WO2016018131A1 - 경화 가능한 석유수지 및 이의 제조방법 - Google Patents
경화 가능한 석유수지 및 이의 제조방법 Download PDFInfo
- Publication number
- WO2016018131A1 WO2016018131A1 PCT/KR2015/008086 KR2015008086W WO2016018131A1 WO 2016018131 A1 WO2016018131 A1 WO 2016018131A1 KR 2015008086 W KR2015008086 W KR 2015008086W WO 2016018131 A1 WO2016018131 A1 WO 2016018131A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- petroleum resin
- group
- silanes
- weight
- curable petroleum
- Prior art date
Abstract
Description
물성 | 실시예 1 | 참조예1 | 참조예2 | 대조구 (HIKOREZ A-1100 자체) | |
연화점(℃) | 97.5 | 108.2 | 100 | 100 | |
Si-O peak intensity(FT-IR) | 있음(흡광도 0.1731) | 있음(흡광도 0.0339) | 있음 | 없음 | |
H-NMR 실란류 프로톤 함량(%) | 7.6 | 1.45 | 1.1 | 0 | |
Si 중량분율(wt%) | 2.21 | - | - | 0 | |
분자량 | Mn | 364 | 310 | 1200 | 1227 |
Mw | 806 | 689 | 2146 | 2181 | |
Mz | 7858 | 6419 | 4398 | 4455 | |
PDI | 2.21 | 2.22 | 1.79 | 1.78 |
물성 | 실시예 2 | 실시예 1 | 실시예 3 | 실시예 4 | 실시예 5 | |
TMVS 함량(DCPD와의 총량에 대한 중량%) | 25 | 20 | 16 | 10 | 5 | |
수율(%) | 25.8 | 27.8 | 28.8 | 30.3 | 33.0 | |
연화점(℃) | 92.5 | 97.5 | 107.0 | 115.5 | 122.0 | |
H-NMR 실란류 프로톤 함량(%) | 9.9 | 7.6 | 6.0 | 3.5 | 1.7 | |
Si 중량분율(wt%) | - | 2.21 | - | 0.82 | - | |
Si-O peak intensity(FT-IR) | 0.2137 | 0.1731 | 0.1444 | 0.0895 | 0.0461 | |
분자량 | Mn | 374 | 364 | 365 | 352 | 354 |
Mw | 801 | 806 | 799 | 822 | 821 | |
Mz | 7509 | 7858 | 7345 | 7846 | 7428 | |
PDI | 2.13 | 2.21 | 2.19 | 2.33 | 2.32 |
물성 | 실시예 1 | 실시예 6 | 실시예 7 | |
열중합 반응시간(hr) | 1 | 2 | 3 | |
수율(%) | 27.8 | 33.9 | 39.3 | |
연화점(℃) | 97.5 | 118.8 | SP 측정안됨 | |
H-NMR 실란류 프로톤 함량(%) | 7.6 | 8.2 | 8.4 | |
Si 중량분율(wt%) | 2.21 | - | - | |
Si-O peak intensity(FT-IR) | 0.1731 | 0.1881 | 0.1957 | |
분자량 | Mn | 364 | 451 | 487 |
Mw | 806 | 947 | 1051 | |
Mz | 7858 | 5398 | 4383 | |
PDI | 2.21 | 2.1 | 2.16 |
Claims (17)
- (a) 나프타 크래킹의 C5-유분, C9-유분 및 디사이클로펜타디엔 중 선택된 적어도 하나 이상의 에틸렌성 불포화기를 갖는 환상의 올레핀류를 포함하는 단량체류, 및 (b) 다음 화학식 1로 표시되는 하나 이상의 실란류를 포함하는 중합용 조성물을 열중합하는 공정을 포함하는 경화가능한 석유수지의 제조방법.화학식 1CH2=CR-(COO)x(CnH2n)ySiR'3상기 식에서, R은 수소 원자 또는 메틸기이고; x 및 y는 0 또는 1이고, 단, x가 1일 때, y는 1이고; n은 1 내지 12의 정수이고, 각 R'은 독립적으로 1 내지 12 개의 탄소 원자를 갖는 알콕시기, 아릴옥시기, 아랄옥시기, 1 내지 12 개의 탄소 원자를 갖는 지방족 아실옥시기, 아미노 또는 치환 아미노기, 또는 1 내지 6 개의 탄소 원자를 갖는 저급 알킬기이고, 단, 3 개의 R' 기 중 2 개 이하가 알킬기이다.
- 제 1 항에 있어서, 실란류는 비닐트리메톡시실란, 비닐트리에톡시실란 및 3-(트리메톡시실릴)프로필 메타크릴레이트로 이루어진 군으로부터 선택된 것을 특징으로 하는, 방법.
- 제 1 항에 있어서, 열중합하는 공정은 가압 하에서 150 내지 300℃의 반응온도 범위로 1 내지 3시간 동안 수행되는 것을 특징으로 하는, 방법.
- 제 1 항에 있어서, 단량체류는 디사이클로펜타디엔을 포함하는 것을 특징으로 하는, 방법.
- 제 1 항에 있어서, 중합용 조성물은 에틸렌성 불포화 이중결합을 포함하지 않는 비중합성 용매를 포함하는 것을 특징으로 하는, 방법.
- 제 1 항에 있어서, 중합용 조성물은 실란류를 단량체류와의 총 중량에 대하여 5 내지 50중량%로 포함하는 것을 특징으로 하는, 방법.
- 제 5 항에 있어서, 중합용 조성물은 비중합성 용매를 단량체류와 실란류와의 총 농도가 30 내지 70중량% 되는 양으로 포함하는 것을 특징으로 하는, 방법.
- 제 1 항에 있어서, 열중합하는 공정 이후로 탈기 및 농축공정을 포함하는 것을 특징으로 하는, 방법.
- 나프타 크래킹의 C5-유분, C9-유분 및 디사이클로펜타디엔 중 선택된 적어도 하나 이상의 에틸렌성 불포화기를 갖는 환상의 올레핀류를 포함하는 단량체류 유래의 반복단위를 포함하며,실란류가 공중합되고,1H-NMR에 의해 결정되는 실란류의 프로톤 함량이 적어도 1.7%인,경화가능한 석유수지.
- 제 9 항에 있어서, 실란류의 프로톤 함량이 적어도 7%인 것을 특징으로 하는, 경화가능한 석유수지.
- 제 9 항에 있어서,X선 형광분석기에 의한 분석을 통해 얻어진 전체 원소 중 실리콘(Si) 원소가 차지하는 중량비율인 Si 중량분율이 적어도 0.3wt%인 것을 특징으로 하는, 경화가능한 석유 수지.
- 제 11 항에 있어서,Si 중량분율이 적어도 2wt%인 것을 특징으로 하는, 경화가능한 석유 수지.
- 제 9 항에 있어서, 실란류는 다음 화학식 1로 표시되는 것 중 선택된 적어도 하나인 것을 특징으로 하는, 경화가능한 석유수지.화학식 1CH2=CR-(COO)x(CnH2n)ySiR'3상기 식에서, R은 수소 원자 또는 메틸기이고; x 및 y는 0 또는 1이고, 단, x가 1일 때, y는 1이고; n은 1 내지 12의 정수이고, 각 R'은 독립적으로 1 내지 12 개의 탄소 원자를 갖는 알콕시기, 아릴옥시기, 아랄옥시기, 1 내지 12 개의 탄소 원자를 갖는 지방족 아실옥시기, 아미노 또는 치환 아미노기, 또는 1 내지 6 개의 탄소 원자를 갖는 저급 알킬기이고, 단, 3 개의 R' 기 중 2 개 이하가 알킬기이다.
- 제 13 항에 있어서, 실란류는 비닐트리메톡시실란, 비닐트리에톡시실란 및 3-(트리메톡시실릴)프로필 메타크릴레이트로 이루어진 군으로부터 선택된 것임을 특징으로 하는, 경화가능한 석유수지.
- 제 9 항에 있어서, 단량체류는 디사이클로펜타디엔을 포함하는 것을 특징으로 하는, 경화가능한 석유수지.
- 제 15 항에 있어서, 중량평균 분자량(Mw)이 500 내지 2000인 것을 특징으로 하는, 경화가능한 석유수지.
- 제 15 항에 있어서, 연화점이 70 내지 150℃ 범위에 있는 것을 특징으로 하는, 경화가능한 석유수지.