WO2012143345A1 - Film material for producing flexible packaging for alkali-containing products and packaging which is alakli-resistant and which is produced from said film material - Google Patents

Film material for producing flexible packaging for alkali-containing products and packaging which is alakli-resistant and which is produced from said film material Download PDF

Info

Publication number
WO2012143345A1
WO2012143345A1 PCT/EP2012/056984 EP2012056984W WO2012143345A1 WO 2012143345 A1 WO2012143345 A1 WO 2012143345A1 EP 2012056984 W EP2012056984 W EP 2012056984W WO 2012143345 A1 WO2012143345 A1 WO 2012143345A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
film material
packaging
product
alkali
Prior art date
Application number
PCT/EP2012/056984
Other languages
German (de)
French (fr)
Inventor
Eddy Daelmans
Arnold Schneider
Original Assignee
Huhtamaki Ronsberg, Zweigniederlassung Der Huhtamaki Deutschland Gmbh & Co. Kg
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huhtamaki Ronsberg, Zweigniederlassung Der Huhtamaki Deutschland Gmbh & Co. Kg filed Critical Huhtamaki Ronsberg, Zweigniederlassung Der Huhtamaki Deutschland Gmbh & Co. Kg
Publication of WO2012143345A1 publication Critical patent/WO2012143345A1/en

Abstract

The invention relates to film material (100) for producing flexible packaging for alkali-containing products, comprising a product side (110) which, when the product is finished, is adjacent to the alkali-containing product, and a film material outer side (120), the side (110) of the film material (100) being a cold adhesive layer (10) to which, in the direction of the film material outer side (120), a colour layer (20) is adjacent. The invention also relates to alkali-resistant packaging produced from said type of film material.

Description

"Foiienmateriai zur Herstellung einer flexiblen Verpackung für alkalihaltige Produkte sowie daraus hergestellte alkaiiresistente Verpackung"  "Foieumen for the production of a flexible package for alkaline products and its resistant to alkali-resistant packaging"
B e s c h r e i u n g S e c tio ns
Die Erfindung betrifft ein Foiienmateriai zur Herstellung einer flexiblen Verpackung für aikaiihaltige Produkte sowie eine aus einem solchen Folienmaterial hergestellte alkaiiresistente Verpackung gemäß den Oberbegriffen der Patentansprüche 1 und 7. Folienmaterialien und Laminate zur Herstellung flexibler Verpackungen sind seit langem bekannt und werden üblicherweise zur Herstellung von Verpackungen für Produkte aus nahezu allen Lebensbereichen verwendet. Bisherige Folienmaterialien eignen sich zu diesem Zweck in aller Regel gut, zumindest solange das zu verpackende Gut nicht in irgend einer Weise aggressive Eigenschaften aufweist, die geeignet sind, das bei der Herstellung der Verpackung verwendete Folienmaterial als Ganzes, oder bestimmte Bestandteile des Folienmaterials, d.h. beispielsweise bestimmte Schichten des Folienmaterials, anzugreifen und unter Umständen strukturell zu zerstören, so dass das Folienmaterial sowie die Verpackung unbrauchbar wird und im schlimmsten Fall das verpackte Gut frei gibt. The invention relates to a Foiienmateriai for producing a flexible packaging for aikaiihaltige products and an alkaiiresistente packaging prepared from such a sheet material according to the preambles of claims 1 and 7. Film materials and laminates for the production of flexible packaging have long been known and are commonly used for the production of packaging for Products from almost all walks of life used. Previous film materials are generally well-suited for this purpose, at least as long as the product to be packaged does not in some way have aggressive properties suitable for use as a whole the film material used in the manufacture of the package, or certain components of the film material, i. For example, certain layers of the film material to attack and possibly structurally destroy, so that the film material and the packaging is useless and in the worst case, the packaged Good releases.
Eine besondere Problematik stellen in diesem Zusammenhang zu verpackende Produkte, Füllstoffe oder sonstige Güter dar, die alkalische Eigenschaften aufweisen, da Farbstoffe, die zum Beschriften oder Färben, kurz zur Designgebung an dem Folienmaterial verwendet werden, in aller Regel nicht aikaliresistent sind, mit der Folge, dass zumindest die farbliche Gestaltung der Verpackung aufgrund der Zerstörung der Farbe durch das verpackte alkalihaltige Produkt in dem Folienmaterial leidet oder vollständig zerstört, zumindest jedoch unansehnlich, wird. A particular problem in this context is to be packaged products, fillers or other goods that have alkaline properties, since dyes that are used for labeling or dyeing, short for the design of the film material, are not usually aikaliresistent, with the result that at least the color design of the packaging due to the destruction of the Color by the packaged alkaline product in the film material suffers or completely destroyed, but at least unsightly, is.
Um diese Problematik zu lösen, die beispielsweise beim Verpacken von Spüimaschi- nen-Reinigungstabletten, kurz als Tabs bezeichnet, auftritt, wurden in der Vergangenheit äußerst kompliziert und aufwendig aufgebaute und deshalb teure Folienmaterialien verwendet, wie sie beispielsweise in Flg. 1 als Stand der Technik dargestellt sind. So wurde gemäß dem bisherigen herkömmlichen Stand der Technik eine Einwirkung von alkalihaltigen Produkten auf eine in einem Folienmaterial vorhandene Farbe dadurch verhindert, dass die Farbe zuäußerst auf dem Folienmaterial aufgebracht wurde, so dass das alkalihaltige Produkt maximal weit von der Farbschicht des In order to solve this problem, which occurs, for example, in the packaging of dishwasher cleaning tablets, referred to for short as tabs, in the past extremely complicated and elaborately constructed and therefore expensive film materials were used, as described, for example, in Flg. 1 are shown as prior art. Thus, according to the prior art, exposure of alkaline-containing products to a color present in a film material has been prevented by applying the ink to the film material to a maximum extent so that the alkaline product is maximally far from the color layer of the film
Folienmaterials angeordnet ist und die Farbschicht durch zumindest vier Schichten von dem alkalihaltigen Produkt getrennt ist. So ist benachbart zu dem alkalihaltigen Produkt gemäß dem Stand der Technik zunächst eine Kaltkleberschicht 10 vorgese- hen, an welche benachbart eine Siegelschicht 50 angeordnet ist, worauf eine Schicht aus einem Kunststoffmaterial, in aller Regel orientiertem Polypropylen 30 folgt, das wiederum von einer Siegelschicht 50 überdeckt ist, an welche sich erst dann die Farbstoffschicht 20 anschließt. Ein wichtiger, aufwendiger und deshalb teurer Schritt bei der Herstellung eines solchen Folienmaterials besteht darin, dass für die Schichten- folge Siegelschicht 50, Kunststoffschicht 30 und nochmals Siegeischicht 50 als eine koextrudierte Schicht aus orientiertem Polypropylen 70 verwendet werden muss, um dem Folienmaterial eine genügende Stabilität zu verleihen, damit daraus eine flexible Verpackung für alkalihaltige Produkte hergestellt werden kann. Ein weiterer Nachteil dieses aufwendigen bisherigen Folienmaterials bzw. Laminats besteht darüber hinaus darin, dass derartige Laminate üblicherweise nach einer Herstellung der Laminate, jedoch vor einer Herstellung der Verpackung, auf Rollen gewickelt werden, um transportiert werden zu können. Da sich jedoch bei einem auf die Rollen Wickeln immer eine Laminatunterseite über eine Laminatoberseite legt, besteht bei dem Laminataufbau gemäß dem Stand der Technik die Gefahr, dass die Klebstoffschicht 10 beim Wickeln die Farbstoffschicht 20 überdeckt und mit dieser verklebt, so dass bei einem späteren Abwickeln des Laminats die Farbstoffschicht 20 an der Klebstoffschicht 10 haften bleibt und das Laminat somit unbrauchbar wird. Aus diesem Grund Ist bei dem bisherigen Laminat gemäß dem Stand der Technik eine zusätzliche Reieaseschicht 60 notwendig, die über der Farbstoffschicht, d.h. außenseitig der späteren herzustellen- den Verpackung angeordnet ist. Diese Releaseschicht ist so ausgebildet, dass sie einem Verkleben des Laminats auf der Rolle entgegenwirkt, da die Releaseschicht 60 mit der Klebstoffschicht 10 keine Klebeverbindung eingeht und darüber hinaus die Farbstoffschicht 20 durch die darüber gelagerte Releaseschicht 60 geschützt ist. Foil material is arranged and the color layer is separated by at least four layers of the alkaline product. Thus, next to the alkaline product according to the prior art, a cold adhesive layer 10 is initially provided, to which a sealing layer 50 is adjacently disposed, followed by a layer of a plastic material, usually oriented polypropylene 30, which in turn results from a sealing layer 50 is covered, to which only then the dye layer 20 connects. An important, expensive and therefore expensive step in the production of such a film material is that, for the layer sequence, sealing layer 50, plastic layer 30 and yet again layer 50 must be used as a coextruded layer of oriented polypropylene 70 in order to provide sufficient stability to the film material to provide a flexible packaging for alkaline products. Another disadvantage of this complex previous film material or laminate is moreover that such laminates are usually wound after production of the laminates, but before production of the packaging, on rolls in order to be transported. However, since a laminate underside always overlies a laminate top when winding on the rolls, in the prior art laminate construction there is a risk that the adhesive layer 10 will, during winding, cover and bond to the dye layer 20 such that upon subsequent unwinding the laminate, the dye layer 20 adheres to the adhesive layer 10 and the laminate is thus unusable. For this reason, in the case of the previous laminate according to the prior art, an additional re-release layer 60 is necessary, which is arranged above the dye layer, ie outside the later-produced packaging. This release layer is designed in such a way that it counteracts adhesion of the laminate to the roll, since the release layer 60 does not adhere to the adhesive layer 10, and beyond that the adhesive layer Dye layer 20 is protected by the overlying release layer 60.
Somit wird der ohnehin bereits aufwendige Aufbau herkömmlicher Laminate zum Herstellen von Verpackungen für alkalihaltige Produkte zusätzlich noch durch die Notwendigkeit der Aufbringung einer Releaseschicht, beispielsweise eines Release- lacks 60 verteuert, der zum Schutz vor Verblocken einerseits sowie zum Schutz der Farbstoffschicht andererseits notwendig ist. Darüber hinaus weist die Releaseschicht selbst jedoch ebenfalls Nachteile auf. So enthält ein Releaselack beispielsweise Wachse, durch welche die hinter der Releaseschicht liegende Farbstoffschicht 20 ihren Glanz verliert, so dass das Gesamterscheinungsbild eines solchen Laminats beein- trächtigt ist. Thus, the already complex structure of conventional laminates for producing packages for alkaline products is additionally made more expensive by the necessity of applying a release layer, for example a release varnish 60, which is necessary for protection against blocking on the one hand and for protecting the dye layer on the other hand. In addition, however, the release layer itself also has disadvantages. For example, a release lacquer contains waxes, through which the dye layer 20 behind the release layer loses its luster, so that the overall appearance of such a laminate is impaired.
Der Erfindung liegt die Aufgabe zugrunde, ein Folienmaterial sowie eine aus einem solchen Foiienmaterial hergestellte Verpackung zur Verfügung zu stellen, die zum einen kostengünstig und materialsparend herzustellen ist, oben genannte Nachteile vermeidet und darüber hinaus geeignet ist, Verpackungen herzustellen, die eine hochglänzende Farbgestaitung aufweisen. The invention has for its object to provide a film material and a package produced from such Foiienmaterial available, which is to produce a cost and material saving, avoids the above disadvantages and is also suitable to produce packages that have a high gloss Farbgestaitung.
Diese Aufgabe wird durch ein Folienmaterial bzw. Laminat gemäß Patentanspruch 1 sowie durch eine alkaliresistente Verpackung gemäß Patentanspruch 7 gelöst. This object is achieved by a film material or laminate according to claim 1 and by an alkali-resistant packaging according to claim 7.
Insbesondere wird die Aufgabe durch ein Foiienmaterial zur Herstellung einer flexiblen Verpackung für alkalihaltige Produkte gelöst, wobei das Folienmaterial eine Produktseite aufweist, an welche im Falle der fertigen Verpackung das aikalihaltige Produkt angrenzt, und ferner eine Folienmaterial-Außenseite aufweist, wobei die Produktseite des Folienmaterials eine Kaltkleberschicht ist, an welche in Richtung der Folienmaterial-Außenseite eine Farbstoffschicht angrenzt. In particular, the object is achieved by a foaming material for producing a flexible package for alkaline products, wherein the foil material has a product side to which the aikalihaltige product in the case of the finished packaging adjacent, and further comprising a foil material outside, wherein the product side of the foil material a Cold adhesive layer is, which is adjacent to a direction of the film material outside a dye layer.
Ein wesentlicher Punkt der Erfindung liegt darin, dass seitens der Erfinder erkannt wurde, dass der Kaltkleber, der sich zwischen dem alkalihaltigen Produkt einerseits und der Farbstoffschicht andererseits befindet, selbst geeignet ist, eine Schutzschicht für die Farbe darzustellen, so dass alkalihaltige Bestandteile des verpackten Guts nicht bis zu der Farbstoffschicht vordringen können und die Farbstoffschicht ihrerseits vor diesen alkalischen Bestandteilen geschützt ist. Darüber hinaus schirmt die Klebstoffschicht auch das alkalihaltige verpackte Produkt ab und schützt dieses vor einem Farbübertrag von der Farbstoffschicht auf das Produkt. Darüber hinaus bietet dieAn essential point of the invention is that it has been recognized by the inventors that the cold glue, which is located between the alkaline product on the one hand and the dye layer on the other hand, is itself suitable to represent a protective layer for the color, so that alkaline components of the packaged Guts can not penetrate to the dye layer and the dye layer is in turn protected from these alkaline components. In addition, the adhesive layer also shields the alkaline-containing packaged product and protects it from color transfer from the dye layer to the product. In addition, the
Kaitkleberschtcht, zusätzlich zu den beiden vorgenannten Vorteilen, noch den zusätz- liehen Nutzen, dass die Kaltkleberschicht als Siege!medium, zum Formen und Verschließen der Verpackung genutzt werden kann. Kaitkleberschtcht, in addition to the two aforementioned advantages, nor the additional benefit that the cold-adhesive layer can be used as Siege! medium, for forming and closing the packaging.
Gemäß einer bevorzugten Ausführungsform der Erfindung ist das erfindungsgemäße Folienmaterial dreischichtig aufgebaut, wobei angrenzend an die Farbstoffschicht, die einerseits unmittelbar an die Kaltkleberschicht angrenzt, auf der der Kaltkleberschicht abgewandten Seite eine Kunststoffschicht aufweist, die bevorzugt eine Poiyolefin- schicht ist, wobei besonders bevorzugt eine orientierte Polypropylenschicht erfindungsgemäß geeignet ist, um das Folienmateriai nach außen, d.h. auf der vom According to a preferred embodiment of the invention, the film material according to the invention is constructed in three layers, adjacent to the dye layer, which on the one hand directly adjacent to the cold adhesive layer on the side facing away from the cold adhesive layer has a plastic layer which is preferably a Poiyolefin- layer, with an oriented preferred Polypropylene layer is suitable according to the invention to the Folienmateriai outwards, ie on the of
Produkt abgewandten Seite abzuschließen. Complete the product side away.
Erfindungsgemäß ist es hierbei in vorteilhafter Weise möglich, als Kunststoffschicht eine orientierte Homo-Polypropylenschicht zu verwenden, so dass das erfindungsgemäße Folienmateriai bzw. Laminat gegenüber dem Stand der Technik den Vorteil einer weitaus günstigeren Herstellung ermöglicht, da auf die Verwendung einer teuren coextrudierten orientierten Polypropylenschicht verzichtet werden kann. According to the invention, it is possible in an advantageous manner to use an oriented homo-polypropylene layer as the plastic layer, so that the foil material or laminate according to the invention has the advantage of a much more favorable production than the prior art since it dispenses with the use of an expensive coextruded oriented polypropylene layer can be.
Darüber hinaus bietet die Verwendung einer einfachen orientierten Homo-Polypropylenschicht den Vorteil, dass diese klar durchscheinend ausgebildet sein kann, so dass eine mittels der Farbstoffschicht bewirkte farbliche Gestaltung exakt, schlierenfrei und scharf mit einem sehr hohen Glanzfaktor möglich ist, wobei dieser Glanzfaktor durch die Verwendung der orientierten Homo-Polypropylenschicht sogar noch verstärkt werden kann. An dieser Stelle sei erwähnt, dass als orientierte Homo-Polypropylenschicht neben einer biaxial orientierten Homo-Polypropylenschicht auch eine monoaxial orientierte Homo-Polypropylenschicht mit einem Reckverhältnis > 1, bevorzugt > 3 und besonders bevorzugt > 6 in Frage kommt, so dass eine derartige erfindungsgemäß hergestellte Verpackung auch durch simples Aufreißen leicht geöffnet werden kann. Des Weiteren besteht die Kaltkleberschicht erfindungsgemäß aus einem Kaltkleber auf Latex- oder Acrylbasis, so dass in vorteilhafter Weise kostengünstige Kaltkleber verwendet werden können, um ein erfindungsgemäßes Folienmaterial zur Herstellung einer flexiblen Verpackung für alkalihaltige Produkte herzustellen. Im übrigen ist es erfindungsgemäß Möglich, eine sehr dünne Kunststoffschicht als nach Außen gerichteten Abschluß des erfindungsgemäßen Folienmaterials zu verwenden, wobei für die Kunststoffschicht eine Dicke im Bereich von 0,5 pm bis 60 pm, bevorzugt eine Dicke im Bereich von 1 μηι bis 50 μηι und besonders bevorzugt eine Dicke im Bereich von 2 pm bis 35 pm in Frage kommen. Die Verwendung einer derartig dünnen Kunststoffschicht, bevorzugt aus orientiertem Homo-Polypropylen, ist erfindungsgemäß möglich, da diese Kunststoffschicht quasi nur als Hüllschicht zur äußeren Stabiiisation des erfindungsgemäßen Folienmaterials dient. Dadurch, dass die Dicke der erfindungsgemäß einsetzbaren Kunststoffschicht derartig dünn ist, resultiert für das damit hergestellte Foiienmateriai ein äußerst geringes Flächengewicht sowie, aufgrund des geringen Materialbedarfs zum Hersteilen einer solchen dünnen Kunststoffschicht, auch gegenüber dem Stand der Technik deutlich reduzierte Kosten. In addition, the use of a simple homo-polypropylene oriented layer has the advantage that it can be made clear translucent, so that caused by the dye layer color design is exact, streak-free and sharp with a very high gloss factor is possible, this gloss factor by the use the oriented homo-polypropylene layer can even be reinforced. At this point, it should be mentioned that as a oriented homo-polypropylene layer in addition to a biaxially oriented homo-polypropylene layer, a monoaxially oriented homo-polypropylene layer with a stretch ratio> 1, preferably> 3 and particularly preferably> 6 is suitable, such that one produced in accordance with the invention Packaging can also be easily opened by simply tearing open. Furthermore, the cold adhesive layer according to the invention consists of a cold adhesive based on latex or acrylic, so that inexpensive cold adhesives can advantageously be used to produce a film material according to the invention for producing a flexible package for alkaline products. Moreover, it is possible according to the invention to use a very thin plastic layer as outwardly directed termination of the film material according to the invention, wherein for the plastic layer has a thickness in the range of 0.5 pm to 60 pm, preferably a thickness in the range of 1 μηι to 50 μηι and more preferably a thickness in the range of 2 pm to 35 pm come into question. The use of such a thin plastic layer, preferably of oriented homo-polypropylene, is possible according to the invention, since this plastic layer serves, as it were, only as an enveloping layer for external stabilization of the film material according to the invention. The fact that the thickness of the plastic layer used in this invention is so thin, resulting for Foiienmateriai produced therewith an extremely low basis weight and, due to the low material requirements for the production of such a thin plastic layer, also compared to the prior art significantly reduced costs.
Im übrigen weist die erfindungsgemäß bevorzugt verwendete orientierte Homo-Poiy- propylenschicht den Zusatznutzen auf, dass diese Schicht gegenüber einer Kaltkleberschicht auf der Rolle nicht zum Verkleben mit der Kaltkleberschicht neigt, sondern Release-Eigenschaften aufweist, so dass erfindungsgemäß auf die Verwendung einer zusätzlichen Releaseschicht verzichtet werden kann, was nochmals zu einer kostengünstigeren Hersteilbarkeit des erfindungsgemäßen Folienmaterials beiträgt. Darüber hinaus kann somit erfindungsgemäß ein sortenreines Kunststoff material, beispielsweise wie vorgenannt ein Polyolefin für die Kunststoffschicht verwendet werden, was eine Entsorgbarkeit einer gebrauchten Packung vereinfacht, Moreover, the oriented homo-polypropylene propylene layer preferably used according to the invention has the additional benefit that this layer does not tend to adhere to the cold adhesive layer with respect to a cold adhesive layer but has release properties, so that according to the invention the use of an additional release layer is dispensed with can be, which in turn contributes to a more cost-effective manufacturability of the film material according to the invention. In addition, therefore, according to the invention a pure plastic material, for example, as previously mentioned a polyolefin can be used for the plastic layer, which simplifies the disposability of a used package,
Die Kaitkleberschicht und die Farbstoffschicht weisen erfindungsgemäß folgende Flächengewichte auf: The Kaitkleberschicht and the dye layer according to the invention have the following basis weights:
Figure imgf000007_0001
Figure imgf000007_0001
Anhand eines Einsatzes von Farbstoff unter Verwendung oben genannten Farbstoffauftrags können erfindungsgemäß vielfältige Gestaltungen des Folienmaterials sowie einer daraus hergestellten Verpackung realisiert werden, was zu einem überzeugenden und ästhetischen Erscheinungsbild einer solchen Verpackung entscheidend beiträgt. Darüber hinaus ist es möglich, Kaltkleberschichten mit den in der Tabelle genannten Flächengewichten einzusetzen, wodurch es vorteilhafterweise möglich ist, eine Belastbarkeit, bzw. mit anderen Worten eine Festigkeit, einer mit der Kaltkleberschicht bewirkten Klebung bzw. Siegelung an jeweilige unterschiedliche Erfordernisse von zu verpackenden Gütern anzupassen und darüber hinaus die Isolierwirkung der Kaltkleberschicht an die jeweilige Baslzität eines aika!ihaitigen Produktes anzupassen, so dass die Farbstoffschicht erfindungsgemäß jedenfalls optimal vor alkalischen Bestandteilen des verpackten Gutes geschützt ist. Darüber hinaus wird die erfindungsgemäße Aufgabe auch durch eine aikaliresistente Verpackung aus einem Folienmaterial gemäß den vorstehenden Ausführungen gelöst. On the basis of a use of dye using the above-mentioned dye application can be realized according to the invention various designs of the film material and a packaging produced therefrom, which contributes decisively to a convincing and aesthetic appearance of such packaging. Moreover, it is possible to use cold glue layers having the basis weights given in the table, whereby it is advantageously possible to have a strength, or in other words a strength, of a bond or seal with the cold glue layer to respective different requirements of goods to be packaged adapt and beyond the insulating effect of the cold adhesive layer to the respective baseliness of an aika! ihaitigen product adapt, so that the dye layer according to the invention in any case optimally protected against alkaline components of the packaged goods. In addition, the object of the invention is also achieved by a aikaliresistente packaging of a film material according to the above.
Weitere Ausführungsformen der Erfindung ergeben sich aus den Unteransprüchen. Nachfolgend wird die Erfindung anhand eines Ausführungsbeispiels beschrieben, das anhand der Abbildungen näher erläutert wird. Hierbei zeigen : Further embodiments of the invention will become apparent from the dependent claims. The invention will be described with reference to an embodiment which is explained in more detail with reference to the figures. Hereby show:
Fig. 1 eine schematische Darstellung eines herkömmlichen Laminats zur Fig. 1 is a schematic representation of a conventional laminate for
Herstellung einer flexiblen Verpackung für aikalihaltige Produkte gemäß dem Stand der Technik; und  Production of a flexible packaging for aikalihaltige products according to the prior art; and
Fig. 2 eine schematische Darstellung eines erfindungsgemäßen Folienmaterials zur Herstellung einer flexiblen Verpackung für aikalihaltige Produkte. In der nachfolgenden Beschreibung werden für gleiche und gleich wirkende Teile dieselben Bezugsziffern verwendet. Fig. 2 is a schematic representation of a film material according to the invention for producing a flexible packaging for aikalihaltige products. In the following description, the same reference numerals are used for the same and like parts.
So zeigt Fig. 2 einen schematischen Aufbau eines erfindungsgemäßen Folienmaterials 100 mit einer Produktseite 110, an welcher ein alkalihaitiges Produkt, nämlich ein Waschmittel-Tab 40, anliegt. Des weiteren weist das Folienmaterial 100 eine Folien- materiai-Außenseite 120 auf, die der Produktseite 110 des Folienmaterials 100 gegenüberliegend angeordnet ist. Die Folienmaterial-Außenseite 120 wird durch ein biaxial orientiertes Homo-Poiypropylenpolymer 30 gebildet, das eine Schichtdicke von 5 μηι hat. An diese Kunststoffschicht 30 aus Polypropylen schließt sich in Richtung Produkt- seite 110 eine Farbstoffschicht 20 an die Polypropylenschicht 30 an. Die Farbschicht weist ein Flächengewicht von 1 g/m2 auf und ist im Wesentlichen vollflächig an der orientierten Polypropylenschicht 30 angeordnet. Als innerste, dem Produkt zuge- wandte und an den Tab 40 angrenzende Schicht ist, wie in Fig. 2 dargestellt, eine Klebstoffschicht 10 vorgesehen, wobei diese durch einen Kaltkleber auf Latexbasis mit einem Flächengewicht von 2,5 g/m2 realisiert ist. An dieser Stelle sei darauf hingewiesen, dass alle oben beschriebenen Teile für sich alleine gesehen und in jeder Kombination, insbesondere die in den Zeichnungen dargestellten Details als erfindungswesentlich beansprucht werden. Abänderungen hiervon sind dem Fachmann geläufig. Thus, FIG. 2 shows a schematic structure of a film material 100 according to the invention with a product side 110 against which an alkaline-containing product, namely a detergent tab 40, is present. Furthermore, the film material 100 has a film material outer side 120, which is arranged opposite the product side 110 of the film material 100. The foil material outer side 120 is formed by a biaxially oriented homo-polypropylene polymer 30 which has a layer thickness of 5 μm. At the product side 110, a dye layer 20 adjoins the polypropylene layer 30 at this plastic layer 30 made of polypropylene. The color layer has a weight per unit area of 1 g / m 2 and is arranged essentially over the whole area on the oriented polypropylene layer 30. The innermost product added to the product As shown in FIG. 2, an adhesive layer 10 that is turned and adjacent to tab 40 is provided, this being realized by a latex-based cold adhesive having a weight per unit area of 2.5 g / m 2 . It should be noted at this point that all of the parts described above are considered to be essential to the invention and in every combination, in particular the details shown in the drawings, as essential to the invention. Variations thereof are familiar to the person skilled in the art.
B e z u g s z e i c h e n : S e c tio ns:
10 Kleberschicht 10 adhesive layer
20 Farbschicht  20 color coat
30 Kunststoffschicht  30 plastic layer
40 Tab  40 tab
50 Siegelschicht  50 sealing layer
60 Releaseschicht  60 release layer
70 coextrudierte Kunststoffschicht  70 coextruded plastic layer
100 Folienmaterial  100 film material
110 Produktseite  110 product page
120 Folienmaterial-Außenseite  120 outer foil material

Claims

P a t e n t a n s p r ü c h e P a n t a n s p r e c h e
Folienmaterial (100) zur Herstellung einer flexiblen Verpackung für alkalihal- tige Produkte mit einer Produktseite (110), an weicher im Falle der fertigen Verpackung das alkalihaltige Produkt angrenzt, und einer Foiienmaterial- außenseite (120), Film material (100) for producing a flexible package for alkaline products having a product side (110) on which the alkaline product adjoins in the case of the finished package, and a film material outside (120),
dadurch gekennzeichnet, dass characterized in that
die Produktseite (110) des Folienmateriais (100) eine Kaltkleberschicht (10) ist, an welche in Richtung der Follenmaterialaußenseite (120) eine Farbstoff- schicht (20) angrenzt. the product side (110) of the film material (100) is a cold adhesive layer (10), against which a dye layer (20) adjoins in the direction of the exterior material of the filler material (120).
Folienmaterial nach Anspruch 1, Foil material according to claim 1,
gekennzeichnet durch marked by
einen dreischichtigen Aufbau, wobei angrenzend an die Farbstoffschicht (20) eine Kunststoffschicht (30) angeordnet ist. a three-layer structure, wherein adjacent to the dye layer (20), a plastic layer (30) is arranged.
Folienmaterial nach einem der vorhergehenden Ansprüche Foil material according to one of the preceding claims
dadurch gekennzeichnet, dass characterized in that
die Kaltkleberschicht (10) aus einen Kaitkleber auf Latex- oder Acrylbasis besteht. the cold adhesive layer (10) consists of a caitic adhesive based on latex or acrylic.
Folienmaterial nach einem der vorhergehenden Ansprüche Foil material according to one of the preceding claims
dadurch gekennzeichnet, dass characterized in that
die Kunststoffschicht (30) eine Polyolefinschicht, bevorzugt eine orientierte Polypropylenschicht, und besonders bevorzugt eine orientierte Homo- Polypropylenschicht Ist. the plastic layer (30) is a polyolefin layer, preferably an oriented polypropylene layer, and particularly preferably an oriented homo-polypropylene layer.
Folienmaterial nach einem der vorhergehenden Ansprüche 2 oder 4, dadurch gekennzeichnet, dass Sheet material according to one of the preceding claims 2 or 4, characterized in that
die Kunststoffschicht (30) eine Dicke im Bereich von 0,5 pm bis 60 pm, bevorzugt eine Dicke im Bereich von 1 pm bis 50 pm und besonders bevorzugt eine Dicke im Bereich von 2 pm bis 35 pm aufweist. the plastic layer (30) has a thickness in the range from 0.5 μm to 60 μm, preferably a thickness in the range from 1 μm to 50 μm and particularly preferably a thickness in the range from 2 μm to 35 μm.
6. Folienmateriai nach einem der vorhergehenden Ansprüche, 6. Folienmateriai according to any one of the preceding claims,
dadurch gekennzeichnet, dass  characterized in that
die Kaltkleberschicht (10) und die Farbstoffschicht (20) folgende Flächengewichte aufweisen :  the cold-adhesive layer (10) and the dye layer (20) have the following basis weights:
Figure imgf000011_0001
Figure imgf000011_0001
7. Alkaliresistente Verpackung aus einem Folienmateriai (100) gemäß einem der vorhergehenden Ansprüche 1 bis 6. 7. Alkali-resistant packaging of a Folienmateriai (100) according to one of the preceding claims 1 to 6.
PCT/EP2012/056984 2011-04-19 2012-04-17 Film material for producing flexible packaging for alkali-containing products and packaging which is alakli-resistant and which is produced from said film material WO2012143345A1 (en)