WO2013086647A1 - Composición biocida de polvo activos, que comprende al menos una sal de cobre y al menos una sal de zinc y procedimiento de fabricación - Google Patents
Composición biocida de polvo activos, que comprende al menos una sal de cobre y al menos una sal de zinc y procedimiento de fabricación Download PDFInfo
- Publication number
- WO2013086647A1 WO2013086647A1 PCT/CL2011/000081 CL2011000081W WO2013086647A1 WO 2013086647 A1 WO2013086647 A1 WO 2013086647A1 CL 2011000081 W CL2011000081 W CL 2011000081W WO 2013086647 A1 WO2013086647 A1 WO 2013086647A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- salt
- copper
- group
- salts
- zinc
- Prior art date
Abstract
Description
Claims