WO2020213389A1 - 熱可塑性樹脂、成形体、及び熱可塑性樹脂用モノマー - Google Patents
熱可塑性樹脂、成形体、及び熱可塑性樹脂用モノマー Download PDFInfo
- Publication number
- WO2020213389A1 WO2020213389A1 PCT/JP2020/014842 JP2020014842W WO2020213389A1 WO 2020213389 A1 WO2020213389 A1 WO 2020213389A1 JP 2020014842 W JP2020014842 W JP 2020014842W WO 2020213389 A1 WO2020213389 A1 WO 2020213389A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thermoplastic resin
- general formula
- structural unit
- group
- reaction
- Prior art date
Abstract
Description
光学ガラスは、耐熱性や透明性、寸法安定性、耐薬品性等に優れ、様々な屈折率(nD)やアッベ数(νD)を有する多種類の材料が存在しているが、材料コストが高い上、成形加工性が悪く、また生産性が低いという問題点を有している。とりわけ、収差補正に使用される非球面レンズに加工するには、極めて高度な技術と高いコストがかかるため実用上大きな障害となっている。
光学用途の熱可塑性透明樹脂としては、特にポリカーボネート樹脂が適しており、光学用途に好適な様々なポリカーボネート樹脂が開発されている。
例えば、特許文献1及び2には、光学ガラスに代わる光学用途に用い得る材料として、ペルヒドロキシジメタノナフタレン骨格を含むポリカーボネート共重合体が記載されている。
また、特許文献3には、高アッベ数の光学レンズを製造し得る樹脂として、デカヒドロ-1,4:5,8-ジメタノナフタレンジオール(D-NDM)を原料とし、特定の構成単位を有するポリカーボネート樹脂が記載されている。
また、特許文献3に記載のポリカーボネート樹脂は、高アッベ数の光学レンズを製造できる点で優れている。ただし、より優れた光学特性を有する成形体を製造し得る光学材料が求められている。
[1]下記一般式(I)で表される構成単位を有する、熱可塑性樹脂。
[2]前記構成単位が、下記一般式(1a)で表される化合物に由来する構成単位(a)と、下記一般式(1b)で表される化合物に由来する構成単位(b)とを含む、上記[1]に記載の熱可塑性樹脂。
[3]構成単位(a)と、構成単位(b)との含有量比〔(a)/(b)〕が、質量比で、1/99~99/1である、上記[2]に記載の熱可塑性樹脂。
[4]前記熱可塑性樹脂が、ポリカーボネート樹脂、ポリエステル樹脂、又はポリエステルカーボネート樹脂である、上記[1]~[3]のいずれか一項に記載の熱可塑性樹脂。
[5]前記熱可塑性樹脂が、下記一般式(I-A)で表される構成単位を有する、上記[1]~[4]のいずれか一項に記載の熱可塑性樹脂。
[6]前記熱可塑性樹脂が、下記一般式(I-B)で表される構成単位を有する、上記[1]~[4]のいずれか一項に記載の熱可塑性樹脂。
[7]前記熱可塑性樹脂が、下記一般式(I-A)で表される構成単位、及び下記一般式(I-B)で表される構成単位を有する、上記[1]~[4]のいずれか一項に記載の熱可塑性樹脂。
[8]前記熱可塑性樹脂が、さらに下記一般式(II)で表される構成単位を有する、上記[5]~[7]のいずれか一項に記載の熱可塑性樹脂。
[9]Qが、下記一般式(i)又は(ii)で表される基である、上記[6]~[8]のいずれか一項に記載の熱可塑性樹脂。
[10]前記熱可塑性樹脂の重量平均分子量(Mw)が5,000~50,000である、上記[1]~[9]のいずれか一項に記載の熱可塑性樹脂。
[11]R1が、メチル基、エチル基、又はフェニル基であり、R2及びR3が、水素原子である、上記[1]~[10]のいずれか一項に記載の熱可塑性樹脂。
[12]R1がメチル基であり、R2及びR3が、水素原子である、上記[1]~[11]のいずれか一項に記載の熱可塑性樹脂。
[13]上記[1]~[12]のいずれか一項に記載の熱可塑性樹脂を含む樹脂組成物を成形してなる、成形体。
[14]前記成形体が、光学部材である、上記[13]に記載の成形体。
[15]前記成形体が、光学レンズである、上記[13]又は[14]に記載の成形体。
[16]下記一般式(1)で表される、熱可塑性樹脂用モノマー。
[17]前記熱可塑性樹脂用モノマーが、光学部材の成形材料として用いられる熱可塑性樹脂を構成するモノマーである、上記[16]に記載の熱可塑性樹脂用モノマー。
本発明の熱可塑性樹脂は、R1が炭素数1~6の炭化水素基である上記構成単位を有するため、低比重化、低複屈折化、光弾性係数の低減化、及び高硬度化した成形体の形成材料となり得る。
これらの中でも、R1として選択し得る、前記炭化水素基としては、炭素数1~3のアルキル基、又はフェニル基が好ましく、メチル基、エチル基、又はフェニル基がより好ましく、メチル基が更に好ましい。
当該熱可塑性樹脂用モノマーは、光学部材の成形材料として用いられる本発明の熱可塑性樹脂を構成する原料モノマーである。
なお、R1、R2、及びR3の好適な態様は、上述の一般式(I)と同じである。
構成単位(a)と構成単位(b)との含有量比〔(a)/(b)〕は、質量比で、好ましくは1/99~99/1、より好ましくは5/95~95/5、更に好ましくは10/90~90/10、より更に好ましくは20/80~80/20、特に好ましくは35/65~65/35である。
他のジオールとしては、例えば、エチレングリコール、1,2-プロパンジオール、1,3-プロパンジオール、1,4-ブタンジオール、1,2-ブタンジオール、1,3-ブタンジオール、ネオペンチルグリコール、1,5-ペンタンジオール、1,6-ヘキサンジオール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、シクロヘキサンジメタノール、トリシクロデカンジメタノール、ペンタシクロペンタデカンジメタノール、2,2,4,4-テトラメチル-1,3-シクロブタンジオール、水添ビスフェノールA、スピログリコール、イソソルバイド、ビスフェノールA、ビスフェノールAP、ビスフェノールAF、ビスフェノールB、ビスフェノールBP、ビスフェノールC、ビスフェノールE、ビスフェノールF、ビスフェノールG、ビスフェノールM、ビスフェノールS、ビスフェノールP、ビスフェノールPH、ビスフェノールTMC、ビスフェノールZ、9,9-ビス(4-(2-ヒドロキシエトキシ)フェニル)フルオレン、9,9-ビス(4-(2-ヒドロキシエトキシ)-3-メチルフェニル)フルオレン、9,9-ビス(4-(2-ヒドロキシエトキシ)-3-tert-ブチルフェニル)フルオレン、9,9-ビス(4-(2-ヒドロキシエトキシ)-3-イソプロピルフェニル)フルオレン、9,9-ビス(4-(2-ヒドロキシエトキシ)-3-シクロヘキシルフェニル)フルオレン、9,9-ビス(4-(2-ヒドロキシエトキシ)-3-フェニルフェニル)フルオレン等が挙げられる。
上記一般式(I-A)で表される構成単位は、前記一般式(I)で表される構成単位にカルボニル基が導入された単位である。
上記一般式(I-A)で表される構成単位は、例えば、前記一般式(1)で表される熱可塑性樹脂用モノマーと、ホスゲン(塩化カルボニル)又は炭酸ジエステルとを反応させることで形成することができる。
上記一般式(I-B)で表される構成単位は、前記一般式(I)で表される構成単位に、ジカルボン酸に由来する構成が付加されたものである。
上記一般式(I-B)で表される構成単位は、例えば、ジオールとして前記一般式(1)で表される熱可塑性樹脂用モノマーと、下記一般式(2a)で表されるジカルボン酸とをエステル化反応させることで形成することができる。
つまり、ポリエステルカーボネート樹脂の態様は、ジオールとして前記一般式(1)で表される熱可塑性樹脂用モノマーと、ホスゲン(塩化カルボニル)又は炭酸ジエステルと、ジカルボン酸とを反応させて形成することができる。
上記一般式(II)で表される構成単位は、下記一般式(2b)で表されるモノマーに由来する単位である。
また、当該モノマーのヒドロキシ基と、別の分子の当該モノマーのカルボキシ基とがエステル化反応をして結合してもよい。
なお、これらの基の少なくとも1つの水素原子は、さらに置換基によって置換されていてもよく、当該置換基としては、炭素数1~6のアルキル基、炭素数3~12のシクロアルキル基、炭素数6~12のアリール基等が挙げられる。
当該炭化水素基としては、炭素数1~12の直鎖又は分岐鎖のアルキレン基、炭素数3~12のシクロアルキレン基、炭素数6~12のアリーレン基等が挙げられ、炭素数1~12の直鎖アルキレン基又は炭素数6~12のアリーレン基が好ましく、メチレン基、エチレン基、又はフェニレン基がより好ましい。
なお、本明細書において、重量平均分子量(Mw)は、ゲルパーミエーションクロマトグラフィー(GPC)法で測定される標準ポリスチレン換算の値であり、具体的には実施例に記載の方法により測定された値を意味する。
なお、本明細書において、熱可塑性樹脂のガラス転移温度(Tg)は、JIS K7121-1987に準拠して、示差熱走査熱量分析計(DSC)を用いて測定した値であって、具体的には実施例に記載の方法により測定された値を意味する。
前記一般式(1)で表される熱可塑性樹脂用モノマーは、ジシクロペンタジエン又はシクロペンタジエンと、官能基(R1、R2、R3)を有する不飽和アルデヒドを原料として、例えば、下記に示すスキームで合成することができる。
まず、工程(i)で、ジシクロペンタジエンと、官能基(R1、R2、R3)を有する上記式(α)で表される不飽和アルデヒドとをディールス・アルダー反応を行うことで、上記式(1-1)で表される化合物を合成する。
なお、上記式(α)で表される不飽和アルデヒドが有する官能基R1、R2、R3は、最終生成物である前記一般式(1)で表される熱可塑性樹脂用モノマーの官能基R1、R2、R3に対応する。
また、ジシクロペンタジエンは、加熱条件下で解重合しシクロペンタジエン(モノシクロペンタジエン)になることが知られていることから、ジシクロペンタジエンの代わりにシクロペンタジエンを使用することも可能である。
さらに、不飽和アルデヒドは、幾何異性体として、シス型とトランス型の二種類が存在するが、それぞれ単独で用いてもよく、二種類を混合して用いてもよい。
なお、式(1-1)で表される化合物(以下、「化合物(1-1)」ともいう)は、実質的に下記式(1-1a)で表される化合物(1段目ディールス・アルダー反応生成物)を経由して生成していると考えられ、生成した式(1-1a)で表される化合物が、新たな親ジエン化合物(Dienophile)として反応系内に存在するシクロペンタジエン(Diene)とディールス・アルダー反応(2段目ディールスアルダー反応)により、式(1-1)で表される化合物が生成されるものと考えられる。
また、反応溶媒としては、炭化水素系溶媒やアルコール系溶媒、エステル系溶媒等を用いることができるが、炭素数6以上の脂肪族炭化水素系溶媒、シクロヘキサン、トルエン、キシレン、エチルベンゼン、メシチレン、プロパノール、ブタノール、2-オクタノール等が好ましい。
また、ディールス・アルダー反応で得られた生成物は、そのまま次工程のヒドロホルミル化反応の原料として用いることも出来るが、蒸留、抽出、晶析等の精製処理を行った上で、次工程に供してもよい。
工程(ii)では、化合物(1-1)に対して、一酸化炭素及び水素ガスを供給し、ロジウム化合物及び有機リン化合物の存在下で、ヒドロホルミル化反応を行うことで、上記式(1-2)で表される化合物(以下、「化合物(1-2)」ともいう)を生成する。
本工程のヒドロホルミル化反応で使用するロジウム化合物は、有機リン化合物と錯体を形成し、一酸化炭素と水素の存在下でヒドロホルミル化活性を示す化合物であれば特に制限はない。
例えば、ロジウムアセチルアセトナートジカルボニル(以下、Rh(acac)(CO)2と記す)、Rh2O3、Rh4(CO)12、Rh6(CO)16、Rh(NO3)3等の触媒前駆物質を有機リン化合物と共に反応混合物中に導入し、反応容器内で触媒活性を持つロジウム金属ヒドリドカルボニルリン錯体を形成させてもよい。また、予めロジウム金属ヒドリドカルボニルリン錯体を調製してそれを反応器内に導入してもよい。
好ましい具体例としては、Rh(acac)(CO)2を溶媒の存在下で有機リン化合物と反応させた後、過剰の有機リン化合物と共に反応器に導入し、触媒活性を有するロジウム-有機リン錯体とする方法が挙げられる。
RA、RB、RCは、炭素数1~4のアルキル基又はアルコキシ基で置換されていてもよいアリール基、炭素数1~4のアルキル基又はアルコキシ基で置換されていてもよい脂環式アルキル基等が挙げられる。
これらの中でも、有機リン化合物としては、トリフェニルホスフィン、又はトリフェニルホスファイトが好ましい。
溶媒としては、化合物(1-1)、ジシクロペンタジエン又はシクロペンタジエン、及び前記ロジウム化合物、前記有機リン化合物を溶解するものであれば特に制限はなく、具体的には、脂肪族炭化水素、脂環式炭化水素、芳香族炭化水素等の炭化水素類、脂肪族エステル、脂環式エステル、芳香族エステル等のエステル類、脂肪族アルコール、脂環式アルコール等のアルコール類、芳香族ハロゲン化物等の溶媒が挙げられる。
これらの中でも、溶媒としては、炭化水素類が好ましく、脂環式炭化水素又は芳香族炭化水素がより好ましい。
反応温度が40℃以上の場合には十分な反応速度が得られ、原料である化合物(1-1)の残留を抑えられる。また、反応温度が160℃以下にすることで、化合物(1-1)や反応生成物に由来する副生物の生成を抑え、反応成績の低下を防ぐことができる。
なお、反応系内に導入したCO及びH2ガスは、反応の進行に伴い減少していくため、予め調製されたCOとH2の混合ガスを適宜補充すると反応制御を簡便に行えることもある。
反応圧力が1MPa以上であれば、十分な反応速度が得られ、原料である化合物(1-1)の残留を抑えることができる。一方、反応圧力が12MPa以下であれば、耐圧性能に優れる高価な設備を必要としなくなるため、経済的に有利である。特に、回分式や半回分式で反応を行う場合、反応終了後にCO及びH2ガスを排出・落圧する必要があり、低圧になるほどCO及びH2ガスの損失が少なくなるため経済的に有利である。
また、ヒドロホルミル化反応で得られた生成物は、そのまま次工程の還元反応の原料として用いることも出来るが、蒸留、抽出、晶析等の精製処理を行った上で、次工程に供してもよい。
工程(iii)では、化合物(1-2)が有するアルデヒド基を水素化して還元することで、上記式(1)で表される熱可塑性樹脂用モノマーを生成する。
アルデヒド基の還元反応は、水素化能を有する触媒及び水素の存在下行われることが好ましい。
触媒としては、例えば、銅、クロム、鉄、亜鉛、アルミニウム、ニッケル、コバルト、及びパラジウムからなる群より選ばれる少なくとも一つの元素を含む触媒が挙げられ、具体的には、Cu-Cr触媒、Cu-Zn触媒、Cu-Zn-Al触媒等の他、Raney-Ni触媒、Raney-Co触媒等が挙げられる。
反応温度を80℃以上にすることで、適度な時間で反応を完結させることができ、生産性の低下や目的物収率の低下を回避することができる。一方、反応温度を180℃以下にすることで、副反応や分解反応の発生を抑制し高い収率で目的物を得ることができる。
水素分圧を0.1MPa以上にすることで、適度な時間で反応を完結させることができ、生産性の低下や目的物収率の低下を回避することができる。一方、水素分圧を20MPa以下にすることで、副反応や分解反応の発生を抑制し、高い収率で目的物を得ることができる。
なお、還元反応の際に、水素ガスと共に、不活性ガス(例えば、窒素又はアルゴン等)を共存させることも可能である。
溶媒としては、例えば、脂肪族炭化水素類、脂環式炭化水素類、芳香族炭化水素類、アルコール類等が挙げられ、これらの中でも、脂環式炭化水素類、芳香族炭化水素類、又はアルコール類が好ましい。具体的には、シクロヘキサン、トルエン、キシレン、メタノール、エタノール、1-プロパノール、2-オクタノール等が好ましい。
また、還元反応で得られた生成物は、例えば、蒸留、抽出、晶析等の精製処理を行ってもよい。
本発明の一態様の熱可塑性樹脂は、前記一般式(1)で表される熱可塑性樹脂用モノマーと、他のモノマーを原料として、溶融重縮合法により製造することができる。
他のモノマーとしては、ホスゲン(塩化カルボニル)、炭酸ジエステル、前記一般式(2a)で表されるジカルボン酸、及び前記一般式(2b)で表されるモノマーから選ばれる1種以上が好ましい。
炭酸ジエステルとしては、例えば、ジフェニルカーボネート、ジトリールカーボネート、ビス(クロロフェニル)カーボネート、m-クレジルカーボネート、ジメチルカーボネート、ジエチルカーボネート、ジブチルカーボネート、ジシクロヘキシルカーボネート等が挙げられる。これらの中でも、反応性及び純度の観点から、ジフェニルカーボネートが好ましい。
炭酸ジエステルの配合量は、ジオール成分及びジカルボン酸成分の合計1モルに対して、好ましくは0.60~1.10モル、より好ましくは0.70~1.05モルである。
2,6位の異性体と、2,7位の異性体との含有量比〔2,6位の異性体/2,7位の異性体〕としては、質量比で、好ましくは1/99~99/1、より好ましくは5/95~95/5、更に好ましくは10/90~90/10、より更に好ましくは20/80~80/20、特に好ましくは35/65~65/35である。
アルカリ金属化合物としては、例えば、アルカリ金属の有機酸塩、無機塩、酸化物、水酸化物、水素化物又はアルコキシド等が挙げられる。これらの中でも、触媒効果、価格、流通量、樹脂の色相への影響等の観点から、炭酸ナトリウム、及び炭酸水素ナトリウムが好ましい。
アルカリ土類金属化合物としては、例えば、アルカリ土類金属化合物の有機酸塩、無機塩、酸化物、水酸化物、水素化物又はアルコキシド等が挙げられる。
含窒素化合物としては、例えば、4級アンモニウムヒドロキシド及びそれらの塩、アミン類等が挙げられる。
これらの中でも、エステル交換触媒としては、酢酸亜鉛、酢酸ジルコニウム、及びチタンテトラブトキサイドから選ばれる1種以上が好ましく、チタンテトラブトキサイドがより好ましい。
次いで、反応系の減圧度を上げながら、反応温度を高めてジオール化合物と、他のモノマーとの反応を行い、最終的には1mmHg以下の減圧下、200~350℃の温度で0.05~2時間重縮合反応を行うことが好ましい。
このような反応は、連続式で行ってもよく、バッチ式で行ってもよい。
上記の反応を行うに際して用いられる反応装置は、錨型攪拌翼、マックスブレンド攪拌翼、ヘリカルリボン型攪拌翼等を装備した縦型であってもよく、パドル翼、格子翼、メガネ翼等を装備した横型であってもスクリューを装備した押出機型であってもよく、また、これらを重合物の粘度を勘案して適宜組み合わせた反応装置を使用することが好適に実施される。
一般的には、公知の酸性物質の添加によって、触媒の失活を行う方法が実施される。
触媒を失活させる酸性物質としては、例えば、安息香酸ブチル等のエステル類、p-トルエンスルホン酸等の芳香族スルホン酸類、p-トルエンスルホン酸ブチル、p-トルエンスルホン酸ヘキシル等の芳香族スルホン酸エステル類、亜リン酸、リン酸、ホスホン酸等のリン酸類、亜リン酸トリフェニル、亜リン酸モノフェニル、亜リン酸ジフェニル、亜リン酸ジエチル、亜リン酸ジn-プロピル、亜リン酸ジn-ブチル、亜リン酸ジn-ヘキシル、亜リン酸ジオクチル、亜リン酸モノオクチル等の亜リン酸エステル類、リン酸トリフェニルリン酸ジフェニル、リン酸モノフェニル、リン酸ジブチル、リン酸ジオクチル、リン酸モノオクチル等のリン酸エステル類、ジフェニルホスホン酸、ジオクチルホスホン酸、ジブチルホスホン酸等のホスホン酸類、フェニルホスホン酸ジエチル等のホスホン酸エステル類、トリフェニルホスフィン、ビス(ジフェニルホスフィノ)エタン等のホスフィン類、ホウ酸、フェニルホウ酸等のホウ酸類、ドデシルベンゼンスルホン酸テトラブチルホスホニウム塩等の芳香族スルホン酸塩類、ステアリン酸クロライド、塩化ベンゾイル、p-トルエンスルホン酸クロライド等の有機ハロゲン化物、ジメチル硫酸等のアルキル硫酸、塩化ンジル等の有機ハロゲン化物等が挙げられる。
これらの中でも、失活効果、樹脂の色相や安定性の観点から、p-トルエンスルホン酸ブチルを用いるのが好ましい。
また、触媒を失活させる酸性物質の添加量は、触媒量1モルに対して、好ましくは0.01~50モル、より好ましくは0.3~20モルである。
濾過で使用するフィルターのメッシュは、好ましくは5μm以下、より好ましくは1μm以下である。
ポリマーフィルターのメッシュは、好ましくは100μm以下、より好ましくは30μm以下である。また、樹脂ペレットを採取する工程は当然低ダスト環境でなければならず、好ましくはクラス1000以下であり、より好ましくはクラス100以下である。
本発明の一態様の熱可塑性樹脂は、より優れた光学特性を有する成形体を製造し得、例えば、低比重化、低複屈折化、光弾性係数の低減化、及び高硬度化した成形体の形成材料となり得る。
なお、本明細書において、屈折率は、JIS K7142に準拠して測定された値を意味する。
なお、本明細書において、比重は、JIS K7112に準拠して測定された値を意味する。
なお、本明細書において、光弾性係数は、エリプソメータ(例えば、日本分光製、製品名「M-220」)を用いて測定された値を意味する。
なお、本明細書において、鉛筆硬度は、JIS-K5600-5-4に準拠して測定された値を意味する。
本発明の一態様の成形体は、上述の熱可塑性樹脂を含む樹脂組成物を成形してなるものである。
成形体の成形材料である樹脂組成物は、上述の熱可塑性樹脂のみから構成されていてもよいが、さらに添加剤を含有してもよい。
本発明の一態様において、前記熱可塑性樹脂の含有量としては、成形品の種類に応じて適宜設定されるが、樹脂組成物の全量(100質量%)に対して、通常30~100質量%、好ましくは50~100質量%、より好ましくは60~100質量%、更に好ましくは70~100質量%、より更に好ましくは80~100質量%である。
これらの添加剤は、それぞれ、一種のみを用いてもよく、二種以上を併用してもよい。
本発明の一態様で用いる酸化防止剤としては、例えば、トリエチレングリコール-ビス[3-(3-tert-ブチル-5-メチル-4-ヒドロキシフェニル)プロピオネート]、1,6-ヘキサンジオール-ビス[3-(3,5-ジ-tert-ブチル-4-ヒドロキシフェニル)プロピオネート]、ペンタエリスリトール-テトラキス[3-(3,5-ジ-tert-ブチル-4-ヒドロキシフェニル)プロピオネート]、オクタデシル-3-(3,5-ジ-tert-ブチル-4-ヒドロキシフェニル)プロピオネート、1,3,5-トリメチル-2,4,6-トリス(3,5-ジ-tert-ブチル-4-ヒドロキシベンジル)ベンゼン、N,N-ヘキサメチレンビス(3,5-ジ-tert-ブチル-4-ヒドロキシ-ヒドロシンナマイド)、3,5-ジ-tert-ブチル-4-ヒドロキシ-ベンジルホスホネート-ジエチルエステル、トリス(3,5-ジ-tert-ブチル-4-ヒドロキシベンジル)イソシアヌレート及び3,9-ビス{1,1-ジメチル-2-[β-(3-tert-ブチル-4-ヒドロキシ-5-メチルフェニル)プロピオニルオキシ]エチル}-2,4,8,10-テトラオキサスピロ(5,5)ウンデカン等が挙げられる。
本発明の一態様で用いる離型剤としては、アルコールと脂肪酸とのエステルを含むことが好ましく、当該エステルを離型剤の全量に対して、90~100質量%含むことがより好ましい。
当該エステルとしては、例えば、一価アルコールと脂肪酸とのエステルや、多価アルコールと脂肪酸との部分エステル又は完全エステルが挙げられる。
具体的な一価アルコールと飽和脂肪酸とのエステルとしては、ステアリルステアレート、パルミチルパルミテート、ブチルステアレート、メチルラウレート、イソプロピルパルミテート等が挙げられる。
具体的な多価アルコールと脂肪酸との部分エステルあるいは全エステルとしては、ステアリン酸モノグリセリド、ステアリン酸モノグリセリド、ステアリン酸ジグリセリド、ステアリン酸トリグリセリド、ステアリン酸モノソルビテート、ベヘニン酸モノグリセリド、カプリン酸モノグリセリド、ラウリン酸モノグリセリド、ペンタエリスリトールモノステアレート、ペンタエリスリトールテトラステアレート、ペンタエリスリトールテトラペラルゴネート、プロピレングリコールモノステアレート、ビフェニルビフェネ-ト、ソルビタンモノステアレート、2-エチルヘキシルステアレート、ジペンタエリスリトールヘキサステアレート等のジペンタエリスルトールの部分エステル又は完全エステル等が挙げられる。
本発明の一態様で用いる加工安定剤としては、例えば、2-t-ブチル-6-(3-t-ブチル-2-ヒドロキシ-5-メチルベンジル)-4-メチルフェニルアクリレート、2,4-ジ-t-ブチル-6-〔1-(3,5-ジ-t-ブチル-2-ヒドロキシフェニル)エチル〕フェニルアクリレート、2,4-ジ-t-アミル-6-〔1-(3,5-ジ-t-アミル-2-ヒドロキシフェニル)エチル〕フェニルアクリレート、2-t-ブチル-6-(3-t-ブチル-2-ヒドロキシ-5-メチルベンジル)-4-メチルフェニルメタクリレート、2,4-ジ-t-アミル-6-〔1-(3,5-ジ-t-アミル-2-ヒドロキシフェニル)エチル〕フェニルメタクリレート等が挙げられる。
当該加工安定剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.01~3.0質量%である。
本発明の一態様で用いる紫外線吸収剤としては、例えば、ベンゾフェノン類、ベンゾトリアゾール類、トリアジン類、ベンゾエート類、サリシレート類、シアノアクリレート類、蓚酸アニリド類、マロン酸エステル類、及びホルムアミジン類等が挙げられる。
当該紫外線吸収剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.001~3.0質量%である。
本発明の一態様で用いる流動性改質剤としては、例えば、「メタブレンTP-001」、「メタブレンTP-003」(商品名、三菱レイヨン株式会社製)等が挙げられる。
当該流動性改質剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.01~10.0質量%である。
本発明の一態様で用いる結晶核剤としては、無機系結晶核剤であってもよく、有機系結晶核剤であってもよい。
無機系結晶核剤としては、例えば、天然又は合成珪酸塩化合物、酸化チタン、硫酸バリウム、リン酸三カルシウム、炭酸カルシウム、リン酸ソーダ、カオリナイト、ハロイサイト、タルク、スメクタイト、バーミュライト、マイカ等が挙げられる。
有機系結晶核剤としては、例えば、アミド;安息香酸ナトリウム、アルミニウムジベンゾエート、カリウムベンゾエート、リチウムベンゾエート、ソジウムβ-ナフタレートソジウムシクロヘキシサンカルボキシレート、フェニルホスホン酸亜鉛等の有機酸金属塩;1,3:2,4-ビス-O-(4-メチルベンジリデン)-D-ソルビトール等のソルビトール誘導体、ノニトール誘導体等が挙げられる。
当該結晶核剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.01~3.0質量%である。
本発明の一態様で用いる強化剤としては、例えば、ガラス繊維、セラミック繊維、炭素繊維、金属被覆ガラス繊維等の無機繊維又は有機繊維等が挙げられる。また、これらは、その表面がシラン系化合物等で表面処理されていてもよい。
当該強化剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.01~3.0質量%である。
本発明の一態様で用いる染料としては、例えば、ニトロソ染料、ニトロ染料、アゾ染料、スチルベンアゾ染料、ケトイミン染料、トリフェニルメタン染料、キサンテン染料、アクリジン染料、キノリン染料、メチン/ポリメチン染料、チアゾール染料、インダミン/インドフェノール染料、アジン染料、オキサジン染料、チアジン染料、硫化染料、アミノケトン/オキシケトン染料、アントラキノン染料、インジゴイド染料、フタロシアニン染料が挙げられる。
当該染料の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.001~3.0質量%である。
本発明の一態様で用いる帯電防止剤としては、例えば、酸化亜鉛、酸化チタン、カーボンブラック等の無機系帯電防止剤;導電性ポリマー、有機系界面活性剤等の有機系帯電防止剤等が挙げられる
当該帯電防止剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.001~3.0質量%である。
本発明の一態様で用いるブルーイング剤としては、一般的なポリカーボネート樹脂と共に用いられるものを使用することができ、例えば、アンスラキノン系染料等が挙げられる。
当該ブルーイング剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.0001~0.001質量%である。
本発明の一態様で用いる抗菌剤としては、例えば、塩素系抗菌剤、フェノール系抗菌剤、イミダゾール系抗菌剤、チアゾール系抗菌剤、第4級アンモニウム系抗菌剤等の有機系抗菌剤や、銀、亜鉛等の金属を保持含有させたゼオライト系抗菌剤、アパタイト系抗菌剤、シリカアルミナ系抗菌剤、セラミック系抗菌剤、リン酸ジルコニウム系抗菌剤、シリカゲル系抗菌剤、ヒドロキシアパタイト系抗菌剤、珪酸カルシウム系抗菌剤等の無機系抗菌剤が挙げられる。
当該抗菌剤の含有量は、樹脂組成物の全量(100質量%)に対して、好ましくは0.01~3.0質量%である。
樹脂組成物中のフェノール成分の含有量は、当該樹脂組成物の全量(100質量%)に対して、好ましくは0.1~3000質量ppm、より好ましくは0.1~2000質量ppm、より好ましくは1~1000質量ppm、更に好ましくは1~800質量ppm、更に好ましくは1~500質量ppm、より更に好ましくは1~300質量ppmである。
また、樹脂組成物中の原料モノマーの含有量は、当該樹脂組成物の全量(100質量%)に対して、好ましくは0.1~3000質量ppm、より好ましくは0.1~1000質量ppm、更に好ましくは1~500質量ppmである。
光学部材としては、例えば、フィルム、プリズム、光学レンズ等が挙げられるが、特に光学レンズが好ましい。
本発明の一態様の光学レンズの表面には、必要に応じ、反射防止層が設けられていてもよい。
反射防止層は、単層であってもよく、多層であってもよい。
また、反射防止層は、有機物から形成されていてもよく、無機物から形成されていてもよいが、無機物から形成されていることが好ましい。
反射防止層を形成する無機物としては、例えば、酸化ケイ素、酸化アルミニウム、酸化ジルコニウム、酸化チタニウム、酸化セリウム、酸化マグネシウム、フッ化マグネシウム等の酸化物あるいはフッ化物が例示される。
これらの中でも、酸化ケイ素、及び酸化ジルコニウムが好ましく、酸化ケイ素と酸化ジルコニウムを併用することがより好ましい。
また、反射防止層に関しては、単層/多層の組み合わせ、またそれらの成分、厚さの組み合わせ等について特に限定はされないが、好ましくは2層構成又は3層構成、特に好ましくは3層構成である。また、該反射防止層全体として、光学レンズの厚さの0.00017~3.3%、具体的には0.05~3μm、特に好ましくは1~2μmとなる厚さで形成するのが好ましい。
ゲル浸透クロマトグラフィー(GPC)を用い、テトラヒドロフランを展開溶媒として、既知の分子量(分子量分布=1)の標準ポリスチレンを用いて検量線を作成した。この検量線に基づいてGPCのリテンションタイムから算出した。
(2)屈折率nd
樹脂を直径40mm、厚さ3mmの大きさの円板に、プレス成形(成形条件:200℃、100kgf/cm2、2分)し、直角に切り出した試験片に対して、精密屈折計(株式会社島津製作所製、製品名「KPR-200」)を用いて測定した。
(3)ガラス転移温度(Tg)
JIS K7121-1987に準拠して、示差熱走査熱量分析計(DSC)を用いて測定した。
(4)比重
上記(4)の屈折率ndの測定で用いた試験片に対して、JIS K7112に準拠して電子比重計(ALFAMiRAGE製、製品名「電子比重計SD-200L」)を用いて、フィルム(成形体)の比重を測定した。
(5)複屈折
樹脂をそれぞれ厚さ100μmのフィルムとし、樹脂のTg+20℃で、一軸1.5倍延伸を行い、600nmにおける位相差を、エリプソメータ(日本分光製、製品名「M-220」)を用いて測定し、複屈折の値を得た。
(6)光弾性係数
樹脂をそれぞれ厚さ100μmのフィルムとし、エリプソメータ(日本分光製、製品名「M-220」)を用いて測定した。
(7)鉛筆硬度
樹脂をそれぞれ厚さ100μmのフィルムとし、JIS K5600-5-4に準拠して、各種硬度の鉛筆(三菱鉛筆(株)製、製品名「ユニ」)を用いて測定した。
・D-NDM-Me:デカヒドロ-1,4:5,8-ジメタノナフタレン-3-メチル-ジメタノール(前記一般式(1)中のR1がメチル基、R2及びR3が水素原子である化合物)
・D-NDM:デカヒドロ-1,4:5,8-ジメタノナフタレンジメタノール(前記一般式(1)中のR1、R2及びR3が水素原子である化合物)
・BPA:2,2’-ビス(4-ヒドロキシフェニル)プロパン
・EG:エチレングリコール
・FDPM:フルオレン-9,9-ジプロピオン酸ジメチル
・DMT:テレフタル酸ジメチル
(1)ガスクロマトグラフィー測定条件
・分析装置:株式会社島津製作所製、キャピラリガスクロマトグラフGC-2010 Plus
・分析カラム:ジーエルサイエンス株式会社製、InertCap1(30m、0.32mmI.D.、膜厚0.25μm)
・オーブン温度:60℃(0.5分間)-昇温速度15℃/分-280℃(4分間)
・検出器:FID、温度280℃
(2)GC-MS測定条件
・分析装置:株式会社島津製作所製、GCMS-QP2010 Plus
・イオン化電圧:70eV
・分析カラム:Agilent Technologies製、DB-1(30m、0.32mmI.D.、膜厚1.00μm)
・オーブン温度:60℃(0.5分間)-昇温速度15℃/分-280℃(4分間)
・検出器温度:280℃
500mLステンレス製反応器に、クロトンアルデヒド149.8g(2.14mol)、ジシクロペンタジエン202.9g(1.53mol)を仕込み、210℃で3時間反応させた。
反応終了後、上記式(1-1)-1で表される化合物116.0gとトリシクロペンタジエン22.0gを含有する反応液を得た。この反応液を単蒸留精製した後の反応液は、ほぼ全量を次工程の反応に供した。
500mlステンレス製反応器に、上記工程(i)で得た上記式(1-1)-1で表される化合物106.8g(0.53mol)と、トリシクロペンタジエン19.8g(0.10mol)の混合液を加え、更に、2-オクタノール120g(0.92mol)、亜リン酸トリフェニル0.58g(1.88mmol)、Rh(acac)(CO)2を0.005g(0.019mmol)を加えた。
そして、反応器内を、窒素及びCO/H2混合ガス(CO/H2=1/1(モル比))による置換を、それぞれ3回行った。次いで、CO/H2混合ガス(CO/H2=1/1(モル比))で系内を加圧して2MPaとし、100℃にて3時間反応を行った。
反応終了後、反応液のガスクロマトグラフィー分析を行ったところ、上記式(1-2)-1で表される二官能性化合物118.3g(0.51mol)と、ペンタシクロペンタデセンモノアルデヒド22.0g(0.10mol)を含む反応液(転化率99.5%、選択率97%)であることを確認した。なお、この反応液は、ほぼ全量を次工程の反応に供した。
500mlステンレス製反応器に、上記工程(ii)で得た上記式(1-2)-1で表される二官能性化合物116.0g(0.50mol)と、ペンタシクロペンタデセンモノアルデヒド21.5g(0.09mol)を含む反応液を加え、更に、2-オクタノール118g(0.90mol)、Cu-Zn-Al触媒(日揮触媒化成株式会社製、製品名「E-01X」)7gを加えた。
そして、水素ガスで系内を加圧して2MPaとし、140℃で5時間反応を行った。
反応終了後、得られたスラリーをメタノールで希釈し、孔径0.2μmのメンブレンフィルターで触媒をろ過した後、エバポレーターを使用して溶媒を留去し、濃縮液を得た。
この濃縮液を、ガスクロマトグラフィー及びGC-MSで分析したところ、分子量236の上記式(1)-1で表されるD-NDM-Meを115.0g(0.49mol)含有することが確認された(主生成物収率98%)。これをさらに蒸留精製して、D-NDM-Me101.2g(0.43mol、純度99.6GC%、蒸留収率88%)を得た。
なお、得られた上記式(1)-1で表されるD-NDM-Meにおいて、「2,6-異性体」(前記一般式(1a)で表される化合物)/「2,7-異性体」(前記一般式(1b)で表される化合物)=35/65~65/35(質量比)であった。
製造例1で合成したD-NDM-Meを250.00g(1.058mol)、ジフェニルカーボネートを229.00g(1.069mol)、及びチタンテトラブトキサイドを20.0mg(6.0×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に添加し、窒素ガスで系内を導入し、窒素雰囲気101.3kPaの下で、攪拌しながら、1時間かけて180℃まで加熱した。そして、180℃に到達した後、30分かけて40kPaまで減圧すると共に、減圧開始から2時間かけて255℃まで昇温をしつつ、留出メタノール及び留出フェノールが60%となったところで、さらに1時間かけて0.133kPa以下まで減圧した。その後、0.133kPa以下で30分間保持して、ポリカーボネート樹脂(1)を得た。
ポリカーボネート樹脂(1)は、前記一般式(I-A)で表される構成単位(式中、R1がメチル基、R2及びR3が水素原子)を有する、Mw=28,000の重合体である。
そして、ポリカーボネート樹脂(1)の物性は、屈折率nd:1.525、Tg:127℃、比重:1.16、複屈折:77nm、光弾性係数:7×10-12Pa-1、鉛筆硬度:Fであった。
製造例1で合成したD-NDM-Meを210.00g(0.888mol)、FDPMを66.00g(0.195mol)、ジフェニルカーボネートを153.00g(0.714mol)、及びチタンテトラブトキサイドを30.0mg(8.8×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、実施例1と同様に操作し、ポリエステルカーボネート樹脂(2)を得た。
ポリエステルカーボネート樹脂(2)は、前記一般式(I-A)で表される構成単位及び前記一般式(I-B)で表される構成単位(各式中、R1がメチル基、R2及びR3が水素原子であり、式(I-B)中のQが上記式(i)で表される基(X1及びX2はメチレン基))を有する、Mw=32,000の重合体である。
そして、ポリエステルカーボネート樹脂(2)の物性は、屈折率nd:1.545、Tg:127℃、比重:1.18、複屈折:14nm、光弾性係数:10×10-12Pa-1、鉛筆硬度:Fであった。
製造例1で合成したD-NDM-Meを193.50g(0.819mol)、EGを8.50g(0.137mol)、DMTを79.50g(0.409mol)、ジフェニルカーボネートを118.80g(0.555mol)、及びチタンテトラブトキサイドを19.0mg(5.6×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、実施例1と同様に操作し、ポリエステルカーボネート樹脂(3)を得た。
ポリエステルカーボネート樹脂(3)は、前記一般式(I-A)で表される構成単位及び前記一般式(I-B)で表される構成単位(各式中、R1がメチル基、R2及びR3が水素原子であり、式(I-B)中のQがフェニレン基)を有する、Mw=29,000の重合体である。
そして、ポリエステルカーボネート樹脂(3)の物性は、屈折率nd:1.537、Tg:134℃、比重:1.20、複屈折:95nm、光弾性係数:35×10-12Pa-1、鉛筆硬度:Fであった。
製造例1で合成したD-NDM-Meを171.06g(0.724mol)、EGを78.61g(1.267mol)、DMTを175.68g(0.905mol)、及びチタンテトラブトキサイドを18.0mg(5.3×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、窒素雰囲気下、230℃まで昇温後、1時間保持し、所定量のメタノールを留出させた。
その後、昇温と減圧を徐々に行い、過剰量のEGを留出させつつ、最終的に270℃、0.1kPa以下で重縮合を行った。適度な溶融粘度になった時点で反応を終了し、ポリエステル樹脂(4)を得た。
ポリエステル樹脂(4)は、前記一般式(I-B)で表される構成単位(式中、R1がメチル基、R2及びR3が水素原子、Qがフェニレン基)を有する、Mw=28,000の共重合体である。
そして、ポリエステル樹脂(4)の物性は、屈折率nd:1.548、Tg:130℃、比重:1.22、複屈折:134nm、光弾性係数:55×10-12Pa-1、鉛筆硬度:Fであった。
特許文献3に記載の方法で合成したD-NDMを250.00g(1.124mol)、ジフェニルカーボネートを243.50g(1.137mol)、及び炭酸水素ナトリウムを0.8mg(9.9×10-6mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、実施例1と同様に操作し、Mw=32,000のポリカーボネート樹脂(i)を得た。
このポリカーボネート樹脂(i)の物性は、屈折率nd:1.531、Tg:133℃、比重:1.20、複屈折:100nm、光弾性係数:8×10-12Pa-1、鉛筆硬度:2Bであった。
BPAを255.00g(1.117mol)、ジフェニルカーボネートを245.00g(1.144mol)、及び炭酸水素ナトリウムを0.8mg(9.9×10-6mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、実施例1と同様に操作し、Mw=33,000のポリカーボネート樹脂(ii)を得た。
このポリエステルカーボネート樹脂(ii)の物性は、屈折率nd:1.582、Tg:143℃、比重:1.20、複屈折:548nm、光弾性係数:80×10-12Pa-1、鉛筆硬度:2Bであった。
特許文献3に記載の方法で合成したD-NDMを200.00g(0.900mol)、FDPMを66.67g(0.197mol)、ジフェニルカーボネートを155.00g(0.724mol)、及びチタンテトラブトキサイドを29.1mg(8.6×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、実施例1と同様に操作し、Mw=32,000のポリエステルカーボネート樹脂(iii)を得た。
このポリエステルカーボネート樹脂(iii)の物性は、屈折率nd:1.550、Tg:132℃、比重:1.21、複屈折:20nm、光弾性係数:11×10-12Pa-1、鉛筆硬度:Bであった。
特許文献3に記載の方法で合成したD-NDMを182.20g(0.820mol)、EGを8.50g(0.137mol)、DMTを79.50g(0.409mol)、ジフェニルカーボネートを119.00g(0.556mol)、及びチタンテトラブトキサイドを18.0mg(5.3×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、実施例1と同様に操作し、Mw=28,000のポリエステルカーボネート樹脂(iv)を得た。
このポリエステルカーボネート樹脂(iv)の物性は、屈折率nd:1.540、Tg:137℃、比重:1.22、複屈折:130nm、光弾性係数:48×10-12Pa-1、鉛筆硬度:Bであった。
特許文献3に記載の方法で合成したD-NDMを166.55g(0.749mol)、EGを81.37g(1.311mol)、DMTを181.83g(0.936mol)、及びチタンテトラブトキサイド:18.0mg(5.3×10-5mol)、それぞれ攪拌機及び留出装置付きの500mL反応器に入れ、窒素雰囲気下、230℃まで昇温後、1時間保持し、所定量のメタノールを留出させた。
その後、昇温と減圧を徐々に行い、過剰量のEGを留出させつつ、最終的に270℃、0.1kPa以下で重縮合を行った。適度な溶融粘度になった時点で反応を終了し、Mw=29,000のポリエステル樹脂(v)を得た。
このポリエステル樹脂(v)の物性は、屈折率nd:1.551、Tg:135℃、比重:1.24、複屈折:162nm、光弾性係数:65×10-12Pa-1、鉛筆硬度:Bであった。
なお、表1におけるそれぞれの樹脂中の各モノマーに由来する構成単位の含有量比は、下記の1H-NMR測定条件に基づき、各モノマーに帰属する1Hの存在比を測定することで算出した。
(1H-NMR測定条件)
・装置:日本電子株式会社製、JNM-ECA500(500MHz)
・測定モード:1H-NMR
・溶媒:CDCl3(重クロロホルム)
・内部標準物質:テトラメチルシラン
一方で、比較例1~5で得た熱可塑性樹脂を用いて成形したフィルムは、複屈折、比重、光弾性係数、及び鉛筆硬度の特性の少なくとも一つが、十分に満足するものではなかった。
Claims (17)
- 構成単位(a)と、構成単位(b)との含有量比〔(a)/(b)〕が、質量比で、1/99~99/1である、請求項2に記載の熱可塑性樹脂。
- 前記熱可塑性樹脂が、ポリカーボネート樹脂、ポリエステル樹脂、又はポリエステルカーボネート樹脂である、請求項1~3のいずれか一項に記載の熱可塑性樹脂。
- 前記熱可塑性樹脂の重量平均分子量(Mw)が5,000~50,000である、請求項1~9のいずれか一項に記載の熱可塑性樹脂。
- R1が、メチル基、エチル基、又はフェニル基であり、R2及びR3が、水素原子である、請求項1~10のいずれか一項に記載の熱可塑性樹脂。
- R1がメチル基であり、R2及びR3が、水素原子である、請求項1~11のいずれか一項に記載の熱可塑性樹脂。
- 請求項1~12のいずれか一項に記載の熱可塑性樹脂を含む樹脂組成物を成形してなる、成形体。
- 前記成形体が、光学部材である、請求項13に記載の成形体。
- 前記成形体が、光学レンズである、請求項13又は14に記載の成形体。
- 前記熱可塑性樹脂用モノマーが、光学部材の成形材料として用いられる熱可塑性樹脂を構成するモノマーである、請求項16に記載の熱可塑性樹脂用モノマー。