WO2012138001A1 - 고무용 산화방지제 및 이를 포함하는 합성고무 - Google Patents
고무용 산화방지제 및 이를 포함하는 합성고무 Download PDFInfo
- Publication number
- WO2012138001A1 WO2012138001A1 PCT/KR2011/002469 KR2011002469W WO2012138001A1 WO 2012138001 A1 WO2012138001 A1 WO 2012138001A1 KR 2011002469 W KR2011002469 W KR 2011002469W WO 2012138001 A1 WO2012138001 A1 WO 2012138001A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- rubber
- antioxidant
- styrene
- butadiene
- formula
- Prior art date
Abstract
Description
Claims (4)
- 제 1 항에 있어서, 상기 화학식 1에서 R2는 탄소수가 8개, 탄소수 10개 및 탄소수 12개인 티오 화합물 중에서 선택된 1종 또는 2종 이상인 것을 특징으로 하는 고무용 산화방지제.
- 고무 100 중량부에 대하여, 청구항 1 또는 청구항 2의 고무용 산화방지제가 0.01 ~ 5 중량부 포함되는 것을 특징으로 하는 합성고무.
- 제 3 항에 있어서, 상기 고무는 부타디엔 중합체, 스티렌-부타디엔 공중합체, 랜덤 스티렌-부타디엔 공중합체, 스티렌-부타디엔-스티렌 블록 공중합체, 스티렌-부타디엔 블록 공중합체 및 스티렌-부타디엔-스티렌- 부타디엔 형태의 다중블록 공중합체 중에서 선택 1종 또는 2종 이상인 것을 특징으로 하는 합성고무.