KR101098865B1 - Manufacturing method of eyeglasses frame - Google Patents

Manufacturing method of eyeglasses frame Download PDF

Info

Publication number
KR101098865B1
KR101098865B1 KR1020090089052A KR20090089052A KR101098865B1 KR 101098865 B1 KR101098865 B1 KR 101098865B1 KR 1020090089052 A KR1020090089052 A KR 1020090089052A KR 20090089052 A KR20090089052 A KR 20090089052A KR 101098865 B1 KR101098865 B1 KR 101098865B1
Authority
KR
South Korea
Prior art keywords
spectacle frame
paint
frame
glasses
color
Prior art date
Application number
KR1020090089052A
Other languages
Korean (ko)
Other versions
KR20110031698A (en
Inventor
박원식
이창우
Original Assignee
박원식
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박원식 filed Critical 박원식
Priority to KR1020090089052A priority Critical patent/KR101098865B1/en
Publication of KR20110031698A publication Critical patent/KR20110031698A/en
Application granted granted Critical
Publication of KR101098865B1 publication Critical patent/KR101098865B1/en

Abstract

본 발명은 합성수지 혹은 금속테로 구성된 안경테를 다양한 디자인으로 제작구성하되, 상기 안경테 외면에 빛의 반사각에 따라 다양한 색상으로 변색하는 도료를 착색시켜 보는 시각에 따라 안경테의 색상이 다양하게 변색되게 구성함으로서, 일반안경테와는 달리 새로운 미감을 창출케 함과 동시에, 제품의 고급화와 함께 소비자들의 욕구를 충족시킬 수 있도록 한 것이다.According to the present invention, the spectacle frame made of synthetic resin or metal frame is manufactured and configured in various designs, and the color of the spectacle frame is variously discolored according to the viewing angle by coloring paints discolored in various colors according to the reflection angle of light on the outer surface of the spectacle frame, Unlike general eyeglass frames, they create new aesthetics and at the same time satisfy the needs of consumers with high quality products.

상기 목적을 달성하기 위하여 본 발명은 합성수지 혹은 금속테로 구성되는 안경테를 구성함에 있어서, 성형된 안경테를 세척, 건조하고, 상기 안경테 외면에 빛의 반사각도에 따라 색상이 달리 표현되는 홀로그램도료나 펄도료와 같은 변색도료를 분사하여 안경테 표면에 변색도료가 골고루 착색되게 한 다음 고온건조하고, 상기 변색도료 표면에 다시 투명수지를 코팅하여 보호막을 형성하고, 고온건조하여 안경테를 제조하는 것으로서 안경테 외면에 코팅된 변색도료에 의해 안경테의 색상이 빛의 반사각도에 따라 달리 표현되게 한 것이다.In order to achieve the above object, the present invention is to construct a spectacle frame made of synthetic resin or metal frame, to wash and dry the molded spectacle frame, the holographic paint or pearl paint is expressed differently according to the angle of light reflection on the outer surface of the spectacle frame Discoloring paint on the surface of the spectacle frame by spraying discoloring paint, such as high-temperature drying, and then coated with a transparent resin on the surface of the discoloration paint to form a protective film, and to produce a spectacle frame by high temperature drying to produce a spectacle frame The color change of the spectacle frame causes the colors of the frames to be expressed differently according to the reflection angle of light.

Description

변색하는 안경테의 제조방법{MANUFACTURING METHOD OF EYEGLASSES FRAME}MANUFACTURING METHOD OF EYEGLASSES FRAME}

본 발명은 변색하는 안경테의 제조방법에 관한 것으로서, 특히 안경테가 빛의 반사각도에 따라 다양한 색상으로 변색되게 하므로서, 새로운 제품의 안경테를 요구하는 소비자들의 욕구를 충족케 함은 물론, 상품성이 우수한 고품질의 안경테를 제공하고자 하는 것이다.The present invention relates to a method for manufacturing a spectacle frame to be discolored, in particular, because the spectacle frame is changed to a variety of colors according to the angle of reflection of light, satisfying the needs of consumers who require a spectacle frame of a new product, as well as high commercial quality To provide a frame of glasses.

일반적으로 안경테는 합성수지 혹은 금속테로 구성되면서 여러 디자인의 제품이 제공되고 있을 뿐 아니라, 색상도 다양하게 표현되고 있다.In general, eyeglass frames are made of synthetic resin or metal frames, and products of various designs are provided, as well as various colors.

그러나 상기에서 제공되고 있는 안경테에 표현된 색상은 주로 단일색상으로 표현되어 있어 미감이 단순할 뿐 아니라 장기간 착용시 쉽게 싫증을 느끼게 된다.However, the color expressed on the spectacle frame provided above is mainly expressed in a single color, so that the aesthetics are not only simple but also easily get tired when worn for a long time.

따라서 다양한 디자인의 안경테 제품을 요구하는 소비자들의 욕구를 충족시키기에는 미흡한 등의 단점이 있는 것이다.Therefore, there is a disadvantage such as insufficient to meet the needs of consumers who require a variety of glasses frame products of the design.

본 발명은 이러한 종래의 제반 단점을 시정하고자 합성수지 혹은 금속테로 구성된 안경테를 다양한 디자인으로 제작구성하되, 상기 안경테 외면에 빛의 반사각에 따라 다양한 색상으로 변색하는 도료를 착색시켜 보는 시각에 따라 안경테의 색상이 다양하게 변색되게 구성함으로서, 일반안경테와는 달리 새로운 미감을 창출케 함과 동시에, 제품의 고급화와 함께 소비자들의 욕구를 충족시킬 수 있도록 한 것이다.The present invention is configured to manufacture a spectacle frame made of synthetic resin or metal frame in a variety of designs in order to correct the various disadvantages of the prior art, the color of the spectacle frame according to the viewing color by coloring the color to the various colors according to the reflection angle of light on the outer surface of the spectacle frame By varying the composition of the discoloration, it is possible to create a new aesthetic unlike general glasses frames, and to satisfy the needs of consumers with high-quality products.

상기 목적을 달성하기 위하여 본 발명은 합성수지 혹은 금속테로 구성되는 안경테를 구성함에 있어서, 성형된 안경테를 세척, 건조하고, 상기 안경테 외면에 빛의 반사각도에 따라 색상이 달리 표현되는 홀로그램도료나 펄도료와 같은 변색도료를 분사하여 안경테 표면에 변색도료가 골고루 착색되게 한 다음 고온건조하고, 상기 변색도료 표면에 다시 투명수지를 코팅하여 보호막을 형성하고, 고온건조하여 안경테를 제조하는 것으로서 안경테 외면에 코팅된 변색도료에 의해 안경테의 색상이 빛의 반사각도에 따라 달리 표현되게 한 것이다.In order to achieve the above object, the present invention is to construct a spectacle frame made of synthetic resin or metal frame, to wash and dry the molded spectacle frame, the holographic paint or pearl paint is expressed differently according to the angle of light reflection on the outer surface of the spectacle frame Discoloring paint on the surface of the spectacle frame by spraying discoloring paint, such as high-temperature drying, and then coated with a transparent resin on the surface of the discoloration paint to form a protective film, and coating the outer surface of the spectacle frame by manufacturing a high-temperature drying frame The color change of the spectacle frame causes the colors of the frames to be expressed differently according to the reflection angle of light.

본 발명은 합성수지 혹은 금속으로 구성된 안경테를 구성하되, 안경테 외면에 홀로그램도료나 펄도료와 같이 빛의 반사각도에 따라 색상이 변하는 변색도료가 착색되게 함으로써, 안경의 착용중 변색도료에 의해 안경테를 보는 각도에 따라 색 상이 변화되게 하여 단일안경테로서 다양한 디자인으로 변화하는 안경의 효과를 얻을 수 있어 장기간 안경을 착용하더라도 쉽게 싫증을 느끼지 않을 뿐 아니라 새로운 디자인의 안경제품을 제공하여 소비자들의 욕구충족은 물론 보다 고급화된 안경제품을 제공할 수 있게 되는 등의 효과가 있는 것이다.The present invention constitutes a spectacle frame made of synthetic resin or metal, but by discoloring the color change color according to the reflection angle of the light, such as holographic paints and pearl paints on the outer surface of the spectacle frame, to see the spectacle frame by discoloring paint while wearing glasses As the color changes according to the angle, it is possible to obtain the effect of glasses that change into various designs as a single glasses frame.It is not easy to get tired of wearing glasses for a long time, but also provides a new design glasses products to satisfy the needs of consumers. It is possible to provide an advanced eyewear product.

이하 본 발명의 실시예를 첨부도면에 따라 상세히 설명한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명에서 제공하고자 하는 안경테는 아크릴수지 혹은 에폭시수지와 같은 합성수지로 구성된 수지안경테나 티타늄, 알미늄, 스테인레스등과 같은 금속안경테에 적용할 수 있으며, 렌즈나 코다리, 안경다리팁과 같은 소재를 조립하기 전에 처리한다.The spectacle frame to be provided in the present invention can be applied to resin glasses frames composed of synthetic resins such as acrylic resins or epoxy resins or metal glasses frames such as titanium, aluminum, stainless steel, etc., and to assemble a material such as a lens, a cord or a glass leg tip. Handle before.

또한 무테안경이나, 렌즈테와 안경다리가 조립된 일반안경에 적용할 수 있다.Also, it can be applied to rimless glasses or general glasses assembled with lens frames and glasses legs.

본 발명의 실시예에서는 금속무테안경이나 일반안경테에 적용되는 안경다리를 기준으로 설명한다.In the embodiment of the present invention will be described on the basis of the eyeglass legs applied to the metal rimless glasses or general eyeglass frames.

[실시예 1]Example 1

[제품성형공정][Product forming process]

프레스금형으로 안경다리를 성형하고, 상기 안경다리 일측 단부에 연결편(11)을 용접구성하여 통상의 안경다리(10)를 제작한다.The spectacles are molded into a press mold, and the connecting piece 11 is welded to one end of the spectacles to produce a normal pair of spectacles 10.

[세척공정][Washing process]

상기 안경다리(10)를 먼저 물로 세척하여 안경다리(10) 표면에 부착된 이물 질을 깨끗이 제거하는 공정이다.The glasses legs 10 are first washed with water to remove foreign substances attached to the surfaces of the glasses legs 10.

상기 세척수단으로서는 안경다리(10)를 초음파 세척하여 표면에 부착된 이물질이 완전분리제거되게 한 다음 다시 물로 깨끗이 헹구어 낸다.As the cleaning means, ultrasonic glasses are cleaned by the ultrasonic bridge 10 to completely remove and remove foreign substances adhering to the surface, and then rinse again with water.

상기 세척공정을 통하여 표면이 깨끗이 세척된 안경다리(10)를 건조기에 투입한 다음 165~170℃에서 5~10분간 건조하여 표면에 부착된 수분을 완전히 제거한다.Through the washing step, the spectacles 10, the surface of which is cleaned, are put in a dryer, and then dried at 165 to 170 ° C. for 5 to 10 minutes to completely remove the moisture attached to the surface.

[변색도료 착색공정][Tarnish Paint Coloring Process]

본 공정은 이물질이 깨끗이 세척건조된 안경다리(10) 표면에 빛의 반사각도에 따라 변색하는 변색도료(20)를 분무하여 착색하는 공정이다.[도 3 참조]This process is a process of spraying and coloring the discoloration paint 20 which is discolored according to the reflection angle of light on the surface of the glass leg 10, the foreign matter is washed and dried cleanly.

상기에서 사용되는 변색도료(20)는 홀로그램도료나 펄도료와 같이 빛의 반사각도에 따라 변색하는 모든 도료의 사용이 가능하다.The color change paint 20 used in the above can be used for all the color change according to the reflection angle of light, such as holographic paints and pearl paints.

변색도료의 착색은 다음과 같이 된다.Coloring of the discoloration paint is as follows.

변색도료를 착색하고자 하는 안경다리(10)를 분무실에 투입한 다음 변색도료(20)를 분무하여 변색도료(20)가 안경다리(10) 외면에 골고루 착색되게 하며, 상기 변색도료(20)로서 본 발명에서는 프리즘이팩트(상품명)를 사용하였다.The color change paint 20 is put into the spray chamber, and then the color change paint 20 is sprayed so that the color change paint 20 is evenly colored on the outer surface of the light leg 10. The color change paint 20 In the present invention, the prism effect (brand name) was used.

이때 안경다리(10) 표면에 착색이 고르게 되도록 하기 위하여 안경다리(10)를 서서히 회전시키거나, 변색도료(20)가 분사되는 분무기를 여러곳에 설치하여 사용할 수도 있다.In this case, in order to evenly color the surface of the glasses 10, the glasses 10 may be rotated slowly, or may be used by installing a sprayer in which the discoloration paint 20 is sprayed.

상기에서와 같이 하여 안경다리(10) 표면에 변색도료(20)의 착색이 완료되면 건조기에 투입하여 165~170℃에서 5~10분간 건조하여 표면에 착색된 변색도료(20) 가 완전히 건조되게 한다.When the color of the discoloration paint 20 is completed on the surface of the glass leg 10 as described above is put into the dryer to dry for 5 to 10 minutes at 165 ~ 170 ℃ to completely dry the color change paint 20 on the surface do.

[보호층 코팅공정][Protective layer coating process]

본 공정은 변색도료(20)가 착색된 안경다리(10) 외면에 투명수지(30)를 분무코팅하여, 변색도료(20)가 보호되게 하는 공정으로서[도 4 참조], 상기에서 사용되는 투명수지(30)는 아크릴수지나 에폭시수지와 같이 코팅된 수지층이 투명하면서 내구성이 우수한 수지의 사용이 가능하다.This process is a process for spray-coating the transparent resin 30 on the outer surface of the glass leg 10, the color change paint 20 is colored, to protect the color change paint 20 [see Fig. 4], the transparent used above The resin 30 may use a resin having excellent durability while having a transparent resin layer coated with an acrylic resin or an epoxy resin.

즉 변색도료(20)의 착색, 건조가 완료된 안경다리(10) 외면에 투명수지(30)를 코팅하여 변색도료(20) 표면에 다시 투명수지(30)가 코팅되게 하고, 상기 안경다리(10)를 건조기에 투입한 다음 155~160℃에서 30분간 건조함으로써, 본 발명이 완료된다.That is, the transparent resin 30 is coated on the surface of the discolored paint 20 by coating the transparent resin 30 on the outer surface of the discolored paint 20 and the drying of the finished glass legs. ) Is put into a dryer and then dried for 30 minutes at 155 ~ 160 ℃, the present invention is completed.

본 공정에서 사용한 투명수지(30)는 "슈프림1000"(제품명)을 적용하였다.As for the transparent resin 30 used in this process, "Supreme 1000" (product name) was applied.

[실시예 2][Example 2]

실시예 2에서는 실시예 1에서와 같은 공정으로 제품을 처리하되 세척공정과 변색도료 착색공정 사이에 전착도장공정이 추가된 것으로서, 실시예 2를 설명한다.In Example 2, the product was treated in the same process as in Example 1, but the electrodeposition coating process was added between the washing process and the discoloration paint coloring process.

[제품성형공정][Product forming process]

실시예 1과 동일하게 처리한다.The same process as in Example 1 is carried out.

[세척공정][Washing process]

실시예 1과 동일하게 처리한다.The same process as in Example 1 is carried out.

[전착도장공정][Deposition Coating Process]

본 공정은 세척건조된 안경다리(10) 표면에 유색도료를 전착도장하여 후공정에서 실시되는 변색도료(20)의 색상표현이 보다 효과적으로 이루어질 수 있게 하는 것이다.This process is to make the color expression of the discoloration paint 20 to be carried out in the post-process by coating the colored paint on the surface of the washed and dried glasses legs 10 more effectively.

즉 세척건조된 안경다리(10) 표면에 유색아크릴수지 혹은 유색에폭시수지를 전착도장하여 전착수지층(50)이 형성되게 한 다음 160~170℃에서 5~10분간 건조하여 안경다리(10) 표면에 유색의 전착수지층(50)이 형성되게 한다.[도 6참조]That is, the electrodeposited resin layer 50 is formed by electrodepositing colored acrylic resin or colored epoxy resin on the washed and dried glasses legs 10, and then dried at 160 to 170 ° C. for 5 to 10 minutes to surface the glasses legs 10. To form a colored electrodeposited resin layer 50 in FIG.

[변색도료 착색공정][Tarnish Paint Coloring Process]

상기 전착도장공정에서 안경다리 표면에 전착수지층(50)이 형성되게 한 다음 상기 전착수지층(50) 위에 실시예 1의 변색도료 착색공정과 동일하게 변색도료(20)가 착색되게 한다.[도 7 참조]In the electrodeposition coating process, the electrodeposition resin layer 50 is formed on the surface of the glasses legs, and then the discoloration paint 20 is colored on the electrodeposition resin layer 50 in the same manner as in the discoloration paint coloring process of Example 1. See FIG. 7]

[보호층 코팅공정][Protective layer coating process]

실시예 1과 동일하게 처리한다.[도 8 참조]The same process as in Example 1 was performed.

상기에서와 같은 공정으로 안경테 제조를 위한 안경다리나 렌즈테와 같은 부품들을 제조하고, 상기에서 제조된 부품을 조립하여 안경테(60)를 구성하고, 상기 안경테(60)에 렌즈(61)나 코다리(62), 안경다리팁(62)과 같은 부품을 조립하여 안경을 완성하게 된다.In the same process as described above to manufacture the parts such as the eyeglass frame or lens frame for the manufacture of the frame, by assembling the components manufactured in the above to constitute the eyeglass frame 60, the lens 61 or the cord ( 62), the parts such as glasses leg tip 62 is assembled to complete the glasses.

상기에서와 같이 제조된 안경테(60)는 안경테(60) 표면에 홀로그램도료나 펄도료와 같이 빛의 반사각도에 따라 색상이 달리 표현되는 변색도료(20)가 착색되어 있어 안경테(60)를 착용하게 되면 보는 각도에 따라 안경테(60)의 색상이 다양하게 변하게 된다.Glasses frame 60 manufactured as described above wears the glasses frame 60 is colored on the surface of the glasses frame 60, the color change paint 20 is expressed differently according to the reflection angle of light, such as holographic paint or pearl paint. The color of the spectacle frame 60 changes in accordance with the viewing angle.

특히 햇빛에 노출되어 반사될 경우 색상이 더욱 선명하고 다양하게 변화하게 되므로 일반안경은 물론 선글라스에 적용하여 사용하여도 우수한 효과를 기대할 수 있게 된다.In particular, when exposed to sunlight, the color changes more vividly and variously, so it is possible to expect excellent effects even when applied to sunglasses as well as general glasses.

따라서 단일 안경테(60)로부터 다양한 색상의 변색을 기대할 수 있게 되므로 소비자들의 욕구충족은 물론 고품질의 안경테제품을 제공할 수 있게 된다.Therefore, it is possible to expect a variety of color changes from a single spectacle frame 60, it is possible to provide high-quality spectacle frame products as well as satisfying the needs of consumers.

도 1 : 본 발명을 적용하고자 하는 안경다리의 일예시도1 is an example of the eyeglass legs to apply the present invention

도 2 : 도 1의 상태에서 안경다리 표면에 변색도료를 착색시킨 상태도FIG. 2: A state diagram in which a discoloration paint is colored on the surface of an eyeglass leg in the state of FIG. 1

도 3 : 본 발명 안경다리의 단면구성도3 is a cross-sectional view of the glasses leg of the present invention

도 4 : 도 3의 상태에서 안경다리 표면에 변색도료가 코팅된 상태도4 is a state in which the discoloration paint is coated on the surface of the glasses in the state of FIG.

도 5 : 도 4의 상태에서 투명수지가 코팅된 상태도5: a state in which the transparent resin is coated in the state of FIG.

도 6 : 도 3의 상태에서 안경다리 표면에 전착수지층이 형성된 상태도6 is a state diagram in which the electrodeposition resin layer is formed on the surface of the glasses in the state of FIG.

도 7 : 도 6의 상태에서 변색도료가 코팅된 상태도7 is a state in which the color change coating is coated in the state of FIG.

도 8 : 도 7의 상태에서 투명수지가 코팅된 상태도8: a state in which the transparent resin is coated in the state of FIG.

도 9 : 본 발명의 안경다리를 무테안경에 작용한 상태의 사시도9 is a perspective view of a state in which the glasses leg of the present invention acted on the rimless glasses

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

(10)--안경다리 (11)--연결편(10)-glasses leg (11)-connection

(20)--변색도료 (30)--투명수지(20)-Tarnish Paint (30)-Transparent Resin

(50)--전착수지층 (60)--안경테(50)-Electrode Resin Layer (60)-Glasses Frame

Claims (2)

성형된 안경다리를 세척건조하고, 상기 안경다리 표면에 도료를 분무, 착색, 건조하고, 도료가 착색, 건조된 안경다리 표면에 투명수지를 코팅, 건조하고, 상기 안경다리를 조립하여 제조하는 안경테의 제조방법에 있어서, 안경다리(10) 표면에 착색되는 도료는 변색도료(20)이고, 착색된 변색도료(20)는 건조기 내에서 165~170℃에서 5~10분간 건조하고, 변색도료가 착색, 건조된 안경다리 표면에 투명수지(30)를 코팅한 다음, 건조기 내에서 155~160℃에서 30분간 건조하여 변색도료가 착색된 안경다리를 제조하고, 상기 안경다리를 조립하여 제조함을 특징으로 하는 변색하는 안경테의 제조방법.Eyeglass frames manufactured by washing and drying molded eyeglass legs, spraying, coloring, and drying paint on the surface of the eyeglass legs, coating and drying transparent resin on the surface of the painted and dried eyeglass legs, and assembling the eyeglass legs. In the manufacturing method of, the color to be painted on the surface of the glass legs 10 is a discoloration paint 20, the colored discoloration paint 20 is dried in the dryer for 5 to 10 minutes at 165 ~ 170 ℃, the discoloration paint After coating the transparent resin 30 on the surface of the colored, dried eyeglasses, and drying for 30 minutes at 155 ~ 160 ℃ in a dryer to produce a color change-colored eyeglasses, and to assemble the glasses legs Method for producing a spectacle frame to be discolored. 삭제delete
KR1020090089052A 2009-09-21 2009-09-21 Manufacturing method of eyeglasses frame KR101098865B1 (en)