WO2012169853A2 - Method for manufacturing eyeglasses with an applied lacquer and mother-of-pearl pattern - Google Patents

Method for manufacturing eyeglasses with an applied lacquer and mother-of-pearl pattern Download PDF

Info

Publication number
WO2012169853A2
WO2012169853A2 PCT/KR2012/004589 KR2012004589W WO2012169853A2 WO 2012169853 A2 WO2012169853 A2 WO 2012169853A2 KR 2012004589 W KR2012004589 W KR 2012004589W WO 2012169853 A2 WO2012169853 A2 WO 2012169853A2
Authority
WO
WIPO (PCT)
Prior art keywords
lacquer
layer
mother
lacquer layer
forming
Prior art date
Application number
PCT/KR2012/004589
Other languages
French (fr)
Korean (ko)
Other versions
WO2012169853A3 (en
Inventor
박신영
Original Assignee
Park Sin Young
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Park Sin Young filed Critical Park Sin Young
Publication of WO2012169853A2 publication Critical patent/WO2012169853A2/en
Publication of WO2012169853A3 publication Critical patent/WO2012169853A3/en

Abstract

The present invention relates to a method for manufacturing eyeglasses with an applied mother-of-pearl pattern. The method for manufacturing the eyeglasses according to one embodiment of the present invention achieves high-quality eyeglasses having a mother-of-pearl pattern, and various other aesthetic qualities, as well as high strength and durability and eco-friendly effects beneficial to the human body.

Description

옻칠 및 자개 문양이 적용된 안경 제조 방법How to make glasses with lacquer and mother-of-pearl
본 발명은 옻칠 및 자개 문양이 적용된 안경을 제조하는 방법에 관한 것이다.The present invention relates to a method of manufacturing glasses applied lacquer and mother-of-pearl pattern.
안경에 일반적으로 사용되는 안경테는 렌즈를 지지하는 역할을 수행함과 동시에 안경의 전체적인 디자인을 결정하는 중요한 요소이다. 아울러, 안경테는 사람의 얼굴에 직접 맞닿는 부분이기 때문에 인체에 유익한 재질로 구현되어야 할 필요성이 있다.Eyeglass frames commonly used in eyeglasses play an important role in supporting the lens and at the same time determine the overall design of the eyeglasses. In addition, the glasses frame is a part directly in contact with the face of the person, there is a need to be implemented in a material beneficial to the human body.
최근 안경 수요자는 안경테를 결정하는데 있어서, 안경테의 전체적인 형상에 의한 미적 디자인을 고려함과 동시에 안경테 표면의 재질 및 문양에 대해서도 상당한 관심을 기울이고 있다. 안경테 표면의 재질 및 문양에 따라 안경의 디자인적 가치가 달라질 뿐만 아니라 피부 등에 악영향을 미칠 수도 있기 때문이다.Recently, the spectacles consumer considers the aesthetic design by the overall shape of the spectacle frame, while paying considerable attention to the material and the pattern of the spectacle frame surface. This is because not only the design value of the glasses depends on the material and the pattern of the surface of the glasses frame but also adversely affect the skin.
일반적으로, 안경테는 외부 충격에 의해 쉽게 파손되지 않을 만큼의 강도를 구비해야 하지만, 높은 강도를 유지하기 위해서 자체 중량이 큰 재질로 제작할 경우 안경 사용자는 크게 피로감을 느끼게 된다. 또한, 기존 안경테는 주로 알루미늄 등과 같은 금속, 목재, 플라스틱으로 통칭되는 합성수지 등을 재질로 하였고, 이들 재질을 갖는 안경용 지지체 표면을 인체에 무해한 물질로 일시에 코팅 처리함과 동시에 천연 또는 인공 색소를 처리하여 안경의 다양한 디자인을 구현해 왔으나, 안경테 표면 자체의 면적이 매우 작기 때문에 미세한 표면 디자인을 구현하는 것은 용이하지 않았다.In general, the spectacle frame should have enough strength not to be easily damaged by an external impact, but if the fabric frame is made of a material having a large weight in order to maintain high strength, the spectacle user will feel fatigue. In addition, the existing spectacle frame is mainly made of metal, such as aluminum, synthetic resin, such as wood, plastic, and the like, the surface of the support for glasses having these materials at the same time with a material that is harmless to the human body at the same time processing a natural or artificial pigment Although various designs of glasses have been implemented, it is not easy to implement a fine surface design because the area of the spectacle frame itself is very small.
따라서 본 발명자는 안경의 형상 및 모양을 디자인함에 있어서, 안경용 지지체의 재질을 소량 사용하여 자체 중량을 줄이되 강도 및 내구성을 유지 또는 상승시키고, 제조 시간을 크게 단축하며, 인체에 유익하고 고급스럽고 현대적인 디자인을 구현할 수 있도록 하는 안경 제조 방법을 고안하기에 이르렀다.Therefore, in the design of the shape and shape of the glasses, the present inventors use a small amount of material of the support for the glasses to reduce their own weight, maintain or increase strength and durability, greatly shorten the manufacturing time, and are beneficial to the human body. The company has come up with a way to make glasses that will enable design.
본 발명은 옻칠 및 자개 문양을 활용하여 고급스럽고 다양한 미감을 구현함과 동시에 강력한 강도 및 내구성을 갖고 인체에 유익한 친환경적 효능을 구비하는 안경을 제조하는 방법을 제공하고자 한다.The present invention is to provide a method of manufacturing glasses that have a high strength and durability while having a beneficial effect on the human body while implementing a luxurious and various aesthetic by using lacquer and mother-of-pearl pattern.
본 발명의 일 구체예는 안경용 지지체를 제공하는 단계; 상기 안경용 지지체의 표면에 옻칠을 수행하여 옻 층을 형성하는 단계; 및 상기 옻 층에 원하는 패턴에 따라 자개를 부착시켜 자개 문양을 형성하는 단계를 포함하는, 옻칠 및 자개 문양이 적용된 안경 제조 방법을 제공한다.One embodiment of the present invention provides a support for glasses; Forming a lacquer layer by performing lacquer on the surface of the eyeglass support; And attaching mother-of-pearl according to a desired pattern on the lacquer layer to form mother-of-pearl pattern.
구체적으로, 본 발명의 일 구체예는 안경용 지지체를 제공하는 단계; 상기 안경용 지지체의 표면을 사포 처리하는 단계; 상기 사포 처리된 안경용 지지체의 표면에 옻칠을 수행하고 이를 건조함으로써 제1 옻 층을 형성하는 단계; 상기 제1 옻 층에 옻칠을 반복 수행함과 동시에 원하는 패턴에 따라 자개를 부착시키고 이를 건조함으로써 자개 문양을 포함하는 제2 옻 층을 형성하는 단계; 상기 제2 옻 층에 정체칠을 도포하고, 사포 처리 후 건조함으로써 정체칠 층을 형성하는 단계; 및 상기 정체칠 층에 사포 처리를 반복 수행하여 광택 처리하는 단계를 포함하는, 옻칠 및 자개 문양이 적용된 안경 제조 방법을 제공한다.Specifically, one embodiment of the present invention comprises the steps of providing a support for glasses; Sanding the surface of the support for spectacles; Forming a first lacquer layer by performing lacquer on the surface of the sandpaper-treated eyeglass support and drying it; Forming a second lacquer layer including a mother-of-pearl pattern by repeatedly performing lacquer on the first lacquer layer and simultaneously attaching the mother-of-pearl and drying it according to a desired pattern; Applying a stagnation coat to the second lacquer layer, and forming a stagnation layer by drying after sandpaper treatment; And repeating the sandpaper treatment on the stagnant lacquer layer to provide a method of manufacturing glasses, lacquer and mother-of-pearl pattern is applied.
본 발명의 일 구체예에 있어서, 상기 제1 옻 층 건조 단계, 상기 제2 옻 층 건조 단계, 및 상기 정체칠 층 건조 단계는 18℃ 내지 19℃의 온도 범위 및 80% 내지 100%의 습도 범위에서 수행될 수 있다.In one embodiment of the present invention, the first lacquer layer drying step, the second lacquer layer drying step, and the stagnation layer drying step is a temperature range of 18 ℃ to 19 ℃ and humidity range of 80% to 100% It can be performed in.
본 발명의 일 구체예에 있어서, 상기 제1 옻 층을 형성하는 단계는 2회 반복 수행될 수 있다.In one embodiment of the present invention, the step of forming the first lacquer layer may be performed twice.
본 발명의 일 구체예에 있어서, 상기 정체칠 층 형성 단계는 3회 반복되어 상 정체칠 층, 중 정체칠 층 및 하 정체칠 층을 형성하는 것일 수 있다.In one embodiment of the present invention, the stagnation layer forming step may be repeated three times to form an upper stagnation layer, a middle stagnation layer and a lower stagnation layer.
본 발명의 일 구체예에 있어서, 상기 광택 처리 단계는 상기 정체칠 층에 콩기름을 적용하는 것을 더 포함할 수 있다.In one embodiment of the present invention, the gloss treatment step may further include applying soybean oil to the stagnation layer.
본 발명의 일 구체예에 있어서, 상기 제2 옻 층 형성 단계는 천연 색소를 배합하는 것을 더 포함하는 것일 수 있다.In one embodiment of the present invention, the step of forming the second lacquer layer may be further comprising a natural pigment.
본 발명의 일 구체예에 있어서, 상기 안경용 지지체는 금속, 합성수지 및 목재로 구성된 군으로부터 선택된 재질일 수 있다.In one embodiment of the present invention, the eyeglass support may be a material selected from the group consisting of metal, synthetic resin and wood.
본 발명의 일 구체예의 안경 제조 방법에 따르면, 자개 문양이 포함된 고급스럽고 다양한 미감을 구현함과 동시에 강력한 강도 및 내구성을 갖고 인체에 유익한 친환경적 효능을 구비하는 안경을 제조할 수 있다.According to the glasses manufacturing method of one embodiment of the present invention, it is possible to produce glasses with high environmental strength and durability while having a high strength and durability while embodying a high quality and various aesthetics including mother-of-pearl pattern.
도 1은 본 발명의 일 실시예에 따른 안경 제조 방법으로 구현된 금속 재질의 안경용 지지체 기반의 안경을 도시한다.FIG. 1 illustrates glasses based on a support for glasses made of a metal material implemented by a method of manufacturing glasses according to an embodiment of the present invention.
도 2는 본 발명의 일 실시예에 따른 안경 제조 방법으로 구현된 목재 재질의 안경용 지지체 기반의 안경을 도시한다.FIG. 2 illustrates glasses based on a support for glasses made of wood material implemented by a method of manufacturing glasses according to an embodiment of the present invention.
도 3은 본 발명의 일 실시예에 따른 안경 제조 방법으로 구현된 합성수지 재질의 안경용 지지체 기반의 안경을 도시한다.3 is a view illustrating glasses based support for glasses made of a synthetic resin material implemented by the method for manufacturing glasses according to an embodiment of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 일 실시예를 상세하게 설명한다. 이하 설명은 본 발명의 일 실시예들을 용이하게 이해하기 위한 것일 뿐이며, 본 발명의 보호범위를 제한하기 위한 것은 아니다. Hereinafter, with reference to the accompanying drawings will be described in detail an embodiment of the present invention. The following description is only for easily understanding the embodiments of the present invention, but is not intended to limit the protection scope of the present invention.
본 발명의 일 구체예는 안경용 지지체를 제공하는 단계; 상기 안경용 지지체의 표면에 옻칠을 수행하여 옻 층을 형성하는 단계; 및 상기 옻 층에 원하는 패턴에 따라 자개를 부착시켜 자개 문양을 형성하는 단계를 포함하는, 옻칠 및 자개 문양이 적용된 안경 제조 방법을 제공한다. 구체적으로는, 안경용 지지체를 제공하는 단계; 상기 안경용 지지체의 표면을 사포 처리하는 단계; 상기 사포 처리된 안경용 지지체의 표면에 옻칠을 수행하고 이를 건조함으로써 제1 옻 층을 형성하는 단계; 상기 제1 옻 층에 옻칠을 반복 수행함과 동시에 원하는 문양에 따라 자개를 부착시키고 이를 건조함으로써 자개 문양을 포함하는 제2 옻 층을 형성하는 단계; 상기 제2 옻 층에 정체칠을 도포하고, 사포 처리 후 건조함으로써 정체칠 층을 형성하는 단계; 및 상기 정체칠 층에 사포 처리를 반복 수행하여 광택 처리하는 단계를 포함하는, 옻칠 및 자개 문양이 적용된 안경 제조 방법을 제공한다.One embodiment of the present invention provides a support for glasses; Forming a lacquer layer by performing lacquer on the surface of the eyeglass support; And attaching mother-of-pearl according to a desired pattern on the lacquer layer to form mother-of-pearl pattern. Specifically, providing a support for glasses; Sanding the surface of the support for spectacles; Forming a first lacquer layer by performing lacquer on the surface of the sandpaper-treated eyeglass support and drying it; Forming a second lacquer layer including the mother-of-pearl pattern by repeatedly performing lacquer on the first lacquer layer and attaching mother-of-pearl according to a desired pattern and drying it; Applying a stagnation coat to the second lacquer layer, and forming a stagnation layer by drying after sandpaper treatment; And repeating the sandpaper treatment on the stagnant lacquer layer to provide a method for producing a glass, lacquer and mother-of-pearl pattern is applied.
본 발명의 일 구체예에 따른 안경 제조 방법은 안경용 지지체를 제공하는 단계를 포함한다. 상기 안경용 지지체는 안경테의 골격을 이루는 것이다. 상기 안경용 지지체는 금속, 합성수지 및 목재로 구성된 군으로부터 선택된 재질일 수 있다. 또한, 상기 안경용 지지체는 금속, 합성수지 및 목재로 구성된 군으로부터 선택된 2 이상의 재질의 조합일 수 있다. 상기 금속은 알루미늄, 스테인리스 스틸, 티타늄 등일 수 있으나, 이에 제한되지 않는다. 상기 목재는 일반적인 나무 재질로서, 다양하게 목재가 채택될 수 있다. 상기 합성수지는 플라스틱 재질이면 족하고, 특별히 제한되지 않으나, 투명 또는 반투명 재질일 수 있다. 본 발명의 일 구체예에 따르면, 상기 안경용 지지체는 기존 안경용 지지체의 굵기보다 얇게 구현될 수 있고, 그 재질의 밀도보다 상당히 낮게 구현될 수 있다. 상기 안경용 지지체는 기존과 같이 원하는 안경테의 전체적인 형상을 기반으로 구성될 수 있으나, 이하 상세하게 설명될 옻 층 및 자개 문양의 부피를 고려하여 그 규격이 결정되어야 한다.Glasses manufacturing method according to an embodiment of the present invention includes providing a support for the glasses. The spectacle supporter forms the frame of the spectacle frame. The eyeglass support may be a material selected from the group consisting of metal, synthetic resin and wood. In addition, the eyeglass support may be a combination of two or more materials selected from the group consisting of metal, synthetic resin and wood. The metal may be aluminum, stainless steel, titanium, or the like, but is not limited thereto. The wood is a general wood material, a variety of wood may be adopted. The synthetic resin is sufficient as long as it is a plastic material, and is not particularly limited, but may be a transparent or translucent material. According to one embodiment of the present invention, the spectacle support may be implemented thinner than the thickness of the existing spectacle support, it may be implemented significantly lower than the density of the material. The spectacle support may be configured based on the overall shape of the desired spectacle frame as in the prior art, the specification should be determined in consideration of the volume of the lacquer layer and mother-of-pearl pattern to be described in detail below.
본 발명의 일 구체예에 따른 안경 제조 방법은 상기 안경용 지지체의 표면에 옻칠을 수행하여 옻 층을 형성하는 단계를 포함한다. 상기 안경용 지지체의 표면에 옻 층을 형성함으로써, 상기 안경은 가볍고, 강력한 강도와 내구성을 갖추게 된다. 또한, 옻 층은 종래부터 인체에 무해하고 오히려 유익한 효능을 갖는 것으로 알려져 있다. 상기 옻 층은 혈액 순환, 두통 방지, 알레르기성 질환의 방지, 비염, 아토피 및 피부질환 예방, 전자파 차단 등에 효능에 있는 것으로 알려져 있으나, 이에 제한되는 것은 아니다. 일반적으로, 안경 사용자는 평소 오랜 시간 동안 안경을 착용한 상태로 생활하기 때문에 피로감을 느끼고 두통 등을 호소하는 경우가 많다. 그러나, 전통적인 생활 의학 문헌에 따르면, 옻칠을 수행함으로써 형성된 옻 층은 혈액 순환, 두통 방지 등에 효능이 있는 것으로 이해될 수 있기 때문에 옻칠을 안경 제조에 적용하는 것은 인체에 유익한 효능도 기대할 수 있게 된다. 또한, 상기 안경용 지지체의 표면에 옻 층을 형성함으로써, 다양한 디자인을 갖는 자개 문양을 처리할 수 있기 때문에, 안경테 표면에 고급스럽고 미세한 디자인을 강건하게 구현할 수 있다.Glasses manufacturing method according to an embodiment of the present invention includes the step of forming a lacquer layer by performing a lacquer on the surface of the support for the glasses. By forming a lacquer layer on the surface of the support for glasses, the glasses are light, strong strength and durability. In addition, lacquer layers are conventionally known to be harmless to humans and have rather beneficial effects. The lacquer layer is known to be effective in blood circulation, headache prevention, prevention of allergic diseases, rhinitis, atopic and skin diseases, electromagnetic shielding, etc., but is not limited thereto. In general, an eyeglass user often feels tired and complains of a headache because he / she lives in a state of wearing glasses for a long time. However, according to the traditional life medical literature, since the lacquer layer formed by performing lacquer can be understood to be effective in blood circulation, headache prevention, etc., the application of lacquer to the manufacture of glasses can also be expected to have beneficial effects on the human body. In addition, by forming a lacquer layer on the surface of the support for the glasses, it is possible to process the mother-of-pearl pattern having a variety of designs, it is possible to implement a high-quality and fine design on the surface of the spectacle frame.
본 발명의 일 실시예에 있어서, 상기 옻 층을 형성하는 단계는 제1 옻 층을 형성하는 단계 및 제2 옻 층을 형성하는 단계를 포함한다. 상기 제1 옻 층을 형성하는 단계는 이하 상세하게 설명될 자개 문양의 안정적인 부착에 기여할 수 있다. 상기 제1 옻 층을 형성하는 단계는 상기 제공된 안경용 지지체의 표면을 사포 처리한 후 진행된다. 상기 사포는 부드러운 재질이어야 하고, 경우에 따라서는 일정량의 수분을 함유할 수 있다. 그 후 상기 사포 처리된 안경용 지지체의 표면에 옻칠을 수행한다. 그 후 건조 단계를 수행해야 하는데, 상기 건조 단계는 18℃ 내지 19℃의 온도 범위 및 80% 내지 100%의 습도 범위에서 수행될 수 있다. 실제 안경 제조 과정에서 상기 온도 범위 및 습도 범위를 벗어났을 경우 제1 옻 층이 상기 안경용 지지체 표면에 강건하고 견고하게 형성되지 않음을 확인하였다. 물론 다른 기타 원인이 있을 수 있으나, 반복 과정 중 상기 온도 범위 및 습도 범위에서 제1 옻 층이 원하는 강도를 견고하게 형성되는 것으로 확인되었다. 또한, 상기 건조 단계는 상기 온도 범위 및 습도 범위에서 건조 숙성시킨 후 일정시간 동안, 예를 들어 약 30분 내지 60분 동안 일광 건조할 경우 통상의 건조 단계보다 약 50% 이상 건조시간을 단축시킬 수 있는 것으로 확인되었다. 또한, 상기 건조 단계는 뒤이어 상기 옻 층 형성 단계를 반복 수행할 수 있다. 바람직하게는 상기 옻 층을 재형성하는 단계 및 재건조 단계를 2회 수행할 수 있다. 상기 옻 층 형성 단계를 반복함으로써, 제1 옻 층이 더욱 강건하고 견고하게 형성된다. 뒤이어, 상기 제2 옻 층을 형성하는 단계를 수행한다. 상기 제2 옻 층 형성 단계는 상기 옻 층에 원하는 패턴에 따라 자개를 부착시켜 자개 문양을 형성하는 단계를 포함한다. 구체적으로, 상기 제1 옻 층에 옻 칠을 반복 수행함과 동시에 원하는 패턴에 따라 자개를 부착시키는 단계를 포함한다. 상기 제2 옻 층 형성 단계에서 다양한 안경테 표면 디자인이 결정된다. 상기 자개는 공지된 자개 재료를 사용할 수 있다. 또한, 상기 자개는 천연 자개 또는 인공 자개일 수 있다. 또한, 상기 자개 표면 그 자체에 별도로 천연 색소로 미세 가공하여 추가적인 문양을 도입할 수도 있다. 이와 같이, 다양한 자개 문양을 표현함으로써, 안경테 표면에 고급스럽고 미세한 문양을 구현할 수 있다. 한편, 상기 제2 옻 층 형성 단계는 천연 색소를 배합하는 것을 더 포함할 수 있고, 이 경우 자개 문양 이외의 다양한 색감을 추가로 구현할 수 있다. 뒤이어, 상기 건조 단계를 수행하며, 이 경우 상기 건조 단계는 이미 설명된 바와 같이, 18℃ 내지 19℃의 온도 범위 및 80% 내지 100%의 습도 범위에서 수행될 수 있다.In one embodiment of the present invention, the forming of the lacquer layer includes forming a first lacquer layer and forming a second lacquer layer. Forming the first lacquer layer may contribute to the stable attachment of the mother-of-pearl pattern to be described in detail below. The step of forming the first lacquer layer is carried out after sanding the surface of the provided support for glasses. The sandpaper should be a soft material, and in some cases may contain a certain amount of water. After that, lacquer is performed on the surface of the sandpaper treated support for glasses. Thereafter, a drying step should be performed, which may be performed at a temperature range of 18 ° C. to 19 ° C. and a humidity range of 80% to 100%. It was confirmed that the first lacquer layer was not firmly and firmly formed on the surface of the support for the glasses when the temperature was outside the temperature range and the humidity range during the actual glasses manufacturing process. Of course, there may be other causes, it was confirmed that the first lacquer layer firmly formed the desired strength in the temperature range and humidity range during the repeating process. In addition, the drying step may shorten the drying time of about 50% or more than the usual drying step for a period of time, for example, about 30 minutes to 60 minutes after daylight drying in the temperature range and humidity range It was confirmed that there is. In addition, the drying step may be followed by repeating the lacquer layer forming step. Preferably, the step of reforming the lacquer layer and the redrying step may be performed twice. By repeating the lacquer forming step, the first lacquer layer is more robust and firmly formed. Subsequently, the step of forming the second lacquer layer is performed. The second lacquer layer forming step may include forming a mother-of-pearl pattern by attaching mother-of-pearl to the lacquer layer according to a desired pattern. Specifically, repeating the lacquer on the first lacquer layer and at the same time comprising the step of attaching mother-of-pearl according to the desired pattern. Various eyeglass frame surface designs are determined in the second lacquer layer forming step. The mother-of-pearl may use a known mother-of-pearl material. In addition, the mother-of-pearl may be natural mother-of-pearl or artificial mother-of-pearl. Further, the mother-of-pearl surface itself may be further processed by micro-processing with natural pigments to introduce additional patterns. As such, by expressing a variety of mother-of-pearl pattern, it is possible to implement a fine and fine pattern on the surface of the spectacle frame. On the other hand, the second lacquer layer forming step may further include blending a natural pigment, in this case it may further implement a variety of colors other than mother-of-pearl pattern. Subsequently, the drying step is performed, in which case the drying step may be performed at a temperature range of 18 ° C. to 19 ° C. and a humidity range of 80% to 100%, as already described.
본 발명의 일 구체예에 따른 안경 제조 방법은 상기 제2 옻 층에 정체칠을 도포하고, 사포 처리 후 건조함으로써 정체칠 층을 형성하는 단계를 포함할 수 있다. 상기 정체칠 층 형성 단계는 3회 반복되어 상 정체칠 층, 중 정체칠 층 및 하 정체칠 층을 형성하는 것일 수 있다. 상기 정체칠을 통해 상기 옻 층 및 자개 문양은 안정적으로 상기 안경용 지지체에 부착된다. 뒤이어, 건조 단계를 수행하며, 이 경우 상기 건조 단계는 이미 설명된 바와 같이, 18℃ 내지 19℃의 온도 범위 및 80% 내지 100%의 습도 범위에서 수행될 수 있다. Glasses manufacturing method according to an embodiment of the present invention may include the step of forming a stagnant fill layer by applying a stagnation fill to the second lacquer layer, and dried after sandpaper treatment. The stagnation layer forming step may be repeated three times to form an upper stagnation layer, a middle stagnation layer and a lower stagnation layer. The lacquer layer and mother-of-pearl pattern is stably attached to the eyeglass support through the stagnation. Subsequently, a drying step is performed, in which case the drying step can be carried out in a temperature range of 18 ° C. to 19 ° C. and a humidity range of 80% to 100%, as already described.
본 발명의 일 구체예에 따른 안경 제조 방법은 상기 정체칠 층에 사포 처리를 반복 수행하여 광택 처리하는 단계를 포함할 수 있다. 이와 같은 광택 처리를 함으로써, 안경용 지지체의 표면이 더욱 윤기가 흐르고 고급스럽게 보인다. 한편, 상기 광택 처리 단계는 상기 정체칠 층에 콩기름을 적용하는 것을 더 포함할 수 있다. Glasses manufacturing method according to an embodiment of the present invention may include the step of repeating the sandpaper treatment on the stagnant lacquer layer to the gloss treatment. By such a gloss treatment, the surface of the support for spectacles becomes more shiny and luxurious. On the other hand, the gloss treatment step may further include applying soybean oil to the stagnant layer.
본 발명의 일 실시예에 따른 안경 제조 방법에 따라 전 처리 과정을 완료한 후 다양한 디자인을 갖는 안경을 제조하였다. 그 결과는 도 1 내지 도 3에 도시된다. 구체적으로, 도 1은 본 발명의 일 실시예에 따른 안경 제조 방법으로 구현된 알루미늄 재질의 안경용 지지체 기반의 안경을 도시하고, 도 2는 본 발명의 일 실시예에 따른 안경 제조 방법으로 구현된 목재 재질의 안경용 지지체 기반의 안경을 도시하며, 도 3은 본 발명의 일 실시예에 따른 안경 제조 방법으로 구현된 플라스틱 재질의 안경용 지지체 기반의 안경을 도시한다.After completing the pretreatment process according to the spectacle manufacturing method according to an embodiment of the present invention to manufacture a spectacles having a variety of designs. The results are shown in Figures 1-3. Specifically, FIG. 1 illustrates glasses based on a support for aluminum glasses implemented as a method of manufacturing glasses according to an embodiment of the present invention, and FIG. 2 is wood implemented by a method of manufacturing glasses according to an embodiment of the present invention. 3 shows glasses based glasses for a material, and FIG. 3 illustrates glasses based glasses support for plastic material implemented by a method for manufacturing glasses according to an embodiment of the present invention.

Claims (8)

  1. 안경용 지지체를 제공하는 단계;Providing a support for the spectacles;
    상기 안경용 지지체의 표면에 옻칠을 수행하여 옻 층을 형성하는 단계; 및Forming a lacquer layer by performing lacquer on the surface of the eyeglass support; And
    상기 옻 층에 원하는 패턴에 따라 자개를 부착시켜 자개 문양을 형성하는 단계; 를 포함하는, 옻칠 및 자개 문양이 적용된 안경 제조 방법.Attaching mother-of-pearl according to a desired pattern on the lacquer layer to form a mother-of-pearl pattern; Containing, lacquer and mother-of-pearl pattern applied glasses manufacturing method.
  2. 안경용 지지체를 제공하는 단계;Providing a support for the spectacles;
    상기 안경용 지지체의 표면을 사포 처리하는 단계;Sanding the surface of the support for spectacles;
    상기 사포 처리된 안경용 지지체의 표면에 옻칠을 수행하고 이를 건조함으로써 제1 옻 층을 형성하는 단계;Forming a first lacquer layer by performing lacquer on the surface of the sandpaper-treated eyeglass support and drying it;
    상기 제1 옻 층에 옻칠을 반복 수행함과 동시에 원하는 패턴에 따라 자개를 부착시키고 이를 건조함으로써 자개 문양을 포함하는 제2 옻 층을 형성하는 단계;Forming a second lacquer layer including a mother-of-pearl pattern by repeatedly performing lacquer on the first lacquer layer and simultaneously attaching the mother-of-pearl and drying it according to a desired pattern;
    상기 제2 옻 층에 정체칠을 도포하고, 사포 처리 후 건조함으로써 정체칠 층을 형성하는 단계; 및Applying a stagnation coat to the second lacquer layer, and forming a stagnation layer by drying after sandpaper treatment; And
    상기 정체칠 층에 사포 처리를 반복 수행하여 광택 처리하는 단계;Performing a sanding treatment on the stagnant lacquer layer repeatedly to perform gloss treatment;
    를 포함하는, 옻칠 및 자개 문양이 적용된 안경 제조 방법.Containing, lacquer and mother-of-pearl pattern applied glasses manufacturing method.
  3. 제2항에 있어서, 상기 제1 옻 층 건조 단계, 상기 제2 옻 층 건조 단계, 및 상기 정체칠 층 건조 단계는 18℃ 내지 19℃의 온도 범위 및 80% 내지 100%의 습도 범위에서 수행되는 것을 특징으로 하는 안경 제조 방법.The method of claim 2, wherein the first lacquer layer drying step, the second lacquer layer drying step, and the stagnation layer drying step are performed at a temperature range of 18 ° C. to 19 ° C. and a humidity range of 80% to 100%. Glasses manufacturing method, characterized in that.
  4. 제2항에 있어서, 상기 제1 옻 층을 형성하는 단계는 2회 반복 수행되는 것을 특징으로 하는 안경 제조 방법.The method of claim 2, wherein the forming of the first lacquer layer is performed twice.
  5. 제2항에 있어서, 상기 정체칠 층 형성 단계는 3회 반복되어 상 정체칠 층, 중 정체칠 층 및 하 정체칠 층을 형성하는 것을 특징으로 하는 안경 제조 방법.The method of claim 2, wherein the forming the stagnation layer is repeated three times to form an upper stagnation layer, a middle stagnation layer, and a lower stagnation layer.
  6. 제2항에 있어서, 상기 광택 처리 단계는 상기 정체칠 층에 콩기름을 적용하는 것을 더 포함하는 것을 특징으로 하는 안경 제조 방법.The method of claim 2, wherein the glossing step further comprises applying soybean oil to the stagnant lacquer layer.
  7. 제2항에 있어서, 상기 제2 옻 층 형성 단계는 천연 색소를 배합하는 것을 더 포함하는 것을 특징으로 하는 안경 제조 방법.The method of claim 2, wherein the forming of the second lacquer layer further comprises blending a natural pigment.
  8. 제1항 또는 제2항에 있어서, 상기 안경용 지지체는 금속, 합성수지 및 목재로 구성된 군으로부터 선택된 재질인 것을 특징으로 하는 안경 제조 방법.The method of claim 1 or 2, wherein the spectacles support is a material selected from the group consisting of metal, synthetic resin and wood.
PCT/KR2012/004589 2011-06-10 2012-06-11 Method for manufacturing eyeglasses with an applied lacquer and mother-of-pearl pattern WO2012169853A2 (en)