WO2015141588A1 - 中空構造体及び車両用部品 - Google Patents
中空構造体及び車両用部品 Download PDFInfo
- Publication number
- WO2015141588A1 WO2015141588A1 PCT/JP2015/057517 JP2015057517W WO2015141588A1 WO 2015141588 A1 WO2015141588 A1 WO 2015141588A1 JP 2015057517 W JP2015057517 W JP 2015057517W WO 2015141588 A1 WO2015141588 A1 WO 2015141588A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fiber
- molded body
- hollow structure
- resin material
- reinforced resin
- Prior art date
Abstract
Description
(σc/σt)×(Hc/Ht)<(Sc/St)<(σt/σc)×(Hc/Ht)
(1)
ここで、上記式(1)における各記号は次の通りである。
Hc=第1成形体の高さ
Ht=第2成形体の高さ
σc=第1繊維強化樹脂材料の上記軸方向における圧縮強度
σt=第2繊維強化樹脂材料の上記軸方向における引張強度
Ac=第1成形体の上記断面における断面積
At=第2成形体の上記断面における断面積
Sc=σc×Ac、第1成形体の構造の圧縮強度
St=σt×At、第2成形体の構造の圧縮強度
(σc/σt)<(Tc×σc)/(Tt×σt)<(σt/σc) (2)
ここで、上記式(2)における各記号は以下の通りである。
Tc=第1成形体の上記断面における平均厚み
Tt=第2成形体の上記断面における平均厚み
さらに、本発明の中空構造体においては、上記第1繊維強化樹脂材料における上記第1強化繊維の体積含有率Vfcと上記第2繊維強化樹脂材料における上記第2強化繊維の体積含有率VftとがVfc>Vftを満たすことが好ましく、上記第1強化繊維の平均繊維長Lcと上記第2強化繊維の平均繊維長LtとがLc>Ltを満たすことが好ましく、また上記第1強化繊維の平均繊維径Dcと上記第2強化繊維の平均繊維径DtとがDc<Dtを満たすことが好ましい。
また本発明は、上記本発明に係る中空構造体が用いられたことを特徴とする車両用部品を提供する。
まず、本発明の中空構造体について説明する。上述した通り本発明の中空構造体は、第1強化繊維と第1マトリックス樹脂とを含有する第1繊維強化樹脂材料からなる第1成形体と、第2強化繊維と第2マトリックス樹脂とを含有する第2繊維強化樹脂材料からなる第2成形体とが組み合わされて中空構造を有するものであり、上記中空構造の軸方向に対して垂直方向の任意の断面において、上記第1成形体の構造の圧縮強度Sc及び上記第2成形体の構造の引張強度Stとの比Sc/Stが上記式(1)を満たすことを特徴とするものである。
また、図1に例示するように、本発明の中空構造体10の上記中空構造の軸方向Xに垂直方向の断面は、第1成形体11及び第2成形体12が組み合わされることによって閉断面とされているところ、本発明の中空構造体10は、当該断面において、第1成形体11の構造の圧縮強度Sc及び上記第2成形体12の構造の引張強度Stとの比Sc/Stが上記式(1)を満たすことを特徴とするものである。
なお、上記図1中、Yは、第1成形体11及び第2成形体12の境界面を示すものである。また、同図中のTc、Ttはそれぞれ第1成形体11、及び第2成形体12の厚みを示し、Hc、Htはそれぞれ第1成形体11、及び第2成形体12の高さを示す。
なお、図1は本発明の中空構造体の一例として、上記中空構造の軸方向において断面形状が一様である例を示したが、勿論、本発明の中空構造体はこのような例に限定されるものではなく、中空構造の軸方向において断面形状が変化している態様も含まれるものである。そして、このように中空構造の軸方向において断面形状が変化している態様の場合、上記比Sc/Stは、全て断面において上記式(1)を満たすことを必要とするものではなく、任意の一つの断面において上記式(1)を満たせばよいものである。
また、本発明の中空構造体は、上記式(1)を満たすことにより、所望の強度を達成するために繊維強化樹脂材料を過剰に使用することを抑制し、最小限の繊維強化樹脂材料の使用量で中空構造体全体としての所望の強度を達成することができる。
このようなことから、本発明の中空構造体は、所定の強度を最小限の繊維強化樹脂材料の使用量で達成することにより、強度と軽量化とを両立できるという効果を奏することができる。
上述した通り、本発明の中空構造体は上記式(1)を満たすことにより、上記第1成形体側から本発明の中空構造体に外力が加わった際に、上記第1成形体が先に破壊することを抑制できるものである。したがって、本発明の中空構造体は、第1成形体側から圧縮応力が負荷される用途に用いられることにより、優れた強度を示すものである。
(Sc/St)=k(Hc/Ht) (3)
この上記式(3)は以下の考え方に基づいて導出されたものである。すなわち、本発明の中空構造体を構成する第1成形体の構造の圧縮強度と第2成形体の構造の引張強度の比(Sc/St)が成形体の形状パラメータ(Hc/Ht)として、上記式(3)の関係を満足すれば、中空構造体を構成する第1繊維強化樹脂材料の圧縮強度と第2繊維強化樹脂材料の引張強度の両方を中空構造体の構造強度の発現に活用でき、このように設計・製造された繊維強化樹脂材料の中空構造体は所定強度を満足する上、最もよい軽量化効果を達成することができる。
ここで、上記式(3)における記号kは係数であり、理想としてはk=1である。また、kは下記式(4)に示す範囲内であることにより軽量化効果が得られるものである。
(σc/σt)<k<(σt/σc) (4)
このようなことから、上記式(1)は、上記式(4)を上記式(3)に代入することによって導出されたものである。
(Sc/St)=k((Hc+E)/(Ht-E)) (3’)
ここで、上記Eは、第1成形体及び第2成形体の境界面と中空構造体の中立面との間の距離である。上記式(3)は、上記Eが無視できるほど小さい場合が多いことを考慮して、Eの記載を省略したものである。なお、上記(3’)式においてEは、中立面が第1成形体と第2成形体との境界面よりも第2成形体側(引張側)にある場合に、“+”となり、第1成形体側(圧縮側)にある場合に、“-”となる。
本発明に用いられる第1成形体及び第2成形体は、両者が組み合わされることによって中空構造を形成するものである。以下、このような第1成形体及び第2成形体について説明する。なお、第1成形体及び第2成形体を構成する上記第1繊維強化樹脂材料及び第2繊維強化樹脂材料については後述する。
(σc/σt)<(Tc×σc)/(Tt×σt)<(σt/σc) (2)
これにより上記第1成形体の平均厚みTcと第2成形体の平均厚みTtを調整することのみで、より軽量で所望の構造強度を達成することができるからである。
なお、上記式(2)において、Tc、Ttはそれぞれは第1成形体及び第2成形体の上記式(2)を満たす断面における平均厚みである。
次に、本発明に用いられる第1繊維強化樹脂材料及び第2繊維強化樹脂材料について説明する。本発明に用いられる第1繊維強化樹脂材料は、第1強化繊維と第1マトリックス樹脂とを含有するものであり、本発明に用いられる第2繊維強化樹脂材料は、第2強化繊維と、第2マトリックス樹脂とを含有するものである。
以下、本発明に用いられる第1繊維強化樹脂材料、及び第2繊維強化樹脂材料のそれぞれについて説明する。
なお、以下の説明においては、第1繊維強化樹脂材料と第2繊維強化樹脂材料とを合わせて「繊維強化樹脂材料」と称する場合があり、第1強化繊維と第2強化繊維とを合わせて「強化繊維」と称する場合があり、第1マトリックス樹脂と第2マトリックス樹脂とを合わせて「マトリックス樹脂」と称する場合がある。
本発明に用いられる強化繊維は、繊維強化樹脂材料の圧縮強度及び引張強度を所望の範囲内にすることができ、かつ上記式(1)を満たすことができるものであれば特に限定されるものではない。このため、本発明に用いられる強化繊維としては無機繊維又は有機繊維のいずれであっても好適に用いることができる。
上記有機繊維としては、例えば、PBO(ポリパラフェニレンベンズオキサゾール)等のポリベンザゾール、アラミド、ポリフェニレンスルフィド、ポリエステル、アクリル、ポリアミド、ポリオレフィン、ポリビニルアルコール、ポリアリレート等の樹脂材料からなる繊維を挙げることができる。
Ln=ΣLi/j ・・・(a)
Lw=(ΣLi2)/(ΣLi) ・・・(b)
なお、強化繊維をロータリーカッターで切断した場合など、繊維長が一定長の場合は数平均繊維長と重量平均繊維長は同じ値になる。
臨界単糸数=600/D (i)
(ここでDは炭素繊維の平均繊維径(μm)である)
0.6×104/D2<N<1×105/D2 (ii)
(ここでDは炭素繊維の平均繊維径(μm)である)
次に、本発明に用いられるマトリックス樹脂について説明する。本発明に用いられるマトリックス樹脂としては、上記式(1)を満たす繊維強化樹脂材料を得ることができるものであれば特に限定されるものではなく、強化繊維の種類等に応じて適宜選択して用いることができる。したがって、本発明に用いられるマトリックス樹脂としては、熱可塑性樹脂を用いてもよく、熱硬化性樹脂を用いてもよい。
本発明に用いられる熱可塑性樹脂としては、例えば、ポリオレフィン樹脂、ポリスチレン樹脂、熱可塑性ポリアミド樹脂、ポリエステル樹脂、ポリアセタール樹脂(ポリオキシメチレン樹脂)、ポリカーボネート樹脂、(メタ)アクリル樹脂、ポリアリレート樹脂、ポリフェニレンエーテル樹脂、ポリイミド樹脂、ポリエーテルニトリル樹脂、フェノキシ樹脂、ポリフェニレンスルフィド樹脂、ポリスルホン樹脂、ポリケトン樹脂、ポリエーテルケトン樹脂、熱可塑性ウレタン樹脂、フッ素系樹脂、熱可塑性ポリベンゾイミダゾール樹脂等を挙げることができる。
上記ポリオレフィン樹脂としては、例えば、ポリエチレン樹脂、ポリプロピレン樹脂、ポリブタジエン樹脂、ポリメチルペンテン樹脂、塩化ビニル樹脂、塩化ビニリデン樹脂、酢酸ビニル樹脂、ポリビニルアルコール樹脂等を挙げることができる。
本発明に用いられる熱硬化性樹脂の例としては、例えば、熱硬化性樹脂の場合、エポキシ樹脂、ビニルエステル樹脂、不飽和ポリエステル樹脂、ジアリルフタレート樹脂、フェノール樹脂、マレイミド樹脂、シアネート樹脂、ベンゾオキサジン樹脂、ジシクロペンタジエン樹脂などの硬化物及びこれらの変性体を挙げることができる。上記エポキシ樹脂としては、分子中にエポキシ基を有するものであれば特に限定されず、例えば、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、ビスフェノールAD型エポキシ樹脂、ビフェニル型エポキシ樹脂、ナフタレン型エポキシ樹脂、脂環式エポキシ樹脂、グリシジルエステル系樹脂、グリシジルアミン系エポキシ樹脂、複素環式エポキシ樹脂、ジアリールスルホン型エポキシ樹脂、ヒドロキノン型エポキシ樹脂及びそれらの変性物などが挙げることができる。なお、熱可塑性樹脂の場合と同様に、本発明に用いられる熱硬化性樹脂は、第1繊維強化樹脂材料及び第2繊維強化複合材料のそれぞれにおいて1種類のみであってもよく、2種類以上であってもよい。
上述した通り、本発明に用いられる繊維強化樹脂材料は、強化繊維とマトリックス樹脂とを含有するものであるが、本発明においては上記マトリックス樹脂として、熱可塑性樹脂が用いられることが好ましい。上記マトリックス樹脂として熱可塑性樹脂が用いられることにより、例えば、第1成形体及び第2成形体をプレス成形によって製造する場合に、成形時間を短くすることができる等の利点があるからである。また、マトリックス樹脂として熱可塑性樹脂を用いることにより、第1成形体及び第2成形体をリサイクル又はリユースすることができる場合があるからである。
第2繊維強化樹脂材料の引張強度σtを上記範囲内にするには、例えば、第2繊維強化樹脂材料中の第2強化繊維の含有率を調整したり、平均繊維長を調整したり、また、第2強化繊維または/及び第2マトリックス樹脂の種類を変更する等の方法により達成される。より具体的には、第2強化繊維の含有率を上げる、平均繊維長を長くする、また、より引張強度の大きい第2強化繊維または/及び第2マトリックス樹脂を用いることで、引張強度を大きくすることができる。逆に、第2強化繊維の含有率を下げる、平均繊維長を短くする、繊維の径を太くする、また、より引張強度の小さい第2強化繊維または/及び第2マトリックス樹脂を用いることで、その引張強度を、第1繊維強化樹脂材料の圧縮強度に近付くように、小さくすることができる。
次に本発明に用いられる繊維強化樹脂材料の製造方法について説明する。本発明に用いられる繊維強化樹脂材料は、一般的に公知の方法を用いて製造することができる。例えば、マトリックス樹脂として熱可塑性樹脂を用いる場合、1.強化繊維をカットする工程、2.カットされた強化繊維を開繊させる工程、3.開繊させた強化繊維と繊維状又は粒子状のマトリックス樹脂を混合した後、加熱圧縮する方法を挙げることができる。
一方、マトリックス樹脂として熱硬化性樹脂を用いる場合は、例えば、強化繊維に熱硬化性樹脂を含浸させ、加圧して一体化する方法を挙げることができる。
次に本発明の中空構造体の製造方法について説明する。本発明の中空構造体は、まず第1成形体及び第2成形体を製造した後、両者を組み合わせて接合して中空構造体とすることによって製造することができる。
次いで、上記第1成形体及び第2成形体を組み合わせて接合する方法としては、例えば、振動溶着方法、超音波溶着方法、通電溶着方法等の溶着方法や、接着剤を用いる接着法や、ボルトナットとを用いる機械締結方法等の一般的に公知の方法を用いることができる。
上述した通り、本発明の中空構造体は上記式(1)を満たすことにより、上記第1成形体側から本発明の中空構造体に外力が加わった際に、上記第1成形体が先に破壊することを抑制できるものである。したがって、本発明の中空構造体は、第1成形体側から圧縮応力が負荷される用途に用いられることにより、優れた強度を示すという効果を奏することができるものである。このような本発明の中空構造体の用途としては、例えば、フレーム、ビーム等のような曲げ部材等を挙げることができるが、これに限られるものではない。
次に、本発明の車両用部品について説明する。上述した通り、本発明の車両用部品は上記本発明に係る中空構造体が用いられたことを特徴とするものである。本発明の車両用部品としては、本発明の中空構造体が用いられているものであれば特に限定されるものではないが、例えば、フロントバンパー、リアバンパー、各ピラー、サイドシル、フロアークロスメンバー等が挙げられる。
(1)各繊維強化樹脂材料中の強化繊維の平均繊維長
各繊維強化樹脂材料中の強化繊維の平均繊維長は、繊維強化樹脂材料を500℃の炉内にて1時間加熱して、熱可塑性樹脂を除去した後、無作為に抽出した強化繊維100本の長さをノギスで1mm単位まで測定し、その平均値とする。平均繊維長が1mmを下回る場合は、光学顕微鏡下で0.1mm単位まで測定する。
なお、本実施例においては、一定のカット長を用いているので、数平均繊維長と重量平均繊維長は一致する。
(2)各繊維強化樹脂材料中の強化繊維の体積含有率
各繊維強化樹脂材料中の強化繊維の体積含有率は、水中置換法により繊維強化樹脂材料の密度を求め、予め測定した強化繊維単独の密度と樹脂単独の密度との関係から、強化繊維の体積含有率を算出する。
(3)各繊維強化樹脂材料の引張強度及び圧縮強度
各繊維強化樹脂材料の引張強度及び圧縮強度は、事前に80℃真空下で24時間乾燥させた試験片をそれぞれJIS K7164:2005とJIS K7076:1991に準拠して測定する。
(4)中空構造体の構造強度評価
各実施例及び比較例の中空構造体の構造強度は、図3に示すような三点曲げ試験を利用して評価する。3点曲げ試験を実施する際、中空構造体をその第1成形体の天面側に垂直に外力Pを直接に与えるように3点曲げ試験装置にセットし、第1成形体又は第2成形体のどちらかが先に破壊した時の外力の大きさを中空構造体の曲げ強度とする。図3中、LはL=500.0mmである。
強化繊維として、平均繊維長20mmにカットした東邦テナックス社製のPAN系炭素繊維「テナックス(登録商標)」STS40-24KS(平均繊維径7μm、密度は約1750kg/m3)を使用し、熱可塑性樹脂としてユニチカ社製のナイロン6樹脂A1030(密度は約1130kg/m3)を使用して、280℃に加熱したプレス装置にて、圧力2.0MPaで5分間加熱圧縮することで面内方向に炭素繊維が2次元ランダム配向した繊維強化樹脂材料1を作製した。
得られた繊維強化樹脂材料1の強化繊維の体積含有率は約30Vf%、平均繊維長は約20mm、引張強度は350MPa、圧縮強度は250MPaとなり、密度は1340kg/m3となった。
参考例1と同じ強化繊維及び熱可塑性樹脂を用い、かつ参考例1と同一の方法により、面内方向に炭素繊維が2次元ランダム配向した、強化繊維の体積含有率が22Vf%の繊維強化樹脂材料2を作製した。
得られた繊維強化樹脂材料2の強化繊維の平均繊維長は約20mm、引張強度は255MPa、圧縮強度は154MPaとなり、密度は1280kg/m3となった。
以下の各実施例及び比較例の中空構造体の主な寸法を示す各値(W1、W2、Wc、Hc、Ht、Tc、Tt)は、図4に示す通りである。また、各実施例及び比較例における中空構造体の長さは一律に600.0mmとした。
第1繊維強化樹脂材料及び第2繊維強化樹脂材料として、参考例1の繊維強化樹脂材料1用い、これを280℃にし、10MPaの圧力で60秒間のコールドプレス成形によってハット形状の第1成形体及び第2成形体とし、第1成形体及び第2成形体をその底面部を向き合わせ振動溶着で接合させて閉じた断面を有する中空構造体とした。このとき、中空断面の主な寸法は、W1=150.0mm、W2=120.0mm、Wc=100.0mm、Hc=55mm、Ht=53.6mm、Tc=5.0mm、Tt=3.6mm、Ac=1146.0mm2、At=825.0mm2とした。構造体としての重量は1585gとなった。また、本実施例の中空構造体の比(Sc/St)=(Ac×σc)/(At×σt)≒1.0となった。
実施例1の中空構造体の曲げ強度を上述した3点曲げ試験で評価すると、第1成形体と第2成形体とがほぼ同時に破壊した。また、中空構造体の曲げ強度は29.7kNとなった。
第1繊維強化樹脂材料及び第2繊維強化樹脂材料として、参考例1の繊維強化樹脂材料1用い、これを280℃にし、実施例1と同じ方法により閉じた断面を有する中空構造体とした。各部の寸法は、W1=150.0mm、W2=120.0mm、Wc=100.0mm、Hc=54.2mm、Ht=70mm、Tc=4.8mm、Tt=3.2mm、Ac=1113.0mm2、At=820.0mm2とした。構造体としての重量は1547gとなった。また、本実施例の中空構造体は、(Sc/St)=0.97となった。
実施例2の中空構造体の曲げ強度を、3点曲げ試験で評価すると、第1成形体と第2成形体とがほぼ同時に破壊した。また、中空構造体の曲げ強度は31.4kNとなった。
第1繊維強化樹脂材料として上記繊維強化樹脂材料1を用い、これを280℃にし、実施例1と同条件でのコールドプレス成形によってハット形状の第1成形体とし、第2繊維強化樹脂材料として上記繊維強化樹脂材料2を用い、これを280℃として上記と同様な条件でのコールドプレス成形によりハット形状の第2成形体として、第1成形体1と第2成形体2をその底面部を向き合わせ振動溶着で接合させて閉じた断面を有する中空構造体とした。各部の寸法は、W1=150.0mm、W2=120.0mm、Wc=100.0mm、Hc=55.0mm、Ht=55.0mm、Tc=5.0mm、Tt=4.9mm、Ac=1146.0mm2、At=1123.0mm2とした。中空構造体としての重量は1802gとなった。また、本実施例の中空構造体は、(Sc/St)=1.0となった。
実施例3の中空構造体の曲げ強度を3点曲げ試験で評価すると、第1成形体と第2成形体とが同時に破壊した。また、中空構造体の曲げ強度は30.3kNとなった。
第1繊維強化樹脂材料及び第2繊維強化樹脂材料として、参考例1の繊維強化樹脂材料1用い、これを280℃にし、実施例1と同じ成形と振動溶着条件で閉じた断面を有する中空構造体とした。各部の寸法は、W1=150.0mm、W2=120.0mm、Wc=100.0mm、Hc=55.0mm、Ht=55.0mm、Tc=5.0mm、Tt=5.0mm、Ac=1146.0mm2、At=1146.0mm2とした。中空構造体の重量は1843gとなった。また、本比較例の中空構造体は(Sc/St)=0.71となった。
比較例1の中空構造体の曲げ強度を3点曲げ試験で評価すると、外力が約30.5kNになった時点で中空構造体の第1成形体が先に破壊し、第2成形体は破壊されなかった。当該中空構造体の曲げ強度は30.5kNとなった。
第1繊維強化樹脂材料及び第2繊維強化樹脂材料として参考例1の繊維強化樹脂材料1用い、これを280℃にし、実施例1と同じ方法により閉じた断面を有する中空構造体とした。各部の寸法は、W1=150.0mm、W2=120.0mm、Wc=100.0mm、Hc=53.6mm、Ht=56.4mm、Tc=6.4mm、Tt=3.3mm、Ac=1477.0mm2、At=753.0mm2とした。中空構造体としての重量は1795gとなった。また、本比較例の中空構造体は、(Sc/St)=1.39となった。
比較例2の中空構造体の曲げ強度を、3点曲げ試験で評価すると、外力が約31.4kNになった時点で引張側の第2成形体が先に破壊し、圧縮側の第1成形体は破壊されなかった。当該中空構造体の曲げ強度は31.4kNとなった。
11 第1成形体
12 第2成形体
11a、12a 底面部
11b、12b 天面部
11c、12c 立面部
X 中空構造の軸方向
Y 第1成形体と第2成形体との境界面
Claims (8)
- 第1強化繊維と第1マトリックス樹脂とを含有する第1繊維強化樹脂材料からなる第1成形体と、第2強化繊維と第2マトリックス樹脂とを含有する第2繊維強化樹脂材料からなる第2成形体とが組み合わされてなり、中空構造を有する中空構造体であって、
前記中空構造の軸方向に対して垂直方向の任意の断面において、前記第1成形体の構造の圧縮強度Sc及び前記第2成形体の構造の引張強度Stとの比Sc/Stが以下の式(1)を満たすことを特徴とする中空構造体。
(σc/σt)×(Hc/Ht)<(Sc/St)<(σt/σc)×(Hc/Ht)
(1)
ここで、前記式(1)における各記号は次の通りである。Hc=第1成形体の高さ、Ht=第2成形体の高さ、σc=第1繊維強化樹脂材料の前記軸方向における圧縮強度、σt=第2繊維強化樹脂材料の前記軸方向における引張強度、Ac=第1成形体の前記断面における断面積、At=第2成形体の前記断面における断面積、Sc=σc×Ac、St=σt×At。 - 前記第1成形体の高さHcと、前記第2成形体の高さHtとが同一の場合に、前記式(1)を満たす前記断面において、以下の式(2)を満たすことを特徴とする、請求項1に記載の中空構造体。
(σc/σt)<(Tc×σc)/(Tt×σt)<(σt/σc) (2)
ここで、前記式(2)における各記号は以下の通りである。Tc=第1成形体の前記断面における平均厚み、Tt=第2成形体の前記断面における平均厚み。 - 前記第1強化繊維及び前記第2強化繊維が2次元ランダム配列していることを特徴とする、請求項1又は請求項2に記載の中空構造体。
- 前記比Sc/Stが1.04×(σc/σt)×(Hc/Ht)≦(Sc/St)≦0.96×(σt/σc)×(Hc/Ht)であることを特徴とする、請求項3に記載の中空構造体。
- 前記第1繊維強化樹脂材料における前記第1強化繊維の体積含有率Vfcと、前記第2繊維強化樹脂材料における前記第2強化繊維の体積含有率Vftとが、Vfc>Vftを満たすことを特徴とする、請求項1から請求項4までのいずれかに記載の中空構造体。
- 前記第1強化繊維の平均繊維長Lcと、前記第2強化繊維の平均繊維長Ltとが、Lc>Ltを満たすことを特徴とする、請求項1から請求項5までのいずれかに記載の中空構造体。
- 前記第1強化繊維の平均繊維径Dcと、前記第2強化繊維の平均繊維径Dtとが、Dc<Dtを満たすことを特徴とする、請求項1から請求項6までのいずれかに記載の中空構造体。
- 請求項1から請求項7までのいずれかの請求項に記載の中空構造体が用いられたことを特徴とする、車両用部品。