WO2015060371A1 - 針状ころ軸受用保持器及び針状ころ軸受 - Google Patents
針状ころ軸受用保持器及び針状ころ軸受 Download PDFInfo
- Publication number
- WO2015060371A1 WO2015060371A1 PCT/JP2014/078154 JP2014078154W WO2015060371A1 WO 2015060371 A1 WO2015060371 A1 WO 2015060371A1 JP 2014078154 W JP2014078154 W JP 2014078154W WO 2015060371 A1 WO2015060371 A1 WO 2015060371A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- needle roller
- roller bearing
- phosphate
- planetary gear
- solid lubricant
- Prior art date
Abstract
Description
(1)遊星歯車機構の遊星歯車を回転自在に支持する針状ころ軸受用保持器であって、
環状部と、前記環状部から軸線方向に延在する複数の柱部とを有し、隣接する前記柱部間でころを保持し、かつ、外輪案内で用いられるとともに、
リン酸塩と、軟質金属系固体潤滑剤及び層状結晶構造物質から選ばれる固体潤滑剤とを含有する複合皮膜、またはリン酸塩と、軟質金属を含むリン酸化合物とを含有する複合皮膜が、少なくとも外周面に形成されていることを特徴とする針状ころ軸受用保持器。
(2)固体潤滑剤がスズ、二硫化モリブデンまたは銅であることを特徴とする上記(1)記載の針状ころ軸受用保持器。
(3)軟質金属を含むリン酸化合物がリン酸スズであることを特徴とする上記(1)記載の針状ころ軸受用保持器。
(4)固体潤滑剤または軟質金属を含むリン酸化合物の複合皮膜中の含有量が0.1~70質量%であることを特徴とする上記(1)~(3)の何れか1項に記載の針状ころ軸受用保持器。
(5)リン酸塩がリン酸マンガンであることを特徴とする上記(1)~(4)の何れか1項に記載の針状ころ軸受用保持器。
(6)遊星歯車機構の遊星歯車を回転自在に支持する針状ころ軸受であって、
上記(1)~(5)の何れか1項に記載の保持器を備え、外輪案内型であることを特徴とする針状ころ軸受。
SCM415材を加工して、図5に示すような針状ころ軸受用保持器を作製し、更に浸炭窒化処理を施した。そして、表1に示すように、比較例2ではリン酸マンガン皮膜、実施例1~4ではリン酸マンガンとリン酸スズとの複合皮膜を形成して試験保持器とした。尚、比較例1では皮膜を設けず、そのままSCM415製の試験保持器を試験保持器とした。
・条件A
キャリア公転数:7600min-1
ピニオン自転数:9300min-1
潤滑油:ATF
潤滑油供給量:0.03L/min/ピニオン
油温:120℃
試験時間:200時間
・条件B
キャリア公転数:8000min-1
ピニオン自転数:13500min-1
潤滑油:ATF
潤滑油供給量:0.03L/min/ピニオン
油温:120℃
試験時間:200時間
リン酸スズを二硫化モリブデンに代え、リン酸マンガンとの複合皮膜にした以外は、実施例1~4と同様にして試験保持器を作製した。
本出願は、2013年10月25日出願の日本特許出願(特願2013-222542)に基づくものであり、その内容はここに参照として取り込まれる。
4~6 遊星歯車機構
10 針状ころ軸受
11 ころ
12 保持器
Claims (6)
- 遊星歯車機構の遊星歯車を回転自在に支持する針状ころ軸受用保持器であって、
環状部と、前記環状部から軸線方向に延在する複数の柱部とを有し、隣接する前記柱部間でころを保持し、かつ、外輪案内で用いられるとともに、
リン酸塩と、軟質金属系固体潤滑剤及び層状結晶構造物質から選ばれる固体潤滑剤とを含有する複合皮膜、またはリン酸塩と、軟質金属を含むリン酸化合物とを含有する複合皮膜が、少なくとも外周面に形成されていることを特徴とする針状ころ軸受用保持器。 - 固体潤滑剤がスズ、二硫化モリブデンまたは銅であることを特徴とする請求項1記載の針状ころ軸受用保持器。
- 軟質金属を含むリン酸化合物がリン酸スズであることを特徴とする請求項1記載の針状ころ軸受用保持器。
- 固体潤滑剤または軟質金属を含むリン酸化合物の複合皮膜中の含有量が0.1~70質量%であることを特徴とする請求項1~3の何れか1項に記載の針状ころ軸受用保持器。
- リン酸塩がリン酸マンガンであることを特徴とする請求項1~4の何れか1項に記載の針状ころ軸受用保持器。
- 遊星歯車機構の遊星歯車を回転自在に支持する針状ころ軸受であって、
請求項1~5の何れか1項に記載の保持器を備え、外輪案内型であることを特徴とする針状ころ軸受。