WO2017104695A1 - Précurseur de matériau d'emballage de barrière vis-à-vis des gaz, procédé pour sa production, matériau d'emballage de barrière vis-à-vis des gaz, et procédé pour produire un emballage - Google Patents

Précurseur de matériau d'emballage de barrière vis-à-vis des gaz, procédé pour sa production, matériau d'emballage de barrière vis-à-vis des gaz, et procédé pour produire un emballage Download PDF

Info

Publication number
WO2017104695A1
WO2017104695A1 PCT/JP2016/087185 JP2016087185W WO2017104695A1 WO 2017104695 A1 WO2017104695 A1 WO 2017104695A1 JP 2016087185 W JP2016087185 W JP 2016087185W WO 2017104695 A1 WO2017104695 A1 WO 2017104695A1
Authority
WO
WIPO (PCT)
Prior art keywords
gas barrier
mass
packaging material
barrier layer
polyvalent metal
Prior art date
Application number
PCT/JP2016/087185
Other languages
English (en)
Japanese (ja)
Inventor
晴香 大森
大森　望
Original Assignee
凸版印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 凸版印刷株式会社 filed Critical 凸版印刷株式会社
Priority to JP2017556090A priority Critical patent/JP6900906B2/ja
Publication of WO2017104695A1 publication Critical patent/WO2017104695A1/fr

Abstract

L'invention concerne un précurseur de matériau d'emballage de barrière vis-à-vis des gaz, lequel précurseur comporte : un support ; une couche de barrière vis-à-vis des gaz disposée directement sur le support et contenant un polymère de poly(acide carboxylique) et au moins un composé du silicium sélectionné parmi le groupe comprenant des composés de silane hydrolysables, leurs hydrolysats, et leurs condensats ; et une couche protectrice disposée directement sur la couche de barrière vis-à-vis des gaz et contenant un constituant de métal multivalent, une résine de polyester, et un agent de dispersion. Le taux de transmission de vapeur d'eau du support à 40° C et sous une humidité relative de 90 % est d'au moins 100 g/m2, la teneur du constituant de métal multivalent est de 40 à 90 % en masse par rapport à la masse totale de la couche protectrice, la teneur de l'agent de dispersion est de 2 à 20 % en masse par rapport au constituant de métal multivalent, et la teneur du composé du silicium est de 2 à 25 % en masse par rapport au polymère de poly(acide carboxylique). Dans la mesure du spectre d'absorption des infrarouges de la couche de barrière vis-à-vis des gaz, le rapport (α/β) entre la hauteur de pic maximale (α) pour le facteur d'absorption dans la plage de longueur d'onde de 1490 cm–1 à 1659 cm–1 et la hauteur de pic maximale (β) pour le facteur d'absorption dans la plage de longueur d'onde de 1660 cm–1 à 1750 cm–1 est d'au moins 1 et inférieur à 7.
PCT/JP2016/087185 2015-12-14 2016-12-14 Précurseur de matériau d'emballage de barrière vis-à-vis des gaz, procédé pour sa production, matériau d'emballage de barrière vis-à-vis des gaz, et procédé pour produire un emballage WO2017104695A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2017556090A JP6900906B2 (ja) 2015-12-14 2016-12-14 ガスバリア性包装材料用前駆体、その製造方法、ガスバリア性包装材料、その製造方法および包装体の製造方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2015-243335 2015-12-14
JP2015-243267 2015-12-14
JP2015243335 2015-12-14
JP2015243267 2015-12-14

Publications (1)

Publication Number Publication Date
WO2017104695A1 true WO2017104695A1 (fr) 2017-06-22

Family

ID=59056738

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/087185 WO2017104695A1 (fr) 2015-12-14 2016-12-14 Précurseur de matériau d'emballage de barrière vis-à-vis des gaz, procédé pour sa production, matériau d'emballage de barrière vis-à-vis des gaz, et procédé pour produire un emballage

Country Status (2)

Country Link
JP (1) JP6900906B2 (fr)
WO (1) WO2017104695A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3741560B1 (fr) * 2018-01-19 2023-07-12 Toppan Printing Co., Ltd. Stratifié formant barrière contre les gaz et emballage pourvu de celui-ci
WO2023199396A1 (fr) * 2022-04-12 2023-10-19 三井化学東セロ株式会社 Stratifié formant une barrière aux gaz

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008146706A1 (fr) * 2007-05-29 2008-12-04 Kureha Corporation Stratifié précurseur barrière contre les gaz, stratifié barrière contre les gaz, procédé de fabrication d'un stratifié précurseur barrière contre les gaz et procédé de fabrication d'un stratifié barrière contre les gaz
WO2014192500A1 (fr) * 2013-05-28 2014-12-04 凸版印刷株式会社 Matériau d'emballage à barrière contre les gaz
WO2015060147A1 (fr) * 2013-10-25 2015-04-30 凸版印刷株式会社 Précurseur de matériau de conditionnement formant barrière gazeuse et matériau de conditionnement formant barrière gazeuse

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6427947B2 (ja) * 2014-05-15 2018-11-28 凸版印刷株式会社 ガスバリア性包装材料

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008146706A1 (fr) * 2007-05-29 2008-12-04 Kureha Corporation Stratifié précurseur barrière contre les gaz, stratifié barrière contre les gaz, procédé de fabrication d'un stratifié précurseur barrière contre les gaz et procédé de fabrication d'un stratifié barrière contre les gaz
WO2014192500A1 (fr) * 2013-05-28 2014-12-04 凸版印刷株式会社 Matériau d'emballage à barrière contre les gaz
WO2015060147A1 (fr) * 2013-10-25 2015-04-30 凸版印刷株式会社 Précurseur de matériau de conditionnement formant barrière gazeuse et matériau de conditionnement formant barrière gazeuse

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3741560B1 (fr) * 2018-01-19 2023-07-12 Toppan Printing Co., Ltd. Stratifié formant barrière contre les gaz et emballage pourvu de celui-ci
WO2023199396A1 (fr) * 2022-04-12 2023-10-19 三井化学東セロ株式会社 Stratifié formant une barrière aux gaz

Also Published As

Publication number Publication date
JP6900906B2 (ja) 2021-07-07
JPWO2017104695A1 (ja) 2018-09-27

Similar Documents

Publication Publication Date Title
JP6904256B2 (ja) コーティング液およびガスバリア性積層体
JP5988543B2 (ja) コーティング液の製造方法、ガスバリア性積層体の製造方法
JP5941474B2 (ja) 複合構造体の製造方法、およびコーティング液の製造方法
JP5282445B2 (ja) ガスバリア性前駆積層体、ガスバリア性積層体およびこれらの製造方法
US20130034674A1 (en) Composite structural material formed product and packaging material using the same, method for producing the composite structural material, and coating liquid
JP6131570B2 (ja) ガスバリア用コーティング液、その製造方法、ガスバリア性積層体の製造方法、包装材料の製造方法および加熱殺菌用包装材料の製造方法
WO2007026751A1 (fr) Film multicouche à barrière de diffusion gazeuse
JP2014231365A (ja) ガスバリア性包装材料
JP6217173B2 (ja) ガスバリア積層体
JP6862815B2 (ja) 熱成形用ガスバリア性積層体、コーティング液、熱成形用ガスバリア性積層体の製造方法および成形体
JP2013208794A (ja) 多層構造体およびそれを用いた製品、ならびに多層構造体の製造方法
JP2013208793A (ja) 多層構造体およびそれを用いた製品、ならびに多層構造体の製造方法
WO2011078366A1 (fr) Composition de revêtement pour sous-couche
JP2021066031A (ja) 積層フィルム、包装袋、積層フィルムの製造方法、および、包装袋の製造方法
EP4169849A1 (fr) Corps multicouche de barrière aux gaz, liquide de revêtement pour sa production, matériau d'emballage, emballage et article emballé
WO2017104695A1 (fr) Précurseur de matériau d'emballage de barrière vis-à-vis des gaz, procédé pour sa production, matériau d'emballage de barrière vis-à-vis des gaz, et procédé pour produire un emballage
WO2022154031A1 (fr) Corps multicouche de barrière aux gaz, liquide de revêtement permettant de le produire, matériau d'emballage, emballage et article emballé
WO2018181457A1 (fr) Film barrière multicouche
JP2019019206A (ja) コーティング液、熱成形用ガスバリア性積層体および成形体
JP7088361B1 (ja) ガスバリア性積層体、包装材料、包装体及び包装物品
WO2022107858A1 (fr) Produit stratifié barrière aux gaz, matériau d'emballage, emballage et article emballé
JP2023127366A (ja) ガスバリア性積層体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16875672

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2017556090

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16875672

Country of ref document: EP

Kind code of ref document: A1