WO2015002398A1 - Procédé de fabrication d'une cellule solaire de type ewt - Google Patents
Procédé de fabrication d'une cellule solaire de type ewt Download PDFInfo
- Publication number
- WO2015002398A1 WO2015002398A1 PCT/KR2014/005487 KR2014005487W WO2015002398A1 WO 2015002398 A1 WO2015002398 A1 WO 2015002398A1 KR 2014005487 W KR2014005487 W KR 2014005487W WO 2015002398 A1 WO2015002398 A1 WO 2015002398A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- emitter
- solar cell
- type
- preparing
- Prior art date
Abstract
L'invention porte sur un procédé pour fabriquer une cellule solaire de type EWT («emitter wrap through»). Selon le procédé pour fabriquer une cellule solaire de type EWT, puisqu'une implantation ionique peut être appliquée pour la formation d'une couche d'émetteur, un processus d'isolation de bord peut être omis simplifiant ainsi davantage le processus de fabrication, et il est avantageux pour la formation d'un émetteur peu profond, d'un émetteur sélectif et analogue, fournissant ainsi un type à contact arrière à efficacité élevée de cellule solaire.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2013-0077252 | 2013-07-02 | ||
KR20130077252A KR20150004488A (ko) | 2013-07-02 | 2013-07-02 | 에미터 랩 스루 타입 태양 전지의 제조 방법 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2015002398A1 true WO2015002398A1 (fr) | 2015-01-08 |
Family
ID=52143943
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2014/005487 WO2015002398A1 (fr) | 2013-07-02 | 2014-06-20 | Procédé de fabrication d'une cellule solaire de type ewt |
Country Status (3)
Country | Link |
---|---|
KR (1) | KR20150004488A (fr) |
TW (1) | TW201503384A (fr) |
WO (1) | WO2015002398A1 (fr) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9525083B2 (en) * | 2015-03-27 | 2016-12-20 | Sunpower Corporation | Solar cell emitter region fabrication with differentiated P-type and N-type architectures and incorporating a multi-purpose passivation and contact layer |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0881694A1 (fr) * | 1997-05-30 | 1998-12-02 | Interuniversitair Micro-Elektronica Centrum Vzw | Cellule solaire et méthode de fabrication |
KR20100098993A (ko) * | 2009-03-02 | 2010-09-10 | 엘지전자 주식회사 | 태양 전지 및 그 제조 방법 |
WO2012108767A2 (fr) * | 2011-02-08 | 2012-08-16 | Tsc Solar B.V. | Procédé de fabrication d'une cellule solaire et cellule solaire ainsi produite |
US20120227794A1 (en) * | 2009-09-18 | 2012-09-13 | Applied Materials, Inc. | Threshold adjustment implants for reducing surface recombination in solar cells |
US20130139871A1 (en) * | 2010-09-29 | 2013-06-06 | Kyocera Corporation | Solar cell module and method of manufacturing solar cell module |
-
2013
- 2013-07-02 KR KR20130077252A patent/KR20150004488A/ko not_active Application Discontinuation
-
2014
- 2014-06-20 WO PCT/KR2014/005487 patent/WO2015002398A1/fr active Application Filing
- 2014-07-01 TW TW103122725A patent/TW201503384A/zh unknown
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0881694A1 (fr) * | 1997-05-30 | 1998-12-02 | Interuniversitair Micro-Elektronica Centrum Vzw | Cellule solaire et méthode de fabrication |
KR20100098993A (ko) * | 2009-03-02 | 2010-09-10 | 엘지전자 주식회사 | 태양 전지 및 그 제조 방법 |
US20120227794A1 (en) * | 2009-09-18 | 2012-09-13 | Applied Materials, Inc. | Threshold adjustment implants for reducing surface recombination in solar cells |
US20130139871A1 (en) * | 2010-09-29 | 2013-06-06 | Kyocera Corporation | Solar cell module and method of manufacturing solar cell module |
WO2012108767A2 (fr) * | 2011-02-08 | 2012-08-16 | Tsc Solar B.V. | Procédé de fabrication d'une cellule solaire et cellule solaire ainsi produite |
Also Published As
Publication number | Publication date |
---|---|
TW201503384A (zh) | 2015-01-16 |
KR20150004488A (ko) | 2015-01-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2018147739A1 (fr) | Procédé de fabrication d'une cellule solaire passivée et cellule solaire passivée ainsi obtenue | |
JP5518212B2 (ja) | 裏面電極型の太陽電池の製造方法 | |
EP2356687B1 (fr) | Cellules solaires photovoltaïques à gorge profonde | |
US9412895B2 (en) | Method of manufacturing photoelectric device | |
JP2022501837A (ja) | 結晶シリコン太陽電池およびその製造方法 | |
US20100120191A1 (en) | Method of forming front contacts to a silicon solar cell wiithout patterning | |
US9666734B2 (en) | Emitter wrap-through solar cell and method of preparing the same | |
EP2810303A2 (fr) | Procédé permettant de former une cellule solaire dotée d'un émetteur sélectif | |
TW201635349A (zh) | 半導體之雷射掺雜 | |
TW201635348A (zh) | 掺雜半導體之方法 | |
CN104362219B (zh) | 一种晶体硅太阳能电池制造工艺 | |
JP6426486B2 (ja) | 太陽電池素子の製造方法 | |
US20130143353A1 (en) | Patterned implant of a dielectric layer | |
US9330917B2 (en) | Passivation layer for workpieces formed from a polymer | |
KR101160114B1 (ko) | 함몰전극형 태양전지의 제조방법 | |
KR20090050756A (ko) | 기판형 태양전지 및 그 제조방법 | |
WO2015002398A1 (fr) | Procédé de fabrication d'une cellule solaire de type ewt | |
CN104205363B (zh) | 制造太阳能电池的方法及其设备 | |
CN103828069B (zh) | 掺杂方法、pn结构、太阳能电池的制作方法及太阳能电池 | |
WO2014071458A1 (fr) | Formation de contacts métalliques | |
Liu et al. | Aluminum local back surface field solar cells with inkjet-opened rear dielectric films | |
KR20120129292A (ko) | 태양 전지의 제조 방법 | |
KR101367405B1 (ko) | 에미터 스루 태양 전지 및 이의 제조 방법 | |
KR101103144B1 (ko) | 후면전극형 태양전지 제조 방법 | |
CN114093980A (zh) | 一种叉指背接触电池的制作方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14819969 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 14819969 Country of ref document: EP Kind code of ref document: A1 |