WO2016125569A1 - サブマージアーク溶接用フラックス - Google Patents
サブマージアーク溶接用フラックス Download PDFInfo
- Publication number
- WO2016125569A1 WO2016125569A1 PCT/JP2016/051239 JP2016051239W WO2016125569A1 WO 2016125569 A1 WO2016125569 A1 WO 2016125569A1 JP 2016051239 W JP2016051239 W JP 2016051239W WO 2016125569 A1 WO2016125569 A1 WO 2016125569A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mass
- flux
- content
- less
- welding
- Prior art date
Abstract
高速での溶接作業性及び溶接金属の耐欠陥性が良好となるサブマージアーク溶接用フラックスを提供する。 サブマージアーク溶接用フラックスを、FのCaF2 換算値:2~22質量%、MgO:8~28質量%、NaのNa2 O換算値及びKのK2 O換算値のうち少なくとも一つ以上の合計:0.5~6.5質量%、MnのMnO換算値:2~22質量%、FeのFeO換算値:0.5~6.5質量%、SiO2 :12~32質量%、Al2 O3 :16~36質量%、ZrO2 :0.4~10質量%、水溶性SiO2 :1質量%未満(0質量%を含む)を含有する組成にする。
Description
本発明は、サブマージアーク溶接用フラックスに関する。
サブマージアーク溶接に用いられるフラックスは、その形態から、溶融型フラックスと焼成型フラックスに大別される。溶融型フラックスは、種々の原料を電気炉などで溶解し、粉砕することにより製造される。一方、焼成型フラックスは、種々の原料をケイ酸アルカリなどのバインダにより結合し、造粒した後、焼成することにより製造される。
また、焼成型フラックスは、焼成温度によって分類され、一般に、400℃以上600℃未満で焼成したものを低温焼成型フラックス、600~1200℃で焼成したものを高温焼成型フラックスという。従来、突合せ継手の高速溶接を行う場合は、ビード外観を良好とするため溶融温度の低い溶融型フラックスが一般的に用いられる。その反面、溶融温度が低いため入熱の高い溶接には不向きであるものの、吹上げを低減しシールド性を向上する目的で、フラックスの粒度を細かくして対応する技術が確立されている。しかし、細かい粒度を多く含むフラックスは、耐アンダーカット性が劣ったり、溶接前の搬送又は溶接時の散布及び回収において大気中に巻き上がり、堆積粉塵となって溶接作業環境が劣化するため、溶接作業者が吸入することで人体への悪影響が懸念されたりする。
そこで、高速サブマージアーク溶接用焼成型フラックスに関し、種々の検討がなされている。
例えば、特許文献1には、高速サブマージアーク溶接用焼成型フラックスに関し、特に多電極サブマージアーク溶接において高速溶接が可能であり、かつ高靭性溶接金属の得られる焼成型フラックスに関する技術が開示されている。
特許文献1の高速サブマージアーク溶接用焼成型フラックスは、SiO2 12~24%, TiO2 9~20%, Al2 O3 15~25%, MnO 8~15%, MgO 18~25%, CaO 1~13%, CaF2 10~20%, 及びFeO 2%以下を主要成分として含有する。そして、このフラックスは、溶接時に前記フラックスが熱分解して発生するガス量が1.5~3%であり、前記主要成分とガス成分の他は不可避的不純物からなる。また、フラックス累積粒度分布において50重量%を占める粒子のメジアン径が500~800μmの範囲内にあり、フラックス中の粒子径295μm以下の粒子は全体の15%以下であり、フラックスのかさ比重が0.7~1.2g/cm3 の範囲内にある。
例えば、特許文献1には、高速サブマージアーク溶接用焼成型フラックスに関し、特に多電極サブマージアーク溶接において高速溶接が可能であり、かつ高靭性溶接金属の得られる焼成型フラックスに関する技術が開示されている。
特許文献1の高速サブマージアーク溶接用焼成型フラックスは、SiO2 12~24%, TiO2 9~20%, Al2 O3 15~25%, MnO 8~15%, MgO 18~25%, CaO 1~13%, CaF2 10~20%, 及びFeO 2%以下を主要成分として含有する。そして、このフラックスは、溶接時に前記フラックスが熱分解して発生するガス量が1.5~3%であり、前記主要成分とガス成分の他は不可避的不純物からなる。また、フラックス累積粒度分布において50重量%を占める粒子のメジアン径が500~800μmの範囲内にあり、フラックス中の粒子径295μm以下の粒子は全体の15%以下であり、フラックスのかさ比重が0.7~1.2g/cm3 の範囲内にある。
また、例えば、特許文献2には、高速サブマージアーク溶接用焼成型フラックスに関し、特に、多電極サブマージアーク溶接において高速溶接が可能であり、かつ溶接金属の酸素量を低減して高靭性が得られる焼成型フラックスに関する技術が開示されている。
特許文献2の、高速サブマージアーク溶接用焼成型フラックスは、SiO2 12~24%, TiO2 1~6%, Al2 O3 15~25%, MnO 6%以下, MgO 25~40%, CaO 1~13%, CaF2 15~28%, 及びFeO 2%以下を主要成分として含有する。そして、このフラックスは、溶接時に前記フラックスが熱分解して発生するガス量が1.5~3%であり、前記主要成分とガス成分の他は不可避的不純物からなる。また、フラックス累積粒度分布において50重量%を占める粒子のメジアン径が500~800μmの範囲内にあり、フラックス中の粒子径295μm以下の粒子は全体の15%以下であり、フラックスのかさ比重が0.7~1.2g/cm3 の範囲内にある。
特許文献2の、高速サブマージアーク溶接用焼成型フラックスは、SiO2 12~24%, TiO2 1~6%, Al2 O3 15~25%, MnO 6%以下, MgO 25~40%, CaO 1~13%, CaF2 15~28%, 及びFeO 2%以下を主要成分として含有する。そして、このフラックスは、溶接時に前記フラックスが熱分解して発生するガス量が1.5~3%であり、前記主要成分とガス成分の他は不可避的不純物からなる。また、フラックス累積粒度分布において50重量%を占める粒子のメジアン径が500~800μmの範囲内にあり、フラックス中の粒子径295μm以下の粒子は全体の15%以下であり、フラックスのかさ比重が0.7~1.2g/cm3 の範囲内にある。
しかしながら、特許文献1に関しては、3電極溶接で溶接速度は200cm/minのため、溶融フラックスで可能な溶接速度と比較すると高速とは言えない。
また、特許文献2に関しては、3電極溶接で溶接速度は160cm/minのため、溶融フラックスで可能な溶接速度と比較すると高速とは言えない。
また、高速サブマージアーク溶接用焼成型フラックスでは、溶接金属の耐欠陥性に優れることも要求されている。
また、特許文献2に関しては、3電極溶接で溶接速度は160cm/minのため、溶融フラックスで可能な溶接速度と比較すると高速とは言えない。
また、高速サブマージアーク溶接用焼成型フラックスでは、溶接金属の耐欠陥性に優れることも要求されている。
そこで、本発明は、高速での溶接作業性及び溶接金属の耐欠陥性が良好となるサブマージアーク溶接用フラックスを提供することを課題とする。
本発明に係るサブマージアーク溶接用フラックスは、FのCaF2 換算値:2~22質量%、MgO:8~28質量%、NaのNa2 O換算値及びKのK2 O換算値のうち少なくとも一つ以上の合計:0.5~6.5質量%、MnのMnO換算値:2~22質量%、FeのFeO換算値:0.5~6.5質量%、SiO2 :12~32質量%、Al2 O3:16~36質量%、ZrO2 :0.4~10質量%、水溶性SiO2 :1質量%未満(0質量%を含む)を含有することを特徴とする。
このような構成によれば、フラックスは、所定成分を所定量含有することで、高速での溶接作業性及び溶接金属の耐欠陥性が良好となる。
なお、本願での高速とは、例えば210~600cm/min以下の溶接速度をいう。また、本願での溶接作業性とは、ビード外観、ビード形状、スラグ剥離性及びアーク安定性の良劣をいう。
なお、本願での高速とは、例えば210~600cm/min以下の溶接速度をいう。また、本願での溶接作業性とは、ビード外観、ビード形状、スラグ剥離性及びアーク安定性の良劣をいう。
このサブマージアーク溶接用フラックスは、更に、CaOの換算値:18質量%以下(0質量%を含まず)を含有することが好ましい。
このような構成によれば、溶接金属の清浄度及び溶融スラグの流動性が向上する。
このような構成によれば、溶接金属の清浄度及び溶融スラグの流動性が向上する。
このサブマージアーク溶接用フラックスは、更に、TiO2 :6質量%以下(0質量%を含まず)を含有することが好ましい。
このような構成によれば、溶接作業性及び溶接金属の靭性が向上する。
このような構成によれば、溶接作業性及び溶接金属の靭性が向上する。
このサブマージアーク溶接用フラックスは、前記Al2 O3 含有量を[Al2 O3 ]、前記TiO2 含有量を[TiO2 ]、前記ZrO2 含有量を[ZrO2 ]としたとき、下記数式(I)を満たすことが好ましい。
このような構成によれば、前記した各成分を所定量とすることに併せて、より厳密に成分を制御することで、更に、溶接作業性が向上する。
このサブマージアーク溶接用フラックスは、更に、B2 O3 :3質量%以下(0質量%を含まず)を含有することが好ましい。
このような構成によれば、溶接金属の靭性が向上する。
このような構成によれば、溶接金属の靭性が向上する。
本発明のサブマージアーク溶接用フラックスでは、高速で溶接作業が行われる高温焼成型フラックスとして好適である。
このサブマージアーク溶接用フラックスは、0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすことが好ましい。
このような構成によれば、溶接作業性及び溶接金属の耐欠陥性が向上し、溶接作業環境が改善する。
このような構成によれば、溶接作業性及び溶接金属の耐欠陥性が向上し、溶接作業環境が改善する。
本発明によれば、各成分の含有量を特定することで、高速での溶接作業性及び溶接金属の耐欠陥性が良好となる。
以下、本発明を実施するための形態について、詳細に説明する。なお、本発明は、以下に説明する実施形態に限定されるものではない。
本発明の実施形態に係るサブマージアーク溶接用フラックス(以下、単にフラックスともいう。)は、F(CaF2 換算値)含有量、MgO含有量、Na(Na2 O換算値)とK(K2 O換算値)との合計の含有量、Mn(MnO換算値)含有量、Fe(FeO換算値)含有量、SiO2 含有量、Al2 O3 含有量、ZrO2 含有量及び水溶性SiO2 含有量を規定したものである。
また、本発明の実施形態に係るフラックスは、更に、CaO(換算値)、TiO2 及びB2 O3 のうち少なくとも1種を含有してもよい。これらの成分を含有する場合は、所定量とすることが好ましい。
以下、本実施形態のフラックスにおける組成限定理由について説明する。なお、本実施形態のフラックスにおける各成分の含有量は、特に断りのない限り、JIS Z 3352:2010に規定される方法で定量した値を、酸化物又はフッ化物に換算した換算値である。また、各成分の含有量は、フラックス全体についての含有量である。また、本実施形態のフラックスにおいては、粒度分布の測定についても、JIS Z 3352:2010に従う。
[FのCaF2 換算値:2~22質量%]
CaF2 などのフッ化物は、溶融スラグの電気伝導性及び流動性を高める効果があり、溶融スラグの高温粘性に影響を与える成分の1つである。この作用は、後述するCaOと同様に、その含有量に比例する。具体的には、F含有量(CaF2 換算値)が2質量%未満の場合、前述した効果が十分に得られず、また、溶融スラグからCOガスの排出を促進し、耐ポックマーク性を改善する効果も期待できない。
CaF2 などのフッ化物は、溶融スラグの電気伝導性及び流動性を高める効果があり、溶融スラグの高温粘性に影響を与える成分の1つである。この作用は、後述するCaOと同様に、その含有量に比例する。具体的には、F含有量(CaF2 換算値)が2質量%未満の場合、前述した効果が十分に得られず、また、溶融スラグからCOガスの排出を促進し、耐ポックマーク性を改善する効果も期待できない。
一方、F含有量(CaF2 換算値)が22質量%を超えると、溶融スラグの流動性が高くなりすぎて、ビード形状が劣化する。よって、F含有量(CaF2 換算値)は2~22質量%とする。F含有量(CaF2 換算値)は、耐ポックマーク性向上の観点から、4質量%以上が好ましく、より好ましくは6質量%以上である。また、ビード形状向上の観点からは、F含有量(CaF2 換算値)は、20質量%以下が好ましく、より好ましくは18質量%以下である。
なお、ここでいうF含有量は、JIS Z 3352:2010に規定される方法(例えばJIS K 1468-2:1999など)で分析して得たフラックスの全F量を、CaF2 で換算した値である。また、本実施形態のフラックスにおけるフッ化物成分は、主にCaF2 であり、その他にAlF3 又はMgF2 などが含まれることがあるが、F含有量(全F量のCaF2 換算値)が前述した範囲内であれば、前述したフッ化物の効果には影響しない。
[MgO:8~28質量%]
MgOは、スラグ剥離性の向上に大きく寄与する成分であり、溶接電源の方式によらず、良好なスラグ剥離性を確保するために必須の成分である。しかしながら、MgO含有量が8質量%未満の場合、その効果が十分に得られず、また、28質量%を超えると、ビード形状が劣化し、溶接電源の種別に依存してスラグ巻込み、融合不良、更にはアンダーカットなどの欠陥が発生しやすくなる。特に、交流式溶接電源においては、前述したスラグ巻き込み及び溶融不良などの溶接欠陥の発生が顕著になる。よって、MgO含有量は8~28質量%とする。
MgOは、スラグ剥離性の向上に大きく寄与する成分であり、溶接電源の方式によらず、良好なスラグ剥離性を確保するために必須の成分である。しかしながら、MgO含有量が8質量%未満の場合、その効果が十分に得られず、また、28質量%を超えると、ビード形状が劣化し、溶接電源の種別に依存してスラグ巻込み、融合不良、更にはアンダーカットなどの欠陥が発生しやすくなる。特に、交流式溶接電源においては、前述したスラグ巻き込み及び溶融不良などの溶接欠陥の発生が顕著になる。よって、MgO含有量は8~28質量%とする。
MgO含有量は、スラグ剥離性向上の観点から、10質量%以上とすることが好ましく、より好ましくは12質量%以上である。また、欠陥発生の抑制の観点から、MgO含有量は26質量%以下とすることが好ましく、より好ましくは24質量%以下である。
なお、ここでいうMgO含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8222:1997など)で分析して得たフラックスの全Mg量を、MgOで換算した値である。この方法で測定した全Mg量には、MgF2 などのMgO以外の成分が含まれることがあるが、これらの成分は微量であるため、MgO含有量(全Mg量のMgO換算値)が前述した範囲内であれば、前述したMgOの効果には影響しない。
なお、ここでいうMgO含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8222:1997など)で分析して得たフラックスの全Mg量を、MgOで換算した値である。この方法で測定した全Mg量には、MgF2 などのMgO以外の成分が含まれることがあるが、これらの成分は微量であるため、MgO含有量(全Mg量のMgO換算値)が前述した範囲内であれば、前述したMgOの効果には影響しない。
[NaのNa2 O換算値及びKのK2 O換算値のうち少なくとも一つ以上の合計:0.5~6.5質量%]
(すなわち、NaのNa2 O換算値及びKのK2 O換算値の合計:0.5~6.5質量%(Na及びKのうち少なくとも一つ以上を含む))
Na及びKは、主に溶接時のアーク安定性とフラックスの吸湿特性に影響を与える成分であり、主に、Na2 O及びK2 Oなどの酸化物の形態で添加される。しかしながら、Na含有量(Na2 O換算値)及びK含有量(K2 O換算値)が合計で0.5質量%未満の場合、溶接時のアーク電圧が不安定となり、ビード外観及びビード形状が劣化する。
(すなわち、NaのNa2 O換算値及びKのK2 O換算値の合計:0.5~6.5質量%(Na及びKのうち少なくとも一つ以上を含む))
Na及びKは、主に溶接時のアーク安定性とフラックスの吸湿特性に影響を与える成分であり、主に、Na2 O及びK2 Oなどの酸化物の形態で添加される。しかしながら、Na含有量(Na2 O換算値)及びK含有量(K2 O換算値)が合計で0.5質量%未満の場合、溶接時のアーク電圧が不安定となり、ビード外観及びビード形状が劣化する。
一方、Na含有量(Na2 O換算値)及びK含有量(K2 O換算値)が合計で6.5質量%を超えると、フラックスの吸湿特性が劣化すると共に、アークが強くなりすぎて不安定となり、ビード外観及びビード形状が劣化する。よって、Na含有量(Na2 O換算値)及びK含有量(K2 O換算値)は、合計で0.5~6.5質量%とする。なお、本実施形態のフラックスは、Na及びKのうち少なくとも一種類が添加されていればよい。
Na含有量(Na2 O換算値)及びK含有量(K2 O換算値)は、アーク電圧の安定化の観点から、合計で1質量%以上であることが好ましく、より好ましくは1.5質量%以上である。また、フラックスの吸湿特性、アーク安定性の観点から、Na含有量(Na2 O換算値)及びK含有量(K2 O換算値)は、合計で6質量%以下であることが好ましく、より好ましくは5.5質量%以下である。
なお、ここでいうNa含有量及びK含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8852:1998など)で分析して得たフラックスの全Na量及び全K量を、それぞれNaO及びK2 Oで換算した値である。また、本実施形態のフラックスにおけるNa成分及びK成分は、主にNa2 O及びK2 Oであるが、その他にNaAlSi3 O8 又はKAlSi3 O8 などが含まれることがある。
また、ここでのNa、Kは、鉱石原料及び水ガラスに由来するものである。
また、ここでのNa、Kは、鉱石原料及び水ガラスに由来するものである。
[MnのMnO換算値:2~22質量%]
Mnは、溶融スラグの粘性及び凝固温度に影響を与えると共に、耐ポックマーク性改善に有効な成分であり、主に、MnO、MnO2 及びMn2 O3 などの酸化物の形態で添加される。各種形態の中でも、特に一酸化マンガン(MnO)の形態で添加すると、その有用性が発揮される。ただし、Mn含有量(MnO換算値)が2質量%未満の場合、その効果が十分に発揮されず、また、22質量%を超えると、スラグが脆くなってスラグ剥離性が劣化する。よって、Mn含有量(MnO換算値)は、2~22質量%とする。
Mnは、溶融スラグの粘性及び凝固温度に影響を与えると共に、耐ポックマーク性改善に有効な成分であり、主に、MnO、MnO2 及びMn2 O3 などの酸化物の形態で添加される。各種形態の中でも、特に一酸化マンガン(MnO)の形態で添加すると、その有用性が発揮される。ただし、Mn含有量(MnO換算値)が2質量%未満の場合、その効果が十分に発揮されず、また、22質量%を超えると、スラグが脆くなってスラグ剥離性が劣化する。よって、Mn含有量(MnO換算値)は、2~22質量%とする。
このMn(MnO換算値)は、耐ポックマーク性向上の観点から、4質量%以上が好ましく、より好ましくは6質量%以上である。また、スラグ剥離性向上の観点からは、Mn(MnO換算値)は、20質量%以下が好ましく、より好ましくは18質量%以下である。なお、ここでいうMn含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8232:2005など)で分析して得たフラックスの全Mn量を、MnOで換算した値である。
[FeのFeO換算値:0.5~6.5質量%]
Feは、脱酸現象を促進し、耐ポックマーク性を高める効果があり、主に、Fe-Siなどの金属粉の形態で添加される。前述した効果は、その存在量に比例し、Fe含有量(FeO換算値)が0.5質量%未満の場合、特に溶接電源が直流式の場合に、十分な効果が得られない。一方、Fe含有量(FeO換算値)が6.5質量%を超えると、スラグの凝固温度に影響を与え、ビード外観、ビード形状及びスラグ剥離が劣化する。よって、Fe含有量(FeO換算値)は0.5~6.5質量%とする。
Feは、脱酸現象を促進し、耐ポックマーク性を高める効果があり、主に、Fe-Siなどの金属粉の形態で添加される。前述した効果は、その存在量に比例し、Fe含有量(FeO換算値)が0.5質量%未満の場合、特に溶接電源が直流式の場合に、十分な効果が得られない。一方、Fe含有量(FeO換算値)が6.5質量%を超えると、スラグの凝固温度に影響を与え、ビード外観、ビード形状及びスラグ剥離が劣化する。よって、Fe含有量(FeO換算値)は0.5~6.5質量%とする。
Fe含有量(FeO換算値)は、耐ポックマーク性の観点から、1質量%以上とすることが好ましく、より好ましくは1.5質量%以上である。また、スラグの凝固温度への影響を考慮すると、Fe含有量(FeO換算値)は、6質量%以下であることが好ましく、より好ましくは5.5質量%以下である。
なお、ここでいうFe含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8202:2000など)で分析して得たフラックスの全Fe量を、FeOで換算した値であり、金属粉として添加されるFe以外に、不可避的不純物として添加されるFeO、Fe2 O3 及びFe3 O4 などが含まれることがある。
[SiO2 :12~32質量%]
SiO2 は、溶融スラグに適度の粘性を与えることによって、主にビード外観及びビード形状を良好にする効果がある。しかしながら、SiO2 含有量が12質量%未満の場合、前述した効果が十分に得られず、ビード外観及びビード形状が劣化する。また、SiO2 含有量が32質量%を超えると、過剰となり、スラグ剥離性が劣化すると共に、スラグの焼付きが激しくなる。よって、SiO2 含有量は12~32質量%とする。
SiO2 は、溶融スラグに適度の粘性を与えることによって、主にビード外観及びビード形状を良好にする効果がある。しかしながら、SiO2 含有量が12質量%未満の場合、前述した効果が十分に得られず、ビード外観及びビード形状が劣化する。また、SiO2 含有量が32質量%を超えると、過剰となり、スラグ剥離性が劣化すると共に、スラグの焼付きが激しくなる。よって、SiO2 含有量は12~32質量%とする。
SiO2 含有量は、ビード外観及びビード形状の向上の観点から、14質量%以上とすることが好ましく、より好ましくは16質量%以上である。また、スラグ剥離性の観点から、SiO2 含有量は30質量%以下とすることが好ましく、より好ましくは28質量%以下である。
なお、ここでいうSiO2 含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8214:1995など)で分析して得たフラックスの全Si量を、SiO2 で換算した値である。この方法で測定した全Si量には、Fe-Siなどの合金として添加されるSiなどSiO2 以外の成分が含まれているが、SiO2 含有量(全Si量のSiO2 換算値)が前述した範囲内であれば、前述したSiO2 の効果には影響しない。
[Al2 O3 :16~36質量%]
Al2 O3 は、溶融スラグの粘性及び融点を調整する成分であり、溶接時のビード形状を良好にする効果がある。しかしながら、Al2 O3 含有量が16質量%未満の場合は、前述した効果が十分に得られず、また、Al2 O3 含有量が36質量%を超えると、溶融スラグの融点が上昇しすぎて、溶接時にビード形状の劣化を招く。よって、Al2 O3 含有量は16~36質量%とする。
Al2 O3 は、溶融スラグの粘性及び融点を調整する成分であり、溶接時のビード形状を良好にする効果がある。しかしながら、Al2 O3 含有量が16質量%未満の場合は、前述した効果が十分に得られず、また、Al2 O3 含有量が36質量%を超えると、溶融スラグの融点が上昇しすぎて、溶接時にビード形状の劣化を招く。よって、Al2 O3 含有量は16~36質量%とする。
Al2 O3 含有量は、溶融スラグの粘性及び融点の調整の観点から、18質量%以上とすることが好ましく、より好ましくは20質量%以上である。また、溶融スラグの融点の観点からは、Al2 O3 含有量は34質量%以下とすることが好ましく、より好ましくは32質量%以下である。これにより、ビード形状を更に良好にすることができる。
なお、ここでいうAl2 O3 含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8220:1995など)で分析して得たフラックスの全Al量を、Al2 O3 で換算した値である。この方法で測定した全Al量には、AlF3 などのAl2 O3 以外の成分が含まれることがあるが、これらの成分は微量であるため、Al2 O3 含有量(全Al量のAl2 O3 換算値)が前述した範囲内であれば、前述したAl2 O3 の効果には影響しない。
[ZrO2 :0.4~10質量%]
ZrO2 は、溶融スラグの粘性及び凝固温度に影響を与えると共に、高速度の溶接でアーク安定性、良好なビード形状及びビード外観並びに良好なスラグ剥離性を得るためには極めて重要な成分である。ZrO2 が0.4質量%未満ではその効果が得られない。一方、ZrO2 が10質量%を超えると、ビード形状が劣化する。よって、ZrO2 含有量は0.4~10質量%とする。
ZrO2 は、溶融スラグの粘性及び凝固温度に影響を与えると共に、高速度の溶接でアーク安定性、良好なビード形状及びビード外観並びに良好なスラグ剥離性を得るためには極めて重要な成分である。ZrO2 が0.4質量%未満ではその効果が得られない。一方、ZrO2 が10質量%を超えると、ビード形状が劣化する。よって、ZrO2 含有量は0.4~10質量%とする。
ZrO2 含有量は、アーク安定性、ビード外観及びビード形状並びにスラグ剥離性の向上の観点から、0.7質量%以上とすることが好ましく、より好ましくは1質量%以上である。また、ビード形状の観点から、ZrO2 含有量は9質量%以下とすることが好ましく、より好ましくは8質量%以下である。
[水溶性SiO2 :1質量%未満(0質量%を含む)]
水溶性SiO2 の含有量が1質量%以上であると、高速での溶接作業性及び溶接金属の耐欠陥性が劣化する。よって、水溶性SiO2 含有量は1質量%未満(0質量%を含む)に規制する。水溶性SiO2 含有量は、高速での溶接作業性及び溶接金属の耐欠陥性の観点から、0.9質量%以下であることが好ましく、より好ましくは0.8質量%以下である。
水溶性SiO2 の含有量が1質量%以上であると、高速での溶接作業性及び溶接金属の耐欠陥性が劣化する。よって、水溶性SiO2 含有量は1質量%未満(0質量%を含む)に規制する。水溶性SiO2 含有量は、高速での溶接作業性及び溶接金属の耐欠陥性の観点から、0.9質量%以下であることが好ましく、より好ましくは0.8質量%以下である。
この水溶性SiO2 は、主に水ガラスなどの結合剤に由来し、その量を低減するには、結合剤が非水溶性に変化する温度以上でフラックスを焼結することが有効である。具体的には、焼成温度を700℃以上とすることが、特に好ましい。水溶性SiO2 の含有量は、主に焼成温度を調整することで制御することができる。
フラックス中の水溶性SiO2 量は、以下の方法により測定することができる。先ず、フラックスを振動ミルにて粒径300μm以下に粉砕し、そこから測定用試料を約0.2g採取する(ステップ1)。次に、石英製三角フラスコに、前述した試料と蒸留水100mlとを入れ、煮沸下で4時間、可溶性成分を抽出した(ステップ2)。その後、抽出液を12時間以上放置した後、抽出液中の沈殿物及び浮遊物などを取り除き、吸光光度法にてSiを定量した(ステップ3)。
なお、ここでいう水溶性SiO2 は、前述した方法で分析して得たフラックスの全Si量を、SiO2 で換算した値であり、前述した全SiO2 とは区別して、その含有量を特定している。
[CaOの換算値:18質量%以下(0質量%を含まず)]
本実施形態のフラックスは、前述した成分に加えて、CaOを含有していてもよい。CaOは、スラグの塩基度を高めて溶接金属の清浄度を高めると共に、溶融スラグの流動性にも影響を与える成分であり、その存在量に比例して、前述した効果が発揮される。CaO含有量が18質量%以下であれば、溶融スラグの流動性が小さくなり、ビードの外観及び形状がより向上する。よって、CaOを添加する場合は18質量%以下(0質量%を含まず)とすることが好ましい。CaO含有量は、ビード外観及び形状の観点から、16質量%以下であることがより好ましく、更に好ましくは14質量%以下である。またCaOの下限値は、特に限定されるものではないが、溶接金属の清浄度向上の観点から、0.1質量%以上であることが好ましい。
本実施形態のフラックスは、前述した成分に加えて、CaOを含有していてもよい。CaOは、スラグの塩基度を高めて溶接金属の清浄度を高めると共に、溶融スラグの流動性にも影響を与える成分であり、その存在量に比例して、前述した効果が発揮される。CaO含有量が18質量%以下であれば、溶融スラグの流動性が小さくなり、ビードの外観及び形状がより向上する。よって、CaOを添加する場合は18質量%以下(0質量%を含まず)とすることが好ましい。CaO含有量は、ビード外観及び形状の観点から、16質量%以下であることがより好ましく、更に好ましくは14質量%以下である。またCaOの下限値は、特に限定されるものではないが、溶接金属の清浄度向上の観点から、0.1質量%以上であることが好ましい。
なお、本実施形態のフラックスには、Ca成分としてCaO以外に、前述したCaF2が含まれる。このため、ここでいうCaO含有量は、JIS Z 3352:2010に規定される方法で分析して得た全Ca量及び全F量から求められる換算値である。従って、CaF2 量が多量の場合は、JIS Z 3352:2010に準拠すると、CaOが0となる場合も存在する。
[TiO2 :6質量%以下(0質量%を含まず)]
本実施形態のフラックスは、前述した成分に加えて、TiO2 を含有していてもよい。TiO2 は、スラグ剥離性向上に有効な成分であり、ビード形状を良好に整える効果もある。また、TiO2 の一部は、溶接時の還元反応によりTiとなり、このTiは溶接金属中に添加されて、靭性向上に寄与する。
前述した作用は、その存在量(TiO2 含有量)に比例する。TiO2 含有量が6質量%以下であれば、ビード形状がより向上する。よって、TiO2 を添加する場合は、6質量%以下(0質量%を含まず)とすることが好ましい。TiO2 含有量は、ビード形状の観点から、5質量%以下であることがより好ましく、更に好ましくは4質量%以下である。またTiO2 含有量の下限値は、特に限定されるものではないが、スラグ剥離性及びビード形状の観点から、0.1質量%以上であることが好ましい。
本実施形態のフラックスは、前述した成分に加えて、TiO2 を含有していてもよい。TiO2 は、スラグ剥離性向上に有効な成分であり、ビード形状を良好に整える効果もある。また、TiO2 の一部は、溶接時の還元反応によりTiとなり、このTiは溶接金属中に添加されて、靭性向上に寄与する。
前述した作用は、その存在量(TiO2 含有量)に比例する。TiO2 含有量が6質量%以下であれば、ビード形状がより向上する。よって、TiO2 を添加する場合は、6質量%以下(0質量%を含まず)とすることが好ましい。TiO2 含有量は、ビード形状の観点から、5質量%以下であることがより好ましく、更に好ましくは4質量%以下である。またTiO2 含有量の下限値は、特に限定されるものではないが、スラグ剥離性及びビード形状の観点から、0.1質量%以上であることが好ましい。
なお、ここでいうTiO2 含有量は、JIS Z 3352:2010に規定される方法(例えばJIS M 8219-1:2012など)で分析して得たフラックスの全Ti量を、TiO2 で換算した値である。
また、フラックスは、下記数式(I)を満たすことが好ましい。下記数式(I)において、[Al2 O3 ]はAl2 O3 含有量(質量%)、[TiO2 ]はTiO2 含有量(質量%)、[ZrO2 ]はZrO2 含有量(質量%)である。
Al2 O3 、TiO2 及びZrO2 は、それぞれ個別にその含有量を規定しているが、本実施形態のフラックスでは、更に、Al2 O3 含有量、TiO2 含有量及びZrO2 含有量の合計量に占めるZrO2 含有量(=[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ]))も規定することが好ましい。
本発明者は、ZrO2 を添加したフラックスの高速での溶接作業性について種々実験研究した結果、Al2 O3 含有量、TiO2 含有量及びZrO2 含有量の合計量に占めるZrO2 含有量(=[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ]))が、高速での溶接作業性について影響を及ぼすことを見出した。
[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ])が0.01以上であれば、ZrO2 を添加した効果が十分に得られやすくなる。一方、[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ])がが0.38以下であれば、スラグ凝固温度が高くなりすぎず、ビード外観及びスラグ剥離性が向上しやすくなる。よって、[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ])が0.01~0.38となるように、各成分の添加量を調整することが好ましい。
[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ])は、ZrO2 の添加の効果をより向上させる観点から、0.02以上とすることがより好ましく、更に好ましくは0.03以上である。また、ビード外観及びスラグ剥離性の観点から、0.33以下であることがより好ましく、更に好ましくは0.28以下である。
なお、フラックスにTiO2 を含まない場合は、前記と同様の理由により、「[ZrO2 ]/([Al2 O3 ]+[ZrO2 ]):0.01~0.38」であることが好ましい。なお、この数式は、実験的に導き出したものである。
[B2 O3 :3質量%以下(0質量%を含まず)]
本実施形態のフラックスは、前述した成分に加えて、酸化硼素、硼砂などを原料とするB2 O3 を含有していてもよい。B2 O3 は靱性向上に有効な成分である。B2 O3 が3質量%以下であれば、溶接金属が硬化しにくく、靱性がより向上する。よって、B2 O3を添加する場合は、3質量%以下(0質量%を含まず)とすることが好ましい。B2 O3 含有量は、靱性の観点から、2質量%以下であることがより好ましく、更に好ましくは1質量%以下である。またB2 O3 含有量の下限値は、特に限定されるものではないが、靱性向上の効果を得る観点から、0.01質量%以上であることが好ましい。
本実施形態のフラックスは、前述した成分に加えて、酸化硼素、硼砂などを原料とするB2 O3 を含有していてもよい。B2 O3 は靱性向上に有効な成分である。B2 O3 が3質量%以下であれば、溶接金属が硬化しにくく、靱性がより向上する。よって、B2 O3を添加する場合は、3質量%以下(0質量%を含まず)とすることが好ましい。B2 O3 含有量は、靱性の観点から、2質量%以下であることがより好ましく、更に好ましくは1質量%以下である。またB2 O3 含有量の下限値は、特に限定されるものではないが、靱性向上の効果を得る観点から、0.01質量%以上であることが好ましい。
[その他の成分]
本実施形態のフラックスにおける上記以外の成分は、Ba、Li、P及びSなどの不可避的不純物である。これらの不可避的不純物のうち、Ba及びLiなどはそれぞれ1.0質量%以下に規制することが好ましく、特に溶接品質に影響するP及びSはそれぞれ0.05質量%以下に規制することが好ましい。また、Ba、Li、P及びSなどは、合計で3質量%以下であることが好ましい。
本実施形態のフラックスにおける上記以外の成分は、Ba、Li、P及びSなどの不可避的不純物である。これらの不可避的不純物のうち、Ba及びLiなどはそれぞれ1.0質量%以下に規制することが好ましく、特に溶接品質に影響するP及びSはそれぞれ0.05質量%以下に規制することが好ましい。また、Ba、Li、P及びSなどは、合計で3質量%以下であることが好ましい。
[フラックス粒度分布]
本発明者は、高温焼結フラックスの高速での溶接作業性について種々実験研究した結果、0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすようにすることで、アンダーカットの発生率が大幅に減少することを見出し、溶接作業環境がより良好となることを確認した。高速溶接時に発生するアンダーカットをより低減し、溶接作業環境をより良好とするためには、0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすこととする。なお、0.3mm以下の粒度及び0.2mm以下の粒度は0質量%であってもよい。
本発明者は、高温焼結フラックスの高速での溶接作業性について種々実験研究した結果、0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすようにすることで、アンダーカットの発生率が大幅に減少することを見出し、溶接作業環境がより良好となることを確認した。高速溶接時に発生するアンダーカットをより低減し、溶接作業環境をより良好とするためには、0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすこととする。なお、0.3mm以下の粒度及び0.2mm以下の粒度は0質量%であってもよい。
[高温焼成型フラックス]
本実施形態フラックスの成分組成は、高温焼成型フラックスとして好適である。すなわち、600~1200℃で焼成することが好ましい。
この温度で焼成することで、水溶性SiO2 の含有量を1質量%未満に制御することができる。
本実施形態フラックスの成分組成は、高温焼成型フラックスとして好適である。すなわち、600~1200℃で焼成することが好ましい。
この温度で焼成することで、水溶性SiO2 の含有量を1質量%未満に制御することができる。
[製造方法]
本実施形態のフラックスを製造する場合は、例えば、前述した組成となるように原料粉を配合し、結合剤と共に混練した後、造粒し、焼成する。その際、結合剤(バインダ)としては、例えば、ポリビニルアルコール又は水ガラスを使用することができる。また、造粒法は、特に限定されるものではないが、転動式造粒機又は押し出し式造粒機などを用いる方法が好ましい。
本実施形態のフラックスを製造する場合は、例えば、前述した組成となるように原料粉を配合し、結合剤と共に混練した後、造粒し、焼成する。その際、結合剤(バインダ)としては、例えば、ポリビニルアルコール又は水ガラスを使用することができる。また、造粒法は、特に限定されるものではないが、転動式造粒機又は押し出し式造粒機などを用いる方法が好ましい。
更に、造粒されたフラックスは、ダスト除去及び粗大粒の解砕などの整粒処理を行い、粒子径を2.5mm以下とすることが好ましい。一方、造粒後の焼成は、ロータリーキルン、定置式バッチ炉及びベルト式焼成炉などで行うことができる。その際の焼成温度は、例えば600~1200℃とすることができるが、前述したように結合剤を非水溶性に変化させる観点から、700℃以上とすることが好ましい。
以上詳述したように、本実施形態のフラックスは、各成分の含有量を特定の範囲にしているため、高速溶接時に良好な溶接作業性及び溶接金属の耐欠陥性を得ることが可能となる。
なお、耐欠陥性は、溶接金属内部に存在する欠陥(スラグ巻込み、融合不良、ブローホールなど)及び溶接金属表面に存在する欠陥(アンダーカット、ポックマーク、ピットなど)があり、本願では、溶融スラグの流動性及びフラックスの粒度を制御しているため、特に溶接金属表面に存在するアンダーカット及びポックマークへの耐欠陥性に効果が高い。
なお、耐欠陥性は、溶接金属内部に存在する欠陥(スラグ巻込み、融合不良、ブローホールなど)及び溶接金属表面に存在する欠陥(アンダーカット、ポックマーク、ピットなど)があり、本願では、溶融スラグの流動性及びフラックスの粒度を制御しているため、特に溶接金属表面に存在するアンダーカット及びポックマークへの耐欠陥性に効果が高い。
また、本実施形態のフラックスの成分組成は、高温焼成型フラックスとして好適であるが、溶融型フラックスとして適用しても、高温焼成型フラックスと同様の効果を得ることができる。
以下、本発明の実施例及び比較例を挙げて、本発明の効果について具体的に説明する。本実施例においては、下記表1に示す鋼板及び表2に示すワイヤを使用し、図1に示す開先形状及び図2に示す電極配置で、下記表3に示す溶接条件により、サブマージアーク溶接での溶接試験を実施した。そして、下記表4に示す実施例のフラックス及び下記表5に示す比較例のフラックスについて、その性能を評価した。なお、本実施例では、下記表4及び表5に示す組成となるように原料を配合し、結合剤(水ガラス)と共に混練した後、造粒し、更にロータリーキルンを用いて下記表4及び表5に示す温度で焼成し、整粒することによりフラックスを得た。なお、表4及び5において、本発明の範囲を満たさないもの、及び好ましい範囲を満たさないものは数値に下線を引いて示す。また、参照する図面については、説明を明確にするため、各部材のスケール、間隔又は位置関係などが誇張、あるいは、部材の一部の図示が省略されている場合がある。
なお、上記表1に示す鋼板組成及び上記表2に示すワイヤ組成の残部は、Fe及び不可避的不純物である。また、上記表4及び表5に示す「式I」は[ZrO2 ]/([Al2 O3 ]+[TiO2 ]+[ZrO2 ]の値である。
実施例及び比較例の各フラックスの評価は、アーク安定性、スラグ剥離性、ビード外観、ビード形状、アンダーカット発生率及びポックマーク発生率について行った。
<アーク安定性>
アーク安定性は、溶接時の電流及び電圧の振れにより評価した。具体的には、溶接電流が±50Aかつアーク電圧が±2Vであったものを◎、溶接電流が±100Aかつアーク電圧が±2Vであったものを○、溶接電流が±100Aかつアーク電圧が±4Vであったものを△、溶接困難であったものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
アーク安定性は、溶接時の電流及び電圧の振れにより評価した。具体的には、溶接電流が±50Aかつアーク電圧が±2Vであったものを◎、溶接電流が±100Aかつアーク電圧が±2Vであったものを○、溶接電流が±100Aかつアーク電圧が±4Vであったものを△、溶接困難であったものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
<スラグ剥離性>
スラグ剥離性は、スラグ除去の容易さ及び焼き付きの有無により評価した。具体的には、スラグが、自然剥離し、焼き付きがなかったものを◎、自然剥離するが、単位溶接長(1m)あたり3箇所以下で焼き付きが発生したものを○、自然剥離せず、単位溶接長(1m)あたり4~9箇所で焼き付きが発生したものを△、自然剥離せず、単位溶接長(1m)あたり10箇所以上で焼き付きが発生したものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
スラグ剥離性は、スラグ除去の容易さ及び焼き付きの有無により評価した。具体的には、スラグが、自然剥離し、焼き付きがなかったものを◎、自然剥離するが、単位溶接長(1m)あたり3箇所以下で焼き付きが発生したものを○、自然剥離せず、単位溶接長(1m)あたり4~9箇所で焼き付きが発生したものを△、自然剥離せず、単位溶接長(1m)あたり10箇所以上で焼き付きが発生したものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
<ビード外観>
ビード外観は、主にビードの波目及び光沢に関する評価であり、溶接部を目視観察することにより行った。その結果、ビードの波目に乱れがなくビードに金属光沢があるものを◎、単位溶接長(1m)あたりにビード波目の乱れが1箇所でビードに金属光沢があるものを○、単位溶接長(1m)あたりにビード波目の乱れが2~4箇所でビードに金属光沢がないものを△、単位溶接長(1m)あたりにビード波目の乱れが5箇所以上ありビードに金属光沢がないものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
ビード外観は、主にビードの波目及び光沢に関する評価であり、溶接部を目視観察することにより行った。その結果、ビードの波目に乱れがなくビードに金属光沢があるものを◎、単位溶接長(1m)あたりにビード波目の乱れが1箇所でビードに金属光沢があるものを○、単位溶接長(1m)あたりにビード波目の乱れが2~4箇所でビードに金属光沢がないものを△、単位溶接長(1m)あたりにビード波目の乱れが5箇所以上ありビードに金属光沢がないものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
<ビード形状>
ビード形状は、主にビードの凹凸及び母材へのなじみに関する評価であり、溶接部を目視観察することにより行った。その結果、ビード形状が、非常に良好であったものを◎、良好であったものを○、やや不良であったものを△、不良であったものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
ビード形状は、主にビードの凹凸及び母材へのなじみに関する評価であり、溶接部を目視観察することにより行った。その結果、ビード形状が、非常に良好であったものを◎、良好であったものを○、やや不良であったものを△、不良であったものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
<アンダーカット発生率>
アンダーカットは、発生がなかったものを◎、単位溶接長(1m)あたりの発生比率が0.5%以下であったものを○、単位溶接長(1m)あたりの発生比率が0.5%を超え1.0%以下であったものを△、単位溶接長(1m)あたりの発生比率が1.0%を超えていたものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
アンダーカットは、発生がなかったものを◎、単位溶接長(1m)あたりの発生比率が0.5%以下であったものを○、単位溶接長(1m)あたりの発生比率が0.5%を超え1.0%以下であったものを△、単位溶接長(1m)あたりの発生比率が1.0%を超えていたものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
<ポックマーク発生率>
ポックマークは、発生がなかったものを◎、単位溶接長(1m)あたりの発生比率が0.5%以下であったものを○、単位溶接長(1m)あたりの発生比率が0.5%を超え1.0%以下であったものを△、単位溶接長(1m)あたりの発生比率が1.0%を超えていたものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
ポックマークは、発生がなかったものを◎、単位溶接長(1m)あたりの発生比率が0.5%以下であったものを○、単位溶接長(1m)あたりの発生比率が0.5%を超え1.0%以下であったものを△、単位溶接長(1m)あたりの発生比率が1.0%を超えていたものを×とした。そして、本実施例では、評価が◎又は○であったものを合格とした。
なお、アンダーカット及びポックマークの検出は、目視により行った。アンダーカット及びポックマークの評価における単位溶接長(1m)あたりの発生比率とは、個々のアンダーカット及びポックマークなどの長さを目視で測定し、アンダーカット及びポックマークの総長さを算出した後、試験部の有効長さで割り返し、単位溶接長あたりに換算したものである。
以上の評価結果を、下記表6及び表7にまとめて示す。
表6に示す実施例No.F1~F17のフラックスは、本発明の範囲を満足するものであるため、全ての評価項目において優れていた。
ただし、実施例No.F13のフラックスは、CaO含有量が18質量%を超えているため、ビード外観及びビード形状の評価が「◎」とならず「○」であった。
実施例No.F14のフラックスは、TiO2 含有量が6質量%を超えているため、ビード形状の評価が「◎」とならず「○」であった。
実施例No.F15のフラックスは、B2 O3 含有量が3質量%を超えるものであり、B2 O3 含有量が3質量%以下のフラックスと比較して溶接金属の靭性が劣化するものと考えられる。
実施例No.F16のフラックスは、粒度分布が好ましい範囲を満たさないため、アンダーカット発生率の評価が「◎」とならず「○」であった。
実施例No.F17のフラックスは、粒度分布の0.3mm以下が好ましい範囲を満たさなかったものの、0.2mm以下が好ましい範囲を満足するものであるため、全ての評価項目において優れていた。
ただし、実施例No.F13のフラックスは、CaO含有量が18質量%を超えているため、ビード外観及びビード形状の評価が「◎」とならず「○」であった。
実施例No.F14のフラックスは、TiO2 含有量が6質量%を超えているため、ビード形状の評価が「◎」とならず「○」であった。
実施例No.F15のフラックスは、B2 O3 含有量が3質量%を超えるものであり、B2 O3 含有量が3質量%以下のフラックスと比較して溶接金属の靭性が劣化するものと考えられる。
実施例No.F16のフラックスは、粒度分布が好ましい範囲を満たさないため、アンダーカット発生率の評価が「◎」とならず「○」であった。
実施例No.F17のフラックスは、粒度分布の0.3mm以下が好ましい範囲を満たさなかったものの、0.2mm以下が好ましい範囲を満足するものであるため、全ての評価項目において優れていた。
一方、表7に示す比較例No.F18~F34のフラックスは、本発明の範囲を満足しないものであるため、以下の結果となった。
比較例No.F18のフラックスは、F含有量(CaF2 換算値)が下限値未満であるため、ポックマークが発生した。
比較例No.F19のフラックスは、F含有量(CaF2 換算値)が上限値を超えているため、ビード形状が劣っていた。
比較例No.F20のフラックスは、MgO含有量が下限値未満であるため、スラグ剥離性が劣っていた。
比較例No.F21のフラックスは、MgO含有量が上限値を超えているため、ビード形状が劣り、アンダーカットが発生した。
比較例No.F19のフラックスは、F含有量(CaF2 換算値)が上限値を超えているため、ビード形状が劣っていた。
比較例No.F20のフラックスは、MgO含有量が下限値未満であるため、スラグ剥離性が劣っていた。
比較例No.F21のフラックスは、MgO含有量が上限値を超えているため、ビード形状が劣り、アンダーカットが発生した。
比較例No.F22のフラックスは、Na含有量(Na2 O換算値)とK含有量(K2 O換算値)との合計量が下限値未満のため、アーク安定性、ビード外観及びビード形状が劣っていた。
比較例No.F23のフラックスは、Na含有量(Na2 O換算値)とK含有量(K2 O換算値)との合計量が上限値を超えているため、アーク安定性、ビード外観及びビード形状が劣っていた。
比較例No.F24のフラックスは、Mn含有量(MnO換算値)が下限値未満のため、ポックマークが発生した。
比較例No.F25のフラックスは、Mn含有量(MnO換算値)が上限値を超えているため、スラグ剥離性が劣っていた。
比較例No.F23のフラックスは、Na含有量(Na2 O換算値)とK含有量(K2 O換算値)との合計量が上限値を超えているため、アーク安定性、ビード外観及びビード形状が劣っていた。
比較例No.F24のフラックスは、Mn含有量(MnO換算値)が下限値未満のため、ポックマークが発生した。
比較例No.F25のフラックスは、Mn含有量(MnO換算値)が上限値を超えているため、スラグ剥離性が劣っていた。
比較例No.F26のフラックスは、Fe含有量(FeO換算値)が下限値未満のため、ポックマークが発生した。
比較例No.F27のフラックスは、Fe含有量(FeO換算値)が上限値を超えているため、スラグ剥離性、ビード外観及びビード形状が劣っていた。
比較例No.F28のフラックスは、SiO2 含有量が下限値未満であるため、ビード外観及びビード形状が劣っていた。
比較例No.F29のフラックスは、SiO2 含有量が上限値を超えているため、スラグ剥離性が劣っていた。
比較例No.F27のフラックスは、Fe含有量(FeO換算値)が上限値を超えているため、スラグ剥離性、ビード外観及びビード形状が劣っていた。
比較例No.F28のフラックスは、SiO2 含有量が下限値未満であるため、ビード外観及びビード形状が劣っていた。
比較例No.F29のフラックスは、SiO2 含有量が上限値を超えているため、スラグ剥離性が劣っていた。
比較例No.F30のフラックスは、Al2 O3 含有量が下限値未満であるため、ビード形状が劣っていた。
比較例No.F31のフラックスは、Al2 O3 含有量が上限値を超えているため、ビード形状が劣っていた。
比較例No.F32のフラックスは、ZrO2 含有量が下限値未満であるため、アーク安定性、スラグ剥離性、ビード外観及びビード形状が劣っていた。
比較例No.F33のフラックスは、ZrO2 含有量が上限値を超えているため、ビード形状が劣っていた。
比較例No.F31のフラックスは、Al2 O3 含有量が上限値を超えているため、ビード形状が劣っていた。
比較例No.F32のフラックスは、ZrO2 含有量が下限値未満であるため、アーク安定性、スラグ剥離性、ビード外観及びビード形状が劣っていた。
比較例No.F33のフラックスは、ZrO2 含有量が上限値を超えているため、ビード形状が劣っていた。
比較例No.F34のフラックスは、水溶性SiO2 含有量が上限値を超えているため、スラグ剥離性、ビード外観及びビード形状が劣り、アンダーカットが発生した。
以上の結果から、本発明のフラックスを用いることにより、高速での溶接作業性及び溶接金属の耐欠陥性を良好にすることが可能であることが確認された。
本発明は、以下の態様を含む。
態様1:
FのCaF2 換算値:2~22質量%、
MgO:8~28質量%、
NaのNa2 O換算値及びKのK2 O換算値のうち少なくとも一つ以上の合計:0.5~6.5質量%、
MnのMnO換算値:2~22質量%、
FeのFeO換算値:0.5~6.5質量%、
SiO2 :12~32質量%、
Al2 O3 :16~36質量%、
ZrO2 :0.4~10質量%、
水溶性SiO2 :1質量%未満を含有することを特徴とするサブマージアーク溶接用フラックス。
態様2:
更に、CaOの換算値:18質量%以下を含有することを特徴とする態様1に記載のサブマージアーク溶接用フラックス。
態様3:
更に、TiO2 :6質量%以下を含有することを特徴とする態様1又は2に記載のサブマージアーク溶接用フラックス。
態様4:
前記Al2 O3 含有量を[Al2 O3 ]、前記TiO2 含有量を[TiO2 ]、前記ZrO2 含有量を[ZrO2 ]としたとき、下記数式(I)を満たすことを特徴とする態様3に記載のサブマージアーク溶接用フラックス。
態様5:
更に、B2 O3 :3質量%以下を含有することを特徴とする態様1~4のいずれかに記載のサブマージアーク溶接用フラックス。
態様6:
高温焼成型フラックスであることを特徴とする態様1~5のいずれかに記載のサブマージアーク溶接用フラックス。
態様7:
0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすことを特徴とする態様1~6のいずれかに記載のサブマージアーク溶接用フラックス。
態様1:
FのCaF2 換算値:2~22質量%、
MgO:8~28質量%、
NaのNa2 O換算値及びKのK2 O換算値のうち少なくとも一つ以上の合計:0.5~6.5質量%、
MnのMnO換算値:2~22質量%、
FeのFeO換算値:0.5~6.5質量%、
SiO2 :12~32質量%、
Al2 O3 :16~36質量%、
ZrO2 :0.4~10質量%、
水溶性SiO2 :1質量%未満を含有することを特徴とするサブマージアーク溶接用フラックス。
態様2:
更に、CaOの換算値:18質量%以下を含有することを特徴とする態様1に記載のサブマージアーク溶接用フラックス。
態様3:
更に、TiO2 :6質量%以下を含有することを特徴とする態様1又は2に記載のサブマージアーク溶接用フラックス。
態様4:
前記Al2 O3 含有量を[Al2 O3 ]、前記TiO2 含有量を[TiO2 ]、前記ZrO2 含有量を[ZrO2 ]としたとき、下記数式(I)を満たすことを特徴とする態様3に記載のサブマージアーク溶接用フラックス。
更に、B2 O3 :3質量%以下を含有することを特徴とする態様1~4のいずれかに記載のサブマージアーク溶接用フラックス。
態様6:
高温焼成型フラックスであることを特徴とする態様1~5のいずれかに記載のサブマージアーク溶接用フラックス。
態様7:
0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすことを特徴とする態様1~6のいずれかに記載のサブマージアーク溶接用フラックス。
本出願は、出願日が2015年2月2日である日本国特許出願、特願第2015-018805号を基礎出願とする優先権主張を伴う。特願第2015-018805号は参照することにより本明細書に取り込まれる。
Claims (7)
- FのCaF2 換算値:2~22質量%、
MgO:8~28質量%、
NaのNa2 O換算値及びKのK2 O換算値のうち少なくとも一つ以上の合計:0.5~6.5質量%、
MnのMnO換算値:2~22質量%、
FeのFeO換算値:0.5~6.5質量%、
SiO2 :12~32質量%、
Al2 O3 :16~36質量%、
ZrO2 :0.4~10質量%、
水溶性SiO2 :1質量%未満(0質量%を含む)を含有することを特徴とするサブマージアーク溶接用フラックス。 - 更に、CaOの換算値:18質量%以下(0質量%を含まず)を含有することを特徴とする請求項1に記載のサブマージアーク溶接用フラックス。
- 更に、TiO2 :6質量%以下(0質量%を含まず)を含有することを特徴とする請求項1に記載のサブマージアーク溶接用フラックス。
- 更に、B2 O3 :3質量%以下(0質量%を含まず)を含有することを特徴とする請求項1~4のいずれか1項に記載のサブマージアーク溶接用フラックス。
- 高温焼成型フラックスであることを特徴とする請求項1~4のいずれか1項に記載のサブマージアーク溶接用フラックス。
- 0.3mm以下の粒度が10質量%以下、及び、0.2mm以下の粒度が3質量%以下のいずれか一方又は両方を満たすことを特徴とする請求項1~4のいずれか1項に記載のサブマージアーク溶接用フラックス。