WO2012173313A1 - Verre décoratif utilisant du papier coréen et son procédé de fabrication - Google Patents
Verre décoratif utilisant du papier coréen et son procédé de fabrication Download PDFInfo
- Publication number
- WO2012173313A1 WO2012173313A1 PCT/KR2011/008848 KR2011008848W WO2012173313A1 WO 2012173313 A1 WO2012173313 A1 WO 2012173313A1 KR 2011008848 W KR2011008848 W KR 2011008848W WO 2012173313 A1 WO2012173313 A1 WO 2012173313A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- eva resin
- hanji
- glass
- heating
- Prior art date
Abstract
Selon la présente invention, sont proposés un verre décoratif utilisant du papier coréen et un procédé de fabrication du verre décoratif. Le verre décoratif exprime la texture antique et la nature délicate du papier coréen fabriqué à l'aide d'une méthode traditionnelle, et exprime de façon appropriée diverses couleurs d'une couche imprimée et d'un dos. La surface externe du papier coréen est phosphorescente de façon à exprimer une élégance visuelle. Le papier coréen est durable et résistant aux rayonnements ultraviolets, permettant ainsi d'étendre la durée de vie de service du verre décoratif. Le procédé de fabrication du verre décoratif comprend : une étape de préparation suivant laquelle on lave, on chauffe et on séche des plaques de verre découpées puis on les empile dans une boîte de stockage ; une étape consistant à introduire les plaques de verre découpées empilées dans la boîte de stockage une par une à l'aide d'un cylindre de levage et d'un cylindre d'aspiration ; une étape consistant à former une couche imprimée par impression d'un motif sur une surface de la plaque de verre découpée par sérigraphie, puis chauffage/séchage de la plaque de verre découpée ; une étape consistant à former une couche de résine d'éthylène-acétate de vinyle (EVA) par application d'une résine d'EVA sur la plaque de verre découpée et une surface arrière de la couche imprimée ; une étape consistant à attacher le papier coréen à la couche de résine d'EVA par pressage de la couche de résine d'EVA sur le papier coréen avec un rouleau et durcissement de la couche de résine d'EVA par chauffage et refroidissement à l'aide d'une presse de façon à former une première couche d'adhérence ; une étape consistant à former une couche de fluorure par application d'une résine de fluorure comme adhésif transparent sur la surface arrière du papier coréen et chauffage et refroidissement de la résine de fluorure jusqu'à un état semi-durci ; une étape consistant à former une couche de résine d'EVA par application de la résine d'EVA sur la surface arrière de la couche de fluorure ; et une étape consistant à fixer une feuille de support de film de PET coloré et imprimé par des motifs à la couche de résine d'EVA appliquée sur la couche de fluorure par pressage de la couche de résine d'EVA par un rouleau et durcissement de la couche de résine d'EVA par chauffage et refroidissement à l'aide d'une presse de façon à former une seconde couche d'adhérence.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2011-0057233 | 2011-06-14 | ||
KR1020110057233A KR101075809B1 (ko) | 2011-06-14 | 2011-06-14 | 한지를 이용한 장식유리 및 그 제조방법 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2012173313A1 true WO2012173313A1 (fr) | 2012-12-20 |
Family
ID=45033197
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2011/008848 WO2012173313A1 (fr) | 2011-06-14 | 2011-11-18 | Verre décoratif utilisant du papier coréen et son procédé de fabrication |
Country Status (2)
Country | Link |
---|---|
KR (1) | KR101075809B1 (fr) |
WO (1) | WO2012173313A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110357448A (zh) * | 2019-07-23 | 2019-10-22 | 嘉善银升玻璃有限公司 | 玻璃表面高温拉丝纹理工艺 |
DE102020102802A1 (de) | 2020-02-04 | 2021-08-05 | Bellicon Ag | Trampolin |
DE102020102803A1 (de) | 2020-02-04 | 2021-08-05 | Bellicon Ag | Trampolin |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101381946B1 (ko) * | 2013-11-18 | 2014-04-07 | 정병수 | 한지 무늬를 가지는 시트 및 이를 구비한 페어 유리 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5795855A (en) * | 1980-12-09 | 1982-06-14 | Yukiaki Tada | Industrial art objects of glass made by forming pattern with paper or cloth and synthetic resin on glass surface |
KR20020003155A (ko) * | 2001-11-10 | 2002-01-10 | 옥문수 | 코팅용액의 제조방법 |
KR20060002543A (ko) * | 2004-07-02 | 2006-01-09 | 박충기 | 한지를 이용한 가구의 문양표현방법 및 그 방법에 의한 가구 |
KR20070021682A (ko) * | 2005-08-19 | 2007-02-23 | 차봉수 | 건축자재용 착색유리 및 그 제조방법 |
KR200451359Y1 (ko) * | 2010-05-12 | 2010-12-10 | 박충배 | 한지 무늬를 갖는 유리 |
-
2011
- 2011-06-14 KR KR1020110057233A patent/KR101075809B1/ko not_active IP Right Cessation
- 2011-11-18 WO PCT/KR2011/008848 patent/WO2012173313A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5795855A (en) * | 1980-12-09 | 1982-06-14 | Yukiaki Tada | Industrial art objects of glass made by forming pattern with paper or cloth and synthetic resin on glass surface |
KR20020003155A (ko) * | 2001-11-10 | 2002-01-10 | 옥문수 | 코팅용액의 제조방법 |
KR20060002543A (ko) * | 2004-07-02 | 2006-01-09 | 박충기 | 한지를 이용한 가구의 문양표현방법 및 그 방법에 의한 가구 |
KR20070021682A (ko) * | 2005-08-19 | 2007-02-23 | 차봉수 | 건축자재용 착색유리 및 그 제조방법 |
KR200451359Y1 (ko) * | 2010-05-12 | 2010-12-10 | 박충배 | 한지 무늬를 갖는 유리 |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110357448A (zh) * | 2019-07-23 | 2019-10-22 | 嘉善银升玻璃有限公司 | 玻璃表面高温拉丝纹理工艺 |
DE102020102802A1 (de) | 2020-02-04 | 2021-08-05 | Bellicon Ag | Trampolin |
DE102020102803A1 (de) | 2020-02-04 | 2021-08-05 | Bellicon Ag | Trampolin |
Also Published As
Publication number | Publication date |
---|---|
KR101075809B1 (ko) | 2011-10-25 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
FI63389C (fi) | Kompoundglas med en dekorerad inneryta och dess framstaellningsfoerfarande | |
CN106029595B (zh) | 在玻璃上印刷的方法 | |
JP3868593B2 (ja) | 押し花密封品 | |
WO2012173313A1 (fr) | Verre décoratif utilisant du papier coréen et son procédé de fabrication | |
JP2007253370A (ja) | 装飾シート | |
CN101531114A (zh) | 一种墙面装饰板的表面处理工艺 | |
JP6760459B2 (ja) | 化粧シート | |
CA2361153A1 (fr) | Couche d'usure pigmente durcie par rayonnement | |
CN107206744A (zh) | 装饰片和具备该装饰片的装饰部件 | |
CA2793206A1 (fr) | Panneau a centre plein renfermant un materiau decoratif et/ou fonctionnel | |
EP1129844A1 (fr) | Plaque décorative faite d'un matériau composite stratifié en verre et/ou plastiques transparents | |
CN105011534A (zh) | 美甲用数码转移贴花及其制作方法 | |
WO2017138828A1 (fr) | Composition décorative multicouches qui sert de support à une image création | |
CN105599517B (zh) | 立体浮雕图案水转印纸及其使用方法 | |
CN106427260A (zh) | 一种板材及其制备方法 | |
JP3871759B2 (ja) | 転写シートを用いた化粧材の製造方法 | |
KR20020078676A (ko) | 인쇄무늬층이 형성된 에틸렌비닐아세테이트 신발창 | |
CN114165010B (zh) | 基于电子束固化技术的3d平板打印装饰板以及用途 | |
CN209683230U (zh) | 一种背透热转印膜 | |
KR20100002466A (ko) | 이미지가 포함된 장식용 유리 및 그 제조 방법 | |
WO2000002739A1 (fr) | Materiau de revetement par transfert et procede de revetement par transfert d'une surface de miroir | |
JP4390942B2 (ja) | 化粧シート | |
CN211395187U (zh) | 一种哑光滴胶墙纸 | |
CN217581001U (zh) | 一种基于3d打印技术处理的木制复合地板 | |
KR20030067042A (ko) | 가죽 원단에 무늬를 인쇄 하는 방법과 이에 의해 인쇄된가죽원단 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 11867983 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 11867983 Country of ref document: EP Kind code of ref document: A1 |