WO2020085687A1 - 클램프용 고강도 페라이트계 스테인리스강 및 그 제조방법 - Google Patents
클램프용 고강도 페라이트계 스테인리스강 및 그 제조방법 Download PDFInfo
- Publication number
- WO2020085687A1 WO2020085687A1 PCT/KR2019/013233 KR2019013233W WO2020085687A1 WO 2020085687 A1 WO2020085687 A1 WO 2020085687A1 KR 2019013233 W KR2019013233 W KR 2019013233W WO 2020085687 A1 WO2020085687 A1 WO 2020085687A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- stainless steel
- ferritic stainless
- strength
- less
- clamps
- Prior art date
Abstract
자동차 또는 일반 호스의 클램프에 적용될 수 있는 고강도 페라이트계 스테인리스강 및 그 제조방법이 개시된다. 본 발명의 일 실시예에 따른 클램프용 고강도 페라이트계 스테인리스강은, 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1) 및 (2)를 만족하며, 평균 직경 0.5㎛ 이하의 석출물의 수가 2.5×106 개/㎟ 이상이다. (1) 0.35% ≤ Si+Al+V ≤ 0.6% (2) 0.09% ≤ C+N ≤ 0.12%
Description
본 발명은 고강도 페라이트계 스테인리스강에 대한 것으로, 보다 상세하게는 자동차 또는 일반 호스의 클램프에 적용될 수 있는 고강도 페라이트계 스테인리스강 및 그 제조방법에 관한 것이다.
페라이트계 스테인리스강은 오스테나이트계 스테인리스강에 비해 가격이 저렴하고 열팽창률이 낮으며 표면광택, 성형성 및 내산화성이 양호하여 내열기구, 싱크대 상판, 외장재, 가전제품, 전자부품 등에 널리 사용되고 있다. 페라이트계 스테인리스강 냉연 박판의 경우 열간압연 공정, 열간압연된 코일의 표면 스케일을 제거하고 재료 내부 응력을 제거하는 소둔산세 공정, 냉간압연 및 소둔 공정을 통해 제조된다.
도 1은 자동차 또는 일반 호스용 클램프를 나타낸다. 클램프는 플라스틱 호스 또는 파이프를 체결하는 역할을 하기 때문에 높은 강도를 필요로 하며, 벤딩 시 크랙 발생이 없어야 하기 때문에 우수한 연성도 동시에 요구된다. 또한, 실내뿐만 아니라 자동차의 실외 환경에 사용되어짐에 따라 내식성이 요구되기 때문에 최근 클램프용 스테인리스강의 수요가 증대되고 있는 상황이다.
일반적으로 제조되는 410UF와 같은 Utility Ferrite의 경우 Cr 함유량이 12% 수준으로 내식성이 열위하며, 연신율이 낮아 클램프용으로 사용할 수 없다. 따라서, 상대적으로 Cr 함유량이 높은 16%Cr 430계(일반 430, 430LX)를 사용하려고 시도하고 있으나, 낮은 인장강도로 시장의 요구를 만족시키기 어려운 실정이다. 시장의 요구사항(SPEC.)인 압연방향 기준으로 0˚, 45˚, 90˚ 3방향 모두에서의 인장강도(TS) 510MPa 이상, 항복강도(YS) 320MPa 이상, 연신율(El) 20% 이상을 만족하기 위해서는 성분계 개발 및 제조공정의 최적화가 선행되어야 한다.
STS430으로 대표되는 페라이트계 스테인리스강에서의 주요 품질 이슈는 리징(Ridging) 개선, 오렌지필(Orange Peel) 개선, 성형시 면 내 이방성 개선과 관련하여 선행 특허 기술들이 다수 존재하나, 자동차 또는 일반 호스의 클램프 용도로 적용될 수 있도록 고강도를 만족하는 성분계에 대한 검토와 제조기술 최적화에 대한 연구는 거의 없는 실정이다.
본 발명은 성분계 중 Si, Al, V, C, N 등의 함량, 열연 무소둔에 의한 석출물 크기 및 석출량 제어를 통해 고강도 구현이 가능한 페라이트계 스테인리스강 및 그 제조방법을 제공하고자 한다.
본 발명의 일 실시예에 따른 클램프용 고강도 페라이트계 스테인리스강은, 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1) 및 (2)를 만족하며, 평균 직경 0.5㎛ 이하의 석출물의 수가 2.5×106 개/㎟ 이상이다.
(1) 0.35% ≤ Si+Al+V ≤ 0.6%
(2) 0.09% ≤ C+N ≤ 0.12%
여기서, Si, Al, V, C, N은 각 원소의 함량(중량%)를 의미한다.
또한, 본 발명의 일 실시예에 따르면, Ni: 0.001 내지 0.5%, P: 0.05% 이하 및 S: 0.005% 이하로 이루어진 그룹에서 선택되는 어느 하나 이상을 더 포함할 수 있다.
또한, 본 발명의 일 실시예에 따르면, 상기 석출물은 Cr 탄질화물을 포함할 수 있다.
또한, 본 발명의 일 실시예에 따르면, 항복강도 320MPa 이상, 인장강도 510MPa 이상 및 연신율 20% 이상일 수 있다.
본 발명의 일 실시예에 따른 클램프용 고강도 페라이트계 스테인리스강 제조방법은, 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1) 및 (2)를 만족하는 슬라브를 1,000 내지 1,200℃로 재가열하여 열간압연하는 단계; 상기 열연강판을 700℃ 이상에서 권취하는 단계; 상기 권취된 열연강판을 60% 이상 압하율로 냉간압연하는 단계; 및 상기 냉연강판을 550 내지 950℃에서 10분 이하 소둔 열처리하는 단계;를 포함하고, 상기 권취된 열연강판의 소둔 열처리를 생략하는 것을 특징으로 한다.
(1) 0.35% ≤ Si+Al+V ≤ 0.6%
(2) 0.09% ≤ C+N ≤ 0.12%
또한, 본 발명의 일 실시예에 따르면, 상기 소둔 열처리된 냉연강판은, 평균 직경 0.5㎛ 이하의 석출물의 수가 2.5×106 개/㎟ 이상일 수 있다.
또한, 본 발명의 일 실시예에 따르면, 상기 석출물은 Cr 탄질화물을 포함할 수 있다.
또한, 본 발명의 일 실시예에 따르면, 상기 소둔 열처리된 냉연강판은, 항복강도 320MPa 이상, 인장강도 510MPa 이상 및 연신율 20% 이상일 수 있다.
본 발명의 실시예에 따른 고강도 페라이트계 스테인리스강은 항복강도 320MPa 이상, 인장강도 510MPa 이상 및 연신율 20% 이상을 만족하여 자동차 등의 클램프 용도로 사용될 수 있다.
도 1은 일반적인 클램프(Clamp)의 형상을 나타내는 그림이다.
도 2는 본 발명의 식 (1)의 값에 따른 항복강도(YS)를 나타내는 그래프이다.
도 3은 본 발명의 식 (2)의 값에 따른 인장강도(TS)를 나타내는 그래프이다.
도 4는 본 발명의 실시예에 따른 발명예와 비교예의 석출물을 주사전자현미경(SEM)과 투과전자현미경(TEM)으로 촬영한 사진이다.
본 발명의 일 실시예에 따른 클램프용 고강도 페라이트계 스테인리스강은, 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1) 및 (2)를 만족하며, 평균 직경 0.5㎛ 이하의 석출물의 수가 2.5×106 개/㎟ 이상이다.
(1) 0.35% ≤ Si+Al+V ≤ 0.6%
(2) 0.09% ≤ C+N ≤ 0.12%
여기서, Si, Al, V, C, N은 각 원소의 함량(중량%)를 의미한다.
이하에서는 본 발명의 실시 예를 첨부 도면을 참조하여 상세히 설명한다. 이하의 실시 예는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 본 발명의 사상을 충분히 전달하기 위해 제시하는 것이다. 본 발명은 여기서 제시한 실시 예만으로 한정되지 않고 다른 형태로 구체화될 수도 있다. 도면은 본 발명을 명확히 하기 위해 설명과 관계 없는 부분의 도시를 생략하고, 이해를 돕기 위해 구성요소의 크기를 다소 과장하여 표현할 수 있다.
본 발명의 일 실시예에 따른 클램프용 고강도 페라이트계 스테인리스강은, 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함한다.
이하, 본 발명의 합금원소 함량의 수치 한정 이유에 대하여 설명한다. 이하에서는 특별한 언급이 없는 한 단위는 중량%이다.
C의 함량은 0.04 내지 0.1%이다.
강 중 C는 페라이트계 스테인리스강에 불가피하게 포함되는 불순물로서, (Cr,Fe)23C6, (Cr,Fe)7C3 탄화물로 석출되어 강도를 향상시키는 역할을 하므로 0.04% 이상 함유한다. 하지만, 모재 내에 과하게 포함될 경우에는 연신율을 저하시켜 제품의 가공성을 현저히 저하시키기 때문에 0.1% 이하로 제한한다.
Si의 함량은 0.2 내지 0.6%이다.
Si은 강 중에 포함되는 불가피한 불순물이지만 제강 시 탈산제 역할로 첨가되는 원소로 페라이트 안정화 원소이다. 강 중 다량 함유되면 재질의 경화를 일으켜 연성을 저하시키기 때문에 통상 0.4% 이하로 관리한다. 하지만, 클램프용 고강도 페라이트계 스테인리스강을 제조하기 위해서는 Si을 최적으로 사용할 필요가 있다. 이에 본 발명에서는 Si 함량을 0.2 내지 0.6%로 제어하여 고용강화 효과로 인장강도 및 항복강도를 향상시켰으며, 연신율을 유지하기 위하여 Si 함량을 0.6% 이하로 제한한다.
Mn의 함량은 0.01 내지 1.5%이다.
Mn은 강 중에 불가피하게 포함되는 불순물이지만 오스테나이트 안정화 원소이기 때문에 로핑 및 리징을 억제하는 역할을 한다. 하지만 다량으로 포함될 경우 용접시 망간계 퓸이 발생하며 MnS상 석출의 원인이 되어 연신율을 저하시키기 때문에 그 함유량을 0.01 내지 1.5%로 제한한다.
Cr의 함량은 14.0 내지 18.0%이다.
Cr은 강의 내식성을 향상시키기 위해 첨가하는 합금원소로, 임계함량은 12%이다. 다만, C 및 N이 함유된 페라이트계 스테인리스강은 입계 부식이 일어날 수 있으며 입계 부식 가능성 및 제조단가 증가를 고려하여 그 함유량을 14.0 내지 18.0%로 제한한다.
Al의 함량은 0.005 내지 0.2%이다.
Al은 강력한 탈산제로써 용강 중 산소의 함량을 낮추는 역할을 하며, 본 발명에서는 0.005% 이상 첨가한다. 다만, 그 함량이 과다할 경우 비금속 개재물 증가로 인해 냉연 스트립의 슬리브 결함이 발생함과 동시에, 용접성을 열화시키는 바 0.2% 이하로 한정하고, 보다 바람직하게는 0.1% 이하로 한정할 수 있다.
V의 함량은 0.005 내지 0.2%이다.
V은 C 및 N을 고정하여 탄질화물을 형성하는 역할을 하며, 탄질화물의 성장을 억제하고 미세화시키는데 효과적인 원소로, 본 발명에서는 0.005% 이상 첨가하고 보다 바람직하게는 0.03% 이상 첨가한다. 다만, 그 함량이 과다할 경우 제조 비용이 급증하는바, 0.2% 이하로 한정하고 보다 바람직하게는 0.1% 이하로 한정할 수 있다.
N의 함량은 0.02 내지 0.1%이다.
강 중 N은 C와 동등하게 불순물 원소로 존재하며, 제조 과정에서 Cr2N 질화물로 석출되어 강도를 향상시키는 역할을 하므로 0.02% 이상 첨가한다. 하지만, 다량의 첨가는 가공성을 저해시킬 뿐만 아니라 냉연제품의 스트레처 스트레인의 원인이 되기 때문에 그 함유량을 0.1% 이하로 제한한다.
또한, 본 발명의 일 실시예에 따르면, Ni: 0.001 내지 0.5%, P: 0.05% 이하 및 S: 0.005% 이하로 이루어진 그룹에서 선택되는 어느 하나 이상을 더 포함할 수 있다.
Ni의 함량은 0.001 내지 0.5%이다. Ni은 Cu, Mn과 함께 오스테나이트 안정화 원소로 오스테나이트 분율을 증가시켜 로핑 및 리징을 억제하는 효과가 있으며, 미량 첨가로 내식성을 향상시키는 역할을 한다. 그러나 다량 첨가시 가공성 열화 및 제조단가 증가로 그 함유량을 전술한 범위로 제한한다.
P의 함량은 0.05% 이하이다. P은 강 중에 포함되는 불가피한 불순물로 산세 시 입계부식을 일으키거나 열간가공성을 저해시키기 때문에 그 함유량을 전술한 범위로 조절한다.
S의 함량은 0.005% 이하이다. S은 강 중에 포함되는 불가피한 불순물로 결정입계에 편석되어 열간가공성을 저해시키기 때문에 그 함유량을 전술한 범위로 제한한다.
상술한 합금원소들을 제외한 스테인리스강의 나머지는 Fe 및 기타 불가피한 불순물로 이루어진다.
또한, 위 성분계 조성과 동시에 아래 식 (1) 및 (2)를 만족한다.
(1) 0.35% ≤ Si+Al+V ≤ 0.6%
(2) 0.09% ≤ C+N ≤ 0.12%
본 발명에서는 고강도를 구현하고자 치환형 원소인 Si, Al, V의 함량 증가에 따른 고용강화 효과로 항복강도(YS)를 증가시켜 320 MPa 이상을 나타낼 수 있다. Si+Al+V 값이 0.35% 미만인 경우 목적하는 항복강도를 구현하기 어려우며, 0.6% 초과의 경우 연신율이 저하된다.
또한, C+N 함량 증가를 통해 Cr 탄질화물 석출량을 증가시키고, 열연 소둔 열처리를 생략하여 석출물 미세화 효과로 가공경화량을 증가시킴으로써 인장강도(TS)를 510 MPa 이상으로 구현할 수 있다. C+N 값이 0.09% 미만인 경우 목적하는 인장강도를 구현하기 어려우며, 0.12% 초과의 경우 연신율이 저하된다.
상술한 합금원소 제어에 따른 본 발명의 미세조직은, 평균 직경 0.5㎛ 이하의 석출물을 2.5×106 개/㎟ 이상 포함할 수 있다. 석출물은 C+N 함량 증대에 따른 (Cr,Fe)23C6, (Cr,Fe)7C3 탄화물 또는 Cr2N 질화물, 즉 Cr-탄질화물일 수 있다. 0.5㎛ 이하의 미세한 석출물을 다량 석출시킴으로써 인장 시 가공경화량을 증가시킬 수 있다.
단, Cr-탄질화물의 석출을 위해서는 합금원소 제어 외에 열연 소둔 열처리의 생략이 요구된다.
본 발명의 일 실시예에 따른 클램프용 고강도 페라이트계 스테인리스강 제조방법은, 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고, 식 (1) 및 (2)를 만족하는 슬라브를 1,000 내지 1,200℃로 재가열하여 열간압연하는 단계; 상기 열연강판을 700℃ 이상에서 권취하는 단계; 상기 권취된 열연강판을 60% 이상 압하율로 냉간압연하는 단계; 및 상기 냉연강판을 550 내지 950℃에서 10분 이하 소둔 열처리하는 단계;를 포함한다.
열간압연 마무리온도는 800℃ 이상인 것이 바람직하다. 800℃ 이상의 마무리압연 온도 및 700℃ 이상에서의 권취를 통해 열연코일 상태에서 미세 석출물을 형성시키며, 이후 열연 소둔 열처리를 생략하여 석출물의 조대화를 방지한다.
일반적으로 클램프용으로 사용되는 페라이트계 스테인리스강은 열간압연 후 열연 소둔 열처리로 상소둔(Batch Annealing Furnace)을 수행하는데, 본 발명에서는 열연 소둔 열처리를 생략하는 것을 특징으로 한다. 상소둔(BAF) 수행 시 열연코일의 석출된 미세 석출물들이 조대화되고 총 개수가 적어져 고강도 확보가 어려워진다.
이하 본 발명의 바람직한 실시예를 통해 보다 상세히 설명하기로 한다.
실시예
아래 표 1의 C, N, Si, Al 및 V을 조절한 성분계의 페라이트계 스테인리스강을 Lab. 진공용해를 하여 슬라브로 제조하였다. 슬라브를 1,000 내지 1,200℃에서 재가열한 후 조압연기와 연속 마무리압연기에 의해 800℃ 이상의 마무리압연 완료 온도로 압연하여 열연판을 제조하였다.
강종 | 합금 성분(중량%) | 구분 | ||||||
C | Si | Mn | Cr | Al | V | N | ||
A | 0.0690 | 0.35 | 0.50 | 16.20 | 0.043 | 0.06 | 0.0360 | 발명예 1 |
B | 0.0631 | 0.30 | 0.48 | 16.29 | 0.083 | 0.03 | 0.0329 | 발명예 2 |
C | 0.0680 | 0.14 | 0.49 | 16.17 | 0.033 | 0.01 | 0.0360 | 비교예 1 |
D | 0.0610 | 0.12 | 0.46 | 16.15 | 0.031 | 0.02 | 0.0310 | 비교예 2 |
E | 0.0689 | 0.14 | 0.46 | 16.16 | 0.033 | 0.01 | 0.0261 | 비교예 3 |
F | 0.0631 | 0.20 | 0.48 | 16.25 | 0.081 | 0.01 | 0.0229 | 비교예 4 |
G | 0.0631 | 0.20 | 0.48 | 16.23 | 0.081 | 0.02 | 0.0229 | 비교예 5 |
H | 0.0631 | 0.30 | 0.47 | 16.29 | 0.083 | 0.03 | 0.0329 | 비교예 6 |
I | 0.0590 | 0.12 | 0.47 | 16.14 | 0.078 | 0.01 | 0.0215 | 비교예 7 |
아래 표 2는 표 1의 합금성분을 갖는 강에 대하여 Si+Al+V, C+N으로 정의되는 식 (1) 및 (2)의 수치를 나타내었으며, 열연소둔 조건 및 냉연소둔재의 석출물 수를 나타내었다. 또한 냉연소둔재의 판면에 있어서 압연방향으로부터 0˚ 방향에 대하여, 상온에서 crosshead speed 20 mm/min로 인장시험을 하여 얻어진 항복강도(YS), 인장강도(TS) 및 연신율(EL)을 나타내었다.
구분 | 강종 | 식 (1)(중량%) | 식 (2)(중량%) | 0.5㎛ 이하석출물 수(106 개/㎟) | 열연소둔 | YS(MPa) | TS(MPa) | EL(%) |
발명예 1 | A | 0.453 | 0.105 | 3.6 | 생략 | 335.0 | 568.0 | 25.0 |
발명예 2 | B | 0.414 | 0.096 | 3.2 | 생략 | 321.2 | 533.9 | 24.3 |
비교예 1 | C | 0.183 | 0.104 | 3.0 | 생략 | 303.0 | 546.0 | 23.0 |
비교예 2 | D | 0.171 | 0.092 | 2.8 | 생략 | 304.0 | 538.0 | 25.0 |
비교예 3 | E | 0.183 | 0.095 | 2.7 | 생략 | 297.0 | 513.0 | 27.0 |
비교예 4 | F | 0.292 | 0.086 | 2.6 | 생략 | 307.7 | 509.2 | 24.2 |
비교예 5 | G | 0.312 | 0.086 | 2.4 | 생략 | 317.8 | 504.8 | 25.0 |
비교예 6 | H | 0.414 | 0.096 | 0.2 | BAF | 304.5 | 494.1 | 28.0 |
비교예 7 | I | 0.208 | 0.081 | 0.2 | BAF | 277.9 | 486.1 | 30.1 |
발명예 1, 2
A, B 강종은 페라이트계 스테인리스강의 C, N, Si, Al 및 V을 조절하여 진공 용해한 것으로 상기의 강을 1,000~1,200℃의 온도범위에서 재가열한 후 조압연기와 연속 마무리압연기에 의해 800℃ 이상의 완료온도로 압연하여 열연판을 제조하고 그 후 열연소둔하지 않고 산세한 다음 냉간압연 및 냉연소둔을 실시하였다.
상기 A, B 강종은 Si+Al+V ≥ 0.35% 를 만족함에 따라 항복강도(YS) ≥ 320MPa 을 만족함을 알 수 있다. 또한, A, B 강종은 C+N ≥ 0.09% 를 만족함에 따라 인장강도(TS) ≥ 510MPa 을 만족함을 알 수 있다.
비교예 1~3
C ~ E 강종은 C+N 수치가 0.09% 이상으로 본 발명의 식 (1)은 만족하나, Si+Al+V 수치가 0.35% 이하로 항복강도(YS) 값이 300MPa 수준으로 낮게 나타남을 확인할 수 있었다.
비교예 4, 5
F 강종 및 G 강종은 Si+Al+V 수치가 0.35% 이하 및 C+N 수치가 0.09% 이하로, 항복강도(YS)와 인장강도(TS) 모두 본 발명의 목표 강도 수준을 만족시키지 못함을 알 수 있다.
비교예 6, 7
H 강종은 Si+Al+V 수치가 0.35% 이상을 만족하고 C+N 수치가 0.09% 이상을 만족하나, 열연 BAF 소둔을 실시함에 따라 항복강도(YS) ≥ 320MPa 과 인장강도(TS) ≥ 510MPa 을 만족시키지 못함을 알 수 있다.
또한, I 강종은 Si+Al+V 수치가 0.355 이상을 만족시키지 못하고 C+N 수치가 0.09% 이상을 만족시키지 못할 뿐만 아니라, 열연 BAF 소둔을 실시함에 따라 항복강도(YS)가 280MPa 이하로 낮게 나타났으며 인장강도(TS) 또한 490MPa 이하로 낮게 나타나 본 발명의 목표 강도를 만족시키지 못함을 알 수 있다.
도 2는 본 발명의 식 (1)의 값에 따른 항복강도(YS)를 나타내는 그래프이며, 도 3은 본 발명의 식 (2)의 값에 따른 인장강도(TS)를 나타내는 그래프이다.
도 2 및 도 3을 참조하면, 본 발명에서 고강도를 구현하고자 치환형 원소의 합 Si+Al+V 으로 정의되는 식 (1)의 값을 0.35% 이상으로 제어함으로써 모재의 고용강화 효과로 항복강도를 증가시켜 320MPa 이상으로 구현할 수 있었다. 또한, C+N 으로 정의되는 식 (2)의 값을 0.09% 이상으로 제어하여 Cr-탄질화물 석출량 증대와 함께 열연소둔 공정 생략에 의한 석출물 미세화 효과로 가공경화량을 증가시켜 인장강도를 510MPa 이상으로 구현할 수 있었다.
도 4는 본 발명의 실시예에 따른 발명예와 비교예의 석출물을 주사전자현미경(SEM)과 투과전자현미경(TEM)으로 촬영한 사진이다. 무소둔 열은 발명예 1의 A 강종 사진이며, BAF 열은 비교예 7의 I 강종 사진이다.
발명예 1의 A 강종의 경우 평균 직경 0.5㎛ 이하의 크기를 가지는 석출물이 다량 형성되어 있는 것을 확인할 수 있는 반면, 비교예 7의 I 강종의 경우 0.5 내지 2.0㎛ 크기의 석출물이 형성되어 있는 것을 확인할 수 있었다. 즉, 합금성분 제어와 함께 열연 무소둔이 함께 만족되어야 본 발명의 해결과제를 달성할 수 있음을 알 수 있다.
상술한 바에 있어서, 본 발명의 예시적인 실시예들을 설명하였지만, 본 발명은 이에 한정되지 않으며 해당 기술 분야에서 통상의 지식을 가진 자라면 다음에 기재하는 청구범위의 개념과 범위를 벗어나지 않는 범위 내에서 다양한 변경 및 변형이 가능함을 이해할 수 있을 것이다.
본 발명에 따른 고강도 페라이트계 스테인리스강은 항복강도 320MPa 이상, 인장강도 510MPa 이상 및 연신율 20% 이상을 만족하여 자동차 등의 클램프 용도로 사용될 수 있다.
Claims (8)
- 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고,하기 식 (1) 및 (2)를 만족하며,평균 직경 0.5㎛ 이하의 석출물의 수가 2.5×106 개/㎟ 이상인 클램프용 고강도 페라이트계 스테인리스강.(1) 0.35% ≤ Si+Al+V ≤ 0.6%(2) 0.09% ≤ C+N ≤ 0.12%(여기서, Si, Al, V, C, N은 각 원소의 함량(중량%)를 의미한다)
- 제1항에 있어서,Ni: 0.001 내지 0.5%, P: 0.05% 이하 및 S: 0.005% 이하로 이루어진 그룹에서 선택되는 어느 하나 이상을 더 포함하는 클램프용 고강도 페라이트계 스테인리스강.
- 제1항에 있어서,상기 석출물은 Cr 탄질화물을 포함하는 클램프용 고강도 페라이트계 스테인리스강.
- 제1항에 있어서,항복강도 320MPa 이상, 인장강도 510MPa 이상 및 연신율 20% 이상인 클램프용 고강도 페라이트계 스테인리스강.
- 중량%로, C: 0.04 내지 0.1%, Si: 0.2 내지 0.6%, Mn: 0.01 내지 1.5%, Cr: 14.0 내지 18.0%, Al: 0.005 내지 0.2%, V: 0.005 내지 0.2%, N: 0.02 내지 0.1%, 나머지 Fe 및 불가피한 불순물을 포함하고, 하기 식 (1) 및 (2)를 만족하는 슬라브를 1,000 내지 1,200℃로 재가열하여 열간압연하는 단계;상기 열연강판을 700℃ 이상에서 권취하는 단계;상기 권취된 열연강판을 60% 이상 압하율로 냉간압연하는 단계; 및상기 냉연강판을 550 내지 950℃에서 10분 이하 소둔 열처리하는 단계;를 포함하고,상기 권취된 열연강판의 소둔 열처리를 생략하는 것을 특징으로 하는 클램프용 고강도 페라이트계 스테인리스강 제조방법.(1) 0.35% ≤ Si+Al+V ≤ 0.6%(2) 0.09% ≤ C+N ≤ 0.12%(여기서, Si, Al, V, C, N은 각 원소의 함량(중량%)를 의미한다)
- 제5항에 있어서,상기 소둔 열처리된 냉연강판은,평균 직경 0.5㎛ 이하의 석출물의 수가 2.5×106 개/㎟ 이상인 클램프용 고강도 페라이트계 스테인리스강 제조방법.
- 제6항에 있어서,상기 석출물은 Cr 탄질화물을 포함하는 클램프용 고강도 페라이트계 스테인리스강 제조방법.
- 제5항에 있어서,상기 소둔 열처리된 냉연강판은,항복강도 320MPa 이상, 인장강도 510MPa 이상 및 연신율 20% 이상인 클램프용 고강도 페라이트계 스테인리스강 제조방법.