WO2014061606A1 - Film antireflet antisalissure, article, et procédé de fabrication de ce film et de cet article - Google Patents
Film antireflet antisalissure, article, et procédé de fabrication de ce film et de cet article Download PDFInfo
- Publication number
- WO2014061606A1 WO2014061606A1 PCT/JP2013/077817 JP2013077817W WO2014061606A1 WO 2014061606 A1 WO2014061606 A1 WO 2014061606A1 JP 2013077817 W JP2013077817 W JP 2013077817W WO 2014061606 A1 WO2014061606 A1 WO 2014061606A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanosheet
- antifouling
- antifouling layer
- silica
- film
- Prior art date
Abstract
L'invention concerne : un film antireflet antisalissure qui présente des propriétés antisalissure améliorées, qui préserve les performances antireflet d'un film de silice poreux, et qui peut conserver un bel aspect pendant longtemps ; un article qui est muni du film antireflet antisalissure ; ainsi qu'un procédé de fabrication de ce film et de cet article. Ledit film antireflet antisalissure comprend un film de silice poreux ainsi qu'une couche antisalissure qui recouvre la surface du film de silice poreux, cette couche antisalissure comportant une pluralité de nanofeuilles, les nanofeuilles étant constituées d'un matériau à faible réfraction dont l'indice de réfraction est de 1,4 à 1,65, et l'épaisseur de film moyenne de la couche antisalissure étant de 0,4 à 40 nm.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2012227967A JP2016001200A (ja) | 2012-10-15 | 2012-10-15 | 防汚性反射防止膜、物品およびその製造方法 |
JP2012-227967 | 2012-10-15 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014061606A1 true WO2014061606A1 (fr) | 2014-04-24 |
Family
ID=50488171
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2013/077817 WO2014061606A1 (fr) | 2012-10-15 | 2013-10-11 | Film antireflet antisalissure, article, et procédé de fabrication de ce film et de cet article |
Country Status (3)
Country | Link |
---|---|
JP (1) | JP2016001200A (fr) |
TW (1) | TW201423142A (fr) |
WO (1) | WO2014061606A1 (fr) |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015155830A1 (fr) * | 2014-04-08 | 2015-10-15 | 日産自動車株式会社 | Structure antiencrassement de durabilité élevée et pièce d'automobile l'utilisant |
WO2017216592A3 (fr) * | 2016-06-15 | 2018-03-15 | Hungaro Lux Light Kft | Film antireflet et son utilisation sur un substrat |
CN111253782A (zh) * | 2020-02-12 | 2020-06-09 | 首钢集团有限公司 | 改性防腐水滑石、水性智能防腐涂料、制备方法及涂层 |
WO2020153352A1 (fr) | 2019-01-21 | 2020-07-30 | 公立大学法人大阪 | Dispersion liquide de couche exfoliée de composé multicouche, et substrat transparent l'utilisant |
CN113289413A (zh) * | 2021-05-25 | 2021-08-24 | 九江市磐泰复合材料有限公司 | 一种高容量氟玻璃纤维过滤材料的制备方法 |
EP3692104A4 (fr) * | 2017-10-03 | 2021-09-01 | Massachusetts Institute of Technology | Matériaux qui résistent à l'encrassement et procédés pour leur identification |
WO2022181628A1 (fr) | 2021-02-24 | 2022-09-01 | 国立大学法人熊本大学 | Dispersion de particules exfoliées d'un composé polysilicate stratifié, et son procédé de production |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN106277839B (zh) * | 2015-05-15 | 2018-10-30 | 中国科学院理化技术研究所 | 一种具有超双疏自清洁及减反增透性能的复合薄膜及其制备方法 |
WO2018190408A1 (fr) * | 2017-04-14 | 2018-10-18 | Hoya株式会社 | Élément optique et film mince optique |
JP7218539B2 (ja) * | 2018-10-19 | 2023-02-07 | 三菱ケミカル株式会社 | 表面被覆層形成用塗工液及び多孔質ケイ素積層体 |
WO2023140194A1 (fr) * | 2022-01-20 | 2023-07-27 | 日東電工株式会社 | Élément optique, son procédé de production et élément optique |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2001342016A (ja) * | 2000-05-26 | 2001-12-11 | Matsushita Electric Works Ltd | 表面処理多孔質体及び多孔質体の表面処理方法 |
JP2006096861A (ja) * | 2004-09-29 | 2006-04-13 | Fuji Photo Film Co Ltd | 塗布組成物、光学機能層、反射防止フィルム、偏光板、及び画像表示装置 |
JP2006350208A (ja) * | 2005-06-20 | 2006-12-28 | Seiko Epson Corp | 光学物品およびその製造方法 |
JP2008249902A (ja) * | 2007-03-29 | 2008-10-16 | Fujifilm Corp | 偏光板用保護フィルム、偏光板、及び液晶表示装置 |
JP2009237551A (ja) * | 2008-03-03 | 2009-10-15 | Keio Gijuku | 反射防止膜及びその形成方法 |
JP2011207751A (ja) * | 2010-03-11 | 2011-10-20 | Mitsubishi Chemicals Corp | シリカ系多孔質膜の製造方法 |
-
2012
- 2012-10-15 JP JP2012227967A patent/JP2016001200A/ja active Pending
-
2013
- 2013-10-11 WO PCT/JP2013/077817 patent/WO2014061606A1/fr active Application Filing
- 2013-10-14 TW TW102136970A patent/TW201423142A/zh unknown
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2001342016A (ja) * | 2000-05-26 | 2001-12-11 | Matsushita Electric Works Ltd | 表面処理多孔質体及び多孔質体の表面処理方法 |
JP2006096861A (ja) * | 2004-09-29 | 2006-04-13 | Fuji Photo Film Co Ltd | 塗布組成物、光学機能層、反射防止フィルム、偏光板、及び画像表示装置 |
JP2006350208A (ja) * | 2005-06-20 | 2006-12-28 | Seiko Epson Corp | 光学物品およびその製造方法 |
JP2008249902A (ja) * | 2007-03-29 | 2008-10-16 | Fujifilm Corp | 偏光板用保護フィルム、偏光板、及び液晶表示装置 |
JP2009237551A (ja) * | 2008-03-03 | 2009-10-15 | Keio Gijuku | 反射防止膜及びその形成方法 |
JP2011207751A (ja) * | 2010-03-11 | 2011-10-20 | Mitsubishi Chemicals Corp | シリカ系多孔質膜の製造方法 |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015155830A1 (fr) * | 2014-04-08 | 2015-10-15 | 日産自動車株式会社 | Structure antiencrassement de durabilité élevée et pièce d'automobile l'utilisant |
WO2017216592A3 (fr) * | 2016-06-15 | 2018-03-15 | Hungaro Lux Light Kft | Film antireflet et son utilisation sur un substrat |
US20190177553A1 (en) * | 2016-06-15 | 2019-06-13 | Hungaro Lux Light Kft. | Antireflection Film and Its Use on a Substrate |
US11029514B2 (en) | 2016-06-15 | 2021-06-08 | Hungaro Lux Light Kft. | Antireflection film and its use on a substrate |
EP3692104A4 (fr) * | 2017-10-03 | 2021-09-01 | Massachusetts Institute of Technology | Matériaux qui résistent à l'encrassement et procédés pour leur identification |
US11267972B2 (en) | 2017-10-03 | 2022-03-08 | Massachusetts Institute Of Technology | Materials that resist fouling and methods for identifying same |
WO2020153352A1 (fr) | 2019-01-21 | 2020-07-30 | 公立大学法人大阪 | Dispersion liquide de couche exfoliée de composé multicouche, et substrat transparent l'utilisant |
KR20210123325A (ko) | 2019-01-21 | 2021-10-13 | 닛산 가가쿠 가부시키가이샤 | 층상 화합물의 박리층 분산액 및 그것을 이용한 투명기판 |
CN111253782A (zh) * | 2020-02-12 | 2020-06-09 | 首钢集团有限公司 | 改性防腐水滑石、水性智能防腐涂料、制备方法及涂层 |
WO2022181628A1 (fr) | 2021-02-24 | 2022-09-01 | 国立大学法人熊本大学 | Dispersion de particules exfoliées d'un composé polysilicate stratifié, et son procédé de production |
KR20230147206A (ko) | 2021-02-24 | 2023-10-20 | 고꾸리쯔다이가꾸호오진 구마모또 다이가꾸 | 층상 폴리규산염 화합물의 박리입자 분산액, 및 그의 제조방법 |
CN113289413A (zh) * | 2021-05-25 | 2021-08-24 | 九江市磐泰复合材料有限公司 | 一种高容量氟玻璃纤维过滤材料的制备方法 |
Also Published As
Publication number | Publication date |
---|---|
JP2016001200A (ja) | 2016-01-07 |
TW201423142A (zh) | 2014-06-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2014061606A1 (fr) | Film antireflet antisalissure, article, et procédé de fabrication de ce film et de cet article | |
JP2015049319A (ja) | 透明基材と防汚性反射防止膜とを備える物品およびその製造方法 | |
JP5078620B2 (ja) | 中空シリカ微粒子、それを含む透明被膜形成用組成物、および透明被膜付基材 | |
WO2011027827A1 (fr) | Article ayant un film à faible réflexion sur une surface de matériau de base | |
WO2015041257A1 (fr) | Plaque de verre trempé à couche anti-reflets et son procédé de production | |
CN103305036B (zh) | 一种含poss减反射膜镀膜液及其制备方法与应用 | |
WO2010018852A1 (fr) | Compositions de revêtement et articles les comportant | |
JP6586897B2 (ja) | 防眩膜付き基材、膜形成用塗布液およびその製造方法 | |
JP5157143B2 (ja) | 反射防止膜付き基体 | |
TW201606357A (zh) | 附防眩膜之基材及物品 | |
JP5370147B2 (ja) | 中空微粒子、その製造方法、塗料組成物および塗膜が形成された物品 | |
WO2013051620A1 (fr) | Procédé de fabrication d'un objet doté d'un film antireflet | |
JP2003202406A (ja) | 反射防止フィルム及びディスプレイ装置 | |
CN102849962A (zh) | 一种二氧化硅超疏水薄膜的制备方法及一种超疏水材料 | |
JP6599666B2 (ja) | 光散乱性被膜を有する透明スクリーン及び光散乱性被膜形成用塗布液 | |
CN103476726A (zh) | 附有低反射膜的玻璃板 | |
JP2017039928A (ja) | 反射防止膜形成用組成物、反射防止膜およびその形成方法 | |
JP5304638B2 (ja) | 中空微粒子、その製造方法、塗料組成物および塗膜が形成された物品 | |
JP2007270098A (ja) | 高屈折率コーティング用組成物 | |
TW201606356A (zh) | 附防眩層之基材及物品 | |
JP2017186205A (ja) | 低反射膜を有する物品 | |
WO2011093484A1 (fr) | Élément hydrophile faiblement réfléchissant | |
JP2013160799A (ja) | 低反射膜付き物品の製造方法 | |
JP2015075707A (ja) | 透明基材と防汚性反射防止膜とを備える物品およびその製造方法 | |
WO2018003772A1 (fr) | Film de revêtement diffusant la lumière dans lequel des nanodiamants polycristallins sont dispersés, et liquide d'application pour former un film de revêtement diffusant la lumière |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13847814 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13847814 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: JP |