WO2014092200A1 - Holding membrane forming film - Google Patents
Holding membrane forming film Download PDFInfo
- Publication number
- WO2014092200A1 WO2014092200A1 PCT/JP2013/083628 JP2013083628W WO2014092200A1 WO 2014092200 A1 WO2014092200 A1 WO 2014092200A1 JP 2013083628 W JP2013083628 W JP 2013083628W WO 2014092200 A1 WO2014092200 A1 WO 2014092200A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- protective film
- film
- forming
- curing
- mass
- Prior art date
Abstract
Description
〔1〕第1表面と第2表面とを有する硬化性の保護膜形成用フィルムであって、
硬化後における第1表面のシリコンウエハに対する接着力が、硬化後における第2表面のシリコンウエハに対する接着力よりも高い保護膜形成用フィルム。 That is, the gist of the present invention is as follows.
[1] A curable protective film-forming film having a first surface and a second surface,
A film for forming a protective film, wherein the adhesive force of the first surface after curing to the silicon wafer is higher than the adhesive force of the second surface to the silicon wafer after curing.
第2表面を含む樹脂層における剥離剤の含有量が、第2表面を含む樹脂層を構成する全固形分のうち剥離剤を除く固形分100質量部に対して0.001~20質量部である〔8〕に記載の保護膜形成用フィルム。 [9] The content of the release agent in the resin layer including the first surface is 0 to 0.001 with respect to 100 parts by mass of the solid content excluding the release agent out of the total solids constituting the resin layer including the first surface. Mass part,
The content of the release agent in the resin layer including the second surface is 0.001 to 20 parts by mass with respect to 100 parts by mass of the solid content excluding the release agent out of the total solids constituting the resin layer including the second surface. The film for forming a protective film according to [8].
図1に示すように、保護膜形成用フィルム10は第1表面aと第2表面bとを有し、硬化後における第1表面aのシリコンウエハに対する接着力が、硬化後における第2表面bのシリコンウエハに対する接着力よりも高い。 [Film for forming a protective film]
As shown in FIG. 1, the protective film-forming
なお、保護膜形成用フィルムを硬化までの間被着体に仮着させておくための機能である(2)初期接着性は、感圧接着性であってもよく、熱により軟化して接着する性質であってもよい。(2)初期接着性は、通常バインダー成分の諸特性や、後述する無機フィラー(C)の配合量の調整などにより制御される。 The protective film-forming film can be provided with (1) sheet shape maintainability and (3) curability by adding a binder component. As the binder component, the polymer component (A) and the curable component (B ) Containing the first binder component or the second binder component containing the curable polymer component (AB) having the properties of the component (A) and the component (B).
In addition, it is a function for temporarily attaching the protective film-forming film to the adherend until it is cured. (2) The initial adhesiveness may be pressure-sensitive adhesiveness, and is softened and bonded by heat. It may be a property to do. (2) The initial adhesiveness is usually controlled by adjusting various properties of the binder component and adjusting the blending amount of the inorganic filler (C) described later.
第1のバインダー成分は、重合体成分(A)と硬化性成分(B)を含有することにより、保護膜形成用フィルムにシート形状維持性と硬化性を付与する。なお、第1のバインダー成分は、第2のバインダー成分と区別する便宜上、硬化性重合体成分(AB)を含有しない。 (First binder component)
A 1st binder component provides a sheet | seat shape maintainability and curability to the film for protective film formation by containing a polymer component (A) and a sclerosing | hardenable component (B). In addition, the 1st binder component does not contain a curable polymer component (AB) for the convenience of distinguishing from a 2nd binder component.
重合体成分(A)は、保護膜形成用フィルムにシート形状維持性を付与することを主目的として保護膜形成用フィルムに添加される。
上記の目的を達成するため、重合体成分(A)の重量平均分子量(Mw)は、通常20,000以上であり、20,000~3,000,000であることが好ましい。重量平均分子量(Mw)の値は、ゲル・パーミエーション・クロマトグラフィー法(GPC)法(ポリスチレン標準)により測定される場合の値である。このような方法による測定は、たとえば、東ソー社製の高速GPC装置「HLC-8120GPC」に、高速カラム「TSK gurd column HXL-H」、「TSK Gel GMHXL」、「TSK Gel G2000 HXL」(以上、全て東ソー社製)をこの順序で連結したものを用い、カラム温度:40℃、送液速度:1.0mL/分の条件で、検出器を示差屈折率計として行われる。
なお、後述する硬化性重合体(AB)と区別する便宜上、重合体成分(A)は後述する硬化機能官能基を有しない。 (A) Polymer component The polymer component (A) is added to the protective film-forming film mainly for the purpose of imparting sheet shape maintenance to the protective film-forming film.
In order to achieve the above object, the weight average molecular weight (Mw) of the polymer component (A) is usually 20,000 or more, preferably 20,000 to 3,000,000. The value of the weight average molecular weight (Mw) is a value when measured by a gel permeation chromatography method (GPC) method (polystyrene standard). The measurement by such a method is carried out, for example, by using a high-speed GPC apparatus “HLC-8120GPC” manufactured by Tosoh Corporation and a high-speed column “TSK gold column H XL- H”, “TSK Gel GMH XL ”, “TSK Gel G2000 H XL ”. (The above, all manufactured by Tosoh Corporation) are connected in this order, and the detector is used as a differential refractometer at a column temperature of 40 ° C. and a liquid feed rate of 1.0 mL / min.
In addition, for convenience to distinguish from the curable polymer (AB) described later, the polymer component (A) does not have a curing functional functional group described later.
重合体成分(A)としては、アクリル系重合体(A1)が好ましく用いられる。アクリル系重合体(A1)のガラス転移温度(Tg)は、好ましくは-60~50℃、より好ましくは-50~40℃、さらに好ましくは-40~30℃の範囲にある。アクリル系重合体(A1)のガラス転移温度が高いと保護膜形成用フィルムのプローブタック値は低下する傾向があり、また、硬化後における接着性が低下する傾向がある。このような傾向があることから、2層以上の樹脂層から保護膜形成用フィルムを形成する場合、第2表面bを含む樹脂層に用いられるアクリル系重合体(A1)のガラス転移温度(Tg)は、-40~-5℃の範囲にあることが特に好ましい。 (A1) As the acrylic polymer polymer component (A), acrylic polymer (A1) is preferably used. The glass transition temperature (Tg) of the acrylic polymer (A1) is preferably in the range of −60 to 50 ° C., more preferably −50 to 40 ° C., and further preferably −40 to 30 ° C. When the glass transition temperature of the acrylic polymer (A1) is high, the probe tack value of the protective film-forming film tends to decrease, and the adhesiveness after curing tends to decrease. Since there exists such a tendency, when forming the film for protective film formation from two or more resin layers, the glass transition temperature (Tg) of the acrylic polymer (A1) used for the resin layer containing the 2nd surface b ) Is particularly preferably in the range of −40 to −5 ° C.
(メタ)アクリル酸エステルとしては、アルキル基の炭素数が1~18であるアルキル(メタ)アクリレート、具体的にはメチル(メタ)アクリレート、エチル(メタ)アクリレート、プロピル(メタ)アクリレート、ブチル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレートなど;環状骨格を有する(メタ)アクリレート、具体的にはシクロアルキル(メタ)アクリレート、ベンジル(メタ)アクリレート、イソボルニル(メタ)アクリレート、ジシクロペンタニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、ジシクロペンテニルオキシエチル(メタ)アクリレート、イミド(メタ)アクリレートなどが挙げられる。また、後述する水酸基を有する単量体、カルボキシル基を有する単量体、アミノ基を有する単量体として例示するもののうち、(メタ)アクリル酸エステルであるものを例示することができる。 The acrylic polymer (A1) contains (meth) acrylic acid ester in at least a constituent monomer.
Examples of (meth) acrylic acid esters include alkyl (meth) acrylates having an alkyl group having 1 to 18 carbon atoms, specifically methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl ( (Meth) acrylate, 2-ethylhexyl (meth) acrylate, etc .; (meth) acrylate having a cyclic skeleton, specifically cycloalkyl (meth) acrylate, benzyl (meth) acrylate, isobornyl (meth) acrylate, dicyclopentanyl ( Examples include meth) acrylate, dicyclopentenyl (meth) acrylate, dicyclopentenyloxyethyl (meth) acrylate, and imide (meth) acrylate. Moreover, what is (meth) acrylic acid ester can be illustrated among what is illustrated as a monomer which has a hydroxyl group mentioned later, a monomer which has a carboxyl group, and a monomer which has an amino group.
また、重合体成分(A)として、ポリエステル、フェノキシ樹脂(後述する硬化性重合体(AB)と区別する便宜上、エポキシ基を有しないものに限る。)、ポリカーボネート、ポリエーテル、ポリウレタン、ポリシロキサン、ゴム系重合体またはこれらの2種以上が結合したものから選ばれる非アクリル系樹脂(A2)の1種単独または2種以上の組み合わせを用いてもよい。このような樹脂としては、重量平均分子量が20,000~100,000のものが好ましく、20,000~80,000のものがさらに好ましい。 (A2) Non-acrylic resin In addition, as the polymer component (A), polyester, phenoxy resin (for the purpose of distinguishing from the curable polymer (AB) described later, limited to those having no epoxy group), polycarbonate, poly One type of non-acrylic resin (A2) selected from ethers, polyurethanes, polysiloxanes, rubber polymers, or a combination of two or more of these may be used, or a combination of two or more types. Such a resin preferably has a weight average molecular weight of 20,000 to 100,000, more preferably 20,000 to 80,000.
硬化性成分(B)は、保護膜形成用フィルムに硬化性を付与することを主目的として保護膜形成用フィルムに添加される。硬化性成分(B)は、熱硬化性成分(B1)、またはエネルギー線硬化性成分(B2)を用いることができる。また、これらを組み合わせて用いてもよい。熱硬化性成分(B1)は、少なくとも加熱により反応する官能基を有する化合物を含有する。また、エネルギー線硬化性成分(B2)は、エネルギー線照射により反応する官能基を有する化合物(B21)を含有し、紫外線、電子線等のエネルギー線の照射を受けると重合硬化する。これらの硬化性成分が有する官能基同士が反応し、三次元網目構造が形成されることにより硬化が実現される。硬化性成分(B)は、重合体成分(A)と組み合わせて用いるため、保護膜形成用フィルムを形成するための塗工用組成物の粘度を抑制し、取り扱い性を向上させる等の観点から、通常その重量平均分子量(Mw)は、10,000以下であり、100~10,000であることが好ましい。 (B) Curable component The curable component (B) is added to the protective film-forming film mainly for the purpose of imparting curability to the protective film-forming film. As the curable component (B), a thermosetting component (B1) or an energy beam curable component (B2) can be used. Moreover, you may use combining these. The thermosetting component (B1) contains at least a compound having a functional group that reacts by heating. The energy ray-curable component (B2) contains a compound (B21) having a functional group that reacts by irradiation with energy rays, and is polymerized and cured when irradiated with energy rays such as ultraviolet rays and electron beams. Curing is realized by the functional groups of these curable components reacting to form a three-dimensional network structure. Since the curable component (B) is used in combination with the polymer component (A), the viscosity of the coating composition for forming the protective film-forming film is suppressed, and the handleability is improved. Usually, its weight average molecular weight (Mw) is 10,000 or less, preferably 100 to 10,000.
熱硬化性成分としては、たとえば、エポキシ系熱硬化性成分が好ましい。
エポキシ系熱硬化性成分は、エポキシ基を有する化合物(B11)を含有し、エポキシ基を有する化合物(B11)と熱硬化剤(B12)を組み合わせたものを用いることが好ましい。 (B1) Thermosetting component As the thermosetting component, for example, an epoxy thermosetting component is preferable.
The epoxy thermosetting component preferably contains a compound (B11) having an epoxy group and a combination of a compound (B11) having an epoxy group and a thermosetting agent (B12).
エポキシ基を有する化合物(B11)(以下、「エポキシ化合物(B11)」ということがある。)としては、従来公知のものを用いることができる。具体的には、多官能系エポキシ樹脂や、ビスフェノールAジグリシジルエーテルやその水添物、オルソクレゾールノボラックエポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、ビフェニル型エポキシ樹脂、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、フェニレン骨格型エポキシ樹脂など、分子中に2官能以上有するエポキシ化合物が挙げられる。これらは1種単独で、または2種以上を組み合わせて用いることができる。 (B11) Compound having an epoxy group As the compound (B11) having an epoxy group (hereinafter sometimes referred to as “epoxy compound (B11)”), a conventionally known compound can be used. Specifically, polyfunctional epoxy resin, bisphenol A diglycidyl ether and its hydrogenated product, orthocresol novolac epoxy resin, dicyclopentadiene type epoxy resin, biphenyl type epoxy resin, bisphenol A type epoxy resin, bisphenol F type Examples thereof include epoxy compounds having two or more functional groups in the molecule, such as epoxy resins and phenylene skeleton type epoxy resins. These can be used individually by 1 type or in combination of 2 or more types.
このような傾向があることから、2層以上の樹脂層から保護膜形成用フィルムを形成する場合は、第2表面bを含む樹脂層において、エポキシ化合物(B11)として、常温において固体であるもののみを用いるときは、重合体成分(A)100質量部に対して、エポキシ化合物(B11)が70~150質量部含まれることが特に好ましい。 When the epoxy compound (B11) is used, the protective film-forming film preferably contains 1 to 1500 parts by mass of the epoxy compound (B11) with respect to 100 parts by mass of the polymer component (A). The content is preferably 3 to 1200 parts by mass. When there are few epoxy compounds (B11), there exists a tendency for the adhesiveness after hardening of the film for protective film formation to fall. Further, when only the epoxy compound (B11) that is solid at room temperature is used, if the epoxy compound (B11) is small, that is, if the polymer component (A) is relatively large, the protective film is formed. There is a tendency for the probe tack value of the film to increase. The normal temperature indicates 25 ° C., and the same applies hereinafter.
Because of this tendency, when forming a protective film-forming film from two or more resin layers, the resin layer containing the second surface b is a solid at room temperature as an epoxy compound (B11). In the case of using only the polymer component, it is particularly preferable that 70 to 150 parts by mass of the epoxy compound (B11) is contained with respect to 100 parts by mass of the polymer component (A).
熱硬化剤(B12)は、エポキシ化合物(B11)に対する硬化剤として機能する。好ましい熱硬化剤としては、1分子中にエポキシ基と反応しうる官能基を2個以上有する化合物が挙げられる。その官能基としてはフェノール性水酸基、アルコール性水酸基、アミノ基、カルボキシル基および酸無水物などが挙げられる。これらのうち好ましくはフェノール性水酸基、アミノ基、酸無水物などが挙げられ、さらに好ましくはフェノール性水酸基、アミノ基が挙げられる。 (B12) Thermosetting agent The thermosetting agent (B12) functions as a curing agent for the epoxy compound (B11). A preferable thermosetting agent includes a compound having two or more functional groups capable of reacting with an epoxy group in one molecule. Examples of the functional group include a phenolic hydroxyl group, an alcoholic hydroxyl group, an amino group, a carboxyl group, and an acid anhydride. Of these, phenolic hydroxyl groups, amino groups, acid anhydrides and the like are preferable, and phenolic hydroxyl groups and amino groups are more preferable.
硬化促進剤(B13)を、保護膜形成用フィルムの熱硬化の速度を調整するために用いてもよい。硬化促進剤(B13)は、特に、熱硬化性成分(B1)として、エポキシ系熱硬化性成分を用いるときに好ましく用いられる。 (B13) Curing accelerator A curing accelerator (B13) may be used to adjust the rate of thermal curing of the protective film-forming film. The curing accelerator (B13) is particularly preferably used when an epoxy thermosetting component is used as the thermosetting component (B1).
保護膜形成用フィルムがエネルギー線硬化性成分を含有することで、多量のエネルギーと長い時間を要する熱硬化工程を行うことなく保護膜形成用フィルムの硬化を行うことができる。これにより、製造コストの低減を図ることができる。
エネルギー線硬化性成分は、エネルギー線照射により反応する官能基を有する化合物(B21)を単独で用いてもよいが、エネルギー線照射により反応する官能基を有する化合物(B21)と光重合開始剤(B22)を組み合わせたものを用いることが好ましい。 (B2) The film for forming the protective film includes an energy beam curable component, so that the film for forming the protective film is cured without performing a heat curing step that requires a large amount of energy and a long time. Can do. Thereby, the manufacturing cost can be reduced.
As the energy ray-curable component, the compound (B21) having a functional group that reacts by irradiation with energy rays may be used alone, but the compound (B21) having a functional group that reacts by irradiation with energy rays and a photopolymerization initiator ( It is preferable to use a combination of B22).
エネルギー線照射により反応する官能基を有する化合物(B21)(以下「エネルギー線反応性化合物(B21)」ということがある。)としては、具体的には、トリメチロールプロパントリアクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、ジペンタエリスリトールモノヒドロキシペンタアクリレート、ジペンタエリスリトールヘキサアクリレートあるいは1,4-ブチレングリコールジアクリレート、1,6-ヘキサンジオールジアクリレート等のアクリレート系化合物が挙げられ、また、オリゴエステルアクリレート、ウレタンアクリレート系オリゴマー、エポキシアクリレート、ポリエーテルアクリレートおよびイタコン酸オリゴマーなどのアクリレート系化合物等の重合構造を有するアクリレート化合物であって、比較的低分子量のものが挙げられる。このような化合物は、分子内に少なくとも1つの重合性二重結合を有する。 (B21) Compound having a functional group that reacts upon irradiation with energy rays Compound (B21) having a functional group that reacts upon irradiation with energy rays (hereinafter sometimes referred to as “energy ray-reactive compound (B21)”) Specifically, trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol monohydroxypentaacrylate, dipentaerythritol hexaacrylate, 1,4-butylene glycol diacrylate, 1,6-hexanediol diacrylate Examples include acrylate compounds such as acrylates, oligoester acrylates, urethane acrylate oligomers, epoxy acrylates, polyether acrylates, and esters. A acrylate compounds having a polymeric structure of acrylate compounds such as Con acid oligomer include those of relatively low molecular weight. Such a compound has at least one polymerizable double bond in the molecule.
エネルギー線反応性化合物(B21)に光重合開始剤(B22)を組み合わせることで、重合硬化時間を短くし、ならびに光線照射量を少なくすることができる。 (B22) By combining the photopolymerization initiator energy beam reactive compound (B21) with the photopolymerization initiator (B22), the polymerization curing time can be shortened and the amount of light irradiation can be reduced.
光重合開始剤(B22)の配合割合が0.1質量部未満であると光重合の不足で満足な硬化性が得られないことがあり、10質量部を超えると光重合に寄与しない残留物が生成し、不具合の原因となることがある。 The blending ratio of the photopolymerization initiator (B22) is preferably 0.1 to 10 parts by mass and more preferably 1 to 5 parts by mass with respect to 100 parts by mass of the energy ray reactive compound (B21). .
If the blending ratio of the photopolymerization initiator (B22) is less than 0.1 parts by mass, sufficient curability may not be obtained due to insufficient photopolymerization, and if it exceeds 10 parts by mass, the residue does not contribute to photopolymerization. May cause a malfunction.
第2のバインダー成分は、硬化性重合体成分(AB)を含有することにより、保護膜形成用フィルムにシート形状維持性と硬化性を付与する。 (Second binder component)
A 2nd binder component provides sheet shape maintenance property and curability to the film for protective film formation by containing a curable polymer component (AB).
硬化性重合体成分は、硬化機能官能基を有する重合体である。硬化機能官能基は、互いに反応して三次元網目構造を構成しうる官能基であり、加熱により反応する官能基や、エネルギー線により反応する官能基が挙げられる。
硬化機能官能基は、硬化性重合体(AB)の骨格となる連続構造の単位中に付加していてもよいし、末端に付加していてもよい。硬化機能官能基が硬化性重合体成分(AB)の骨格となる連続構造の単位中に付加している場合、硬化機能官能基は側鎖に付加していてもよいし、主鎖に直接付加していてもよい。硬化性重合体成分(AB)の重量平均分子量(Mw)は、保護膜形成用フィルムにシート形状維持性を付与する目的を達成する観点から、通常20,000以上である。 (AB) Curable polymer component The curable polymer component is a polymer having a functional functional group. The curing functional group is a functional group that can react with each other to form a three-dimensional network structure, and examples thereof include a functional group that reacts by heating and a functional group that reacts by energy rays.
The functional functional group may be added to the unit of a continuous structure that becomes the skeleton of the curable polymer (AB) or may be added to the terminal. When the functional functional group is added in the unit of the continuous structure that becomes the skeleton of the curable polymer component (AB), the functional functional group may be added to the side chain or directly to the main chain. You may do it. The weight average molecular weight (Mw) of the curable polymer component (AB) is usually 20,000 or more from the viewpoint of achieving the purpose of imparting sheet shape maintainability to the protective film-forming film.
また、上述のアクリル系重合体(A1)と同様の重合体であって、単量体として、エポキシ基を有する単量体を用いて重合したもの(エポキシ基含有アクリル系重合体)であってもよい。このような単量体としては、たとえばグリシジル(メタ)アクリレート等のグリシジル基を有する(メタ)アクリル酸エステルが挙げられる。
エポキシ基含有アクリル系重合体を用いる場合、その好ましい態様はアクリル系重合体(A1)と同様である。 An example of a functional group that reacts by heating is an epoxy group. Examples of the curable polymer component (AB) having an epoxy group include a high molecular weight epoxy group-containing compound and a phenoxy resin having an epoxy group.
Moreover, it is a polymer similar to the above-mentioned acrylic polymer (A1), which is polymerized using a monomer having an epoxy group as a monomer (epoxy group-containing acrylic polymer). Also good. Examples of such monomers include (meth) acrylic acid esters having a glycidyl group such as glycidyl (meth) acrylate.
When an epoxy group-containing acrylic polymer is used, the preferred embodiment is the same as that of the acrylic polymer (A1).
また、たとえば側鎖に水酸基等の官能基Xを有する原料重合体に、官能基Xと反応しうる官能基Y(たとえば、官能基Xが水酸基である場合にはイソシアネート基等)およびエネルギー線照射により反応する官能基を有する低分子化合物を反応させて調製した重合体を用いてもよい。
この場合において、原料重合体が上述のアクリル系重合体(A1)に該当するときは、その原料重合体の好ましい態様は、アクリル系重合体(A1)と同様である。 Examples of the functional group that reacts with energy rays include a (meth) acryloyl group. As the curable polymer component (AB) having a functional group that reacts with energy rays, an acrylate compound having a polymer structure such as polyether acrylate, and the like having a high molecular weight can be used.
In addition, for example, a raw material polymer having a functional group X such as a hydroxyl group in a side chain, a functional group Y that can react with the functional group X (for example, an isocyanate group when the functional group X is a hydroxyl group) and energy beam irradiation Alternatively, a polymer prepared by reacting a low molecular compound having a functional group that reacts with the above may be used.
In this case, when the raw material polymer corresponds to the above-mentioned acrylic polymer (A1), the preferred mode of the raw material polymer is the same as that of the acrylic polymer (A1).
第1表面aを含む樹脂層にアクリル系重合体(A1)を用いる場合、第2表面bを含む樹脂層におけるアクリル系重合体(A1)のガラス転移温度(Tg)と同様に、そのガラス転移温度(Tg)は、-40~-5℃の範囲にあることが好ましい。
第1表面aを含む樹脂層にアクリル系重合体(A1)を用いる場合、第2表面bを含む樹脂層におけるアクリル系重合体(A1)の重量平均分子量と同様に、その重量平均分子量は600,000~1,200,000であることが好ましい。
第1表面aを含む樹脂層において、エポキシ化合物(B11)として、常温において固体であるもののみを用いるときは、第2表面bを含む樹脂層におけるエポキシ化合物(B11)の含有量と同様に、重合体成分(A)100質量部に対して、エポキシ化合物(B11)が70~150質量部含まれることが好ましい。 As described above, depending on the main composition of the binder component, the first surface a is included in the case where a substantial difference is not caused between the adhesive force on the first surface and the adhesive force on the second surface of the protective film-forming film. The following can be said about the resin layer.
When the acrylic polymer (A1) is used for the resin layer including the first surface a, the glass transition temperature (Tg) of the acrylic polymer (A1) in the resin layer including the second surface b is similar to the glass transition temperature. The temperature (Tg) is preferably in the range of −40 to −5 ° C.
When the acrylic polymer (A1) is used for the resin layer including the first surface a, the weight average molecular weight is 600, similar to the weight average molecular weight of the acrylic polymer (A1) in the resin layer including the second surface b. , 1,000 to 1,200,000 is preferable.
In the resin layer including the first surface a, when only the epoxy compound (B11) that is solid at room temperature is used, similarly to the content of the epoxy compound (B11) in the resin layer including the second surface b, It is preferable that 70 to 150 parts by mass of the epoxy compound (B11) is contained with respect to 100 parts by mass of the polymer component (A).
保護膜形成用フィルムは、無機フィラー(C)を含有していてもよい。無機フィラー(C)を保護膜形成用フィルムに配合することにより、硬化後の保護膜における熱膨張係数を調整することが可能となり、被着体に対して硬化後の保護膜の熱膨張係数を最適化することで半導体装置の信頼性を向上させることができる。また、硬化後の保護膜の吸湿性を低減させることも可能となる。
さらに、保護膜にレーザーマーキングを施すことにより、レーザー光により削り取られた部分に無機フィラー(C)が露出して、反射光が拡散するために白色に近い色を呈する。これにより、保護膜形成用フィルムが後述する着色剤(D)を含有する場合、レーザーマーキング部分と他の部分にコントラスト差が得られ、印字が明瞭になるという効果がある。 (C) The film for forming an inorganic filler protective film may contain an inorganic filler (C). By blending the inorganic filler (C) in the protective film-forming film, it is possible to adjust the thermal expansion coefficient in the cured protective film, and the thermal expansion coefficient of the protective film after curing with respect to the adherend. By optimizing, the reliability of the semiconductor device can be improved. It is also possible to reduce the hygroscopicity of the protective film after curing.
Furthermore, by applying laser marking to the protective film, the inorganic filler (C) is exposed in the portion scraped off by the laser light, and the reflected light diffuses to exhibit a color close to white. Thereby, when the film for protective film formation contains the coloring agent (D) mentioned later, there is an effect that a contrast difference is obtained between the laser marking portion and other portions, and the printing becomes clear.
保護膜形成用フィルムには、着色剤(D)を配合することができる。着色剤を配合することで、半導体装置を機器に組み込んだ際に、周囲の装置から発生する赤外線等による半導体装置の誤作動を防止することができる。また、レーザーマーキング等の手段により保護膜に刻印を行った場合に、文字、記号等のマークが認識しやすくなるという効果がある。すなわち、保護膜が形成された半導体装置や半導体チップでは、保護膜の表面に品番等が通常レーザーマーキング法(レーザー光により保護膜表面を削り取り印字を行う方法)により印字されるが、保護膜が着色剤(D)を含有することで、保護膜のレーザー光により削り取られた部分とそうでない部分のコントラスト差が充分に得られ、視認性が向上する。 (D) Colorant (D) can be mix | blended with the film for colorant protective film formation. By blending the colorant, malfunction of the semiconductor device due to infrared rays or the like generated from surrounding devices when the semiconductor device is incorporated into equipment can be prevented. In addition, when the protective film is engraved by means such as laser marking, there is an effect that marks such as characters and symbols can be easily recognized. That is, in a semiconductor device or semiconductor chip on which a protective film is formed, the product number or the like is usually printed on the surface of the protective film by a laser marking method (a method in which the surface of the protective film is scraped off and printed). By containing the colorant (D), a sufficient difference in contrast between the portion of the protective film scraped by the laser beam and the portion not removed is obtained, and the visibility is improved.
着色剤(D)の配合量は、保護膜形成用フィルムを構成する全固形分100質量部に対して、好ましくは0.1~35質量部、さらに好ましくは0.5~25質量部、特に好ましくは1~15質量部である。 As the colorant, organic or inorganic pigments and dyes are used. Among these, black pigments are preferable from the viewpoint of electromagnetic wave and infrared shielding properties. Examples of the black pigment include carbon black, iron oxide, manganese dioxide, aniline black, activated carbon, and the like, but are not limited thereto. Carbon black is particularly preferable from the viewpoint of increasing the reliability of the semiconductor device. A coloring agent (D) may be used individually by 1 type, and may be used in combination of 2 or more type.
The blending amount of the colorant (D) is preferably 0.1 to 35 parts by weight, more preferably 0.5 to 25 parts by weight, particularly 100 parts by weight of the total solid content constituting the protective film-forming film. The amount is preferably 1 to 15 parts by mass.
無機物と反応する官能基および有機官能基と反応する官能基を有するカップリング剤(E)を、保護膜形成用フィルムの被着体に対する接着性、密着性および/または保護膜の凝集性を向上させるために用いてもよい。また、カップリング剤(E)を使用することで、保護膜形成用フィルムを硬化して得られる保護膜の耐熱性を損なうことなく、その耐水性を向上させることができる。このようなカップリング剤としては、チタネート系カップリング剤、アルミネート系カップリング剤、シランカップリング剤等が挙げられる。これらのうちでも、シランカップリング剤が好ましい。 (E) Coupling agent Adhesiveness, adhesion, and / or protection of a coupling agent (E) having a functional group that reacts with an inorganic substance and a functional group that reacts with an organic functional group to an adherend of a protective film-forming film. It may be used to improve the cohesiveness of the film. Moreover, the water resistance can be improved by using a coupling agent (E), without impairing the heat resistance of the protective film obtained by hardening | curing the film for protective film formation. Examples of such coupling agents include titanate coupling agents, aluminate coupling agents, silane coupling agents, and the like. Of these, silane coupling agents are preferred.
このようなシランカップリング剤としてはγ-グリシドキシプロピルトリメトキシシラン、γ-グリシドキシプロピルメチルジエトキシシラン、β-(3,4-エポキシシクロヘキシル)エチルトリメトキシシラン、γ-(メタクリロキシプロピル)トリメトキシシラン、γ-アミノプロピルトリメトキシシラン、N-6-(アミノエチル)-γ-アミノプロピルトリメトキシシラン、N-6-(アミノエチル)-γ-アミノプロピルメチルジエトキシシラン、N-フェニル-γ-アミノプロピルトリメトキシシラン、γ-ウレイドプロピルトリエトキシシラン、γ-メルカプトプロピルトリメトキシシラン、γ-メルカプトプロピルメチルジメトキシシラン、ビス(3-トリエトキシシリルプロピル)テトラスルファン、メチルトリメトキシシラン、メチルトリエトキシシラン、ビニルトリメトキシシラン、ビニルトリアセトキシシラン、イミダゾールシランなどが挙げられる。これらは1種単独で、または2種以上混合して使用することができる。 As the silane coupling agent, the functional group that reacts with the organic functional group is a group that reacts with the functional group of the polymer component (A), the curable component (B), the curable polymer component (AB), and the like. Some silane coupling agents are preferably used.
Such silane coupling agents include γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, γ- (methacryloxy). Propyl) trimethoxysilane, γ-aminopropyltrimethoxysilane, N-6- (aminoethyl) -γ-aminopropyltrimethoxysilane, N-6- (aminoethyl) -γ-aminopropylmethyldiethoxysilane, N -Phenyl-γ-aminopropyltrimethoxysilane, γ-ureidopropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, bis (3-triethoxysilylpropyl) tetrasulfane, methyltri Methoxysilane , Methyltriethoxysilane, vinyltrimethoxysilane, vinyltriacetoxysilane, and imidazolesilane. These can be used individually by 1 type or in mixture of 2 or more types.
保護膜形成用フィルムの第1表面における接着力と第2表面における接着力を調整するために、剥離剤を添加することもできる。剥離剤としては、ポリジメチルシロキサン、ポリフェニルメチルシロキサン、ポリジフェニルシロキサンなどのシリコーン化合物やフッ素化合物が挙げられる。
これらの中でも、シリコーン化合物が好ましく、側鎖として芳香環含有基を有するオルガノポリシロキサンであって、かつ、25℃における動粘度が50~100,000mm2/sであるものがより好ましい。ポリシロキサンとは、-Si(X)2-O-で表される単位構造(Xは側鎖を表す)が複数連結した化合物であり、この単位構造の数は特に限定されないが、通常3以上である。単位構造の数の増減により、上記の動粘度の値を制御することができる。 (F) In order to adjust the adhesive force on the first surface and the adhesive force on the second surface of the release agent protective film-forming film, a release agent may be added. Examples of the release agent include silicone compounds such as polydimethylsiloxane, polyphenylmethylsiloxane, and polydiphenylsiloxane, and fluorine compounds.
Among these, a silicone compound is preferable, and an organopolysiloxane having an aromatic ring-containing group as a side chain and a kinematic viscosity at 25 ° C. of 50 to 100,000 mm 2 / s is more preferable. Polysiloxane is a compound in which a plurality of unit structures represented by —Si (X) 2 —O— (X represents a side chain) is connected, and the number of unit structures is not particularly limited, but usually 3 or more It is. The kinematic viscosity value can be controlled by increasing or decreasing the number of unit structures.
前記芳香環含有基の例としては、フェニル基、アラルキル基が挙げられる。ここでいうアラルキル基とは、アルキル部が直鎖状または分岐鎖状であり、アルキル部の炭素数が好ましくは1~5、より好ましくは1~3であり、アリール部の炭素数が好ましくは6~10、より好ましくは6であるアラルキル基である。アラルキル基の好ましい例としては、ベンジル基、フェニルエチル基、フェニルプロピル基、フェニルイソプロピル基が挙げられる。前記芳香環含有基としては、アラルキル基が好ましい。 The silicone compound lowers the adhesion with the support by the siloxane portion of the organopolysiloxane and has a high lipid solubility by having the above aromatic ring-containing group in the side chain, and other components in the composition for forming a protective film High compatibility with. In addition, the curing component (B) in the composition for forming a protective film often has an aromatic ring as a constituent component, and in such a case, the compatibility of the silicone compound with the aromatic ring-containing group further increases. .
Examples of the aromatic ring-containing group include a phenyl group and an aralkyl group. The aralkyl group here means that the alkyl part is linear or branched, the alkyl part preferably has 1 to 5 carbon atoms, more preferably 1 to 3 carbon atoms, and the aryl part preferably has carbon atoms. An aralkyl group of 6 to 10, more preferably 6. Preferable examples of the aralkyl group include a benzyl group, a phenylethyl group, a phenylpropyl group, and a phenylisopropyl group. The aromatic ring-containing group is preferably an aralkyl group.
保護膜形成用フィルムには、上記の他に、必要に応じて各種添加剤が配合されてもよい。各種添加剤としては、レベリング剤、可塑剤、帯電防止剤、酸化防止剤、イオン捕捉剤、ゲッタリング剤、連鎖移動剤などが挙げられる。 (G) In addition to the above, various additives may be added to the general-purpose additive protective film-forming film as necessary. Examples of various additives include leveling agents, plasticizers, antistatic agents, antioxidants, ion scavengers, gettering agents, chain transfer agents, and the like.
かかる溶媒としては、酢酸エチル、酢酸メチル、ジエチルエーテル、ジメチルエーテル、アセトン、メチルエチルケトン、アセトニトリル、ヘキサン、シクロヘキサン、トルエン、ヘプタンなどが挙げられる。 The film for forming a protective film is obtained, for example, using a composition (composition for forming a protective film) obtained by mixing the above components at an appropriate ratio. The composition for forming a protective film may be diluted with a solvent in advance, or may be added to the solvent during mixing. Moreover, you may dilute with a solvent at the time of use of the composition for protective film formation.
Examples of such a solvent include ethyl acetate, methyl acetate, diethyl ether, dimethyl ether, acetone, methyl ethyl ketone, acetonitrile, hexane, cyclohexane, toluene, heptane and the like.
たとえば、保護膜形成用フィルムを工程フィルム上に製膜することができる。製膜は、工程フィルム上に保護膜形成用フィルムを形成するための組成物をロールナイフコーター、グラビアコーター、ダイコーター、リバースコーターなど一般に公知の方法にしたがって塗工し、乾燥させることによって行う。
工程フィルムは、そのまま後述する支持シートやカバーフィルムとして用いることができる。また、保護膜形成用フィルムを、その製膜後に工程フィルムから支持シートやカバーフィルムに転写してもよい。工程フィルムが、支持シートまたはカバーフィルムのいずれか一方であり、かつ、転写される材料が、支持シートまたはカバーフィルムの他の一方であってもよい。 The manufacturing method of the film for protective film formation concerning this invention is not specifically limited.
For example, a protective film-forming film can be formed on the process film. Film formation is performed by applying a composition for forming a protective film-forming film on the process film according to a generally known method such as a roll knife coater, gravure coater, die coater, reverse coater, and drying.
The process film can be used as it is as a support sheet or cover film which will be described later. Moreover, you may transfer the film for protective film formation from a process film to a support sheet or a cover film after the film formation. The process film may be either the support sheet or the cover film, and the material to be transferred may be the other one of the support sheet or the cover film.
保護膜形成用複合シートは、保護膜形成用フィルムの第2表面側に支持シートを剥離可能に形成して得られる。保護膜形成用複合シートの形状は、枚葉のものに限られず、長尺の帯状のものであってもよく、これを巻収してもよい。支持シートとしては、剥離シートが挙げられ、また、後述する粘着シートを用いることができる。 [Composite sheet for protective film formation]
The composite sheet for forming a protective film is obtained by forming a support sheet on the second surface side of the film for forming a protective film so as to be peelable. The shape of the composite sheet for forming a protective film is not limited to a single sheet, and may be a long strip or roll it up. Examples of the support sheet include a release sheet, and an adhesive sheet described later can be used.
保護膜形成用複合シートの構成がかかる構成であると、保護膜形成用複合シートが、ダイシング工程において被着体を支持するためのダイシングシートとして機能する場合に支持シートと保護膜形成用フィルムの間の密着性が保たれ、ダイシング工程において保護膜形成用フィルム付チップが支持シートから剥がれることを抑制するという効果が得られる。保護膜形成用複合シートが、ダイシング工程において被着体を支持するためのダイシングシートとして機能する場合、ダイシング工程において保護膜形成用フィルム付ウエハに別途ダイシングシートを貼り合せてダイシングをする必要がなくなり、半導体装置の製造工程を簡略化できる。 The pressure-sensitive adhesive layer includes various conventionally known pressure-sensitive adhesives (for example, rubber-based, acrylic-based, silicone-based, urethane-based, vinyl ether-based general-purpose pressure-sensitive adhesives, pressure-sensitive adhesives, energy ray-curable pressure-sensitive adhesives, A thermal expansion component-containing pressure-sensitive adhesive or the like).
When the composition of the protective film-forming composite sheet is such a configuration, when the protective film-forming composite sheet functions as a dicing sheet for supporting the adherend in the dicing step, the support sheet and the protective film-forming film The adhesiveness between them is maintained, and the effect of suppressing the chip with the protective film-forming film from peeling off from the support sheet in the dicing step is obtained. When the protective film-forming composite sheet functions as a dicing sheet for supporting the adherend in the dicing process, there is no need to dice by dicing a separate dicing sheet to the wafer with the protective film-forming film in the dicing process. The manufacturing process of the semiconductor device can be simplified.
次に、本発明の保護膜形成用フィルムの利用方法について、上述した保護膜形成用複合シートを半導体装置の製造に適用した場合を例にとって説明する。 [Method for Manufacturing Semiconductor Device]
Next, a method for using the protective film-forming film of the present invention will be described taking as an example the case where the above-described protective film-forming composite sheet is applied to the manufacture of a semiconductor device.
工程(1):保護膜形成用フィルムと支持シートとを剥離、
工程(2):保護膜形成用フィルムを支持体に載置、
工程(3):保護膜形成用フィルムを硬化して保護膜を得る、
工程(4):保護膜と支持体とを剥離、
工程(5):半導体ウエハと、保護膜形成用フィルムまたは保護膜とをダイシング。 The method for manufacturing a semiconductor device according to the present invention preferably includes a step of attaching a protective film-forming film of the protective film-forming composite sheet to a semiconductor wafer to obtain a semiconductor chip having the protective film. Specifically, a protective film-forming film of the protective film-forming composite sheet is attached to the back surface of a semiconductor wafer having a circuit formed on the front surface, and then a semiconductor chip having a protective film on the back surface is obtained. The protective film is preferably a protective film for a semiconductor wafer or a semiconductor chip. The method for manufacturing a semiconductor device according to the present invention preferably further includes the following steps (1) to (5), wherein steps (1) to (4) are performed in this order, and step (5) is arbitrarily performed. It is characterized by performing in order. In addition, when using an adhesive sheet as a support sheet as mentioned above, it is preferable to perform a process (5) before a process (1) from a viewpoint of simplifying the manufacturing process of a semiconductor device.
Step (1): peeling off the protective film-forming film and the support sheet,
Step (2): placing the protective film-forming film on the support,
Step (3): The protective film-forming film is cured to obtain a protective film.
Step (4): peeling off the protective film and the support,
Step (5): Dicing the semiconductor wafer and the protective film-forming film or protective film.
工程(6):保護膜にレーザー印字。 In addition to the steps (1) to (5), the method for manufacturing a semiconductor device according to the present invention may further include the following step (6). After the step (4), the step (6) ) Can also be performed.
Step (6): Laser printing on the protective film.
粘着シート貼付装置(リンテック(株)製 Adwill RAD3600F12)を用いて、テーブル温度60℃で保護膜形成用フィルムの第1表面を、350μm厚に研磨したシリコンウエハの研磨面(2000番仕上げ)に貼付し、シリコンウエハと保護膜形成用フィルムの積層体を得た。 <Removability on the second surface>
Using a pressure-sensitive adhesive sheet sticking device (Adwill RAD3600F12 manufactured by Lintec Corporation), the first surface of the protective film-forming film is stuck to a polished surface (No. 2000 finish) of a silicon wafer polished to a thickness of 350 μm at a table temperature of 60 ° C. Thus, a laminate of the silicon wafer and the protective film forming film was obtained.
粘着シート貼付装置(リンテック(株)製 Adwill RAD3600F12)を用いて、テーブル温度60℃で保護膜形成用フィルムの第1表面を、500μm厚に研磨したシリコンウエハの研磨面(2000番仕上げ)に貼付し、シリコンウエハと保護膜形成用フィルムの積層体を得た。 <Adhesive strength of first surface and second surface>
Using a pressure-sensitive adhesive sheet sticking device (Adwill RAD3600F12 manufactured by Lintec Corporation), the first surface of the protective film-forming film is stuck to a polished surface (No. 2000 finish) of a silicon wafer polished to a thickness of 500 μm at a table temperature of 60 ° C. Thus, a laminate of the silicon wafer and the protective film forming film was obtained.
実施例または比較例で作成した保護膜形成用フィルムの第2表面において、理学工業社製PROBETACKTESTERを用い、JIS Z0237:1991 参考5に準拠して、プローブタック値を測定した。具体的には、熱硬化前の保護膜形成用フィルムを25mm×25mmの試験片に切り取り、23℃の環境下、その試験片の第2表面に、70℃に加熱された直径5mmのステンレス製プローブを10秒間、接触荷重0.98N/cm2で接触させた後、プローブを10mm/秒の速度で試験片から離し、その際の応力を測定した。 <Probe tack value>
The probe tack value was measured on the second surface of the protective film-forming film prepared in Examples or Comparative Examples using PROBETACKTESTER manufactured by Rigaku Industry Co., Ltd. according to JIS Z0237: 1991 Reference 5. Specifically, the film for forming a protective film before thermosetting is cut into a 25 mm × 25 mm test piece, and in a 23 ° C. environment, the second surface of the test piece is made of stainless steel having a diameter of 5 mm heated to 70 ° C. After contacting the probe for 10 seconds with a contact load of 0.98 N / cm 2 , the probe was separated from the test piece at a speed of 10 mm / second, and the stress at that time was measured.
第2表面における再剥離性の評価において得た保護膜形成用フィルム付チップを支持体に仮固定せずに、130℃、2時間で保護膜形成用フィルムを熱硬化し、支持体と保護膜とチップの積層体を得、試料とした。
また、第2表面における再剥離性の評価において、支持体上で熱硬化して得た保護膜とチップの積層体のうち、評価が「良好」であったものを試料とした。 <Laser marking aptitude>
The protective film-forming film was thermally cured at 130 ° C. for 2 hours without temporarily fixing the chip with the protective film-forming film obtained in the evaluation of removability on the second surface to the support, and the support and the protective film A chip laminate was obtained and used as a sample.
Moreover, in the evaluation of the removability on the second surface, a sample having a “good” evaluation among the laminates of the protective film and the chip obtained by thermosetting on the support was used as a sample.
良好:CCDカメラによるコントラスト値が70%超
可 :CCDカメラによるコントラスト値が30~70%
不良:CCDカメラによるコントラスト値が30%未満 Recognition evaluation was performed using a CCD camera mounted on a microscope. The evaluation criteria are as follows.
Good: Contrast value with CCD camera is over 70% Possible: Contrast value with CCD camera is 30-70%
Bad: Contrast value by CCD camera is less than 30%
保護膜形成用組成物(α)を構成する各成分とその配合量を下記に示す。各成分の配合量は固形分換算の質量部を示し、本発明において固形分とは溶媒以外の全成分をいう。
(A)重合体成分:n-ブチルアクリレート55質量部、メチルメタクリレート15質量部、グリシジルメタクリレート20質量部、及び2-ヒドロキシエチルアクリレート10質量部を共重合してなるアクリル系重合体(重量平均分子量:90万、ガラス転移温度:-28℃)/100質量部
(B)硬化性成分:
(B11)ビスフェノールA型エポキシ樹脂(エポキシ当量180~200g/eq、常温において固体である)50質量部、及びジシクロペンタジエン型エポキシ樹脂(大日本インキ化学工業(株)製 エピクロンHP-7200HH、常温において固体である)50質量部からなる熱硬化性成分/100質量部
(B12)熱活性潜在性エポキシ樹脂硬化剤(ジシアンジアミド(旭電化製 アデカハ-ドナー3636AS))/2.8質量部
(B13)硬化促進剤(2-フェニル-4,5-ジヒドロキシメチルイミダゾール(四国化成工業(株)製 キュアゾール2PHZ))/2.8質量部
(C)無機フィラー:シリカフィラー(溶融石英フィラー(平均粒径3μm))/300質量部
(D)着色剤:黒色顔料(カーボンブラック(三菱化学社製#MA650、平均粒径28nm))/10質量部
(E)カップリング剤:シランカップリング剤(日本ユニカー製 A-1110)/1質量部
(F)剥離剤:シリコーン化合物(モメンティブ・パフォーマンス・マテリアルズ・ジャパン社製 XF42-334)/(A)~(F)の合計100質量部に対して0.1質量部 [Protective film-forming composition (α)]
Each component which comprises the composition for protective film formation ((alpha)), and its compounding quantity are shown below. The compounding quantity of each component shows the mass part of solid content conversion, and solid content means all components other than a solvent in this invention.
(A) Polymer component: acrylic polymer (weight average molecular weight) obtained by copolymerizing 55 parts by mass of n-butyl acrylate, 15 parts by mass of methyl methacrylate, 20 parts by mass of glycidyl methacrylate, and 10 parts by mass of 2-hydroxyethyl acrylate : 900,000, glass transition temperature: -28 ° C) / 100 parts by mass (B) curable component:
(B11) 50 parts by mass of bisphenol A type epoxy resin (epoxy equivalent 180 to 200 g / eq, solid at normal temperature) and dicyclopentadiene type epoxy resin (Epicron HP-7200HH, manufactured by Dainippon Ink & Chemicals, Inc.) Thermosetting component consisting of 50 parts by mass / 100 parts by mass (B12) thermoactive latent epoxy resin curing agent (dicyandiamide (Adekaha Donor 3636AS manufactured by Asahi Denka)) / 2.8 parts by mass (B13) Curing accelerator (2-phenyl-4,5-dihydroxymethylimidazole (Curesol 2PHZ manufactured by Shikoku Kasei Kogyo Co., Ltd.)) / 2.8 parts by mass (C) inorganic filler: silica filler (fused quartz filler (average particle size 3 μm )) / 300 parts by mass (D) Colorant: Black pigment (carbon black (Mitsubishi Chemical) # MA650, average particle size 28 nm) / 10 parts by mass (E) coupling agent: silane coupling agent (A-1110 by Nihon Unicar) / 1 part by mass (F) Release agent: silicone compound (momentive performance・ 0.1 parts by mass with respect to a total of 100 parts by mass of Materials Japan XF42-334) / (A) to (F)
(F)成分の配合量を、(A)~(F)の合計100質量部に対して0.5質量部としたこと以外は、保護膜形成用組成物(α)と同様である。 [Composition for forming protective film (β)]
The amount of component (F) is the same as that of the protective film-forming composition (α) except that the amount of component (A) to (F) is 0.5 parts by mass with respect to 100 parts by mass in total.
(F)成分の配合量を、(A)~(F)の合計100質量部に対して1.5質量部としたこと以外は、保護膜形成用組成物(α)と同様である。 [Protective film-forming composition (γ)]
The amount of component (F) is the same as that for the protective film-forming composition (α) except that the amount of component (F) is 1.5 parts by mass with respect to 100 parts by mass in total of (A) to (F).
(F)成分の配合量を、(A)~(F)の合計100質量部に対して3.0質量部としたこと以外は、保護膜形成用組成物(α)と同様である。 [Protective film-forming composition (δ)]
The amount of component (F) is the same as that for the protective film-forming composition (α) except that the amount of component (F) is 3.0 parts by mass with respect to 100 parts by mass in total of (A) to (F).
重合体成分(A)の代わりに、下記の重合体成分(A’)を用いたこと以外は、保護膜形成用組成物(α)と同様である。
(A’)重合体成分:n-ブチルアクリレート15質量部、メチルメタクリレート50質量部、グリシジルメタクリレート20質量部、及び2-ヒドロキシエチルアクリレート15質量部を共重合してなるアクリル系重合体(重量平均分子量:90万、ガラス転移温度:-1℃) [Protective film-forming composition (ε)]
It is the same as the composition (α) for forming a protective film except that the following polymer component (A ′) is used instead of the polymer component (A).
(A ′) Polymer component: acrylic polymer (weight average) obtained by copolymerizing 15 parts by mass of n-butyl acrylate, 50 parts by mass of methyl methacrylate, 20 parts by mass of glycidyl methacrylate, and 15 parts by mass of 2-hydroxyethyl acrylate (Molecular weight: 900,000, glass transition temperature: -1 ° C)
(F)成分の配合量を、(A)~(F)の合計100質量部に対して0質量部としたこと以外は、保護膜形成用組成物(α)と同様である。 [Composition for forming protective film (ζ)]
The component (F) is the same as the protective film-forming composition (α) except that the amount of component (F) is 0 part by mass with respect to 100 parts by mass in total of (A) to (F).
剥離シートとして、片面に剥離処理を行ったポリエチレンテレフタレートフィルム(リンテック社製 SP-P502010、厚さ50μm)を用意した。保護膜形成用組成物(α)のメチルエチルケトン溶液(固形分濃度61重量%)を、上記剥離シートの剥離処理面上に乾燥後の厚さが25μmとなるように塗布、乾燥(乾燥条件:オーブンにて120℃、3分間)して、剥離シート上に樹脂層(α)を形成した。 (Example 1)
As a release sheet, a polyethylene terephthalate film (SP-P502010 manufactured by Lintec Corporation, thickness 50 μm) having a release treatment on one side was prepared. A methyl ethyl ketone solution (solid content concentration: 61% by weight) of the composition for forming a protective film (α) was applied on the release-treated surface of the release sheet so that the thickness after drying was 25 μm, and dried (drying conditions: oven At 120 ° C. for 3 minutes to form a resin layer (α) on the release sheet.
次いで、保護膜形成用組成物(ζ)のメチルエチルケトン溶液(固形分濃度61重量%)を上記剥離シートの剥離処理面上に乾燥後の厚さが25μmとなるように塗布、乾燥(乾燥条件:オーブンにて120℃、3分間)して、剥離シート上に樹脂層(ζ)を形成した。 Further, as another release sheet, a polyethylene terephthalate film (SP-P502010, Lintec Corporation, thickness 50 μm) having a release treatment on one side was prepared.
Next, a methyl ethyl ketone solution (solid content concentration: 61% by weight) of the composition for forming a protective film (ζ) was applied onto the release-treated surface of the release sheet so that the thickness after drying was 25 μm and dried (drying conditions: A resin layer (ζ) was formed on the release sheet by heating in an oven at 120 ° C. for 3 minutes.
保護膜形成用組成物(α)に代わりに、保護膜形成用組成物(β)を用いたこと以外は実施例1と同様の方法で保護膜形成用フィルムを得た。各評価結果を表1に示す。 (Example 2)
A protective film-forming film was obtained in the same manner as in Example 1 except that the protective film-forming composition (β) was used instead of the protective film-forming composition (α). Each evaluation result is shown in Table 1.
保護膜形成用組成物(α)に代わりに、保護膜形成用組成物(γ)を用いたこと以外は実施例1と同様の方法で保護膜形成用フィルムを得た。各評価結果を表1に示す。 (Example 3)
A protective film-forming film was obtained in the same manner as in Example 1, except that the protective film-forming composition (γ) was used instead of the protective film-forming composition (α). Each evaluation result is shown in Table 1.
保護膜形成用組成物(α)に代わりに、保護膜形成用組成物(δ)を用いたこと以外は実施例1と同様の方法で保護膜形成用フィルムを得た。各評価結果を表1に示す。 Example 4
A protective film-forming film was obtained in the same manner as in Example 1, except that the protective film-forming composition (δ) was used instead of the protective film-forming composition (α). Each evaluation result is shown in Table 1.
保護膜形成用組成物(α)に代わりに、保護膜形成用組成物(ε)を用いたこと以外は実施例1と同様の方法で保護膜形成用フィルムを得た。各評価結果を表1に示す。 (Example 5)
A protective film-forming film was obtained in the same manner as in Example 1 except that the protective film-forming composition (ε) was used instead of the protective film-forming composition (α). Each evaluation result is shown in Table 1.
保護膜形成用組成物(α)に代わりに、保護膜形成用組成物(ζ)を用いたこと以外は実施例1と同様の方法で保護膜形成用フィルムを得た。各評価結果を表1に示す。 (Comparative Example 1)
A protective film-forming film was obtained in the same manner as in Example 1 except that the protective film-forming composition (ζ) was used instead of the protective film-forming composition (α). Each evaluation result is shown in Table 1.
a:第1表面
b:第2表面
100:保護膜形成用複合シート
1:基材
2:粘着剤層
3:粘着シート
4:治具接着層
5:界面接着調整層
6:せん断強度測定ツール
7:支持体
8:チップ
9:金属板
11:保護膜
20:保護膜付チップ
DESCRIPTION OF SYMBOLS 10: Film for protective film formation a: 1st surface b: 2nd surface 100: Composite sheet for protective film formation 1: Base material 2: Adhesive layer 3: Adhesive sheet 4: Jig adhesion layer 5: Interface adhesion adjustment layer 6: Tool for measuring shear strength 7: Support 8: Tip 9: Metal plate 11: Protective film 20: Tip with protective film
Claims (9)
- 第1表面と第2表面とを有する硬化性の保護膜形成用フィルムであって、
硬化後における第1表面のシリコンウエハに対する接着力が、硬化後における第2表面のシリコンウエハに対する接着力よりも高い保護膜形成用フィルム。 A curable protective film-forming film having a first surface and a second surface,
A film for forming a protective film, wherein the adhesive force of the first surface after curing to the silicon wafer is higher than the adhesive force of the second surface to the silicon wafer after curing. - 硬化後における第1表面のシリコンウエハに対する接着力と硬化後における第2表面のシリコンウエハに対する接着力との比(第1表面のシリコンウエハに対する接着力/第2表面のシリコンウエハに対する接着力)が、1.2~100である請求項1に記載の保護膜形成用フィルム。 The ratio of the adhesive force of the first surface to the silicon wafer after curing and the adhesive force of the second surface to the silicon wafer after curing (adhesion force of the first surface to the silicon wafer / adhesion force of the second surface to the silicon wafer) is The protective film-forming film according to claim 1, wherein the film is 1.2 to 100.
- 第1表面は保護膜を形成する被着体に貼付される請求項1または2に記載の保護膜形成用フィルム。 The film for forming a protective film according to claim 1 or 2, wherein the first surface is attached to an adherend forming a protective film.
- 第2表面は支持体に仮固定される請求項1~3のいずれかに記載の保護膜形成用フィルム。 4. The protective film-forming film according to claim 1, wherein the second surface is temporarily fixed to the support.
- 硬化後における第2表面のシリコンウエハに対する接着力が0.01~100Nである請求項1~4のいずれかに記載の保護膜形成用フィルム。 The protective film-forming film according to any one of claims 1 to 4, wherein the adhesive force of the second surface to the silicon wafer after curing is 0.01 to 100 N.
- 第2表面のプローブタック値が0.01~3N/5mmΦである請求項1~5のいずれかに記載の保護膜形成用フィルム。 6. The protective film-forming film according to claim 1, wherein the probe tack value of the second surface is 0.01 to 3 N / 5 mmΦ.
- 組成の異なる2層以上の樹脂層からなる請求項1~6のいずれかに記載の保護膜形成用フィルム。 The protective film-forming film according to any one of claims 1 to 6, comprising two or more resin layers having different compositions.
- 少なくとも第2表面を含む樹脂層が剥離剤を含有し、第2表面を含む樹脂層における剥離剤の含有量が、第1表面を含む樹脂層における剥離剤の含有量よりも多い請求項7に記載の保護膜形成用フィルム。 The resin layer including at least the second surface contains a release agent, and the content of the release agent in the resin layer including the second surface is greater than the content of the release agent in the resin layer including the first surface. The film for protective film formation of description.
- 第1表面を含む樹脂層における剥離剤の含有量が、第1表面を含む樹脂層を構成する全固形分のうち剥離剤を除く固形分100質量部に対して0~0.001質量部であり、
第2表面を含む樹脂層における剥離剤の含有量が、第2表面を含む樹脂層を構成する全固形分のうち剥離剤を除く固形分100質量部に対して0.001~20質量部である請求項8に記載の保護膜形成用フィルム。 The content of the release agent in the resin layer including the first surface is 0 to 0.001 parts by mass with respect to 100 parts by mass of the solid content excluding the release agent out of the total solids constituting the resin layer including the first surface. Yes,
The content of the release agent in the resin layer including the second surface is 0.001 to 20 parts by mass with respect to 100 parts by mass of the solid content excluding the release agent out of the total solids constituting the resin layer including the second surface. The film for forming a protective film according to claim 8.