WO2014133164A1 - Feuille de cuivre dont la surface a été traitée et noircie, procédé permettant de fabriquer une feuille de cuivre dont la surface a été traitée et noircie, stratifié recouvert de cuivre et carte de circuit imprimé flexible - Google Patents
Feuille de cuivre dont la surface a été traitée et noircie, procédé permettant de fabriquer une feuille de cuivre dont la surface a été traitée et noircie, stratifié recouvert de cuivre et carte de circuit imprimé flexible Download PDFInfo
- Publication number
- WO2014133164A1 WO2014133164A1 PCT/JP2014/055173 JP2014055173W WO2014133164A1 WO 2014133164 A1 WO2014133164 A1 WO 2014133164A1 JP 2014055173 W JP2014055173 W JP 2014055173W WO 2014133164 A1 WO2014133164 A1 WO 2014133164A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- copper foil
- flexible printed
- wiring board
- printed wiring
- treated copper
- Prior art date
Abstract
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201480010680.3A CN105008593B (zh) | 2013-02-28 | 2014-02-28 | 黑化表面处理铜箔、黑化表面处理铜箔的制造方法、覆铜层压板及柔性印刷线路板 |
KR1020157019621A KR20150090265A (ko) | 2013-02-28 | 2014-02-28 | 흑색화 표면 처리 구리박, 흑색화 표면 처리 구리박의 제조 방법, 구리 클래드 적층판 및 플렉시블 프린트 배선판 |
KR1020167031887A KR102116928B1 (ko) | 2013-02-28 | 2014-02-28 | 흑색화 표면 처리 구리박, 흑색화 표면 처리 구리박의 제조 방법, 구리 클래드 적층판 및 플렉시블 프린트 배선판 |
JP2014532134A JP5705381B2 (ja) | 2013-02-28 | 2014-02-28 | 黒色化表面処理銅箔、黒色化表面処理銅箔の製造方法、銅張積層板及びフレキシブルプリント配線板 |
MYPI2015702425A MY181562A (en) | 2013-02-28 | 2014-02-28 | Black color surface-treated copper foil, method of manufacturing black color surface-treated copper foil, copper-clad laminate and flexible printed wiring board |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013039388 | 2013-02-28 | ||
JP2013-039388 | 2013-02-28 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014133164A1 true WO2014133164A1 (fr) | 2014-09-04 |
Family
ID=51428422
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2014/055173 WO2014133164A1 (fr) | 2013-02-28 | 2014-02-28 | Feuille de cuivre dont la surface a été traitée et noircie, procédé permettant de fabriquer une feuille de cuivre dont la surface a été traitée et noircie, stratifié recouvert de cuivre et carte de circuit imprimé flexible |
Country Status (6)
Country | Link |
---|---|
JP (1) | JP5705381B2 (fr) |
KR (2) | KR20150090265A (fr) |
CN (1) | CN105008593B (fr) |
MY (1) | MY181562A (fr) |
TW (1) | TWI690625B (fr) |
WO (1) | WO2014133164A1 (fr) |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016035604A1 (fr) * | 2014-09-02 | 2016-03-10 | 三井金属鉱業株式会社 | Feuille de cuivre traitée en surface noircie et feuille de cuivre comprenant une feuille support |
WO2016117587A1 (fr) * | 2015-01-22 | 2016-07-28 | 三井金属鉱業株式会社 | Film de cuivre ultra-mince à support et son procédé de fabrication |
KR20160099439A (ko) | 2015-02-12 | 2016-08-22 | 후쿠다 킨조쿠 하쿠훈 코교 가부시키가이샤 | 처리 동박 및 그 처리 동박을 사용한 구리 피복 적층판 그리고 프린트 배선판 |
WO2016158775A1 (fr) * | 2015-03-31 | 2016-10-06 | 三井金属鉱業株式会社 | Feuille de cuivre rugosifiée, feuille de cuivre pourvue d'un support, plaque stratifiée cuivrée, et carte de circuit imprimé |
JPWO2016093109A1 (ja) * | 2014-12-08 | 2017-09-14 | 三井金属鉱業株式会社 | プリント配線板の製造方法 |
WO2017179416A1 (fr) * | 2016-04-14 | 2017-10-19 | 三井金属鉱業株式会社 | Feuille de cuivre traitée en surface, feuille de cuivre avec support et procédés de fabrication de stratifié revêtu de cuivre et carte de circuit imprimé l'utilisant |
JP2020183573A (ja) * | 2019-05-09 | 2020-11-12 | ナミックス株式会社 | 複合銅部材 |
JP2020183571A (ja) * | 2019-05-09 | 2020-11-12 | ナミックス株式会社 | 銅表面の加工装置 |
KR20230141859A (ko) | 2021-03-29 | 2023-10-10 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 동장 적층판 및 프린트 배선판 |
KR20230159392A (ko) | 2021-03-26 | 2023-11-21 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 캐리어를 구비한 구리박, 동장 적층판 및 프린트 배선판 |
KR20230160813A (ko) | 2021-03-26 | 2023-11-24 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 캐리어를 구비한 구리박, 동장 적층판 및 프린트 배선판 |
KR20230161954A (ko) | 2021-03-29 | 2023-11-28 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 동장 적층판 및 프린트 배선판 |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2017014608A (ja) * | 2015-07-06 | 2017-01-19 | 古河電気工業株式会社 | 電解銅箔、リチウムイオン二次電池用負極電極及びリチウムイオン二次電池、プリント配線板並びに電磁波シールド材 |
US9397343B1 (en) | 2015-10-15 | 2016-07-19 | Chang Chun Petrochemical Co., Ltd. | Copper foil exhibiting anti-swelling properties |
CN106229344B (zh) | 2016-08-19 | 2019-10-15 | 京东方科技集团股份有限公司 | 薄膜晶体管、其制备方法及显示装置 |
KR102180926B1 (ko) | 2017-06-28 | 2020-11-19 | 에스케이넥실리스 주식회사 | 우수한 작업성 및 충방전 특성을 갖는 동박, 그것을 포함하는 전극, 그것을 포함하는 이차전지, 및 그것의 제조방법 |
TWI694176B (zh) * | 2018-08-10 | 2020-05-21 | 南韓商Kcf科技有限公司 | 具有較佳工作性及充放電特性之銅箔、包含其之電極、包含其之二次電池及其製造方法 |
CN111058063B (zh) * | 2018-10-16 | 2021-02-02 | 长春石油化学股份有限公司 | 电解铜箔、包含其的电极、及包含其的锂离子电池 |
US11365486B2 (en) | 2018-10-16 | 2022-06-21 | Chang Chun Petrochemical Co., Ltd. | Electrolytic copper foil, electrode comprising the same, and lithium ion battery comprising the same |
JP7352939B2 (ja) * | 2019-05-09 | 2023-09-29 | ナミックス株式会社 | 複合銅部材 |
CN115135043B (zh) * | 2022-07-18 | 2023-03-07 | 东莞市国盈电子有限公司 | 一种传感器线路板及其制造工艺 |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2004263300A (ja) * | 2003-02-12 | 2004-09-24 | Furukawa Techno Research Kk | ファインパターンプリント配線用銅箔とその製造方法 |
WO2007105635A1 (fr) * | 2006-03-10 | 2007-09-20 | Mitsui Mining & Smelting Co., Ltd. | Feuille de cuivre electrolytique traitee en surface et son procede de production |
JP2009004423A (ja) * | 2007-06-19 | 2009-01-08 | Hitachi Cable Ltd | キャリア箔付き銅箔 |
JP2009176768A (ja) * | 2008-01-21 | 2009-08-06 | Ube Ind Ltd | セミアディティブ法による銅配線絶縁フィルムの製造法、及びこれらから製造された銅配線絶縁フィルム |
JP2010013738A (ja) * | 2004-02-06 | 2010-01-21 | Furukawa Electric Co Ltd:The | 表面処理銅箔及びその製造方法 |
WO2012046804A1 (fr) * | 2010-10-06 | 2012-04-12 | 古河電気工業株式会社 | Feuille de cuivre et son procédé de fabrication, feuille de cuivre avec support et son procédé de fabrication, carte de circuit imprimé et carte de circuit imprimé multicouche |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3306404B2 (ja) * | 2000-01-28 | 2002-07-24 | 三井金属鉱業株式会社 | 表面処理銅箔の製造方法及びその製造方法で得られた表面処理銅箔を用いた銅張積層板 |
JP2004256832A (ja) * | 2003-02-24 | 2004-09-16 | Mitsui Mining & Smelting Co Ltd | 黒色化処理面を備える表面処理銅箔及びその表面処理銅箔を用いたプラズマディスプレイの前面パネル用の磁気遮蔽導電性メッシュ |
US7341796B2 (en) * | 2004-02-17 | 2008-03-11 | Nippon Mining & Metals Co., Ltd | Copper foil having blackened surface or layer |
US6979627B2 (en) | 2004-04-30 | 2005-12-27 | Freescale Semiconductor, Inc. | Isolation trench |
JP2006210689A (ja) * | 2005-01-28 | 2006-08-10 | Fukuda Metal Foil & Powder Co Ltd | 高周波プリント配線板用銅箔及びその製造方法 |
CN101180178B (zh) * | 2005-04-04 | 2011-11-09 | 宇部兴产株式会社 | 敷铜层压体 |
JP4958045B2 (ja) | 2006-10-27 | 2012-06-20 | 三井金属鉱業株式会社 | フレキシブル銅張積層板製造用の表面処理銅箔及びその表面処理銅箔を用いて得られるフレキシブル銅張積層板 |
WO2010046804A2 (fr) * | 2008-10-21 | 2010-04-29 | Alembic Limited | Procédé de préparation du losartan potassium forme i |
-
2014
- 2014-02-28 WO PCT/JP2014/055173 patent/WO2014133164A1/fr active Application Filing
- 2014-02-28 JP JP2014532134A patent/JP5705381B2/ja active Active
- 2014-02-28 CN CN201480010680.3A patent/CN105008593B/zh active Active
- 2014-02-28 MY MYPI2015702425A patent/MY181562A/en unknown
- 2014-02-28 KR KR1020157019621A patent/KR20150090265A/ko active Search and Examination
- 2014-02-28 KR KR1020167031887A patent/KR102116928B1/ko active IP Right Grant
- 2014-03-03 TW TW103106970A patent/TWI690625B/zh active
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2004263300A (ja) * | 2003-02-12 | 2004-09-24 | Furukawa Techno Research Kk | ファインパターンプリント配線用銅箔とその製造方法 |
JP2010013738A (ja) * | 2004-02-06 | 2010-01-21 | Furukawa Electric Co Ltd:The | 表面処理銅箔及びその製造方法 |
WO2007105635A1 (fr) * | 2006-03-10 | 2007-09-20 | Mitsui Mining & Smelting Co., Ltd. | Feuille de cuivre electrolytique traitee en surface et son procede de production |
JP2009004423A (ja) * | 2007-06-19 | 2009-01-08 | Hitachi Cable Ltd | キャリア箔付き銅箔 |
JP2009176768A (ja) * | 2008-01-21 | 2009-08-06 | Ube Ind Ltd | セミアディティブ法による銅配線絶縁フィルムの製造法、及びこれらから製造された銅配線絶縁フィルム |
WO2012046804A1 (fr) * | 2010-10-06 | 2012-04-12 | 古河電気工業株式会社 | Feuille de cuivre et son procédé de fabrication, feuille de cuivre avec support et son procédé de fabrication, carte de circuit imprimé et carte de circuit imprimé multicouche |
Cited By (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016035604A1 (fr) * | 2014-09-02 | 2016-03-10 | 三井金属鉱業株式会社 | Feuille de cuivre traitée en surface noircie et feuille de cuivre comprenant une feuille support |
JPWO2016093109A1 (ja) * | 2014-12-08 | 2017-09-14 | 三井金属鉱業株式会社 | プリント配線板の製造方法 |
JP2018138702A (ja) * | 2015-01-22 | 2018-09-06 | 三井金属鉱業株式会社 | キャリア付極薄銅箔及びその製造方法 |
KR20170057327A (ko) * | 2015-01-22 | 2017-05-24 | 미쓰이금속광업주식회사 | 캐리어 부착 극박 동박 및 그 제조 방법 |
JPWO2016117587A1 (ja) * | 2015-01-22 | 2017-07-06 | 三井金属鉱業株式会社 | キャリア付極薄銅箔及びその製造方法 |
WO2016117587A1 (fr) * | 2015-01-22 | 2016-07-28 | 三井金属鉱業株式会社 | Film de cuivre ultra-mince à support et son procédé de fabrication |
KR20160099439A (ko) | 2015-02-12 | 2016-08-22 | 후쿠다 킨조쿠 하쿠훈 코교 가부시키가이샤 | 처리 동박 및 그 처리 동박을 사용한 구리 피복 적층판 그리고 프린트 배선판 |
WO2016158775A1 (fr) * | 2015-03-31 | 2016-10-06 | 三井金属鉱業株式会社 | Feuille de cuivre rugosifiée, feuille de cuivre pourvue d'un support, plaque stratifiée cuivrée, et carte de circuit imprimé |
WO2017179416A1 (fr) * | 2016-04-14 | 2017-10-19 | 三井金属鉱業株式会社 | Feuille de cuivre traitée en surface, feuille de cuivre avec support et procédés de fabrication de stratifié revêtu de cuivre et carte de circuit imprimé l'utilisant |
JPWO2017179416A1 (ja) * | 2016-04-14 | 2019-02-21 | 三井金属鉱業株式会社 | 表面処理銅箔、キャリア付銅箔、並びにそれらを用いた銅張積層板及びプリント配線板の製造方法 |
TWI711139B (zh) * | 2016-04-14 | 2020-11-21 | 日商三井金屬鑛業股份有限公司 | 表面處理銅箔、附有載體之銅箔以及使用此等之貼銅層積板及印刷配線板之製造方法 |
JP2020183571A (ja) * | 2019-05-09 | 2020-11-12 | ナミックス株式会社 | 銅表面の加工装置 |
JP2020183573A (ja) * | 2019-05-09 | 2020-11-12 | ナミックス株式会社 | 複合銅部材 |
JP7409602B2 (ja) | 2019-05-09 | 2024-01-09 | ナミックス株式会社 | 複合銅部材 |
JP7456578B2 (ja) | 2019-05-09 | 2024-03-27 | ナミックス株式会社 | 銅表面の加工装置 |
KR20230159392A (ko) | 2021-03-26 | 2023-11-21 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 캐리어를 구비한 구리박, 동장 적층판 및 프린트 배선판 |
KR20230160813A (ko) | 2021-03-26 | 2023-11-24 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 캐리어를 구비한 구리박, 동장 적층판 및 프린트 배선판 |
KR20230141859A (ko) | 2021-03-29 | 2023-10-10 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 동장 적층판 및 프린트 배선판 |
KR20230161954A (ko) | 2021-03-29 | 2023-11-28 | 미쓰이금속광업주식회사 | 조화 처리 구리박, 동장 적층판 및 프린트 배선판 |
Also Published As
Publication number | Publication date |
---|---|
KR20150090265A (ko) | 2015-08-05 |
TWI690625B (zh) | 2020-04-11 |
KR102116928B1 (ko) | 2020-05-29 |
CN105008593B (zh) | 2018-08-24 |
KR20160135369A (ko) | 2016-11-25 |
JPWO2014133164A1 (ja) | 2017-02-09 |
TW201447051A (zh) | 2014-12-16 |
MY181562A (en) | 2020-12-29 |
JP5705381B2 (ja) | 2015-04-22 |
CN105008593A (zh) | 2015-10-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP5705381B2 (ja) | 黒色化表面処理銅箔、黒色化表面処理銅箔の製造方法、銅張積層板及びフレキシブルプリント配線板 | |
JP5686840B2 (ja) | 表面処理電解銅箔及びその表面処理銅箔を用いて得られる銅張積層板 | |
JP5475897B1 (ja) | 表面処理銅箔及びそれを用いた積層板、銅箔、プリント配線板、電子機器、並びに、プリント配線板の製造方法 | |
JP2013019056A5 (fr) | ||
WO2014073695A1 (fr) | Feuille de cuivre traitée en surface et stratifié l'utilisant | |
JP5706026B1 (ja) | 配線板用銅箔及び配線板 | |
JP2014141738A (ja) | 表面処理銅箔及びそれを用いた積層板 | |
JP5362923B1 (ja) | 表面処理銅箔及びそれを用いた積層板 | |
JP5432357B1 (ja) | 表面処理銅箔及びそれを用いた積層板、銅張積層板、プリント配線板並びに電子機器 | |
JP5855244B2 (ja) | 表面処理銅箔及びそれを用いた積層板、プリント配線板、電子機器及びプリント配線板を製造する方法 | |
JP5362922B1 (ja) | 表面処理銅箔及びそれを用いた積層板 | |
JP2014111824A (ja) | 表面処理銅箔及びそれを用いた積層板 | |
JP4999126B2 (ja) | 回路部品 | |
JP2014065974A (ja) | 表面処理銅箔及びそれを用いた積層板、銅張積層板、プリント配線板並びに電子機器 | |
TWI734976B (zh) | 表面處理銅箔、覆銅積層板及印刷線路板 | |
JP6845382B1 (ja) | 表面処理銅箔、銅張積層板、及びプリント配線板 | |
JP6081883B2 (ja) | 銅箔及びそれを用いた積層板、電子機器の製造方法、並びに、プリント配線板の製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref document number: 2014532134 Country of ref document: JP Kind code of ref document: A |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14757093 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 20157019621 Country of ref document: KR Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 14757093 Country of ref document: EP Kind code of ref document: A1 |