WO2017130427A1 - Composition de résine photosensible, élément photosensible, procédé de formation de motif de réserve, et procédé de fabrication de panneau tactile - Google Patents
Composition de résine photosensible, élément photosensible, procédé de formation de motif de réserve, et procédé de fabrication de panneau tactile Download PDFInfo
- Publication number
- WO2017130427A1 WO2017130427A1 PCT/JP2016/059953 JP2016059953W WO2017130427A1 WO 2017130427 A1 WO2017130427 A1 WO 2017130427A1 JP 2016059953 W JP2016059953 W JP 2016059953W WO 2017130427 A1 WO2017130427 A1 WO 2017130427A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- photosensitive
- resin composition
- layer
- photosensitive resin
- component
- Prior art date
Abstract
L'invention concerne une composition de résine photosensible qui comprend un composant (A) consistant en un polymère de liant, un composant (B) consistant en un composé photopolymérisable, et un composant (C) consistant en un initiateur de photopolymérisation. Ledit composant (B) contient un (méth)acrylate possédant six liaisons éthyléniquement insaturées par molécule, et un (méth)acrylate possédant un squelette de cycle isocyanurique.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2017563664A JPWO2017130427A1 (ja) | 2016-01-28 | 2016-03-28 | 感光性樹脂組成物、感光性エレメント、レジストパターンの形成方法及びタッチパネルの製造方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016-014363 | 2016-01-28 | ||
JP2016014363 | 2016-01-28 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017130427A1 true WO2017130427A1 (fr) | 2017-08-03 |
Family
ID=59397562
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2016/059953 WO2017130427A1 (fr) | 2016-01-28 | 2016-03-28 | Composition de résine photosensible, élément photosensible, procédé de formation de motif de réserve, et procédé de fabrication de panneau tactile |
Country Status (3)
Country | Link |
---|---|
JP (1) | JPWO2017130427A1 (fr) |
TW (1) | TW201728999A (fr) |
WO (1) | WO2017130427A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2021039187A1 (fr) * | 2019-08-27 | 2021-03-04 | 富士フイルム株式会社 | Film de transfert, procédé de production de film de transfert, procédé de production de stratifié, stratifié, capteur de panneau tactile et panneau tactile |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2000112121A (ja) * | 1998-10-06 | 2000-04-21 | Fuji Photo Film Co Ltd | 感光性樹脂組成物 |
JP2005010205A (ja) * | 2003-06-16 | 2005-01-13 | Mitsui Chemicals Inc | 感光性組成物及びそれを用いたプリント配線基板の製造方法 |
JP2012048202A (ja) * | 2010-07-30 | 2012-03-08 | Hitachi Chem Co Ltd | 感光性樹脂組成物、感光性エレメント、レジストパターンの製造方法、リードフレームの製造方法、プリント配線板の製造方法及びプリント配線板 |
WO2014010345A1 (fr) * | 2012-07-09 | 2014-01-16 | 東レ株式会社 | L'INVENTION FOURNIT UNE PLAQUE À BUSES EXCELLENTE EN TERMES DE DURABILITÉ FACE À L'ESSUYAGE, ET DE PROPRIÉTÉS POUR REPOUSSER L'ENCRE MÊME EN CAS DE MISE EN œUVRE D'UNE ENCRE ADHÉRANT FACILEMENT À LA PLAQUE À BUSES. PLUS PRÉCISÉMENT, L'INVENTION CONCERNE UN PROCÉDÉ DE FORMATION DE FILM DURCI À BASE DE SILICONE CÔTÉ FACE DE DÉCHARGE D'ENCRE DE PLAQUE À BUSES POUR IMPRIMANTE À JET D'ENCRE, QUI COMPORTE : (1) UNE ÉTAPE DE PRÉPARATION D'UNE COMPOSITION DE SILICONE CONDENSÉE CONTENANT AU MOINS UNE SORTE DE COMPOSÉ CHOISIE PARMI UN GROUPE CONSTITUÉ D'UN COMPOSÉ BISMUTH ET D'UN COMPOSÉ AMIDINE CYCLIQUE; (2) UNE ÉTAPE DE FORMATION DE FILM DE REVÊTEMENT AU COURS DE LAQUELLE CETTE COMPOSITION DE SILICONE CONDENSÉE EST APPLIQUÉE SUR UNE FACE DE DÉCHARGE D'ENCRE DE LA PLAQUE À BUSES; ET (3) UNE ÉTAPE DE DURCISSEMENT À TEMPÉRATURE ÉLEVÉE DE CE FILM DE REVÊTEMENT. |
JP2014048428A (ja) * | 2012-08-30 | 2014-03-17 | Jsr Corp | 感放射線性組成物、表示素子用硬化膜の形成方法、表示素子用硬化膜及び表示素子 |
WO2014050567A1 (fr) * | 2012-09-27 | 2014-04-03 | 日立化成株式会社 | Composition de résine photosensible, élément photosensible, procédé de formation d'un motif de résist et procédé de fabrication d'un panneau tactile |
JP2015087429A (ja) * | 2013-10-28 | 2015-05-07 | 日立化成株式会社 | 感光性樹脂組成物、感光性エレメント及びレジストパターンの形成方法 |
JP2015175961A (ja) * | 2014-03-14 | 2015-10-05 | 日立化成株式会社 | 感光性樹脂組成物、感光性エレメント、レジストパターンの形成方法及びタッチパネルの製造方法 |
-
2016
- 2016-03-28 JP JP2017563664A patent/JPWO2017130427A1/ja active Pending
- 2016-03-28 WO PCT/JP2016/059953 patent/WO2017130427A1/fr active Application Filing
-
2017
- 2017-01-26 TW TW106103079A patent/TW201728999A/zh unknown
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2000112121A (ja) * | 1998-10-06 | 2000-04-21 | Fuji Photo Film Co Ltd | 感光性樹脂組成物 |
JP2005010205A (ja) * | 2003-06-16 | 2005-01-13 | Mitsui Chemicals Inc | 感光性組成物及びそれを用いたプリント配線基板の製造方法 |
JP2012048202A (ja) * | 2010-07-30 | 2012-03-08 | Hitachi Chem Co Ltd | 感光性樹脂組成物、感光性エレメント、レジストパターンの製造方法、リードフレームの製造方法、プリント配線板の製造方法及びプリント配線板 |
WO2014010345A1 (fr) * | 2012-07-09 | 2014-01-16 | 東レ株式会社 | L'INVENTION FOURNIT UNE PLAQUE À BUSES EXCELLENTE EN TERMES DE DURABILITÉ FACE À L'ESSUYAGE, ET DE PROPRIÉTÉS POUR REPOUSSER L'ENCRE MÊME EN CAS DE MISE EN œUVRE D'UNE ENCRE ADHÉRANT FACILEMENT À LA PLAQUE À BUSES. PLUS PRÉCISÉMENT, L'INVENTION CONCERNE UN PROCÉDÉ DE FORMATION DE FILM DURCI À BASE DE SILICONE CÔTÉ FACE DE DÉCHARGE D'ENCRE DE PLAQUE À BUSES POUR IMPRIMANTE À JET D'ENCRE, QUI COMPORTE : (1) UNE ÉTAPE DE PRÉPARATION D'UNE COMPOSITION DE SILICONE CONDENSÉE CONTENANT AU MOINS UNE SORTE DE COMPOSÉ CHOISIE PARMI UN GROUPE CONSTITUÉ D'UN COMPOSÉ BISMUTH ET D'UN COMPOSÉ AMIDINE CYCLIQUE; (2) UNE ÉTAPE DE FORMATION DE FILM DE REVÊTEMENT AU COURS DE LAQUELLE CETTE COMPOSITION DE SILICONE CONDENSÉE EST APPLIQUÉE SUR UNE FACE DE DÉCHARGE D'ENCRE DE LA PLAQUE À BUSES; ET (3) UNE ÉTAPE DE DURCISSEMENT À TEMPÉRATURE ÉLEVÉE DE CE FILM DE REVÊTEMENT. |
JP2014048428A (ja) * | 2012-08-30 | 2014-03-17 | Jsr Corp | 感放射線性組成物、表示素子用硬化膜の形成方法、表示素子用硬化膜及び表示素子 |
WO2014050567A1 (fr) * | 2012-09-27 | 2014-04-03 | 日立化成株式会社 | Composition de résine photosensible, élément photosensible, procédé de formation d'un motif de résist et procédé de fabrication d'un panneau tactile |
JP2015087429A (ja) * | 2013-10-28 | 2015-05-07 | 日立化成株式会社 | 感光性樹脂組成物、感光性エレメント及びレジストパターンの形成方法 |
JP2015175961A (ja) * | 2014-03-14 | 2015-10-05 | 日立化成株式会社 | 感光性樹脂組成物、感光性エレメント、レジストパターンの形成方法及びタッチパネルの製造方法 |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2021039187A1 (fr) * | 2019-08-27 | 2021-03-04 | 富士フイルム株式会社 | Film de transfert, procédé de production de film de transfert, procédé de production de stratifié, stratifié, capteur de panneau tactile et panneau tactile |
Also Published As
Publication number | Publication date |
---|---|
JPWO2017130427A1 (ja) | 2018-12-20 |
TW201728999A (zh) | 2017-08-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR102526280B1 (ko) | 감광성 수지 조성물, 감광성 엘리먼트, 레지스트 패턴의 형성 방법 및 터치 패널의 제조 방법 | |
TWI636329B (zh) | 感光性樹脂組成物、感光性元件及抗蝕劑圖案的形成方法 | |
JP5626428B2 (ja) | 感光性樹脂組成物、並びにこれを用いた感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法 | |
WO2012067107A1 (fr) | Composition de résine photosensible, élément photosensible, procédé de formation d'un motif de réserve et procédé de fabrication d'une plaquette de circuit imprimé | |
WO2015098870A1 (fr) | Composition de résine photosensible, élément photosensible, procédé de formation d'un motif de réserve et procédé de fabrication d'une carte à circuit imprimé | |
JP6229256B2 (ja) | 感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法 | |
JPWO2010134549A1 (ja) | 感光性樹脂組成物 | |
JP5899798B2 (ja) | 感光性樹脂組成物、感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法 | |
JP6332028B2 (ja) | 感光性樹脂組成物、感光性エレメント、レジストパターンの形成方法及びタッチパネルの製造方法 | |
KR20170085038A (ko) | 감광성 수지 조성물, 감광성 엘리먼트, 레지스터 패턴의 형성 방법 및 프린트 배선판의 제조 방법 | |
JP2021015296A (ja) | 感光性エレメント、レジストパターンの形成方法、及び、プリント配線板の製造方法 | |
WO2018100730A1 (fr) | Élément photosensible, procédé de formation d'un motif de réserve et procédé de production de carte à câblage imprimé | |
WO2015156292A1 (fr) | Composition de résine photosensible, élément photosensible, et procédé de fabrication de substrat de verre traité | |
WO2017130427A1 (fr) | Composition de résine photosensible, élément photosensible, procédé de formation de motif de réserve, et procédé de fabrication de panneau tactile | |
JP6263955B2 (ja) | 感光性樹脂組成物、感光性エレメント及びレジストパターンの形成方法 | |
JP2017040710A (ja) | 感光性樹脂組成物、感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法 | |
WO2017056530A1 (fr) | Composition de résine photosensible, élément photosensible, procédé de formation de motif de réserve et procédé de fabrication de panneau tactile | |
WO2012014580A1 (fr) | Composition de résine photosensible, élément photosensible l'utilisant, procédé de formation d'un motif de réserve, procédé de production d'une grille de connexion, carte de câblage imprimé et procédé de production de carte de câblage imprimé | |
WO2022102675A1 (fr) | Élément photosensible, procédé de production de produit durci, procédé de production de motif de produit durci, et procédé de production de carte de câblage | |
JP5117235B2 (ja) | 感光性樹脂組成物および積層体 | |
JP6451058B2 (ja) | 感光性樹脂組成物、これを用いた感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法 | |
JP2016161666A (ja) | 感光性樹脂組成物、感光性エレメント及びガラス基板の加工方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16888013 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2017563664 Country of ref document: JP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 16888013 Country of ref document: EP Kind code of ref document: A1 |