WO2014157963A1 - Resin composition for polarizer protecting film, polarizer protecting film, polarizing plate comprising same, and method for manufacturing polarizing plate - Google Patents

Resin composition for polarizer protecting film, polarizer protecting film, polarizing plate comprising same, and method for manufacturing polarizing plate Download PDF

Info

Publication number
WO2014157963A1
WO2014157963A1 PCT/KR2014/002614 KR2014002614W WO2014157963A1 WO 2014157963 A1 WO2014157963 A1 WO 2014157963A1 KR 2014002614 W KR2014002614 W KR 2014002614W WO 2014157963 A1 WO2014157963 A1 WO 2014157963A1
Authority
WO
WIPO (PCT)
Prior art keywords
protective film
polarizer
polarizing plate
resin composition
fine particles
Prior art date
Application number
PCT/KR2014/002614
Other languages
French (fr)
Korean (ko)
Inventor
김혜민
장영래
김헌
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020140035588A external-priority patent/KR101600584B1/en
Priority claimed from KR1020140035589A external-priority patent/KR101586845B1/en
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to US14/780,957 priority Critical patent/US10473825B2/en
Priority to CN201480018913.4A priority patent/CN105102490B/en
Priority to JP2016505400A priority patent/JP2016522838A/en
Publication of WO2014157963A1 publication Critical patent/WO2014157963A1/en
Priority to US16/591,085 priority patent/US11125918B2/en

Abstract

The present invention relates to a resin composition for a polarizer protecting film, a polarizer protecting film, a polarizing plate comprising the same, and a method for manufacturing the polarizing plate and, more particularly, to a resin composition for a polarizer protecting film exhibiting high hardness and excellent characteristics, a polarizer protecting film, a polarizing plate comprising the same, and a method for manufacturing the polarizing plate. The polarizing plate of the present invention exhibits excellent hardness, flexibility, and optical characteristics, and thus can be useful in various fields.

Description

【명세서】  【Specification】
【발명의 명칭】  [Name of invention]
편광자 보호 필름용 수지 조성물, 편광자 보호 필름, 이를 포함하는 편광판 및 편광판의 제조방법  Resin composition for polarizer protective film, polarizer protective film, polarizing plate containing same and manufacturing method of polarizing plate
【기술분야】  Technical Field
본 발명은 편광자 보호 필름용 수지 조성물， 편광자 보호 필름, 이를 포함하는 편광판 및 편광판의 제조방법에 관한 것이다. 보다 상세하게는, 우수한 물리적, 광학적 특성을 나타내는 편광자 보호 필름용 수지 조성물， 편광자 보호 필름, 이를 포함하는 편광판 및 편광판의 제조방법에 관한 것이다.  The present invention relates to a resin composition for a polarizer protective film, a polarizer protective film, a polarizing plate including the same, and a manufacturing method of the polarizing plate. More specifically, the present invention relates to a resin composition for a polarizer protective film, a polarizer protective film, a polarizing plate including the same, and a manufacturing method of the polarizing plate, which exhibits excellent physical and optical properties.
본 출원은 2013년 3월 27일에 한국특허청에 제출된 한국 특허 출원 제 10-2013-0033002호, 2013년 3월 27일에 한국특허청에 제출된 한국 특허 출원 제 10-2013-0033004호, 2014년 3월 26일에 한국특허청에 제출된 한국 특허 출원 제 10-2014-0035588호, 및 2014년 3월 26일에 한국특허청에 제출된 한국 특허 출원 제 10-2014-0035589호의 출원일의 이익을 주장하며, 그 내용 전부는 본 명세서에 포함된다.  This application is filed with Korean Patent Application No. 10-2013-0033002, filed with the Korean Patent Office on March 27, 2013, and Korean Patent Application No. 10-2013-0033004, 2014, filed with the Korean Patent Office on March 27, 2013. Claims the benefits of Korean Patent Application No. 10-2014-0035588 filed with the Korean Patent Office on March 26, 2014, and Korean Patent Application No. 10-2014-0035589 filed with the Korean Patent Office on March 26, 2014 All of the content is included in this specification.
【배경기술】  Background Art
액정 디스플레이 (liquid crystal display, LCD)는 현재 가장 널리 사용되고 있는 평판 디스플레이 증 하나이다. 일반적으로 액정 디스플레이는 TFT(Thin Film Transistor) 어레이 기판과 칼라필터 기판 사이에 액정층이 봉입된 구조를 취한다. 상기 어레이 기판과 칼라필터 기판에 존재하는 전극에 전기장을 인가하면 그 사이에 봉입된 액정층의 액정 분자의 배열이 변하게 되고 이를 이용해 영상을 표시하게 된다.  Liquid crystal displays (LCDs) are one of the most widely used flat panel displays. In general, a liquid crystal display has a structure in which a liquid crystal layer is enclosed between a thin film transistor (TFT) array substrate and a color filter substrate. When an electric field is applied to the electrodes on the array substrate and the color filter substrate, the arrangement of the liquid crystal molecules of the liquid crystal layer enclosed therebetween is changed to display an image by using the electric field.
한편, 어레이 기판과 칼라필터 기판의 외측에는 편광판이 구비되어 있다. 편광판은 백라이트로부터 입사되는 빛 및 액정층을 통과한 빛 중 특정 방향의 빛을 선택적으로 투과함으로써 편광을 제어할 수 있다.  On the other hand, the polarizing plate is provided outside the array substrate and the color filter substrate. The polarizer may control polarization by selectively transmitting light in a specific direction among light incident from the backlight and light passing through the liquid crystal layer.
편광판은 일반적으로 빛을 특정 방향으로 편광시킬 수 있는 편광자 (polarizer)에， 상기 편광자를 지지 및 보호하기 위한 보호 필름을 접착시킨 구조로 이루어진다.  The polarizing plate generally has a structure in which a protective film for supporting and protecting the polarizer is adhered to a polarizer capable of polarizing light in a specific direction.
상기 보호 필름으로는, 트리아세틸셀를로오스 (TAC)로 이루어진 필름이 널리 이용되고 있다. 또한, 고경도 및 내마모성의 특성을 갖는 필름을 달성하기 위해 하드코팅 층올 코팅하는 보호 필름이 제안되고 있다. 한편, 요즘에는 액정 장치의 용도가 광범위해져 여러 분야의 장치에 사용되고 있어， 편광판의 경도의 향상 및 박형화에 대한 관심이 높아지고 있다. As said protective film, it consists of triacetyl cellulose (TAC). Films are widely used. In addition, a protective film for coating a hard coat layer in order to achieve a film having properties of high hardness and wear resistance has been proposed. On the other hand, these days, the use of liquid crystal devices has become widespread, and they are used in devices of various fields, and interest in improving the hardness and thinning of polarizing plates is increasing.
이러한 필요성에 대하여 TAC 필름을 생략하고, 편광자의 표면에 광중합성 화합물을 이용하여 보호층을 형성한 편광판이 일본 공개특허공보 2005-010329호 등에 제안되어 있다. 그러나， 층분한 경도를 가지며 박형화가 가능하도록 낮은 두께를 나타내며 대량 생산 공정에 적합하도록 층분한 가요성을 나타내는 편광판에 대해서 여전히 개발이 요구되고 있다.  For this necessity, a polarizing plate in which a TAC film is omitted and a protective layer is formed on the surface of the polarizer using a photopolymerizable compound is proposed in JP-A-2005-010329 and the like. However, there is still a need for development of a polarizing plate having a layered hardness, a low thickness to enable thinness, and a layered flexibility to be suitable for a mass production process.
【발명의 내용】  [Content of invention]
【해결하고자 하는 과제】  Problem to be solved
상기와 같은 과제를 해결하기 위하여, 본 발명은 고경도 및 고투명도를 나타내고 박형화가 가능하며, 동시에 우수한 가요성을 나타내어 컬 또는 크렉이 발생하지 않는 편광자 보호 필름용 수지 조성물, 편광자 보호용 필름, 이를 포함하는 편광판 및 편광판의 제조방법을 제공한다.  In order to solve the above problems, the present invention exhibits high hardness and high transparency, and can be thinned, and at the same time exhibits excellent flexibility, a resin composition for a polarizer protective film that does not generate curl or crack, a polarizer protective film, and the like. It provides a polarizing plate and a manufacturing method of a polarizing plate.
【과제의 해결 수단】  [Measures of problem]
상기와 같은 문제를 해결하기 위해서 본 발명은, 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머를 포함하는 바인더; 및 광 개시제를 포함하는 수지 조성물을 제공한다.  In order to solve the above problems, the present invention is a binder comprising a polyfunctional acrylate monomer, and an acrylate oligomer having an elongation of 5 to 200%; And a photoinitiator.
또한, 본 발명은, 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함하는 편광자 보호필름을 제공한다.  The present invention also provides a polarizer protective film comprising a cured resin with a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%.
또한 본 발명은， 편광자; 및 상기 편광자의 적어도 일 면에 구비되는 보호필름을 포함하며, 상기 보호 필름은 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함하는 편광판을 제공한다.  In addition, the present invention, a polarizer; And a protective film provided on at least one surface of the polarizer, wherein the protective film provides a polarizing plate including a curable resin with a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%. .
또한, 본 발명은 이형 필름 상에 다관능 아크릴레이트계 모노머， 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머를 포함하는 바인더; 및 광 개시제를 포함하는 수지 조성물을 도포하는 단계; In addition, the present invention is a binder comprising a polyfunctional acrylate monomer, and an acrylate oligomer having an elongation of 5 to 200% on a release film; And Applying a resin composition comprising a photoinitiator;
상기 도포된 '수지 조성물을 광경화하여 보호 필름을 형성하는 단계; 편광자의 일 면에 상기 보호 필름을 라미네이트하여 접착시키는 단계를 포함하는 편광판의 제조방법을 제공한다. A step of applying a flower spectacle the "resin composition forming a protective film; It provides a method of manufacturing a polarizing plate comprising the step of laminating and bonding the protective film on one side of the polarizer.
【발명의 효과】  【Effects of the Invention】
본 발명의 편광자 보호필름에 따르면, 고경도， 내찰상성, 고투명도를 나타내며 우수한 가공성으로 컬 또는 크택이 발생하지 않아 각종 디스플레이 기기에 유용하게 적용할 수 있으며, TAC 필름과 같은 기재 필름에 별도의 코팅없이 적용하여 박형화가 가능하다. 특히, 연신 필름을 포함하지 않으므로, 위상차값이 실질적으로 0에 가까울 정도로 낮아 편광자 보호용 필름뿐 아니라, 이러한 낮은 위상차값이 요구되는 각종 디바이스에 용도의 제한없이 사용될 수 있다. ' According to the polarizer protective film of the present invention, it exhibits high hardness, scratch resistance, high transparency and can be usefully applied to various display devices because it does not generate curl or crtack due to excellent processability, and is separately coated on a base film such as a TAC film. It can be made thin without any application. In particular, since it does not include a stretched film, the retardation value is low enough to be substantially close to zero, and can be used for various devices in which such a low retardation value is required, as well as the polarizer protective film, without limitation of use. '
또한, 우수한 가공성 및 가요성을 나타내어 대면적 또는 곡면 디스플레이에도 적용이 가능한 장점이 있다.  In addition, there is an advantage that can be applied to large area or curved display by showing excellent processability and flexibility.
【발명을 실시하기 위한 구체적인 내용】  [Specific contents to carry out invention]
본 발명의 수지 조성물은, 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머를 포함하는 바인더; 및 광 개시제를 포함한다.  The resin composition of the present invention is a binder comprising a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%; And photoinitiators.
본 발명의 편광자 보호 필름은, 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머와의 경화 수지를 포함한다.  The polarizer protective film of the present invention contains a polyfunctional acrylate monomer and a cured resin with an acrylate oligomer having an elongation of 5 to 200%.
본 발명의 편광판은， 편광자; 상기 편광자의 적어도 일 면에 구비되는 보호 필름을 포함하며, 상기 보호 필름은 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머와의 경화 수지를 포함한다.  Polarizing plate of the present invention, a polarizer; And a protective film provided on at least one surface of the polarizer, wherein the protective film includes a polyfunctional acrylate monomer and a cured resin with an acrylate oligomer having an elongation of 5 to 200%.
본 발명의 편광판의 제조방법은, 이형 필름 상에 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머를 포함하는 바인더; 및 광 개시제를 포함하는 수지 조성물을 도포하는 단계; 상기 도포된 수지 조성물을 광경화하여 보호 필름을 형성하는 단계; 및 편광자의 일 면에 상기 보호 필름을 라미네이트하여 접착시키는 단계를 포함한다. Method for producing a polarizing plate of the present invention, a binder comprising a polyfunctional acrylate monomer, and an acrylate oligomer having an elongation of 5 to 200% on a release film; And applying a resin composition comprising a photoinitiator; Photocuring the applied resin composition to a protective film Forming; And laminating the protective film on one surface of the polarizer and adhering the protective film.
본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는 바, 특정 실시예들을 예시하고 하기에서 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균둥물 내지 대체물을 포함하는 것으로 이해되어야 한다.  As the invention allows for various changes and numerous modifications, particular embodiments will be illustrated and described in detail below. However, this is not intended to limit the present invention to a specific disclosed form, it should be understood to include all modifications, fluctuations and substitutes included in the spirit and scope of the present invention.
이하, 본 발명의 편광자 보호 필름용 수지 조성물, 편광자 보호 필름， 이를 포함하는 편광판 및 편광판의 제조방법에 대해 보다 상세히 설명한다. 본 발명의 명세서에서 아크릴레이트계란, 아크릴레이트 뿐만 아니라 메타크릴레이트, 또는 아크릴레이트나 메타크릴레이트에 치환기가 도입된 유도체를 모두 의미한다.  Hereinafter, the resin composition for a polarizer protective film of the present invention, a polarizer protective film, a polarizing plate including the same, and a manufacturing method of the polarizing plate will be described in more detail. In the present specification, the acrylate-based means not only acrylate but also methacrylate or a derivative in which a substituent is introduced into acrylate or methacrylate.
본 발명의 일 측면에 따른 편광자 보호 필름은, 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신을을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함한다.  The polarizer protective film according to one aspect of the present invention includes a curable resin with a polyfunctional acrylate monomer and an acrylate oligomer having 5 to 200% of a god.
상기 편광자 보호 필름은 편광자를 외부로부터 보호하는 용도로 사용한다.  The polarizer protective film is used for the purpose of protecting the polarizer from the outside.
일반적으로 사용되는 편광자 보호 필름으로는 폴리에틸렌테레프탈레이트 (polyethyleneterephtalate, PET)와 같은 폴리에스테르 (polyester), 사이클릭 을레핀 공중합체 (cyclic olefin copolymer, COC), 폴리아크릴레이트 (polyacrylate, PAC), 플리카보네이트 (polycarbonate, PC), 폴리에틸렌 (polyethylene, PE), 폴리메틸메타크릴레이트 (polymethylmethacrylate, PMMA), 폴리에테르에테르케톤 (polyetheretherketon, PEEK), 폴리에틸렌나프탈레이트 (polyethylenenaphthalate, PEN), 폴리에테르이미드 (polyetherimide, PEI), 폴리이미드 (polyimide, PI) 또는 트리아세틸샐를로오스 (triacetylcdlulose, TAC) 등으로 이루어진 기재를 들 수 있다.  Commonly used polarizer protective films include polyesters such as polyethylene terephthalate (PET), cyclic olefin copolymers (COC), polyacrylates (polyacrylates, PACs), and polycarbonates. (polycarbonate, PC), polyethylene (PE), polymethylmethacrylate (PMMA), polyetheretherketon (PEEK), polyethylenenaphthalate (PEN), polyetherimide (PEI) ), Polyimide (PI) or triacetylsalose (triacetylcdlulose (TAC)).
상기 기재 중에서도 특히 트리아세틸셀를로오스 (TAC) 필름이 광학적 특성이 우수하여 많이 사용되고 있다. 그런데 상기 TAC 필름은 단독으로 사용할 경우 표면 경도가 약하고 습도에 취약하여 , 하드코팅 등의 기능성 코팅층을 추가할 필요가 있다. 그러나 이와 같이 기능성 코팅층을 더 포함할 경우 보호 필름의 전체 두께가 높아져 최근의 박형화 요구에 부합하지 못하고 추가 코팅으로 인해 필름에 컬이나 크랙 등이 발생할 우려가 있다. 이에, 본 발명은 범용적으로 사용되고 있는 TAC 필름올 대체하며， 별도의 코팅층을 포함하지 않으면서도 층분한 경도 및 박형화 추세에 부합할 수 있도록 낮은 두께를 갖는 보호 필름을 제공한다. 또한 본 발명의 보호 필름은 편광자 보호 필름에 요구되는 우수한 광학 특성을 나타내며, 생산, 가공, 보관 및 운반 등에 용이하도록 우수한 가요성을 나타낼 수 있다. 또한, 연신 필름을 포함하지 않으므로, 위상차값이 실질적으로 0에 가까울 정도로 낮아 편광자 보호용 필름뿐 아니라, 이러한 낮은 위상차값이 요구되는 각종 디바이스에 용도의 제한 없이 사용될 수 있다. Among the above substrates, triacetyl cellulose (TAC) films are particularly used because of their excellent optical properties. By the way, the TAC film alone When used, the surface hardness is weak and vulnerable to humidity, it is necessary to add a functional coating layer such as hard coating. However, if the functional coating layer is further included in this way, the overall thickness of the protective film is increased, which may not meet recent thinning requirements, and additional coating may cause curl or crack in the film. Accordingly, the present invention replaces the TAC film that is commonly used, and provides a protective film having a low thickness so as to meet the trend of thinner hardness and thinning without including a separate coating layer. In addition, the protective film of the present invention exhibits excellent optical properties required for the polarizer protective film, it may exhibit excellent flexibility to facilitate production, processing, storage and transport. In addition, since the stretched film is not included, the retardation value is substantially close to zero, so that the retardation value can be used not only for the polarizer protective film but also for various devices requiring such a low retardation value without any use limitation.
더하여, 우수한 가공성 및 가요성을 나타내어 대면적 또는 곡면 디스플레이에도 적용이 가능한 장점이 있다.  In addition, there is an advantage that can be applied to large area or curved display by showing excellent processability and flexibility.
본 발명의 편광자 보호 필름은 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함한다.  The polarizer protective film of the present invention contains a cured resin with a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%.
상기 다관능 아크릴레이트계 모노머는 아크릴레이트계 관능기를 2개 이상으로 포함하고 분자량이 1,000 g/mol 미만인 것을 의미한다. 보다 구체적으로 예를 들어 핵산디올디아크릴레이트 (HDD A), 트리프로필렌글리콜 디아크릴레이트 (TPGDA), 에틸렌글리콜 디아크릴레이트 (EGDA), 트리메틸을프로판 트리아크릴레이트 (TMPTA), 트리메틸을프로판에톡시 트리아크릴레이트 (TMPEOTA), 글리세린 프로폭실화 트리아크릴레이트 (GPTA), 펜타에리트리를 테트라아크릴레이트 (PETA), 또는 디펜타에리트리를 핵사아크릴레이트 (DPHA) 등을 들 수 있으나， 본 발명의 다관능 아크릴레이트계 모노머가 이에 제한되는 것은 아니다. 상기 다관능 아크릴레이트계 모노머는 서로 가교되거나, 또는 후술하는 아크릴레이트계 올리고머와 가교되어 보호 필름에 일정한 강도와 내마모성을 부여하는 역할을 한다.  The multifunctional acrylate monomer means that the acrylate-based functional group contains two or more and has a molecular weight of less than 1,000 g / mol. More specifically, for example, nucleic acid diol diacrylate (HDD A), tripropylene glycol diacrylate (TPGDA), ethylene glycol diacrylate (EGDA), trimethyl to propane triacrylate (TMPTA), trimethyl propane ethoxy Triacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA), pentaerythritol to tetraacrylate (PETA), or dipentaerythr to nuxaacrylate (DPHA). The polyfunctional acrylate monomer is not limited thereto. The multifunctional acrylate monomer crosslinks with each other, or crosslinks with an acrylate oligomer which will be described later to serve to impart a certain strength and wear resistance to the protective film.
상기 다관능 아크릴레이트계 모노머는 단독으로 또는 서로 다른 종류를 조합하여 사용할 수 있다. The polyfunctional acrylate monomers alone or different Type can be used in combination.
상기 아크릴레이트계 을리고머는 ASTM D638에 의해 측정하였을 때, 약 5 내지 약 200%, 또는 약 5 내지 약 100%, 또는 약 10 내지 약 50%의 신율을 가지는 아크릴레이트로써 특히, 아크릴레이트 관능기를 2개 이상으로 가지고 있는 을리고머를 의미한다. 상기 아크릴레이트계 올리고머의 신율이 상기 범위를 가질 때 기계적 물성의 저하 없이 우수한 유연성과 탄성을 나타낼 수 있다. 상기와 같은 신율 범위를 만족하는 아크릴레이트계 올리고머는 유연성과 탄성이 우수하여 상기 아크릴레이트계 모노머와 경화 수지를 형성하며, 이를 포함하는 보호 필름에 층분한 가요성, 컬 특성 등을 부여할 수 있음을 기초로 하여 본 발명에 이르게 되었다.  The acrylate-based oligomer is an acrylate having an elongation of about 5 to about 200%, or about 5 to about 100%, or about 10 to about 50%, as measured by ASTM D638. It means the lizolimer which has two or more. When the elongation of the acrylate oligomer has the above range, it may exhibit excellent flexibility and elasticity without deteriorating mechanical properties. The acrylate oligomer that satisfies the elongation range as described above is excellent in flexibility and elasticity to form the acrylate-based monomer and cured resin, and can provide a layered flexibility and curl characteristics to a protective film including the same. Based on this, the present invention has been reached.
본 발명의 일 실시예에 따르면, 상기 아크릴레이트계 을리고머의 중량평균분자량은 약 1,000 내지 약 10,000 g/mol, 또는 약 1,000 내지 약 5,000 g/mol, 또는 약 1,000 내지 약 3,000 g/mol의 범위를 가질 수 있다.  According to one embodiment of the present invention, the weight average molecular weight of the acrylate-based oligomer is about 1,000 to about 10,000 g / mol, or about 1,000 to about 5,000 g / mol, or about 1,000 to about 3,000 g / mol It can have a range.
본 발명의 일 실시예에 따르면, 상기 아크릴레이트계 올리고머는 에틸렌 옥사이드 (ethylene oxide), 프로필렌 옥사이드 (propylene oxide), 또는 카프로락톤 (caprolactone) 중 1종 이상으로 변성된 아크릴레이트계 올리고머일 수 있다. 상기 변성된 아크릴레이트계 을리고머를 사용할 경우 변성에 의해 상기 아크릴레이트계 올리고머에 유연성이 더욱 부여되어 보호 필름의 컬 특성 및 가요성이 증가할 수 있다.  According to one embodiment of the present invention, the acrylate oligomer may be an acrylate oligomer modified with one or more of ethylene oxide, propylene oxide, or caprolactone. When the modified acrylate oligomer is used, flexibility may be further provided to the acrylate oligomer by modification, thereby increasing curl characteristics and flexibility of the protective film.
상기 아크릴레이트계 올리고머는 단독으로 또는 서로 다른 종류를 조합하여 사용할 수 있다ᅳ  The acrylate oligomer may be used alone or in combination with each other.
본 발명의 보호 필름은 상술한 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머가 자외선에 의해 경화된 경화 수지를 포함한다. 또한, 본 발명의 보호 필름은 트리아세틸셀롤로오스 (TAC) 성분을 포함하지 않는다.  The protective film of this invention contains the above-mentioned polyfunctional acrylate-type monomer and cured resin by which the acrylate oligomer which has elongation of 5 to 200% is hardened by ultraviolet-ray. In addition, the protective film of this invention does not contain a triacetyl cellulose (TAC) component.
본 발명의 일 실시예에 따르면， 상기 경화 수지는 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머가 약 2:8 내지 약 8:2, 또는 약 3:7 내지 약 7:3, 또는 약 4:6 내지 약 6:4의 중량비로 경화되어 있는 것일 수 있다. 상기 경화 수지가 상기 범위로 경화될 때 본 발명의 보호 필름은 기계적 특성의 저하없이 층분하 가요성을 가질 수 있다. According to one embodiment of the invention, the cured resin is a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200% of about 2: 8 to about 8: 2, or about 3: 7 to Or about 7: 3, or cured at a weight ratio of about 4: 6 to about 6: 4. When the cured resin is cured in the above range, the protective film of the present invention is divided into layers without deterioration of mechanical properties. It can be flexible.
본 발명의 보호 필름은， 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머가 경화된 경화 수지를 포함함으로써 광학 물성의 저하 없이 고경도 및 박형화가 가능하다. 또한 하드코팅과 같은 별도의 기능성 코팅층 없이도 표면 경도 및 내스크래치 특성이 우수하다. 더하여 우수한 유연성, 내층격성 및 가요성을 확보할 수 있어, 대면적 또는 곡면 디스플레이에도 적용이 가능하다ᅳ 또한 연신 필름이 아닌 경화 수지층을 포함하므로， 위상차값이 실질적으로 0에 가까울 정도로 낮아 편광자 보호용 필름뿐 아니라, 낮은 위상차값이 요구되는 각종 디스플레이 장치에 용도의 제한없이 사용될 수 있다.  The protective film of the present invention, by including a polyfunctional acrylate monomer and a cured resin cured acrylate oligomer having an elongation of 5 to 200%, it is possible to high hardness and thinness without deterioration of optical properties. In addition, the surface hardness and scratch resistance is excellent without a separate functional coating layer such as hard coating. In addition, it is possible to secure excellent flexibility, layer resistance and flexibility, so that it can be applied to a large area or curved display. In addition, since it includes a cured resin layer instead of a stretched film, the phase difference value is substantially close to zero for polarizer protection. In addition to the film, it can be used without any limitation in various display apparatuses in which low retardation values are required.
본 발명에 따른 보호 필름은 상술한 다관능 아크릴레이트계 모노머와 함께 아크릴레이트계 올리고머가 가교 중합된 경화 수지를 포함함으로써, 고경도를 나타내면서도 동시에 유연성을 갖출 수 있다. 이에 따라, 별도의 기능성 코팅층 없이 편광자 보호층의 기능을 하면서 동시에 하드코팅 층의 역할을 하여 다기능성의 편광자 보호 필름으로 적용할 수 있다.  The protective film according to the present invention includes a cured resin in which an acrylate oligomer is cross-polymerized together with the polyfunctional acrylate monomer described above, thereby exhibiting high hardness and at the same time having flexibility. Accordingly, it can be applied as a multifunctional polarizer protective film by acting as a hard coating layer while also functioning as a polarizer protective layer without a separate functional coating layer.
본 발명의 일 실시예에 따르면, 본 발명의 보호 필름은 무기 미립자를 더 포함할 수 있다. 상기 무기 미립자는 상기 경화 수지 내에 분산되어 있는 형태로 포함될 수 있다.  According to an embodiment of the present invention, the protective film of the present invention may further include inorganic fine particles. The inorganic fine particles may be included in a form dispersed in the cured resin.
상기 무기 미립자로 입경이 나노 스케일인 무기 미립자, 예를 들어 입경이 약 lOOnm 이하, 또는 약 10 내지 약 lOOnm, 또는 약 10 내지 약 50nm의 나노 미립자가 될 수 있다. 또한 상기 무기 미립자로는 예를 들어 실리카 미립자, 알루미늄 옥사이드 입자, 티타늄 옥사이드 입자, 또는 징크 옥사이드 입자 등을 포함할 수 있다.  The inorganic fine particles may be inorganic fine particles having a nanoscale particle diameter, for example, nanoparticles having a particle diameter of about 100 nm or less, or about 10 to about 100 nm, or about 10 to about 50 nm. In addition, the inorganic fine particles may include, for example, silica fine particles, aluminum oxide particles, titanium oxide particles, or zinc oxide particles.
상기 무기 미립자를 포함함으로써 보호 필름의 경도를 더욱 향상시킬 수 있다.  By containing the said inorganic fine particle, the hardness of a protective film can be improved further.
본 발명의 일 실시예에 따르면, 상기 보호 필름이 무기 미립자를 더 포함하는 경우, 상기 경화 수지의 총 중량을 100 증량부로 할 때， 상기 무기 미립자를 약 1 내지 약 100 중량부로 포함할 수 있으며, 또는 약 10 내지 약 50 증량부로 포함할 수 있다. 상기 무기 미립자를 상기 범위로 포함함으로써 고경도와 가요성이 모두 우수한 보호 필름을 제공할 수 있다. 본 발명의 일 실시예에 따르면, 상기 보호 필름은 두께가 약 10/ΛΠ 이상, 예를 들어 약 10 내지 약 200/ ， 또는 약 10 내지 약 100 , 또는 약 10 내지 약 50 , 또는 약 10 내지 약 40//m, 또는 약 10 내지 약 30 의 두께를 가질 수 있다. 본 발명에 따르면, 상기와 같은 두께를 가짐으로써 별도의 코팅층을 포함하는 필름에 비하여 박형화가 가능하며， 컬이나 크랙 발생 없이 고경도의 보호 필름을 제공할 수 있다ᅳ According to an embodiment of the present invention, when the protective film further includes inorganic fine particles, when the total weight of the cured resin is 100 parts by weight, the inorganic fine particles may include about 1 to about 100 parts by weight, Or about 10 to about 50 increments. By including the inorganic fine particles in the above range, a protective film excellent in both high hardness and flexibility can be provided. According to one embodiment of the invention, the protective film has a thickness of at least about 10 / ΛΠ, for example about 10 to about 200 /, or about 10 to about 100, or about 10 to about 50, or about 10 to about 40 // m, or from about 10 to about 30. According to the present invention, by having the thickness as described above can be thinner than a film including a separate coating layer, it is possible to provide a protective film of high hardness without the occurrence of curl or crack 랙
상기와 같은 본 발명의 편광자 보호 필름은 상기 다관능 아크릴레이트계 모노머, 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머， 광 개시제, 및 선택적으로 무기 미립자, 유기 용매를 포함하는 수지 조성물을 광경화시켜 형성할 수 있다.  The polarizer protective film of the present invention as described above photocured the resin composition comprising the multifunctional acrylate monomer, an acrylate oligomer having an elongation of 5 to 200%, a photoinitiator, and optionally inorganic fine particles, an organic solvent. Can be formed.
본 발명의 다른 일 측면에 따르면， 다관능 아크릴레이트계 모노머， 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머를 포함하는 바인더; 및 광 개시제를 포함하는 수지 조성물을 제공한다.  According to another aspect of the invention, a binder comprising a polyfunctional acrylate monomer, and an acrylate oligomer having an elongation of 5 to 200%; And a photoinitiator.
상기 다관능 아크릴레이트계 모노머， 및 5 내지 200%의 신을을 갖는 아크릴레이트계 올리고머에 대한 보다 구체적인 설명은 상기 보호 필름에서 상술한 바와 같다.  A more detailed description of the multifunctional acrylate monomer and the acrylate oligomer having 5 to 200% of the god is as described above in the protective film.
본 발명의 일 실시예에 따르면, 상기 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머를 포함하는 바인더의 총 중량을 100 중량부로 할 때, 상기 다관능 아크릴레이트계 모노머를 약 20 내지 약 80 중량부로 포함할 수 있으며, 또는 약 30 내지 약 70 중량부로， 또는 약 40 내지 약 60 중량부로 포함할 수 있다. 상기 다관능 아크릴레이트계 모노머를 상기 범위로 포함함으로써 고경도와 가요성이 모두 우수한 보호 필름을 형성할 수 있다. 상기 다관능 아크릴레이트계 모노머의 함량이 20 중량부보다 낮으면 가교 밀도가 낮아져 연필 경도나 내스크래치성과 같은 도막의 기계적 특성이 저하될 수 있고, 80 중량부보다 많으면 도막이 부서지기 쉬워 층분한 가요성을 가질 수 없다.  According to an embodiment of the present invention, when the total weight of the binder including the polyfunctional acrylate monomer and the acrylate oligomer having an elongation of 5 to 200% is 100 parts by weight, the polyfunctional acrylic About 20 to about 80 parts by weight of the monomer may be included, or about 30 to about 70 parts by weight, or about 40 to about 60 parts by weight. By including the polyfunctional acrylate monomer in the above range, a protective film excellent in both high hardness and flexibility can be formed. When the content of the polyfunctional acrylate monomer is lower than 20 parts by weight, the crosslinking density is lowered, so that mechanical properties of the coating film, such as pencil hardness or scratch resistance, may be lowered. Can not have
본 발명의 일 실시예에 따르면， 상기 바인더의 총 중량을 100 중량부로 할 때, 상기 아크릴레이트계 을리고머를 약 20 내지 약 80 중량부로 포함할 수 있으며, 또는 약 30 내지 약 70 중량부로, 또는 약 40 내지 약 60 중량부로 포함할 수 있다. 상기 아크릴레이트계 올리고머의 함량이 20 중량부보다 함량이 낮을 경우 도막은 층분한 가요성을 갖지 못할 수 있고 80 중량부 이상을 사용할 경우 기계적 특성이 부족할 수 있다. According to an embodiment of the present invention, when the total weight of the binder is 100 parts by weight, the acrylate-based oligomer may include about 20 to about 80 parts by weight, or about 30 to about 70 parts by weight, Or about 40 to about 60 parts by weight. Of the acrylate oligomer If the content is lower than 20 parts by weight, the coating film may not have a sufficient flexibility, and when using more than 80 parts by weight may lack mechanical properties.
본 발명의 일 실시예에 따르면, 상기 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머는 약 2:8 내지 약 8:2, 또는 약 3:7 내지 약 7:3, 또는 약 4:6 내지 약 6:4의 중량비로 포함될 수 있다. 상기 경화 수지가 상기 범위로 경화될 때 본 발명의 보호 필름은 기계적 특성의 저하없이 충분한 가요성을 가질 수 있다.  According to one embodiment of the invention, the multifunctional acrylate monomer and the acrylate oligomer having an elongation of 5 to 200% is about 2: 8 to about 8: 2, or about 3: 7 to about 7: 3 Or in a weight ratio of about 4: 6 to about 6: 4. When the cured resin is cured in the above range, the protective film of the present invention may have sufficient flexibility without deterioration of mechanical properties.
본 발명의 수지 조성물에 따르면, 바인더 성분으로 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신을을 갖는 아크릴레이트계 올리고머를 포함하며， 이들이 서로 중합되어 경화된 경화 수지는 광학 물성의 저하 없이 얇은 두께의 보호 필름을 형성할 수 있다. 또한 이렇게 형성된 보호 필름은 하드코팅과 같은 별도의 기능성 코팅층 없이도 표면 경도 및 내스크래치 특성이 우수하다. 더하여 우수한 유연성 및 가요성을 확보할 수 있다. 또한 연신 필름이 아닌 경화 수지층을 포함하므로， 위상차값이 실질적으로 0에 가까울 정도로 낮아 편광자 보호용 필름뿐 아니라, 낮은 위상차값이 요구되는 각종 디스플레이 장치에 용도의 제한없이 사용될 수 있다.  According to the resin composition of the present invention, a binder component includes a polyfunctional acrylate monomer and an acrylate oligomer having a fluorine of 5 to 200%, and the cured resin cured by polymerizing with each other has a thin thickness without deteriorating optical properties. The protective film of can be formed. In addition, the protective film thus formed is excellent in surface hardness and scratch resistance even without a separate functional coating layer such as hard coating. In addition, excellent flexibility and flexibility can be achieved. In addition, since it includes a cured resin layer that is not a stretched film, the phase difference value is substantially close to zero, and can be used for various display devices that require a low phase difference value as well as a polarizer protective film, without limitation of use.
상기 광 개시제로는 1ᅳ히드록시 -시클로헥실 -페닐 케톤, 2-하이드록시 -2-메틸 -1-페닐 -1-프로판온,  Examples of the photoinitiator include 1'hydroxy-cyclohexyl-phenyl ketone, 2-hydroxy-2-methyl-1-phenyl-1-propanone,
2-하이드록시 -1-[4-(2-하이드록시에톡시)페닐] -2-메틸 -1-프로판온, 2-hydroxy-1- [4- (2-hydroxyethoxy) phenyl] -2-methyl-1-propanone,
메틸벤조일포르메이트, α,α-디메톡시 -α-페닐아세토페논，Methylbenzoylformate, α, α-dimethoxy-α-phenylacetophenone,
2-벤조일 -2- (디메틸아미노) -1-[4-(4-모포린일)페닐] -1-부타논, 2-benzoyl-2- (dimethylamino) -1- [4- (4-morpholinyl) phenyl] -1-butanone,
2-메틸 -1-[4- (메틸씨오)페닐] -2-(4-몰포린일) -1-프로판온 2-methyl-1- [4- (methylthio) phenyl] -2- (4-morpholinyl) -1-propanone
디페닐 (2,4,6-트리메틸벤조일) -포스핀옥사이드, 또는 비스 (2,4,6-트리메틸벤조일) -페닐포스핀옥사이드 등을 들 수 있으나, 이에 제한되지는 않는다. 또한 현재 시판되고 있는 상품으로는 Irgacure 184, Irgacure 500, Irgacure 651, Irgacure 369, Irgacure 907, Darocur 1173, Darocur MBF, Irgacure 819, Darocur TPO, Irgacure 907, Esacure KIP 100F 등을 들 수 있다. 이들 광 개시제는 단독으로 또는 서로 다른 2종 이상을 흔합하여 사용할 수 있다. 본 발명의 일 실시예에 따르면, 상기 바인더의 총 중량을 100 중량부로 할 때, 상기 광 개시제를 약 1 내지 약 10 중량부로 포함할 수 있으며, 또는 약 1 내지 약 8 중량부로 포함할 수 있다. Diphenyl (2,4,6-trimethylbenzoyl) -phosphine oxide, or bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide, and the like. Commercially available products include Irgacure 184, Irgacure 500, Irgacure 651, Irgacure 369, Irgacure 907, Darocur 1173, Darocur MBF, Irgacure 819, Darocur TPO, Irgacure 907, and Esacure KIP 100F. These photoinitiators can be used individually or in mixture of 2 or more types different from each other. According to an embodiment of the present invention, the total weight of the binder is 100 In weight parts, the photoinitiator may be included in an amount of about 1 to about 10 parts by weight, or about 1 to about 8 parts by weight.
본 발명의 수지 조성물은 각 성분들의 배합이 균일하고 적절한 점도를 가져 코팅 공정에 문제가 없는 경우 용매를 포함하지 않는 무용제 형태로 사용할 수 있다.  The resin composition of the present invention may be used in the form of a solvent-free solvent containing a solvent when the formulation of each component is uniform and has an appropriate viscosity and there is no problem in the coating process.
한편, 본 발명의 수지 조성물은 각 성분들의 균일한 배합 및 도포성을 위하여 유기 용매를 더 포함할 수 있다.  On the other hand, the resin composition of the present invention may further include an organic solvent for uniform blending and coating properties of each component.
상기 유기 용매로는 메탄을, 에탄올, 이소프로필알코을, 부탄을과 같은 알코올계 용매, 2-메톡시에탄올， 2-에톡시에탄올, 1-메톡시 -2-프로판올과 같은 알콕시 알코을계 용매, 아세톤， 메틸에틸케톤, 메틸이소부틸케톤， 메틸프로필케톤, 사이클로핵사논과 같은 케톤계 용매, 프로필렌글리콜모노프로필에테르， 프로필렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 에틸렌글리콜모노프로필에테르, 에틸렌글리콜모노부틸에테르, 디에틸렌글리콜모노메틸에테르, 디에틸글리콜모노에틸에테르, 디에틸글리콜모노프로필에테르, 디에틸글리콜모노부틸에테르, 디에틸렌글리콜 -2-에틸헥실에테르와 같은 에테르계 용매, 벤젠, 를루엔, 자일렌과 같은 방향족 용매 등을 단독으로 또는 흔합하여 사용할 수 있다.  Examples of the organic solvent include methane, alcohol solvents such as ethanol, isopropyl alcohol, butane, alkoxy alcohol solvents such as 2-methoxyethanol, 2-ethoxyethanol, and 1-methoxy-2-propanol, and acetone. ， Ketone solvents such as methyl ethyl ketone, methyl isobutyl ketone, methyl propyl ketone, cyclonucleanone, propylene glycol monopropyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl Ether solvents such as ether, diethylene glycol monomethyl ether, diethyl glycol monoethyl ether, diethyl glycol monopropyl ether, diethyl glycol monobutyl ether, diethylene glycol-2-ethylhexyl ether, benzene, toluene, Aromatic solvents, such as xylene, etc. can be used individually or in mixture.
본 발명의 일 실시예에 따르면, 상기 유기 용매의 함량은 수지 조성물의 물성을 저하시키기 않는 범위 내에서 다양하게 조절할 수 있으므로 특별히 제한하지는 않는다.  According to one embodiment of the present invention, the content of the organic solvent is not particularly limited because it can be variously adjusted within a range that does not lower the physical properties of the resin composition.
본 발명의 일 실시예에 따르면, 본 발명의 수지 조성물은 무기 미립자를 더 포함할 수 있다. 상기 무기 미립자는 상기 다관능 아크릴레이트계 모노머에 분산된 형태로 수지 조성물에 포함될 수 있다. 상기 무기 미립자로 입경이 나노 스케일인 무기 미립자, 예를 들어 입경이 약 lOOnm 이하, 또는 약 10 내지 약 lOOnm, 또는 약 10 내지 약 50nm의 나노 미립자가 될 수 있다. 또한 상기 무기 미립자로는 예를 들어 실리카 미립자, 알루미늄 옥사이드 입자, 티타늄 옥사이드 입자, 또는 징크 옥사이드 입자 등을 포함할 수 있다.  According to an embodiment of the present invention, the resin composition of the present invention may further include inorganic fine particles. The inorganic fine particles may be included in the resin composition in a form dispersed in the multifunctional acrylate monomer. The inorganic fine particles may be inorganic fine particles having a nanoscale particle diameter, for example, nanoparticles having a particle diameter of about 100 nm or less, or about 10 to about 100 nm, or about 10 to about 50 nm. In addition, the inorganic fine particles may include, for example, silica fine particles, aluminum oxide particles, titanium oxide particles, or zinc oxide particles.
상기 무기 미립자를 포함함으로써 보호 필름의 경도를 더욱 향상시킬 수 있다ᅳ By including the inorganic fine particles to further improve the hardness of the protective film ᅳ
본 발명의 일 실시예에 따르면, 상기 수지 조성물이 무기 미립자를 더 포함하는 경우, 상기 바인더의 총 중량을 100 증량부로 할 때, 상기 무기 미립자를 약 1 내지 약 100 중량부로 포함할 수 있으며, 또는 약 10 내지 약 50 증량부로 포함할 수 있다. 상기 무기 미립자를 상기 범위로 포함함으로써 고경도와 가요성이 모두 우수한 보호 필름을 형성할 수 있다.  According to an embodiment of the present invention, when the resin composition further includes inorganic fine particles, when the total weight of the binder is 100 parts by weight, the inorganic fine particles may include about 1 to about 100 parts by weight, or About 10 to about 50 parts by weight. By including the said inorganic fine particle in the said range, the protective film excellent in both high hardness and flexibility can be formed.
한편, 상기 수지 조성물은 전술한 상기 다관능 아크릴레이트계 모노머, 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머, 무기 미립자， 광 개시제, 유기 용매 외에도， UV 흡수제, 계면활성제, 황변 방지제， 레벨링제， 방오제 등 본 발명이 속하는 기술 분야에서 통상적으로 사용되는 첨가제를 추가로 포함할 수 있다. 또한 그 함량은 본 발명의 보호 필름의 물성을 저하시키지 않는 범위 내에서 다양하게 조절할 수 있으므로, 특별히 제한하지는 않는다.  On the other hand, the resin composition is the above-mentioned polyfunctional acrylate monomer, acrylate-based oligomer having an elongation of 5 to 200%, inorganic fine particles, photoinitiator, organic solvent, UV absorber, surfactant, anti-yellowing agent, It may further include additives commonly used in the art, such as leveling agents, antifouling agents. In addition, since the content can be variously adjusted within a range that does not lower the physical properties of the protective film of the present invention, it is not particularly limited.
본 발명의 일 실시예에 따르면, 예를 들어 상기 수지 조성물은 첨가제로 계면활성제를 포함할 수 있으며, 상기 계면활성제는 1 내지 2 관능성의 불소계 아크릴레이트, 불소계 계면 활성제 또는 실리콘계 계면 활성제일 수 있다. 이때 상기 계면활성제는 상기 경화 수지 내에 분산 또는 가교되어 있는 형태로 포함될 수 있다.  According to one embodiment of the present invention, for example, the resin composition may include a surfactant as an additive, and the surfactant may be a 1 to 2 functional fluorine-based acrylate, a fluorine-based surfactant, or a silicone-based surfactant. In this case, the surfactant may be included in the form of being dispersed or crosslinked in the cured resin.
또한， 상기 첨가제로 황변 방지제를 포함할 수 있으며, 상기 황변 방지제로는 벤조페논계 화합물 또는 벤조트리아졸계 화합물 등을 들 수 있다.  In addition, a yellowing inhibitor may be included as the additive, and the yellowing inhibitor may include a benzophenone compound or a benzotriazole compound.
상기와 같이, 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머를 포함하는 바인더, 광 개시제, 및 선택적으로 유기 용매, 무기 미립자, 기타 첨가제를 포함하는 수지 조성물을 광경화시킴으로써 편광자 보호 필름을 형성할 수 있다.  As described above, a resin composition comprising a binder comprising a multifunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%, a photoinitiator, and optionally an organic solvent, inorganic fine particles, and other additives is viewed. By polarizing, a polarizer protective film can be formed.
본 발명의 다른 일 측면에 따르면， 편광자; 및 상기 편광자의 적어도 일 면에 구비되는 보호 필름을 포함하며, 상기 보호 필름은 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함하는 편광판을 제공한다.  According to another aspect of the invention, the polarizer; And a protective film provided on at least one side of the polarizer, wherein the protective film includes a polyfunctional acrylate monomer and a cured resin with an acrylate oligomer having an elongation of 5 to 200%. do.
본 발명의 또 다른 일 측면에 따르면, 이형 필름 상에 다관능 아크릴레이트계 모노머, 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머를 포함하는 바인더; 및 광 개시제를 포함하는 수지 조성물을 도포하는 단계; 상기 도포된 수지 조성물을 광경화하여 보호 필름을 형성하는 단계; 및 편광자의 일 면에 상기 보호 필름을 라미네이트하여 접착시키는 단계를 포함하는 편광판의 제조방법을 제공한다. According to another aspect of the invention, the polyfunctional on the release film A binder comprising an acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%; And applying a resin composition comprising a photoinitiator; Photocuring the applied resin composition to form a protective film; And it provides a method of manufacturing a polarizing plate comprising the step of laminating and bonding the protective film on one side of the polarizer.
먼저, 다관능 아크릴레이트계 모노머, 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머, 및 광 개시제를 포함하는 수지 조성물을 이형 필름 상에 도포한다. 상기 수지 조성물에 포함되는 성분에 대한 구체적인 설명은 상기 편광자 보호 필름에서 설명한 바와 같다. 상기 수지 조성물은 선택적으로 유기 용매, 무기 미립자, 첨가제 등을 더 포함할 수 있다.  First, a resin composition containing a polyfunctional acrylate monomer, an acrylate oligomer having an elongation of 5 to 200%, and a photoinitiator is applied onto a release film. The detailed description about the component contained in the said resin composition is as having demonstrated in the said polarizer protective film. The resin composition may optionally further include an organic solvent, inorganic fine particles, additives, and the like.
상기 이형 필름은 본 발명이 속하는 기술분야에서 통상적으로 사용되는 것이라면 제한 없이 사용될 수 있다. 본 발명의 일 실시예에 따르면, 상기 이형 필름은 폴리에스테르 필름, 폴리에틸렌 필름， 폴리에틸렌테레프탈레이트 필름, 폴리프로필렌 필름 등의 폴리을레핀계 필름 : 또는 테프론계 필름일 수 있으며, 바람직하게는 박리가 용이하도록 실리콘계 수지, 멜라민계 수지 또는 요소계 수지 등으로 이형 처리된 필름일 수 있다. 상기 이형 필름의 두께는 특별히 한정하지 않으나, 약 20 내지 약 200^11의 두께를 갖는 이형 필름을 주로 사용할 수 있다. The release film may be used without limitation as long as it is commonly used in the art to which the present invention pertains. According to one embodiment of the invention, the release film is a polyester film, polyethylene film, polyethylene terephthalate film, poly polrieul repin-based film such as a polypropylene film may be or teflon-based film, preferably to facilitate exfoliation The film may be a release treatment with a silicone resin, melamine resin or urea resin. The thickness of the release film is not particularly limited, but a release film having a thickness of about 20 to about 200 ^ 11 may be mainly used.
상기 이형 필름은 수지 조성물의 경화 후 상기 보호 필름을 편광자에 부착하기 전 박리하여 제거될 수 있다. 또는 운반 및 보관 등에 유리하도록 편광자에 부착한 후에 제거될 수도 있다.  The release film may be removed by peeling after curing the resin composition before attaching the protective film to the polarizer. Or may be removed after attachment to the polarizer to favor transport and storage or the like.
상기 수지 조성물을 도포하는 방법은 본 기술이 속하는 기술분야에서 사용될 수 있는 것이면 특별히 제한되지 않으며， 예를 들면 바코팅 방식， 나이프 코팅방식 , 를 코팅방식 , 블레이드 코팅방식 , 다이 코팅방식 , 마이크로 그라비아 코팅방식 , 콤마코팅 방식 , 슬릇다이 코팅방식， 립 코팅방식 , 또는 솔루션 캐스팅방식 등을 이용할 수 있다.  The method of applying the resin composition is not particularly limited as long as it can be used in the technical field to which the present technology belongs, and for example, a bar coating method, a knife coating method, a coating method, a blade coating method, a die coating method, and a microgravure coating method. The method, the comma coating method, the sludge die coating method, the lip coating method, or the solution casting method can be used.
다음에, 도포된 수지 조성물에 조외선을 조사하여 광경화 반응을 수행함으로써 보호 필름을 형성할 수 있다. 상기 자외선을 조사하기 전, 수지 조성물의 도포면을 평탄화하고 조성물에 포함된 용매를 휘발시키기 위해 건조하는 과정을 더 수행할 수 있다. 상기 자외선의 조사량은, 예를 들면 약 20 내지 약 600 mJ/cm2일 수 있다. 자외선 조사의 광원으로는 본 기술이 속하는 기술분야에서 사용될 수 있는 것이면 특별히 제한되지 않으며, 예를 들면 고압 수은 램프, 메탈 할라이드 램프, 블랙 라이트 (black light) 형광 램프 등을 사용할 수 있다. 상기 수지 조성물이 완전히 경화된 후 TAC과 같은 기재 필름이나 별도의 코팅층 없이 단일층으로 형성된 편광자 보호 필름올 수득할 수 있다. 본 발명의 편광자 보호 필름에 따르면， 보호 필름을 편광자 상에 직접 형성하지 않고 별도의 이형 필름 상에 도포하여 경화하므로 기재 수축의 영향을 받지 않아 컬이나 크랙이 발생하지 않으며 고경도의 보호 필름을 형성할 수 있다. 또한, 낮은 위상차값을 나타내며， 광투과율， 헤이즈 등 편광자 보호 필름에 요구되는 광학 물성의 저하 없이 고경도의 편광자 보호 필름을 제공할 수 있다. Next, a protective film can be formed by irradiating an ultraviolet ray to the apply | coated resin composition and performing a photocuring reaction. Before irradiating the ultraviolet rays, a process of flattening the coated surface of the resin composition and drying to volatilize the solvent included in the composition may be further performed. The irradiation amount of ultraviolet rays may be, for example, about 20 to about 600 mJ / cm 2 . The light source for ultraviolet irradiation is not particularly limited as long as it can be used in the art to which the present technology belongs, and for example, a high pressure mercury lamp, a metal halide lamp, a black light fluorescent lamp, or the like can be used. After the resin composition is completely cured, a polarizer protective film formed of a single layer without a base film such as TAC or a separate coating layer may be obtained. According to the polarizer protective film of the present invention, since the protective film is applied to a separate release film and cured instead of directly forming on the polarizer, it is not affected by the shrinkage of the substrate and does not generate curls or cracks and forms a high hardness protective film. can do. In addition, it is possible to provide a high hardness polarizer protective film exhibiting a low phase difference value and without deteriorating optical properties required for a polarizer protective film such as light transmittance and haze.
본 발명의 보호 필름은 고경도, 가요성, 내찰상성, 고투명도 등을 나타내어 편광자 보호용으로 단일층의 필름으로 사용 가능하며 다양한 표시 장치에 유용하게 이용될 수 있다.  The protective film of the present invention exhibits high hardness, flexibility, scratch resistance, high transparency, and can be used as a single layer film for polarizer protection and can be usefully used in various display devices.
본 발명에 있어서, 상기 보호 필름은 상기 편광자의 한쪽 면에만 포함되거나, 상기 편광자의 양쪽 면에 모두 포함될 수 있다.  In the present invention, the protective film may be included only on one side of the polarizer, or both sides of the polarizer.
편광자는 여러 방향으로 진동하면서 입사되는 빛으로부터 한쪽 방향으로 진동하는 빛만을 추출할 수 있는 특성을 나타낸다. 이러한 특성은 요오드를 흡수한 PVA(poly vinyl alcohol)를 강한 장력으로 연신하여 달성할 수 있다. 예를 들어 보다 구체적으로, PVA 필름을 수용액에 담가 팽윤 (swelling)시키는 팽윤하는 단계, 상기 팽윤된 PVA 필름에 편광성을 부여하는 이색성 물질로 염색하는 단계, 상기 염색된 PVA 필름올 연신 (stretch)하여 상기 이색성 염료 물질을 연신 방향으로 란하게 배열시키는 연신 단계, 및 상기 연신 단계를 거친 PVA 필름의 색을 보정하는 보색 단계를 거쳐 편광자를 형성할 수 있다. 그러나, 본 발명의 편광판이 이에 제한되는 것은 아니다.  The polarizer exhibits a property of extracting only light vibrating in one direction from incident light while vibrating in various directions. This property can be achieved by stretching polyvinyl alcohol (PVA) absorbing iodine with strong tension. For example, more specifically, swelling by swelling the PVA film in an aqueous solution, dyeing with a dichroic material imparting polarization to the swelled PVA film, stretching the dyed PVA filmol The polarizer may be formed through a stretching step of arranging the dichroic dye material in a stretching direction, and a complementary color step of correcting a color of the PVA film subjected to the stretching step. However, the polarizing plate of the present invention is not limited thereto.
본 발명의 편광판은 상기 편광자의 적어도 일 면에 구비되는 보호 필름을 포함한다.  The polarizing plate of the present invention includes a protective film provided on at least one surface of the polarizer.
상기 보호 필름은 약 10卿이상, 예를 들어 약 10 내지 약 ΙΟΟμπι, 또는 약 10 내지 약 50 , 또는 약 10 내지 약 40 , 또는 약 10 내지 약 30卿의 두께를 가질 수 있다. The protective film is about 10 μs or more, for example about 10 to about ΙΟΟμπι, or About 10 to about 50, or about 10 to about 40, or about 10 to about 30 mm 3 thickness.
또한, 본 발명의 편광판의 전체 두께는 약 45/m이상, 예를 들어 약 45 내지 약 250 , 또는 약 50 내지 약 120卿, 또는 약 50 내지 약 100 가 될 수 있다. 본 발명에 따르면, 상기와 같은 박형의 두께를 가지면서도 컬이나 크랙 발생 없이 고경도를 달성할 수 있다.  In addition, the total thickness of the polarizing plate of the present invention may be about 45 / m or more, for example, about 45 to about 250, or about 50 to about 120 kPa, or about 50 to about 100. According to the present invention, while having a thin thickness as described above, it is possible to achieve high hardness without curling or cracking.
상기 보호 필름은 다관능 아크릴레이트계' 모노머 및 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함하며, 선택적으로 상기 경화 수지 내에 분산되어 있는 무기 미립자를 더 포함할 수 있다. 이에 대한 보다 구체적인 설명과 상기 보호 필름을 제조하는 방법은 상기 편광자용 보호 필름에서 설명한 바와 같다. The protective film is comprising a cured resin with the polyfunctional acrylate, the monomer and, and 5 to acrylic having elongation of 200% acrylate oligomer, and optionally may further include an inorganic fine particle which is dispersed in the cured resin . A more detailed description thereof and a method of manufacturing the protective film are as described in the protective film for polarizer.
본 발명의 일 실시예에 따르면, 본 발명의 편광판은 상기 편광자 및 보호 필름 사이에 구비되는 접착제층을 더 포함할 수 있다.  According to an embodiment of the present invention, the polarizing plate of the present invention may further include an adhesive layer provided between the polarizer and the protective film.
상기 접착제층은 투명성을 갖고 편광자의 편광 특성이 유지될 수 있는 편광자용 접착제를 포함하는 것일 수 있다. 사용 가능한 접착제로는 당 기술분야에 알려져 있는 것이면 특별히 제한되지 않는다. 예를 들면, 일액형 또는 이액형의 폴리비닐알콜 (PVA)계 접착제, 아크릴계 접착제， 폴리우레탄계 접착제, 에폭시계 접착제, 스티렌 부타디엔 고무계 (SBR) 접착제, 또는 핫멜트형 접착제 등이 있으나, 본 발명이 이들 예에만 한정되는 것은 아니다.  The adhesive layer may include a polarizer adhesive, which may have transparency and maintain polarization characteristics of the polarizer. Usable adhesives are not particularly limited as long as they are known in the art. For example, there are one-component or two-component polyvinyl alcohol (PVA) adhesives, acrylic adhesives, polyurethane adhesives, epoxy adhesives, styrene butadiene rubber (SBR) adhesives, hot melt adhesives, and the like. It is not limited only to an example.
상기 접착제층의 두께는 약 0.1 내지 약 10 , 또는 약 0.1 내지 약 5 일 수 있으나, 본 발명이 이들 예에만 한정되는 것은 아니다.  The thickness of the adhesive layer may be about 0.1 to about 10, or about 0.1 to about 5, but the present invention is not limited only to these examples.
다음에, 형성된 보호 필름올 접착제를 이용하여 편광자에 라미네이트하여 접착시킴으로써 본 발명의 편광판을 수득할 수 있다. 이때, 상기 이형 필름은 수지 조성물의 경화 후 상기 보호 필름을 편광자에 부착하기 전이나 또는 후에 선택적으로 박리하여 제거될 수 있다.  Next, the polarizing plate of this invention can be obtained by laminating and bonding to a polarizer using the formed protective film all adhesive agent. In this case, the release film may be removed by selectively peeling off or after attaching the protective film to the polarizer after curing of the resin composition.
본 발명의 일 실시예에 따르면, 상기 보호 필름은 편광자의 양 면에 부착할 수 있다.  According to one embodiment of the invention, the protective film may be attached to both sides of the polarizer.
본 발명의 다른 실시예에 따르면, 상기 보호 필름은 편광자의 일 면에만 부착하고, 다른 일 면에는 TAC과 같은 다른 범용의 필름을 부착할 수 있다. 이때, 상기 보호 필름이 사용자와 대면하는 최외각에 위치하도록 할 수 있다. 이처럼 본 발명의 보호 필름은 최외각층에 적합한 고경도, 내스크래치성, 및 광학 특성을 나타낸다. According to another embodiment of the present invention, the protective film is attached only to one side of the polarizer, the other side to attach another general purpose film such as TAC Can be. In this case, the protective film may be positioned at the outermost side facing the user. As described above, the protective film of the present invention exhibits high hardness, scratch resistance, and optical properties suitable for the outermost layer.
본 발명의 보호 필름은 TAC 필름을 대체할 수 있을 정도로 우수한 특성을 나타내며, 따라서 이를 포함하는 편광판은 우수한 연필 경도, 컬 특성, 가요성 및 광학 특성을 가질 수 있다.  The protective film of the present invention exhibits excellent properties that can replace the TAC film, and thus the polarizing plate including the same may have excellent pencil hardness, curling properties, flexibility and optical properties.
예를 들어 본 발명의 일 실시예에 따르면, 본 발명의 편광판은, 상온에서 24 시간 동안 노출시킨 후 평면에 위치시켰을 때, 상기 편광판의 각 모서리 또는 일 변이 평면에서 이격되는 거리의 평균값이 약 3mm 이하, 또는 약 2mm 이하, 또는 약 1mm 이하일 수 있다.  For example, according to one embodiment of the present invention, the polarizing plate of the present invention, when exposed to room temperature for 24 hours and placed in a plane, the average value of the distance from each corner or one side plane of the polarizing plate is about 3mm Or about 2 mm or less, or about 1 mm or less.
또한 본 발명의 편광판은, 500g 하중에서의 연필 경도가 1H 이상， 또는 2H 이상, 또는 3H 이상일 수 있다.  In addition, the polarizing plate of the present invention, the pencil hardness at 500g load may be 1H or more, or 2H or more, or 3H or more.
또한, 본 발명의 편광판은 단체 투과율이 40% 이상, 또는 42% 이상일 수 있다.  In addition, the polarizing plate of the present invention may have a single transmittance of 40% or more, or 42% or more.
또한, 본 발명의 편광판은 직경 15mm, 또는 12mm, 또는 5mm의 원통형 만드텔에 끼워 감았을 때 크랙이 발생하지 않을 수 있다.  In addition, the polarizing plate of the present invention may not be cracked when it is wound around a cylindrical mantel of 15mm, 12mm, or 5mm in diameter.
또한, 본 발명의 편광판에 구비되는 보호 필름은 0 내지 lnm, 또는 0 내지 0.6nm, 또는 0 내지 0.5nm의 면 방향 위상차값을 나타낼 수 있다.  In addition, the protective film provided in the polarizing plate of the present invention may exhibit a plane direction retardation value of 0 to 1 nm, 0 to 0.6 nm, or 0 to 0.5 nm.
이와 같은 본 발명의 보호 필름을 구비하는 편광판은, 다양한 분야에서 활용이 가능하다. 예를 들어 이동통신 단말기, 스마트폰, 기타 모바일 기기, 디스플레이 기기, 전자칠판, 옥외 전광판, 각종 표시부의 용도로 사용될 수 있다. 본 발명의 일 실시예에 따르면, 상기 편광판은 TN(Twisted Nematic), STN(Super Twisted Nematic) 액정용 편광판일 수 있으며， IPS(In-Plane Switching), Super-IPS, FFS(Fringe Field Switching) 등의 수평배향모드용 편광판일 수도 있고, 수직배향모드용 편광판일 수도 있다.. 이하, 발명의 구체적인 실시예를 통해, 발명의 작용 및 효과를 보다 상술하기호 한다. 다만, 이러한 실시예는 발명의 예시로 제시된 것에 불과하며, 이에 의해 발명의 권리범위가 정해지는 것은 아니다. <실시예 > 보호 필름의 제조 The polarizing plate provided with such a protective film of this invention can be utilized in various fields. For example, it can be used for mobile communication terminals, smart phones, other mobile devices, display devices, electronic blackboards, outdoor billboards, and various display units. According to an embodiment of the present invention, the polarizing plate may be a twisted nematic (TN), a polarizing plate for super twisted nematic (STN) liquid crystal, an in-plane switching (IPS), a super-IPS, a fringe field switching (FFS), or the like. It may be a polarizing plate for the horizontal alignment mode, or may be a polarizing plate for the vertical alignment mode. Hereinafter, the operation and effects of the invention will be described in more detail. However, these embodiments are only presented as an example of the invention, whereby the scope of the invention is not determined. <Example> Manufacture of protective film
실시예 1  Example 1
트리메틸올프로판 트리아크릴레이트 (TMPTA) 50g, DPCA120 (Nippon Kayaku, 카프로락톤 변성 6 관능기 아크릴레이트, ASTM D638로 측정한 신율 12%, Mw 1,950) 20g, PU3400 (미원, 에틸렌 옥사이드 변성 3 관능기 아크릴레이트, ASTM D638로 측정한 신율 20%, Mw 2,500) 30g, 광개시제 (상품명 Darocur TPO) 6g, UV흡수제 (상품명 Chimassorb 81) 3g, MEK lOg을 흔합하여 코팅액을 제조하고 PET 이형 필름에 bar 코팅하였다. 이를 60°C에서 2분간 건조한 후, 질소 분위기에서 black UV를 조사하여 두께가 25 인 보호 필름을 얻었다. 실시예 2 50 g of trimethylolpropane triacrylate (TMPTA), DPCA120 (Nippon Kayaku, caprolactone modified 6 functional acrylate, 12% elongation measured by ASTM D638, Mw 1,950) 20 g, PU3400 (miwon, ethylene oxide modified trifunctional acrylate, A 20% elongation measured by ASTM D638, 30 g of Mw 2,500), 6 g of a photoinitiator (trade name Darocur TPO), 3 g of a UV absorber (trade name Chimassorb 81), and MEK lOg were mixed to prepare a coating solution and bar coating the PET release film. It was dried for 2 minutes at 60 ° C, and then irradiated with black UV in a nitrogen atmosphere to obtain a protective film having a thickness of 25. Example 2
트리메틸올프로판 트리아크릴레이트 (TMPTA) 50g, DPCA120 20g, TA604AU (일본유지, 에틸렌 옥사이드 변성 3 관능기 아크릴레이트, ASTM D638로 측정한 신율 49%, Mw 2,300) 30g, 광개시제 (상품명 Darocur TPO) 6g, UV흡수제 (상품명 Chimassorb 81) 3g, MEK lOg을 흔합하여 코팅액을 제조하고 PET 이형 필름에 bar 코팅하였다. 이를 60°C에서 2분간 건조한 후, 질소 분위기에서 black UV를 조사하여 두께가 25 인 보호 필름을 얻었다. 실시예 3 50 g of trimethylolpropane triacrylate (TMPTA), 20 g of DPCA120, TA604AU (Japan oil, ethylene oxide modified trifunctional acrylate, 49% elongation measured by ASTM D638, Mw 2,300) 30 g, photoinitiator (trade name Darocur TPO) 6 g, UV A coating solution was prepared by mixing 3 g of an absorbent (trade name Chimassorb 81) and MEK lOg, and bar coating the PET release film. After drying for 2 minutes at 60 ° C., black UV irradiation in a nitrogen atmosphere to obtain a protective film having a thickness of 25. Example 3
C150 (Nano resin의 TMPTA에 20nm Si02가 50% 분산되어 있는 제품, 25g, Si0225g) 50g, PU340020g, TA604AU 30g, 광개시제 (상품명 Darocur TPO 6g, UV흡수제 (상품명 Chimassorb 81) 3g, MEK lOg을 흔합하여 코팅액을 제조하고 PET 이형 필름에 bar 코팅하였다. 이를 60°C에서 2분간 건조한 후, 질소 분위기에서 black UV를 조사하여 두께가 인 보호 필름을 얻었다. 비교예 1 50 g of C150 (20% Si0 2 dispersed in TMPTA in Nano resin, 25 g, Si0 2 25 g) 50 g, PU340020 g, TA604AU 30 g, photoinitiator (trade name Darocur TPO 6 g, UV absorber (trade name Chimassorb 81) 3 g, MEK lOg) A coating solution was prepared by mixing and bar coating on a PET release film, which was dried at 60 ° C. for 2 minutes, and then irradiated with black UV in a nitrogen atmosphere to obtain a protective film having a thickness.
트리메틸올프로판 트리아크릴레이트 (TMPTA) 50g, EB1290 (SK Cytec, 6 관능기 우레탄 아크릴레이트, ASTM D638로 측정한 신율 0%, Mw 1,000) 50g, 광개시제 (상품명 Darocur TPO) 6g, UV흡수제 (상품명 Chimassorb 81) 3g, MEK 10g을 흔합하여 코팅액을 제조하고 40 m두께의 TAC 필름에 bar 코팅하였다. 이를 60°C에서 2분간 건조한 후， 질소 분위기에서 black UV를 조사하여 TAC 필름 상에 두께가 6 인 보호 필름을 얻었다. 편광판의 제조 50 g of trimethylolpropane triacrylate (TMPTA), EB1290 (SK Cytec, 6 functional urethane acrylate, elongation 0% measured by ASTM D638, Mw 1,000) 50 g, photoinitiator (trade name Darocur TPO) 6 g, UV absorber (trade name Chimassorb 81 ) 3g, MEK 10 g of the mixture was mixed to prepare a coating solution and bar coated onto a 40 m thick TAC film. After drying for 2 minutes at 60 ° C., black UV irradiation in a nitrogen atmosphere to obtain a protective film having a thickness of 6 on the TAC film. Preparation of Polarizer
실시예 4  Example 4
실시예 1에서 제조한 보호 필름을 아크릴계 접착제를 이용하여 접착층의 두께가 대략 1卿가 되도록 PVA필름과 라미네이션하여 접착하고, PET 이형필름을 박리하몄다.  The protective film prepared in Example 1 was laminated by laminating with a PVA film so that the thickness of the adhesive layer was approximately 1 mm by using an acrylic adhesive, and the PET release film was peeled off.
PVA의 다른 한 면에는 40 두께의 TAC을 동일한 방법으로 접착시킴으로써 편광판을 제조하였다. 실시예 5  On the other side of the PVA, a polarizing plate was prepared by bonding a 40-thick TAC in the same way. Example 5
PVA 필름의 한 쪽 면에는 실시예 2의 보호 필름을 부착하고 다른 한 면에는 40 ιη두께의 TAC 필름을 부착하여 실시예 4와 동일한 방법으로 편광판을 제조하였다. 실시예 6  A polarizing plate was prepared in the same manner as in Example 4 by attaching a protective film of Example 2 to one side of the PVA film and a TAC film having a thickness of 40 η to the other side. Example 6
PVA 필름의 한 쪽 면에는 실시예 3의 보호 필름을 부착하고 다른 한 면에는 40 두께의 TAC 필름을 부착하여 실시예 4와 동일한 방법으로 편광판을 제조하였다. 비교예 2  A polarizing plate was prepared in the same manner as in Example 4 by attaching the protective film of Example 3 to one side of the PVA film and attaching a TAC film of 40 thickness to the other side. Comparative Example 2
PVA 필름의 한 쪽 면에는 비교예 1의 코팅층이 형성된 TAC 필름을 부착하고 다른 한 면에는 40 두께의 TAC 필름을 부착하여 실시예 4와 동일한 방법으로 편광판을 제조하였다. 비교예 3  On one side of the PVA film was attached a TAC film having a coating layer of Comparative Example 1 and the other side was attached a TAC film of 40 thickness to prepare a polarizing plate in the same manner as in Example 4. Comparative Example 3
PVA 필름의 양 면에 40 두께의 TAC 필름을 아크릴계 접착제를 이용하여 접착충의 두께가 대략 1 가 되도록 PVA 필름과 라미네이션하여 접착하여 편광판을 제조하였다. On both sides of the PVA film, a 40-thick TAC film is laminated with a PVA film using an acrylic adhesive so that the thickness of the adhesive is approximately 1 Adhesion was performed to prepare a polarizing plate.
<실험예 > Experimental Example
<측정 방법 >  <Measurement method>
1)두께  1) Thickness
디지털 마이크로미터기를 이용하여 측정하였다.  Measurement was made using a digital micrometer.
2) 투과율 2) transmittance
Hazemeter(HM 150)를 이용하여 투과율과 헤이즈를 측정하였다.  The transmittance and the haze were measured using a Hazemeter (HM 150).
3) 위상차 3) phase difference
위상차 측정기 (Axoscan)을 이용하여 면 방향 위상차 값을 측정하였다.  The retardation value was measured using a phase difference measuring instrument (Axoscan).
4)연필 경도 4) pencil hardness
연필경도 측정기를 이용하여 상기 편광판 표면에 대하여 측정 표준 Measurement standard for the surface of the polarizer using a pencil hardness tester
JIS K5400에 따라 500g의 하중으로 5회 왕복한 후 홈집이 없는 경도를 확인하였다. After reciprocating five times with a load of 500 g according to JIS K5400, the hardness without grooves was confirmed.
5) 내스크래치성 5) Scratch Resistance
Steel wool #0000에 일정한 하중을 걸어 왕복하여 10회 문지른 뒤 홈집이 생기지 않는 하중을 확인하였다.  A constant load was placed on steel wool # 0000 and reciprocated 10 times to check the load without grooves.
6) 컬 특성 6) Curl Characteristics
각 편광판을 10cm X 10cm로 잘라 24시간 동안 보관한 후 평면에 위치시켰을 때 각 모서리의 일변이 평면으로부터 이격되는 거리의 평균값을 측정하였다.  Each polarizing plate was cut into 10 cm × 10 cm and stored for 24 hours, and then the average value of the distance from which one side of each corner is spaced apart from the plane was measured.
7) 원통형 굴곡 테스트 7) Cylindrical bend test
각 편광판을 직경 5mm의 원통형 만드렐에 끼워 감은 후 크랙 발생유무를 판단하여 크랙이 발생하지 않은 경우를 OK, 크랙이 발생한 경우를 X로 평가하였다. 상기 물성 측정 결과를 하기 표 1에 나타내었다. Each polarizer is wound into a cylindrical moldrel with a diameter of 5mm, and it is OK to determine if cracks have occurred. The case was evaluated with X. The physical property measurement results are shown in Table 1 below.
【표 11  Table 11
Figure imgf000020_0001
상기 표 1과 같이, 본 발명의 실시예의 편광판은 각 물성에서 모두 양호한 특성을 나타내었다. 특히, 비교예 2와 같이 TAC 및 코팅층을 포함하는 종래의 보호필름 및 TAC만을 포함하는 비교예 3과 비교하여， 낮은 두께로 고경도 및 우수한 컬 특성과 가요성, 낮은 위상차 등을 나타내어 박형화가 요구되는 표시 장치에 유용하게 사용될 수 있다.
Figure imgf000020_0001
As shown in Table 1, the polarizing plate of the embodiment of the present invention exhibited good properties in all the physical properties. In particular, compared with the conventional protective film including TAC and coating layer and Comparative Example 3 including only TAC as in Comparative Example 2, it exhibits high hardness, excellent curl characteristics, flexibility, low phase difference, etc. at a low thickness, and requires thinning. It can be usefully used for the display device.

Claims

【특허청구범위】 [Patent Claims]
【청구항 1】  [Claim 1]
다관능 아크릴레이트계 모노머， 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머를 포함하는 바인더; 및  A binder comprising a polyfunctional acrylate monomer, an acrylate oligomer having an elongation of 5 to 200%; And
광 개시제를 포함하는 수지 조성물.  Resin composition containing a photoinitiator.
【청구항 2】 [Claim 2]
제 1항에 있어서,  The method of claim 1,
상기 바인더의 총 중량을 100 증량부로 할 때, 상기 다관능 아크릴레이트계 모노머를 20 내지 80 증량부, 상기 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머를 20 내지 80 중량부, 및 상기 광 개시제를 1 내지 10 중량부로 포함하는 수지 조성물.  When the total weight of the binder is 100 parts by weight, 20 to 80 parts by weight of the polyfunctional acrylate monomer, 20 to 80 parts by weight of an acrylate oligomer having an elongation of 5 to 200%, and Resin composition containing 1-10 weight part of photoinitiators.
【청구항 3】 [Claim 3]
거 11항에 있어서,  According to claim 11,
상기 다관능 아크릴레이트계 모노머는 핵산디올디아크릴레이트 (HDDA), 트리프로필렌글리콜 디아크릴레이트 (TPGDA), 에틸렌글리콜 디아크릴레이트 (EGDA), 트리메틸을프로판 트리아크릴레이트 (TMPTA), 트리메틸올프로판에톡시 트리아크릴레이트 (TMPEOTA), 글리세린 프로폭실화 트리아크릴레이트 (GPTA), 펜타에리트리를 테트라아크릴레이트 (PETA), 및 디펜타에리트리를 핵사아크릴레이트 (DPHA)로 이루어진 군에서 선택되는 1종 이상을 포함하는 수지 조성물.  The polyfunctional acrylate monomers include nucleic acid diol diacrylate (HDDA), tripropylene glycol diacrylate (TPGDA), ethylene glycol diacrylate (EGDA), trimethyl to propane triacrylate (TMPTA), trimethylolpropane 1 type selected from the group consisting of methoxy triacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA), pentaerythritol tetraacrylate (PETA), and dipentaerythrine nuxaacrylate (DPHA) Resin composition containing the above.
【청구항 4】 [Claim 4]
제 1항에 있어서,  The method of claim 1,
상기 아크릴레이트계 올리고머는 아크릴레이트 관능기를 2개 이상 가지고 있고 에틸렌 옥사이드 (ethylene oxide), 프로필렌 옥사이드 (propylene oxide) 및 카프로락톤 (caprolactone)로 이루어진 군으로부터 선택된 1종 이상으로 변성된 것인 수지 조성물. The acrylate oligomer is a resin composition having at least two acrylate functional groups and modified with at least one selected from the group consisting of ethylene oxide, propylene oxide and caprolactone.
【청구항 5】 [Claim 5]
제 1항에 있어서,  The method of claim 1,
무기 미립자를 더 포함하는 수지 조성물.  Resin composition containing an inorganic fine particle further.
【청구항 6】 [Claim 6]
제 5항에 있어서,  The method of claim 5,
상기 바인더의 총 중량을 100 중량부로 할 때, 상기 무기 미립자를 1 내지 100 중량부로 포함하는 수지 조성물.  When the total weight of the binder is 100 parts by weight, the resin composition comprising 1 to 100 parts by weight of the inorganic fine particles.
【청구항 7】 [Claim 7]
제 5 항에 있어서,  The method of claim 5,
상기 무기 미립자는 실리카 나노 미립자, 알루미늄 옥사이드 미립자, 티타늄 옥사이드 미립자 및 징크 옥사이드 미립자로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 수지 조성물.  The inorganic fine particles are at least one resin composition selected from the group consisting of silica nanoparticles, aluminum oxide fine particles, titanium oxide fine particles and zinc oxide fine particles.
【청구항 8] [Claim 8]
거 1 1 항에 있어서,  According to claim 1 1,
유기 용매를 더 포함하는 수지 조성물. 【청구항. A resin composition further comprising an organic solvent. Claims.
9】 9】
제 1 항에 있어서,  The method of claim 1,
편광자 보호 필름을 형성하는데 사용되는 것인 수지 조성물.  The resin composition used to form a polarizer protective film.
【청구항 10] [Claim 10]
다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함하는 편광자 보호 필름.  A polarizer protective film comprising a cured resin with a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%.
【청구항 11】 [Claim 11]
제 10항에 있어서,  The method of claim 10,
상기 경화 수지는 상기 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머가 2:8 내지 8:2의 중량비로 경화되어 있는 편광자 보호 필름. The cured resin is the polyfunctional acrylate monomer and 5 to A polarizer protective film, wherein an acrylate-based oligomer having an elongation of 200% is cured at a weight ratio of 2: 8 to 8: 2.
【청구항 12】 [Claim 12]
제 10항에 있어서,  The method of claim 10,
상기 다관능 아크릴레이트계 모노머는 핵산디올디아크릴레이트 (HDDA), 트리프로필렌글리콜 디아크릴레이트 (TPGD A), 에틸렌글리콜 디아크릴레이트 (EGDA), 트리메틸올프로판 트리아크릴레이트 (TMPTA), 트리메틸을프로판에록시 트리아크릴레이트 (TMPEOTA), 글리세린 프로폭실화 트리아크릴레이트 (GPTA): 펜타에리트리를 테트라아크릴레이트 (PETA), 및 디펜타에리트리를 핵사아크릴레이트 (DPHA)로 이루어진 군에서 선택되는 1종 이상을 포함하는 편광자 보호 필름. The polyfunctional acrylate monomers include nucleic acid diol diacrylate (HDDA), tripropylene glycol diacrylate (TPGD A), ethylene glycol diacrylate (EGDA), trimethylolpropane triacrylate (TMPTA), and trimethyl propane. Ethoxy triacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA) : 1 selected from the group consisting of pentaerythritol tetraacrylate (PETA), and dipentaerythroxy nuxaacrylate (DPHA) Polarizer protective film containing more than one type.
【청구항 13】 [Claim 13]
제 10항에 있어서,  The method of claim 10,
상기 아크릴레이트계 올리고머는 아크릴레이트 관능기를 2개 이상 가지고 있고 에틸렌 옥사이드 (ethylene oxide), 프로필렌 옥사이드 (propylene oxide) 및 카프로락톤 (caprolactone)로 이루어진 군으로부터 선택된 1종 이상으로 변성된 것인 편광자 보호 필름.  The acrylate oligomer has at least two acrylate functional groups and is a polarizer protective film modified by at least one selected from the group consisting of ethylene oxide, propylene oxide and caprolactone. .
【청구항 14】 [Claim 14]
제 10항에 있어서,  The method of claim 10,
상기 경화 수지 내에 분산되어 있는 무기 미립자를 더 포함하는 편광자 보호 필름.  The polarizer protective film further containing the inorganic fine particle disperse | distributed in the said cured resin.
【청구항 15】 [Claim 15]
제 14항에 있어서,  The method of claim 14,
상기 경화 수지의 중량을 100 중량부로 할 때, 상기 무기 미립자를 1 내지 100 중량부로 포함하는 편광자 보호 필름. The polarizer protective film containing 1-100 weight part of said inorganic fine particles, when the weight of the said cured resin is 100 weight part.
【청구항 16】 [Claim 16]
제 14항에 있어서,  The method of claim 14,
상기 무기 미립자는 실리카 나노 미립자, 알루미늄 옥사이드 미립자, 티타늄 옥사이드 미립자 및 징크 옥사이드 미립자로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 편광자 보호 필름.  The inorganic fine particle is a polarizer protective film comprising at least one selected from the group consisting of silica nano fine particles, aluminum oxide fine particles, titanium oxide fine particles and zinc oxide fine particles.
【청구항 17】 [Claim 17]
편광자; 및  Polarizer; And
상기 편광자의 적어도 일 면에 구비되는 보호 필름을 포함하며, 상기 보호 필름은 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머와의 경화 수지를 포함하는 편광판.  And a protective film provided on at least one surface of the polarizer, wherein the protective film comprises a curable resin with a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200%.
【청구항 18】 [Claim 18]
제 17항에 있어서,  The method of claim 17,
상기 경화 수지는 상기 다관능 아크릴레이트계 모노머 및 5 내지 200%의 신율을 갖는 아크릴레이트계 올리고머가 2:8 내지 8:2의 중량비로 경화되어 있는 편광판.  The cured resin is a polarizing plate wherein the polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200% are cured at a weight ratio of 2: 8 to 8: 2.
【청구항 19】 [Claim 19]
제 17항에 있어서,  The method of claim 17,
상기 다관능 아크릴레이트계 모노머는 핵산디을디아크릴레이트 (HDDA), 트리프로필렌글리콜 디아크릴레이트 (TPGDA), 에틸렌글리콜 디아크릴레이트 (EGDA), 트리메틸을프로판 트리아크릴레이트 (TMPTA), 트리메틸을프로판에톡시 트리아크릴레이트 (TMPEOTA), 글리세린 프로폭실화 트리아크릴레이트 (GPTA), 펜타에리트리를 테트라아크릴레이트 (PETA), 및 디펜타에리트리를 핵사아크릴레이트 (DPHA) 로 이루어진 군에서 선택되는 1종 이상을 포함하는 편광판. The polyfunctional acrylate monomers include nucleic acid didi diacrylate (HDDA), tripropylene glycol diacrylate (TPGDA), ethylene glycol diacrylate (EGDA), trimethyl to propane triacrylate (TMPTA), and trimethyl to propane. 1 type selected from the group consisting of methoxy triacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA), pentaerythritol tetraacrylate (PETA), and dipentaerythrine nuxaacrylate (DPHA) Polarizing plate containing the above.
【청구항 20] [Claim 20]
제 17항에 있어서,  The method of claim 17,
상기 아크릴레이트계 올리고머는 아크릴레이트 관능기를 2개 이상 가지고 있고 에틸렌 옥사이드 (ethylene oxide), 프로필렌 옥사이드 (propylene oxide) 및 카프로락톤 (caprolactone)로 이루어진 군으로부터 선택된 1종 이상으로 변성된 것인 편광판.  The acrylate oligomer is a polarizing plate having at least two acrylate functional groups and modified with at least one selected from the group consisting of ethylene oxide, propylene oxide and caprolactone.
【청구항 21】 [Claim 21]
제 17항에 있어서,  The method of claim 17,
상기 보호 필름은 상기 경화 수지 내에 분산되어 있는 무기 미립자를 더 포함하는 편광판.  The protective film further comprises an inorganic fine particle dispersed in the cured resin.
【청구항 22] [Claim 22]
제 17항에 있어서,  The method of claim 17,
상기 보호 필름은 상기 편광자의 양 면에 구비되는 편광판.  The protective film is provided on both sides of the polarizer.
【청구항 23】 [Claim 23]
제 17항에 있어서,  The method of claim 17,
상기 편광자 및 상기 보호 필름 사이에 구비되는 접착제층을 더 포함하는 편광판.  A polarizer further comprising an adhesive layer provided between the polarizer and the protective film.
【청구항 24] [Claim 24]
제 17항에 있어서,  The method of claim 17,
상기 보호 필름의 두께는 10 내지 100，인 편광판.  The thickness of the said protective film is 10-100, The polarizing plate.
【청구항 25] [Claim 25]
제 17항에 있어서,  The method of claim 17,
상기 편광판의 두께는 45 내지 250 인 편광판.  The polarizing plate has a thickness of 45 to 250.
【청구항 26】 제 17항에 있어서, [Claim 26] The method of claim 17,
500g 하중에서 ,ΙΗ이상의 연필 경도를 나타내는 편광판.  A polarizer showing a pencil hardness of more than ΙΗ at 500g load.
【청구항 27】 [Claim 27]
제 17항에 있어서,  The method of claim 17,
상온에서 24 시간 동안 노출시킨 후 평면에 위치시켰을 때, 상기 편광판의 각 모서리 또는 일 변이 평면에서 이격되는 거리의 평균값이 약 3mm 이하인 편광판. ' When exposed to room temperature for 24 hours and then placed in a plane, the average value of the distance of each corner or one side of the polarizing plate from the plane is about 3mm or less. '
【청구항 28】 [Claim 28]
제 17항에 있어서,  The method of claim 17,
직경 15mm의 원통형 만드렐에 끼워 감았을 때 크랙이 발생하지 않는 편광판.  A polarizer that does not cause cracks when wound into a cylindrical mandrel with a diameter of 15 mm.
【청구항 29】 [Claim 29]
이형 필름 상에 다관능 아크릴레이트계 모노머， 및 5 내지 200%의 신율을 갖는 아크릴레이트계 을리고머를 포함하는 바인더; 및 광 개시제를 포함하는 수지 조성물을 도포하는 단계;  A binder comprising a polyfunctional acrylate monomer and an acrylate oligomer having an elongation of 5 to 200% on a release film; And applying a resin composition comprising a photoinitiator;
상기 도포된 수지 조성물을 광경화하여 보호 필름을 형성하는 단계; 및  Photocuring the applied resin composition to form a protective film; And
편광자의 일 면에 상기 보호 필름을 라미네이트하여 접착시키는 단계를 포함하는 편광판의 제조방법.  Laminating the protective film on one side of the polarizer and a method of manufacturing a polarizing plate comprising the step of bonding.
【청구항 30】 [Claim 30]
제 29항에 있어서,  The method of claim 29,
상기 편광자의 일 면에 상기 보호 필름을 라미네이트하여 접착시키는 단계 이전 또는 이후에 상기 이형 필름을 박리하는 단계를 더 포함하는 편광판의 제조방법.  Peeling the release film before or after the step of laminating the protective film on one side of the polarizer and after bonding.
PCT/KR2014/002614 2013-03-27 2014-03-27 Resin composition for polarizer protecting film, polarizer protecting film, polarizing plate comprising same, and method for manufacturing polarizing plate WO2014157963A1 (en)