WO2015114914A1 - Cu-Ga合金スパッタリングターゲット及びその製造方法 - Google Patents
Cu-Ga合金スパッタリングターゲット及びその製造方法 Download PDFInfo
- Publication number
- WO2015114914A1 WO2015114914A1 PCT/JP2014/080465 JP2014080465W WO2015114914A1 WO 2015114914 A1 WO2015114914 A1 WO 2015114914A1 JP 2014080465 W JP2014080465 W JP 2014080465W WO 2015114914 A1 WO2015114914 A1 WO 2015114914A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- phase
- alloy
- sputtering target
- powder
- alloy sputtering
- Prior art date
Abstract
本発明のCu-Ga合金スパッタリングターゲットは、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体であり、該焼成体におけるCu-Ga合金結晶粒は、γ相粒子がγ1相結晶粒中に分散した組織を有する。また、上記スパッタリングターゲットを製造する方法は、純Cu粉末とCu-Ga合金粉末との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、これにより得られた焼成体を、温度:450~650℃の範囲において0.1~1.0℃/minの冷却速度で冷却する工程とを有する。
Description
本発明は、CIGS薄膜型太陽電池の光吸収層を形成するためのCu-In-Ga-Se化合物膜(以下、CIGS膜と略記する。)を形成するときに使用するCu-Ga合金スパッタリングターゲット及びその製造方法に関する。
本願は、2014年1月28日に、日本に出願された特願2014-013184号に基づき優先権を主張し、その内容をここに援用する。
本願は、2014年1月28日に、日本に出願された特願2014-013184号に基づき優先権を主張し、その内容をここに援用する。
近年、カルコパイライト系の化合物半導体による薄膜型太陽電池が実用に供せられるまでになってきた。この化合物半導体による薄膜型太陽電池は、ソーダライムガラス基板の上にプラス電極となるMo電極層、CIGS膜からなる光吸収層、ZnS、CdSなどからなるバッファ層、マイナス電極となる透明電極層の順番で層が形成された基本構造を有している。
上記光吸収層の形成方法として、例えば、多元蒸着法により成膜する方法が知られている。この方法により得られた光吸収層は、高いエネルギー変換効率が得られるが、点源からの蒸着のため、大面積の基板に成膜した場合には、膜厚分布の均一性が低下しやすい。そのため、スパッタリング法によって光吸収層を形成する方法が提案されている。
スパッタリング法により上記光吸収層を形成する方法としては、先ず、Inターゲットを使用してスパッタによりIn膜を成膜し、このIn膜上に、Cu-Ga二元系合金スパッタリングターゲットを使用してスパッタリングすることにより、Cu-Ga二元系合金膜を成膜し、次いで、得られたIn膜及びCu-Ga二元系合金膜からなる積層プリカーサ膜をSe雰囲気中で熱処理してCIGS膜を形成する方法(セレン化法)が採用されている。
さらに、以上の技術を背景に、以下で説明する技術が提案されている。この技術では、前記Cu-Ga合金膜及びIn膜の積層プリカーサ膜を、金属裏面電極層側からGa含有量の高いCu-Ga合金層、Ga含有量の低いCu-Ga合金層、In層の順序でスパッタリング法により作製し、これをセレン及び/又は硫黄雰囲気中で熱処理することにより、界面層(バッファ層)側から金属裏面電極層側への薄膜光吸収層内部でのGaの濃度勾配を徐々(段階的)に変化させている。これにより、開放電圧の大きい薄膜型太陽電池を実現すると共に、薄膜光吸収層の他の層からの剥離を防止することができる。この場合、Cu-Ga合金スパッタリングターゲット中のGa含有量は、1~40原子%とすることが提案されている。
このようなCu-Ga合金層を形成するためのCu-Ga合金スパッタリングターゲットとして、水アトマイズ装置で作製したCu-Ga混合微粉をホットプレスにより焼結させたCu-Ga合金焼成体スパッタリングターゲットが提案されている(例えば、特許文献1を参照)。このCu-Ga合金焼成体スパッタリングターゲットは、単一組成からなり、Cu-Ga合金のX線回折で得られたグラフにおける主ピーク以外のピーク強度が、主ピークに対して5%以下であり、その平均結晶粒径が、5~30μmとなっている。また、このターゲットでは、酸素含有量が350~400ppmのものが得られている。
一方、CIGS膜からなる光吸収層の発電効率を向上させるため、アルカリ性ガラス基板からの拡散により光吸収層にNaを添加することが有効とされている(例えば、非特許文献1を参照)。しかしながら、アルカリ性ガラスに代えてポリマーフィルムなどを基材とするフレキシブルCIGS太陽電池の場合、アルカリ性ガラス基板を備えていないことから、Naの供給源を提供できないという不都合がある。非特許文献1では、上記Naの添加については、ソーダライムガラスをMo電極層と基板との間に成膜する方法が提案されているが、ソーダライムガラスに成膜する場合、製造プロセスが増え、生産性が低下してしまう。そこで、Cu-In-Ga(以下、CIGと称する)プリカーサ膜にナトリウム化合物を添加し、光吸収層へのNa供給を確保する技術が提案されている(例えば、特許文献2を参照)。
石塚 他、「カルコパライト系薄膜太陽電池の開発の現状と将来展望」、Journal of the Vacuum Society of Japan, Vol53, 2010 p.25
上述した従来の技術には、以下に示す課題が残されている。
上記特許文献1に記載されたCu-Ga合金スパッタリングターゲットは、ホットプレスにより作製された焼結体であり、その焼結体中のCu-Ga合金粒は、実質的にγ相であるか、又は、主要相がγ相で構成された組織を有している。即ち、このCu-Ga合金スパッタリングターゲットは、比較的脆い性質を持つγ相からなる単相組織になっているといえる。ところが、このγ相で構成されると、加工性に乏しいだけでなく、スパッタリング時において、パーティクルが発生しやすくなり、異常放電が増大するという問題があった。
上記特許文献1に記載されたCu-Ga合金スパッタリングターゲットは、ホットプレスにより作製された焼結体であり、その焼結体中のCu-Ga合金粒は、実質的にγ相であるか、又は、主要相がγ相で構成された組織を有している。即ち、このCu-Ga合金スパッタリングターゲットは、比較的脆い性質を持つγ相からなる単相組織になっているといえる。ところが、このγ相で構成されると、加工性に乏しいだけでなく、スパッタリング時において、パーティクルが発生しやすくなり、異常放電が増大するという問題があった。
また、上記提案された技術では、ホットプレスにより、Cu-Ga合金スパッタリングターゲットの作製を行うことで、酸素含有量が低減されるとともに、スパッタリング時の異常放電が少なくなる。しかし、CIGS薄膜型太陽電池の製造の観点からは、より酸素含有量の少ないスパッタリングターゲットが要望されている。このより少ない酸素含有量を得る手法として、溶解法がある。この溶解法によれば、酸素含有量を40~50ppmに大幅に低減したCu-Ga合金スパッタリングターゲットを作製することもできるが、このスパッタリングターゲットでは、酸素含有量を大幅に低減できる反面、平均粒径が830~1100μmと非常に大きくなり、異常放電が増大する不都合がある。
また、上記提案された製造方法によるCIGスパッタリングターゲットの場合、金属素地のCIGスパッタリングターゲットに非導電性のナトリウム化合物を適切に混入できず、スパッタリング時に異常放電が発生しやすく、安定した成膜が困難であるという問題があった。
本発明は、上述した課題に鑑みてなされたものであって、高濃度のGa成分を有するCu-Ga合金焼成体によるスパッタリングターゲットに関して、パーティクル発生を低減でき、酸素含有量をさらに低減可能であると共に、高濃度のNaを含有しつつも、異常放電を一層抑制したCu-Ga合金スパッタリングターゲット及びその製造方法を提供することを目的とする。
本発明では、上述した課題を解決するために以下の態様を有する。
(1)本発明のCu-Ga合金スパッタリングターゲットは、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体であって、前記焼成体におけるCu-Ga合金結晶粒は、γ相粒子がγ1相結晶粒中に分散した組織を有する。
(2)前記(1)のCu-Ga合金スパッタリングターゲットの前記γ相の平均粒子数が、一つのγ1結晶粒中に6~36個存在し、前記γ1相結晶粒の平均粒径が、15.0~75.0μmである。
(3)前記(1)又は(2)のCu-Ga合金スパッタリングターゲットの前記焼成体の酸素量が200質量ppm以下である。
(4)前記(1)から(3)のいずれかのCu-Ga合金スパッタリングターゲットの前記焼成体は、さらに、Na:0.05~10.0原子%を含有し、前記焼成体中に、Na化合物相が分散している。
(5)前記(4)のCu-Ga合金スパッタリングターゲットにおける前記Na化合物相は、NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上からなる。
(6)前記(1)から(3)のいずれかのCu-Ga合金スパッタリングターゲットを製造する方法であって、純Cu粉末とCu-Ga合金粉末との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程とを有する。
(7)前記(4)又は(5)に記載のCu-Ga合金スパッタリングターゲットを製造する方法であって、純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程とを有する。
(1)本発明のCu-Ga合金スパッタリングターゲットは、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体であって、前記焼成体におけるCu-Ga合金結晶粒は、γ相粒子がγ1相結晶粒中に分散した組織を有する。
(2)前記(1)のCu-Ga合金スパッタリングターゲットの前記γ相の平均粒子数が、一つのγ1結晶粒中に6~36個存在し、前記γ1相結晶粒の平均粒径が、15.0~75.0μmである。
(3)前記(1)又は(2)のCu-Ga合金スパッタリングターゲットの前記焼成体の酸素量が200質量ppm以下である。
(4)前記(1)から(3)のいずれかのCu-Ga合金スパッタリングターゲットの前記焼成体は、さらに、Na:0.05~10.0原子%を含有し、前記焼成体中に、Na化合物相が分散している。
(5)前記(4)のCu-Ga合金スパッタリングターゲットにおける前記Na化合物相は、NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上からなる。
(6)前記(1)から(3)のいずれかのCu-Ga合金スパッタリングターゲットを製造する方法であって、純Cu粉末とCu-Ga合金粉末との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程とを有する。
(7)前記(4)又は(5)に記載のCu-Ga合金スパッタリングターゲットを製造する方法であって、純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程とを有する。
以上の様に、本発明によるCu-Ga合金スパッタリングターゲットは、Ga:29.5~43.0原子%という高濃度Ga成分を有するCu-Ga合金焼成体であって、該焼成体におけるCu-Ga合金結晶粒は、γ相粒子がγ1相結晶粒中に分散した組織を有する。特に、前記γ相粒子の平均粒子数が、6~36個であり、前記γ1相結晶粒の平均粒径が、15.0~75.0μmであり、Cu-Ga合金のγ1相結晶粒内に、微細なCu-Ga合金のγ相粒子が分散するので、Cu-Ga合金スパッタリングターゲットにおける母相がγ1相結晶粒で構成される。この母相中に微細なγ相粒子が分散されることにより、ターゲット脆性を改善でき、しかも、スパッタリング時のパーティクル発生を低減できる。さらに、前記焼成体には、Na:0.05~10.0原子%も含有され、該焼成体中に、Na化合物(NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上)相を分散させている。そのため、本発明のCu-Ga合金スパッタリングターゲットによれば、Cu-Ga合金スパッタリングターゲットにおける脆性を改善し、しかも、スパッタリング時のパーティクル発生を低減し、ターゲット中の酸素含有量をさらに低減可能であると共に、高濃度のNaを含有しつつも、異常放電を一層抑制することができる。
また、本発明によるCu-Ga合金スパッタリングターゲットの製造方法では、純Cu粉末とCu-Ga合金粉末との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程、或いは、純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程とを有している。そのため、前記焼成体におけるCu-Ga合金結晶粒は、微細なγ相粒子がγ1相結晶粒中に分散した組織を有することになり、脆性が改善され、しかも、スパッタリング時のパーティクル発生が低減されたCu-Ga合金スパッタリングターゲットが得られる。
以下、本発明の実施形態に係るCu-Ga合金スパッタリングターゲット及びその製造方法の実施形態について具体的に説明する。
なお、本発明における前記γ相及びγ1相とは、図1に示されるCu-Ga合金に係る状態図における490℃以上で安定なγ相(Gaが29.5~34.7原子%の範囲に存在するPhase-γ)及び645℃以下で安定なγ1相(Gaが29.8~37.6原子%の範囲に存在するPhase-γ1)とにそれぞれ対応している。
本実施形態のCu-Ga合金スパッタリングターゲットの焼成体は、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有している。前記焼成体の組織は、Cu-Ga合金結晶粒を母相(マトリクス相)とし、その母相は、Cu-Ga合金のγ相粒子とγ1相結晶粒とを含むこととし、特に、該母相は、平均粒径:15.0~75.0μmのγ1相結晶粒中に、平均粒子数:6~36個のγ相粒子が分散した組織を有している。
上記引用文献1で提案されたCu-Ga合金スパッタリングターゲットの製作では、Cu粉末とGa粉末との混合粉末をホットプレスすることにより、Cu-Ga合金焼結体を得ている。通常、得られた焼結体をホットプレス温度から冷却してスパッタリングターゲットを製作している。この場合、図1のCu-Ga合金の状態図(出典、Desk Handbook : Phase Diagrams for Binary Alloys(ASM International))からも分かるように、焼結体の組織は、Cu-Ga合金粒の単相にしかならず、しかも、この平均粒径も大きかった。例えば、Ga:29.5~34.7原子%含有し、残部がCuであるようなCu-Ga合金の場合、焼結体中のCu-Ga合金粒は、主としてγ相により構成される。このγ相は、元々、比較的脆い性質を有するため、スパッタリング時におけるパーティクル発生、異常放電発生の要因になっていた。
そこで、本発明では、このCu-Ga合金粒の母相を、γ相とγ1相との2相で構成するようにして、γ相に比較して柔らかいγ1相中に、微細なγ相を分散させた組織とした。Cu-Ga合金スパッタリングターゲット中のCu-Ga合金粒が、このような組織を有することにより、脆性を改善でき、しかも、Cu-Ga合金相の平均粒径を小さくすることができるので、スパッタリング時におけるパーティクル発生、異常放電発生を抑制することができる。
ここで、本実施形態のCu-Ga合金スパッタリングターゲットを製作するには、純Cu粉末とCu-Ga合金粉末との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成した後、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却すると、焼成体中に、γ相粒子とγ1相結晶粒との2相で構成される組織構造を有するCu-Ga合金粒を形成できることが判明した。図1のCu-Ga合金に係る状態図からも分かるように、焼成体に対する冷却過程において、上記冷却条件(冷却速度)を調整することにより、γ1結晶粒内におけるγ相の分散状態を変化させることができる。
γ1相中におけるγ相の分散状態の変化について説明する。先ず、成形体の焼成後における冷却過程において、焼成温度付近では、γ相が安定であるため、この状態で急冷すると、Cu-Ga合金粒の主相がγ相の焼成体が得られる。これに対して、この冷却の途中で、例えば、温度:450~650℃の範囲において、0.1~1.0℃/minの遅い冷却速度で徐冷すると、γ相中に微細なγ1相が現われる。この遅い冷却速度による冷却過程において、γ相とγ1相の存在比が徐々に変化するので、γ1相中に微細なγ相が形成された時点で、冷却速度を速めると、微細なγ相粒子がγ1相結晶粒中に分散した組織を有するCu-Ga合金粒を得ることができる。
本実施形態のCu-Ga合金スパッタリングターゲットでは、Cu-Ga合金粒が、平均粒径:15.0~75.0μmのγ1相結晶粒中に、平均粒子数:6~36個のγ相粒子が分散した組織を有する。上記冷却速度が遅すぎると、Cu-Ga合金粒が大きくなり、微細なγ相粒子が分散していても、異常放電発生が増加するので、γ1相結晶粒の平均粒径を75.0μm以下とした。γ相粒子の平均粒子数が、6個未満の場合には、異常放電防止の効果が得られなくなり、その平均粒子数が、36個を超える場合には、冷却速度を0.1℃/minより小さくする必要がある。この条件では、γ1母相が粗大化して、γ1相の平均粒径が75μmを超えるため、異常放電が増加して、良好なスパッタリングを行えなくなり、さらに、冷却速度のコントロールが困難になる。上記γ1相結晶粒の平均粒径は、好ましくは25~50μmであり、上記γ相粒子の平均粒子数は、好ましくは10~30個であるが、これに限定されることはない。
また、本実施形態のCu-Ga合金スパッタリングターゲットの他の製造方法では、純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程とを有する。上述した本発明によるCu-Ga合金スパッタリングターゲットの製造方法は、純Cu粉末とCu-Ga合金粉末との混合粉末の場合であったが、本発明による他の製造方法では、混合粉末にNa化合物を含む混合粉末の場合であり、冷却工程については、上述の本発明による製造方法の場合と同様である。なお、添加されたNa化合物は、焼成体中では、Cu-Ga合金粒同士の界面に、Na化合物相として存在していることが確認されている。冷却工程での好ましい温度範囲は490~645℃であり、上記冷却速度は、好ましくは0.2~0.9℃/minであるが、これに限定されることはない。
上記特許文献2に開示されたスパッタリングターゲットの製造方法においては、CIG合金に、Naを添加していた。これに対して、本発明の製造方法では、Na単体ではなく、Naを化合物の状態で添加するとともに、Na化合物相の粗大化を抑制し、スパッタリングターゲット中の酸素含有量を制限した。また、本発明の製造方法では、スパッタリングターゲット中のCu-Ga合金の母相(マトリクス相)の平均粒径を最適化し、その母相には、γ相粒子とγ1相結晶粒とが含まれるようにして、Naを含有しつつも、異常放電を抑制したCu-Ga合金スパッタリングターゲットを実現した。
なお、Na化合物の状態で含まれるNa含有量を上記範囲内に設定した理由は、Na含有量が10原子%を超えると、十分な焼結密度を確保することができなくなると同時に、スパッタリング時の異常放電が増加するためである。一方、Na含有量が0.05原子%より少ないと、スパッタ膜中のNa含有量が不足し、目的とするNa添加CuGa合金膜を得ることができない。上記Na含有量は、好ましくは1.0~6.0原子%であるが、これに限定されることはない。
また、本実施形態のCu-Ga合金スパッタリングターゲットは、酸素含有量が200質量ppm以下であることが好ましい。Na化合物を添加したCu-Ga合金スパッタリングターゲット中に酸素が存在すると、酸素とNa化合物とが反応し、吸湿性の高いNaOが形成される可能性がある。特に、酸素含有量が200質量ppmを超えると、スパッタリングターゲットに異常放電が発生する可能性が高いため、酸素含有量を200質量ppm以下とした。上記酸素含有量の下限値は10質量ppmであってもよい。上記酸素含有量は、好ましくは50~100質量ppmであるが、これに限定されることはない。
さらに、本発明に係るCu-Ga合金スパッタリングターゲットでは、金属素地中のγ1相結晶粒の平均粒径が15.0~75.0μmであるので、上記のNa化合物を含有していても、粗大なNa化合物相が生成されない。なお、γ1相結晶粒の平均粒径が75.0μmを超えると、Na化合物相が粗大化しやすくなり、好ましくない。また、γ1相結晶粒の平均粒径が15.0μm未満であると、γ相粒子の微細分散構造が現われず、しかも、酸素含有量が200質量ppmを超えやすくなり、好ましくない。
以上の様に、本発明のCu-Ga合金スパッタリングターゲットでは、金属素地中に、微細なγ相粒子がγ1相結晶粒内に分散しており、そのγ1相結晶粒の平均粒径が15.0~75.0μmであり、平均粒径が8.5μm以下のNa化合物相が微細に分散し、さらには、酸素含有量が200質量ppm以下であるので、酸素含有量が低くかつ粒径が小さいため、異常放電が大幅に低減される。
なお、Gaの含有量を29.5原子%以上とした理由は、29.5原子%未満であると、γ1相結晶粒の平均粒径が減少し、酸素含有量が増加しやすくなるためである。また、Gaの含有量を43.0原子%以下とした理由は、43.0原子%を超えると、γ相の存在割合が減少し、γ1相結晶粒の平均粒径が増大して、粗大なNa化合物相が生成されやすくなるためである。また、Na化合物には、NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上を用いることができる。ここで、Na化合物におけるNa以外の元素F、S、Se及びAlについては、ターゲット組成における不純物として扱い、不可避不純物に含めた。上記Gaの含有量は、好ましくは30.0~34.7原子%であるが、これに限定されることはない。
一方、本実施形態に係るCu-Ga合金スパッタリングターゲットの製造方法は、上記した本発明に係るCu-Ga合金スパッタリングターゲットを製造する方法であって、純Cu粉末、Cu-Ga合金粉末及びNa化合物を混合した混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼結する工程を有している。即ち、このスパッタリングターゲットの製造方法では、純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼結するので、焼成中にそれぞれの原料粉から相互拡散が起こり、Cu-Ga合金のγ相が初相となるが、冷却の途中で、温度:450~650℃の範囲において、0.1~1.0℃/minの遅い冷却速度で焼成体を徐冷することにより、γ相中でγ1相が現われ、次いで、γ相が微細となり、他方で、γ1相が成長する。そのため、冷却された焼成体のCu-Ga合金粒内では、微細なγ相粒子がγ1相結晶粒内に分散した状態の結晶構造が得られる。
ここで、本発明による代表例として、Gaを35.0原子%含有したCu-Ga合金スパッタリングターゲットについて、X線回折(XRD)による回折ピークを測定した結果を、図2に示す。この結果からわかるように、Cu-Ga合金のγ相に帰属する回折ピークと、γ1相に帰属する回折ピークとの両方が観察される。
なお、X線回折(XRD)で使用した装置及び測定条件は下記の通りである。
・装置:理学電気社製(RINT-Ultima/PC)
・管球:Cu
・管電圧:40kV
・管電流:40mA
・走査範囲(2θ):40°~70°
・スリットサイズ:発散(DS)2/3度、散乱(SS)2/3度、受光(RS)0.8mm
・測定ステップ幅:2θで0.02度
・スキャンスピード:毎分1度
・試料台回転数:30rpm
図2の場合では、γ相に帰属する回折ピークの強度とγ1相に帰属する回折ピークの強度との比は約1:2となり、γ相とγ1相との2相が明確に組織中に形成されていることがわかる。
なお、X線回折(XRD)で使用した装置及び測定条件は下記の通りである。
・装置:理学電気社製(RINT-Ultima/PC)
・管球:Cu
・管電圧:40kV
・管電流:40mA
・走査範囲(2θ):40°~70°
・スリットサイズ:発散(DS)2/3度、散乱(SS)2/3度、受光(RS)0.8mm
・測定ステップ幅:2θで0.02度
・スキャンスピード:毎分1度
・試料台回転数:30rpm
図2の場合では、γ相に帰属する回折ピークの強度とγ1相に帰属する回折ピークの強度との比は約1:2となり、γ相とγ1相との2相が明確に組織中に形成されていることがわかる。
また、上記代表例のCu-Ga合金スパッタリングターゲットについて、電子線後方散乱回折法(EBSD)により取得した画像を図3に示す。実際のEBSD画像は、結晶粒に係る結晶方位の違いが色分けされたカラー画像であるが、図3に示す画像では、この色に応じて白黒の濃淡で表示されている。そのため、その濃淡で表された領域がγ1相の結晶粒を示している。このスパッタリングターゲットの焼結体における主相は、図1のCu-Ga合金に係る状態図から、低温でより安定なγ1相であると判断できる。この濃淡で表された領域、即ち、γ1相のCu-Ga合金粒の個々について観ると、各領域には、γ1相結晶粒の結晶方位とは異なる斑点状領域が分散している様子を観察することができる。即ち、γ1相結晶粒内に分散した斑点状領域が、高温でより安定なγ相の結晶粒を表している。
以上の結果から、本発明のCu-Ga合金スパッタリングターゲットは、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体からなり、微細なγ相粒子がγ1相結晶粒中に分散した組織を有することが確認された。
なお、塑性変形し易い純Cu粉末を原料に用いることで、成形体とする際に、形状保持が容易になる。また、純Cu粉末は室温大気中で酸化されるが、還元性雰囲気中での加熱で容易に還元されるため、酸素含有量を増加させる原因にはならない。さらに、50原子%GaのCu-Ga合金粉末を使用することで、焼結時に液相が発生し、高密度な焼成体が得られる。
本実施形態のCu-Ga合金スパッタリングターゲットには、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体である場合と、Ga:29.5~43.0原子%、さらに、Na:0.05~10.0原子%と、残部:Cu及び不可避不純物(Na化合物におけるNa以外の元素を含む)との組成を有する焼成体である場合とが含まれる。これらの焼成体の金属素地には、Cu-Ga合金のγ相及びγ1相がともに存在して、微細なγ相粒子がγ1相結晶粒中に分散した組織を有している。なお、Naを含有させた場合では、NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上からなるNa化合物相がCu-Ga合金粒の粒界に分散した組織を有している。本実施形態のCu-Ga合金スパッタリングターゲットの焼結体における主相(母相)は、γ1相の結晶組織を有している。
上記γ1相結晶粒の平均粒径は、スパッタリングターゲットから切り出した試料の表面を鏡面に研磨し、硝酸と純水とからなるエッチング液にてエッチングした後、結晶粒界を判別することができる倍率:50~1000倍の範囲内の光学顕微鏡にて顕微鏡写真を撮り、図4に示したように、得られた写真の1辺を11等分する10本の直線(白線で表示)を描き、この10本の直線が通過する結晶粒を計数し、下記計算式を用いて求めた。
平均粒径=(写真上の10本の線分の長さを実際の長さに補正した値)/(10本の線分が通過するγ1相結晶粒の数)
上記γ相粒子の平均粒子数についても、図4に示した写真の10本の直線を利用して、10本の線分が通過するγ相結晶粒の数を計数し、その数を10本の線分が通過するγ1相結晶粒の数で割ることにより求めた。
平均粒径=(写真上の10本の線分の長さを実際の長さに補正した値)/(10本の線分が通過するγ1相結晶粒の数)
上記γ相粒子の平均粒子数についても、図4に示した写真の10本の直線を利用して、10本の線分が通過するγ相結晶粒の数を計数し、その数を10本の線分が通過するγ1相結晶粒の数で割ることにより求めた。
上記Na化合物相の平均粒径についても、EPMAにより取得したNaの元素分布マッピング像に基づいて測定することができる。その像においては、白い領域がNaの存在を示しており、Na化合物相の大きさを表している。この白い領域をNa化合物粒子1個として、その占める面積S(μm2)を測定して求め、粒径D=(S/π)1/2の式から、当該Na化合物の粒径Dを求めた。そして、一辺100μmの正方形の領域10箇所中に観察されたNa化合物粒子の個数と粒径Dから平均粒径(Dの平均値)と最大粒径(Dの最大値)を算出した。
また、上記酸素含有量は、JIS Z 2613「金属材料の酸素定量方法通則」に記載された赤外線吸収法で測定した。
上記本実施形態のスパッタリングターゲットを製造する方法は、純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼結する工程を有している。
この製造方法の一例について詳述すると、先ず、マイクロトラックで測定したD50が2~3μmの純Cu粉と、D50が20~30μmのCu-Ga合金アトマイズ粉末とを、目標組成となるように秤量する。次に、ヘンシェルミキサーを用いてAr雰囲気下において回転数:2800rpmで1分間混合して、純Cu粉とCu-Ga合金アトマイズ粉末との混合粉末とする。なお、このCu-Ga合金アトマイズ粉末は、Gaの濃度が50原子%となるようにガスアトマイズ装置内で溶解し、Arガスでアトマイズすることによって製造される。
この製造方法の一例について詳述すると、先ず、マイクロトラックで測定したD50が2~3μmの純Cu粉と、D50が20~30μmのCu-Ga合金アトマイズ粉末とを、目標組成となるように秤量する。次に、ヘンシェルミキサーを用いてAr雰囲気下において回転数:2800rpmで1分間混合して、純Cu粉とCu-Ga合金アトマイズ粉末との混合粉末とする。なお、このCu-Ga合金アトマイズ粉末は、Gaの濃度が50原子%となるようにガスアトマイズ装置内で溶解し、Arガスでアトマイズすることによって製造される。
次に、得られた混合粉末を、500~2000kgf/cm2の成型圧で圧粉体(成形体)とする。この圧粉体を炉中に配し、10~100L/minで還元性ガスを流しつつ、700~1000℃の焼成温度まで10℃/minで加熱し、5時間保持する。この後、温度:450~650℃の範囲において、450℃の温度まで、0.1~1.0℃/minの冷却速度で冷却し、自然冷却させる。焼成温度から450℃までの冷却過程において、上記の冷却速度にすることによりγ相の微細な組織を発生させている。得られた焼成体の表面部と外周部とを旋盤加工して、直径50mm、厚み6mmのスパッタリングターゲットを作製する。
次に、加工後のスパッタリングターゲットを、Cu製のバッキングプレートにボンディングする。このように作製したCu-Ga合金スパッタリングターゲットは、Arガスをスパッタガスとした直流(DC)マグネトロンスパッタ装置に供される。
なお、Naが添加された場合のCu-Ga合金スパッタリングターゲットについては、上記の混合粉末に、目標組成となるように秤量したNa化合物を加えられる以外は、Naが添加されない場合と同様の手順により製造される。
なお、Naが添加された場合のCu-Ga合金スパッタリングターゲットについては、上記の混合粉末に、目標組成となるように秤量したNa化合物を加えられる以外は、Naが添加されない場合と同様の手順により製造される。
この本実施形態のCu-Ga合金スパッタリングターゲットは、Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体であって、該焼成体におけるCu-Ga合金結晶粒は、γ相粒子がγ1相結晶粒中に分散した組織を有している。特に、前記γ相粒子の平均粒子数が、6~36個であり、前記γ1相結晶粒の平均粒径が、15.0~75.0μmであるので、微細なγ相粒がγ1相中に均一に分散した組織となることにより、パーティクル発生を低減することができ、異常放電が大幅に低減される。
また、前記焼成体は、さらに、Na:0.05~10.0原子%を含有し、焼成体中には、NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上からなるNa化合物相が分散しており、酸素含有量が200質量ppm以下に抑えられている。そのため、スパッタリングで得られるプリカーサ膜中の酸素量の増大を抑制することにより、CIGS薄膜型太陽電池の光吸収層中の光電変換効率の向上に寄与することができる。
また、本実施形態のスパッタリングターゲットの製造方法では、純Cu粉末とCu-Ga合金粉末との混合粉末、或いは、純Cu粉末とCu-Ga合金粉末とNa化合物との混合粉末からなる成形体を還元性雰囲気中で加熱し、常圧焼成して焼成体を得た後、該焼成体の冷却過程で、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する。この温度範囲では、通常の冷却速度より遅いため、図1に示したCu-Ga系状態図からも分かるように、最初、Cu-Ga合金の主相はγ相であるが、温度が低くなるにつれて、このγ相中にγ1相が出現し、温度がさらに低くなると、γ1相がγ相中で大きく成長する。ここで、冷却速度を通常の速さにすることにより、微細なγ相粒子がγ1相結晶粒中に分散した組織を維持して冷却される。この様にして、焼成体におけるγ相粒子がγ1相結晶粒中に分散した組織を有するCu-Ga合金結晶粒からなる焼成体が得られる。
次に、本発明に係るスパッタリングターゲット及びその製造方法を、上記実施形態に基づき作製した実施例により、評価した結果を説明する。
先ず、Gaの濃度が50原子%のCu-Ga合金アトマイズ粉末(表中のCuGa粉)と、純Cu粉末と、Na化合物(NaF、Na2S、Na2Se、Na2AlF6)とを、表1に示される重量比率になるように配合し、実施例1~13の混合粉末とした。次に、得られた混合粉末を、1500kgf/cm2の成型圧で圧粉体(成形体)とした。さらに、表2に示されるように、これらの混合粉末のうち、実施例1~9は水素雰囲気中で常圧焼結させ、また、実施例10、11は一酸化炭素雰囲気中で常圧焼結させ、さらに実施例12、13はアンモニア分解ガス雰囲気中で常圧焼結させた。これらの常圧焼結は、50L/minで還元性ガスを流しつつ、840℃の焼成温度で5時間保持して行った。この焼成後の焼成体の冷却過程では、温度:450~650℃の範囲において、表2に示される冷却速度で冷却し、その温度範囲より低温になった後には、自然冷却を行った。
一方、比較例として、Gaの濃度が50原子%のCu-Ga合金アトマイズ粉末(表中のCuGa粉)と、Cu粉末と、Na化合物を、表1に示される重量比率になるように配合し、比較例1~5の混合粉末とした。なお、比較例3、4では、Gaの含有量が本発明の範囲から外れるように、Cu-Ga合金粉末を配合し、比較例5では、Na化合物を過剰に配合した。次に、得られた混合粉末を、上記実施例と同様に圧粉体(成形体)とした。
さらに、表2に示されるように、比較例1~5は水素雰囲気中で常圧焼結させ、温度:450~650℃の範囲において、表2に示される冷却速度で冷却し、この温度範囲より低温になった後には、自然冷却を行った。このうち比較例1、2は、冷却速度が本発明の範囲から外れた値とした。
なお、表2には、実施例1~13及び比較例1~5のスパッタリングターゲットについて、Ga、Na、Cuに関する組成分析の結果を、「ターゲット組成(原子%)」欄に示した。このターゲットの組成は、ICP法(高周波誘導結合プラズマ法)を用いて測定した。
なお、表2には、実施例1~13及び比較例1~5のスパッタリングターゲットについて、Ga、Na、Cuに関する組成分析の結果を、「ターゲット組成(原子%)」欄に示した。このターゲットの組成は、ICP法(高周波誘導結合プラズマ法)を用いて測定した。
上記で作製した実施例1~13及び比較例1~5のCu-Ga合金スパッタリングターゲットについて、母相(マトリクス相)の平均粒径、γ相の平均分散粒子数、酸素含有量を測定し、さらに、スパッタリング時の異常放電回数を測定した。
<マトリクス相平均粒径>
母相(マトリクス相)であるγ1相結晶粒の平均粒径は、スパッタリングターゲットから切り出した試料の表面を鏡面に研磨し、硝酸と純水とからなるエッチング液にてエッチングした後、結晶粒界を判別することができる倍率:50~1000倍の範囲内の光学顕微鏡にて顕微鏡写真を撮り、図4に示したように、得られた写真の1辺を11等分する10本の直線(白線で表示)を描き、この10本の直線が通過する結晶粒を計数し、下記計算式を用いて求めた。
(平均粒径)=(写真上の10本の線分の長さを実際の長さに補正した値)/(10本の線分が通過するγ1相結晶粒の数)
γ相粒子の平均分散粒子数についても、図4に示した写真の10本の直線を利用して、10本の線分が通過するγ相結晶粒の数を計数し、その数を10本の線分が通過するγ1相結晶粒の数で割ることにより求めた。
以上の測定結果を、表3の「マトリクス相平均粒径(μm)」欄、「平均分散粒子数(個)」欄に示した。なお、γ相が存在しない場合には、「なし」と表記し、γ相結晶粒の粒径が小さいため、計測できない場合には、「観察不能」と表記した。
母相(マトリクス相)であるγ1相結晶粒の平均粒径は、スパッタリングターゲットから切り出した試料の表面を鏡面に研磨し、硝酸と純水とからなるエッチング液にてエッチングした後、結晶粒界を判別することができる倍率:50~1000倍の範囲内の光学顕微鏡にて顕微鏡写真を撮り、図4に示したように、得られた写真の1辺を11等分する10本の直線(白線で表示)を描き、この10本の直線が通過する結晶粒を計数し、下記計算式を用いて求めた。
(平均粒径)=(写真上の10本の線分の長さを実際の長さに補正した値)/(10本の線分が通過するγ1相結晶粒の数)
γ相粒子の平均分散粒子数についても、図4に示した写真の10本の直線を利用して、10本の線分が通過するγ相結晶粒の数を計数し、その数を10本の線分が通過するγ1相結晶粒の数で割ることにより求めた。
以上の測定結果を、表3の「マトリクス相平均粒径(μm)」欄、「平均分散粒子数(個)」欄に示した。なお、γ相が存在しない場合には、「なし」と表記し、γ相結晶粒の粒径が小さいため、計測できない場合には、「観察不能」と表記した。
<酸素含有量>
酸素含有量については、JIS Z 2613「金属材料の酸素定量方法通則」に記載された赤外線吸収法で測定した。その結果を、表3の「酸素量(質量ppm)」欄に示した。
酸素含有量については、JIS Z 2613「金属材料の酸素定量方法通則」に記載された赤外線吸収法で測定した。その結果を、表3の「酸素量(質量ppm)」欄に示した。
<異常放電回数>
スパッタリング時の異常放電については、下記の成膜条件で12時間スパッタリングを行い、異常放電の回数を測定した。
・電源:パルスDC500W
・全圧:0.4Pa
・スパッタガス:Ar=47.5sccm、O2:2.5sccm
・ターゲット-基板(TS)距離:70mm
異常放電回数は、MKSインスツルメンツ社製DC電源(型番:RPDG-50A)のアークカウント機能により計測した。
その測定結果を、表3の「異常放電(回)」欄に示した。
スパッタリング時の異常放電については、下記の成膜条件で12時間スパッタリングを行い、異常放電の回数を測定した。
・電源:パルスDC500W
・全圧:0.4Pa
・スパッタガス:Ar=47.5sccm、O2:2.5sccm
・ターゲット-基板(TS)距離:70mm
異常放電回数は、MKSインスツルメンツ社製DC電源(型番:RPDG-50A)のアークカウント機能により計測した。
その測定結果を、表3の「異常放電(回)」欄に示した。
表3に示された結果によれば、実施例1~13のCu-Ga合金スパッタリングターゲットのいずれにおいても、Cu-Ga合金のγ1相に係る平均粒径は、15.0~75.0μmの範囲内にあり、Cu-Ga合金のγ相粒子に係る平均分散粒子数は、6~36個の範囲内にあって、Cu-Ga合金スパッタリングターゲットにおける母相がγ1相粒子で構成され、この母相中に微細なγ相粒子が分散された組織を有しており、しかも、スパッタリング時の異常放電発生が皆無であることが確認された。さらに、実施例3~13のCu-Ga合金スパッタリングターゲットのいずれにおいても、Naが添加された場合であるが、ターゲット中の酸素含有量が、200ppm以下に低減されていることも確認された。
一方、比較例1の場合では、冷却速度が大きいため、γ1相粒子中のγ相粒子の生成が確認されず、異常放電が発生した。比較例2の場合では、冷却速度が小さ過ぎため、γ1相の平均粒径が大きくなってしまい、微細なγ相粒子が分散されても、異常放電が発生した。比較例3の場合では、Gaが不足したため、或いは、比較例4の場合では、Gaが過剰であったため、いずれの場合も、γ1相粒子中のγ相粒子の存在を観察できないほど小さく、異常放電が発生した。比較例5の場合では、Naの添加が過剰であったため、Na酸化物相の分散が、γ1相粒子の平均粒径を小さくする結果となった。しかも、比較例5の場合では、γ1相粒子中のγ相粒子の存在が観察できないほど小さく、γ1相粒子中のγ相粒子の生成も確認されず、異常放電が発生した。
以上の様に、本発明による高濃度Ga成分のCu-Ga合金焼成体におけるCu-Ga合金結晶粒は、微細なγ相粒子がγ1相結晶粒中に分散した組織を有していることが確認され、Cu-Ga合金スパッタリングターゲットにおける母相がγ1相で構成され、この母相中に微細なγ相粒子が分散されることにより、ターゲット脆性を改善でき、しかも、スパッタリング時のパーティクル発生を低減できることが分かった。さらに、前記焼成体中に、Na化合物(NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上)相を分散させたCu-Ga合金スパッタリングターゲットにおいても、母相がγ1相で構成されて脆性を改善でき、しかも、スパッタリング時のパーティクル発生を低減し、ターゲット中の酸素含有量をさらに低減可能であると共に、高濃度のNaを含有しつつも、異常放電を一層抑制することができることが分かった。
本発明のCu-Ga合金スパッタリングターゲットによれば、パーティクル発生を低減でき、酸素含有量をさらに低減可能であると共に、高濃度のNaを含有しつつも、異常放電を一層抑制することができる。また、本発明のCu-Ga合金スパッタリングターゲットによれば、CIGS薄膜型太陽電池の光吸収層中の光電変換効率の向上に寄与することができる。
Claims (7)
- Ga:29.5~43.0原子%と、残部:Cu及び不可避不純物との組成を有する焼成体であって、
前記焼成体におけるCu-Ga合金結晶粒は、γ相粒子がγ1相結晶粒中に分散した組織を有するCu-Ga合金スパッタリングターゲット。 - 前記γ相の平均粒子数が、一つのγ1結晶粒中に6~36個であり、
前記γ1相の平均粒径が、15.0~75.0μmである請求項1に記載のCu-Ga合金スパッタリングターゲット。 - 前記焼成体の酸素量が200質量ppm以下である請求項1又は2に記載のCu-Ga合金スパッタリングターゲット。
- 前記焼成体は、さらに、Na:0.05~10.0原子%を含有し、
前記焼成体中に、Na化合物相が分散している請求項1から3のいずれかに記載のCu-Ga合金スパッタリングターゲット。 - 前記Na化合物相は、NaF、Na2S、Na2Se及びNa3AlF6の少なくとも1種以上からなる請求項4に記載のCu-Ga合金スパッタリングターゲット。
- 請求項1から3のいずれかに記載のCu-Ga合金スパッタリングターゲットを製造する方法であって、
純Cu粉末とCu-Ga合金粉末との混合粉末からなる成形体を、還元性雰囲気中で、還元性雰囲気中で加熱して常圧焼成する工程と、
得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程と、
を有するCu-Ga合金スパッタリングターゲットの製造方法。 - 請求項4又は5に記載のCu-Ga合金スパッタリングターゲットを製造する方法であって、
純Cu粉末、Cu-Ga合金粉末及びNa化合物との混合粉末からなる成形体を、還元性雰囲気中で加熱して常圧焼成する工程と、
得られた焼成体を、温度:450~650℃の範囲において、0.1~1.0℃/minの冷却速度で冷却する工程と、
を有するCu-Ga合金スパッタリングターゲットの製造方法。