WO2020080162A1 - Plaque de verre - Google Patents

Plaque de verre Download PDF

Info

Publication number
WO2020080162A1
WO2020080162A1 PCT/JP2019/039489 JP2019039489W WO2020080162A1 WO 2020080162 A1 WO2020080162 A1 WO 2020080162A1 JP 2019039489 W JP2019039489 W JP 2019039489W WO 2020080162 A1 WO2020080162 A1 WO 2020080162A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass
glass plate
plate
resin
less
Prior art date
Application number
PCT/JP2019/039489
Other languages
English (en)
Japanese (ja)
Inventor
田中　歩
洋平 細田
Original Assignee
日本電気硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本電気硝子株式会社 filed Critical 日本電気硝子株式会社
Priority to JP2020553081A priority Critical patent/JPWO2020080162A1/ja
Publication of WO2020080162A1 publication Critical patent/WO2020080162A1/fr

Abstract

Cette plaque de verre est intégrée à une plaque de résine pour produire un composite verre-résine, et est caractérisée en ce que la composition de verre contient, sur une base molaire : 45-80% de SiO2; 5-30% de Al2O3; 0-20% de Li2O + Na2O + K2O; 3-35% de MgO; 1-35% de CaO; et 0-15% de SrO + BaO.
PCT/JP2019/039489 2018-10-15 2019-10-07 Plaque de verre WO2020080162A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2020553081A JPWO2020080162A1 (ja) 2018-10-15 2019-10-07 ガラス板

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018194037 2018-10-15
JP2018-194037 2018-10-15

Publications (1)

Publication Number Publication Date
WO2020080162A1 true WO2020080162A1 (fr) 2020-04-23

Family

ID=70284327

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/039489 WO2020080162A1 (fr) 2018-10-15 2019-10-07 Plaque de verre

Country Status (2)

Country Link
JP (1) JPWO2020080162A1 (fr)
WO (1) WO2020080162A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015143182A (ja) * 2013-12-25 2015-08-06 旭硝子株式会社 可動ホーム柵用のガラス基板および合わせガラス
JP2016052990A (ja) * 2012-05-11 2016-04-14 旭硝子株式会社 積層体用の前面ガラス板および積層体
JP2017520496A (ja) * 2014-05-02 2017-07-27 コーニング インコーポレイテッド 強化ガラスおよびその組成物

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016052990A (ja) * 2012-05-11 2016-04-14 旭硝子株式会社 積層体用の前面ガラス板および積層体
JP2015143182A (ja) * 2013-12-25 2015-08-06 旭硝子株式会社 可動ホーム柵用のガラス基板および合わせガラス
JP2017520496A (ja) * 2014-05-02 2017-07-27 コーニング インコーポレイテッド 強化ガラスおよびその組成物

Also Published As

Publication number Publication date
JPWO2020080162A1 (ja) 2021-09-16

Similar Documents

Publication Publication Date Title
JP6256763B2 (ja) 合わせガラス
JP2020128331A (ja) 軽量複合合わせガラス
JP2019503963A (ja) 非対称ガラス積層板
JP2017508693A (ja) 積層ガラス
WO2017183381A1 (fr) Verre feuilleté pour véhicules
JP2016539890A (ja) 向上したエッジ強度を有するガラスラミネート構造体
EP4265579A2 (fr) Compositions de verre automobile pouvant être mises en forme par fusion, articles et stratifiés associés
WO2018030093A1 (fr) Verre feuilleté pour véhicules
JP2019182692A (ja) ガラス板及びそれを用いたガラス樹脂複合体
WO2018030095A1 (fr) Verre feuilleté pour véhicules
WO2017183382A1 (fr) Verre feuilleté pour véhicules
WO2019070788A1 (fr) Stratifié de verre présentant une faible contrainte de compression, une grande profondeur de couche, une couche de verre interne renforcée chimiquement et procédé associé
JP2018145082A (ja) ガラス樹脂複合体
JP7011227B2 (ja) 車両用合わせガラス
WO2018193788A1 (fr) Composite verre-résine
WO2020080162A1 (fr) Plaque de verre
WO2019151000A1 (fr) Composite verre/résine
WO2018193721A1 (fr) Plaque de verre
WO2018163903A1 (fr) Composite verre-résine
JP2019131430A (ja) ガラス板
JP6959566B2 (ja) ガラス板
JP2019182706A (ja) ガラス板及びそれを用いたガラス樹脂複合体
WO2018163904A1 (fr) Composite de verre et de résine
WO2018163902A1 (fr) Composite verre-résine
JP2019172566A (ja) ガラス樹脂複合体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19873643

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020553081

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19873643

Country of ref document: EP

Kind code of ref document: A1