WO2017090537A1 - 硬化性組成物および硬化物 - Google Patents

硬化性組成物および硬化物 Download PDF

Info

Publication number
WO2017090537A1
WO2017090537A1 PCT/JP2016/084333 JP2016084333W WO2017090537A1 WO 2017090537 A1 WO2017090537 A1 WO 2017090537A1 JP 2016084333 W JP2016084333 W JP 2016084333W WO 2017090537 A1 WO2017090537 A1 WO 2017090537A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
meth
group
curable composition
mass
Prior art date
Application number
PCT/JP2016/084333
Other languages
English (en)
French (fr)
Inventor
圭介 ▲高▼木
室伏　英伸
Original Assignee
旭硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 旭硝子株式会社 filed Critical 旭硝子株式会社
Publication of WO2017090537A1 publication Critical patent/WO2017090537A1/ja

Abstract

屈折率が高く、かつアッベ数が低い硬化物を得ることができる低粘度の硬化性組成物、および屈折率が高く、かつアッベ数が低い硬化物の提供。　（メタ）アクリロイル基およびフルオレン構造を有する化合物（Ａ）と；重合性官能基を有さず、フルオレン構造を有する化合物（Ｂ）と；（メタ）アクリロイル基およびビフェニル構造を有する化合物（Ｃ）と；重合開始剤（Ｄ）とを含み；すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量％のうち、化合物（Ａ）が１～２０質量％であり、化合物（Ｂ）が９～４０質量％であり、化合物（Ｃ）が４５～８９質量％であり；すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量部に対して、重合開始剤（Ｄ）が、０．０１～１０質量部である、硬化性組成物。

Description

硬化性組成物および硬化物
　本発明は、硬化性組成物、および硬化性組成物を硬化した硬化物に関する。
　硬化性組成物を硬化した硬化物は、（ｉ）インプリント法、注型成形法等によって硬化性組成物から様々な形状のものを短時間で形成できる、（ｉｉ）ガラスに比べ割れにくい、（ｉｉｉ）ガラスに比べ軽量である、等の利点を有することから、ガラスに代わる光学部材用の材料として注目されている。従来熱可塑性樹脂も同様の理由から使用されてきたが、射出成型プロセスにおけるスプール、ランナーによる歩留まりの悪さが指摘されている。
　カメラ等の光学系においては、色収差の補正等を目的に、アッベ数の異なるレンズを組み合わせることがある。そこで、アッベ数が高いレンズとともに、アッベ数が低いレンズも求められる。そのため、硬化性組成物としては、屈折率が高く、かつアッベ数が低い硬化物を得ることができるものが求められることがある。
　屈折率が高く、かつアッベ数が低い硬化物を得ることができる硬化性組成物としては、たとえば、下記のものが提案されている。（１）（メタ）アクリロイルオキシ基およびフルオレン構造を有する化合物の４０～７８質量％と、（メタ）アクリロイル基を有し、フルオレン構造を有しない化合物の２０～５９質量％と、重合開始剤の０．１～５質量％とを含み、硬化物のアッベ数が１０～４０である硬化性組成物（特許文献１）。
　しかし、（メタ）アクリロイルオキシ基およびフルオレン構造を有する化合物は、高粘度であり、しかも（１）の硬化性組成物における当該化合物の含有率が高いため、（１）の硬化性組成物は、粘度が高く、取扱性が悪い。
　屈折率が高い硬化物を得ることができる低粘度の硬化性組成物としては、たとえば、下記のものが提案されている。
　（２）ポリオールに由来する構造単位を有しないウレタン（メタ）アクリレートと、ビフェニル構造および重合性官能基を有する化合物と、フルオレン構造および重合性官能基を有する化合物と、重合開始剤とを含む硬化性組成物（特許文献２）。
　（３）ビフェニル構造および重合性官能基を有する化合物と、フルオレン構造および重合性官能基を有する化合物と、重合開始剤とを含む硬化性組成物（特許文献３）。
特開２０１０－０３７４７０号公報 特開２００９－１３２８４２号公報 特開２０１２－０８２３８７号公報
　ビフェニル構造および重合性官能基を有する化合物は、屈折率が高く、低粘度であるため、硬化物の屈折率の低下を抑えつつ、上記（２）、（３）の硬化性組成物の粘度を下げることができる。しかし、上記（２）、（３）の硬化性組成物を硬化した硬化物は、屈折率の高さがいまだ不充分である。
　本発明は、屈折率が高く、かつアッベ数が低い硬化物を得ることができる低粘度の硬化性組成物、および屈折率が高く、かつアッベ数が低い硬化物を提供する。
　本発明は、下記の態様を有する。
＜１＞（メタ）アクリロイル基を有し、かつ下式（１）で表されるフルオレン構造を有する化合物（Ａ）と、
　重合性官能基を有さず、かつ下式（１）で表されるフルオレン構造を有する化合物（Ｂ）と、
　（メタ）アクリロイル基を有し、かつ下式（２）で表されるビフェニル構造を有する化合物（Ｃ）（ただし、前記化合物（Ａ）と同じものを除く。）と、
　重合開始剤（Ｄ）と、を含み、
　すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量％のうち、前記化合物（Ａ）が、１～２０質量％であり、前記化合物（Ｂ）が、９～４０質量％であり、前記化合物（Ｃ）が、４５～８９質量％であり、
　すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量部に対して、前記重合開始剤（Ｄ）が、０．０１～１０質量部である、硬化性組成物。
Figure JPOXMLDOC01-appb-C000006
 　（式（１）、（２）中、＊印は結合手を表し、フルオレン構造およびビフェニル構造は、置換基を有していてもよい。）
＜２＞前記化合物（Ａ）が、下式（Ａ１）で表される、上記＜１＞に記載の硬化性組成物。
Figure JPOXMLDOC01-appb-C000007
 　（式（Ａ１）中、Ｒ１は、水素原子またはメチル基である。Ｒ２は、－ＣＨ２－、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＣＨ３）－、ＣＨ２ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－、または－ＣＨ２ＣＨ（ＯＲ４）ＣＨ２－（ただし、Ｒ４は（メタ）アクリロイル基である。）である。ａは０～４の整数である。Ｒ３は水素原子またはアルキル基である。）
＜３＞前記式（Ａ１）中、Ｒ２は、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－、または－ＣＨ２ＣＨ（ＯＲ４）ＣＨ２－（ただし、Ｒ４は（メタ）アクリロイル基である。）でり、ａは、１または２の整数である、上記＜２＞に記載の硬化性組成物。
＜４＞前記化合物（Ｂ）が下式（Ｂ１）で表される、上記＜１＞～＜３＞のいずれかに記載の硬化性組成物。
Figure JPOXMLDOC01-appb-C000008
 　（式（Ｂ１）中、Ｘは、水酸基、－Ｏ（Ｒ６Ｏ）ｂＨ（ただし、Ｒ６は－ＣＨ２－、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＣＨ３）－、ＣＨ２ＣＨ２ＣＨ２－、または－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－であり、ｂは１～４の整数である。）、グリシジルオキシ基、またはアミノ基である。Ｒ５は、水素原子またはアルキル基である。）
＜５＞前記式（Ｂ１）におけるＸが、水酸基または２－ヒドロキシエトキシ基である、上記＜４＞に記載の硬化性組成物。
＜６＞前記化合物（Ｃ）が下式（Ｃ１）または下式（Ｃ２）で表される、上記＜１＞～＜５＞のいずれかに記載の硬化性組成物。
Figure JPOXMLDOC01-appb-C000009
 （式（Ｃ１）、式（Ｃ２）中、Ｒ７は、水素原子またはメチル基である。なお、化合物（Ｃ１）において、－ＣＨ２ＯＣ（Ｏ）ＣＲ７＝ＣＨ２は、２つのフェニル基のうち左側のフェニル基に対して右側のフェニル基のオルト位またはメタ位に結合する。Ｒ８は、水素原子またはメチル基である。Ｒ９は、水素原子またはメチル基である。ｍは、１または２である。）
＜７＞フッ素原子を有し、かつ（メタ）アクリロイル基を１つ以上有する化合物（Ｅ）（ただし、前記化合物（Ａ）または前記化合物（Ｃ）と同じものを除く。）をさらに含み、
　すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量％のうち、前記化合物（Ｅ）が、０．０１～５質量％である、上記＜１＞～＜６＞のいずれかに記載の硬化性組成物。
＜８＞前記化合物（Ｅ）が下式（Ｅ１）で表され、すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量％のうち、前記化合物（Ｅ）が、０．０１～５質量％である、上記＜１＞～＜６＞のいずれかに記載の硬化性組成物。
Figure JPOXMLDOC01-appb-C000010
 （式（Ｅ１）中、Ｒ１０は、水素原子またはメチル基である。Ｒ１１は、炭素数１～２０のアルキレン基、炭素数３～２０のシクロアルキレン基、炭素数６～２０の芳香族基およびこれらを組み合わせて得られる基からなる群から選ばれる１種である。Ｒｆ、炭素原子間にエーテル性酸素原子を有していてもよい、炭素数２０以下のフルオロアルキル基である。）
＜９＞上記＜１＞～＜８＞のいずれかに記載の硬化性組成物を硬化した硬化物。
＜１０＞温度２５℃における粘度が２０Ｐａ・ｓ以下である、上記＜９＞に記載の硬化性組成物を硬化した硬化物。
＜１１＞波長５８９ｎｍの光に対する屈折率が１．６１以上である、上記＜９＞又は＜１０＞に記載の硬化性組成物を硬化した硬化物。
＜１２＞下記式（Ｉ）から求められるアッベ指数が２４以下である、上記＜９＞～＜１１＞のいずれかに記載の硬化性組成物を硬化した硬化物。
＜１３＞上記＜１＞～＜１１＞のいずれかに記載の硬化性組成物をインプリント法又は注型成形法により硬化させる硬化物の製造方法。
　本発明の硬化性組成物によれば、屈折率が高く、かつアッベ数が低い硬化物を得ることができる。また、本発明の硬化性組成物は、低粘度である。本発明の硬化物は、屈折率が高く、かつアッベ数が低い。
　本明細書において、式（Ａ１）で表される化合物を化合物（Ａ１）とも記す。他の式で表される化合物についてもこれに準じて記す。
　「（メタ）アクリロイル基」とは、アクリロイル基およびメタクリロイル基の総称である。
　「（メタ）アクリレート」とは、アクリレートおよびメタクリレートの総称である。
＜硬化性組成物＞
　本発明の硬化性組成物は、化合物（Ａ）と、化合物（Ｂ）と、化合物（Ｃ）と、重合開始剤（Ｄ）とを必須成分として含む。
　本発明の硬化性組成物は、必要に応じて化合物（Ｅ）、化合物（Ｆ）、添加剤、溶剤等を含んでいてもよい。
　本発明の硬化性組成物の２５℃における粘度は、２０Ｐａ・ｓ以下が好ましく、０．１～１５Ｐａ・ｓがより好ましく、１～１２Ｐａ・ｓがさらに好ましい。硬化性組成物の粘度が前記範囲の上限値以下であれば、硬化性組成物の取扱性がよくなり、硬化性組成物をインプリント用のモールドに容易に接触させたり、注型成形用のモールドに容易に注入したりできる。硬化性組成物の粘度が前記範囲の下限値以上であれば、硬化性組成物が基材の表面から流れ出すことなく、硬化性組成物を簡便に基材の表面に塗布できる。
　（化合物（Ａ））
　化合物（Ａ）は、（メタ）アクリロイル基を有し、かつ下式（１）で表されるフルオレン構造を有するものである。
Figure JPOXMLDOC01-appb-C000011
　ただし、式（１）中、＊印は結合手を表す。フルオレン構造は、アルキル基、ヒドロキシル基、アミノ基、ハロゲン基などの置換基を有していてもよい。
　化合物（Ａ）としては、合成のしやすさ、入手のしやすさの点から、化合物（Ａ１）が好ましい。
Figure JPOXMLDOC01-appb-C000012
　ただし、式（Ａ１）中、Ｒ１は、水素原子またはメチル基である。Ｒ２は、－ＣＨ２－、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＣＨ３）－、ＣＨ２ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－、または－ＣＨ２ＣＨ（ＯＲ４）ＣＨ２－（ただし、Ｒ４は（メタ）アクリロイル基である。）である。Ｒ２としては、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－、または－ＣＨ２ＣＨ（ＯＲ４）ＣＨ２－が好ましく、－ＣＨ２ＣＨ２－が特に好ましい。ａは、０～４の整数である。ａとしては、１または２が好ましく、１が特に好ましい。Ｒ３は、水素原子またはアルキル基である。アルキル基としては、メチル基、エチル基、またはプロピル基が好ましい。Ｒ３としては、水素原子が特に好ましい。
　なお、式（Ａ１）中、Ｒ１～Ｒ３及びａはいずれも２つ存在するが、それぞれのＲ１～Ｒ３及びａは、独立して上記した定義を取り得るものであり、それぞれの定義の範囲内で異なるものであることできる。これは、式中に、複数の同じ記号が存在する場合には、同様である。
　化合物（Ａ）の例としては、下記の化合物が挙げられる。
　９，９－ビス（４－（メタ）アクリロイルオキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシメトキシフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシエトキシ）フェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシプロポキシ）フェニル）フルオレン、９，９－ビス（４－（３－（メタ）アクリロイルオキシプロポキシ）フェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジメトキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジエトキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジプロポキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリメトキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリエトキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリプロポキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシメトキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシエトキシ）－３－メチルフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシプロポキシ）－３－メチルフェニル）フルオレン、９，９－ビス（４－（３－（メタ）アクリロイルオキシプロポキシ）－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジメトキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジエトキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジプロポキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリメトキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリエトキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリプロポキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシメトキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシエトキシ）－３－エチルフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシプロポキシ）－３－エチルフェニル）フルオレン、９，９－ビス（４－（３－（メタ）アクリロイルオキシプロポキシ）－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジメトキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジエトキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジプロポキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリメトキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリエトキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリプロポキシ－３－エチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシメトキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシエトキシ）－３－プロピルフェニル）フルオレン、９，９－ビス（４－（２－（メタ）アクリロイルオキシプロポキシ）－３－プロピルフェニル）フルオレン、９，９－ビス（４－（３－（メタ）アクリロイルオキシプロポキシ）－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジメトキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジエトキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシジプロポキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリメトキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリエトキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシトリプロポキシ－３－プロピルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシ－（２－ヒドロキシ）プロポキシフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシ－（２－ヒドロキシ）プロポキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（メタ）アクリロイルオキシ－（２－ヒドロキシ）プロポキシエトキシフェニル）フルオレン等。
　化合物（Ａ）の市販品としては、大阪ガスケミカル社製のＥＡ－０２００、ＥＡ－０５００、ＥＡ－１０００等、新中村化学工業社製のＡ－ＢＰＥＦ等が挙げられる。化合物（Ａ）は、１種を単独で用いてもよく、２種以上を併用してもよい。
　（化合物（Ｂ））
　化合物（Ｂ）は、重合性官能基を有さず、かつ下式（１）で表されるフルオレン構造を有する。
Figure JPOXMLDOC01-appb-C000013
　ただし、式（１）中、＊印は結合手を表し、フルオレン構造は、アルキル基、ヒドロキシル基、アミノ基、ハロゲン基などの置換基を有していてもよい。ここで、重合性官能基は、重合性の炭素－炭素二重結合を有する基であり、ビニル基、アリル基、（メタ）アクリロイル基等が挙げられる。
　化合物（Ｂ）としては、合成のしやすさ、入手のしやすさの点から、下式（Ｂ１で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000014
　式（Ｂ１中、Ｘは、水酸基、－Ｏ（Ｒ６Ｏ）ｂＨ（ただし、Ｒ６は－ＣＨ２－、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＣＨ３）－、ＣＨ２ＣＨ２ＣＨ２－、または－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－であり、ｂは１～４の整数である。）、グリシジルオキシ基、またはアミノ基である。Ｘとしては、水酸基または２－ヒドロキシエトキシ基が好ましく、水酸基が特に好ましい。
　Ｒ５は、水素原子またはアルキル基である。アルキル基としては、メチル基、エチル基、またはプロピル基が好ましい。Ｒ５としては、水素原子が特に好ましい。
　化合物（Ｂ）の例としては、下記の化合物が挙げられる。
　９，９－ビス（４－ヒドロキシフェニル）フルオレン、９，９－ビス（４－ヒドロキシ－３－メチルフェニル）フルオレン、９，９－ビス（４－（２－ヒドロキシエトキシ）フェニル）フルオレン、９，９－ビス（４－グリシジルオキシフェニル）フルオレン、９，９－ビス（４－アミノフェニル）フルオレン等。
　化合物（Ｂ）の市販品としては、大阪ガスケミカル社製のＢＰＦ、ＢＣＦ、ＢＰＥＦ等、ＪＦＥケミカル社製のビスフェノールフルオレン、ビスクレゾールフルオレン、ビスアミノフェニルフルオレン等が挙げられる。化合物（Ｂ）は、１種を単独で用いてもよく、２種以上を併用してもよい。
　（化合物（Ｃ））
　化合物（Ｃ）は、（メタ）アクリロイル基を有し、かつ下式（２）で表されるビフェニル構造を有するもの（ただし、化合物（Ａ）と同じものを除く。）である。
Figure JPOXMLDOC01-appb-C000015
　ただし、式（２）中、＊印は結合手を表し、ビフェニル構造は、アルキル基、ヒドロキシル基、アミノ基、ハロゲン基などの置換基を有していてもよい。
　化合物（Ｃ）としては、合成のしやすさ、入手のしやすさの点から、下式（Ｃ１）で表される化合物、または下式（Ｃ２）で表される化合物が好ましく、硬化性組成物の低粘度化の点から、化合物（Ｃ１）が特に好ましい。
Figure JPOXMLDOC01-appb-C000016
　上記式（Ｃ１）、（Ｃ２）中、Ｒ７は、水素原子またはメチル基である。また、ＣＨ２ＯＣ（Ｏ）ＣＲ７＝ＣＨ２は、２つのフェニル環のうち、左側のフェニル環が結合する位置基に対して右側のフェニル環のオルト位またはメタ位に結合するのが好ましい。Ｒ８は、水素原子またはメチル基である。Ｒ９は、水素原子またはメチル基である。ｍは、１または２である。ｍとしては、１が特に好ましい。
　化合物（Ｃ）の例としては、下記の化合物が挙げられる。
　ｏ－フェニルベンジル（メタ）アクリレート、ｍ－フェニルベンジル（メタ）アクリレート、エトキシ化ｏ－フェニルフェノール（メタ）アクリレート等。
　なお、ｐ－フェニルベンジル（メタ）アクリレートは２５℃で固体であるが、ｏ－フェニルベンジル（メタ）アクリレートまたはｍ－フェニルベンジル（メタ）アクリレートに溶解させて用いることができる。
　化合物（Ｃ）の市販品としては、ＤＩＣ社製のＥＫＺ－９４８、新中村化学工業社製のＡ－ＬＥＮ－１０、東亞合成社製のＴＯ－１４６３等が挙げられる。化合物（Ｃ）は、１種を単独で用いてもよく、２種以上を併用してもよい。
　（重合開始剤（Ｄ））
　重合開始剤（Ｄ）は、硬化方法（光硬化または熱硬化）等に応じて適宜選択される。
　重合開始剤（Ｄ）としては、光重合開始剤または熱重合開始剤が挙げられる。重合開始剤（Ｄ）としては、硬化物の製造のしやすさの点から、光重合開始剤が好ましい。
　光重合開始剤としては、光を吸収することによってラジカルを発生する光ラジカル重合開始剤等が挙げられる。光重合開始剤としては、硬化物の製造のしやすさの点から、光ラジカル重合開始剤が好ましい。
　光ラジカル重合開始剤としては、アルキルフェノン系光重合開始剤、アシルホスフィンオキシド系光重合開始剤、チタノセン系光重合開始剤、オキシムエステル系光重合開始剤、オキシフェニル酢酸エステル系光重合開始剤、ベンゾイン系光重合開始剤、ベンゾフェノン系光重合開始剤、チオキサントン系光重合開始剤、ベンジル－（ｏ－エトキシカルボニル）－α－モノオキシム、グリオキシエステル、３－ケトクマリン、２－エチルアンスラキノン、カンファーキノン、テトラメチルチウラムスルフィド、アゾビスイソブチロニトリル、ベンゾイルペルオキシド、ジアルキルペルオキシド、ｔｅｒｔ－ブチルペルオキシピバレート等が挙げられる。感度および相溶性の点から、アルキルフェノン系光重合開始剤、アシルホスフィンオキシド系光重合開始剤、ベンゾイン系光重合開始剤またはベンゾフェノン系光重合開始剤が好ましい。光重合開始剤は、１種を単独で用いてもよく、２種以上を併用してもよい。
　熱重合開始剤としては、２，２’－アゾビスイソブチロニトリル、ベンゾイルペルオキシド、ｔｅｒｔ－ブチルヒドロペルオキシド、クメンヒドロペルオキシド、ジ－ｔｅｒｔ－ブチルペルオキシド、ジクミルペルオキシド等が挙げられる。分解温度の点から、２，２’－アゾビスイソブチロニトリル、ベンゾイルペルオキシドが好ましい。
　熱重合開始剤は、１種を単独で用いてもよく、２種以上を併用してもよい。
　（化合物（Ｅ））
　化合物（Ｅ）は、フッ素原子を有し、かつ（メタ）アクリロイル基を１つ以上有するものである（ただし、化合物（Ａ）または化合物（Ｃ）と同じものを除く）。
　化合物（Ｅ）としては、他の成分との相溶性の点から、フルオロ（メタ）アクリレートが好ましい。さらに、合成のしやすさ、入手のしやすさの点から、化合物（Ｅ１）が好ましい。
Figure JPOXMLDOC01-appb-C000017
 　式（Ｅ１）中、Ｒ１０は、水素原子またはメチル基である。Ｒ１１は、炭素数１～２０のアルキレン基、炭素数３～２０のシクロアルキレン基、炭素数６～２０の芳香族基およびこれらを組み合わせて得られる基からなる群から選ばれる１種が好ましく、炭素数１～１０の直鎖状若しくは分岐状のアルキレン基、炭素数３～１０のシクロアルキレン基、炭素数６～１２の芳香族基、またはこれらの組み合わせからなる基がさらに好ましく、炭素数１～１０の直鎖状若しくは分岐状のアルキレン基、炭素数３～１０のシクロアルキレン基、又はこれらの組み合わせからなる基が特に好ましい。これらの基は置換基を有していてもよく、置換基としては水酸基が好ましい。Ｒｆは、炭素原子間にエーテル性酸素原子を有していてもよい、炭素数２０以下、好ましくは４～１２のフルオロアルキル基である。
　フルオロ（メタ）アクリレートとしては、下記の単官能または２官能の化合物が挙げられる。化合物（Ｅ１）としては、下記の単官能の化合物が挙げられる。
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＨ（ＯＨ）ＣＨ２ＣＦ２ＣＦ２ＣＦ（ＣＦ３）２、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＨ（ＯＨ）ＣＨ２ＣＦ２ＣＦ２ＣＦ（ＣＦ３）２、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ（ＣＦ３）２、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ（ＣＦ３）２、
　ＣＨ２＝ＣＨＣ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）１０Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）８Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）６Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）１０Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）８Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）６Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２（ＣＦ２）６Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２（ＣＦ２）６Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２（ＣＦ２）７Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２（ＣＦ２）７Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＦ２ＣＦ２Ｈ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２（ＣＦ２ＣＦ２）２Ｈ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２（ＣＦ２ＣＦ２）４Ｈ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＦ２ＣＦ２Ｈ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２（ＣＦ２ＣＦ２）２Ｈ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２（ＣＦ２ＣＦ２）４Ｈ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＦ２ＯＣＦ２ＣＦ２ＯＣＦ３、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＦ２Ｏ（ＣＦ２ＣＦ２Ｏ）３ＣＦ３、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＦ２ＯＣＦ２ＣＦ２ＯＣＦ３、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＦ２Ｏ（ＣＦ２ＣＦ２Ｏ）３ＣＦ３、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＦ（ＣＦ３）ＯＣＦ２ＣＦ（ＣＦ３）Ｏ（ＣＦ２）３Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＦ（ＣＦ３）Ｏ（ＣＦ２ＣＦ（ＣＦ３）Ｏ）２（ＣＦ２）３Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＦ（ＣＦ３）ＯＣＦ２ＣＦ（ＣＦ３）Ｏ（ＣＦ２）３Ｆ、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＦ（ＣＦ３）Ｏ（ＣＦ２ＣＦ（ＣＦ３）Ｏ）２（ＣＦ２）３Ｆ、
　ＣＨ２＝ＣＦＣ（Ｏ）ＯＣＨ２ＣＨ（ＯＨ）ＣＨ２（ＣＦ２）６ＣＦ（ＣＦ３）２、
　ＣＨ２＝ＣＦＣ（Ｏ）ＯＣＨ２ＣＨ（ＣＨ２ＯＨ）ＣＨ２（ＣＦ２）６ＣＦ（ＣＦ３）２、
　ＣＨ２＝ＣＦＣ（Ｏ）ＯＣＨ２ＣＨ（ＯＨ）ＣＨ２（ＣＦ２）１０Ｆ、
　ＣＨ２＝ＣＦＣ（Ｏ）ＯＣＨ２ＣＨ（ＣＨ２ＯＨ）ＣＨ２（ＣＦ２）１０Ｆ、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２ＣＦ２（ＯＣＦ２ＣＦ２）ｐＯＣＦ２ＣＨ２ＯＣ（Ｏ）ＣＨ＝ＣＨ２（ただし、ｐは１～２０の整数である。）、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２ＣＦ２（ＯＣＦ２ＣＦ２）ｐＯＣＦ２ＣＨ２ＯＣ（Ｏ）Ｃ（ＣＨ３）＝ＣＨ２（ただし、ｐは１～２０の整数である。）、
　ＣＨ２＝ＣＨＣ（Ｏ）ＯＣＨ２（ＣＦ２）４ＣＨ２ＯＣ（Ｏ）ＣＨ＝ＣＨ２、
　ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）ＯＣＨ２（ＣＦ２）４ＣＨ２ＯＣ（Ｏ）Ｃ（ＣＨ３）＝ＣＨ２等。
　化合物（Ｅ）は、１種を単独で用いてもよく、２種以上を併用してもよい。
　（化合物（Ｆ））
　化合物（Ｆ）は、（メタ）アクリロイル基を１つ以上有するものである（ただし、化合物（Ａ）、化合物（Ｃ）または化合物（Ｅ）と同じものを除く）。
　化合物（Ｆ）としては、（メタ）アクリロイル基に酸素原子を介して炭素数１～３０の有機基が結合したものが好ましい。有機基の炭素数は４～２０が好ましく、４～１２がより好ましい。
　有機基としては、直鎖アルキル基、分岐アルキル基、シクロアルキル基、アリル基、橋かけ炭化水素基、オキシアルキレン鎖の繰り返し構造を有する基、芳香族基、複素環基等が挙げられる。これらの基は、炭素原子の一部が窒素原子、酸素原子等のヘテロ原子またはケイ素原子で置換されていてもよく、水素原子の一部が水酸基、アミノ基等の官能基で置換されていてもよく、不飽和結合や遊離カルボキシ基を有していてもよい。有機基としては、直鎖アルキル基、分岐アルキル基、シクロアルキル基、または橋かけ炭化水素基が好ましい。
　化合物（Ｆ）としては、（メタ）アクリロイルオキシ基を１つ有する化合物（Ｆ１）まは（メタ）アクリロイルオキシ基を２つ以上有する化合物（Ｆ２）が挙げられる。ただし、この場合、化合物（Ｆ１）または（Ｆ２）からは、化合物（Ａ）、化合物（Ｃ）または化合物（Ｅ）と同じものは除かられる。
　化合物（Ｆ１）としては、（メタ）アクリル酸エステル化合物（Ｆ１）としては、下記の例が挙げられる。
　２－エチルヘキシル（メタ）アクリレート、ブチル（メタ）アクリレート、エトキシエチル（メタ）アクリレート、メトキシエチル（メタ）アクリレート、アリル（メタ）アクリレート、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、オクチル（メタ）アクリレート、デシル（メタ）アクリレート、ｎ－ブチル（メタ）アクリレート、ｔｅｒｔ－ブチル（メタ）アクリレート、ベヘニル（メタ）アクリレート、ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレート、ラウリル（メタ）アクリレート、グリシジル（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、２－メチル－２－アダマンチル（メタ）アクリレート、２－エチル－２－アダマンチル（メタ）アクリレート、３－ヒドロキシ－１－アダマンチル（メタ）アクリレート、１－アダマンチル（メタ）アクリレート、イソボルニル（メタ）アクリレート、４－ｔｅｒｔ－ブチルシクロヘキシル（メタ）アクリレート、３－（トリメトキシシリル）プロピル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、（２－（ｔｅｒｔ－ブチルアミノ）エチル（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、２－ヒドロキシ－３－フェノキシプロピル（メタ）アクリレート、２－（４－ベンゾイル－３－ヒドロキシフェノキシ）エチル（メタ）アクリレート、フェノキシエチレングリコール（メタ）アクリレート、フェノキシジエチレングリコール（メタ）アクリレート、メトキシトリエチレングリコール（メタ）アクリレート、メトキシポリエチレングリコール（メタ）アクリレート、２－（メタ）アクリロイロキシエチルヘキサヒドロフタル酸、２－（メタ）アクリロイロキシエチルコハク酸、ベンジル（メタ）アクリレート、１，２，２，６，６－ペンタメチル－４－ピペリジル（メタ）アクリレート等。
　化合物（Ｆ２）としては、ジオール（グリコール等）の（メタ）アクリレート、トリオール（グリセロール、トリメチロール等）の（メタ）アクリレート、テトラオール（ペンタエリスリトール等）の（メタ）アクリレート、ウレタン（メタ）アクリレート、またはエポキシ（メタ）アクリレートが好ましい。
　化合物（Ｆ２）としては、下記の例が挙げられる。
　ポリオキシエチレングリコールジ（メタ）アクリレート（エチレングリコールジ（メタ）アクリレート、ジエチレングリコールジ（メタ）アクリレート、テトラエチレングリコールジ（メタ）アクリレート等）、ポリプロピレングリコールジ（メタ）アクリレート（ジプロピレングリコールジ（メタ）アクリレート等）、１，３－ブタンジオールジ（メタ）アクリレート、１，４－ブタンジオールジ（メタ）アクリレート、グリセロール１，３－ジグリセロレートジ（メタ）アクリレート、１，６－ヘキサンジオールエトキシレートジ（メタ）アクリレート、１，６－ヘキサンジオールプロポキシレートジ（メタ）アクリレート、１，６－ヘキサンジオールジ（メタ）アクリレート、３－ヒドロキシ－２，２－ジメチルプロピオネートジ（メタ）アクリレート、１，９－ノナンジオールジ（メタ）アクリレート、１，１０－デカンジオールジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、ネオペンチルグリコールプロポキシレートジ（メタ）アクリレート、グリセロールジ（メタ）アクリレート、プロピレングリコールグリセロレートジ（メタ）アクリレート、トリプロピレングリコールジ（メタ）アクリレート、トリエチレングリコールジ（メタ）アクリレート、テトラエチレングリコールジ（メタ）アクリレート、トリプロピレングリコールグリセロレートジ（メタ）アクリレート、２－ヒドロキシ－３－アクリロイロキシプロピル（メタ）アクリレート、２－メチル－１，３－プロパンジオールジアクリレート、トリシクロデカンジメタノールジアクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンエトキシトリ（メタ）アクリレート、エトキシ化トリメチロールプロパントリアクリレート、プロポキシ化トリメチロールプロパントリアクリレート、１，３－ビス（３－メタクリロイロキシプロピル）－１，１，３，３－テトラメチルジシロキサン、グリセリンプロポキシトリ（メタ）アクリレート、ペンタエリスリトールジ（メタ）アクリレートモノステアリル酸、トリメチロールプロパンエトキシレートメチルエーテルジ（メタ）アクリレート、ペンタリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ペンタエリスリトールエトキシテトラ（メタ）アクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート、プロポキシ化ペンタエリスリトールテトラアクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート等。化合物（Ｆ）は、１種を単独で用いてもよく、２種以上を併用してもよい。
　（添加剤）
　添加剤としては、界面活性剤、酸化防止剤（耐熱安定剤）、チクソトロピック剤、消泡剤、耐光安定剤、ゲル化防止剤、光増感剤、樹脂、樹脂オリゴマー、炭素化合物、金属微粒子、金属酸化物微粒子、シランカップリング剤、他の有機化合物等が挙げられる。
　（溶剤）
　本発明の硬化性組成物は、溶剤を含んでもよい。ただし、硬化性組成物を硬化する前には、溶剤を除去することが好ましい。
　溶剤としては、化合物（Ａ）～（Ｃ）、（Ｅ）、（Ｆ）および重合開始剤（Ｄ）を溶解可能であればいずれも用いることができ、エステル構造、ケトン構造、水酸基、およびエーテル構造のいずれか１つ以上を有する溶剤が好ましい。溶剤を使用する場合、硬化性組成物中の溶剤の含有量は、目的の粘度、塗布性、目的とする膜厚等によって適宜調整すればよい。
　（硬化性組成物の各成分の含有割合）
　化合物（Ａ）の割合は、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量％のうち、１～２０質量％であり、３～１５質量％が好ましく、５～１２質量％がより好ましい。該割合が前記範囲の下限値以上であれば、硬化物の屈折率を高くする効果および硬化物のアッベ数を低くする効果が得られる。また、硬化物の機械的特性が良好となる。該割合が前記範囲の上限値以下であれば、硬化性組成物の粘度が低く抑えられる。
　化合物（Ｂ）の割合は、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量％のうち、９～４０質量％であり、１５～３７質量％が好ましく、２０～３５質量％がより好ましい。該割合が前記範囲の下限値以上であれば、硬化物の屈折率が高くなり、かつ硬化物のアッベ数が低くなる。該割合が前記範囲の上限値以下であれば、硬化性組成物の粘度が低く抑えられる。また、硬化物の機械的特性が良好となる。
　化合物（Ｃ）の割合は、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量％のうち、４５～８９質量％であり、５０～８０質量％が好ましく、５５～７０質量％がより好ましい。該割合が前記範囲の下限値以上であれば、硬化性組成物の粘度を低くできる。該割合が前記範囲の上限値以下であれば、硬化物の屈折率の低下が抑えられる。
　重合開始剤（Ｄ）の含有量は、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量部に対して、０．０１～１０質量部であり、０．１～７質量部が好ましく、０．３～５質量部がより好ましい。該含有量が前記範囲の下限値以上であれば、容易に硬化物を形成できる。該含有量が前記範囲の上限値以下であれば、均一に混合することができることから、硬化物に残存する重合開始剤（Ｄ）が少なくなり、硬化物の物性の低下が抑えられる。
　化合物（Ｅ）を含む場合、化合物（Ｅ）の割合は、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量％のうち、０．０１～５質量％が好ましく、０．１～４質量％がより好ましく、０．３～３質量％がさらに好ましい。該割合が前記範囲の下限値以上であれば、硬化物の離型性に優れる。割合が前記範囲の上限値以下であれば、硬化物の屈折率の低下および硬化物のアッベ数の上昇が抑えられる。
　本発明の硬化性組成物は化合物（Ｆ）をできるだけ含まないことが好ましい。化合物（Ｆ）の割合は、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量％のうち、０～５質量％が好ましく、０～３質量％がより好ましい。該割合が前記範囲の上限値以下であれば、硬化物の屈折率の低下および硬化物のアッベ数の上昇が抑えられる。
　添加剤等の他の成分の合計の添加量は、本発明の効果を損なわない範囲であればよく、すべての（メタ）アクリロイル基を有する化合物と化合物（Ｂ）との合計１００質量部に対して、５質量部以下が好ましく、３質量部以下がより好ましい。
　以上説明した本発明の硬化性組成物にあっては、以下の理由から、屈折率が高く、かつアッベ数が低い硬化物を得ることができ、また、本発明の硬化性組成物は低粘度である。
　本発明の硬化性組成物は、屈折率が高く、かつアッベ数が低い、（メタ）アクリロイル基およびフルオレン構造を有する特定の化合物（Ａ）を含むため、硬化物の屈折率を高く、かつ硬化物のアッベ数を低くできる。しかし、化合物（Ａ）だけでは硬化物の屈折率を高く、かつ硬化物のアッベ数を低くするには限界がある。
　そこで、重合性官能基を有しないことで屈折率がさらに高くされ、かつアッベ数がさらに低くされたフルオレン構造を有する特定の化合物（Ｂ）をさらに含ませることによって、硬化物の屈折率をさらに高く、かつ硬化物のアッベ数をさらに低くしている。しかし、化合物（Ａ）は粘度が高く、しかも化合物（Ｂ）は２５℃で固体のものが多いため、化合物（Ａ）および化合物（Ｂ）の混合物は、粘度がかなり高い。
　そこで、粘度が低く、屈折率があまり低くなく、かつアッベ数が低い、（メタ）アクリロイル基およびビフェニル構造を有する特定の化合物（Ｃ）をさらに含ませることによって、硬化物の屈折率の低下を抑えつつ、硬化性組成物の粘度を低下させている。
＜硬化物＞
　本発明の硬化物は、本発明の硬化性組成物を硬化したものである。本発明の硬化物を基材の表面に形成して、硬化物からなる層と基材からなる層とを有する積層体としてもよい。
　硬化物の波長５８９ｎｍの光に対する屈折率は、１．６１以上が好ましく、１．６３以上がより好ましい。屈折率が前記範囲の下限値以上であれば、光学部材の材料とした場合、薄肉化が可能となる。上限は特に限定されないが、有機物であることを考慮すると１．８５程度である。
　硬化物の下式（Ｉ）から求めたアッベ数は、２４以下が好ましく、２３以下がより好ましい。アッベ数が前記範囲の上限値以下であれば、光学部材の材料とした場合、アッベ数の高い材料と組み合わせることで色収差を減少させることができる。アッベ数は低ければ低いほどよく、下限は特に限定されないが、有機物であることを考慮すると１９程度である。
　νＤ＝（ｎＤ－１）／（ｎＦ－ｎＣ）　　（Ｉ）
　ただし、νＤは、アッベ数であり、ｎＤは、波長５８９ｎｍの光に対する屈折率であり、ｎＦは、波長４８６ｎｍの光に対する屈折率であり、ｎＣは、波長６５６ｎｍの光に対する屈折率である。
　（硬化物の製造方法）
　本発明の硬化物を製造する方法としては、微細パターンの反転パターンを表面に有するモールドと硬化性組成物とを接触させた状態で該硬化性組成物を硬化させて、微細パターンを表面に有する硬化物を形成する方法（インプリント法）；モールドのキャビティ内に硬化性組成物を注入し、該硬化性組成物を硬化させて硬化物を形成する方法（注型成形法）等が挙げられる。
　硬化方法は、光硬化または熱硬化が挙げられ、重合開始剤（Ｄ）に応じて適宜選択すればよい。硬化方法としては、硬化物の製造のしやすさの点から、光硬化が好ましい。
　以上説明した本発明の硬化物にあっては、本発明の硬化性組成物を硬化したものであるため、屈折率が高く、かつアッベ数が低い。
　以下、実施例によって本発明を具体的に説明するが、本発明はこれらの実施例に限定して解釈されない。なお、例１～３は実施例であり、例４、５は比較例である。
　（硬化性組成物の粘度）
　硬化性組成物の粘度は、動的粘弾性測定装置（Ａｎｔｏｎ　Ｐａａｒ社製、Ｐｈｙｓｉｃａ　ＭＣＲ３０１）を用いて、１０ｓ－１の剪断速度における動的粘弾性を２５℃で測定し、求めた。
　（硬化性組成物の屈折率）
　硬化性組成物の屈折率は、アッベ屈折計（アタゴ社製、多波長アッベ屈折計ＤＲ－Ｍ２）を用い、温度：２５℃、波長：５８９ｎｍにおいて測定した。
　（硬化性組成物のアッベ数）
　硬化性組成物のアッベ数は、アッベ屈折計（同上）を用い、温度：２５℃で、波長：５８９ｎｍ、４８６ｎｍ、および６５６ｎｍのそれぞれの屈折率を測定し、下式（Ｉ）から算出した。
　νＤ＝（ｎＤ－１）／（ｎＦ－ｎＣ）　　（Ｉ）
　ただし、νＤは、アッベ数であり、ｎＤは、波長５８９ｎｍの光に対する屈折率であり、ｎＦは、波長４８６ｎｍの光に対する屈折率であり、ｎＣは、波長６５６ｎｍの光に対する屈折率である。
　（硬化物の屈折率）
　シリコンウエハの表面に硬化性組成物を塗布し、高圧水銀ランプから紫外線を露光量：３０００ｍＪ／ｃｍ２で照射して、膜状の硬化物を形成した。屈折率測定装置（米国メトリコン社製プリズムカプラ：２０１０／Ｍ）を用いて、膜状の硬化物の波長４７３ｎｍ、５９４ｎｍおよび６５８ｎｍの光に対する屈折率を測定し、装置付属のＭｅｔｒｉｃｏｎ
　Ｆｉｔを用いて波長５８９ｎｍの光に対する屈折率を算出した。
　（硬化物のアッベ数）
　上述の装置付属のＭｅｔｒｉｃｏｎ　Ｆｉｔを用いて各波長における屈折率を算出し、上式（Ｉ）からアッベ数を算出した。
　（化合物（Ａ））
　化合物（Ａ１－１）：９，９－ビス（４－（２－アクリロイルオキシエトキシ）フェニル）フルオレン（大阪ガスケミカル社製、オグソール（商品名）ＥＡ－０２００、溶剤：トルエン（５質量％）、ｎＤ：１．６０８、νＤ：２４．８、２５℃における粘度：１０００００ｍＰａ・ｓ以上）。
Figure JPOXMLDOC01-appb-C000018
　（化合物（Ｂ））
　化合物（Ｂ１－１）：９，９－ビス（４－ヒドロキシフェニル）フルオレン（大阪ガスケミカル社製、ＢＰＦ、ｎＤ：１．６８０、νＤ：１９、２５℃において固体）。
Figure JPOXMLDOC01-appb-C000019
　（化合物（Ｃ））
　化合物（Ｃ１－１）：ｏ－フェニルベンジルアクリレート（ＤＩＣ社製、ユニディック（商品名）ＥＫＺ－９４８、ｎＤ：１．５８５、νＤ：２４．１、２５℃における粘度：２８ｍＰａ・ｓ）。
Figure JPOXMLDOC01-appb-C000020
　（重合開始剤（Ｄ））
　重合開始剤（Ｄ－１）：光ラジカル重合開始剤（ＢＡＳＦジャパン社製、ＩＲＧＡＣＵＲＥ（商品名）１８４）。
　（化合物（Ｅ））
　化合物（Ｅ１－１）：ＣＨ２＝Ｃ（ＣＨ３）Ｃ（Ｏ）Ｏ（ＣＨ２）２（ＣＦ２）６Ｆ。
　（例１）
　化合物（Ａ１－１）の１．５０ｇ（ＥＡ－０２００の１．５８ｇ：大阪ガスケミカル社製「ＥＡ－０２００」、揮発分として５質量％のトルエンを含む）、化合物（Ｂ１－１）の４．４５ｇ、化合物（Ｃ１－１）の１０．０ｇ、およびメチルエチルケトンの５．０ｇを均一になるように混合し、４０℃で溶媒の減圧留去を行った。得られた溶液に重合開始剤（Ｄ－１）の０．４８ｇを混合し、例１の硬化性組成物を得た。各成分の量を表１に示す。粘度、屈折率およびアッベ数を表２に示す。
　（例２～５）
　化合物（Ａ１－１）、化合物（Ｂ１－１）、化合物（Ｃ１－１）、化合物（Ｄ－１）および化合物（Ｅ１－１）の量を表１に示す量に変更した以外は、例１と同様にして硬化性組成物を得た。粘度、屈折率およびアッベ数を表２に示す。
Figure JPOXMLDOC01-appb-T000021
Figure JPOXMLDOC01-appb-T000022
　化合物（Ａ）～（Ｃ）及び（Ｄ）を含む例１～３は、化合物（Ｂ）を含まない例４、５に比べ、硬化物の屈折率が高く、かつアッベ数が低かった。また、化合物（Ｃ）を４５質量％以上含む例１～３は、化合物（Ｃ）が４５質量％未満の例４に比べ、硬化性組成物の粘度が低かった。
　本発明の硬化性組成物は、光学部材（レンズ、プリズム、反射防止膜、光導波路、ＬＥＤ封止材等）、記録メディア、半導体デバイス製造等に用いられる材料として有用である。
　なお、２０１５年１１月２６日に出願された日本特許出願２０１５－２３１０１４号の明細書、特許請求の範囲、図面、及び要約書の全内容をここに引用し、本発明の明細書の開示として、取り入れるものである。

Claims (13)

  1. 　（メタ）アクリロイル基を有し、かつ下式（１）で表されるフルオレン構造を有する化合物（Ａ）と、
    　重合性官能基を有さず、かつ下式（１）で表されるフルオレン構造を有する化合物（Ｂ）と、
    　（メタ）アクリロイル基を有し、かつ下式（２）で表されるビフェニル構造を有する化合物（Ｃ）（ただし、前記化合物（Ａ）と同じものを除く。）と、
    　重合開始剤（Ｄ）と、を含み、
    　すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量％のうち、前記化合物（Ａ）が、１～２０質量％であり、前記化合物（Ｂ）が、９～４０質量％であり、前記化合物（Ｃ）が、４５～８９質量％であり、
    　すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量部に対して、前記重合開始剤（Ｄ）が、０．０１～１０質量部である、硬化性組成物。
    Figure JPOXMLDOC01-appb-C000001
     　ただし、＊印は結合手を表し、フルオレン構造およびビフェニル構造は、置換基を有していてもよい。
  2. 　前記化合物（Ａ）が、下式（Ａ１）で表される、請求項１に記載の硬化性組成物。
    Figure JPOXMLDOC01-appb-C000002
     　（式（Ａ１）中、Ｒ１は、水素原子またはメチル基である。Ｒ２は、－ＣＨ２－、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＣＨ３）－、ＣＨ２ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－、または－ＣＨ２ＣＨ（ＯＲ４）ＣＨ２－（ただし、Ｒ４は（メタ）アクリロイル基である。）である。ａは０～４の整数である。Ｒ３は水素原子またはアルキル基である。）
  3. 　前記式（Ａ１）中、Ｒ２は、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－、または－ＣＨ２ＣＨ（ＯＲ４）ＣＨ２－（ただし、Ｒ４は（メタ）アクリロイル基である。）でり、ａは、１または２の整数である、請求項２に記載の硬化性組成物。
  4. 　前記化合物（Ｂ）が下式（Ｂ１）で表される、請求項１～３のいずれかに記載の硬化性組成物。
    Figure JPOXMLDOC01-appb-C000003
     　（式（Ｂ１）中、Ｘは、水酸基、－Ｏ（Ｒ６Ｏ）ｂＨ（ただし、Ｒ６は－ＣＨ２－、－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ（ＣＨ３）－、ＣＨ２ＣＨ２ＣＨ２－、または－ＣＨ２ＣＨ（ＯＨ）ＣＨ２－であり、ｂは１～４の整数である。）、グリシジルオキシ基、またはアミノ基である。Ｒ５は、水素原子またはアルキル基である。）
  5. 　前記式（Ｂ１）におけるＸが、水酸基または２－ヒドロキシエトキシ基である、請求項４に記載の硬化性組成物。
  6. 　前記化合物（Ｃ）が下式（Ｃ１）または下式（Ｃ２）で表される、請求項１～５のいずれかに記載の硬化性組成物。
    Figure JPOXMLDOC01-appb-C000004
     （式（Ｃ１）、式（Ｃ２）中、Ｒ７は、水素原子またはメチル基である。なお、化合物（Ｃ１）において、－ＣＨ２ＯＣ（Ｏ）ＣＲ７＝ＣＨ２は、２つのフェニル基のうち左側のフェニル基に対して右側のフェニル基のオルト位またはメタ位に結合する。Ｒ８は、水素原子またはメチル基である。Ｒ９は、水素原子またはメチル基である。ｍは、１または２である。）
  7. 　フッ素原子を有し、かつ（メタ）アクリロイル基を１つ以上有する化合物（Ｅ）（ただし、前記化合物（Ａ）または前記化合物（Ｃ）と同じものを除く。）をさらに含み、
    　すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量％のうち、前記化合物（Ｅ）が、０．０１～５質量％である、請求項１～６のいずれかに記載の硬化性組成物。
  8. 　前記化合物（Ｅ）が下式（Ｅ１）で表され、すべての（メタ）アクリロイル基を有する化合物と前記化合物（Ｂ）との合計１００質量％のうち、前記化合物（Ｅ）が、０．０１～５質量％である、請求項１ないし６のいずれかに記載の硬化性組成物。
    Figure JPOXMLDOC01-appb-C000005
     （式（Ｅ１）中、Ｒ１０は、水素原子またはメチル基である。Ｒ１１は、炭素数１～２０のアルキレン基、炭素数３～２０のシクロアルキレン基、炭素数６～２０の芳香族基およびこれらを組み合わせて得られる基からなる群から選ばれる１種である。Ｒｆ、炭素原子間にエーテル性酸素原子を有していてもよい、炭素数２０以下のフルオロアルキル基である。）
  9. 　請求項１～８のいずれかに記載の硬化性組成物を硬化した硬化物。
  10. 　温度２５℃における粘度が２０Ｐａ・ｓ以下である、請求項９に記載の硬化性組成物を硬化した硬化物。
  11. 　波長５８９ｎｍの光に対する屈折率が１．６１以上である、請求項９又は１０に記載の硬化性組成物を硬化した硬化物。
  12. 　下記式（Ｉ）から求められるアッベ指数が２４以下である、請求項９～１１のいずれかに記載の硬化性組成物を硬化した硬化物。
  13. 　請求項１～１１のいずれかに記載の硬化性組成物をインプリント法又は注型成形法により硬化させる硬化物の製造方法。
PCT/JP2016/084333 2015-11-26 2016-11-18 硬化性組成物および硬化物 WO2017090537A1 (ja)