WO2012150804A2 - 담체를 이용한 나노 파우더 제조 방법 - Google Patents

담체를 이용한 나노 파우더 제조 방법 Download PDF

Info

Publication number
WO2012150804A2
WO2012150804A2 PCT/KR2012/003422 KR2012003422W WO2012150804A2 WO 2012150804 A2 WO2012150804 A2 WO 2012150804A2 KR 2012003422 W KR2012003422 W KR 2012003422W WO 2012150804 A2 WO2012150804 A2 WO 2012150804A2
Authority
WO
WIPO (PCT)
Prior art keywords
carrier
nanoparticles
metal
vapor
stirring
Prior art date
Application number
PCT/KR2012/003422
Other languages
English (en)
French (fr)
Other versions
WO2012150804A3 (ko
Inventor
고석근
Original Assignee
주식회사 나노케미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 나노케미 filed Critical 주식회사 나노케미
Publication of WO2012150804A2 publication Critical patent/WO2012150804A2/ko
Publication of WO2012150804A3 publication Critical patent/WO2012150804A3/ko

Abstract

본 발명은 진공 증착조, 상기 진공 증착조 내에 구비된 교반조; 상기 교반조 내에 구비되고 담체를 교반하는 스크류; 및 상기 진공 증착조 내에 교반조 상부에 구비되고 나노입자 형성을 위한 증기 입자를 발생시키는 증착원으로 구성되는, 담체에 부착된 나노 파우더 제조 장치를 사용하고, a) 상기 진공 증착조의 진공도가 10-4 내지 1 torr 가 되도록 불활성 기체를 진공 증착조에 포함시키는 단계; b) 상기 증착원을 이용하여 나노입자 형성을 위한 증기 입자를 발생시키는 단계; c) 상기 스크류의 속도를 1 내지 200rpm으로 조절하여 담체를 교반하는 단계; 및 d) 상기 담체 상에 증기 입자를 증착하여 나노입자를 형성하는 단계를 포함하는 것을 특징으로 하는, 담체에 부착된 나노 파우더 제조 방법에 관한 것이다.

Description

【명세서】
담체를 이용한 나노 파우더 제조 방법
【기술분야】
본 발명은 담체를 이용한 나노 파우더 제조 방법에 관한 것이다. 본 출원은 2011년 5월 2일에 한국 특허청에 제출된 한국 특허 출원 제 1으2011ᅳ 0041584호의 출원일의 이익을 주장하며, 그 내용 전부는 본 명세서에 포함된다. 【배경기술】
나노 입자는 화학적 방법으로는, 수용액 상태에서 존재하는 금속 이온들에 환원제와 분산제를 첨가함으로써 금속이온들이 금속고체입자로 전환되는 초기 과정에서 형성된다.
상기와 같은 화학적 방법은， 나노 입자 크기의 제어 및 나노 입자의 분리가 용이하지 않고， 산화 환원제의 종류， 분산제， PH, 온도 등에 따라 나노 입자의 특성이 달라지므로， 나노 입자의 제조에 있어서 재연성 측면에서 많은 문제점을 가지고 있다.
또한， 상기와 같은 화학적 방법은， 금속을 산이나 염기에 먼저 녹여 이온 형태로 산화시키고 이를 다시 환원제를 사용하여 금속원소로 환원시키는 과정에서 많은 산화환원시약을 사용해야 하므로 사용한 시약 폐기물의 처리를 위한 추가적 비용이 많이 발생한다.
또한， 상기와 같은 화학적 방법^로 나노 입자를 제조할 경우， 산업에 이용하기 위해서는 흔합제， 안정화제， 유기용매， 상용화제 등 다른 화학약품의 처리가 필요한 데， 그 결과 다른 화학약품들과의 예기치 않은 반웅이 진행되어， 최종 제품의 변색이 일어나 상품성이 떨어지고， 초기의 분산제가 최종 제품의 화학물질들간의 연계성이 떨어져서 분산제가 해리되며， 나노 입자들 간에도 서로 뭉쳐져 크기가 커지게 되어 나노 입자의 효과를 얻을 수 없는 문제점이 발생하기 때문에， 나노 입자의 산업에의 웅용이 제한되고 있다.
상기 화학적 방법과는 달리, 물리적으로 금속원자 증기 (vapor)의 웅축을 이용하여 나노 입자를 만드는 방법이 있는데, 이는 금속이나 금속화합물을 고온에서 기체로 만들고 이를 낮은 온도로 팽창시키면서 금속원자 증기를 급속하게 웅축시켜 나노 입자를 형성하는 것이다. 상기 방법은 금속이나 금속화합물에 고온을 가하여 증기를 만들거나， 디시 스퍼터링 (DC sputtering), 디시-알에프 스퍼터링 (DC-RF sputter), ECR, 레이저 빔 스퍼터링 (laser beam sputter)을 이용하여 전자나 에너지를 가진 입자를 고체에 조사함으로써 발생하는 원자증기를 낮은 온도의 기체에 분사하거나 낮은 온도의 영역을 통과하게 하여 상기 원자증기들이 급속히 웅축되어 나노 크기의 입자를 형성하게 하는 것이다.
상기 물리적인 방법들은 금속 그 자체를 증기로 만들어 이를 다시 금속 나노 입자로 만들기 때문에 화학적 방법과는 달리 막대한 양의 시약 사용 문제 및 이로 인한 폐수처리문제가 발생하지 않아 공정이 단순한 장점이 있다.
또 다른 물리적 방법으로는 기계적인 힘을 재료에 가하여 재료를 미세한 입자로 분쇄하는 기계적 분쇄 방식이 있는데， 재료를 10 nm 사이즈의 나노 입자로 가공하기 위해선 장시간의 분쇄공정이 필요하다.
상기 물리적 방법들은 분말 중 80 ~ 90%의 입자가 나노 입자보다 상당히 큰 마이크로미터 크기로 형성되며, 이러한 진공 설비를 이용한 물리적 방법으로 나노 입자를 만들 경우, 입자의 크기가 불균일하고 생산성이 낮아 경제성이 떨어지는 문제점이 있다.
따라서， 최근에는 진공상태에서 물리적인 방법으로 금속 또는 금속산화물을 증기화하고， 교반되는 담체 위에 금속■ 또는 산화물 증기를 증착시켜 나노 입자를 형성하는 방법이 시도되고 있다.
【발명의 상세한 설명】
【기술적 과제】
상기 종래 기술의 문제점을 해결하기 위하여， 본 발명은 물리적 기상증착법 (physical vapor deposition)을 이용하여 나노 입자 증기를 발생시키고， 담체 상에 나노 입자를 증착하는 것을 특징으로 하는 나노 파우더 제조 방법을 제공하는 것을 목적으로 한다.
또한, 본 발명은 나노 입자의 성장을 제어하여 나노 입자의 크기와 함량을 효과적으로 제어할 수 있는 나노 파우더 제조 방법을 제공하는 것을 목적으로 한다.
【기술적 해결방법】 상기 목적을 달성하기 위하여 , 본 발명은， 진공 증착조， 상기 진공 증착조 내에 구비 된 교반조; 상기 교반조 내에 구비되고 담체를 교반하는 스크류; 및 상기 진공 증착조 내에 교반조 상부에 구비 되고 나노입자 형성을 위한 증기 입자를 발생시 키는 증착원으로 구성되는， 담체에 부착된 나노 파우더 제조 장치를 사용하고，
a) 상기 진공 증착조의 진공도가 10—4 내지 1 torr 가 되도록 불활성 기체를 진공 증착조에 포함시 키는 단계 ; b) 상기 증착원을 이용하여 나노입자 형성을 위 한 증기 입자를 발생시키는 단계 ; c) 상기 스크류의 속도를 1 내지 200rpm 으로 조절하여 담체를 교반하는 단계 ; 및 d) 상기 담체 상에 증기 입자를 증착하여 나노입자를 형성하는 단계를 포함하는 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법을 제공한다.
【유리 한 효과】
본 발명에 따르면， 담체에 균일하게 나노 입자를 형성시 킬 수 있어 균일한 크기 의， 담체에 부착된 나노 파우더를 제조할 수 있다.
【도면의 간단한 설명】
도 1 은 본 발명 의 나노 파우더 제조 방법에서 나노 입자 증기의 이동은 평균자유경로를 이용함을 나타낸 모식도이다.
도 2 는 소금 담체 상에 약 40ppm 농도의 은 나노 파우더를 형성하기 전 (좌측)과 후 (우측)의 사진이다.
도 3a 는 히드록실 에 틸 셀를로오스 (hydroxyl ethyl cellulose, HEC) 담체 상에 은 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다.
도 3b 는 은 나노 입자가 부착된 HEC 담체를 물에 용해시켜 수득한 은 나노 입자가 균일하게 분산된 용액의 사진이다.
도 4 는 모래 담체 상에 은 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다.
도 5 는 소금 담체 상에 Si 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다.
도 6 은 설탕 담체 상에 금 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 도 7은 도 6에서 만든 금 나노 입자 /설탕을 물에 녹인 것이다. 금 나노 입자가 완전히 분산되어 콜로이드를 형성한 것을 볼 수 있다.
도 8 은 설탕 담체 상에 백금 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 사진에서 보듯이 나노 입자 형성 후 백금 나노 입자의 고유색인 회색을 띄고 있는 것을 볼 수 있다.
도 9 은 포도당 담체 상에 Pd 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 형성 후 엷은 회색을 띄는데 Pd 가 나노 입자가 될 경우 입자 회색을 띄기 때문이다.
도 10 는 도 8 에서 Pd/포도당을 물에 녹였을 때의 사진이다. 전체적으로 회색의 콜로이드 (colloid)를 형성한 것을 볼 수 있다.
도 11 은 PET 폴라스틱 알갱이들 위에 은 나노 입자를 형성한 것 (좌측)과， 이를 섭씨 180 도에서 녹인 것 (우측)의 사진이다. 사진에서 보듯이 PET 플라스틱 고분자에 은 나노 입자들이 완전히 녹아 전체적으로 노란색을 띄는 것을 볼 수 있다.
도 12은 PTFE (테프론) 분말에 은 나노 입자를 형성한 것 (좌측)과, 이를
250 °C 고온에서 녹인 것 (우측)의 사진이다.
【발명의 실시를 위한 형태】
이하에서， 본 발명을 더욱 상세히 설명하도록 한다.
본 발명은， 진공 증착조， 상기 진공 증착조 내에 구비된 교반조; 상기 교반조 내에 구비되고 담체를 교반하는 스크류; 및 상기 진공 증착조 내에 교반조 상부에 구비되고 나노입자 형성을 위한 증기 입자를 발생시키는 증착원으로 구성되는， 담체에 부착된 나노 파우더 제조 장치를 사용하고，
a) 상기 진공 증착조의 진공도가 10—4 내지 1 torr 가 되도톡 불활성 기체를 진공 증착조에 포함시키는 단계; b) 상기 증착원을 이용하여 나노입자 형성을 위한 증기 입자를 발생시키는 단계; c) 상기 스크류의 속도를 1 내지 200rpm 으로 조절하여 담체를 교반하는 단계; 및 d) 상기 담체 상에 증기 입자를 증착하여 나노 입자를 형성하는 단계를 포함하는 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법을 제공한다. 본 발명의 나노 파우더 제조 방법은, 진공 증착조， 상기 진공 증착조 내에 구비된 교반조; 상기 교반조 내에 구비되고 담체를 교반하는 스크류; 및 상기 진공 증착조 내에 교반조 상부에 구비되고 나노입자 형성을 위한 증기 입자를 발생시키는 증착원으로 구성되는， 담체에 부착된 파우더 제조 장치를 사용하는 것을 특징으로 한다.
본 발명에 따른 나노 파우더 제조 방법은， 상기 진공 증착조의 진공도를 10"4 내지 1 torr 로 조절하는 것을 특징으로 한다. 상기 진공도가 1요4 torr 이하의 저진공에선 나노입자 형성을 위한 증기 입자가 발생되는 증착원으로부터 가까운 담체쪽에는 나노입자 형성을 위한 증기 입자가 두¾게 증착되지만， 담체들이 증착원에서 멀어질수록 증기 입자들의 평균 자유 행적의 거리가 짧아져서 증기 입자는 담체에 증착되지 않게 된다.
본 발명에서는 원자화된 증기의 비산 방향이 담체 반대 방향이어서 금속 증기는 상방으로 비산하지만 진공도가 10_4 내지 1 torr 이기 때문에 내부에 채워진 불활성 가스로 인한 금속 증기 입자와 불활성 가스 입자간의 층돌이 일어나 평균자유경로가 짧아져서 금속 증기 입자가 중력에 의해 하향방향으로 이동하여 교반되는 담체 상에 증착됨으로써 나노 입자를 형성한다.
상기 진공 증착조의 진공도는 불활성 가스를 포함시켜 조절하며, 상기 불활성 가스는 아르곤 (Ar), 네은 (Ne), N2, 02， CH4 등일 수 있으나, 반드시 이에 제한되지는 않는다.
본 발명에 따른 나노 파우더 제조 방법에서, 상기 증착원을 이용하여 나노입자 형성을 위한 증기입자를 발생시키는 단계는， 물리적 기상증착법을 사용할 수 있으며， 그 예로 저항 가열법, 플라즈마 가열법， 유도가열법， 레이저 가열법 등의 열 증착， 디시 스퍼터링 (DC Sputtering), 디시 알에프 스퍼터링 (DO RF Sputtering), 레이저 스퍼터링, 전자 빔 증착 (E-Beam Evaproation) 등을 들 수 있으나， 반드시 이에 제한되는 것은 아니다.
상기 나노 입자의 원재료로는 금속， 금속화합물， 유기물 등을 사용할 수 있으나， 반드시 이에 제한되지는 않는다.
상기 금속으로는 코발트， 구리， 은， 니켈， 망간， 팔라듐, 인듐， 철， 텅스텐， 티타늄， 이들의 합금을 사용할 수 있으나， 반드시 이에 제한되지는 않는다. 상기 금속화합물은 금속 산화물, 금속 질화물， 금속 탄화물, 금속 탄 질화물일 수 있으나， 반드시 이에 제한되지는 않는다.
상기 금속화합물의 예로, 금속 산화물인 알루미나 (A1203), 금속 탄화물인 텅스텐 카바이드 (WC), 금속 질화물인 질소 알루미늄 (A1N), 금속 탄 질화물인 탄질화 티타늄 (TiCN)을 들 수 있으나, 반드시 이에 제한되지는 않는다.
본 발명의 바람직 한 실시 예에 따르면， 상기 담체로는 활성탄, 탄화수소 화합물， 알루미나 (A1203), 텅스텐 카바이드 (WC), 유리 , 모래， 또는 물이나 용매에 녹는 물질， 예컨대 포도당， 설탕, 소금， PMMA, 히드록실 에 틸 셀를로오스 (hydroxyl ethyl cellulose, HEC), PET, PTFE 등을 사용할 수 있다.
또한， 본 발명에 따른 나노 파우더 제조 방법은， 상기 스크류의 속도를
1 내지 200 rpm 으로 조절하는 것을 특징으로 한다.
상기 교반속도가 1 rpm 미만일 경우에는 교반이 충분히 이루어지지 않아 증기 입자가 담체 표면에 균일하게 부착되지 못하는 문제점 이 있으며， 교반 속도가 200 rpm 을 초과할 경우에는 교반되는 담체가 비산되는 문제점 이 있다.
본 발명에 따른 나노 파우더 제조 방법은, 증착조의 진공도 스크류의 속도 등을 조절함으로써 나노 입자의 성 장을 제어하여 나노 파우더의 크기와 함량을 효과적으로 제어할 수 있다.
본 발명에 따른 나노 파우더 제조 방법은， 상기 담체 상에 증기 입자를 증착하여 나노 입자를 형성하는 단계를 포함하는 것을 특징으로 한다.
상기 담체 상에 증기 입자를 증착하여 나노 입자를 형성하는 단계에서는, 나노입자 형성을 위 한 증기 입자가 담체 상에 증착되어 나노 입자를 형성하기 위한 핵을 형성하며， 이후 상기 핵이 증기 입자의 추가적 인 증착에 의해 나노 입자를 형성 한 후에 담체가 교반， 회 전되 어 흔합되며 , 증기 입자가 증착되지 않은 새로운 담체 상, 또는 증기 입자가 증착되지 않은 담체 부위에 증기 입자가 증착됨으로써 , 균일한 크기 의 나노 입자를 형성할 수 있다.
바람직하게는， 상기 나노입자 형성을 위 한 증기 입자는 담체 상에 분당 단위면적 당 1 A 내지 10 두께로 증착된다.
본 발명에 따라 제조된 담체에 부착된 나노 파우더 에 대해， 추가적 인 반웅을 진행하여 최종 웅용 물질을 합성할 수 있다. 즉， 담체와, 증착되는 증기 입자는 반웅하여 산화물 (oxide), 질화물 (nitride), 탄화물 (carbide) 또는 질탄화물 (carbonitride) 나노 파우더를 형성할 수 있다.
예를 들어, 기존에 고온 /고압에서 합성되던 질소 알루미늄 (A1N), 알루미나 (A1203), 메탈 카바이드 (Metal carbide), 메탈 나이트라이드 (Metal nitride) 등을 본 발명의 제조방법에 따라 저온에서 합성 및 코팅할 수 있다.
또한， 본 발명에 따르면, 담체로 웅용제품의 한 종류 이상의 화합물 또는 최종 웅용 제품의 한 성분을 사용하고 이러한 담체 상에 형성된 나노 입자를 포함한 응용 제품들을 제조할 수 있다.
예를 들어， 활성탄 담체 상에 텅스텐 나노 입자를 형성하거나， 텅스텐 분말 상에 코발트 (Co)를 나노 입자로 형성한 후 불활성 가스 분위기에서 탄화처리하여 텅스텐 카바이드 (WC) 또는 코발트 (Co)가 도핑된 나노 텅스텐 카바이드를 합성할 수 있다. 이와 같이 담체로 기능성 재료를 사용하고 담체 상에 나노 입자를 형성한 후， 후속 처리를 통해 웅용 제품을 제조할 수 있다.
또한, 본 발명에 따르면， 담체로 물， 극성 유기용매， 비극성 유기용메에 잘 녹는 물질을 사용하고 이러한 담체 상에 나노 입자를 형성한 후 담체를 용해시켜 제거한 후， 금속 또는 금속화합물의 나노 파우더만 회수할 수도 있다.
이하 첨부된 도면을 참조하여 본 발명의 실시예를 통해 본 발명을 설명하도록 한다. 이들 실시예는 단지 예시적인 것일 뿐， 본 발명의 기술적 범위를 한정하는 것은 아니다.
<실시예 >
〈실시예 1〉 소금-은 나노 파우더의 제조
진공조에 아르곤 (Ar)을 주입하여 진공도를 10-3torr 로 조절한 후, 은을 증착원으로 하여 직류 스퍼터 (DC Sputter)로 은 증기를 발생시켰다. 이 때， 상기 은 증기가 비산되는 방향은 담체인 소금이 담겨있는 교반조의 반대 방향， 즉 상향 방향이 되도톡 장치하였다.
상기 소금은 교반조에 구비된 회전 스크류에 의하여 교반되며， 이 때 스크류에 의한 소금의 교반속도는 lOOrpm이하가 유지되도록 하였다. 상기 은 증기를 소금 담체에 증착시켜 약 40ppm 의 농도로 은 나노 입자가 소금에 붙은， 소금-은 나노 파우더를 제조하였다.
〈실시예 2> HEC-은 나노 파우더의 제조
상기 실시예 1 에서， 담체로 히드록실 에틸 셀롤로오스 (hydroxyl ethyl cellulose(HEC))을 사용하고 은을 증착원으로 사용하는 것을 제외하고는 실시예 1과 동일한 방법으로 실시하여， HEC-은 나노 파우더를 제조하였다.
〈실시예 3> 물-은 나노 파우더의 제조
상기 실시예 1 에서， 담체로 물을 사용하고 은을 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여， 물-은 나노 파우더를 제조하였다.
<실시예 4〉 모래-은 나노 파우더의 제조
상기 실시예 1 에서， 담체로 모래를 사용하고 은을 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여, 모래ᅳ은 나노 파우더를 제조하였다.
〈실시예 5> 소금 -Si 나노 파우더의 제조
상기 실시예 1에서， 담체로 소금을 사용하고 Si를 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여， 소금 -Si 나노 파우더를 제조하였다.
<실시예 6〉 설탕ᅳ금 나노 파우더의 제조
상기 실시예 1 에서， 담체로 설탕을 사용하고 금을 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여， 설탕-금 나노 파우더를 제조하였다.
〈실시예 7> 설탕 -백금 나노 파우더의 제조
상기 실시예 1 에서， 담체로 설탕을 사용하고 백금을 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여， 설탕 -백금 나노 파우더를 제조하였다.
〈실시예 8> 포도당 -Pd 나노 파우더의 제조 상기 실시예 1 에서， 담체로 포도당을 사용하고 Pd 를 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여， 포도당 -Pd 나노 파우더를 제조하였다.
〈실시예 9>PET-은 나노 파우더의 제조
상기 실시예 1에서, 담체로 PET를 사용하고 은을 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여, PET-은 나노 파우더를 제조하였다.
〈실시예 10>PTFE-은 나노 파우더의 제조
상기 실시예 1 에서， 담체로 PTFE (테프론)를 사용하고 은을 증착원으로 사용하는 것을 제외하고는 실시예 1 과 동일한 방법으로 실시하여， PTFE-은 나노 파우더를 제조하였다. 상기 실시예 1 내지 10에서 담체의 외관 변화를 육안으로 관찰하였다. 도 2 는 소금 담체 상에 약 40ppm 농도의 은 나노 파우더를 만들기 전과 후의 사진이다. 사진에서 보듯이 초기 소금의 색은 흰색이었지만 엷은 노란색으로 변화하여 은 나노 입자가 형성된 것을 확인할 수 있다.
도 3a 는 히드록실 에틸 셀를로오스 (hydroxyl ethyl cellulose, HEC) 담체 상에 은나노 입자를 형성하기 전 후의 사진이다. 도 3b 에서 보듯이 은 나노 입자가 부착된 HEC담체에 물을 첨가하여 은 나노 입자가 완전하게 분산된 용액을 얻을 수 있다.
도 4 는 모래에 은 나노 입자를 형성 하기 전 후의 사진이다. 사진에서 보듯이 모래는 은 나노 입자를 형성하기 전 밝은 색을 띄다가 은 나노 입자를 형성한 후 옅은 진한 색으로 변한 것을 확인할 수 있다.
도 5 는 소금 담체 상에 Si 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 사진에서 보듯이 소금 담체는 나노 입자 형성 전 백색을 띄고 있었지만 소금 담체 상에 Si 나노 입자가 형성된 후 엷은 연두색을 띄는 것을 볼 수 있다. 도 6 은 설탕 담체 상에 금 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 사진에서 보듯이 설탕 담체는 금 나노 입자가 형성된 후 금 나노 입자의 고유색인 진한 보라색을 띄고 있는 것을 볼 수 있다.
도 7 은 도 6 에서 만든 금나노 입자 /설탕을 물에 녹인 것이다. 금 나노 입자가 완전히 분산되어 콜로이드를 형성한 것을 볼 수 있다.
도 8 은 설탕 담체 상에 백금 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 사진에서 보듯이 설탕 담체는 백금 나노 입자 형성 후 백금 나노 입자의 고유색인 회색을 띄고 있는 것을 볼 수 있다.
도 9 은 포도당 담체 상에 Pd 나노 입자를 형성하기 전 (좌측)과 후 (우측)의 사진이다. 사진에서 보듯이 포도당 담체 상에 Pd 나노 입자가 형성된 후 포도당은 ^은 회색을 띄는데 이는 , Pd 가 나노 입자가 될 경우 회색을 띄기 때문이다.
도 10 는 도 8 에서 Pd/포도당을 물에 녹였을 때의 사진이다. 전체적으로 회색의 콜로이드 (colloid)를 형성한 것을 볼 수 있다.
도 11 은 PET 플라스틱 알갱이들 위에 은 나노 입자를 형성한 것 (좌측)과， 이를 섭씨 180 도에서 녹인 것 (우측)의 사진이다. 사진에서 보듯이
PET 플라스틱 고분자에 은 나노 입자들이 완전히 녹아 전체적으로 노란색을 띄는 것을 볼 수 있다.
도 12은 PTFE (테프론) 분말에 은 나노 입자를 형성한 것 (좌측)과， 이를 섭씨 250 도 고온에서 녹인 것 (우측)의 사진이다. 사진에서 보듯이 전체적으로 노란색을 띄어 은 나노 입자들이 균일하게 테프론 고분자와 섞여 있는 것을 볼 수 있다.

Claims

【특허청구범위】
【청구항 1】
진공 증착조， 상기 진공 증착조 내에 구비된 교반조; 상기 교반조 내에 구비되고 담체를 교반하는 스크류; 및 상기 진공 증착조 내에 교반조 상부에 구비되고 나노입자 형성을 위한 증기 입자를 발생시키는 증착원으로 구성되는， 담체에 부착된 나노 파우더 제조 장치를 사용하고
a) 상기 진공 증착조의 진공도가 1(Γ4 내지 1 torr 가 되도록 불활성 기체를 진공 증착조에 포함시키는 단계;
b) 상기 증착원을 이용하여 나노입자 형성을 위한 증기 입자를 발생시키는 단계;
c) 상기 스크류의 속도를 1 내지 200rpm 으로 조절하여 담체를 교반하는 단계; 및
d) 상기 담체 상에 증기 입자를 증착하여 나노 입자를 형성하는 단계를 포함하는 것을 특징으로 하는 담체에 부착된 나노 파우더 제조 방법.
【청구항 2】
청구항 1 에 있어서， 상기 증착원을 이용하여 나노입자 형성을 위한 증기 입자를 발생시키는 단계는， 저항 가열법， 플라즈마 가열법, 유도가열법， 레이저 가열법， 디시 스퍼터링， 디시 알에프 스퍼터링， 레이저 스퍼터링, 또는 전자 빔 증착을 사용하는 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법.
【청구항 3】
청구항 1 에 있어서， 상기 나노 입자의 원재료는 금속， 금속화합물 또는 유기물인 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법.
【청구항 4】
청구항 3 에 있어서， 상기 금속은 코발트， 구리， 은， 니켈， 망간， 팔라듐， 인듐, 철， 텅스텐， 티타늄 및 이들의 합금으로 이루어진 군으로부터 선택되는 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법.
【청구항 5】 청구항 3 에 있어서， 상기 금속화합물은 금속 산화물， 금속 질화물， 금속 탄화물 또는 금속 탄 질화물인 것을 특징으로 하는, 담체에 부착된 나노 파우더 제조 방법 .
【청구항 6】
청구항 5 에 있어서 , 상기 금속화합물은 알루미나 (A1203), 텅스텐 카바이드 (WC), 질소 알루미늄 (A1N) 또는 탄질화 티 타늄 (TiCN)인 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법 .
【청구항 7】
청구항 1 에 있어서 , 상기 담체는 최종 웅용 제품의 한 종류 이상의 화합물 또는 최종 웅용 제품의 하나 이상의 성분인 것을 특징으로 하는, 담체에 부착된 나노 파우더 제조 방법 .
【청구항 8】
청구항 1 에 있어서， 상기 담체는 물， 극성 유기용매 , 비극성 유기용매에 잘 녹는 물질인 것을 특징으로 하는, 담체에 부착된 나노 파우더 제조 방법 .
【청구항 9】
청구항 1 에 있어서， 상기 담체는 활성 탄， 탄화수소 화합물, 알루미나 (A1203), 텅스텐 카바이드 (WC), 유리， 모래 , 포도당， 설탕， 소금， PMMA 및 히드록실 에 틸 셀를로오스로 이루어진 군으로부터 선택된 하나인 것을 특징으로 하는, 담체에 부착된 나노 파우더 제조 방법 .
【청구항 10】
청구항 1 에 있어서， 상기 나노 입자 증기를 담체 상에 분당 단위 면적 당 1 A 내지 10 두께로 증착하는 것을 특징으로 하는， 담체에 부착된 나노 파우더 제조 방법 .
【청구항 11】
청구항 1 에 있어서， 상기 담체와， 증착되는 나노 입자 증기 가 반웅하여 산화물 (oxide), 질화물 (nitride), 탄화물 (carbide) 또는 질탄화물 (carbonitride) 나노 파우더를 형성하는 것을 특징으로 하는, 담체에 부착된 나노 파우더 제조 방법 .
PCT/KR2012/003422 2011-05-02 2012-05-02 담체를 이용한 나노 파우더 제조 방법 WO2012150804A2 (ko)