-05-31 2008-01-08 Donaldson Company, Inc. Air filter with fine fiber and spun bonded media
US7488365B2 (en) 2001-12-03 2009-02-10 Donaldson Company, Inc. Filter element using corrugated media sheet
WO2003080905A1 (fr) 2002-03-26 2003-10-02 Nano Technics Co., Ltd. Dispositif de fabrication et procede de preparation de nanofibres par un processus de filage par « electro-soufflage »
US6827764B2 (en) 2002-07-25 2004-12-07 3M Innovative Properties Company Molded filter element that contains thermally bonded staple fibers and electrically-charged microfibers
US20040038014A1 (en) 2002-08-20 2004-02-26 Donaldson Company, Inc. Fiber containing filter media
US7381788B2 (en) 2002-08-30 2008-06-03 Toyo Boseki Kabushiki Kaisha Method for continuous production of polyamide
US7138482B2 (en) 2002-11-07 2006-11-21 Mitsubishi Gas Chemical Company, Inc. Production method of polyamide
US7300272B1 (en) 2003-01-23 2007-11-27 Hills, Inc. Fiber extrusion pack including split distribution plates
US7008465B2 (en) 2003-06-19 2006-03-07 Donaldson Company, Inc. Cleanable high efficiency filter media structure and applications for use
US7585437B2 (en) 2003-09-08 2009-09-08 Technicka Universita V Liberci Method of nanofibres production from a polymer solution using electrostatic spinning and a device for carrying out the method
US20090205226A1 (en) 2005-03-02 2009-08-20 Wisconsin Engineering, Cz S.R.O. Snow blower apparatus
US20070074628A1 (en) 2005-09-30 2007-04-05 Jones David C Coalescing filtration medium and process
US7608125B2 (en) 2006-05-24 2009-10-27 Johns Manville Nonwoven fibrous mat for MERV filter and method of making
US20080116125A1 (en) 2006-11-20 2008-05-22 Kx Technologies Llc Fluid filtration apparatus and method of using the same
US8308834B2 (en) 2007-03-05 2012-11-13 Bha Group, Inc. Composite filter media
US8759475B2 (en) 2007-03-27 2014-06-24 Rhodia Operations Continuous production of polyamides
WO2009010020A2 (fr) 2007-07-17 2009-01-22 Elmarco S.R.O, Procédé servant à filer une matrice liquide, dispositif pour la production de nanofibres par filage électrostatique de matrice liquide et électrode de filage pour un tel dispositif
US20090199717A1 (en) 2007-11-20 2009-08-13 Clarcor Inc. Filtration Medias, Fine Fibers Under 100 Nanometers, and Methods
EP2321029A2 (fr) 2008-07-18 2011-05-18 Clarcor INC. Milieu filtrant à plusieurs composants avec un accessoire de nanofibres
US8512432B2 (en) 2008-08-01 2013-08-20 David Charles Jones Composite filter media
WO2010107503A1 (fr) 2009-03-19 2010-09-23 Millipore Corporation Élimination de micro-organismes dans des échantillons de fluide en utilisant des milieux de filtration à nanofibres
US8236082B2 (en) 2009-06-19 2012-08-07 Hollingsworth & Vose Company Flutable fiber webs with high dust holding capacity
US8778047B2 (en) 2009-06-19 2014-07-15 Hollingsworth & Vose Company Flutable fiber webs with high dust holding capacity
US8784542B2 (en) 2009-07-15 2014-07-22 Dsm Ip Assets B.V. Nanofibre membrane layer for water and air filtration
US8679218B2 (en) 2010-04-27 2014-03-25 Hollingsworth & Vose Company Filter media with a multi-layer structure
US8639220B2 (en) 2010-05-14 2014-01-28 Samsung Electronics Co., Ltd. Method and system for providing Wi-Fi service by Wi-Fi device
US20110305872A1 (en) 2010-06-09 2011-12-15 Jun Li Non-fouling, anti-microbial, anti-thrombogenic graft-from compositons
US20120175298A1 (en) 2010-10-21 2012-07-12 Eastman Chemical Company High efficiency filter
US8777599B2 (en) 2011-02-07 2014-07-15 Fiberio Technology Corporation Multilayer apparatuses and methods for the production of microfibers and nanofibers
US20130233789A1 (en) 2012-03-09 2013-09-12 Ina PARKER High efficiency and high capacity glass-free fuel filtration media and fuel filters and methods employing the same
US8668854B2 (en) 2012-06-07 2014-03-11 Verdex Technologies, Inc. Process and apparatus for producing nanofibers using a two phase flow nozzle
US20150145175A1 (en) 2012-10-05 2015-05-28 Honeywell International Inc. Nanofiber filtering material for disposable/reusable respirators
US20140097558A1 (en) 2012-10-05 2014-04-10 Honeywell International Inc. Nanofiber filtering material for disposable/reusable respirators
WO2014074818A2 (fr) 2012-11-08 2014-05-15 Emergent Sensor Technologies, Llc Filtre sélectif et procédés d'utilisation
US20140166945A1 (en) 2012-12-13 2014-06-19 Juanita N. Kurtin Ceramic composition having dispersion of nano-particles therein and methods of fabricating same
US8808594B1 (en) 2013-03-16 2014-08-19 Verdex Technologies, Inc. Coform fibrous materials and method for making same
US20150111019A1 (en) 2013-10-21 2015-04-23 E I Du Pont De Nemours And Company Electret nanofibrous web
US20150107457A1 (en) 2013-10-21 2015-04-23 E I Du Pont De Nemours And Company Electret nanofibrous web as air filtration media
US20150157971A1 (en) 2013-12-09 2015-06-11 Nano and Advanced Materials Institute Ltd. Interlaced Filtration Barrier
WO2018227069A1 (fr) * 2017-06-08 2018-12-13 Ascend Performance Materials Operations Llc Non-tissés en nanofibres de polyamide

Non-Patent Citations (14)

* Cited by examiner, † Cited by third party
Title
"Kirk-Othmer, Encyclopedia of Chemical Technology", vol. 18, 1982, WILEY, pages: 328371
"The Handbook of Plasticizers", 2004, CHEMTEC PUBLISHING
AUSSAWASATHIEN ET AL., JOURNAL OF MEMBRANE SCIENCE, vol. 315, 2008, pages 11 - 19
BJORGE ET AL., DESALINATION, vol. 249, 2009, pages 942 - 948
BJORGE ET AL.: "Performance assessment of electrospun nanofibers for filter applications", DESALINATION, vol. 249, 2009, pages 942 - 948, XP026751129, DOI: 10.1016/j.desal.2009.06.064
BLANCHARD: "Quantifying Sterilizing Membrane Retention Assurance", BIOPROCESS INTERNATIONAL, vol. 5, no. 5, 2007, pages 44 - 51
ELLISON ET AL., POLYMER, vol. 48, no. 11, 2007, pages 3306 - 3316
GLASSCOCK ET AL., HIGH PERFORMANCE POLYAMIDES FULFILL DEMANDING REQUIREMENTS FOR AUTOMOTIVE THERMAL MANAGEMENT COMPONENTS, 10 June 2016 (2016-06-10), Retrieved from the Internet <URL:http://www2.dupont.com!Automotive/en-US/assets/downloads/knowledge%20center/HTN-whitepaper-R8.pdf>
GOPAL ET AL., JOURNAL OF MEMBRANE SCIENCE, vol. 289, 2007, pages 210 - 219
HASSAN ET AL., J 20 MEMBRANE SCI., vol. 427, 2013, pages 336 - 344
HASSAN ET AL., J MEMBRANE SCI., vol. 427, 2013, pages 336 - 344
INTERNATIONAL NONWOVEN JOURNAL, 2003, pages 21 - 28
LI ET AL., NANO LETTERS, vol. 5, no. 5, 2005, pages 913 - 916
TSAI ET AL.: "Electrospinning Theory and Techniques", 14TH ANNUAL INTERNATIONAL TANDEC NONWOVENS CONFERENCE, 9 November 2004 (2004-11-09)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU205640U1 (ru) * 2020-12-03 2021-07-26 Ольга Александровна Лещинская Электростатический фильтр
CN114889252A (zh) * 2022-04-29 2022-08-12 广东埃力生高新科技有限公司 一种气凝胶-双组分针刺纤维毡的复合材料及其制备方法和应用

Also Published As

Publication number Publication date
TW202110520A (zh) 2021-03-16
CA3138150A1 (fr) 2020-11-05
CN113710344A (zh) 2021-11-26
BR112021020488A2 (pt) 2022-02-15
JP2022530806A (ja) 2022-07-01
EP3962626A1 (fr) 2022-03-09
JP7340037B2 (ja) 2023-09-06
TWI758722B (zh) 2022-03-21
MX2021013375A (es) 2021-11-25
KR20210153137A (ko) 2021-12-16
CA3138150C (fr) 2023-09-19

Similar Documents

Publication Publication Date Title
US11376534B2 (en) Polyamide nanofiber nonwovens for filters
CA3138150C (fr) Milieu filtrant comprenant une couche de nanofibres de polyamide
US8394155B2 (en) Thermally stabilized bag house filters and media
JP5619723B2 (ja) 塵集積容量が向上しかつ高湿度環境に対する抵抗性が向上した空気濾過媒体
JP5696919B2 (ja) ナノウェブとスクリムの耐久性積層物
EP2142275B1 (fr) Dépoussiéreurs à sacs filtrants
JP4785928B2 (ja) 凝集ろ材および方法
KR101315000B1 (ko) 기체 스트림으로부터 미립자 물질을 여과하기 위한 여과매질
CN108778452B (zh) 包括包含合成纤维的过滤层的过滤介质
JP2010538813A (ja) 改良されたプリーツ付きナノウェブ構造体
JP4737039B2 (ja) 吸気用フィルター不織布

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20727779

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 3138150

Country of ref document: CA

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112021020488

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 2021564444

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20217039357

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2020727779

Country of ref document: EP

Effective date: 20211201

REG Reference to national code

Ref country code: BR

Ref legal event code: B01E

Ref document number: 112021020488

Country of ref document: BR

Free format text: APRESENTAR A TRADUCAO SIMPLES DA FOLHA DE ROSTO DA CERTIDAO DE DEPOSITO DA PRIORIDADE US 62/841,485 DE 01/05/2019 OU DECLARACAO CONTENDO, OBRIGATORIAMENTE, TODOS OS DADOS IDENTIFICADORES DESTA (DEPOSITANTE(S), INVENTOR(ES), NUMERO DE REGISTRO, DATA DE DEPOSITO E TITULO), CONFORME O ART. 15 DA PORTARIA 39/2021. O DOCUMENTO APRESENTADO NAO ESTA TRADUZIDO.

ENP Entry into the national phase

Ref document number: 112021020488

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20211013

WWE Wipo information: entry into national phase